DE2919445A1 - Resin concrete mouldings prodn. - using mould release agent contg. reactant for the resin

Info

Publication number: DE2919445A1
Application number: DE19792919445
Authority: DE
Inventors: Hans Dr Haeberle
Original assignee: Wienerberger Baustoffindustrie AG
Current assignee: Wienerberger Baustoffindustrie AG
Priority date: 1978-05-22
Filing date: 1979-05-15
Publication date: 1979-12-06
Also published as: AT375907B; ATA371478A

Abstract

Resin concrete mouldings, e.g. of polyester resin with mineral additives, are produced in shell moulds coated with release agent e.g. oil, wax or film, contg. a substance which reacts chemically with the resin binder. Pref. the additive in the release agent participates in polymerisation of the resin, its reaction time with the resin being less than that required for hardening. Pref. it is a tert. amine, organo-metallic cpd. and/or organic peroxide, in amt. of >=1 wt.% esp. 3-15%. Adhesion to the mould is prevented, and the mouldings are easily removed without damage, well before the time required for complete hardening, giving increased output from the moulds.

Description

P a t e n t a n m e l d u n gP a t e n t a n m e l d u n g

"Verfahren zur Herstellung von Formkörpern sowie Trennmittel zur Verwendung bei diesem Verfahren" Die Erfindung betrifft zunächst ein Verfahren zur Herstellung von aus Kunstharzbeton bestehenden Formkörpern in Schalungsformen unter Verwendung eines auf die Arbeits= flächen dieser Schalungsformen aufgebrachten Trennmittels, z.B. eines Öles, Wachses, einer Folie, eines Trennpapiers, einer Wachslösung, Wachsemulsjon, eines Fettes, Kunststoffes, od dgl. Beschichtung."Process for the production of moldings and release agents for use in this procedure " The invention relates first of all to a method for the production of molded bodies made of synthetic resin concrete in shuttering molds using one applied to the work surfaces of these formwork forms Release agent, e.g. an oil, wax, a film, a release paper, a wax solution, Wax emulsion, a grease, plastic, or the like. Coating.

Bekanntlich hat sich Kunstharzbeton, d.h. ein Gemenge. As is well known, synthetic resin concrete, i.e. a mixture.

aus meist mineralischen Zuschlagstoffen und einem Kunstharz, z'.B. einem Polyesterharz, für die Herstellung verschiedener Produkte, insbesondere für Bauelemente der Abwassertechnik, außerordentlicht gut bewahrt, weil er sehr dicht und gegen chemisch aggressive Bestandteile-solcher Abrässer weitgehend t X unempfindlich ist,-hohe strömungsgünstige Oberflächenglätte und kostengünstige Produktionsmöglichkeit ergibt.mostly made of mineral aggregates and a synthetic resin, e.g. a polyester resin, for the manufacture of various products, especially for Components of sewage technology, extremely well preserved because it is very tight and largely t X insensitive to chemically aggressive components - such abrasives is, -high aerodynamic surface smoothness and inexpensive production option results.

Eine gewisse Problematik bei der Herstellung solcher, oft vergleichsweise zu Zementbetonerzeugnissen besonders dünn-'. A certain problem in the production of such, often comparatively particularly thin to cement-concrete products.

wandig und filigran gestalteter Produkte ergibt sich beim Entschalen, also beim Ablösen der Formkörper von der Oberfläche einer Schalungsform, und zwar insbesondere dann, wenn die Formkörper nach einem für die mit Trennmittel versehene Ober= fläche abrasiven Verfahren gefertigt werden.walled and filigree designed products result from demoulding, so when detaching the molded body from the surface of a formwork, namely especially when the molded body is after a release agent for the Surface abrasive processes are manufactured.

Nach dem heutigen Stand der Technik ist mit den üblichen Trennmittelsystemen, wie Schalolen, Wachsemulsionen, Trennfolien, Ttennpápieren, Wachslösungen und emulsionen, Fetten, Kunst~ stofEbeschichtungen etc. ein Lösen des Formkdrpers von den Schalungswänden erst nach dessen Härtung zerstörungsfrei gewährleistet. According to the current state of the art, the usual release agent systems, such as formulas, wax emulsions, separating foils, adhesive paper, wax solutions and emulsions, Greases, plastic coatings, etc. a detachment of the molded body from the formwork walls only guaranteed non-destructively after it has hardened.

Begreiflicherweise ist es aus wirtschaftlichen Erwägungen wünschenswert., die Entschalungder herzustellenden Formkörper möglichst frühzeitig,vor der vollståndigen Durchhärtung, also nach möglichst kurzer Verweilzeit des Formkörpers in der Form durchzuführen, um diese Schalungsform ehestmöglich für einen neuen Fertigungsvorgang verwenden zu können. It is understandably desirable for economic reasons., the moldings to be produced are removed as early as possible, before they are complete Complete hardening, i.e. after the molded body has stayed in the mold for as short a time as possible to carry out this formwork form as soon as possible for a new production process to be able to use.

Dem steht jedoch die Klebeneigung des Kunstharz-Binde mittels (Polyesterharz, Epoxydharz, Metacrylatharz, Polyurethan usw.- bzw. Kombinationen derartiger Bindemittel miteinander) an den Oberflächen der Schalungsform (Karton, Holz, Kunststoff, Metall od.dgl.) entgegen. Um diese Haftung des Formkörpers an der Schalungsoberfläche zu überwinden, bedarf es einer. However, this is offset by the tendency of the synthetic resin bandage to stick (polyester resin, Epoxy resin, methacrylate resin, polyurethane etc. or combinations of such binders with each other) on the surfaces of the formwork form (cardboard, wood, plastic, metal or the like.) contrary. To this adhesion of the molding to the formwork surface overcome, it takes one.

erheblichen mechanischen Beanspruchung des Formkörpers, der Ser jedoch-in einem noch nicht voll ausgehärteten Zustand festigkeitsmäßig nicht gewachsen ist und infolgedessen er durch den Vorgang der Entformung (Entschalung). eine Zerstörung erleidet.considerable mechanical stress on the molded body, but the Ser-in is not able to withstand a not yet fully cured state in terms of strength and, as a result, it through the process of demolding (demoulding). a destruction suffers.

Ziel der vorliegenden Erfindung ist die Behebung dieser oben geschilderten Schwierigkeiten und gemäß dem wesentlichsten Erfindungsmerkmal wird dieses Ziel dadurch erreicht, daß bei einem Verfahren der eingangs bezeichneten Gattung dem Trenn= mittel eine mit dem Kunstharzbinder der Formkörpermasse chemisch reagierende sowie durch diese Reaktion dessen Klebe kraft zumindest verringernde Substanz hinzugefügt und mit der Formkörperoberfläche in Kontakt gebracht wird. The aim of the present invention is to remedy these described above Difficulties and according to the most essential feature of the invention, this goal becomes achieved by the fact that in a method of the type mentioned Release agent one that reacts chemically with the synthetic resin binder of the molding compound as well as through this reaction its adhesive force at least reducing substance is added and is brought into contact with the molded body surface.

Dank dieser'Maßnahme wird ein Kleben der Formkörpermasse an den Arbeitsflächen der Schalung zuverlässig'verhinderi und der Formkörper läßt sich leicht und beschädigungsfrei von den Arbeitsflächen abheben bzw. aus.der Schalungsform entfernen, und zwar sa.-hon.wesentlich vor seiner endgültigen Erhärtung, so daß dadurch die Herstellungsleistung erheblich erhöht werden kann. Thanks to this measure, the molding compound will stick to the work surfaces the formwork reliably'verhinderi and the molded body can be easily and damage-free of the Lift off work surfaces or remove them from the formwork, and that sa.-hon. substantially before its final hardening, so that the Manufacturing output can be increased significantly.

Nach einer bevorzugten Ausführungsform des erfindungs= gemäßen Verfahrens wird eine Substanz verwendet, die reagierend in die Polymerisation des Kunstharzbinders eingreift, d;h. According to a preferred embodiment of the process according to the invention a substance is used that is reactive in the polymerization of the synthetic resin binder intervenes, i.e.

die Reaktionsgeschwindigkeit der Polymerisation wesentlich zu steigern vermag.to increase the reaction rate of the polymerization significantly able.

Um den Formkörper schon vor dessen vollständiger Erhärtung aus der Schalungsform entfernen zu können, soll die Dauer'der Reaktion der Substanz mit dem' Kunstharzbinder kürzer als die Abbindezeit (Härtungsdauer) der Formkörpermasse sein. To the molded body before it has completely hardened from the To be able to remove formwork form, the duration of the reaction of the substance should be the 'synthetic resin binder is shorter than the setting time (curing time) of the molding compound be.

Die Erfindung ist hinsichtlich der Wahl der Substanz in mannigfachen Varianten ausführbar. So kann man beispielsweise zur Erzielung des von'der Erfindung angestrebten Effektes dem Trennmittel einen -Anteil an tertiären Aminen und/oder einen :--Anteil metallorganischer Verbindungen bzw. organischer Peroxyde hinzufügen. The invention is manifold in terms of the choice of substance Variants can be implemented. So you can, for example, to achieve the von'der invention Desired effect of the release agent a proportion of tertiary amines and / or one: - Add a proportion of organometallic compounds or organic peroxides.

Üblicherweise wird die Substanz einem flüssigen Trenn= mittel in gelöster, emulgierter oder dispergierter Form hin= zugefügt, grundsätzlich beträgt der Feststoffanteil des Trenn= mittels zwischen-5 und 20 Gew-% vorzugsweise- eines als Trenn= mittel benutzten Wachses. Usually the substance is in a liquid release agent dissolved, emulsified or dispersed form = added, basically amounts to the solids content of the separating means between -5 and 20% by weight, preferably one wax used as a separating agent.

Die Ereindung ist aber auchauf feste Trennmittel, z.B. The connection is also based on solid release agents, e.g.

auf-Trennfolien, Trennpapiere 6., anwendbar; in diesem Fall kann die Substanz als Beschichtung eines solchen Trenn= mittels mit der Formkörperoberfläche in Kontakt gebracht werden.on release films, release papers 6., applicable; in this case the Substance as a coating of such a separating means with the surface of the molded body be brought into contact.

Im Zusammenhang mit dem oben bezeìchneten Verfahren erstreckt sich die Erfindung auch auf ein zur Verwendung bei diesem Verfahren geeignetes Trennmittel, welches als Zusatz einen Anteil--jener- Substanz enthält, die mit einem Kunstharzbindemittel dessen Kiebekraft zumindest verringernd reagiert, hiezu beispielsweise Anteil tertiärer Amine, metallorganischer Verbindungen bzw. organischer. Peroxyde enthält. In connection with the above-mentioned procedure, the invention also relates to a release agent suitable for use in this process, which, as an additive, contains a proportion - that substance - which is bound with a synthetic resin binder whose propulsive force reacts at least diminishingly, for example the proportion of tertiary Amines, organometallic compounds or organic. Contains peroxides.

Der Anteil dieser Zusätze soll mindestens 10 Gew-%, Vorzugsweise zvischen 5 und' 20 Gew-% betragen. The proportion of these additives should be at least 10% by weight, preferably between 5 and 20% by weight.

Das Trennmittel Kann flüssig, vorzugsweise sprühfähig, sein und kann die Substanz in gelöster, emulgierter oder, dispergierter Form enthalten. Nach dein Auftragen-des Trenn= mittels auf die Arbeitsflächen der Schalungsform ist keine Ablüftzeit nötig, weil die trennaktive Substanz auch in gelöster, emulgierter oder dispergierter Form ihre gewünschten Eigenschaften aufweist. The release agent can and can be liquid, preferably sprayable contain the substance in dissolved, emulsified or dispersed form. After your Applying the separating means on the work surfaces of the formwork is not required Flash-off time necessary because the separating substance is also in dissolved, emulsified or dispersed form has its desired properties.

Nach einer bevorzugten Ausführungsform besteht das Trenn= mittel aus 5 - 25 Gew-% Wachs, 3 - 15 Gew-% der die Klebekraft des Kunstharzbinders verringernden, trennaktiven Substanz und 70 ~ 72 Gew-% eines Lösungsmittels. According to a preferred embodiment, the separating agent consists from 5 - 25% by weight wax, 3 - 15% by weight of the wax that reduces the adhesive strength of the synthetic resin binder, separation active substance and 70 ~ 72% by weight of a solvent.

Das Trennmittel kann aber auch von einer Folie, e'inem Papier., e'iner Kunststoffunterlage verkörpert sein, in welchem Fall dann die genannte Substanz eine der Formkörpermasse zuzuwendende Beschichtung einer auf die Arbeitsfläche der Schalungsform aufbriiigbaren schmiegsamen Folie od.dgl. bildet. The release agent can, however, also consist of a film, a paper., A Plastic base be embodied, in which case then the said substance a coating to be applied to the molding compound on the working surface of the Formwork form aufbriiigbaren flexible film or the like. forms.

Ein Ausführungsbeispiel' des erfindungsgemäßen Verfahrens sei nach£olqend geschildert: Zur Herstellung einer sogenannten Sohlschale, die bekanntlich den'Boden einer aus Beton-Eiprofilen bestehenden Abwasserleitung verkleidet, wurde ein aus 90 Gew-% mineralischem Zuschlag und 10 Gew-% härtbarem Polyesterharz bestehendes Gemenge als Formkörpermasse angefertigt und in eine Schalungsform aus Stahl, die vorteilhafterweise mit rauhen Innenflächen (Arbeitsflächen) ausgebildet war, eingefüllt. Diese Arbeitsflächen wurden vor dem Einfüllender Formkörpermasse mit einem Trennmittel besprüht, welches aus 10 Gew-% Wachs, 10 Gew-% eines tertiären Amines und 80 Gew-% eines Lösungsmittels, nAm h ch Methylenchlorid, bestand. An exemplary embodiment of the method according to the invention is given in accordance with £ olqend described: For the production of a so-called sole shell, the is known to cover the floor of a sewer pipe made of concrete egg profiles, was made from 90% by weight mineral aggregate and 10% by weight hardenable polyester resin existing mixture made as a molded body mass and made into a formwork form Steel, advantageously designed with rough inner surfaces (work surfaces) was filled. These work surfaces were before the molding compound was poured in sprayed with a release agent, which consists of 10% by weight wax, 10% by weight of a tertiary Amines and 80% by weight of a solvent, namely methylene chloride, consisted.

In dieser Schalungsform wurde die Formkörpermasse bei Raumtemperatur durch sechs Minuten belassen. Diese Zeitdauer genügte, um die angestrebte, die Xlebekraft des Kunstharz= binders im Bereich der Formkörper,oberfläche beseitigende Reaktion zwischen der genannten Substanz und dem Kunstharzblnder ablaufen zu lassen. Noch vor der völligen Erhärtung der Form= körper, masse, die erfahrungsgemäß nach etwa zwanzig bis fünfund= zwanzig Minuten eintritt, konnte der filigran gestaltete Formkörper beschädigungsfrei aus der, Schalungsform entnommen werden und ließ sich ohne Schwierigkeit von den Wandungen der ,1 Schalungsform (ArbeitsElAchen) blasen. The molding compound was in this formwork at room temperature left through for six minutes. This period of time was sufficient to achieve the desired vitality of the synthetic resin binder in the area of the moldings, surface-eliminating reaction to drain between the substance mentioned and the synthetic resin band. Yet before the complete hardening of the form = body, mass, which experience shows after about twenty to five = twenty minutes, the filigree shaped body could Can be removed from the formwork form without damage and could be easily removed Blow from the walls of the, 1 formwork form (ArbeitsElAchen).

Claims

P a t e n t a n s p'r u c h e 1. Process for the production of from Resin concrete existing moldings in shuttering forms using at least a release agent applied to the work surfaces of these formwork forms, e.g. an oil. Wax, a film or the like., Characterized in that this Release agent one with the synthetic resin binder of the molding compound chemically. responsive and as a result of this reaction, at least a substance which reduces its adhesive strength is added and is brought into contact with the surface of the shaped body. 2. Method according to claim 1, characterized by the use of a substance that is reactive in the polymerization of the resin binder engages.

3. The method according to claim 1 or 2, characterized in that = the duration of the reaction of the substance with the synthetic resin binder is shorter than the setting time (Cure time) of the molding compound.

4. The method according to any one of claims 1 to 3, characterized in that that the release agent has a proportion of tertiary amines and / or a proportion of organometallic 5. Organic peroxides compounds added. rird.

5. The method according to any one of claims 1 to 4, characterized in dissolved, em that the substance is a liquid release agent in. dissolved, emulsified or dispersed form is added.

6. The method according to any one of claims 1 to 5, characterized in that the solids content of the release agent between 5 and 20% by weight, preferably one wax used as a release agent.

7. The method according to any one of claims 1 'to 4, characterized in that that the substance as a coating of a film forming the release agent with the Molded body surface is brought into contact.

'8..Release agent for use in a method according to one of the Claims 1 to 6, 'characterized in that there is a proportion of an additive Contains substance which, when used with a synthetic resin binder, can be used to adhere to the adhesive; at least reacts diminishingly, e.g. a proportion of tertiary amines, organometallic compounds or, organic peroxides contains: 9. Release agent according to claim a; characterized, that the proportion of the additive is at least 10% by weight, preferably between 3 and 15 % By weight.

10. Release agent according to claim 8 or 9, characterized = characterized that it is liquid, preferably sprayable, and the substance is emulsified in dissolved form or in dispersed form.

11.- release agent according to one of claims 8 to 10, characterized marked-t * That the solids content in the liquid release agent is between 5 and 20% by weight, preferably contains about 10% by weight of a wax that supports the release effect.

12. Release agent according to one of the. Claims 8 to 11, characterized in that that it contains 5 - 25% by weight of wax, 3-15% by weight of the adhesive force the substance reducing the synthetic resin binder and 70 - 72% by weight of a solvent, e.g.

Methylene chloride.

13. Release agent according to claim 8 or 9, characterized in that the substance'die coating to be sent to the molding compound onto the work surface the formwork attachable-conformable film or the like. -forms.