DE2953478C2 - Process for the production of a composite material with a plastic substrate and a synthetic resin lacquer coating applied thereon - Google Patents
Process for the production of a composite material with a plastic substrate and a synthetic resin lacquer coating applied thereonInfo
- Publication number
- DE2953478C2 DE2953478C2 DE2953478A DE2953478A DE2953478C2 DE 2953478 C2 DE2953478 C2 DE 2953478C2 DE 2953478 A DE2953478 A DE 2953478A DE 2953478 A DE2953478 A DE 2953478A DE 2953478 C2 DE2953478 C2 DE 2953478C2
- Authority
- DE
- Germany
- Prior art keywords
- polyethylene
- coating
- composite material
- substrate
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Die Erfindung betrifft ein Verfahren zur Herstellung eines Verbundmaterials mit einem Kunststoffsubstrat und einem aus einer wäßrigen Polyurethanharzdispersion, die einen anionischen oder nicht-ionischen Emulgator und Polyethylen enthält, aufgebrachten Kunstharzlacküberzug.The invention relates to a method for producing a composite material with a plastic substrate and one of an aqueous polyurethane resin dispersion containing an anionic or nonionic emulsifier and polyethylene contains, applied synthetic resin varnish coating.
Aus der FR-PS 14 96 584 ist bekannt, eine derartige Polyurethanharzdispersion auf ein Substrat aus Polyethy- !en aufzubringen. Der anionische oder nicht-ionische Emulgator kann der wäßrigen Lösung des Polyurethanhar-From FR-PS 14 96 584 is known, such a polyurethane resin dispersion on a substrate made of polyethylene ! en to raise. The anionic or non-ionic emulsifier can be the aqueous solution of the polyurethane resin
zes zur Herabsetzung der Oberflächenspannung zugesetzt werden. Welchen Effekt das Polyethylen bringt, ist nicht angegeben. Nach dem Trocknen der Polyurethanharzdispersion kann der erhaltene Überzug vom Substrat als weiche transparente Folie abgezogen werden. Der Überzug ist also nicht haftfest und somit auch nicht |zes can be added to reduce surface tension. What effect the polyethylene brings is not specified. After the polyurethane resin dispersion has dried, the coating obtained can be removed from the substrate can be peeled off as a soft transparent film. The coating is therefore not adherent and therefore also not |
abriebfest. Der Überzug ist daher nicht geeignet, einem mit Verzierung oder Beschriftung versehenen Gegen- i abrasion resistant. The coating is therefore not suitable for a counter- i
stand aus hartem bis halbhartem Schaumkunststoff, der im Gebrauch starken Abriebkräften ausgesetzt ist.was made of hard to semi-hard foam plastic, which is exposed to strong abrasive forces during use.
Schutz zu verleihen.To give protection.
Derartige Gegenstände sind z. B. Wegwerf-Becher, Schalen und mit Aufschrift versehene Schildchen aus geschäumten thermoplastischen Harzen, wie Polystyrol. Sie finden wegen ihrer Wärmebeständigkeit gegenüber heißen und kalten Getränken, ihres günstigen Verhältnisses von Festigkeil zu Gewicht und ihrer Wirtschaftlich- |Such items are z. B. Disposable cups, bowls and labeled labels foamed thermoplastic resins such as polystyrene. You will find opposed to because of their heat resistance hot and cold drinks, their favorable ratio of solid wedge to weight and their economic |
keil verbreitet Einsatz. Schaumkunststoffe werden auch in großem Umfang in der Verpackungsindustric zur f wedge widespread use. Foam plastics are also used on a large scale in the packaging industry for f
Etikettierung von Behältern, wie Glasflaschen und Töpfe, verwendet, wodurch Trennwände beim Transport |Labeling of containers, such as glass bottles and pots, used, creating partitions during transport |
wegfallen können.can be omitted.
Schaumkunststoffe, die zu Bechern, Schalen und mit Beschriftung versehenen Schildchen verarbeitet werden, sind meist relativ hart oder halbhart und neigen daher zum Abrieb, wenn sie einem nur mäßigen Gleitkontakt ausgesetzt werden. Bei den meisten der eben genannten Einsatzzwecke sind die Außenflächen der GegenständeFoam plastics that are processed into cups, bowls and labels with labels, are usually relatively hard or semi-hard and therefore tend to wear off if they have only moderate sliding contact get abandoned. For most of the purposes just mentioned, the outer surfaces of the objects are
'S mit Reklamebildern oder informativen Mitteilungen verziert oder bedruckt. Die Außenflächen müssen aber sowohl Stoß- wie Abriebkräften ohne Beschädigung standhalten. Wenn das Material als beschriftete Schildchen verwendet wird oder als Trennwände zwischen Behältern dient, wird bei langem Transport die beschriftete Außenseite starker Beschädigung durch Schurren und Abrieb ausgesetzt, was ihrem Verkaufswert abträglich ist.It's decorated or printed with advertising images or informative messages. But the outside areas have to withstand both impact and abrasion forces without damage. If the material as a labeled label is used or serves as partitions between containers, the labeled The outside is exposed to severe damage from chipping and abrasion, which is detrimental to its sales value.
Ein die Außenseite der Gegenstände schützender Überzug wird im allgemeinen nicht aufgebracht. Die TypenA coating protecting the outside of the articles is generally not applied. The guys
von klaren transparenten Überzügen, die es gibt, sind entweder zu teuer oder für ausgedehnte industrielle rof the clear transparent coatings that exist are either too expensive or for extensive industrial r
Verwendung nicht geeignet. Die im Handel erhältlichen Überzugsmaterialien sind allgemein solche auf Basis fUsage not suitable. The commercially available coating materials are generally those based on f
organischer Lösungsmittel, die beim Trocknen die Umwelt belasten. Außerdem bieten sie den Behältern keinen ausreichenden Schutz gegen Abrieb bei langem Transport.organic solvents that pollute the environment when drying. In addition, they do not offer the containers any adequate protection against abrasion during long transport.
Der Erfindung liegt daher die Aufgabe zugrunde, ein Verfahren zur Herstellung eines Verbundmalcrials anzugeben, bei welchem auf einem harten bis halbharten Schaumkunststoffsubstrat, das auf wenigstens einigen Oberflächenbereichen verziert oder bedruckt ist, ein Überzug aufgebracht wird, der fest am Substrat haftci. ihm hohen Abrieb und verbesserte Naß- und Trocken-Kratzfestigkeit verleiht. Der Überzug soll in Wasser unlöslich, geschmack- und geruchsfrei und nicht giftig sein, so daß das Verbundmaterial in Form von Trinkbechern und Schildchen auf den Außenflächen von Nahrungsmittel- und Getränkebehältern gefahrlos angewendet werdenThe invention is therefore based on the object of a method for producing a composite painting indicate which on a hard to semi-hard foam plastic substrate that on at least some Surface areas is decorated or printed, a coating is applied, which is firmly adhered to the substrate. him imparts high abrasion and improved wet and dry scratch resistance. The coating should be insoluble in water, be tasteless and odorless and non-toxic, so that the composite material in the form of drinking cups and Labels are safe to use on the exterior of food and beverage containers
Die Aufgabe wird durch ein Verfahren der eingangs angegebenen Gattung gelöst, das dadurch gekennzeichnet ist, daß auf ein Substrat aus einem harten bis halbharlen Schaumkunststoff mit [Mindestens einer Schicht Verzierungs- und/oder Druckfarbe auf mindestens einigen Oberflächenbereichen der Überzug aus einem wäßrigen Gemisch, das Polyurethanharz und mit einem nicht ionischen oder anionischen Emulgator cmulgicricsThe object is achieved by a method of the type specified at the beginning, which is characterized in that is that on a substrate made of a hard to semi-hard foam plastic with [At least one layer Decorative and / or printing ink on at least some surface areas of the coating of an aqueous Mixture, the polyurethane resin and with a non-ionic or anionic emulsifier cmulgicrics
H5 Polyethylen in einem Feststoffverhältnis von I :9 bis 1 :1 iuifgcbracht wird, wobei das wäßrige Gemisch bis zu
30Gcw.-% eines niedermolekularen Alkohols enthalten kann und das fertige Produkt dehnbar ist.
Bevorzugte Ausfühfungsformen sind in den Utueransprüchcn angegeben.
Bei dem erfindungsgemäßen Verfahren wird ein Substrat aus hartem oder halbhartem Schaumkunststoff,H5 is polyethylene in a solids ratio of 1: 9 to 1: 1 iuifgcbracht, wherein the aqueous mixture can contain up to 30 wt .-% of a low molecular weight alcohol and the finished product is stretchable.
Preferred embodiments are specified in the claims.
In the method according to the invention, a substrate made of hard or semi-hard foam plastic,
insbesondere Schaumpolystyrol oderSchaumpolyethylen, verwendet.in particular expanded polystyrene or expanded polyethylene is used.
Auf das Substrat wird der Überzug aus einem wäßrigen Gemisch aufgebracht, das Polyurethanharz und Poiyethylenharz enthält Das Poiyethylenharz ist mit einem nicht-ionischen oder anionischen Emulgator emulj giert. Ein besonders geeignetes Polyurethanharz ist ein aliphatisches, in Wasser dispergiertes Harz, und dasThe coating is applied to the substrate from an aqueous mixture, the polyurethane resin and Polyethylene resin contains The polyethylene resin is emulsified with a non-ionic or anionic emulsifier greed. A particularly suitable polyurethane resin is an aliphatic resin dispersed in water, and that
Polyethylenharz ein nicht-ionisch in Wasser emulgiertes Harz niedrigen bis mittleren Molekulargewichts. Das Polyurethanharz und das Polyethylenharz liegen in dem wäßrigen Gemisch in einem Feststoffverhältnis im Bereich von 1:9 bis 1 : !,insbesondere 1 :1 vor. Als nicht-ionisches Emulgiermittel für das Polyelhylcnharz ist Nonylphenoxi-poly-(elhylenoxi)-ethanol und als anionisches Emulgiermittel ist Morpholinoleat, Kaliumolcal oder Natriumoleal besonders geeignet. Das wäßrige Gemisch, das auf das Substrat aufgebracht wird, hat vorzugsweise eine Viskosität im Bereich von etwa 18 bis 35 Sekunden, gemessen im Zahn-Becher Nr. 2 bei 183 bis 29,4° CPolyethylene resin is a resin of low to medium molecular weight non-ionically emulsified in water. That The polyurethane resin and the polyethylene resin are in a solids ratio in the aqueous mixture Range from 1: 9 to 1:!, Especially 1: 1. As a non-ionic emulsifier for the polyethylene resin Nonylphenoxy-poly- (ethyleneoxy) -ethanol and as an anionic emulsifier is morpholine oleate, potassium olcal or sodium oleal are particularly suitable. The aqueous mixture that is applied to the substrate has preferably a viscosity in the range of about 18 to 35 seconds as measured in Zahn cup # 2 at 183 up to 29.4 ° C
Es werden nun die Komponenten des wäßrigen Gemisches, aus dem erfindungsgemäß ein Überzug auf Substrate aus hartem bis halbhartem Schaumkunststoff mit mindestens einer Schichi Verzierungs- und/oder Druckfarbe auf mindestens einigen Oberflächenbereichen aufg°bracht wird, näher beschrieben.The components of the aqueous mixture from which a coating according to the invention is now applied Substrates made of hard to semi-hard foam plastic with at least one layer of decoration and / or Printing ink is applied to at least some surface areas, described in more detail.
Ein besonders geeignetes Polyethylen ist ein oxidiertes Polyethylen-Hornopolymerisat, insbesondere ein Handelsprodukt mit einem Erweichungspunkt von 1400C (ASTM E-28), einer Härte (dmm) von unter 0,5 (ASTM D-5), einer Dichte (g/cm3) von 038 (ASTM D-1505), einer Brookfield-Viskosität von 30.000 mPa · s bei 149°C und einer Säurezahl von 16 mg KOH/g. Dieses Homopolymerisat ist in USA für die Verwendung in Verbindung mit Verpackungsmaterialien zugelassen.A particularly useful polyethylene is an oxidized polyethylene Hornopolymerisat, in particular a commercial product having a softening point of 140 0 C (ASTM E-28), a hardness (dmm) of less than 0.5 (ASTM D-5) a density (g / cm 3 ) of 038 (ASTM D-1505), a Brookfield viscosity of 30,000 mPas at 149 ° C. and an acid number of 16 mg KOH / g. This homopolymer is approved in the USA for use in connection with packaging materials.
Die GrundforfeKlIation einer nicht-ionischen Polyethyienemulsion mit dem vorstehend beschriebenen oxidierten Polyethylen-Homopoiymerisat, nachstehend mit Polyethylen bezeichnet, ist folgende:The basic form of a nonionic polyethylene emulsion with the oxidized one described above Polyethylene homopolymer, hereinafter referred to as polyethylene, is the following:
Gew.-TeileParts by weight
Polyethylen 40,0Polyethylene 40.0
Alkylphenoxi-polyoxiethylen-ethanol 10,0Alkylphenoxy-polyoxyethylene-ethanol 10.0
KOH 90% Flocken 1.0KOH 90% flakes 1.0
Na2S2O, 0,4Na 2 S 2 O, 0.4
Wasser bis zu 30% Feststoffgehalt 120.0Water up to 30% solids content 120.0
Ein besonders geeignetes Polyurethanharz ist ein Handelsprodukt, das ist eine wäßrige kolloidale Dispersion eines aliphatischen Urethans, mit einem Feststoffgehalt von 34 ± 1, pH von 7,5 bis 8,5, einer Viskosität von 400 bis 800 mPa · s und einer Dichte von r,05Sg/cm3; es hat ausgezeichnete mechanische Stabilität und übersteht 5 Zyklen im Gefrier-Tau-Stabiliiämest. Dieses Produkt hat die nachstehend aufgeführten Eigenschaften:A particularly suitable polyurethane resin is a commercial product, that is an aqueous colloidal dispersion of an aliphatic urethane, with a solids content of 34 ± 1, pH from 7.5 to 8.5, a viscosity from 400 to 800 mPa · s and a density of r .05Sg / cm 3 ; it has excellent mechanical stability and withstands 5 freeze-thaw stabilization cycles. This product has the following characteristics:
Härtungsschema:Curing scheme:
Lufttrocknung 6 StundenAir drying 6 hours
Beschleunigungstrocknung 10 Min. bei 93° CAccelerated drying for 10 minutes at 93 ° C
Reißfestigkeit, gehärtet 10 Min. bei 93° C 35 M PaTear strength, cured 10 min. At 93 ° C 35 M Pa
Taber-Abrieb 28 mg VerlustTaber abrasion 28 mg loss
Chemikalienbeständigkeit ausgezeichnetExcellent chemical resistance
Ein geeigneter nicht-ionischer Emulgator ist ein polyoxiethyliertes Nonylphenol, genauer gesagt ein Nonylphenoxipoly-(ethylenoxi)-ethanol. Solch ein Tensid ist wegen seines nicht-ionischen Charakters sowohl mit anionischen als auch mit kationischen Mitteln verwendbar.A suitable nonionic emulsifier is a polyoxyethylated nonylphenol, more precisely a nonylphenoxy poly (ethyleneoxy) ethanol. Such a surfactant is both anionic because of its non-ionic character as well as with cationic agents.
Verschiedene andere nicht-ionische Emulgatoren können verwendet werden. Unter den anionischen Emulgatoren.die verwendet werden können, sind Morpholinoleat, Kaliumoleat und Natriumoleat zu nennen.Various other nonionic emulsifiers can be used. Among the anionic emulsifiers. The Morpholine oleate, potassium oleate and sodium oleate may be used.
Das wäßrige Gemisch enthält zusätzlich zu dem Polyurethanharz und dem emulgierten Polyethylen einen niedermolekularen Alkohol, weil er drei Vorteile bringt. Der Alkohol ist mit dem aus dem wäßrigen Gemisch Austretenden in allen Verhältnissen gut verträglich. Er gib: dem Gemisch hohe Lagerstabilität, verleiht ihm DruckbarkcJt oder Gleitfähigkeit, so daß es mittels Gummidruck aufgebracht werden kann, und setzt seine Oberflächenspannung und den Reibungskoeffizienten herab.The aqueous mixture contains, in addition to the polyurethane resin and the emulsified polyethylene, a low molecular weight alcohol because it has three advantages. The alcohol is the same as that from the aqueous mixture Leaving people well tolerated in all circumstances. He gives: the mixture high storage stability, gives it Printability or slidability, so that it can be applied by means of rubber pressure, and continues its Surface tension and the coefficient of friction.
Die Oberflächenspannung des Gemisches, aus dem der Überzug aufgebracht wird, kann ferner durch Zugabe kleiner Mengen mit Wasser mischbarer Silikonöle gesenkt werden. Silikonöle verbessern auch die Gleitfähigkeit. In dem weiter unten gebrachten Beispiel werden zwei Handelsprodukte verwendet, die die nachstehenden Eigenschaften haben.The surface tension of the mixture from which the coating is applied can also be increased by adding small amounts of water-miscible silicone oils can be reduced. Silicone oils also improve lubricity. In the example given below, two commercial products are used, the following Have properties.
SilikonölSilicone oil
1 II1 II
'Form , Emulsion Flüssigkeit'' Form, emulsion liquid
aktive Bestandteile, Gew.-% 35 100active ingredients, wt% 35 100
spez. Gew., g/cm3 0,99 1,01spec. Wt., G / cm 3 0.99 1.01
Oberflächenspannung bei 25°C, N/cm — 23,6 · IO-5 Surface tension at 25 ° C, N / cm - 23.6 · IO- 5
Wenn gewünscht, kann·, wie in der einschlägigen Technik bekannt, ein UV-Indikator zugegeben werden, so daß festgestellt werden kann, wo das Gemisch aufgebracht z. B. aufgedruckt worden ist. Dies ibt besonders wichtig, wenn der Überzug farblos und transparent ist und im Dünnfilmauftrag aufgebracht wurde.If desired, as is known in the art, a UV indicator can be added, so that can be determined where the mixture is applied e.g. B. has been printed. This is special important if the coating is colorless and transparent and has been applied using a thin film application.
Die Bereitung eines wäßrigen Gemisches, das in dem Verfahren nach der Erfindung zur Herstellung eines Verbundmaterials auf ein Substrat aus Schaumkunststoff aufgebracht werden kann, wird nun an einem Beispiel beschrieben.The preparation of an aqueous mixture, which in the method according to the invention for the preparation of a Composite material can be applied to a substrate made of foam plastic, is now based on an example described.
Zur Herstellung einer Menge von 3,75 Liter, wurden die nachstehend aufgeführten Bestandteile in den angegebenen Mengen eingesetzt und vermischt Polyethylenharz und Polyurethanharz sind die weiter vorn näher beschriebenen Handelsprodukte.To make 3.75 liters, the ingredients listed below were added to the The specified amounts used and mixed polyethylene resin and polyurethane resin are the ones above commercial products described in more detail.
Menge (Gew.)Amount (weight)
1660,00 g1660.00 g
B Poiyurethanharz 1470,00 gB Polyurethane resin 1470.00 g
700,00 g
767,5C/g
7.60 g
0,23 g
Gesamt 3605,- g700.00 g
767.5C / g
7.60 g
0.23 g
Total 3605 g
Nachstehend werden die Feststoffgehalte in Gewichtsprozent der vorstehend angeführten Bestandteile ge-The solids contents in percent by weight of the constituents listed above are given below.
;| bracht:; | brings:
Bestandteile % Feststoffgehalt ArtComponents% solids Art
A 30,0 wäßrige EmulsionA 30.0 aqueous emulsion
B 33,3 wäßrige DispersionB 33.3 aqueous dispersion
E 30,0 wäßrige EmulsionE 30.0 aqueous emulsion
F 100,0 F 100.0
Die Komponenten E und F können beide wahlfrei zur Verbesserung der Gleitfähigkeit und/oder zur Herabsetzung der Oberflächenspannung des Gemisches eingesetzt werden, abhängig von dem Druckverfahren, nach dem es auf das Substrat aufgebracht v/erden soll. Wenn das Gemisch mittels Gummidruck aufgebracht werden soll, sind diese wahlfreien Komponenten wertvolle Zusätze zur Erreichung besserer Ergebnisse, wenn nur vorbestimmte Oberflächenbereiche des Rollenmaterials zu überziehen sind und andere Bereiche ohne Überzug bleiben sollen.Components E and F can both optionally be used to improve lubricity and / or to reduce it the surface tension of the mixture can be used, depending on the printing process to which it is to be applied to the substrate. When the mixture is applied by means of rubber pressure these optional components are valuable additions for achieving better results, if only predetermined surface areas of the roll material are to be coated and other areas without a coating should stay.
Eine geeignete Methode zum Mischen der vorstehend aufgeführten Komponenten durch kontinuierlichesA suitable method of mixing the components listed above by continuous
4Q Rühren t„-steht darin, daß man das Polyurethanharz (B) nimmt und mit dem Wasser (C) vermischt. Diese Mischung wird dann der wäßrigen Polyethylenemulsion (A) . ugegeben, wobei das Rühren ständig fortgesetzt wird. Der niedrigmoiekulare Alkohol, insbesondere Isopropanol (D) wird dann dem Gemisch unter Rühren zugefügt. Es folgt die Zugabe der wahlfreien Silikonöle E und/oder F, wobei weitergerührt wird. Die Komponente E wird in einer Menge von 0.2 Gewichtsprozent, die Komponente F in einer Menge von 0,005 Gcwienlsprozent.bezogcnaufdas Gemisch der Komponenten A bis D zugegeben.Stirring means that you take the polyurethane resin (B) and mix it with the water (C). These Mixture is then the aqueous polyethylene emulsion (A). added, stirring continuously will. The low molecular alcohol, in particular isopropanol (D), is then added to the mixture while stirring added. The optional silicone oils E and / or F are then added while stirring is continued. The component E is in an amount of 0.2 percent by weight, component F in an amount of 0.005 percent by weight, based on the Mixture of components A to D added.
Die Komponente E ist eine SilrLonemulsion, abgestellt auf die Verwendung als Formtrenn- und Gleitmittel. Derartige Silikone sind Dimethylpolysiloxane niedriger Oberflächenspannung und ausgezeichneter Gleitfähigkeit, geeignet zur Verwendung bei der Herstellung von Druckfarben. Sie verleihen der Druckfarbe Gleitfähigkeit und unterstützen den Druckvorgang. Die Komponente E ist eine sehr stabile Emulsion. Die Zugabe derComponent E is a silicone emulsion, designed for use as a mold release agent and lubricant. Such silicones are dimethylpolysiloxanes with low surface tension and excellent lubricity, suitable for use in the manufacture of printing inks. They give the printing ink lubricity and support the printing process. Component E is a very stable emulsion. The addition of the
J0 Komponente E zu eine:n wäßrigen Druckfarbensystem, welches auch mit Wasser verdünnbar ist. verbessert die Fließ- und Verlauf-Eigenschaften der Zusammensetzung.J 0 component E to an: n aqueous printing ink system which can also be thinned with water. improves the flow and leveling properties of the composition.
Das Polyurethan- und das Polyethylen-Harz liegen in dem wäßrigen Gemisch, aus dem der Überzug aufgebracht wird, in einem Feststoffverhältnis im Bereich von 1:9 bis 1:1, vorzugsweise 1 :1 vor. Das Gemisch schließt auch einen niedermolekularen Alkohol als Druckaaditiv in einer Menge von 0 bis 30 Gewichtsprozent,The polyurethane and the polyethylene resin are in the aqueous mixture from which the coating is applied is, in a solids ratio in the range from 1: 9 to 1: 1, preferably 1: 1. The mixture also includes a low molecular weight alcohol as a printing additive in an amount of 0 to 30 percent by weight,
bezogen auf die drei Hauptbestandteile Polyethylen, Polyurethan und Was'pr ein. Isopropanol ist besonders geeignet.based on the three main components polyethylene, polyurethane and Was'pr. Isopropanol is special suitable.
Als Substrate sind besonders bevorzugt geschäumtes Polystyrol, Polyethylen, Polypropylen und Polyurethan, welche in Form endloser Folien einer Picke von z. B. 0,005 bis 0,076 cm hergestellt worden sind. Die Oberfläche der frischgeformten Folien wird gewöhnlich einer Corona-Entladung oder t_iner ähnlichen Behandlung unter-Particularly preferred substrates are foamed polystyrene, polyethylene, polypropylene and polyurethane, which in the form of endless foils a pick of z. B. 0.005 to 0.076 cm have been made. The surface the freshly formed foils are usually subjected to a corona discharge or similar treatment.
w worfen, urn sie polar zu machen. Nachdem die Folie in Form einer Roll? wie gewünscht bedruckt und verziert ist, üblicherweise mit zwei bis vier verschiedenen Farben von Druckfarben, wird das wäßrige Gemisch als dönngr Film auf den vorher bedruckten Flächen aufgebracht, gewöhnlich als Film einer Dicke von 0,00254 bif-0,127 mm. Der erhaltene Überzug ist farblos und gibt dem verzierten Substrat hohen Abriebwiderstand, hohen Glanz und Gleitfähigkeit. Wenn das wäßrige Gemisch auf übliche Druckfarben aufgebracht worden ist, so isi keine w thrown to make them polar. After the slide in the form of a roll? is printed and decorated as desired, usually with two to four different colors of printing inks, the aqueous mixture is applied as a thin green film to the previously printed areas, usually as a film 0.00254 by 0.127 mm thick. The coating obtained is colorless and gives the decorated substrate high abrasion resistance, high gloss and lubricity. If the aqueous mixture has been applied to conventional printing inks, there is none
hr, Nachbehandlung, erforderlich. Wenn es aber auf unver/.ierte oder unbedrucktc Flächen iiufgcbriichl wird, mt:ß das Substrat polar gemacht werden, wie in der einschlägigen Technik bekannt. Das wäßrige Gemisch wird nadi dem Aufbringen erhitvK. um das Wasser vornehmlich durch Verdampfen zu entfernen und zu trocknen. h r, follow-up treatment, required. If, however, it is printed on unprinted or unprinted surfaces, the substrate must be made polar, as is known in the relevant technology. The aqueous mixture is heated after application. to remove and dry the water primarily by evaporation.
Langlransporltcsts mit nach dem erfindungsgemäßen Verfahren hcrgcstciitcn Vcrbundmalcrialien in FormLong transporltcsts with composite paints made according to the method according to the invention in the form
von beschrifteten Schildchen haben gezeigt, daß kein oder nur geringes Abschurren oder Verkratzen der
Substrate eingetreten ist selbst dort, wo sich·Schildchen in direktem Gleitkontakt über lange Zeit ohne Zwischenwände
zwischen den Behältern befanden. Der Überzug verklebt nicht und da er aus einem wäßrigen
Gemisch aufgebaut wird, eignet er sich für viele verschiedene Arten von Druckverfahren.of labeled labels have shown that little or no scraping or scratching of the
Substrate entered even where labels were in direct sliding contact for a long time without partitions between the containers. The coating does not stick and since it consists of an aqueous
If the mixture is built up, it is suitable for many different types of printing processes.
Tests haben gezeigt, daß das erfindungsgemäß hergestellte Verbundmaterial verbesserte Abschurrfestigkeit 5
hat, was den Transport von mit beschrifteten Schildchen versehenen Flaschen und Topfen ohne Zwischenwände
oder Polster gestattet. Der Überzug zeigte immer hohen Glanz und ausgezeichnete Abriebfestigkeit in Karton-Vibrationstests
und Reibtests mit gefüllten und verschlossenen Behältern. Die Gleitfähigkeit wurde mittels
Gleitwinkel- und Reibungskoeffizienten-Tests bestimmt, welche zeigten, daß die gefüllten Behälter Oberflächen
mit voll befriedigender Gleitfähigkeit haben. Es ist auch keine Änderung der Farbdichte, der Druck- oder io
Verzierungsfarben durch den Überzug festzustellen gewesen.Tests have shown that the composite material produced according to the invention has improved scraping resistance 5, which means that bottles and pots provided with labeled labels can be transported without partitions
or upholstery permitted. The coating always showed high gloss and excellent abrasion resistance in cardboard vibration tests and rub tests with filled and sealed containers. The lubricity was measured by means of
Slip angle and coefficient of friction tests determined which showed that the filled container had surfaces
with fully satisfactory sliding properties. There was also no change in the color density, printing or decorative colors through the coating.
Claims (4)