DE2706550A1 - Sepn. of solids from a suspension - by addn. of a water soluble ethylene oxide polymer to form floating foam - Google Patents
Sepn. of solids from a suspension - by addn. of a water soluble ethylene oxide polymer to form floating foamInfo
- Publication number
- DE2706550A1 DE2706550A1 DE19772706550 DE2706550A DE2706550A1 DE 2706550 A1 DE2706550 A1 DE 2706550A1 DE 19772706550 DE19772706550 DE 19772706550 DE 2706550 A DE2706550 A DE 2706550A DE 2706550 A1 DE2706550 A1 DE 2706550A1
- Authority
- DE
- Germany
- Prior art keywords
- polymer
- water
- ppm
- ethylene oxide
- solids
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
Titel: Äthylenoxid-Polymere für die SchaumflotationTitle: Ethylene Oxide Polymers for Foam Flotation
Beschreibung Äthylenoxid-Polymere für die Schaumflotation Die Erfindung betrifft die Schaumflotation eines suspendierten Materials in einem flüssigen Medium unter Verwendung eines wasserlöslichen Polyäthylenoxids. Das Polymer kann vollständig aus Äthylenoxideinheiten bestehen oder auch noch einen geringen Anteil von Propylenoxideinheiten aufweisen. Der wesentliche Punkt ist jedoch, daß das Polymer letztlich wasserlöslich ist.Description Ethylene Oxide Polymers for Foam Flotation The invention relates to the froth flotation of a suspended material in a liquid medium using a water-soluble polyethylene oxide. The polymer can be completely consist of ethylene oxide units or a small proportion of propylene oxide units exhibit. The essential point, however, is that the polymer will ultimately be water soluble is.
Die Schaumflotation wird auf vielen Gebieten angewandt, für die sie ursprünglich nicht vorgesehen war. Diese Ausweitung der Anwendbarkeit ergab sich aufgrund der Wirtschaftlichkeit gegenüber den bisherigen Verfahren. Die Gewinnung von Schwebstoffen bei Kochprozessen in der Paper- und Pappeindustriebei der Verhüttung von Erzen u.dgl. geschah zur Verhinderung der Verluste an diesen suspendierten Materialien. Sie lassen sich in vielfältiger Weise wirtschaftlich nutzen. In vielen Fällen haben diese Systeme eine zweifache Funktion: sie gestatten nämlich die Rückgewinnung von wertvollen Produkten, die vorher verloren wurden und andererseits gestatten sie die Erfüllung von Vorschriften und Anforderungen hinsichtlich Umweltverschmutzung u.dgl.Foam flotation is used in many areas for which it was not originally intended. This extension of applicability resulted due to the economic efficiency compared to the previous process. The extraction of suspended solids in cooking processes in the paper and cardboard industry during smelting of ores and the like was done to prevent the loss of these suspended materials. They can be used economically in a variety of ways. In many cases have these systems have a twofold function: they allow the recovery of valuable products that were previously lost and on the other hand they allow compliance with regulations and requirements related to environmental pollution etc.
Flotation wird zur Abtrennung von organischen und anorganischen Stoffen und Gemischen aus einem flüssigen Medium angewandt. In den meisten, jedoch nicht in allen Fällen, ist das flüssige Medium Wasser. Die Anwendungsgebiete der Schaumflotation sind zahllos. Die Hauptgebiete sind Aufarbeitung von Abfällen, Verhüttung von Erzen, Gewinnung verschiedener Stoffe aus ihrer Umgebung u.dgl. Beim Aufarbeiten von Abfällen kann es sich um solche aus der Förderung von Ölen, um die Abwasserreinigung, um Pappe- und Papierherstellungssysteme, um Wäschenzur Entfernung von Stäuben, Flugasche u.dgl., zharnduelfnrbeitung von Abfällen von Fleisch und Nahrungsmittel. Bei der Erzverhüttung geht es um die Abtrennung der gewünschten Produkte von den unerwünschten, z.B. Kupferverhüttung und Kohleaufbereitung.Flotation is used to separate organic and inorganic substances and mixtures of a liquid medium are applied. Most of them, but not in all cases, the liquid medium is water. The areas of application of foam flotation are innumerable. The main areas are processing of waste, smelting of ores, Extraction of various substances from their environment and the like when processing waste it can be those from the pumping of oils to wastewater treatment in order to Cardboard and papermaking systems to remove dust, fly ash and laundry and the like, plastering of meat and food waste. In the Ore smelting is about the separation of the desired products from the undesired, e.g. copper smelting and coal processing.
Flotationsverfahren sind auch sehr geeignet bei der Ölrückgewinnung aus der Wasserflutung,aus Abwässern von Maschinen-und Automobilindustrie sowie von Wäschen, wie der Abscheidung von Flugstaub aus basischen sauerstoffblasenden Öfen, insbesondere Eisenoxidschwebstoffe aus den Hochofenabgasen, von Koksstäuben aus der Herstellung von Koks und der Stahlgowinnung, die sich alle in einem wäßrigen Waschmedium befinden.Flotation processes are also very suitable for oil recovery from water flooding, from sewage from machine and automotive industries as well as from Washes, such as the separation of fly ash from basic oxygen-blowing ovens, in particular iron oxide suspended matter from the blast furnace exhaust gases, from coke dust the production of coke and the steel mill, which are all in an aqueous Washing medium.
Die Schaumflctition findet ganz allgemein in speziellen Anlagen statt, die größtenteils auf dem gleichen Prinzip arbeiten (US-PS 2 446 655; 2 759 607; 2 994 432; 3 969 923; 3 785 490; 3 836 460; 3 842 004; 3 883 426; 3 884 803 und 28 323). Eines der weitest angewendeten Flotationssysteme ist unter der Bezeichnung "WEMCO" bekannt. Im11Bulletin Nr. F8-B2"der Firma Envirotech. Corporation werden WEMCO-Einheiten gezeigt, mit denen eine durch mechanische Einführung von Luft bewirkte Flotation zur Abscheidung von Feststoffen, Ölen und/oder organischen Substanzen aus großen Wasservolumina angegeben ist . Diese Anlagen bestehen aus vier Flotationszellen, jeweils ausgestattet mit einem niotorgetriebenen Selbstbelüftungssystem. Wird der Rotormechanismus in Gang gesetzt, so arbeitet er als Pumpe und drückt das Wasser durch einen "Dispenser" und erzeugt dabei ein Vakuum in dem Standrohr. Das Vakuum zieht Gas in das Standrohr und mischt es in das Abwasser.The foaming process takes place quite generally in special systems, most of which work on the same principle (US Pat. No. 2,446,655; 2,759,607; 2,994,432; 3,969,923; 3,785,490; 3,836,460; 3,842,004; 3,883,426; 3 884 803 and 28 323). One of the most widely used flotation systems is under the name "WEMCO" known. Im11 Bulletin No. F8-B2 "from Envirotech. Corporation WEMCO units shown with which one effected by mechanical introduction of air Flotation for the separation of solids, oils and / or organic substances is given from large volumes of water. These systems consist of four flotation cells, each equipped with a niotor-driven self-ventilation system. Will the When the rotor mechanism is set in motion, it works as a pump and pushes the water through a "dispenser" creating a vacuum in the standpipe. The vacuum draws gas into the standpipe and mixes it into the sewage.
Dieses Gas/Wasser-Gemisch gelangt durch den Dispenser mit hoher Geschwindigkeit unter Scherkraft, so daß das Gas kleine Blasen bildet. Die Schwebstoffe legen sich an die Gasblasen und steigen mit ihnen an die Oberfläche und ergeben einen dichten Scilaum, der ausgetragen wird mit Abschäumern und anschließend aufgearbeitet wird. Die meisten Systeme arbeiten ähnlich, wobei die Differenzen im allgemeinen nur bei der Schaumbildung liegen.This gas / water mixture passes through the dispenser at high speed under shear force so that the gas forms small bubbles. The suspended solids settle to the gas bubbles and rise with them to the surface and result in a dense one Scilaum, which is discharged with skimmers and then processed. Most systems work in a similar way, with the differences generally only at the foaming.
Das Verfahren wird häufig durch Chemikalien verbessert, die dem einlaufenden Strom in die Zelle zugesetzt erden.The process is often improved by adding chemicals to the incoming Ground current added to the cell.
Es wurde nun erfindungsgeniß festgestellt, wenn eine bestimmte Art von Polymeren dem Wasser enthaltend die Schwebstoffe vor oder während des Schaumflotation zugesetzt werden, die Wirksamkeit so weit sich verbessern läßt, daß die Schwebstoffe zu einem größeren Ausmaß gewonnen werten können. Die Polymeren, cìie man erfindungsgemäß dafür anwendet, sind in erster Linie solche, die die Einheit O-CH2-CH2 enthalten. Mit anderen Worten: Polyäthylenoxide.It has now been determined according to the invention when a certain species of polymers to the water containing the suspended solids before or during foam flotation are added, the effectiveness can be improved so far that the suspended matter to be able to judge gained to a greater extent. The polymers that can be used according to the invention uses for are primarily those that have the unit O-CH2-CH2 contain. In other words: polyethylene oxide.
Polyäthylenoxide unterschiedlicher Molekulargewichte sind ebenso wirksam für den erfindungsgemäßen Zweck wie Copolymere von Äthylenoxid mit einem geringen Anteil an anderen Monomeren wie Propylenoxid. Die einzige Bedingungen ist für das Polymer, daß es unter den in der Praxis eintretenden Bedingungen wasserlöslich ist. Diese Polymere sind nicht-ionogen. Die Zugabe geringer Anteile von kationischen oder anionischen Stoffen, die einpolymerisiert werdenn oder eine sonstige Zugabe derartiger Verbindungen, kann manchmal von Vorteil sein.Polyethylene oxides of different molecular weights are also effective for the purpose of the invention such as copolymers of ethylene oxide with a minor Share in other monomers such as propylene oxide. The only conditions are for that Polymer that it is water-soluble under the conditions occurring in practice. These polymers are non-ionic. The addition of small amounts of cationic or anionic substances that are polymerized or some other addition such connections can sometimes be beneficial.
Die erfindungsgemäß angewandten Polymeren sind im allgemeinen Handelsprodukte und werden durch Polymerisation von Alkylenoxiden nach üblichen Verfahren erhalten. Ein Handelsprodukt entspricht der Formel worin R ein Wasserstoffatom oder eine organische Gruppe sein kann. Jedenfalls haben bei hochpolymeren Stoffen die Endgruppen keinen oder nur einen sehr geringfügigen Einfluß auf Eigenschaften und Wirksamkeit. x kann 1000 bis 500 000 betragen. Die Molekulargewichte der erfindungsgemäß anzuwendenden Polymeren lannenzwischen etwa 44- 000 und 22 000 0001 vorzugsweise etwa 100 000 bis 10 000 OO01liegen. Wie oben erwähnt ist der begrenzende Faktor für das Molekulargewicht einiger Arten der Polymeren die Löslichkeit in Wasser.The polymers used according to the invention are generally commercial products and are obtained by polymerizing alkylene oxides by customary processes. A commercial product corresponds to the formula wherein R can be a hydrogen atom or an organic group. In any case, in the case of high-polymer substances, the end groups have no or only a very slight influence on properties and effectiveness. x can be 1,000 to 500,000. The molecular weights of the polymers to be used according to the invention are between about 44,000 and 22,000,0001, preferably about 100,000 to 10,000,000. As mentioned above, the limiting factor on the molecular weight of some types of polymers is their solubility in water.
Polyäthylenoxide sind über ihr gesamtes Molekulargewichtsbereich wasserlöslich, jedoch sind Mischpolymere mit beispielsweise Propylenoxid wasserlöslich abhängig vom Molekulargewicht.Polyethylene oxides are water-soluble over their entire molecular weight range, however, copolymers with, for example, propylene oxide are dependent on water-soluble on molecular weight.
Das Molekulargewicht und das Gewichtsverhältnis von Äthylenoxid zu den anderen Monomeren sind daher bei der Herstellung im Hinblick auf die Wasserlöslichkeit des Polymeren zu berücksichtigen. Die erfindungsgemäß angewandten Polymeren sind in relativ geringen Anteilen schon wirksam, so daß das erfindungsgemäße Verfahren außerordentlich wirtschaftlich ist. Zur Verbesserung der Schaumflotation reichen schon etwa 0,001 bis 100 ppm, vorzugsweise 0,01 bis 10 ppmlaus. Höhere Anteile sind wirksam, Jedoch unwirtschaftlich. Die jeweils anzuwendende Polymermenge hängt ab vom Flotationssystem, den herrschenden Verfahrensbedindungen, Art und Menge der Schwebstoffe und der Verweilzeiten. Die erforderlichen Konzentrationen können Jedoch leicht ermittelt werden.The molecular weight and weight ratio of ethylene oxide too the other monomers are therefore in the preparation with regard to the water solubility of the polymer must be taken into account. The polymers used according to the invention are already effective in relatively small proportions, so that the process according to the invention is extremely economical. Sufficient to improve froth flotation already about 0.001 to 100 ppm, preferably 0.01 to 10 ppm louse. Higher proportions are effective, but uneconomical. The amount of polymer to be used in each case depends the flotation system, the prevailing process conditions, the type and amount of Suspended solids and the residence times. The required concentrations can, however can be easily determined.
Um die Wirksamkeit des erfindungsgemäßen Verfahrens zu zeigen, wurden verschiedene Laboruntersuchungen durchgeführt. Die Verbesserung der Trennarbeit bei der Schaumflotation wurde an Wasser enthaltend verschiedene Arten von Schwebstoffen allein oder in Kombination mit Öl untersucht. Nach den Laboruntersuchungen wurden auch bereits Untersuchungen für großtechnische Trennvorgänge vorgenommen.In order to show the effectiveness of the method according to the invention, various laboratory tests carried out. The improvement of the separation work In the case of froth flotation, water containing various types of suspended solids was used studied alone or in combination with oil. According to the laboratory tests were Investigations for large-scale separation processes have also already been carried out.
Beispiel 1 Abscheidung von Koksstaub In einer Laboratoriumseinheit nach dem System lfEMC0 wurde die Wirksamkeit von Polyäthylenoxid auf die Abtrennung von Koksstaub aus dem wäßrigen Medium durch Schaumflotation ermittelt .Example 1 Separation of Coke Dust In a laboratory unit according to the system lfEMC0 the effectiveness of polyethylene oxide on the separation of coke dust from the aqueous medium determined by foam flotation.
Verfahrensbedingungen: 25 1 Wasser gemischt mit einem Mischer 1500 UpM 2,5 g Koksstaub: 60 °,0 44 /um; 40 % 74 /um'entsprechend 1000 ppm Koks in Suspension 6 /ul Heizöl Nr. 2 6 /ul Methylisobutylcarbinol als Schäumer Mischprogramm: 30 s nach Zugabe des Kokspulvers, 30 s nach Zugabe des Öls, 15 s Luft einrühren untettugabe von Methylisobutylcarbinol und dem erfindungsgemäßen Polymer, 4 min Abblasen (scrape) mi1;Luft (schäumen).Process conditions: 25 liters of water mixed with a mixer 1500 Rpm 2.5 g coke dust: 60 °, 0.44 µm; 40% 74 μm, corresponding to 1000 ppm coke in suspension 6th / ul heating oil No. 2 6 / ul methyl isobutylcarbinol as a foamer Mixing program: 30 s after Add the coke powder, stir in air 30 s after adding the oil, stir in air for 15 s of methyl isobutyl carbinol and the polymer according to the invention, 4 min blow-off (scrape) mi1; air (foaming).
Die Ergebnisse sind in der folgenden Tabelle 1 zusammengestellt.The results are compiled in Table 1 below.
Tabelle :
T a b e l l e 1
Beispiel 2 Um zu zeigen, daß die Verbesserung nicht einer speziellen Anlage zuzuschreiben ist, wurde in Abwandlung des Beispiels 1 ein Versuch durchgeführt in einer "Denver"-Flotationsanlage.Example 2 To show that the improvement is not a specific one Is to be attributed to the plant, a test was carried out in a modification of Example 1 in a "Denver" flotation facility.
Versuchsbedingungen: 4 1 Leitungswasser1 gemischt mit 1500 UpM 4 g Koksstaub: 60 9' 44 /um; 40 9' 74 /umlentsprechend 1000 ppm Koks 10 /ul Heizöl Nr. 2 10 ,um Methylisobuthylcarbinol Mischprogramm: 2 min ffir Koksstaub, 45 s ohne Luft nach Zugabe der Zusätze, 15 s mit Luft, 4 min Abschäumen mit Luft.Test conditions: 4 l of tap water1 mixed at 1500 rpm, 4 g Coke dust: 60 9 '44 µm; 40 9 '74 / equivalent to 1000 ppm coke 10 / ul heating oil no. 2 10 to methyl isobutyl carbinol mixing program: 2 min for coke dust, 45 s without Air after adding the additives, 15 s with air, 4 min skimming with air.
Tabelle 2: T a b e l l e 2 Mol Polymer ppm Schwebstoff Polymer ppm in Abwasser Vergleich - - 900 Polyäthylenoxid 4000000 0,1 300 Polyäthylenoxid 4000000 0,2 180 Polyäthylenoxid 200000 0,2 300 Polyäthylenoxid 600000 0,2 300 Polyäthylenoxid 600000 0,2 280 Polyäthylenoxid 300000 0,2 600 Polyäthylenoxid 5000000 0,2 180 Alle erfindungsgemäß angewandten Polymeren waren wirksam, woraus sich ergibt, daß die Wirkungssteigerung des Flotationsverfahrens nicht in der Anlage zu sehen ist.Table 2: T a b e l l e 2 moles of polymer ppm suspended matter Polymer ppm in wastewater comparison - - 900 polyethylene oxide 4,000,000 0.1 300 polyethylene oxide 4,000,000 0.2 180 polyethylene oxide 200,000 0.2 300 polyethylene oxide 600,000 0.2 300 polyethylene oxide 600,000 0.2 280 polyethylene oxide 300,000 0.2 600 polyethylene oxide 5,000,000 0.2 180 All The polymers used in the present invention were effective, from which it can be seen that the The increase in the effectiveness of the flotation process cannot be seen in the plant.
Beispiel 3 Es wurde eine weitere Versuchsreihe durchgeführt mit Koksstäuben in Abwandlung des Beispiels 1 und zwar mit besonders geringen Mengen im Vergleich gegeniiber Zusätzen, die üblicherweise angewandt werden. Das hier angewandte Polymer hatte ein Molekulargewicht von 4 000 000.Example 3 Another series of tests was carried out with coke dust as a modification of Example 1, with particularly small amounts in comparison compared to additives that are commonly used. The polymer used here had a molecular weight of 4,000,000.
Tabelle 3 Polymer ppp Schwebstoff ppm in Abwasser Vergleich - 900 Polyäthylenoxid 0,015 500 Polyäthylenoxid 0,045 375 Polyäthylenoxid 0,075 230 Polyätllylenoxid 0,15 190 Vergleichsprodukt 0,2 550 Vergleichsprodukt 0,5 400 Vergleichsprodukt 1,0 280 Daraus ergibt sich, daß das erfindungsgemäße Polymer selbst bei außerordentlich geringen Mengen hoch wirksam ist und als berächtlich wirksamer als die üblichen Produkte bezeichnet werden kann. Table 3 Polymer ppp suspended solids ppm in wastewater comparison - 900 Polyethylene oxide 0.015 500 polyethylene oxide 0.045 375 polyethylene oxide 0.075 230 polyethylene oxide 0.15 190 Comparative product 0.2 550 Comparative product 0.5 400 Comparative product 1.0 280 It follows that the polymer of the present invention is even extremely high in small amounts is highly effective and remarkably more effective than the usual Products can be designated.
Beispiel 4 Um die Wirksamkeit der Polymeren in WEMC0-Schaumflotationsanlagen zu zeigen, wurde ein Versuch in einer Fabrik in Pennsylvania durchgefiihr-t. Das zu reinigende wänrlge System kam aus der Wäsche der Koksofenabgase. Im allgemeinen wird der Flugkoks mit den Abgasen abgeblasen.Example 4 To the effectiveness of the polymers in WEMC0 foam flotation plants To show, an experiment was carried out in a factory in Pennsylvania. That The awkward system to be cleaned came from the scrubbing of the coke oven exhaust gases. In general the flying coke is blown off with the exhaust gases.
Vor dem Abblasen wurden die Koksstäube aus dem Abgas durch ein übliches Waschsystem ausgewaschen. In der in Rede stehenden Fabrik wurde das aus diesen Wäschan kommende Wasser in einer WEMC0 -Schaumflotationszelle aufbereitat zur Abtrennung der Stäube und Wiederverwendung von Wasser und Stäuben.Before being blown off, the coke dusts were removed from the exhaust gas through a conventional Wash system washed out. In the factory in question, that was what became of these laundry incoming water processed in a WEMC0 foam flotation cell for separation of dust and reuse of water and dust.
Tabelle 4 Tag erfindungsgemäße Polymer ppm Schwebstoffe Behandlung ppm in Gas 1 ohne - 800 1 mit 0,045 43 2 ohne ~ 164 2 mit 0,045 53 3 ohne ~ 350 3 mit 0,045 42 Das angewandte Polymer hatte ein ltolekulargewicht von 4 000 000. Table 4 Day polymer according to the invention ppm suspended solids treatment ppm in gas 1 without - 800 1 with 0.045 43 2 without ~ 164 2 with 0.045 53 3 without ~ 350 3 with 0.045 42 The polymer used had an oil molecular weight of 4,000,000.
Es wurden weitere Untersuchungen durchgeführt, um die Wirksamkeit des erfindungsgemciß angewandten Polymeren auf andere Schwebstoffe und Öl zu zeigen. Diese Untersuchungen wurden entweder im Produktionsgang mit einer chaumflotationseinheit durchgeführt oder es wurden Proben des zulaufenden Wassers genommen und diese Proben in Laboreinheiten unter sucht.More research was done to determine its effectiveness of the polymer used in the present invention to other particulate matter and oil. These investigations were either in the production process with a foam flotation unit performed or samples of the incoming water were taken and these samples examined in laboratory units.
Beispiel 5 Den Untersuchungen wurde ein Abwasser unterzogen, welches nicht nur verschiedene Arten von Schwebstoffen, sondern auch Öltröpfchen enthielt. Die Schwebstoffe bestanden aus Sand, Schmutz, Schlamm, Ton und verschiedenen organischen Produkten. Bei diesen Untersuchungen wurden Abwasserproben von der Stelle wo sie anfielen genommen, unmittelbar in das Laboratorium gebracht und in einer 'ZEMC0-Schaumflotationslaboratoriumsanlage untersucht. Das Rohwasser hatte einen Schwebstoffgehalt von 500 ppm und einen Ölgehalt von 140 ppm. Unter Verwendung von erfindungsgemäßen Polyäthylenoxiden mit einem Molekulargewicht von 4 000 000 in einer Menge von 0,3 ppm konnte der Schwebstoffgehalt auf 200 ppm und der Öl gehalt auf 10 ppm verringert werden. Daraus ergibt sich, daß die erfindungsgemäße Behandlung nicht nur wirksam ist, sondern den flandelsprodukten hinsichtlich Kosten-Leistungs-Vergleich überlegen.Example 5 The tests were carried out on waste water which contained not only various types of suspended matter, but also oil droplets. The suspended solids consisted of sand, dirt, mud, clay, and various organic substances Products. During these investigations, wastewater samples were taken from the place where they were were taken, brought directly to the laboratory and in a 'ZEMC0 foam flotation laboratory facility examined. The raw water had a suspended matter content of 500 ppm and an oil content of 140 ppm. Using polyethylene oxides according to the invention with a Molecular weight of 4,000,000 in an amount of 0.3 ppm could reduce the suspended matter content to 200 ppm and the oil content can be reduced to 10 ppm. This results in, that the treatment according to the invention is not only effective, but also the flandels products superior in terms of cost-performance comparison.
Beispiel 6 In Abwandlung des Beispiels 5 wurde ein Abwasser mit in etwa den gleichen Schwebstoffen, jedoch in geringerer Menge untersucht, nämlich mit einem Schwebstoffgehalt von 170 ppm und einem Ölgehalt von 100 ppm. Nach der erfindungsgemäßen Behandlung war der Schwebstoff nur mehr 150 ppm und der Ölgehalt 80 ppm.Example 6 In a modification of Example 5, wastewater with in about the same suspended solids, but examined in a smaller amount, namely with a suspended matter content of 170 ppm and an oil content of 100 ppm. After Treatment according to the invention, the suspended matter was only 150 ppm and the oil content 80 ppm.
Beispiel 7 In diesem Fall wurde ein Wasser enthaltend Flugasche der erfindungsgemäßen Schaumflotation zur Reinigung der aus den Abgaswäschen kommenden Trübe angewandt. Es ist bekannt, daß der Anteil an Flugasche,der normalerweise aus Kesselfeuerungen in die Atmosphire geht, sehr beträchtlich sein würde, außer wenn aufwendige Wäscher zur Anwendung gelangen. In diesen Systemen wird Wasser gegebenenfalls mit Zusätzen in die Abgase gesprüht, welches den Hauptanteil an Schwebstoffen niederschlägt. Dieses Wasser wird kontinuierlich umgepumpt und eingespritzt und wenn der Schwebstoffgehalt eine bestimmte Grenze erreicht hat, ein Volumen durch Scllaumflotation aufbereitet, woraufhin das Wasser wieder verwendet oder als Reinwasser ausgetragen werden kann. In dem Abwasser aus den Wäschern lag in erster Linie Flugasche als Schwebstoff und Öltröpfchen vor.Example 7 In this case, a water containing fly ash was used Foam flotation according to the invention for cleaning the coming from the exhaust gas scrubbing Applied cloudy. It is known that the proportion of fly ash that normally consists of Boiler firing goes into the atmosphere, very considerably be would, unless expensive scrubbers are used. In these systems If necessary, water with additives is sprayed into the exhaust gases, which is the main component precipitates on suspended matter. This water is continuously pumped around and injected and when the suspended matter content has reached a certain limit, a volume is prepared by flooding, after which the water is reused or can be discharged as pure water. Lying in the sewage from the scrubbers primarily fly ash as suspended matter and oil droplets.
Tabelle 5 Tag erfindungsgemäße MG Polymer Schwebstoffe Öl Behandlung ppm ppm ppm 1 rohes Wasch- - - 57,4 250 wasser 1 erfindungsgem. 4 000 000 0,225 40,0 250 1 Vergleichs- nicht 7,5 50,0 250 produkt bestimmt 2 rohes Wasch- - - 66,0 221 wasser 2 erfindungsgem. lJ 000 000 0,225 27,7 197 2 Vergleichs- nicht 7,5 42,6 215 produkt bestimmt 7,5 42 6 Diese Versuche in großtechnisc}lem Umfang ergaben zufriedenstellende Werte trotz der Tatsache, daß am ersten Tag praktisch keine Beeinfussung des Ölanteils festzustellen war. Table 5 Day MG polymer suspended solids oil treatment according to the invention ppm ppm ppm 1 raw washing - - 57.4 250 water 1 according to the invention. 4,000,000 0.225 40.0 250 1 comparative not 7.5 50.0 250 product determined 2 raw washing - - 66.0 221 water 2 according to the invention. lJ 000 000 0.225 27.7 197 2 comparative not 7.5 42.6 215 product determined 7.5 42 6 These tests on a large technical scale showed satisfactory values despite the fact that there was practically no influence on the first day the oil content could be determined.
Trotzdem ergibt sicll aus dieser Aufstellung die t)berlegen heit der erfindungsgemhßen l'olymeren.Nonetheless, this list shows the t) superiority of the l'olymers according to the invention.
Erfindungsgemäß lassen sich die in Rede stehenden Polymeren allein oder zusammen mit Lösungsmitteln, Stabilisatoi ren u.dgl. anwenden, insbesondere auch zur Verhüttung und/oder Konzentrierung von Erzen. Die in obigen Beispielen angewandten Polymeren wurden sämtliche in Form wäßriger Lösungen zugeführt.According to the invention, the polymers in question can be used alone or together with solvents, stabilizers and the like. Use, in particular also for smelting and / or concentrating ores. The ones in the examples above The polymers used were all supplied in the form of aqueous solutions.
Claims (4)