DE2722076A1 - Lining, esp. veneering, shaped articles with adhesive - by using an intermediate fabric or perforated sheet layer to allow use of hot melt adhesives - Google Patents

Lining, esp. veneering, shaped articles with adhesive - by using an intermediate fabric or perforated sheet layer to allow use of hot melt adhesives

Info

Publication number
DE2722076A1
DE2722076A1 DE19772722076 DE2722076A DE2722076A1 DE 2722076 A1 DE2722076 A1 DE 2722076A1 DE 19772722076 DE19772722076 DE 19772722076 DE 2722076 A DE2722076 A DE 2722076A DE 2722076 A1 DE2722076 A1 DE 2722076A1
Authority
DE
Germany
Prior art keywords
adhesive
indicated
coated
esp
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19772722076
Other languages
German (de)
Other versions
DE2722076C2 (en
Inventor
Alfons Dr Lamping
Hans Landsiedel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henkel Dorus GmbH and Co KG
Original Assignee
Dr Rudolf Schieber GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dr Rudolf Schieber GmbH and Co KG filed Critical Dr Rudolf Schieber GmbH and Co KG
Priority to DE2722076A priority Critical patent/DE2722076C2/en
Publication of DE2722076A1 publication Critical patent/DE2722076A1/en
Application granted granted Critical
Publication of DE2722076C2 publication Critical patent/DE2722076C2/en
Expired legal-status Critical Current

Abstract

Substrates, esp. shaped articles, are lined by cementing the substrate (A) and the cover sheet (B) with adhesive, if necessary under heat and/or pressure, in the presence of an intermediate structure, (C), which resists mechanical stress and which is opt. coated with adhesive. (C) may be a woven or knitted fabric or a web, or a sheet of plastic, metal or paper provided with perforations, esp. in raster-arrangement. A pref. sheet is of thermoplastic material, esp. polyolefin. The process is used for lining ridged articles in furniture, esp. for sheathing profiles and for bonding fragile veneers. Breaking of (B), esp. veneer, is prevented.

Description

Verfahren zum Kaschieren von Trägern Method for laminating carriers

Die Erfindung betrifft ein Verfahren zum Kaschieren von Trägern, insbesondere Formteilen durch Verklebung von Träger und Auflagebahn mit Klebstoff, gegebenenfalls unter Anwendung von Druck und/oder bei erhöhter Temperatur.The invention relates to a method for laminating carriers, in particular Molded parts by gluing the carrier and support sheet with adhesive, if necessary using pressure and / or at elevated temperature.

Die Herstellung von Verbundstoffen durch Verklebung ist bekannt. Dies kann beispielsweise durch Laminieren und Beschichten einerseits oder durch Dublieren bzw. Kaschieren andererseits erfolgen. Beim Dublieren bzw. Kaschieren werden bereits feste Bahnen oder ein Formteil als Träger mit einer Auflagebahn verklebt, was in der Regel unter Druckanwendung, zum Teil bei erhöhter Temperatur, erreicht wird.The production of composite materials by gluing is known. this can for example by lamination and coating on the one hand or by doubling or lamination on the other hand take place. When duplicating or laminating, solid tracks or a molded part as a carrier with a support track stuck together, which is usually under the application of pressure, sometimes at elevated temperature, is achieved.

Bei der "Veredelung" von Formteilen durch deren Kaschierung mit dekorativer Deckfolie bzw. Auflagefurnier, ergeben sich insbesondere dann Probleme, wenn nicht ebene, kantige Formteile überzogen werden sollen. Hierbei sind z.B. Edelholzfurniere durch die auftretenden Biegebeanspruchungen, die wechselnd aus unterschiedlichen Richtungen angreifen können, stark bruchgefährdet. Dadurch ergeben sich in der Praxis insbesondere bei Verwendung der wertvollen exotischen Edelholzfurniere erhebliche Verluste. Selbst wenn die Verklebung ohne Rissbildung etc. durchgeführt wird, ist der erhaltene Verbund häufig nur beschränkt reissfest, insbesondere bei erhöhter Temperatur. Dies gilt insbesondere für Formteilträger, auf die die Auflagebahn mittels Schmelzkleber aufgebracht worden ist, wenn dieser aufgrund der Strukturierung oder des Profils des Formsteils starken Biegebeanspruchungen ausgesetzt ist.When "refining" molded parts by laminating them with decorative Cover sheet or overlay veneer, problems arise in particular when not flat, angular moldings are to be coated. Here are e.g. fine wood veneers due to the bending stresses that occur, which alternate from different Directions can attack, very likely to break. This results in practice especially when using the valuable exotic fine wood veneers Losses. Even if the bond is carried out without cracking etc. the composite obtained is often only tear-resistant to a limited extent, especially in the case of increased Temperature. This applies in particular to molded part carriers on which the support web is by means of Hot melt adhesive has been applied if this is due to the structuring or the profile of the molded part is exposed to strong bending stresses.

Zwar besitzen die üblicherweise als Schmelzkleberfilme bezeichneten Materialien eine hervorragende Adhäsion an den verschiedensten miteinander zu verklebenden Materialien und auch eine gute Kälte- und Wärmeflexibilität. Die Bruchdehnung kann bis zu mehreren 100 % betragen und auch die Reissfestigkeitswerte können, je nach verwendetem Ausgangsmaterial,zwischen etwa 50 kp/cm2 bei Schmelzkleberfilmen auf Xthylenvinylacetat-Basis bis zu über 500 kp/cm2 bei Filmen aus Polyurethanen liegen. Diese Schmelzkleberfilme besitzen aber ein sehr starkes Rückstellvermögen und eine so hohe Elastizität, dass sich aufgrund dieser Eigenschaft eine Anwendung auf Gebieten, wo es um mehr starre Verbindungen geht, verbietet. Daher wird bei der Verwendung von Furnieren zur Auflage auf scharfkantigen Profilen häufig noch auf traditionelle Art mit Hilfe von Harnstoffharzleimen in Formpressen verleimt. Um ein Reissen des Furniers über den scharfkantigen Profilen zu vermeiden, werden andere Nachteile, wie begrenzte Topfzeit, geringe Abbindegeschwindigkeit, lange Presszeit, hohe Presstemperatur von Harnstoffharzleim in Kauf genommen.It is true that they usually have hot-melt adhesive films Materials have excellent adhesion to the most varied of materials to be glued together Materials and also good cold and heat flexibility. The elongation at break can up to several 100% and also the tensile strength values can, depending on used starting material, between about 50 kp / cm2 for hot melt adhesive films Xthylenevinylacetate base up to over 500 kp / cm2 for films made of polyurethane. However, these hot melt adhesive films have a very strong resilience and such a high elasticity that this property is suitable for use in areas where more rigid connections are involved. Therefore, at the use of veneers to rest on sharp-edged profiles often still glued in the traditional way with the help of urea resin glue in compression molding. In order to avoid tearing the veneer over the sharp-edged profiles other disadvantages, such as limited pot life, slow setting speed, long Pressing time, high press temperature of urea resin glue accepted.

Der Erfindung liegt die Aufgabe zugrunde, ein verbessertes Verfahren der eingangs genannten Art zu schaffen. Hierbei soll insbesondere ein Verfahren bereitgestellt werden, in dem die Auf lagebahn bzw. das Deckfurnier unter verminderter Rissgefahr der Bahn bzw. des Furniers mit Formteilen ebener, insbesondere aber profilierter Art, zu einem besonders abrissfesten Verbund zusammengefügt werden kann.The invention is based on the object of an improved method of the type mentioned at the beginning. In particular, a method is intended here are provided, in which the web or the face veneer under reduced Risk of cracking of the membrane or the veneer with molded parts that are even, but especially more profiled Art that can be joined together to form a particularly tear-resistant composite.

Nach einem Aspekt dieser Aufgabe soll die Furnierung von aus Spanplatten hergestellten Formkörpern in der Möbelindustrie, die scharfkantige Profile aufweisen, bei Verwendung von Schmelzklebern unter Beibehaltung der Vorteile, die bislang auf dem Einsatz von Harnstoffharzleim beruhten, erreicht werden.One aspect of this task is to veneer from particle board manufactured moldings in the furniture industry that have sharp-edged profiles, when using hot melt adhesives while maintaining the advantages that were previously available based on the use of urea resin glue.

Diese Aufgabe wird bei einem Verfahren der eingangs genannten Art dadurch gelöst, dass die Verklebung unter Zusammenführung von Träger und Auflagebahn bzw. -furnier, bei Anwesenheit eines dazwischen befindlichen, mechanisch belastbaren Gebildes, das gegebenenfalls mit Kleber beschichtet ist, durchgeführt wird.This task is performed in a method of the type mentioned at the beginning solved by the fact that the bond with the merging of the carrier and support sheet or veneer, in the presence of a mechanically resilient one in between Structure, which is optionally coated with adhesive, is carried out.

Bei dieser Anordnung werden die physikalischen Eigenschaften des fertigen Produktes durch eine Kombination der guten Eigenschaften des verwendeten Klebers wie des zwischengefügten Gebildes in vorteilhafter Weise bestimmt. Hierbei trägt das zwischenliegende Gebilde offenbar in vorteilhafter Weise zu den Klebeeigenschaften des verwendeten Klebesystems bei, wodurch beispielsweise Furniere leicht, schnell und sauber, im wesentlichen unter Vermeidung von Rissgefahr, verklebt werden können. Das zwischengefügte Gebilde trägt nicht nur zu einer Verbesserung der mechanischen Kennwerte des erzeugten Verbundes und zu einer Vereinfachung des Verfahrens bei, sondern es gestattet nunmehr auch den Einsatz von Heissschmelzklebern auf Gebieten, auf denen bislang in befriedigender Weise nur mit Hilfe von Harnstoffharzleim verklebt werden konnte. Darüberhinaus kann das Gebilde als Träger unterschiedlicher Kleber-, Härter-bzw. Beschleunigersysteme dienen, wodurch eine optimale Abstimmung der Klebeeigenschaften auf unterschiedliche Auflagebahn- bzw. Deckfurnier- und Trägermaterialien erzielt werden kann.With this arrangement, the physical properties of the finished Product through a combination of the good properties of the adhesive used as determined in an advantageous manner of the interposed structure. Here contributes the intermediate structure evidently has an advantageous effect on the adhesive properties of the adhesive system used, which makes veneers, for example, easy and quick and can be glued cleanly, essentially avoiding the risk of cracking. The intermediate structure not only contributes to an improvement in the mechanical Characteristic values of the created composite and to a simplification of the process, but it now also allows the use of hot melt adhesives in areas on which so far glued in a satisfactory manner only with the help of urea resin glue could be. In addition, the structure can be used as a carrier of different adhesive, Hardener or Accelerator systems are used, whereby an optimal coordination of the adhesive properties achieved on different support sheet or face veneer and carrier materials can be.

Da das zwischenliegende Gebilde eine vorteilhafte Beeinflussung der Eigenschaften des Klebeverbundes bewirken soll, wird dies im allgemeinen einen elastischen, mechanisch beanspruchbaren biegefähigen Körper darstellen, der unter Klebebedingungen nicht zerstört werden kann. Durch letztere Eigenschaft soll sichergestellt sein, dass nach Beendigung des Klebevorgangs das Gebilde im wesentlichen noch immer als solches vorliegt und damit eine Verbesserung der mechanischen Eigenschaften bewirken kann. Sofern dies gewünscht ist, kann allerdings das Gebilde selbst aus einem unter Klebebedingungen zur Verklebung beitragenden Material bestehen,was insbesondere dann der Fall ist, wenn das Gebilde ausschliesslich als Träger zur Aufnahme zweier verschiedenartiger Kleber- bzw. Härtersysteme zur Abstimmung auf unterschiedliches Deck- und Trägermaterial dienen soll.Since the intermediate structure has an advantageous influence on the To bring about properties of the adhesive bond, this is generally an elastic, represent mechanically stressable bendable body under adhesive conditions cannot be destroyed. The latter property is intended to ensure that after the end of the gluing process, the structure is still essentially as such is present and thus bring about an improvement in the mechanical properties can. If this is desired, however, the structure itself can consist of an adhesive material contributing to the bonding, which is particularly the case, if the structure is used exclusively as a carrier to accommodate two different types Adhesive or hardener systems to match different cover and carrier materials should serve.

Diese Ausführungsform ist jedoch im Rahmen der Erfindung weniger bevorzugt.However, this embodiment is less preferred within the scope of the invention.

Im allgemeinen stellt das Gebilde ein Gewebe, Vlies oder Gewirke, z.B. aus textilem Material, Glasfaser, etc., dar.In general, the structure is a woven, non-woven or knitted fabric, e.g. made of textile material, glass fiber, etc.

Es kann jedoch auch eine, vorzugsweise Öffnungen aufweisende, Bahn aus Kunststoff, Metall oder Papier bzw. Mischungen oder Kombinationen hiervon darstellen. Wenngleich es für viele Zwecke ausreichend ist, als Gebilde ein Gewebe oder gar Vlies einzusetzen, so werden doch besonders gute Festigkeitswerte beim Einsatz eines Gewirkes oder auch einer rasterförmige Öffnungen aufweisenden Bahn aus mechanisch gut belastbarem Material, wie thermoplastischer Folie, Metall, etc., erzielt. Als Gebildematerial ist insbesondere thermoplastischer Kunststoff, z.B. Polyolefin und besonders vorteilhaft Polyäthylen bzw. Polypropylen, bevorzugt, da sich die thermoplastischen Materialien bei in der Hitze erfolgendem Verpressungsvorgang besonders elastisch verhalten und sich der Profilierung des Formkörpers in jeder Weise anpassen können. Damit werden optimale Adhäsions- bzw. Kohäsionswerte erhältlich, da der auf dem Gebilde befindliche Kleber an jedem Ort optimal zur Auflagebahn zu liegen kommt bzw. diese zu benetzen vermag. In der Regel werden solche thermoplastischen Materialien für das Gebilde jedoch nur dann herangezogen, wenn die Temperatur bei der Verklebungsstufe so eingestellt ist, dass zwar der Kleber aktiviert (sofern Heissiegelkleber angewandt wird) nicht aber das Gebilde vollkommen aufgeschmolzen wird.However, it can also be a web, preferably having openings made of plastic, metal or paper or mixtures or combinations thereof. Although it is sufficient for many purposes, as a structure a fabric or even Use fleece, so are particularly good strength values when using a Knitted or a grid-like openings having web made of mechanical easily resilient material, such as thermoplastic film, metal, etc., achieved. as Formed material is in particular thermoplastic plastic, e.g. polyolefin and particularly advantageous polyethylene or polypropylene, preferred because the thermoplastic Materials are particularly elastic when the pressing process takes place in the heat behave and can adapt to the profiling of the molding in any way. This enables optimal adhesion or cohesion values to be obtained, since the Adhesives located in the structure come to rest optimally in relation to the support web at every location or is able to wet them. Usually such thermoplastic materials are used for the structure, however, only used if the temperature at the bonding stage is set in such a way that the adhesive is activated (if hot-seal adhesive is used will) but the structure is not completely melted.

Durch die in dem Gebilde mit Vorteil angebrachten Öffnungen' wobei es bevorzugt ist, dass sich diese in einer rasterförmigen Anordnung befinden, ist es möglich, dass beispielsweise einseitig oder zweiseitig auf dem Gebilde aufgebrachter Kleber bei dem Pressvorgang homogen auf Ober- und Unterseite des Gebildes gelangt und damit zu einer bestmöglichen Kohäsion zwischen Formteil und Auflage beiträgt. Dies kann jedoch auch durch die Verwendung eines Gebildematerials erzielt werden, das unter Klebebedingungen permeabel bzw. semipermeabel wird. Je nach Anwendungszweck kann es zweckmässig sein, das Gebilde einseitig oder zweiseitig mit Kleber zu beschichten, der in letzterem Fall identisch oder unterschiedlich sein kann. So ist es auch möglich, z.B. auf der Unterseite des durchbrochenen Gebildes eine und auf der Oberseite des Gebildes die andere Komponente eines Zweikomponentenklebers aufzubringen. In gleicher Weise kann auf eine Seite Kleber und auf die anderen Seite Härter, letzterer z.B. in Form eines aufgetrockneten Härterfilms, aufgetragen sein. Bei der Verwendung von Härterfilm sei besonders auf die stark saure Substanzen inkorporierenden Filme der Patentanmeldung P ?7.l9..?6.9.:9....Through the openings made in the structure with advantage it is preferred that these are in a grid-like arrangement it is possible that, for example, one-sided or two-sided applied to the structure During the pressing process, glue reaches the top and bottom of the structure homogeneously and thus contributes to the best possible cohesion between the molded part and the support. However, this can also be achieved by using a building material, which becomes permeable or semi-permeable under adhesive conditions. Depending on the application it may be useful to coat the structure with adhesive on one or both sides, which in the latter case can be identical or different. So it is also possible E.g. one on the underside of the openwork structure and one on the top of the To apply the other component of a two-component adhesive structure. In the same Adhesive can be used on one side and hardener on the other, the latter e.g. be applied in the form of a dried hardener film. When using of hardener film pay special attention to the strongly acidic substances-incorporating films the patent application P? 7.l9 ..? 6.9.:9 ....

der Anmelderin verwiesen, die eine überaus rasche Aushärtung von Harnstoffharzleim gestatten. Letzterer kann z.B. auf dem Träger, der Innenseite der Auflagebahn und/oder der anderen Seite des Gebildes aufgebracht sein.referenced by the applicant, the extremely rapid hardening of urea resin glue allow. The latter can e.g. on the carrier, the inside of the support web and / or be applied to the other side of the structure.

Wenngleich die Verklebung von Auf lagebahn bzw. Deckfurnier mit dem Träger, z.B. einem gewinkelten Formteil, durch den auf dem zwischengefügten Gebilde enthaltenen Kleber bewirkt wird, so ist es nicht ausgeschlossen, dass der Träger und/oder die Auflagebahn bzw. das Deckfurnier ebenfalls mit Kleber oder Härter beaufschlagt worden sind. Es ist offenbar, dass hier beliebige Kombinationen von Härter bzw. Kleber nicht nur auf den zu verklebenden Flächen von Auflagebahn und Träger sondern auch auf Ober- und Unterseite des Gebildes möglich sind.Although the bonding of the sheet or face veneer with the Support, e.g. an angled molding, through the one on the intermediate structure contained glue is effected, so it is not excluded that the carrier and / or the overlay or the face veneer also with glue or Have been applied harder. It is obvious that there are arbitrary combinations here of hardener or adhesive not only on the surfaces to be bonded of the support sheet and carriers but also on the top and bottom of the structure are possible.

Der vorteilhaft in rasterförmiger Konfiguration aufgetragene Kleber kann z.B. einenHeissiegelkleber auf Basis von Polyester, Polyamid oder Polyurethan darstellen. Besonders bevorzugt ist jedoch die Verwendung von Polyäthylenvinylacetatkleber, der einseitig oder zweiseitig auf einem Polyäthylengitter aufgetragen ist. So lässt sich z.B. die Furnierung von aus Spanplatten hergestellten Formkörpern in der Möbelindustrie besonders gut unter Vermeidung des üblicherweise eingesetzten Harnstoffharzleimes dann erreichen, wenn Schmelzkleber auf EVA-Basis auf dem genannten Thermoplastengitter zwischen Furnier und den zu furnierenden Formkörpern gebracht und sodann in einer Presse von aussen durch das Furnier Wärme zugeführt wird.The adhesive applied advantageously in a grid-shaped configuration can, for example, be a heat seal adhesive based on polyester, polyamide or polyurethane represent. However, the use of polyethylene vinyl acetate adhesive is particularly preferred, which is applied on one or both sides of a polyethylene grid. So lets e.g. the veneering of moldings made from chipboard in the furniture industry particularly good while avoiding the urea resin glue usually used then achieve when hot melt adhesive on EVA basis on the said thermoplastic mesh brought between veneer and the molded bodies to be veneered and then in a Heat is supplied to the press from the outside through the veneer.

Hierbei hat sich gezeigt, dass der so verstärkte Schmelzkleberfilm auch das bei der Verarbeitung von Furnieren häufig auftretende Reissen des Furnierblattes verhindert, weil das Furnier aufgrund der Kombination der hervorragenden Adhäsion des Schmelzkleberfilms am Holz und der guten mechanischen Eigenschaften des zwischengeführten Gitters besonders gut zusammengehalten wird.It has been shown here that the hotmelt adhesive film reinforced in this way also the tearing of the veneer sheet, which often occurs when processing veneers prevented because the veneer due to the combination of excellent adhesion the hotmelt adhesive film on the wood and the good mechanical properties of the intermediate Lattice is held together particularly well.

Nach einer besonderen Ausführungsform der Erfindung kann das zwischengeführte Gebilde beispielsweise ein thermoplastisches Gittergewebe bzw. Gewirke darstellen, dessen Ober- und/oder Unterseite niedrigerschmelzend als das Innere des Gewebes bzw.According to a particular embodiment of the invention, the intermediate A structure, for example, a thermoplastic mesh fabric or knitted fabric represent, the top and / or bottom of which has a lower melting point than the inside of the fabric respectively.

Gewirkes eingestellt sind. Hierdurch kann bei der Verklebung von Auflagebahn bzw. Deckfurnier und Träger unter Druck-und Temperaturbedingungen, bei denen lediglich die relativ niedriger schmelzende Ober- und/oder Unterschicht als Heissiegelkleber zu wirken vermag, das Gitter selbst sowohl zur vorteilhaften dauernden Beeifnlussung der mechanischen Eigenschaften des Verbundes wie auch zur Bewirkung der Verklebung selbst beitragen. Derartige spezielle Gebildeausführungen können beispielsweise dadurch erzeugt sein, dass die Gebilde an Ober-und/oder Unterseite einen gegenüber dem Inneren stark erhöhten Weichmachergehalt aufweisen, der zu dem gewünschten Gefälle der thermoplastischen Flusseigenschaften innerhalb des thermDplastischen Gitters führt. In diesem Fall dient das Gebilde, wie bereits angeführt, sowohl als Stütz- und Festigungs- wie auch Klebeelement gleichzeitig. Ähnliche Wirkungen können auch durch die gezielte, analog abgestufte Zumischung vernetzender bzw.Knitted fabrics are set. This can result in the gluing from Support web or face veneer and carrier under pressure and temperature conditions which only the relatively lower melting upper and / or lower layer than Hot-seal adhesive is able to work, both the grid itself and the advantageous permanent Influence of the mechanical properties of the composite as well as the effect contribute to the bonding itself. Such special structure designs can be generated, for example, that the structures on the top and / or bottom have a significantly increased plasticizer content compared to the interior, which is part of the Desired gradient of the thermoplastic flow properties within the thermDplastic Lattice leads. In this case, as already mentioned, the structure serves both as Supporting and fixing as well as adhesive element at the same time. Similar effects can be also through the targeted, analogue graded admixture of cross-linking or

vernetzter Anteile innerhalb des Thermoplastgitters erhältlich sein.be available crosslinked portions within the thermoplastic grid.

Wenngleich das Gebilde in der Regel mit Schmelzkleber beaufschlagt ist, so kann dies nach einem weiteren Aspekt der Erfindung auch alternativ Glutinleim aufweisen. Auch ist es möglich, dass das Gebilde auf der einen Seite Glutinleim und auf der anderen Heisschmelzkleber aufweist. Eine derartige Kleberkonstellation erfordert jedoch auf der Fläche, die den Glutinleim trägt, eine etwas hydrophile Natur. In solchen Fällen kann das Gebilde beispielsweise selbst einen Verbund, z.B. aus Polyester-Papier oder Polyester-Polyvinylalkohol, darstellen.Although the structure is usually applied with hot melt adhesive is, then, according to a further aspect of the invention, this can alternatively also be glutin glue exhibit. It is also possible that the structure has glow glue on one side and has hot melt adhesive on the other. Such a glue constellation however, requires a somewhat hydrophilic surface on the surface that bears the glutinic glue Nature. In such cases, for example, the structure itself can be a composite, e.g. made of polyester paper or polyester-polyvinyl alcohol.

Der Träger besteht in der Regel aus Holz, Papier, Pappe, Kunststoff oder Metall bzw. Mischungen oder Kombinationen hiervon. Das erfindungsgemässe Verfahren kann mit besonderem Vorteil dann angewandt werden, wenn der Träger ein nicht planes, profiliertes oder kantiges Formteil darstellt. Dieses kann selbstverständlich an den zu verklebenden Flächen ebenfalls mit Kleber beaufschlagt sein. In diesem Fall ist es dann nicht immer erforderlich, dass das zwischengeführte Gebilde ebenfalls Kleber enthält.The carrier is usually made of wood, paper, cardboard, plastic or metal or mixtures or combinations of this. The inventive Method can be used with particular advantage when the carrier is a does not represent a flat, profiled or angular shaped part. This can of course adhesive must also be applied to the surfaces to be bonded. In this In this case, it is not always necessary that the intermediate structure also Contains glue.

Die Verwendung des Gebildes in dem erfindungsgemässen Verfahren erlaubt eine besonders schonende Arbeitsweise dann, wenn das Gebilde zunächst mit der Innenseite der Auflagebahn und erst sodann der hieraus gebildete Verbund mit dem Träger verklebt werden. Hierdurch wird die Stabilität von empfindlichen Deckfurnieren, z.B.exotischen Furnierhölzern, erheblich erhöht und die Rissgefahr beim Verkleben entsprechend vermindert, da sich das derart an seiner Innenseite "verstärkte" Deckfurnier den dann zum Teil in gegensinniger Weise auftretenden Biegebeanspruchungen besser gewachsen zeigt. Bei einer derartigen Arbeitsweise kann es bevorzugt sein, auf der mit der Innenseite der Auf lagebahn zu verklebenden Oberseite des Gebildes einen bei niedriger Temperatur schmelzenden Kleber zu verwenden,bei der der gegebenenfalls auf der Unterseite des Gebildes vorliegende Kleber noch nicht aktiviert wird.The use of the structure in the method according to the invention is permitted a particularly gentle way of working when the structure is first turned on the inside the support web and only then the composite formed from it is glued to the carrier will. This increases the stability of sensitive face veneers, e.g. exotic ones Veneers, considerably increased and the risk of cracking when gluing accordingly reduced, as the face veneer "reinforced" in this way on its inside then partly in opposite directions occurring bending stresses better shows. In such a way of working, it may be preferred to use the Inside of the web to be glued to the top of the structure one at lower Use temperature melting glue, where appropriate on the underside the structure present adhesive is not yet activated.

Das erfindungsgemässe Verfahren hat seine bevorzugte Anwendung zur Kaschierung kantiger Formteile in der Möbelindustrie. Hier können insbesondere Profile mit fragilen Deckfurnieren ummantelt werden. Eine weitere bevorzugte Anwendung besteht in der Kantenverleimung von Spanplatten etc. durch übergezogene Deckfolien bzw. -furniere.The inventive method has its preferred application for Laminating angular molded parts in the furniture industry. Profiles in particular can be used here be coated with fragile face veneers. Another preferred application is in the edge gluing of chipboard etc. through coated cover foils or veneers.

Claims (24)

Verfahren zum Kaschieren von Trägern PATENTANSPRÜCHE Verfahren zum Kaschieren von Trägern, insbesondere Formteilen durch Verleimung von Träger und Auf lagebahn mit Klebstoff, gegebenenfalls unter Anwendung von Druck und/oder bei erhöhter Temperatur, dadurch g e -k e n n z e i c h n e t , dass die Verklebung unter Zusammenführung von Träger und Auf lagebahn bei Anwesenheit eines dazwischen befindlichen, mechanisch belastbaren Gebildes, das gegebenenfalls mit Kleber beschichtet ist, durchgeführt wird.Method for laminating carriers. PATENT CLAIMS Method for Laminating supports, in particular molded parts, by gluing supports and Overlay web with adhesive, if necessary with the application of pressure and / or with increased temperature, as a result of which the bond is not indicated with the merging of the carrier and the support web in the presence of one in between located, mechanically resilient structure, which may be coated with adhesive is carried out. 2. Verfahren nach Anspruch 1, dadurch g e k e n n -z e i c h n e t , dass das Gebilde ein Gewebe, Vlies oder Gewirke darstellt.2. The method according to claim 1, characterized in that g e k e n n -z e i c h n e t that the structure is a woven, non-woven or knitted fabric. 3. Verfahren nach Anspruch 1, dadurch g e k e n n -z e i c h n e t , dass das Gebilde eine Öffnungen aufweisende Bahn aus Kunststoff, Metall oder Papier darstellt.3. The method according to claim 1, characterized in that g e k e n n -z e i c h n e t that the structure has an apertured sheet made of plastic, metal or paper represents. 4. Verfahren nach Anspruch 3, dadurch g e k e n n -z e i c h n e t , dass die Öffnungen rasterförmig angeordnet sind.4. The method according to claim 3, characterized in that g e k e n n -z e i c h n e t that the openings are arranged in a grid. 5. Verfahren nach Anspruch 3 oder 4, dadurch g e k e n nz e i c h n e t , dass die Bahn aus thermoplastischem Kunststoff, insbesondere Polyolefin, besteht.5. The method according to claim 3 or 4, characterized g e k e n nz e i c h n e t that the sheet made of thermoplastic material, in particular polyolefin, consists. 6. Verfahren nach einem der vorhergehenden Ansprüche, dadurch g e k e n n z e i c h n e t , dass die Bahn unter Klebebedingungen semipermeabel wird.6. The method according to any one of the preceding claims, characterized g e it is not indicated that the web becomes semi-permeable under adhesive conditions. 7. Verfahren nach einem der vorhergehenden Ansprüche, dadurch g e k e n n z e i c h n e t , dass das Gebilde einseitig mit Kleber beschichtet ist.7. The method according to any one of the preceding claims, characterized g e it is not indicated that the structure is coated on one side with adhesive. 8. Verfahren nach einem der vorhergehenden Ansprüche, dadurch g e k e n n z e i c h n e t , dass das Gebilde beidseitig mit Kleber beschichtet ist.8. The method according to any one of the preceding claims, characterized g e it is not indicated that the structure is coated with adhesive on both sides. 9. Verfahren nach Anspruch 8, dadurch g e k e n n -z e i c h n e t , dass das Gebilde auf der einen Seite mit Kleber beschichtet ist, der von dem auf der anderen Seite verschieden ist.9. The method according to claim 8, characterized in that g e k e n n -z e i c h n e t that the structure on the one hand is coated with glue, which is different from the one on the other side. 10. Verfahren nach einem der vorhergehenden Ansprüche, dadurch g e k e n n z e i c h n e t , dass das Gebilde ein- oder zweiseitig mit Härter, z.B. in Form eines aufgetrockneten Härterfilms, beaufschlagt ist und die Verklebung durch den auf Träger und/oder Auflagebahn aufgebrachten Kleber bewirkt wird.10. The method according to any one of the preceding claims, characterized g e it is not indicated that the structure is coated on one or both sides with hardener, e.g. in the form of a dried-on hardener film, is applied and the bond through the adhesive applied to the carrier and / or overlay is effected. 11. Verfahren nach einem der Ansprüche 7 bis 9, dadurch g e k e n n z e i c h n e t , dass der Kleber in rasterförmiger Konfiguration aufgetragen ist.11. The method according to any one of claims 7 to 9, characterized g e k e n It is not noted that the adhesive is applied in a grid-like configuration is. 12. Verfahren nach einem der Ansprüche 7 bis 9 oder 11, dadurch g e k e n n z e i c h n e t , dass der Kleber ein Heissiegelkleber auf Basis von Polyester, Polyaanid,Polyurethan oder Äthylen-vinylacetat bzw. Copolymerisaten hiervon ist.12. The method according to any one of claims 7 to 9 or 11, characterized in g it is not noted that the adhesive is a hot-seal adhesive based on polyester, Polyanide, polyurethane or ethylene-vinyl acetate or copolymers thereof. 13. Verfahren nach einem der Ansprüche 7 bis 9 oder 11 und 12, dadurch g e k e n n z e i c h n e t , dass man ein Polyäthylengewebe bzw,-gewirke, das beidseitig mit Polyäthylenvinylacetat beaufschlagt ist, verwendet.13. The method according to any one of claims 7 to 9 or 11 and 12, characterized it is not indicated that one is a polyethylene fabric or knitted fabric that is on both sides is applied with polyethylene vinyl acetate, used. 14. Verfahren nach einem der Ansprüche 7 bis 9 oder 11 bis 13, dadurch g e k e n n z e i c h n e t , dass man ein thermoplastisches Gewebe b2w. Gewirke als Gebilde verwendet, dessen Ober- und/oder Unterseite niedriger schmelzend als das Innere des Gewebes bzw. Gewirkes eingestellt ist, und die Verklebung von Auflagebahn und Träger unter Druck- und Temperaturbedingungen durchführt, bei denen lediglich die niedriger schmelzende Ober- und/oder Unterschicht als Heissiegelkleber zu wirken vermag.14. The method according to any one of claims 7 to 9 or 11 to 13, characterized it is not noted that a thermoplastic fabric b2w. Knitted fabrics used as a structure, the top and / or bottom of which melts lower than the inside of the fabric or knitted fabric is set, and the gluing of the overlay and carries out carriers under pressure and temperature conditions at which only the lower melting top and / or bottom layer to act as a hot-seal adhesive able. 15. Verfahren nach Anspruch 14, dadurch g e k e n n -z e i c h n e t , dass das thermoplastische Gewebe und/oder Gewirke an Ober- und/oder Unterseite einen höheren Weichmachergehalt aufweist.15. The method according to claim 14, characterized in that g e k e n n -z e i c h n e t that the thermoplastic fabric and / or knitted fabric on the top and / or bottom has a higher plasticizer content. 16. Verfahren nach einem der Ansprüche 7 bis 9 oder 11, dadurch g e k e n n z e i c h n e t , dass das Gebilde auf zumindest einer,ggf. hydrophil eingestellten,Seite Glutinleim enthält.16. The method according to any one of claims 7 to 9 or 11, characterized in g It is not indicated that the structure is based on at least one, possibly hydrophilic set, side contains ember glue. 17. Verfahren nach Anspruch 16, dadurch g e k e n n -z e i c h n e t , dass man ein Gebilde verwendet, das einen Verbund darstellt, auf dessen hydrophiler Seite Glutinleim und auf dessen anderer Seite Heissschmelzkleber aufgetragen ist.17. The method according to claim 16, characterized in that g e k e n n -z e i c h n e t that one uses a structure that represents a composite, on its hydrophilic Glutine glue on the other side and hot-melt adhesive applied on the other side. 18. Verfahren nach Anspruch 17, dadurch g e k e n n -z e i c h n e t . dass der Verbund aus Polyester-Papier besteht.18. The method according to claim 17, characterized in that g e k e n n -z e i c h n e t. that the composite consists of polyester paper. 19. Verfahren nach einem der vorhergehenden Ansprüche, dadurch g e k e n n z e i c h n e t , dass der Träger ein aus Holz, Papier, Pappe, Kunststoff oder Metall zumindest teilweise bestehendes Formteil darstellt, das gegebenenfalls mit Kleber bzw. Härter beaufschlagt ist.19. The method according to any one of the preceding claims, characterized g e no indication that the carrier is made of wood, paper, cardboard, plastic or metal represents at least partially existing molded part, which optionally is applied with glue or hardener. 20. Verfahren nach einem der vorhergehenden Ansprüche, dadurch g e k e n n z e i c h n e t , dass die Auflagebähn eine Kunststoff- bzw. Metallfolie oder insbesondere ein Deckfurnier ist.20. The method according to any one of the preceding claims, characterized g e no indication that the support conveyor a plastic or metal foil or in particular a face veneer. 21. Verfahren nach einem der vorhergehenden Ansprüche, dadurch g e k e n n z e i c h n e t , dass das Gebilde zunächst mit der Innen seite der Auf lagebahn und sodann der hieraus gebildete Verbund mit dem Träger verklebt werden.21. The method according to any one of the preceding claims, characterized g e it is not indicated that the structure is initially with the inside of the top layer web and then the composite formed therefrom are glued to the carrier. 22. Anwendung der Verfahren nach einem der Ansprüche 1 bis 21 zur Kaschierung kantiger Formteile, in der Möbelindustrie, insbesondere zur Profilummantelung.22. Application of the method according to any one of claims 1 to 21 for Lamination of angular molded parts, in the furniture industry, especially for profile wrapping. 23. Anwendung des Verfahrens nach Anspruch 21 zur Verklebung fragiler Deckfurniere.23. Use of the method according to claim 21 for bonding more fragile Face veneers. 24. Anwendung des Verfahrens nach Anspruch 22 zur Kantenverleimung durch übergezogene Deckfolie bzw. -furnier.24. Application of the method according to claim 22 for edge gluing through coated cover foil or veneer.
DE2722076A 1977-05-16 1977-05-16 Process for the production of angular molded parts continuously coated with fragile face veneer Expired DE2722076C2 (en)