DE2636122A1 - Enamel for magnetic guides of electromagnet sheet - consisting of silicon, boron, aluminium, alkali, calcium and cobalt oxide(s) - Google Patents

Enamel for magnetic guides of electromagnet sheet - consisting of silicon, boron, aluminium, alkali, calcium and cobalt oxide(s)

Info

Publication number
DE2636122A1
DE2636122A1 DE19762636122 DE2636122A DE2636122A1 DE 2636122 A1 DE2636122 A1 DE 2636122A1 DE 19762636122 DE19762636122 DE 19762636122 DE 2636122 A DE2636122 A DE 2636122A DE 2636122 A1 DE2636122 A1 DE 2636122A1
Authority
DE
Germany
Prior art keywords
enamel
al2o3
sio2
weight
cao
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19762636122
Other languages
German (de)
Other versions
DE2636122C3 (en
DE2636122B2 (en
Inventor
Geb Strutschlova Portatschenko
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
STRUTSCHKOV ALEKSANDR ARKADJEVITSCH
Original Assignee
STRUTSCHKOV ALEKSANDR ARKADJEVITSCH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by STRUTSCHKOV ALEKSANDR ARKADJEVITSCH filed Critical STRUTSCHKOV ALEKSANDR ARKADJEVITSCH
Priority to DE19762636122 priority Critical patent/DE2636122C3/en
Publication of DE2636122A1 publication Critical patent/DE2636122A1/en
Publication of DE2636122B2 publication Critical patent/DE2636122B2/en
Application granted granted Critical
Publication of DE2636122C3 publication Critical patent/DE2636122C3/en
Expired legal-status Critical Current

Abstract

Enamel for magnetic guides of electromagnet sheet, consisting of SiO2, B2O3, Al2O3, R2O (in which R is an alkali metal), also contains CaO and Co2O3. It has the compsn. 36-48 (wt.)% SiO2, 25 30% B2O3, 7-12% Al2O3, 6-12% CaO, 7-12% R2O and 0.8-2.5% Co2O3. It can also contain 0.01-0.5% Fe2O3. Used in the electronics, radio and electrical industries. The enamel has high electrical insulating properties and high adhesion to sheet steel. It is suitable for use in the industrial scale. A typical enamel had compsn. 46.5% SiO2, 28.0% B2O3, 8.0% Al2O3, 7.0% CaO, 8.0% Na2O, 2.0% Co2O3 and 0.5% Fe2O3.

Description

Larisa Arkadjewna PortatschenkoLarisa Arkadyevna Portachenko

Aleksandr Arkadjewitsch Strutschkow Nowgrorod/UdSSR ENAIL FÜR MAGNETLEITER AUS ELEKTROMAGNETBLECH Die Erfindung betrifft Emails für Magnetleiter aus Stahl-(Elektromagnetblech) blech/. Die erwähnten Magnetleiter werden in der Elektronen-, radiotechnischen und elektrotechnischen Industrie verwendet.Aleksandr Arkadjewitsch Strutschkow Novgrorod / USSR ENAIL FOR MAGNETIC LADDER FROM ELECTROMAGNETIC SHEET The invention relates to enamels for magnetic conductors made of steel (electromagnetic sheet) sheet/. The mentioned magnetic conductors are used in the electronic, radio-technical and used in the electrotechnical industry.

Bekannt ist ein Email für Magnetleiter aus Stahlblech, bestehend aus SiO2, B2O3, Al2O3,TiO2, NiO, NaO, Fe2O3, CuO und ZnO, wobei das Komponentenverhältnis wie folgt ist (Gew.%): SiO2. . . . . . . . . . . . . . . . . . . 31- 33 B2O3. . . . . . . . . . . . . . . . . . . 24- 24,8 Al2O3. . . . . . . . . . . . . . . . . . . 21,3- 23 TiO2. . . . . . . . . . . . . . . . . . . 0,55-0,60 NiO. . . . . . . . . . . . . . . . . . . .2,6-2,7 Na2O. . . . . . . . . . . . . . . . . . . 10,8-11,2 Fe2O3. . . . . . . . . . . . . . . . . . bis 0,5 CuO. . . . . . . . . . . . . . . . . . . 1,6- 1,7 ZnO. . . . . . . . . . . . . . . . . . .2,1-2,7 (siehe Urheberschein der UdSSR Nr. 197120). An enamel for magnetic conductors made of sheet steel is known made of SiO2, B2O3, Al2O3, TiO2, NiO, NaO, Fe2O3, CuO and ZnO, with the component ratio is as follows (wt.%): SiO2. . . . . . . . . . . . . . . . . . . 31-33 B2O3. . . . . . . . . . . . . . . . . . . 24-24.8 Al2O3. . . . . . . . . . . . . . . . . . . 21.3-23 TiO2. . . . . . . . . . . . . . . . . . . 0.55-0.60 NiO. . . . . . . . . . . . . . . . . . . .2.6-2.7 Na2O. . . . . . . . . . . . . . . . . . . 10.8-11.2 Fe2O3. . . . . . . . . . . . . . . . . . up to 0.5 CuO. . . . . . . . . . . . . . . . . . . 1.6-1.7 ZnO. . . . . . . . . . . . . . . . . . .2.1-2.7 (please refer Copyright certificate of the USSR No. 197120).

Das bekannte Email enthält 21,3 bis 23 Gew.R hluminiumoxid. Die Einführung von Al2O3 in größeren Mengen in das Email mit einem System SiO2-B2O3-a2O führt zu einer starken Verringerung des spezifischen Widerstandes des Emails, was seinerseits eine Verschlechterung der elektromagnetischen Parameter der Magnetleiter zur Folge hat. Die Elektroisolationseigenschaften von Al2O3 entfalten sich nur in alkalifreien Emails. The well-known enamel contains 21.3 to 23% by weight of aluminum oxide. The introduction of Al2O3 in larger quantities in the enamel with a system SiO2-B2O3-a2O leads to a strong reduction in the resistivity of the enamel, which in turn result in a deterioration in the electromagnetic parameters of the magnetic conductors Has. The electrical insulation properties of Al2O3 unfold only in alkali-free Emails.

(Haftsubstanzen) Als Verkettllngsoxide/werden im bekannten Email NiO und CuO verwendet. Diese Oxide sind nicht wirksam genug, da sie keine feste Verbindung (Adhäsion) des Emails mit dem Stahl gewährleisten. Au2erdem konnen diese Oxide in einer Reihe von Bällen eine Verringerung der elektromagnetischen Parameter von Magnetleitern herbeiführen. (Adhesive substances) As chain oxides / are known in enamel NiO and CuO used. These oxides are not effective enough as they are not solid Ensure connection (adhesion) of the enamel with the steel. You can also use this Oxides in a number of balls reduce the electromagnetic parameters by magnetic conductors.

Das bekannte Email hat wegen der ihm eigenen nachteile kein industrielle Verwendung gefunden. The well-known enamel does not have an industrial one because of its inherent disadvantages Use found.

Die vorliegende Erfindung bezweckt die Beseitigung der erwähnten Nachteile. The present invention aims to obviate the aforementioned Disadvantage.

Der Erfindung wurde die Aufgabe zugrundegelegt, bei in ein Email , das SiO2, B2O3, Al203, R20 enthält, wo"R ein Alkalimetall ist, solche Komponenten einzuführen und ein derartiges Verhältnis der angegebenen Komponenten zu X wählen, daß das Email hohe Elektroisolationseigenschaften zur Verbesserung der elektromagnetischen Parameter der Magnetleiter auf. The invention was based on the object in an email containing SiO2, B2O3, Al203, R20 where "R is an alkali metal, such components to introduce and choose such a ratio of the specified components to X, that the enamel has high electrical insulation properties to improve the electromagnetic Parameters of the magnetic conductor.

sowie dem aufweist weist /eine hohe Adhäsion auf / Stahlblech / , um dadurch schen eine einen stark monolithi/ Magnetleiter zu gewinnen, und,großtechnische Verwendung garantiert. as well as has / has high adhesion / sheet steel /, in order to gain a strong monolithic / magnetic conductor, and, large-scale Usage guaranteed.

Erfindungsgemäß wurde die Aufgabe dadurch gelöst, daß das vorgeschlagene Email neben den oben erwähnten Komponenten ebenfolgendem falls CaO und Co2O3 enthält bei / Verhältnis der Komponenten im Email (in Gew.%): SiO2 0 0 0 0 0 0 0 0 . . . . . . . . . . 0 36- 48 B2O3. . . . . . . . . . . . . . . . . 25 - 30 Al2O3. . . . . . . . . . . . . . . . . 7 - 12 CaO.. . . . . . . . . . . . . . . . . . 6 - 12 R2O. . . . . . . . . . . . . . . . . . . 7 - 12 Co2O3. . . . . . . . . . . . . . . . . . 0,8 - 2,5 Das erfindungsgemäße Email kann auch als Zusatz Fe2O3 in einer Menge von 0,01- 0,5 Gew.% enthalten, das in die Zusammendie setzung des Emails durch / Ausgangsrohstoffe gelangt. According to the invention the object was achieved in that the proposed Email in addition to the above-mentioned components also the following if it contains CaO and Co2O3 at / ratio of the components in the enamel (in% by weight): SiO2 0 0 0 0 0 0 0 0. . . . . . . . . . 0 36-48 B2O3. . . . . . . . . . . . . . . . . 25 - 30 Al2O3. . . . . . . . . . . . . . . . . 7 - 12 CaO ... . . . . . . . . . . . . . . . . 6 - 12 R2O. . . . . . . . . . . . . . . . . . . 7 - 12 Co2O3. . . . . . . . . . . . . . . . . . 0.8-2.5 The enamel according to the invention can also be used as an additive Fe2O3 in one Amount of 0.01-0.5 wt.% Contain that in the composition of the enamel through / Raw materials reached.

Das Vorhandensein von Kalziumoxid und Kobaltoxid in der Zusammensetzung des erfindungsgemäßen Emails sichert eine hohe Adhäsion des Emails am Stahlblech. The presence of calcium oxide and cobalt oxide in the composition of the enamel according to the invention ensures high adhesion of the enamel to the steel sheet.

Dank dem oben angegebenenVerhältnis der Komponenten im Email werden die Elektroisolationseigenschaften des Emails bedeutend erhoht und damit auch die elektromagnetischen Parameter der Magnetleiter. Es verbessert sich die Adhäsion des Emails am Stahlblech und dadurch der Grad der monolithischen Einheit des Magnetleiters. Das Email findet weitgehend industrielle Anwendung bei der Produktion von Magnetleitern. Thanks to the above-mentioned ratio of components in the email the electrical insulation properties of the enamel are significantly increased and thus also the electromagnetic parameters of the magnetic conductor. The adhesion improves of the enamel on the sheet steel and thereby the degree of monolithic unity of the magnetic conductor. The enamel is widely used in industry in the production of magnetic conductors.

Das erfindungsgemäßr Email wird folgendermaßen hergestellt .. eine Zunächst wird / Beschickung zubereitet; dabei werden als Komponenten der Beschickung folgende Stoffe verwendet: 1) Quarzsand bzw. reines Siliziumdioxid; 2) Borsäure; 3) Tonerde bzw. reines Aluminiumoxid; 4) Kreide bzw. reines Kalziumkarbonat; 5) technisches bzw, reines Kobalt(II)- oder Kobalt (III)-oxid 6) Rohstoffe für die Komponente R20 a) Soda; b) Natronsalpeter; c) Kalisalpeter; d) Pottasche; e) Lithiumkarbonat. The enamel according to the invention is produced as follows First / charge is prepared; are used as components of the feed the following substances are used: 1) quartz sand or pure silicon dioxide; 2) boric acid; 3) alumina or pure aluminum oxide; 4) chalk or pure calcium carbonate; 5) technical or pure cobalt (II) or cobalt (III) oxide 6) raw materials for the Component R20 a) soda; b) sodium nitrate; c) Potash nitrate; d) potash; e) lithium carbonate.

Der Gehalt der Beschickung an Komponenten wird durch den Gehalt des Emails an Oxiden bestimmt. The component content of the feed is determined by the content of the Emails determined on oxides.

Die Komponenten der Beschickung werden dosiert, gemischs und in einem Drehofen bzw.Herdofen bei 1400- 1500°C bis zum volen Durchkochen gekocht. Das gekochte Emil fritet man, indem durch man es /ein Sieb auf Wasser gießt bzw. durch Walzen durchläßt. Weiterhin wird das Email in Form einer Fritte getrocknet, durch Trockenvermahlung in einer Schwingmühle bis zu einer Peinheit von 9o' Durchgang durch ein Sieb mit 10 000 Staschen/om2 gemahlen.Moglich ist auch eine Naßvermahlung der Fritte. The components of the feed are dosed, mixed and in one Rotary oven or hearth oven cooked at 1400--1500 ° C until it boils through. The cooked Emil is fried by pouring it / a sieve onto water or by rolling it lets through. Furthermore, the enamel is dried in the form of a frit by dry grinding in a vibrating mill up to a punit of 9o 'through a sieve with 10,000 pockets / om2 ground. Wet grinding of the frit is also possible.

Aus dem gemahlenen Email wird eine wäßrige Suspension mit einer Dichte von 1,4- 2 g/cm3 zubereitet. Daraufhin wird auf ein Stahlblechband ein Emailüberzug in Form einer wäßrigen Suspension aufgetragen. Die Überzugsstärke schwankt zwischen 8 bis 30 µm, je nach der Stärke des Bandes. Man befestigt den Überzug auf dem Stahlband durch Aufschmelzen bzw. Antrocknen0 Danach wird das Stahlband mit dem aufgetragenen Überzug zur Herstellung von Magnetleitern nach der bekannten Technologie verwendet. The ground enamel becomes an aqueous suspension with one Density of 1.4-2 g / cm3 prepared. An enamel coating is then placed on a sheet steel tape applied in the form of an aqueous suspension. The coating thickness varies between 8 to 30 µm, depending on the thickness of the tape. The cover is attached to the steel band by melting or drying0 Then the steel strip is applied with the Coating used for the production of magnetic conductors according to the known technology.

Zum besseren Verständnis der vorliegenden Erfindung werden nachfolgend Beispiel der Zusammensetzung von Ausgangs beschickung und Email sowie die technischen Daten des Emails und der Magnetleiter angeführt, bei deren Herstellung das erfindungsgemäße Email verwendet wurde. For a better understanding of the present invention, the following Example of the composition of the initial charge and enamel as well as the technical Data of the email and the magnetic conductor listed, in the manufacture of which the invention Email was used.

Beispiel 1 Zusammensetzung der Beschickung (Gew. teile): (bezogen auf 100 Gew.teile Email) Quarzsand . . . . . . . . . . . . . . 47,4 Borsäure. . . . . . . . . . . . . . . 51,3 Tonerde. . . . . . . . . . . . . . . . 8,36 Kreide . . . . . . . . . . . . . . . . 12,8 Soda. . . . . . . . . . . . . . . . . . 5,75 Natronsalpeter. . . . . . . . . . . . 14,4 Kobalt (III)-oxid. . . . . . . . . . . 2,05 142,06 Zusammensetzung des Emails (Gew.%) SiO2. . . . . . . . . . . . . 46,5 B2O3. . . . . . . . . . . . . 28,0 Al2O3. . . . . . . . . . . . . 8,0 CaO. . . . . . . . . . . . . . 7,0 Na20. . . . . . . . . . . . . 8,0 Co2O3. . . . . . . . . . . . . 2,0 Fe2O3. . . . . . . . . . . . . 0,5 700 Technische Daten des Emails und der Magnetleiter Linearer Ausdehnungskoeffizient des Emails (α), Grd-1...6,1.10@ (Wärmebeständigkeit) Wärmeresistenz/ Emails nach Douglas ( # ,T), °C........189 Dielektrische Konstant des Emails (#)..............6,46 Temperatur des vollständigen Auseinanderfließens der tropfen , °C.......................................860-880 (Leistungsverluste) spezifische Wattverluste/im Magnetleiter, W/kg: bei einer Schwingungsfrequenz von 400-1000 Hz ....14-15 bei einer Schwingungsfrequenz von 50 Hz ..........1,5-2,2 Die Adhäsionseigenschaften des Emails sind gut. Beim Biegen des Bandes aus Stahlblech mit Emailüberzug <splittert das Email um einen Dorn. mit einem Durchmesser von 10 mm <-> nicht ab. Beim Testen der Magnetleiter auf schlag festigkeit wurde kein Absplittern von Email vom Stahlband beobachtet; die Magnetleiter bleihen dabei vollständig monolitisch. Example 1 Composition of the charge (parts by weight): (based on on 100 parts by weight of enamel) quartz sand. . . . . . . . . . . . . . 47.4 boric acid. . . . . . . . . . . . . . . 51.3 alumina. . . . . . . . . . . . . . . . 8.36 chalk . . . . . . . . . . . . . . . . 12.8 soda. . . . . . . . . . . . . . . . . . 5.75 Sodium nitrate. . . . . . . . . . . . 14.4 cobalt (III) oxide. . . . . . . . . . . 2.05 142.06 Composition of the enamel (wt.%) SiO2. . . . . . . . . . . . . 46.5 B2O3. . . . . . . . . . . . . 28.0 Al2O3. . . . . . . . . . . . . 8.0 CaO. . . . . . . . . . . . . . 7.0 Na20. . . . . . . . . . . . . 8.0 Co2O3. . . . . . . . . . . . . 2.0 Fe2O3. . . . . . . . . . . . . 0.5 700 Technical data of the enamel and the magnetic conductor Linear expansion coefficient of the enamel (α), Grd-1 ... 6,1.10 @ (heat resistance) heat resistance / enamels according to Douglas (#, T), ° C ........ 189 Dielectric constant of the enamel (#) .............. 6.46 temperature the complete disintegration of the droplets, ° C ....................................... 860-880 (Power losses) Specific watt losses / in the magnetic conductor, W / kg: at one oscillation frequency from 400-1000 Hz .... 14-15 with an oscillation frequency of 50 Hz .......... 1.5-2.2 The adhesive properties of the enamel are good. When bending the strip of sheet steel with enamel coating <the enamel splinters around a thorn. with a diameter of 10 mm <-> not off. When testing the magnetic conductor for impact resistance no chipping of enamel from the steel strip observed; the magnetic conductors stick completely monolithic.

Beispiel 2 Zusammensetzung der Beschickung (Gew.teile) : (bezogen auf 100 Gew.teile Email) Quarzsand, gereinigt von Fe2O3. . . . . . . . . . . . 46,2 Borsäure. . . . . . . . . . . . . . . . . . . . . . . 51,31 Tonerde. . . . . . . . . . . . . . . . . . . . . . . . 8,49 Kreide. . . . . . . . . . . . . . . . . . . . . . . . 13,03 Natronsalpeter. . . . . . . . . . . . . . . . . . . . 13,71 Soda. . . . . . . . . . . . . . . . . . . . . . . . . 8,57 Kobalt(III)-oxid . . . . . . . . . . . . . . . . 2,2 143,51 Zusammensetzung des Emails (Gew.%): SiO2. . . . . . . . . . . . . . . . . . . . . . . . . 45,0 B2O3. . . . . . . . . . . . . . . . . . . . . . . . . 28,0 Al2O3. . . . . . . . . . . . . . . . . . . . . . . . 8,0 CaO. . . . . . . . . . . . . . . . . . . . . . . . . 7,0 Na2O. . . . . . . . . . . . . . . . . . . . . . . . . 10,0 Co2O3. . . . . . . . . . . . . . . . . . . . . . . . . 2,0 100 Technische Daten des Emails und der Magnetleiter: Linearer Ausdehnungskoeffizient des Emails (α), Grad-1. 7,1 10-6 Wärmeresistenz des Emails nach Douglas (# #), °C.........162 Dielektrische Konstante des Emails ( # ).................6,686 Temperatur des vollständigen Auseinanderfließens der Tropfen , °C.....................................860-880° Spezifische Wattverluste im Magnetleiter, W/kg: bei einer Schwingungsfrequenz von 400-1000 Hz ... 14 - 15 bei einer Schwingungsfrequenz von 50 Hz ......... 1,5-2,2. Example 2 Composition of the charge (parts by weight): (based on on 100 parts by weight of enamel) quartz sand, cleaned of Fe2O3. . . . . . . . . . . . 46.2 Boric acid. . . . . . . . . . . . . . . . . . . . . . . 51.31 clay. . . . . . . . . . . . . . . . . . . . . . . . 8.49 chalk. . . . . . . . . . . . . . . . . . . . . . . . 13.03 sodium nitrate. . . . . . . . . . . . . . . . . . . . 13.71 soda. . . . . . . . . . . . . . . . . . . . . . . . . 8.57 cobalt (III) oxide. . . . . . . . . . . . . . . . 2.2 143.51 Composition of the enamel (% by weight): SiO2. . . . . . . . . . . . . . . . . . . . . . . . . 45.0 B2O3. . . . . . . . . . . . . . . . . . . . . . . . . 28.0 Al2O3. . . . . . . . . . . . . . . . . . . . . . . . 8.0 CaO. . . . . . . . . . . . . . . . . . . . . . . . . 7.0 Na2O. . . . . . . . . . . . . . . . . . . . . . . . . 10.0 Co2O3. . . . . . . . . . . . . . . . . . . . . . . . . 2.0 100 Technical data of the enamel and the magnetic conductor: Linear expansion coefficient of the enamel (α), grade-1. 7.1 10-6 Heat resistance of enamel according to Douglas (# #), ° C ......... 162 Dielectric constant of the enamel (#) ................. 6,686 Temperature at which the drops flow apart completely, ° C ..................................... 860-880 ° Specific Watt losses in the magnetic conductor, W / kg: at an oscillation frequency of 400-1000 Hz ... 14 - 15 with an oscillation frequency of 50 Hz ......... 1.5-2.2.

der Das Email mit/ erwähnten Zusammensetzung verfügt über hohe Adhäsion am Band aus Stahlblech, analog dem Email im Beispiel 1. The enamel with / mentioned composition has high adhesion on a strip made of sheet steel, analogous to the enamel in example 1.

Beispiel 3 Zusammensetzung der Beschickung (Gew.teile): (bezogen auf 100 Gew.teile Email) Quarzsand, gereinigt von Fe2O3. . . . . . . . . . . . 44,0 Borsäure. . . . . . . . . . . . . . . . . . . . . . . 51,3 Tonerde. . . . . . . . . . . . . . . . . . . . . . . 8,36 Kreide. . . . . . . . . . . . . . . . . . . . . . . . 12,8 Natronsalpeter. . . . . . . . . . . . . . . . . . . . 10,96 Soda. . . . . . . . . . . . . . . . . . . . . . . . . 13,68 Kobalt(III)-oxid . . . . . . . . . . . . . . . . 2,05 143,15 Zusammensetzung des Emails (Gew.%): SiO2. . . . . . . . . . . . . . . . . . . . . . . . 43,0 B2O3. . . . . . . . . . . . . . . . . . . . . . . . 28,0 Al2O3. . . . . . . . . . . . . . . . . . . . . . . . 8,0 CaO. . . . . . . . . . . . . . . . . . . . . . . . . 7,0 Na2O. . . . . . . . . . . . . . . . . . . . . . . . 12,0 Co2O3. . . . . . . . . . . . . . . . . . . . . . . . 2,0 100 Technische Daten des Emails und der Magnetleiter: Linearer Ausdehnungskoeffizient des Emails (α), Grad-1 7,47x10-@ Wärmeresistenz des Emails nach Dougles (# T), °C........154 Dielektrische Konstante des Emails ( # )............6,961 Temperatur des vollständigen Auseinanderfließens der Tropfen , °C...................................860-870 t Spezifische Wattverluste im Magnetleier, W/kg: bei einer Schwingungsfrequenz von 400/1000 Hz, .... 14-16 der Das Email mit/erwähnten Zusammensetzung verfügt über hohe Adhäsion am Band aus Stahlblech, analog dem Email im Beispiel 1. Example 3 Composition of the charge (parts by weight): (based on on 100 parts by weight of enamel) quartz sand, cleaned of Fe2O3. . . . . . . . . . . . 44.0 Boric acid. . . . . . . . . . . . . . . . . . . . . . . 51.3 alumina. . . . . . . . . . . . . . . . . . . . . . . 8.36 chalk. . . . . . . . . . . . . . . . . . . . . . . . 12.8 sodium nitrate. . . . . . . . . . . . . . . . . . . . 10.96 soda. . . . . . . . . . . . . . . . . . . . . . . . . 13.68 cobalt (III) oxide. . . . . . . . . . . . . . . . 2.05 143.15 Composition of the enamel (% by weight): SiO2. . . . . . . . . . . . . . . . . . . . . . . . 43.0 B2O3. . . . . . . . . . . . . . . . . . . . . . . . 28.0 Al2O3. . . . . . . . . . . . . . . . . . . . . . . . 8.0 CaO. . . . . . . . . . . . . . . . . . . . . . . . . 7.0 Na2O. . . . . . . . . . . . . . . . . . . . . . . . 12.0 Co2O3. . . . . . . . . . . . . . . . . . . . . . . . 2.0 100 Technical data of the email and the magnetic conductor: Linear expansion coefficient of the enamel (α), degree-1 7.47x10- @ heat resistance of the email to Dougles (# T), ° C ........ 154 Dielectric constant of the email (#) ............ 6.961 Temperature at which the drops flow completely apart , ° C ................................... 860-870 t Specific watt losses in the magnetic lyre, W / kg: at a vibration frequency of 400/1000 Hz, .... 14-16 of the email with / mentioned Composition has high adhesion to the sheet steel tape, analogous to enamel in example 1.

Beispiel 4 Zusammensetzung der Beschickgung (Gew.teile): (bezogen auf 100 Gew.teile Email) Quarzsand, gereinigt von Fe2O3. . . . . . . . . . . 43,0 Borsäure. . . . . . . . . . . . . . . . . . . . . . 49,84 Tonerde. . . . . . . . . . . . . . . . . . . . . . . 8,0 Kreide. . . . . . . . . . . . . . . . . . . . . . ,.12,46 Pottasche. . . . . . . . . . . . . . . . . . . . . . 2,95 Soda. . . . . . . . . . . . . . . . . . . . . . . . 10,26 Natronsalpeter. . . . . . . . . . . . . . . . . . . 10,96 Kobalt (II)-oxid . . . . . . . . . . . . . . . . 1,82 139,29 Zusammensetzung des Emails (Gew.%): SiO2. . . . . . . . . . . . . . . . . . . . . . . . 43,0 B2O3. . . . . . . . . . . . . . . . . . . . . . . . 28,0 Al2O3. . . . . . . . . . . . . . . . . . . . . . . 8,0 CaO. . . . . . . . . . . . . . . . . . . . . . . . 7,0 K2O. . . . . . . . . . . . . . . . . . . . . . . . 2,0 Na2O. . . . . . . . . . . . . . . . . . . . . . . .10,0 Co2O3. . . . . . . . . . . . . . . . . . . . . . . 2,0 100 Technische Daten das Emails und der Magnetleiter: Linearer Ausdehnungskoeffizient des Emails (α), Grad-1... 7,61. Example 4 Composition of the charge (parts by weight): (based on on 100 parts by weight of enamel) quartz sand, cleaned of Fe2O3. . . . . . . . . . . 43.0 Boric acid. . . . . . . . . . . . . . . . . . . . . . 49.84 clay. . . . . . . . . . . . . . . . . . . . . . . 8.0 chalk. . . . . . . . . . . . . . . . . . . . . . , .12.46 potash. . . . . . . . . . . . . . . . . . . . . . 2.95 soda. . . . . . . . . . . . . . . . . . . . . . . . 10.26 sodium nitrate. . . . . . . . . . . . . . . . . . . 10.96 cobalt (II) oxide. . . . . . . . . . . . . . . . 1.82 139.29 Composition of the enamel (wt.%): SiO2. . . . . . . . . . . . . . . . . . . . . . . . 43.0 B2O3. . . . . . . . . . . . . . . . . . . . . . . . 28.0 Al2O3. . . . . . . . . . . . . . . . . . . . . . . 8.0 CaO. . . . . . . . . . . . . . . . . . . . . . . . 7.0 K2O. . . . . . . . . . . . . . . . . . . . . . . . 2.0 Na2O. . . . . . . . . . . . . . . . . . . . . . . .10.0 Co2O3. . . . . . . . . . . . . . . . . . . . . . . 2.0 100 Technical data of the email and the magnetic conductor: Linear Expansion coefficient of the enamel (α), degree-1 ... 7.61.

10-6 Wärmeresistenz des Emails nach Douglas ( # T), °C .........152 Temperatur des vollständigen Auseinanderfließens der Tropfen , °C.............................890-910 Dielektrische Konstante des Emails (#)...........7,0 Spezifische Wattverluste im Magnetleiter, W/kg: bei einer Schwingungsfrequenz von 50 Hz, W/kg .....1,5-2,2 der Das Email mit/erwähnten Zusammensetzung verfügt über hohe Adhäesion am Band aus Stahlblech, analog dem Email in Beispiel 1. 10-6 Heat resistance of the enamel according to Douglas (# T), ° C ......... 152 Temperature at which the drops flow apart completely, ° C ............................. 890-910 Dielectric constant of the enamel (#) ........... 7.0 Specific watt loss im Magnetic conductor, W / kg: at an oscillation frequency of 50 Hz, W / kg ..... 1.5-2.2 der The enamel with / mentioned composition has high adhesion to the tape Sheet steel, analogous to the enamel in example 1.

Beispiel 5 Zusammensetzung der Beschickgung (Gew.teile): (bezogen auf 100 Gew.teile Email) Quarzsand. . . . . . . . . . . . . . . . . . . . . 48,1 Borsäure. . . . . . . . . . . . . . . . . . . . . 53,4 Tonerde. . . . . . . . . . . . . . . . . . . . . . 7,0 Kreide. . . . . . . . . . . . . . . . . . . . . . 10,68 Soda. . . . . . . . . . . . . . . . . . . . . . . 6,48 Natronsalpeter. . . . . . . . . . . . . . . 8,22 Kobalt (III)-oxid . . . . . . . . . . . . 2,5 136,74 Zusammensetzung des Emails (Gew.%): SiO2. . . . . . . . . . . . . . . . . . . . . 47,49 B2O3. . . . . . . . . . . . . . . . . . . . . 30,0 Al2O3. . . . . . . . . . . . . . . . . . . . 7,0 CaO. . . . . . . . . . . . . . . . . . . . . . 6,0 Na2O. ....... . . . . . . . . . . . . . . . . 7,0 Co2O3. . . . . . . . . . . . . . . . . . . . . 2,5 Fe2O3. . . . . . . . . . . . . . . . . . . . . 0,01 100 Technische Daten des Emails und der Magnetleiter: Linearer Ausdehnungskoeffizient des Emails (α), Grad-1...5,9. Example 5 Composition of the charge (parts by weight): (based on on 100 parts by weight of enamel) quartz sand. . . . . . . . . . . . . . . . . . . . . 48.1 Boric acid. . . . . . . . . . . . . . . . . . . . . 53.4 alumina. . . . . . . . . . . . . . . . . . . . . . 7.0 chalk. . . . . . . . . . . . . . . . . . . . . . 10.68 soda. . . . . . . . . . . . . . . . . . . . . . . 6.48 Sodium nitrate. . . . . . . . . . . . . . . 8.22 cobalt (III) oxide. . . . . . . . . . . . 2.5 136.74 Composition of the enamel (% by weight): SiO2. . . . . . . . . . . . . . . . . . . . . 47.49 B2O3. . . . . . . . . . . . . . . . . . . . . 30.0 Al2O3. . . . . . . . . . . . . . . . . . . . 7.0 CaO. . . . . . . . . . . . . . . . . . . . . . 6.0 Na2O. ........ . . . . . . . . . . . . . . . 7.0 Co2O3. . . . . . . . . . . . . . . . . . . . . 2.5 Fe2O3. . . . . . . . . . . . . . . . . . . . . 0.01 100 Technical Data of the email and the magnetic conductor: linear expansion coefficient of the email (α), degree -1 ... 5.9.

10-6 Wärmeresistenz des Emails nach Douglas ( # T), °C.........194 Temperatur des vollständigen Auseinanderfließens der Tropfen , °C..................................920 Dielektrische Konstante des Emails ( 6 Spezifische Wattverluste im Magnetleiter bei einer Schwingungsfrequenz von 400-1000 Hz, W/kg...........15-18 Die Adhäsioneigenschaften des Emails sind gut. Beim Biegen des Bandes aus Stahlblech mit Emailüberzug<splittert das Email> um einen Dorn mit einem Durchmesser von 10 mmYnicht ab. 10-6 Heat resistance of the enamel according to Douglas (# T), ° C ......... 194 Temperature at which the drops flow apart completely, ° C .................................. 920 Dielectric constant of the enamel (6 specific watt losses in the magnetic conductor at a vibration frequency of 400-1000 Hz, W / kg ........... 15-18 The adhesive properties of the email are good. When bending the tape made of sheet steel with an enamel coating <splinters the enamel> around a mandrel with a diameter of 10 mm.

Beim Tasten der Magnetleiter auf Schlagfestigkeit wurde kein Absplittern des Emails vom Stahlband beobachtet. Die Magnetleiter bleiben dabei villständig monolitisch.When the magnetic conductors were tested for impact resistance, there was no chipping of the enamel observed from the steel band. The magnetic conductor stay while being villainous monolithic.

Beispiel 6 Zusammensetzung der Beschickgung (Gew.teile): (bezogen auf 100 Gew.teile Email) Quarzsand. . . . . . . . . . . . . . . . . . . 37,5 Borsäure. . . . . . . . . . . . . . . . . . . 46,28 Tonerde. . . . . . . . . . . . . . . . . . . . 12,0 Kreide. . . . . . . . . . . . . . . . . . . . 21,36 Natronsalpeter. . . . . . . . . . . . . . . . 10,96 Lithiumkarbonat. . . . . . . . . . . . . . . . 4,94 Soda. . . . . . . . . . . . . . . . . . . . . . 10,26 Kobalt (III)-oxid . . . . . . . . . . . . . 1,5 144,80 Zusammensetzung das Emails (Gew.%): SiO2. . . . . . . . . . . . . . . . . . . . . . 36,0 B2O3. . . . . . . . . . . . . . . . . . . . . . 26,0 Al2O3. . . . . . . . . . . . . . . . . . . . . 12,0 CaO. . . . . . . . . . . . . . . . . . . .. . . 12,0 Na2O. . . . . . . . . . . . . . . . . . . . . . 10,0 Li2O. . . . . . . . . . . . . . . . . . . . . . 2,0 Co2O3. . . . . . . . . . . . . . . . . . . . . . 1,5 Fe2O3. . . . . . . . . . . . . . . . . . . . . . 0,5 100 Technische Daten des Emails und der Magnetleiter: Linearer Ausdehnungskoeffizient des Emails (α), Grad-1...8,049.Example 6 Composition of the charge (parts by weight): (based on on 100 parts by weight of enamel) quartz sand. . . . . . . . . . . . . . . . . . . 37.5 boric acid. . . . . . . . . . . . . . . . . . . 46.28 clay. . . . . . . . . . . . . . . . . . . . 12.0 chalk. . . . . . . . . . . . . . . . . . . . 21,36 sodium nitrate. . . . . . . . . . . . . . . . 10.96 lithium carbonate. . . . . . . . . . . . . . . . 4.94 soda. . . . . . . . . . . . . . . . . . . . . . 10.26 cobalt (III) oxide. . . . . . . . . . . . . 1.5 144.80 Composition of the enamel (% by weight): SiO2. . . . . . . . . . . . . . . . . . . . . . 36.0 B2O3. . . . . . . . . . . . . . . . . . . . . . 26.0 Al2O3. . . . . . . . . . . . . . . . . . . . . 12.0 CaO. . . . . . . . . . . . . . . . . . . ... . 12.0 Na2O. . . . . . . . . . . . . . . . . . . . . . 10.0 Li2O. . . . . . . . . . . . . . . . . . . . . . 2.0 Co2O3. . . . . . . . . . . . . . . . . . . . . . 1.5 Fe2O3. . . . . . . . . . . . . . . . . . . . . . 0.5 100 Technical data of the enamel and the magnetic conductor: Linear expansion coefficient of enamel (α), grade-1 ... 8.049.

10-6 Wärmeresistenz des Emails nach Douglas ( # T), °C.........143 Dielektrische Konstante des Emails (#) .......... 7,36 Temperatur des vollständigen Auseinanderfließens der Tropfen in °C............................910 Spezifische Wattverluste im Magnetleiter bei einer Schwingungsfrequenz von 50 Hz, W/kg....................1,5-2,3. der Das Email mit/erwähnten Zusammensetzung verfügt über hohe Adhäsion am Band aus Stahlblech, analog dem Email in Beispiel 1. 10-6 Heat resistance of the enamel according to Douglas (# T), ° C ......... 143 Dielectric Constant of the email (#) .......... 7.36 Temperature of the complete disintegration the drop in ° C ............................ 910 Specific watt losses in the magnetic conductor at an oscillation frequency of 50 Hz, W / kg .................... 1.5-2.3. the that Enamel with / mentioned composition has high adhesion to the strip made of sheet steel, analogous to the email in example 1.

Beispiel 7 Zusammensetzung der Beschickgung (Gew.teile): (bezogen auf 100. Gew.teile Email): Quarzsand, gereinigt von Fe2O3. . . . . . . . . . . 46,2 Borsäure. . . . . . . . . . . . . . . . . . . . . . 49,84 Tonerde. . . . . . . . . . . . . . . . . . . . . . 8,0 Kreide. . . . . . . . . . . . . . . . . . . . . . . 12,49 Natronsalpeter. . . . . . . . . . . . . . . . . . . 13,71 Soda. . . . . . . . . . . . . . . . . . . . . . . . 8,57 Kobalt(III)-oxid . . . . . . . . . . . . . . . 0,8 139,61 Zusammensetzung des Emails (Gew.%): SiO2. . . . . . . . . . . . . . . . . . . 46,2 B2O3. . . . . . . . . . . . . . . . . . . 28,0 Al2O3. . . . . . . . . . . . . . . . . . 8,0 CaO. . . . . . . . . . . . . . . . . . . . 7,0 Na2O. . . . . . . . . . . . . . . . . . . 10,0 Co2O3. . . . . . . . . . . . . . . . . . . 0,8 100 Technische Daten des Emails und der Magnetleiter: Linearer Ausdehnungskoeffizient des Emails (α), Grad-1... 7,1. Example 7 Composition of the charge (parts by weight): (based on to 100 parts by weight of enamel): Quartz sand, cleaned of Fe2O3. . . . . . . . . . . 46.2 Boric acid. . . . . . . . . . . . . . . . . . . . . . 49.84 clay. . . . . . . . . . . . . . . . . . . . . . 8.0 chalk. . . . . . . . . . . . . . . . . . . . . . . 12.49 sodium nitrate. . . . . . . . . . . . . . . . . . . 13.71 soda. . . . . . . . . . . . . . . . . . . . . . . . 8.57 cobalt (III) oxide. . . . . . . . . . . . . . . 0.8 139.61 Composition of the enamel (% by weight): SiO2. . . . . . . . . . . . . . . . . . . 46.2 B2O3. . . . . . . . . . . . . . . . . . . 28.0 Al2O3. . . . . . . . . . . . . . . . . . 8.0 CaO. . . . . . . . . . . . . . . . . . . . 7.0 Na2O. . . . . . . . . . . . . . . . . . . 10.0 Co2O3. . . . . . . . . . . . . . . . . . . 0.8 100 Technical data of the email and the magnetic conductor: Linear expansion coefficient of the enamel (α), degree-1 ... 7.1.

10-6 Wärmeresistenz des Emails nach Douglas ( # T), °C.........162 Temperatur des vollständigen Auseinanderfließens der Tropfen in OC................. ....860-880 Dielektrische Konstante des Emails ( £ ) 6,686 Spezifische Wattverluste im Magnetleiter, W/kg: bei einer Schwingungsfrequenz von 400-1000 Hz .... 14-17 bei einer Schwingungsfrequenz von 50 Hz...........1,5-2,2 der Das Email mit/ erwähnten Zusammensetzung verfügt über hohe Adhäsion am Band aus Stahlblech, analog dem Email in Beispiel 1. 10-6 Heat resistance of the enamel according to Douglas (# T), ° C ......... 162 Temperature of the complete dissolution of the droplets in OC ................. .... 860-880 Dielectric constant of enamel (£) 6,686 Specific watt losses in the magnetic conductor, W / kg: at an oscillation frequency of 400-1000 Hz .... 14-17 at an oscillation frequency of 50 Hz ........... 1.5-2.2 of the email mentioned with / Composition has high adhesion to the sheet steel tape, analogous to enamel in example 1.

Claims (2)

PATENTANSPRÜCHE Elektromag-1. Email für Magnetleiter aus / netblech, bestehend aus bei SiO2, B2O3, Al2O3, R2O, wo/ R ein Alkalimetall ist, d a d u r c h g e k e n n ze i c h n e t ,daß es ebenfalls CaO und Co203 enthält, wobei das Yerhältnis der Komponenten im Email (in Gew.% folgendes ist: SiO2. . . . . . . . . . . . . . . 36- 48 B2O3. . . . . . . . . . . . . . . 25- 30 Al2O3. . . . . . . . . . . . . . 7- 12 CaO. . . . . . . . . . . . . . . . 6- 12 R2O. . . . . . . . . . . . . . . . 7- 12 Co2O3. . . . . . . . . . . . . . . 0,8- 2,5. PATENT CLAIMS Elektromag-1. Enamel for magnetic conductors made of / net sheet metal, consisting of SiO2, B2O3, Al2O3, R2O, where / R is an alkali metal, d a d u r c h g e k e n n n n n e t that it also contains CaO and Co203, whereby the The ratio of the components in the enamel (in% by weight the following is: SiO2......... . . . . . . . 36-48 B2O3. . . . . . . . . . . . . . . 25-30 Al2O3. . . . . . . . . . . . . . 7-12 CaO. . . . . . . . . . . . . . . . 6- 12 R2O. . . . . . . . . . . . . . . . 7-12 Co2O3. . . . . . . . . . . . . . . 0.8-2.5. 2. Email nach Anspruch 1, d a d u r c h g e k e n n -z e i c h n e t ,daß es ebenfalls Fe2O3 in einer Menge von 0,01- 0,5 Gew.% enthält. 2. Email according to claim 1, d a d u r c h g e k e n n -z e i c h n e t that it also contains Fe2O3 in an amount of 0.01-0.5% by weight.
DE19762636122 1976-08-11 1976-08-11 Enamel of the system SiO ↓ 2 ↓ B ↓ 2 ↓ O ↓ 3 ↓ Al ↓ 2 ↓ R ↓ 2 ↓ O, where R is an alkali metal, for magnetic conductors made of electromagnetic sheet metal Expired DE2636122C3 (en)