DE3004905A1 - Heat transfer, flame resistant laminated board - has top and bottom layer impregnated with soln. of hydrate, phosphate or sulphate crystals contg. water of crystallisation - Google Patents

Heat transfer, flame resistant laminated board - has top and bottom layer impregnated with soln. of hydrate, phosphate or sulphate crystals contg. water of crystallisation

Info

Publication number
DE3004905A1
DE3004905A1 DE19803004905 DE3004905A DE3004905A1 DE 3004905 A1 DE3004905 A1 DE 3004905A1 DE 19803004905 DE19803004905 DE 19803004905 DE 3004905 A DE3004905 A DE 3004905A DE 3004905 A1 DE3004905 A1 DE 3004905A1
Authority
DE
Germany
Prior art keywords
ceramic
heat transfer
glass
rock
fireproof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE19803004905
Other languages
German (de)
Inventor
Ernst Josef 6903 Neckargemünd Lohrum
Geb. Boehmer Herta Lohrum
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WILSER FRIED
Original Assignee
WILSER FRIED
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WILSER FRIED filed Critical WILSER FRIED
Priority to DE19803004905 priority Critical patent/DE3004905A1/en
Publication of DE3004905A1 publication Critical patent/DE3004905A1/en
Ceased legal-status Critical Current

Abstract

In a multilayer, flame resistant, heat transfer reducing laminated board with a bottom and top layer of pressed mineral-, clay-, aluminium oxide-, glass-, ceramic-, graphite-, basalt-, vegetable- or animal fibres or wool thereof, both the top and bottom layer are impregnated with a liq. to viscous soln. of hydrate-, sulphate- or phosphate crystals contg. water of crystallisation e.g. potassium aluminium sulphate, disodium (ortho)phosphate, trisodium phosphate, tetrametaphosphate, other orthophosphates contg. water of crystallisation, monosodium phosphate or "marble white chalk O". The soln. is prepd. by heating and/or addition of water. On exposure to high temps. e.g. 1000 deg.C, water of crystallisation separates off, cooling the board and reducing heat transfer. On longer exposure to elevated temps., a recrystallisation of the water of crystallisation occurs with simultaneous high heat energy formation and a desensifying of the surfaces and the board. The desensifying brings about heat storage with delayed release. During the delay, heat transfer is interrupted.

Description

Verbundplatten, mehrflächig, feuerfest,Composite panels, multi-surface, fireproof,

den Wärmedurchgang reduzierend.reducing the heat transfer.

Feuerbeständige oder teilweise feuerbeständige, nicht brennbare, den Wärmedurchgang hemmende Platten sind bekannt. Zudem ist bekannt, daß solche Platten hergestellt werden aus zusammengepreßten Tonerdesilikat- oder Keramik- oder Glas- oder Graphit- oder Aluminiumoxid- oder Silikat- oder Basalt- oder anderen Gesteinsfasern oder daraus hergestellter Wolle. Außerdem ist bekannt, daß solche herkömmlichen Platten, auch Wärmedämmplatten genannt, unter Zufügung z. B. von Phenolharzen unterschiedlicher Modifikationen oder Gips oder Silikatverbindungen u. a. gebunden, stabilisiert und verdichtet werden.Fire-resistant or partially fire-resistant, non-flammable, den Plates preventing the passage of heat are known. It is also known that such plates are made of compressed alumina silicate or ceramic or glass or graphite or alumina or silicate or basalt or other rock fibers or wool made from it. It is also known that such conventional Panels, also called thermal insulation panels, with the addition of z. B. of phenolic resins different Modifications or gypsum or silicate compounds, among others. bound, stabilized and be condensed.

Die Neuerung betrifft Verbundplatten, mehrflächig, bestehend aus einer Unter- und mindestens einer Oberfläche - siehe Fig. 1 -die beide übereinandergelagert sind. Beide Flächen wahlweise bestehend aus mit oder ohne Bindemittel zusammengepreßten Mineral- oder Tonerdesilikat- oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit- oder Basalt- oder anderen Gesteins-oder Silizium- oder auch pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle. Soweit diese aus anorganischen Fasern bestehen sind sie nicht brennbar und verfügen über eine geringe Wärmeleitzahl, wenn sie aus pflanzlichen oder tierischen Fasern hergestellt sind, sind diese teils brennbar oder flnmmhemmend ausgerüstet und haben ein relativ geringes Wärmeleitvermögen. Die Neuerung hat zum Gegenstand, beide Wärmedämmflächen, somit die Unter- als auch die Oberfläche der Verbundplatte in Ergänzung der Wärmedämmleistung die diese Flächen ausweisen bzw. besitzen, mit feuerfesten, den Wärmedurchgang bzw. Wärmefluß weiter reduzierenden und zugleich Wärmeenergie abbauenden Lösungen zu tränken oder zu imprägnieren und zugleich zu beschichten. Diese Lösungen sind hergestellt aus durch Zufuhr von Wärme oder Zufügung von Wasser oder beidem in flüssige bis viskose Lösung gebrachten kristallwasserhaltigen Hydrat- oder Sulfat- oder Phosphat-Kristallinen bzw.The innovation concerns composite panels, multi-surface, consisting of one Below and at least one surface - see Fig. 1 - both of which are superimposed are. Both surfaces optionally consisting of pressed together with or without binding agent Mineral or alumina silicate or alumina or glass or ceramic or Graphite or basalt or other rock or silicon or also vegetable or animal fibers or wool made therefrom. As far as these from inorganic Fibers, they are not flammable and have a low coefficient of thermal conductivity, if they are made from vegetable or animal fibers, these are partial Flammable or flame-retardant and have a relatively low thermal conductivity. The object of the innovation is both thermal insulation surfaces, thus the lower as well as the surface of the composite panel in addition to the thermal insulation performance of these surfaces identify or possess, with refractory, the heat transfer or heat flow further to soak or impregnate reducing and at the same time heat energy dissipating solutions and to be coated at the same time. These solutions are made from by feeding Heat or the addition of water or both brought into a liquid to viscous solution Hydrate or sulfate or phosphate crystalline or crystalline water containing water of crystallization

-Granulaten oder -Pulver, wie: Kaliumaluminiumsulfat oder Dinatriumorthophosphat oder Dinatriumphosphat oder Trinatriumphosphat oder Tetrametaphosphat oder anderen kristallwasserhaltigen Orthophosphaten bzw. Mononatriumphosphat oder Marmorweißkalkhydrat 0. Flächen und Platten, die nach diesem Verfahren der Neuerung getränkt und dadurch imprägniert und zugleich beschichtet sind, trocknen mit der eingebrachten Lösung durch Wärmebehandlung bzw. Zufuhr von Wärme bei relativ niederen Temperaturen aus. In solche ausgetrockneten Flächen als auch Verbundplatten sondern die darin getrockneten Lösungen dieser Neuerung während kürzerer und längerer Expositionszeiten (der Verbundplatten) in Flanenbereichen hoher Temperaturen von z. B. 100000 bis über 11000C Rristallwasser in die Flächen und Platten auch nach außen ab. Es entsteht hierdurch eine Verdunstung, die eine Abkühlung bewirkt. Zugleich wird der Wärmefluß durch die Flächen bzw. Verbundplatten zusätzlich erheblich redusiert. Nach längeren Expositionszeiten der Verbundplatten in hohen Temperaturbereichen tritt eine Wiederkristallisierung des Kristallwassers unter erheblicher Wärmeenerglebindung so ein, daß erst nach langerer Expositionszeit der Verbundplatten in hohen Temperaturbereichen eine Verdichtung in den Flächen und der Verbu.ndplatte eintreten kann. Diese Verdichtung bewirkt auf den Unterseiten der Flächen oder in den Verbundplatten eine verzögert einsetzende Wärme speicherung.-Granules or powders, such as: potassium aluminum sulfate or disodium orthophosphate or disodium phosphate or trisodium phosphate or tetrametaphosphate or others Orthophosphates containing water of crystallization or monosodium phosphate or marble white lime hydrate 0. Surfaces and panels that are soaked by this process of innovation and thereby are impregnated and coated at the same time, dry with the introduced solution by heat treatment or supply of heat at relatively low temperatures. In such dried out surfaces as well as composite panels but the ones dried in them Solutions of this innovation during shorter and longer exposure times (of the composite panels) in flank areas of high temperatures of z. B. 100000 to over 11000C crystal water into the surfaces and plates also to the outside. This creates evaporation, which causes a cooling. At the same time, the heat flow through the surfaces or composite panels also significantly reduced. After long exposure times of the composite panels Recrystallization of the water of crystallization occurs in high temperature ranges with considerable heat energy binding in such a way that only after a long exposure time the composite panels in high temperature ranges a compaction in the surfaces and the Verbu.ndplatte can enter. This compression causes on the undersides the surfaces or in the composite panels a delayed onset of heat storage.

Während der Verzögerungszeit ist der Wärmedurchfluß weitgehendst unterbrochen. Die Schmelzbereiche vorbezeichneter Phosphat-, Rydrat- bzw. Sulfat-Kristalline sind unterschiedlich So liegt der Schmelzpunkt des Kaliumaluminiumsulfates mit 12 Mol Kristallwasser bei 920C, der Schmelzpunkt des Dinatriumorthophosphates mit 12 Mol Kristallwasser bei 34,60C und der Schmelzpunkt z. B. von Dlnatriumorthophosphat mit korrigiertem pH-Wert bsi 33°O, dies u. a0 weil dadurch auch das physikalisch-chemische Verhalten der daraus hergestellten Lösungen, die in die Flächen bzw. Verbundplatten eingebracht sind, unterschiedlich ist, sieht diese Neuerung vor, die aufgeführten Phosphat-, Hydrat- oder Sulfat-Kristalline getrennt voneinander zu lösen und die Jeweils hergestellten Lösungen miteinander zu einer Mehrkomponentenlösung wahlweise gänzlich oder nur teilweise zu vermischen und mit dieser Mehrkomponentenlösung die Flächen der Verbundplatten dergestalt zu imprägnieren bzw. zu tränken, daß die Kristallwasserabgabe der getrockneten Lösungen je nach Lösungskomponente in die Flächen der Verbundplatten wahlweise beginnt bei 33°C oder 450C oder bei 70 bis 1500C oder bei 600 bis 8000C oder sich stufe.nweise in diesen Temperaturbereichen vollzieht und ein Verbrennen z. B. der tus tierischen oder pflanzlichen Fasern hergestellten Flächen insbesondere dann nicht möglich ist, wenn mit den Mehrkomponentenlösungen auch die Außenseiten der Flächen bzw.During the delay time, the flow of heat is largely interrupted. The melting ranges of the above-mentioned phosphate, hydrate and sulfate crystallines are different The melting point of potassium aluminum sulfate is 12 mol Water of crystallization at 920C, the melting point of disodium orthophosphate at 12 mol Water of crystallization at 34.60C and the melting point z. B. of disodium orthophosphate with corrected pH value up to 33 ° O, this partly because it also affects the physico-chemical Behavior of the solutions produced from it, which are in the surfaces or composite panels are introduced, is different, this innovation provides for those listed To dissolve phosphate, hydrate or sulfate crystalline separately from one another and the Solutions produced in each case together to form a multi-component solution optionally to be mixed completely or only partially and with this multi-component solution to impregnate or soak the surfaces of the composite panels in such a way that the Release of water of crystallization of the dried solutions depending on the solution component in the Areas of the composite panels either starts at 33 ° C or 450C or at 70 to 1500C or at 600 to 8000C or gradually in these temperature ranges takes place and a burning z. B. made of tus animal or vegetable fibers Surfaces in particular is not possible when using the multi-component solutions also the outside of the surfaces or

Platten beschichtet sind. Außerdem sieht die Neuerung vor, den Mehrkomponentenlösungen verschiedenartige Substanzen, wie Salze oder Phosphatgläser beizufügen. Weiter hat die Neuerung zum Gegenstand, daß nach Imprägnierung der Flächen der Verbundplatte an die Unterseite der unteren Fläche der Verbundplatte amorphe körnige Kieselsäure beschichtungsweise angelagert wird und Diatomeen-Erde zwischen Unter- und Oberfläche der Verbundplatte eingelagert wird. Damit eine Verdunstung der getrockneten Lösung nach der Verbundplattenaußenseite erfolgen kann, hat diese Neuerung mit zum Gegenstand, daß auf die Außenseite der Oberfläche perforierte Bleche oder Metallgewebe angelagert wurden. Siehe Fig. 2. Auch sieht diese Neuerung vor, daß die Unterfläche zusammen mit der Oberfläche an Gewebe, hergestellt aus Keramik- oder Donerdesilikat- oder Glas- oder Asbestfaser angesteppt oder angenietet wird, das wahlweise dampfdurchlässig oder mit einer Magnetstrahlen abschirmenden Aluminiumfolie kaschiert ist. Siehe Fig. 3. Vorgesehen ist eine allseitige feuerfeste Außenbeschichtung der Verbundplatten gemäß dieser Neuerung. Damit mehrere Verbundplatten miteinander verbunden bzw. zusammengefügt werden können, hat diese Neuerung mit zum Gegenstand, die Ränder bzw. Kanten der Verbundplatten mit fugenabdichtenden tiberlappungsstreifen auszustatten. Siehe Fig. 4e Zur zusätzlichen Erhöhung der Wärmedämmleistung als auch zur quantitativen Erhöhung der Kristallwasserabgabe sieht diese Neuerung ergänzend vor, in die Flächen der Verbundplatten Nuten oder Vertiefungen einzuarbeiten, die mit den viskosen Lösungen der Kristalline verfüllt werden, die anschließend durch eine Beschichtung abgedeckt werden. Siehe bigo 5.Plates are coated. The innovation also provides for multi-component solutions to add various substances such as salts or phosphate glasses. Has continued the innovation on the subject that after impregnation of the surfaces of the composite panel amorphous granular silica to the underside of the lower surface of the composite panel is deposited by coating and diatomaceous earth between the surface and the surface the composite panel is stored. This means that the dried solution evaporates can take place after the composite panel outside, this innovation has the object, that on the outside of the surface perforated sheets or metal mesh deposited became. See Fig. 2. This innovation also provides that the lower surface together with the surface on fabric made of ceramic or donor silicate or Glass or asbestos fiber is stitched or riveted, which is optionally vapor permeable or is laminated with an aluminum foil shielding magnetic rays. Please refer Fig. 3. A fire-resistant outer coating on all sides of the composite panels is provided according to this innovation. So that several composite panels are connected or joined together can be, this innovation has the subject, the edges or edges of the Equip composite panels with joint-sealing overlapping strips. See fig. 4e For an additional increase in the thermal insulation performance as well as for a quantitative increase The water of crystallization release provides for this innovation in addition, in the areas of the Composite panels incorporate grooves or depressions that deal with the viscous solutions the crystalline are filled, which is then covered by a coating will. See bigo 5.

Claims (14)

Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend0 Schutzansprüche 1 Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder Donerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle dadurch gekennzeichnet, daß die Unter- als auch die Oberfläche imprägniert oder getränkt ist mit durch Zufuhr von Wärme oder Zufügung von Wasser oder beidem in flüssiger bis viskoser Lösung gebrachten kristallwasserhaltigen Hydrat- oder Sulfat- oder Phosphat-Kristallinen, wie: Kaliumaluminiumsulfat oder Dinatriumorthophosphat oder Dinatriumphosphat oder Trinatriumphosphat oder Tetrametaphosphat oder anderen kristallwasserhaltigen Orthophosphaten bzw. Mononatriumphosphat oder Marmorweißkalkhydrat 0. Composite panels, multi-surface, fireproof, reducing heat transfer0 Protection claims 1 composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or donor silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them manufactured wool, characterized in that the bottom and the surface is impregnated or soaked with by adding heat or adding water or both hydrate containing water of crystallization brought in liquid to viscous solution or sulfate or phosphate crystallines such as: potassium aluminum sulfate or disodium orthophosphate or disodium phosphate or trisodium phosphate or tetrametaphosphate or others Orthophosphates containing water of crystallization or monosodium phosphate or marble white lime hydrate 0. 2. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder Tonerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach knspruch 1 dadurch gekennzeichnet, daß die einzelnen aufgeführten kristallwasserhaltigen Kristalline jeweils voneinander getrennt durch Zufuhr von Wärme oder Zufügung von Wasser in flüssige Lösung gebracht sind und die einzelnen Lösungen miteinander zu einer Mehrkomponentenlösung vermischt sind, mittels der die Unter- als auch wahlweise die Oberfläche der Verbundplatte imprägniert ist.2. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or alumina silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them manufactured wool according to claim 1, characterized in that the individual listed Crystallines containing water of crystallization are separated from one another by the addition of Heat or the addition of water are brought into liquid solution and the individual Solutions are mixed with one another to form a multicomponent solution, by means of which the bottom and optionally the surface of the composite panel is impregnated. 3. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral - oder lonerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 und 2 dadurch gekennzeichnet, daß der Mehrkomponentenlösung das nicht wasserlösliche Madrellsche Salz oder wahlweise das amorphe Produkt "Phosphatgläser" oder das "Eurrolsche Salz" zugesetzt ist und mit dieser Mehrkomponentenlösung bzw. -mischung die Unter- als auch wahlweise die Oberfläche der Verbundplatte imprägniert und beschichtet ist.3. Composite panels, multi-surface, fireproof, the heat transmission reducing, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or ion silicate or aluminum oxide or glass or ceramic or Graphite or basalt or other rock or vegetable or animal fibers or wool produced therefrom according to claims 1 and 2, characterized in that that the multicomponent solution, the water-insoluble Madrell salt or optionally the amorphous product "phosphate glasses" or the "Eurrol salt" is added and with this multi-component solution or mixture, the sub- and optionally the Surface of the composite panel is impregnated and coated. 4. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder Tonerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 3 dadurch gekennzeichnet, daß nach der Imprägnierung der Unter- als auch der Oberfläche der Verbundplatte an die Unterseite der Unterfläche amorphe körnige Kieselsäure durch Beschichtung angelagert ist.4. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or alumina silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them produced wool according to claims 1 to 3, characterized in that according to the impregnation of the underside and the surface of the composite panel on the underside amorphous granular silica is deposited on the undersurface by coating. 5. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder onerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 4 dadurch gekennzeichnet, daß wahlweise zwischen Unter- und Oberfläche oder auf die Innenseite der Unterfläche eine Schicht Diatomeen-Erde ein- bzw. angelagert ist.5. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or earth silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them produced wool according to claims 1 to 4, characterized in that optionally a layer between the lower surface and the surface or on the inside of the lower surface Diatomaceous earth is embedded or attached. 6. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder Tonerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 4 dadurch gekennzeichnet, daß wahlweise zwischen Unter- und Oberfläche oder auf die Unterseite der Unterfläche eine Polie oder ein Blech aus Aluminium ein- bzw. angelagert ist.6. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or alumina silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them produced wool according to claims 1 to 4, characterized in that optionally between Under and surface or on the underside of the under surface a polie or a sheet of aluminum is embedded or attached. 7. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder Uonerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 6 dadurch gekennzeichnet, daß auf die Außenseite der Oberfläche wahlweise perforierte Aluminium- oder Stahlbleche oder galvanisch metallisiertes Metallgewebe angelagert ist.7. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or earth silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them produced wool according to claims 1 to 6, characterized in that on the outside of the surface optionally perforated aluminum or steel sheets or galvanically metallized metal mesh is deposited. 8. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder Tonerdesilikat-oder liuminiumoxid- oder Glas- oder Keramik- oder Graphit-oder haait- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 6 dadurch gekennzeichnet, daß die Unter-oder wahlweise die Oberfläche angesteppt oder angenietet ist an ein im Hochvakuum metallisiertes Glasseiden- oder Asbest-oder Tonerdesilikatfasergewebe oder Mischgewebe, hergestellt aus Blasfaser- und Keramikfasergarnen oder Mischgewebe, hergestellt aus Asbestfaser- und Keramik- = lonerdesilikatfasergarnen.8. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or alumina silicate or liuminiumoxid- or glass or ceramic or graphite or haait or other rock or vegetable or animal fibers or from them produced wool according to claims 1 to 6, characterized in that the Under or optionally the surface is stitched or riveted to a in a high vacuum metallized glass silk or asbestos or alumina silicate fiber fabric or mixed fabric, made from blown fiber and ceramic fiber yarns or blended fabrics made of asbestos fiber and ceramic = ioner desilicate fiber yarns. 9. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusannnengepreßten Mineral- oder lonerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 6 dadurch gekennseichnet, daß die Unterals auch Oberfläche der Platte, diese hergestellt aus Mineral-oder Gesteinsfaser mit Fasern aus Tonerdesilikat vermischt ist.9. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or ion silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them manufactured wool according to claims 1 to 6, characterized in that the Under and surface of the plate, this made of mineral or rock fiber is mixed with fibers of alumina silicate. 10. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder lonerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 9 dadurch gekennzeichnet, daß die Unterfläche zusammen mit der Oberfläche an Gewebe, dieses hergestellt aus Keramik-, Asbest- oder Glasfaser oder aus einem Mischgewebe derselben angesteppt oder angenietet ist, auf dessen Außenseite eine Aluminiumfolie ankaschiert ist.10. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or ion silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them manufactured wool according to claims 1 to 9, characterized in that the Lower surface together with the surface of tissue, this made of ceramic, Asbestos or glass fiber or from a mixed fabric of the same stitched or riveted is, on the outside of which an aluminum foil is laminated. 11. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder onerdesilikat-oder lluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 10 dadurch gekennzeichnet, daß die Stirn- = Seitenkanten der Verbundplatten , als auch die Oberfläche der Platten durch Streichen, Tränken oder Spritzen mit Marmorweißkalkhydrat oder wahlweise mit Binder oder Mörtel aus Tonerdesilikat beschichtet sind.11. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or clay silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them produced wool according to claims 1 to 10, characterized in that the Front = side edges of the composite panels, as well as the surface of the panels through Brushing, soaking or spraying with marble white lime hydrate or optionally with a binder or mortar made of alumina silicate are coated. 12. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder onerdesilikat-oder Aluminiuioxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 11 dadurch gekennzeichnet, daß an die Ränder bzw. Kanten dieser Platten ein plattenverbindender Überlappungsstreifen, hergestellt aus zusammengepreßten Keramikfasermatten, imprägniert mit gelösten Phosphat-Kristallinen, angebracht ist.12. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or earth silicate or aluminum oxide or glass or ceramic or graphite or Basalt or other rock or vegetable or animal fibers or from them produced wool according to claims 1 to 11, characterized in that an the edges or edges of these panels have a panel-connecting overlap strip, made of compressed ceramic fiber mats, impregnated with dissolved phosphate crystallines, is appropriate. 13. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder onerdesilikat-oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit-oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach den Ansprüchen 1 bis 12 dadurch gekennzeichnet, daß wahlweise in die Unter- oder Oberfläche der Platte Nuten oder Vertiefungen eingearbeitet sind, die mit einer viskose Lösung kristallwasserhaltiger Phosphat-Kristalline verfüllt sind 13. Composite panels, multi-surface, fireproof, reducing heat transfer, Bottom and surface optionally consisting of pressed together to form surfaces Mineral or clay silicate or Alumina or glass or Ceramic or graphite or basalt or other rock or vegetable or animal fibers or wool produced therefrom according to claims 1 to 12 thereby characterized in that optionally in the bottom or surface of the plate or grooves Wells are incorporated with a viscous solution containing water of crystallization Phosphate crystalline are filled 14. Verbundplatten, mehrflächig, feuerfest, den Wärmedurchgang reduzierend, Unter- als auch Oberfläche wahlweise bestehend aus zu Flächen zusammengepreßten Mineral- oder Tonerdesilikat- oder Aluminiumoxid- oder Glas- oder Keramik- oder Graphit- oder Basalt- oder anderen Gesteins- oder pflanzlichen oder tierischen Fasern oder daraus hergestellter Wolle nach Anspruch 13 dadurch gekennzeichnet, daß die Verfüllung mit Marmorweißkalkhydrat oder wahlweise mit einer Tetrafluoräthylen-Folie oder mit Silikatmörtel überdeckt ist.14. Composite panels, multilayer, fireproof, den Reducing heat transfer, bottom and surface optionally consisting of to Mineral or alumina silicate or aluminum oxide or compressed surfaces Glass or ceramic or graphite or basalt or other rock or vegetable or animal fibers or wool produced therefrom according to claim 13 characterized that the filling with marble white lime hydrate or optionally with one Tetrafluoroethylene film or covered with silicate mortar.
DE19803004905 1980-02-09 1980-02-09 Heat transfer, flame resistant laminated board - has top and bottom layer impregnated with soln. of hydrate, phosphate or sulphate crystals contg. water of crystallisation Ceased DE3004905A1 (en)