DE2620824C3 - Binder for the production of building materials to be hardened in an autoclave and a process for its extraction - Google Patents
Binder for the production of building materials to be hardened in an autoclave and a process for its extractionInfo
- Publication number
- DE2620824C3 DE2620824C3 DE2620824A DE2620824A DE2620824C3 DE 2620824 C3 DE2620824 C3 DE 2620824C3 DE 2620824 A DE2620824 A DE 2620824A DE 2620824 A DE2620824 A DE 2620824A DE 2620824 C3 DE2620824 C3 DE 2620824C3
- Authority
- DE
- Germany
- Prior art keywords
- binder
- production
- strength
- cao
- hardened
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
2. Verfahren zur Gewinnung von Bindemittel nach Anspruch 1, dadurch gekennzeichnet, daß ails Ausgangsrohstoff bei einer Temperatur von 700—8500C thermisch behandelter Destillierschlamm und Quarzsand verwendet werden, die in einem Verhältnis von-^j-< 0,51 genommen und zusammen oder einzeln bis zu einer spezifischen Oberfläche von 2000—5000 cmVg gemahlen werden. 2. A method for obtaining binder according to claim 1, characterized in that all the starting raw material thermally treated distillation sludge and quartz sand are used at a temperature of 700-850 0 C, which are taken in a ratio of- ^ j- <0.51 and put together or individually ground to a specific surface area of 2000-5000 cmVg.
Die vorliegende Erfindung bezieht sich auf ein Bindemittel zur Herstellung von Baumaterialien die im Autoklaven gehärtet werden, dessen Zusammensetzung es ermöglicht, verschiedenen Baumaterialien hoher Festigkeit und mit minimalen Aufwendungen herzustellen. The present invention relates to a binder for the production of building materials in the Autoclaves are cured, the composition of which allows different building materials to be cured To produce strength and with minimal effort.
Die Erfindung kann zur Herstellung von Schwer- und Leichtbeton, von Schaumbeton, Silikatziegel sowie von Putz- und Mauermörtel, vorzugsweise für Industriebau Wohnungs- und öffentliches Bauwesen eingesetzt werden.The invention can be used for the production of heavy and lightweight concrete, foam concrete, silica brick and of Plastering mortar and masonry mortar, preferably used for industrial construction, residential and public construction will.
Gegenwärtig sind verschiedene Bindemittel wie: Gips, Kalk und Zement bekannt, die in Abhängigkeit von Erhärtungsbedingungen in zwei Gruppen aufgeteilt werden: in Luftabbinder und hydraulische Bindemittel.At present, various binders such as: plaster of paris, lime and cement are known which are dependent of hardening conditions can be divided into two groups: air binders and hydraulic binders.
Besonders gute Aussichten bieten hydraulische Bindemittel, die ein breites Anwendungsgebiet haben. Hydraulische Bindemittel gehören zu den zusammengesetzten Stoffen, deren Grundlage die Oxyde CaO, SiO 2, Al2O3, Fe2O3 bilden und die in verschiedenen Verfahren gewonnen werden können. Eines der Verfahren ist ein Verfahren zur Gewinnung von Bindemittel aus Abfällen der Sodaproduktion. Die Abfälle der Sodaproduktion, die den festen Rückstand von Destillierschlamrn darstellen, die CaO, SiO2, AI2O3, Fe2O3, MgO, CaCO1, CaSO4 enthalten, werden einer Wärmebehandlung be:i einer Temperatur von 850—1500°C unterzogen. Dabei werden die Abfälle der Sodaproduktion mit Beimengungen von anorganischen Zusatzmitteln genommen. Als Zusatzmittel können Ton, Kalk, Siliziumoxid, Magnesiumoxid. Manganoxid und Eisenoxid verwendet werden. Nach der Wärmebehandlung von Destillierschlamm gemäß bekannter Technologie zur Gewinnung von Zementklinker erhält man ein Bindemittel, das für die Herstellung von Mörtel und Beton im Bauwesen verwendet werden kann (s. DDR-Patentschrift Nr. 79 684).Hydraulic binders, which have a wide range of applications, offer particularly good prospects. Hydraulic binders belong to the composite materials, the basis of which are the oxides CaO, SiO 2, Al 2 O 3 , Fe 2 O 3 and which can be obtained in various processes. One of the processes is a process for obtaining binding agents from waste from soda production. The waste from soda production, which is the solid residue of distillation sludge containing CaO, SiO 2 , Al 2 O 3 , Fe 2 O 3 , MgO, CaCO 1 , CaSO 4, is heat treated at a temperature of 850-1500 ° C subjected. The waste from soda production with admixtures of inorganic additives is removed. As additives can clay, lime, silicon oxide, magnesium oxide. Manganese oxide and iron oxide can be used. After the heat treatment of distillation sludge according to known technology for the production of cement clinker, a binder is obtained which can be used for the production of mortar and concrete in construction (see GDR patent specification No. 79,684).
Infolge der Unbeständigkeit der chemischen Zusammensetzung des festen Rückstandes der Abfälle derAs a result of the instability of the chemical composition of the solid residue of the waste
ίο Sodaproduktion ist es jedoch äußerst kompliziert, die Menge und den prozentualen Gehalt der einzuführenden Zusatzmittel zu variieren.However, ίο making soda is extremely complicated that To vary the amount and percentage of additives to be introduced.
Der Prozeß der Bildung von Aluminaten, Aluminatferriten sowie Trikalzium- und Bikalziumsilikaten ist außerdem bei Temperaturen nicht unterhalb 13000C möglich. Zu gleicher Zeit kommt bei einer Temperatur von 1000° C und darüber hinaus eine starke Zersetzung von CaCl2 und NaCl zustande, die im festen Rückstand bis 8 Gew.-% enthalten sind. Die entstehenden Chloride als Cl2 und HCl werden mit Rauchgasen herausgetragen und verunreinigen die Atmosphäre.The process of formation of aluminates, and tricalcium Aluminatferriten and Bikalziumsilikaten is also possible at temperatures not lower than 1300 0 C. At the same time, at a temperature of 1000 ° C. and beyond, there is strong decomposition of CaCl 2 and NaCl, which are contained in the solid residue up to 8% by weight. The resulting chlorides as Cl 2 and HCl are carried out with flue gases and pollute the atmosphere.
Das Vorhandensein stark basischer Kalziumaluminate und Tetrr.kalziumaluminatferrite in diesem Bindemittel schränkt seine Anwendung zur Herstellung von Betonen ein, die in Sulfatmedium genutzt werden.The presence of strongly basic calcium aluminates and tetra calcium aluminate ferrites in this binder restricts its use in the manufacture of concretes that are used in sulphate medium.
Das Spülen des festen Rückstandes zwecks Entfernung von Chloriden verkompliziert den Prozeß der Gewinnung von Bindemitteln aus den Abfällen der Sodaproduktion und macht denselben unwirtschaftlich.Rinsing the solid residue to remove chlorides complicates the process of Extraction of binding agents from the waste from soda production and makes it uneconomical.
jo Bei einer Brenntemperatur von 850— 13000C gemäß dieser Technologie entstehen praktisch keine hochbasischen Kalziumaluminate und Kalziumsiiikate. Deshalb weist das Bindemitte! äußerst niedrige Festigkeitseigenschaften auf und Erzeugnisse auf seiner Grundlage sind nicht wasserbeständig.jo virtually no highly basic calcium aluminates and Kalziumsiiikate In an internal temperature of 850- 1300 0 C in accordance with this technology. That is why the binder has! extremely low strength properties and products based on it are not water resistant.
Die zur Zeit bekannten Verfahren sichern nicht eine wirtschaftliche und rationelle Verarbeitung von Abfällen
der Sodaproduktion. Die Ursache liegt in hohen Kosten der Vorbereitungsarbeiten, da aus den Abfällen
Chloride ausgespült werden müssen und die Aufwendungen für Zusatzmittel sich als sehr hoch erweisen. Die
Gewinnung eines Bindemittels ist außerdem mit einem hohen Energieverbrauch verbunden.
Der Erfindung liegt die Aufgabe zugrunde, ein Bindemittel zu entwickeln, dessen Zusammensetzung
die Herstellung von im Autoklaven zu härtenden Baumaterialien gewährleistet, die hohe Fastigkeitsparameter,
Wasserbeständigkeit und Sulfatbeständigkeit aufweisen und deren Herstellung mit minimalenThe currently known methods do not ensure an economical and rational processing of waste from soda production. The cause lies in the high costs of the preparatory work, since chlorides have to be rinsed out of the waste and the costs for additives turn out to be very high. The production of a binding agent is also associated with high energy consumption.
The invention is based on the object of developing a binder, the composition of which ensures the production of building materials to be cured in the autoclave, which have high fastness parameters, water resistance and sulfate resistance and whose production is minimal
so Aufwendungen verbunden ist.so expenses is associated.
Diese Aufgabe wird dadurch gelöst, daß das Bindemittel zur Herstellung von im Autoklaven zu härtenden Baumaterialien auf der Grundlage von Abfällen der Sodaproduktion, die CaO1 SiO2, Ai2O3, Fe2O3, MgO, CaCO3, CaSO4 enthalten, erfindungsgemäß auch bis zu 2 Gew.-% CaCI2 und NaCl-Spuren enthält und die übrigen Komponenten in folgenden Mengen (Gew.-%) vertreten sind:This object is achieved in that the binder for the production of building materials to be hardened in the autoclave on the basis of waste from soda production, which contain CaO 1 SiO 2 , Al 2 O 3 , Fe 2 O 3 , MgO, CaCO 3 , CaSO 4, according to the invention also contains up to 2% by weight of CaCl 2 and traces of NaCl and the other components are represented in the following amounts (% by weight):
Zweckmäßigerweise ist das Bindemittel unter Verwendung von thermisch bei einer Temperatur von 700 bis 8500C behandeltem Destillierschlamm und Quarzsand, als Ausgangsrohstoffe, die in einem Verhältnis von -j^j-< 0,51 genommen werden, und semeinsam oder einzeln bis zu einer spezifischen Oberfläche von 2000—5000 cm2/g zermahlen werden, zu gewinnen.Conveniently, the binding agent using heat treated at a temperature of 700-850 0 C Destillierschlamm and quartz sand, as the starting raw materials, which are taken in a ratio of j ^ j <0.51, and semeinsam or individually up to a specific Surface areas of 2000-5000 cm 2 / g are ground to obtain.
Nachstehend wird die Erfindung anhand der Beschreibung fier Durchführung des vorgeschlagenen Verfahrens erläutertIn the following, the invention will be described based on the description fier implementation of the proposed method explained
Der feste Rückstand der Abfälle der Sodaproduktion (Destillierschlamm) wird bei einer Temperatur von 700—8500C gebrannt, wobei durch Entsäuerung von CaCC<3 daraus mindestens 30% aktives CaO gewonnen werden.The solid residue of the waste from the production of soda ash (Destillierschlamm) is fired at a temperature of 700-850 0 C, wherein by acidification of CaCO <3 obtained from at least 30% active CaO.
In der Tabelle 1 ist der Gehalt an aktivem CaO im Brennprodukt (im Destillierschlamm) in Abhängigkeit von der Temperatur aufgeführtIn Table 1, the content of active CaO in the combustion product (in the distillation sludge) is dependent listed on the temperature
2020th
Brenntemperatur,
1CFiring temperature,
1 C
Gehalt an aktivem CaO im
gebrannten Rückstand, %Active CaO content in
burned residue,%
700
800
850700
800
850
30,5
35,5
40,530.5
35.5
40.5
JC)JC)
Unter aktivem CaO versteht man das in nicht gebundener Form vorhandene CaO, das eine hohe Löschgeschwindigkeit aufweistActive CaO is understood to be the CaO present in unbound form, which is high Has erase speed
Der gebrannte Destillierschlamm wird mit einer r> kieselerdehaltigen Komponente (Quarzsand) in bestimmten Verhältnissen vermischt Diese Verhältnisse werden dui.ii dis Bedingungen der Erzielung einer maximalen Festigkeit des erhärteten Steines und der vorgegebenen Phasenzusammensetzung festgelegt.The burned distillation sludge is made with a component containing silica (quartz sand) in certain Mixed conditions These conditions are dui.ii dis conditions for the achievement of a maximum strength of the hardened stone and the specified phase composition.
Wie es aus der in dieser Beschreibung vorgeschlagenen graphischen Darstellung (Fig. 1) zu ersehen ist, entspricht dieser Bedingung im Gemisch das Molverhältnis des aktiven CaO und SiO2, das gleich S"''" < 0,51As can be seen from the graphic representation proposed in this description (FIG. 1), the molar ratio of the active CaO and SiO 2 in the mixture corresponds to this condition, which is equal to S "″"<0.51
ist.
In der graphischen Darstellung ist der Einfluß desis.
The graph shows the influence of the
Molverhältnisses von J^ im Gemisch auf die Druckfestigkeit abgebildet Die Abszissenachse der graphischen Darstellung istMolar ratio of J ^ in the mixture mapped to compressive strength. The axis of abscissas of the graph is
das Molverhältnis =i_. ;the molar ratio = i_. ;
die Ordinatenachse der graphischen Darstellung ist die Druckfestigkeit R ( ς^\\the ordinate axis of the graph is the compressive strength R ( ς ^ \\
Kurve 1 zeigt die Abhängigkeit der Festigkeit der Festigkeit von dem Molverhältnis ^^ bei einem GehaltCurve 1 shows the dependence of the strength of the strength on the molar ratio ^^ at a content
des Brennproduktes an aktivem CaO von 40,5%. toof the combustion product of active CaO of 40.5%. to
Kurve II zeigt die Abhängigkeit der Festigkeit vonCurve II shows the strength as a function of
OtOOtO
dem Molverhältnis „.' beim Gehalt des Brennproduktes
an aktivem CaO von 35,5%.
Kurve HI zeigt die Abhängigkeit der Festigkeit von br>the molar ratio "." with active CaO content of 35.5% in the firing product.
Curve HI shows the dependence of the strength on b r >
dem Molverhältnis sj'() beim Gehalt des Brennproduktes an aktivem CaO von 30,5%. Beim vorgegebenen Komponentenverhältnis unter Bedingungen der hydrothermalen Behandlung des Gemisches entstehen vorzugsweise schwachbasische Kalziumhydrosilikate, die hohe Fesügkeitseigenschaften und eine Wasser- und Sulfatbeständigkeit des erhärteten Steines verursachen.the molar ratio sj ' () for the active CaO content of the combustion product of 30.5%. With the specified component ratio under the conditions of hydrothermal treatment of the mixture, weakly basic calcium hydrosilicates are preferably formed, which cause high adhesion properties and water and sulfate resistance of the hardened stone.
Der vorbereitete Rohstoff wird zusammen oder getrennt bis zur spezifischen Oberfläche von 2000— 5000 cm2/g gemahlen. Das auf diese Weise zubereitete Rohstoffgemisch stellt ein Bindemittel für Autoklaverhärtung dar. Infolge einer feinen Zerkleinerung der Komponenten vergrößert sich ihre Reaktionsfläche, was zur Steigerung der Geschwindigkeit der Entstehung von Neubildungen in Form von schwachbasischen Kalziumhydrosilikaten im Prozeß der nachfolgenden hydrothermalen Behandlung des Bindemittels und der Erzeugnisse auf seiner Grundlage führtThe prepared raw material is ground together or separately to a specific surface area of 2000-5000 cm 2 / g. The raw material mixture prepared in this way represents a binding agent for autoclave hardening. As a result of the fine comminution of the components, their reaction surface increases, which increases the speed of the formation of new formations in the form of weakly basic calcium hydrosilicates in the process of the subsequent hydrothermal treatment of the binding agent and the products its basis
Die hydrothermale Behandlung erfolgt im Medium des gesättigten Dampfes bei einer Temperatur von 150—175°C, wodurch mikrokristallines Gel folgender Zusammensetzung C-S-H (I) und Tobermorit (II A") entstehen, die eine maximale mechanische Festigkeit des hergestellten Materials bewirken.The hydrothermal treatment takes place in the medium of saturated steam at a temperature of 150-175 ° C, resulting in the following microcrystalline gel Composition C-S-H (I) and tobermorite (II A ") arise, which bring about a maximum mechanical strength of the material produced.
Die im Bindemittel vorhandenen Chloride werden in schwerlöslichen Verbindungen gebunden, die eine zusätzliche Steigerung der Festigkeit sichern.The chlorides present in the binder are bound in poorly soluble compounds, which one ensure an additional increase in strength.
Durch das vorgeschlagene Verfahren zur Gewinnung des Bindemittels wird der Energieverbrauch für den Brennprozeß stark verringert und eine Verunreinigung der Atmosphäre der Umwelt ausgeschlossen.The proposed method for obtaining the binder, the energy consumption for the The burning process is greatly reduced and the atmosphere of the environment is not polluted.
Die Technologie der Gewinnung des vorgeschlagenen Bindemittels ist einfach genug, da sie lediglich zwei Arbeitsgänge enthält: Brennen im vorgegebenen Temperaturenbereich und gemeinsames oder getrenntes Mahlen.The technology of obtaining the proposed binder is simple enough as it only has two Operations include: firing in the specified temperature range and joint or separate Grind.
Weitere Vorteile der Erfindung werden aus der nachfolgenden konkreten Beschreibung der Beispiele der Gewinnung eines Bindemittels auf der Grundlage der Abfälle der Sodaproduktion gemäß dem vorgeschlagenen Verfahren ersichtlich.Further advantages of the invention will become apparent from the following specific description of the examples the recovery of a binder based on the waste from soda production according to the proposed one Process evident.
Die Abfälle der Sodaproduktion (Destillierschlamm) wurden bei einer Temperatur von 8500C gebrannt. Der Gehalt des Brennprodukts an aktivem CaO betrug 40,5%.The waste from the production of soda ash (Destillierschlamm) were fired at a temperature of 850 0 C. The active CaO content of the firing product was 40.5%.
Danach wurde der gebrannte. Destillierschlamm und der Quarzsand getrennt bis üu einer spezifischen Oberfläche von 5000 cm2/g gemahlen. Die gewonnenen Komponenten wurden bei einem Verhältnis vonAfter that, the burned one became. Distillation sludge and quartz sand are ground separately to a specific surface area of 5000 cm 2 / g. The components obtained were at a ratio of
aktivem gj^ = 0,51 dosiert und vermischt Es fiel ein Bindemittel folgender chemischer Zusammensetzung an:active gj ^ = 0.51 dosed and mixed It occurred Binding agent of the following chemical composition:
CaO SiO2 Al2O3 Fe2O3 MgO SO3" 30,08 50,80 3,16 1,60 2,90 2,20CaO SiO 2 Al 2 O 3 Fe 2 O 3 MgO SO 3 "30.08 50.80 3.16 1.60 2.90 2.20
übrige Beimengungen Cl"other admixtures Cl "
R2OR 2 O
4,524.52
1,101.10
Bei dieser Brenntemperatur erfolgt eine vollständige Entsäuerung von CaCO3, deshalb weist das Bindemittel eine maximale Festigkeit aiii.At this firing temperature, CaCO 3 is completely deacidified, which is why the binder has a maximum strength aiii.
Die Abfälle der Sodaproduktion (Destillierschlamm) wurden bei einer Temperatur von 800"C gebrannt. Der Gehalt des Brennstoffes an aktivem CaO betrug 35,5%.The waste from soda production (distillation sludge) was burned at a temperature of 800 "C. The Active CaO content of the fuel was 35.5%.
Der gebrannte Desiiliierschlamm und der Quarzsand wurden bis zur spezifischen Oberfläche 3000cm2/g gemahlen und danach bei einem Verhältnis von aktivemThe burned desilatory sludge and the quartz sand were ground to a specific surface area of 3000 cm 2 / g and then at a ratio of active
SK Γ = °'60 vermiscnt· Es f'el ein Bindemittel folgender chemischer Zusammensetzung an:SK Γ = ° '60 mixed-up There is a binding agent of the following chemical composition:
CaOCaO
33,5233.52
SiO2 MgO Al2O3 Fe2O3 SiO 2 MgO Al 2 O 3 Fe 2 O 3
47,00 2,00 3,5147.00 2.00 3.51
übrige Beimengungen SO3 Cl"other additions SO 3 Cl "
R2O 1,50 Spuren R 2 O 1.50 traces
Bei vorgegebener Brenntemperatur des festen Rückstandes erfolgt eine unvollständige Entsäuerung von CaCO3, deswegen werden die Festigkeitsparameter des Bindemittels gesenkt. Die Senkung der Festigkeitscharakteristiken ist außerdem darauf zurückzuführen, At a given firing temperature of the solid residue, CaCO 3 is incompletely deacidified, which is why the strength parameters of the binder are reduced. The decrease in strength characteristics is also due to
daß das Molverhältnis =~- nicht im optimalen Bereich liegtthat the molar ratio = ~ - not in the optimal range lies
Die Abfälle der Sodaproduktion (Destillierschlamm) wurde bei einer Temperatur von 700° C gebrannt. Der Gehalt des Brennproduktes an aktivem CaO betrug 30,5%.The waste from soda production (distillation sludge) was burned at a temperature of 700 ° C. Of the Active CaO content of the firing product was 30.5%.
Der gebrannte Destillierschlamm und der Quarzsand wurden bis zur spezifischen Oberfläche von 1500 cm2/g gemahlen.The burnt distillation sludge and the quartz sand were ground to a specific surface area of 1500 cm 2 / g.
Die zubereiteten Komponenten wurden so vermischtThe prepared components were thus mixed
daß das Verhältnis ~£ 0,10 betrug. Es fiel ein Bindemittel folgender chemischer Zusammensetzungthat the ratio was ~ £ 0.10. A binder with the following chemical composition fell
CaO
14,20CaO
14.20
SiO2 SiO 2
68,50 1,5768.50 1.57
MgO Al2O3 1,93 MgO Al 2 O 3 1.93
Fe2O3 0,72 Fe 2 O 3 0.72
übrige Beimengungen SO3 Cl" 10,10other additions SO 3 Cl "10.10
R2O 1,70 1,05 Spuren R 2 O 1.70 1.05 traces
Dieses Beispiel zeigt, daß die Festigkeitscharakteristiken des Bindemittels in einem wesentlichen Maße von der Mahlfeinheit der Komponenten abhängen. Mit Verringerung der spezifischen Oberfläche des Bindemittels sinkt seine FestigkeitThis example shows that the strength characteristics of the binder depend to a significant extent on the fineness of grind of the components. With Reducing the specific surface area of the binder decreases its strength
Aus den entsprechenden Beispielen 1, 2 und 3 gewonnenen Bindemitteln wurden 3 χ 3 χ 3 cm große Probestücke nach bekannter Technologie hergestelltThe binders obtained from the corresponding examples 1, 2 and 3 were 3 × 3 × 3 cm in size Test pieces produced according to known technology
Die Plastizität des Gemisches war in allen Fällen gleich. Der Durchmesser des Zerfließens des Kegels auf einem Rütteltisch betrug 120 ±2 mm.The plasticity of the mixture was the same in all cases. The diameter of the deliquescence of the cone on a vibrating table was 120 ± 2 mm.
Die verformten Probestücke wurden nach vorherigem Halten an der Luft während 4 Stunden einer Autoklavebehandlung nach einem Ablauf 4+6+4St bei einem Dampfdruck von 8 at Oberdruck ausgesetztThe deformed test pieces became one after being held in the air for 4 hours Autoclave treatment after a sequence of 4 + 6 + 4h exposed to a vapor pressure of 8 at overpressure
In 24 Stunden nach der Dampfbehandlung wurden die Festigkeitsdaten des Bindemineis und seine Phasenzusammensetzung untersuchtIn 24 hours after the steam treatment, the strength data of the binding mine and its phase composition were obtained examined
Die Versuchsergebnisse sind in der Tabelle 2 aufgeführtThe test results are shown in Table 2
Lfd. Gehalt des
Nr. Gemisches an
BrennproduktSerial Salary of
No mixture at
Firing product
Wasser-FeststolT-Vcrhältnis Water-to-solid ratio
Druckfestigkeit R Compressive strength R
kp/cnrkp / cnr
1. bü1. bü
2. 652. 65
3. 173. 17th
0,41
0,38
0,100.41
0.38
0.10
985
339
665985
339
665
Aus der Analyse der in der Tabelle 2 aufgeführtei Angaben ergibt sich, daß die Anwesenheit voi Chlorverbindungen im Bindemittel seine Festigkeits ι s werte positiv beeinflußt. Mit der Erhöhung des Gehalt des Brennproduktes an aktivem CaO steigen di< Festigkeitswerte des Bindemittels ebenfalls an.Analysis of the information given in Table 2 shows that the presence of voi Chlorine compounds in the binder have a positive effect on its strength values. With the increase in salary of the active CaO firing product, the strength values of the binder also increase.
Die maximale Festigkeit des Bindemittels wird bein Verhältnis des aktiven CaO zu S1O2 von 0,51 erreicht.
21) Die Phasenzusammensetzung des erhärteten Steine ist in der Hautsache durch schwachbasische Kalziumhy
drosihkate vertreten. Hierdurch weisen dieselben eini
hohe Wasser- und Sulfatbeständigkeit auf.The maximum strength of the binder is achieved at a ratio of active CaO to S1O2 of 0.51.
21) The phase composition of the hardened stones is represented in the skin matter by weakly basic Kalziumhy drosihkate. As a result, they have some high water and sulfate resistance.
Die Versuche mit Betonprobestücken im Wasser mi >> geringem Härtegrad zeigten, daß die Festigkeit de Probestücke mit der Zeit ansteigtThe experiments with concrete specimens in the water mi >> low hardness showed that the strength of the specimens increased with time
Das Fehlen von Kalziumhydroaluminaten und TetraThe absence of calcium hydroaluminates and tetra
kalziumhydroaluminatferriten im erhärteten Stein si chert eine hohe Sulfatbeständigkeit von BetonerzeugCalcium hydroaluminate ferrite in the hardened stone ensures that concrete products are highly resistant to sulphates
jo nissen auf der Grundlage des vorgeschlagenen Binde mittels.jo nissen based on the proposed bandage by means of.
Bei einem Gehalt des Bindemittels an CaO unter 20°/i und von SiO2 über 70% sinken die Fesligkeilswerte de: Bindemittels wesentlich, da ein Teil des SiO2 und des übrigen Komponenten des Bindemittels mit CaC ungebunden bleiben und demzufolge als inerte Füllmit tel auftreten.If the CaO content of the binder is below 20 % and SiO 2 exceeds 70%, the solid wedge values de: binder decrease significantly, since some of the SiO 2 and the remaining components of the binder remain unbound with CaC and consequently occur as inert fillers .
Wenn die Menge an CaO im Bindemittel 50°/< übersteigt und die Menge an SiO2 unter 40% beträgt, se wird die Festigkeit auch stark sinken, da wenig fest( starkbasische Kalziumhydrosiükaic entstehen.If the amount of CaO in the binding agent exceeds 50 ° / <and the amount of SiO 2 is below 40%, the strength will also decrease significantly, since less solid (strongly basic calcium hydrosiükaic are formed.
Nachstehend sind einige Eigenschaften des Bindemit tels aufgeführt das industriemäßig gewonnen wurde.Below are some properties of the binder tels listed which was won industrially.
Lfd. Bezeichnung der
Nr. EigenschaftenSerial description of
No properties
Meßeinheiten Units of measurement
Kennzifiergröße Identifier size
Das vorliegende Bindemittel sowie die auf seineiThe present binder as well as the on hisi
Grundlage hergestellten Erzeugnisse, die die obenange führten Eigenschaften aufweisen, können erfolgreich irr Industriebau und im Wohnungs- und öffentlicher Bauwesen eingesetzt werden.Products manufactured on the basis of the above Have led properties, can successfully irr industrial construction and in residential and public Construction are used.
Hierzu 1 Blatt Zeichnungen1 sheet of drawings
Claims (1)