DE29813125U1 - Conductive yarn - Google Patents

Conductive yarn

Info

Publication number
DE29813125U1
DE29813125U1 DE29813125U DE29813125U DE29813125U1 DE 29813125 U1 DE29813125 U1 DE 29813125U1 DE 29813125 U DE29813125 U DE 29813125U DE 29813125 U DE29813125 U DE 29813125U DE 29813125 U1 DE29813125 U1 DE 29813125U1
Authority
DE
Germany
Prior art keywords
yarn
conductive
stainless steel
strand
threads
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE29813125U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHINA TEXTILE INST TUCHENG
Original Assignee
CHINA TEXTILE INST TUCHENG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHINA TEXTILE INST TUCHENG filed Critical CHINA TEXTILE INST TUCHENG
Priority to DE29813125U priority Critical patent/DE29813125U1/en
Publication of DE29813125U1 publication Critical patent/DE29813125U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

PatentanwälteTergau & Pohl, Nürnberg * J .* ; · ***! ·**··**. SeitePatent AttorneysTergau & Pohl, Nuremberg * J .* ; · ***! ·**··**. Page

2 Beschreibung2 Description

3 Leitfähiges Garn 3 Conductive yarn

6 Die Erfindung betrifft eine neue Garnstruktur mit leitfähigen Eigenschaften, ein Gewebe6 The invention relates to a new yarn structure with conductive properties, a fabric

7 mit leitfähigen Eigenschaften und eine Vorrichtung zur Herstellung eines Garns mit leitfä-7 with conductive properties and a device for producing a yarn with conductive

8 higen Eigenschaften.8 higen properties.

10 Eine herkömmliche Struktur eines leitfähigen Garns, wie sie in der Figur 1 gezeigt ist,10 A conventional structure of a conductive yarn as shown in Figure 1,

11 besteht aus einem Faden oder Strang eines nichtleitenden Garnes, der mit einer dünnen11 consists of a thread or strand of non-conductive yarn, which is coated with a thin

12 Lage einer dünnen leitfähigen Metallfolie 12 überzogen ist. Die Breite der Folie reicht von12 layer of a thin conductive metal foil 12. The width of the foil ranges from

13 1 bis 2 Millimetern und verleiht dem Garn leitende Eigenschaften. Das leitfähige Garn ist13 1 to 2 millimeters and gives the yarn conductive properties. The conductive yarn is

14 des weiteren mit durchschnittlich nichtleitendem Garn zu einem leitfähigen Gewebe für14 further with average non-conductive yarn to form a conductive fabric for

15 die Verwendung bei besonderen Anwendungen verwoben. Als ein anschauliches Beispiel ie müssen Gewebe, die zum Herstellen von leitenden Fechtjacken verwendet werden, eine15 for use in special applications. As an illustrative example, the fabrics used to make conductive fencing jackets must have a

17 ausreichende Festigkeit aufweisen. Die Schaltung von elektrischen Anzeigevorrichtun-17 have sufficient strength. The circuit of electrical display devices

18 gen, die mit einem Fechter verbunden sind, muß die Leitfähigkeitseigenschaften von18 genes connected to a fencer must have the conductivity properties of

19 Fechtjacken nutzen. Die Festigkeit von Bekleidungsstücken wird durch ein verwobenes19 fencing jackets. The strength of clothing is increased by an interwoven

20 Garn mit einer hohen Zugfestigkeit erreicht. Deshalb muß ein Fechter üblicherweise wäh-20 yarn with a high tensile strength. Therefore, a fencer usually has to

21 rend eines Wettkampfes drei Bekleidungsstücke tragen. Dies ist ziemlich unbequem. Zu-21 wear three items of clothing during a competition. This is quite uncomfortable.

22 sätzlich macht die dünne Folie, die um das Garn gewickelt ist, das Gewebe weniger flexi-22 In addition, the thin film wrapped around the yarn makes the fabric less flexible.

23 bei. Es ist wünschenswert, bekannte Garnstrukturen zu verbessern.23. It is desirable to improve known yarn structures.

25 In Hinblick auf die obigen Probleme stellt die Erfindung eine neue Garnstruktur bereit, die25 In view of the above problems, the invention provides a new yarn structure which

26 einen Garnstrang verwendet, der mit zwei sich kreuzenden leitfähigen rostfreien Stahlfä-26 uses a yarn strand that is connected to two intersecting conductive stainless steel threads.

27 den umwickelt ist, um einen leitfähigen Garnfaden herzustellen, der eine große Festigkeit27 which is wrapped around to produce a conductive yarn thread that has a high strength

28 und gute Leitfähigkeitseigenschaften hat. Die Garnstruktur der Erfindung hat eine überle-28 and has good conductivity properties. The yarn structure of the invention has a superior

29 gene Zugfestigkeit und erfüllt die Anforderungen zur Herstellung von Fechtjacken.29 tensile strength and meets the requirements for the production of fencing jackets.

31 Nun werden die Struktur und die Eigenschaften der Erfindung unten detailliert unter Be-31 Now, the structure and characteristics of the invention are described in detail below under

32 zugnahme auf die beigefügten Zeichnungen beschrieben.32 with reference to the accompanying drawings.

34 KURZE BESCHREIBUNG DER ZEICHNUNGEN34 BRIEF DESCRIPTION OF THE DRAWINGS

N:\AN\98478.DOC 22. Juli 1998N:\AN\98478.DOC 22 July 1998

Patentanwälte Tergau & Pohl, Nürnberg · *; **J* ·**· ***&iacgr; .**..·*. SeitePatent Attorneys Tergau & Pohl, Nuremberg · *; **J* ·**· ***&iacgr; .**..·*. Page

&igr; Figur 1 ist eine schematische Ansicht, die den Aufbau eines bekannten leitfähigen Gar-&igr; Figure 1 is a schematic view showing the structure of a known conductive gar-

2 nes zeigt.2 nes shows.

4 Figur 2 zeigt den Aufbau von leitfähigem Garn gemäß der Erfindung.4 Figure 2 shows the structure of conductive yarn according to the invention.

6 Figur 3 beschreibt den Herstellungsprozess des leitfähigen Garns gemäß der Erfindung.6 Figure 3 describes the manufacturing process of the conductive yarn according to the invention.

&bgr; GENAUE BESCHREIBUNG BEVORZUGTER AUSFÜHRUNGEN&bgr; DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

10 Unter bezugnahme auf die Figur 2 verwendet die Erfindung Führungssräder, um zwei10 Referring to Figure 2, the invention uses guide wheels to drive two

11 rostfreie Fäden 3 um einen nichtleitenden Garnfaden 1 in einer Weise zu wickeln, in der11 stainless steel threads 3 around a non-conductive yarn thread 1 in a manner in which

12 sie einander kreuzen, um eine unvollständig abgeschirmte Struktur auszubilden. Ein sol-12 they cross each other to form an incompletely shielded structure. Such a

13 eher Faden hat nicht nur eine gute Festigkeit, sondern hat durch die rostfreien Fäden13 rather thread not only has a good strength, but has due to the rust-proof threads

14 auch eine überragende oder ausgezeichnete Leitfähigkeit.14 also has superior or excellent conductivity.

is Die bevorzugte Wickeldichte der rostfreien Stahlfäden rund um das leitfähige Garn ge-is The preferred winding density of the stainless steel threads around the conductive yarn

17 maß der Erfindung reicht von 100 bis 500 Umwicklungen pro Meter. Die Durchmesser der17 The invention ranges from 100 to 500 wraps per meter. The diameters of the

is bevorzugten rostfreien Stahlfäden liegt zwischen 0,06 und 0,12 Zentimeter. Die Garn-The preferred stainless steel threads are between 0.06 and 0.12 centimeters. The yarn

19 oder Feinheitsnummer des nichtleitenden Garns 3 ist vorzugsweise zwischen 500 und19 or fineness number of the non-conductive yarn 3 is preferably between 500 and

20 3000 Denier. Mit den obigen Kombinationen kann die Garn- oder Feinheitsnummer des20 3000 Denier. With the above combinations, the yarn or fineness number of the

21 leitfähigen Garns mehr als 1000 Denier erreichen, und das Gewebe hat einen elektri-21 conductive yarn can reach more than 1000 denier, and the fabric has an electrical

22 sehen Oberflächenwiderstand unterhalb von 5 Ohm. Eine Fechtjacke, die aus einem sol-22 see surface resistance below 5 ohms. A fencing jacket made of such a

23 chen Gewebe hergestellt wurde, weist eine hohe Leitfähigkeit und Festigkeit auf, während23 fabric has a high conductivity and strength, while

24 sie infolge ihrer fein gewobenen Struktur für die Träger weich und bequem ist.24 Due to its finely woven structure it is soft and comfortable for the wearer.

26 Die Garnstruktur gemäß der Erfindung weist tatsächlich die folgenden Vorteile auf.26 The yarn structure according to the invention actually has the following advantages.

28 1. Rostfreie Stahlfäden haben eine gute Leitfähigkeit und das Material ist leicht zu erlan-28 1. Stainless steel threads have good conductivity and the material is easy to obtain.

29 gen. Die vorliegende Erfindung hat keine Umweltemissionen, anders als beim Stand der29 gen. The present invention has no environmental emissions, unlike the prior art

30 Technik, der nichtleitendes Garn verwendet, das mit Metall überzogen oder plattiert ist.30 Technique that uses non-conductive yarn coated or plated with metal.

31 Deshalb kann die Erfindung Material- und Herstellungskosten signifikant reduzieren.31 Therefore, the invention can significantly reduce material and manufacturing costs.

33 2. Die Struktur des leitfähigen Garns gemäß der Erfindung enthält einen Strang oder Fa-33 2. The structure of the conductive yarn according to the invention contains a strand or fiber

34 den eines nichtleitenden Garnes, das mit zwei rostfreien Stahlfäden umhüllt ist, und des-34 that of a non-conductive yarn covered with two stainless steel threads, and

N:\AN\98478.DOC 22. Juli 1998N:\AN\98478.DOC 22 July 1998

Patentanwälte Tergau & Pohl, Nürnberg ·**;'"' ·"·"*: ,"..··. SeitePatent Attorneys Tergau & Pohl, Nuremberg ·**;'"'·"·"*:,"...··. Page

* ·4 &igr;* ·4 &igr;

&igr; halb hat das Gewebe eine größere Festigkeit als herkömmliches leitfähiges Garngewebe&igr; half the fabric has a greater strength than conventional conductive yarn fabric

2 auf.2 on.

4 3. Herkömmliches leitfähiges Garn wird aus nichtleitendem Garn, das mit einer äußeren4 3. Conventional conductive yarn is made from non-conductive yarn coated with an outer

5 Schicht aus einer dünnen Metallfolie überzogen ist, hergestellt und weist so eine höhere &bgr; Steifheit und eine größere Dicke auf. Ein solches Garn ist schädlich für eine Fertigungs-7 ausrüstung von nachfolgenden Herstellungsprozessen. Das leitfähige Garn gemäß der5 layer of a thin metal foil, thus having a higher β stiffness and a greater thickness. Such a yarn is harmful to a manufacturing 7 equipment of subsequent manufacturing processes. The conductive yarn according to the

&bgr; Erfindung verwendet dünnere rostfreie Stahlfäden, und demgemäß weisen die Gewebe-&bgr; invention uses thinner stainless steel threads, and accordingly the fabrics

9 produkte eine bessere Weichheit auf. Deshalb wird es die Fertigungsausrüstung nicht9 products have better softness. Therefore, the manufacturing equipment will not

10 beschädigen.10 damage.

12 4. Aus dem erfindungsgemäßen Garn hergestellte Stoffe weisen aufgrund ihrer einheitli-12 4. Fabrics made from the yarn according to the invention have, due to their uniform

13 chen Garnstruktur einen besseren Glanz auf. Deshalb sind sie für Fechtjacken vorteilhaft, &eegr; da diese weiß sein müssen.13 The yarn structure gives it a better shine. This makes them ideal for fencing jackets, &eegr; as these have to be white.

ie Die Figur 3 zeigt ein bevorzugtes Herstellungsverfahren für leitfähiges Garn gemäß derie Figure 3 shows a preferred manufacturing process for conductive yarn according to the

17 Erfindung, bei dem Führungsräder nichtleitendes Garn 1 zu einer leeren Spindel 4 führen.17 Invention in which guide wheels guide non-conductive yarn 1 to an empty spindle 4.

ie Am Austritt winden oder wickeln sich rostfreie Stahlfäden um das nichtleitende Garn 1,ie At the outlet, stainless steel threads wind or wrap around the non-conductive yarn 1,

is während die Spindel 4 rotiert, um einen halbfertigen Strang des Garnfaden zu bilden.is while the spindle 4 rotates to form a semi-finished strand of yarn thread.

20 Dann wird der halbfertige Strang erneut mit dem obigen Herstellungsverfahren behandelt,20 Then the semi-finished strand is treated again with the above manufacturing process,

21 während die leere Spindel 4 in der entgegengesetzten Richtung rotiert. Demgemäß win-21 while the empty spindle 4 rotates in the opposite direction. Accordingly,

22 det oder wickelt sich ein weiterer rostfreier Stahlfaden um den halbfertigen Garnfaden,22 det or another stainless steel thread wraps around the half-finished yarn thread,

23 um einen Strang eines leitfähigen Garnfadens zu bilden, der mit zwei sich kreuzenden23 to form a strand of conductive yarn thread connected to two crossing

24 rostfreien Stahlfäden 3 umwickelt ist.24 stainless steel threads 3 are wrapped around.

26 Wie oben beschrieben, stellt die neue leitfähige Gamstruktur gemäß der Erfindung klar26 As described above, the new conductive yarn structure according to the invention clearly

27 eine bessere Anwendbarkeit bereit, die aus dem Stand der Technik bei der Herstellung27 provides a better applicability that is based on the state of the art in the manufacture

28 von Garnstrukturen nicht bekannt ist.28 of yarn structures is not known.

30 Zusammenfassend betrifft die Erfindung Garn, das leitfähige Eigenschaften aufweist. Das30 In summary, the invention relates to yarn that has conductive properties.

31 leitfähige Garn besteht hauptsächlich aus einem Strang oder Faden nichtleitenden Gar-31 Conductive yarn consists mainly of a strand or thread of non-conductive yarn

32 nes, das über Kreuz mit zwei rostfreien Stahlfäden umwickelt ist. Das Garn, das so her-32 nes, which is wound crosswise with two stainless steel threads. The yarn, which is thus

33 gestellt wurde, zeigt eine bessere Weichheit, eine höhere Schlagfestigkeit und gute Leit-33 shows better softness, higher impact resistance and good conductivity

34 fähigkeitseigenschaften und ist insbesondere für die Verwendung bei Fechtjacken an-34 properties and is particularly suitable for use in fencing jackets.

35 wendbar.35 reversible.

N:\AN\98478.DOC 22. Juli 1998N:\AN\98478.DOC 22 July 1998

Claims (1)

Patentanwälte Tergau & Pohl, Nürnberg .* *.,J ; · · &iacgr;#..# Seite -|Patent attorneys Tergau & Pohl, Nuremberg .* *.,J ; · · &iacgr;# .. # Page -| &igr; 98478-10/24&igr; 98478-10/24 2 22. Juli 19982 22 July 1998 3 Ansprüche3 Claims 5 1. Garnstruktur mit leitfähigen Eigenschaften, enthaltend einen Strang aus nichtlei-5 1. Yarn structure with conductive properties, containing a strand of non-conductive 6 tendem Garn, das mit leitfähigem Material umwickelt ist, dadurch gekennzeichnet,6 tendem yarn which is wrapped with conductive material, characterized in 7 daß zwei Fäden (3) aus leitfähigem Material kreuzweise um den Strang aus nichta leitendem Garn (1) gewickelt sind.7 that two threads (3) of conductive material are wound crosswise around the strand of non-conductive yarn (1). 10 2. Garnstruktur nach Anspruch 1, dadurch gekennzeichnet, daß die Fäden (3) aus10 2. Yarn structure according to claim 1, characterized in that the threads (3) consist of 11 leitfähigem Material aus rostfreiem Stahl bestehen.11 conductive material made of stainless steel. 13 3. Gamstruktur nach einem der Ansprüche 1 oder 2, dadurch gekennzeichnet, daß13 3. Yarn structure according to one of claims 1 or 2, characterized in that 14 die Wickeldichte der rostfreien Stahlfäden (3) um das nichtleitende Garn (1) von is 100 bis 500 Umwicklungen pro Meter reicht.14 the winding density of the stainless steel threads (3) around the non-conductive yarn (1) ranges from 100 to 500 windings per meter. &igr;? 4. Garnstruktur nach einem der vorhergehenden Ansprüche, dadurch gekennzeich-18 net, daß der Durchmesser der rostfreien Stahlfäden (3) zwischen 0,06 cm und&igr;? 4. Yarn structure according to one of the preceding claims, characterized in that the diameter of the stainless steel threads (3) is between 0.06 cm and is 0,12 cm liegt.is 0.12 cm. 21 5. Garnstruktur nach einem der vorhergehenden Ansprüche, dadurch gekennzeich-21 5. Yarn structure according to one of the preceding claims, characterized 22 net, daß die Garn- oder Feinheitsnummer des nichtleitenden Garnes (1) zwischen22 net that the yarn or fineness number of the non-conductive yarn (1) is between 23 500 und 3000 Denier liegt.23,500 to 3,000 denier. 25 6. Garnstruktur nach einem der vorhergehenden Ansprüche, dadurch gekennzeich-25 6. Yarn structure according to one of the preceding claims, characterized 26 net, daß die Garn- oder Feinheitsnummer des leitfähigen Garns mehr als 100026 net that the yarn or count of the conductive yarn is more than 1000 27 Denier beträgt.27 denier. 29 7. Garnstruktur mit leitfähigen Eigenschaften, enthaltend einen Strang aus nichtlei-29 7. Yarn structure with conductive properties, comprising a strand of non-conductive 30 tendem Garn, das kreuzweise mit zwei rostfreien Stahlfäden umwickelt ist, um30 tensile yarn, which is cross-wound with two stainless steel threads to 31 verflochtene leitfähige Garnstränge zu bilden, die zu einem leitenden Gewebe31 interwoven conductive yarn strands to form a conductive fabric 32 verwoben werden können, dadurch gekennzeichnet, daß die Wickeldichte von32 can be woven, characterized in that the winding density of 33 rostfreien Stahlfäden (3) zwischen 100 und 500 Wicklungen pro Meter ist und der33 stainless steel threads (3) between 100 and 500 windings per meter and the 34 Durchmesser von rostfreien Stahlfäden (3) von 0,06 bis 0,12 Zentimeter reicht und34 diameters of stainless steel threads (3) ranging from 0.06 to 0.12 centimetres and 35 die Garn- oder Feinheitsnummer des nichtleitenden Garnes (1) zwischen 500 und35 the yarn or count number of the non-conductive yarn (1) is between 500 and N:\AN\98478.DOC 22. Juli 1998N:\AN\98478.DOC 22 July 1998 Patentanwälte Tergau & Pohl, Nürnberg .* *, , J · · · &iacgr;*.«* SeitePatent Attorneys Tergau & Pohl, Nuremberg .* *, , J · · · &iacgr;*.«* Page &igr; 3000 Denier liegt, wobei Gewebe, die aus solchen rostfreien Stahlfäden (3) gefer-&igr; 3000 denier, whereby fabrics made from such stainless steel threads (3) 2 tigt sind, einen elektrischen Oberflächenwiderstand von unter 5 Ohm haben und2 have an electrical surface resistance of less than 5 ohms and 3 die Garn- oder Feinheitsnummer des verflochtenen leitfähigen Garns über 10003 the yarn or fineness number of the interwoven conductive yarn is over 1000 4 Denier liegt.4 denier. e 8. Leitfähiges Gewebe, dadurch gekennzeichnet, daß das leitfähige Garn nach ei-e 8. Conductive fabric, characterized in that the conductive yarn is 7 nem der Ansprüche 1 bis 7 zu einem leitfähigen Gewebe verwoben ist.7 nem of claims 1 to 7 is woven into a conductive fabric. s 9. Leitfähiges Gewebe nach Anspruch 8, dadurch gekennzeichnet, daß der elektri-s 9. Conductive fabric according to claim 8, characterized in that the electrical io sehe Oberflächenwiderstand des Gewebes unter 5 Ohm liegt.The surface resistance of the tissue is below 5 ohms. 12 10. Vorrichtung zur Herstellung einer Garnstruktur mit leitfähigen Eigenschaften, da-12 10. Device for producing a yarn structure with conductive properties, 13 durch gekennzeichnet, daß Führungsräder und wenigstens eine leere Spindel (4)13 characterized in that guide wheels and at least one empty spindle (4) 14 derart angeordnet sind und betrieben werden, so daß ein Strang nichtleitenden14 are arranged and operated in such a way that a strand of non-conductive 15 Garnes (1) durch die Führungsräder der wenigstens einen leeren Spindel (4) zu-15 yarn (1) through the guide wheels of the at least one empty spindle (4) 16 geführt wird, die während dieses Vorgangs in eine erste Richtung rotiert, wobei16, which rotates in a first direction during this process, whereby 17 sich am Austritt ein rostfreier Stahlfaden (3) um den Strang des nichtleitenden17 a stainless steel thread (3) is wound around the strand of the non-conductive is Garnes (1) wickelt, um einen halbfertigen Strang des leitfähigen Garnfadens her-is yarn (1) to produce a semi-finished strand of the conductive yarn thread. 19 zustellen, und so daß dieser halbfertige Strang anschließend erneut durch Füh-19, and so that this half-finished strand is then again guided through 20 rungsräder derselben wenigstens einen oder einer weiteren zweiten leeren Spin-20 rotation wheels of the same at least one or another second empty spinning 21 del (4) zugeführt wird, die während dieses Vorgangs in einer der ersten Richtung21 del (4) which during this process is directed in one of the first directions 22 entgegengesetzten Richtung rotiert, wobei sich ein weiterer rostfreier Stahlfaden22 rotates in the opposite direction, with another stainless steel thread 23 (3) so um den halbfertigen Strang wickelt, daß sich die rostfreien Stahlfäden (3),23 (3) is wound around the half-finished strand in such a way that the stainless steel threads (3), 24 die sich um den Strang des nichtleitenden Garnes (1) winden, überkreuzen.24 which wind around the strand of non-conductive yarn (1) and cross each other. N:\AN\98478.DOC 22. Juli 1998N:\AN\98478.DOC 22 July 1998
DE29813125U 1998-07-23 1998-07-23 Conductive yarn Expired - Lifetime DE29813125U1 (en)