DE2526791A1 - PRINTER COLOR - Google Patents
PRINTER COLORInfo
- Publication number
- DE2526791A1 DE2526791A1 DE19752526791 DE2526791A DE2526791A1 DE 2526791 A1 DE2526791 A1 DE 2526791A1 DE 19752526791 DE19752526791 DE 19752526791 DE 2526791 A DE2526791 A DE 2526791A DE 2526791 A1 DE2526791 A1 DE 2526791A1
- Authority
- DE
- Germany
- Prior art keywords
- ultraviolet light
- acid
- inclusion compound
- fixed
- tung oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
"Druckerfarbe""Printer color"
Die Erfindung betrifft Druckerfarben, und insbesondere für Tiefdruck geeignete Farben, die bei Ultraviolett-Bestrahlung schnell zu einem harten Film abtrocknen und vor Beendigung der Polymerisation in einer Alkalilösung löslich sind.The invention relates to printing inks, and more particularly Inks suitable for gravure printing, which dry quickly to a hard film when exposed to ultraviolet radiation and are soluble in an alkali solution before the completion of the polymerization.
Bei Tiefdruckverfahren werden die zu druckenden Linien oder Punkte auf der Oberfläche der Druckplatte oder -walze eingeätzt oder graviert. Zur Erstellung eines Druckes wird so viel Farbe auf die Fläche der Druckplatte gegeben, bis alle Hohlräume damit ausgefüllt sind, wobei überschüssige Farbe abgewischt, die Papierbögen auf die Druckplatte gelegt und normalerweise mittels Druckwalzen eine Andruckkraft aufgetragen wird.In gravure printing, the lines or points to be printed are on the surface of the printing plate or -roll etched or engraved. To create a print, so much color is applied to the surface of the printing plate given until all voids are filled with it, wiping off excess paint, the sheets of paper placed on the pressure plate and a pressure is normally applied by means of pressure rollers.
609819/1053609819/1053
Das Papier wird bis zu einem gewissen Grade in die Tiefdruckvertiefunken hineingedrückt oder gezwängt, wodurch die Farbe von der Platte auf das Papier überführt wird, um einen abdruck zu ergeben. Durch das Tiefdruckverfahren können dicke Drucke mit hauchdünnen Linienmustern erzeugt werden, weshalb sich dieses Verfahren ideal zum Drucken von Banknoten eignet.The paper gets into that to some extent Deeply pressed or forced in, whereby the ink is transferred from the plate to the paper to give a print. By the gravure printing process thick prints with wafer-thin line patterns can be produced, which is why this process is ideal for printing banknotes.
Die bisher bei Tiefdrücken verwendeten Druckerfarben zum Drucken von Banknoten weisen zwei diesbezügliche inherente Nachteile auf.The printing inks previously used in gravure printing for printing banknotes have two inherent disadvantages in this regard.
Da zunächst das Banknotendrucken eine dicke Schicht oder einen dicken Druck erforderlich macht, um starke Tiefdruckwirkung zu erzielen, ist es oft für die herkömmlichen Druckerfarben unmöglich, schnell genug abzutrocknen, so daß kein Versetzen im Druck der Papierbögen auftritt. 7-ur Vermeidung dieses Problems werden Ein schießbögen bei den meisten modernen Geldnotendruckmaschinen verwendet, so daß kein Verschmieren auftritt. Dies bedeutet jedoch, daß auch ein Verfahren zur Herausnahme der Einschießbögen angewandt werden muß, das mit dem Druckvorgang entweder von Hand oder maschinell ausgeführt wird. Eine derartige Einschießbögenentnahme ist sowohl zeitals auch kostenaufwendig.Since first of all, banknote printing requires a thick layer or print to have a strong gravure printing effect to achieve, it is often impossible for conventional printing inks to dry off quickly enough, so that there is no offset in the printing of the paper sheets. 7-ur avoidance of this problem will be a shooting arc used on most modern bill printing machines so that smearing does not occur. However, this means that also a method for removing slip sheets must be used, which is carried out with the printing process either by hand or by machine. Such a slip sheet removal is both time and also costly.
Hinzu kommt, daß die herkömmlichen Tiefdruckfarben oleaphil sind und mit fettlöslichen Kitteln gesäubert werden massen. Das in diesem Zusaramenhang am weitesten verwendete Lösungsmittel ist Trichloräthylen, ein giftiges Industrielösungsraittel. Bei den meisten Tiefdruckmaschinen wird Trichloräthylen als Reinigungsflüssigkeit zum Abwischen der Walzen verwendet, und zwar trotz der Tatsache,In addition, the conventional gravure inks are oleaphilous and are to be cleaned with liposoluble coats. The most widely used in this context The solvent is trichlorethylene, a toxic industrial solvent. Most gravure printing machines use trichlorethylene as a cleaning fluid for wiping of the rollers used, despite the fact
- 3 609819/1053 - 3 609819/1053
daß Trichloräthylen gemäßigt volatil und in der Dampfphase ein schädlicher Verschmutzungsstoff ist, der für Buchdrucker eine Gesundheitsgefährdung darstellt.that trichlorethylene is moderately volatile and in the vapor phase is a noxious pollutant that poses a health hazard to book printers.
e ist es . ufgäbe der Erfindung einen btoffträger zu schaffen, der in einer Druckerfarbe verwendet werden kann, um die oben angeführten Probleme zu überwinden .e it is. According to the invention, a substrate would be used that can be used in a printing ink to overcome the problems noted above .
Demzufolge wird nach der Erfindung eine Druckerfarbe geschaffen , die sich zum Tiefdruck eignet und ein Pigment zusammen mit einem Ultraviolettfixierträgerstoff enthält, der die Einschlußverbindung eines Tungöls einer ungesättigter» Bikarbonsäure aufweist.Accordingly, according to the invention, there is provided a printing ink which is suitable for gravure printing and contains a pigment together with an ultraviolet fixing vehicle, which has the inclusion compound of a tung oil of an unsaturated bicarboxylic acid.
Die erfindungsgemäßen Farben eignen sich zum miefdruck und sind alkalilöslich, so daL· ein anstatt des Trichloräthylens als !Reinigungsmittel zum .Vbwischen der Walzen verwendet werden kann.The colors invention are suitable for m iefdruck and alkali, such as length can be used instead of one as trichlorethylene! Detergent to .Vbwischen the rolls.
Die Farben trocknen im ultravioletten Licht sehr schnell zu einem harten Film, so daß ein Verfahren zürn Einschies sen von Papierbögen beim Drucken nicht erforderlich ist.The colors dry very quickly in the ultraviolet light to a hard film, so that a process for inclusion It is not necessary to use sheets of paper when printing.
Tungöl wird in der Gegenwart von ultravioletten Licht polymerisiert, was ? uf die Jirkung der vorhandenen Ulstearinsäure, die drei konjugierte Doppelbindungen im I-olekül des Tungöls enthält und einer durch Ultraviolett bestrahlung initiierten radialen Polymerisation.ausgesetzt wird, um einen harten Film zu bilden.Tung oil polymerizes in the presence of ultraviolet light, what? on the effect of the ulstearic acid present, which contains three conjugated double bonds in the I molecule of tung oil and one by ultraviolet Radiation initiated radial polymerization. is exposed to form a hard film.
Das Vorhandensein der Olstearinsäure erlaubt auch, daß das Tungöl den Umsetzungen nach Diels-^lder unterworfenThe presence of the olstearic acid also allows that the tung oil is subjected to Dielder's reactions
— 4-609819/1053 - 4-609819 / 1053
wird, wobei verschiedene ungesätigte Bikarbonsäuren, z.B. Fumarsäure, Maleinsäure, Einschlußverbindungen bilden. Diese chemischen Reaktionen führen zur allgemeinen Einführung der Säuregruppen in den Tungölhauptteil, wodurch die Einschlußverbindung säurehaltig wird und im Alkali eine größere Lösbarkeit erwirbt.with various unsaturated bicarboxylic acids, e.g. fumaric acid, maleic acid, form inclusion compounds. These chemical reactions lead to the general Introduction of the acid groups into the main part of the tung oil, whereby the inclusion compound becomes acidic and acquires greater solubility in alkali.
Es hat sich herausgestellt, daß bei der in bestimmten Verhältnissen durchgeführten Umsetzung von Tungöl und der ungesättigten Bikarbonsäure die Einschlußverbindung immernoch einige konjugierte Doppelverbindungen im Hauptteil des Moleküls aufweisen kann, so daß die Einschlußverbindung alkalilöslich ist und durch das Einwirken von ultraviolettem Licht hart wird. Somit ergibt z.B. die Reaktion von 100 Gewichtsanteilen Tungöl mit weniger als 15 Gewichtsteilen Fumarsäure in inerter Atmosphäre, z.B. Stickstoff, eine alkalilösliche Einschlußverbindung, die sich bei Bestrahlung mit ultraviolettem Licht zu einem starken und harten Film mit einer günstigen Resistenz gegen Lösungsmittel polymerisiert. Eine derartige Ein— Schlußverbindung kann bei der Zusammenstellung einer Tiefdruckerfarbe verwendet werden, da sie bei Ultraviolettbestrahlung schnell trocknet, wobei Natriumhydroxid anstelle von Trichloräthylen als Reinigungsmittel zum Abwischen der Walzen benutzt werden kann.It has been found that when carried out in certain ratios conversion of tung oil and of the unsaturated bicarboxylic acid, the inclusion compound still has some conjugated double compounds in the main part of the molecule, so that the inclusion compound is alkali-soluble and by the action of ultraviolet light becomes hard. Thus, for example, reacting 100 parts by weight of tung oil with less than 15 parts by weight of fumaric acid in an inert atmosphere, e.g. nitrogen, an alkali-soluble inclusion compound which, upon exposure to ultraviolet light, becomes a polymerized strong and hard film with a favorable resistance to solvents. Such a one- Closing compound can be used in the composition of a gravure ink as it is exposed to ultraviolet radiation dries quickly, using sodium hydroxide instead of trichlorethylene as a cleaning agent Wiping the rollers can be used.
Wird der Fumarsäuregehalt der Einschlußverbindung erhöht, erhöht sich auch die Alkalilöslichkeit der Einschlußverbindung, wogegen jedoch die empfindlichkeit gegenüber ultraviolettem Licht abnimmt. Es hat sich jedoch im allgemeinen herausgestellt, daß für eine schnelle durch ultraviolettes Licht eingeleitete Polymerisierung weniger als 20 Gewichtsanteile ungesättigter Bikarbonsäure pro 100 .Gewichtsteil Tungöl vorkommen.If the fumaric acid content of the inclusion compound is increased, the alkali solubility of the inclusion compound also increases, while the sensitivity to ultraviolet is increased Light decreases. However, it has generally been found that for rapid by ultraviolet Light initiated polymerization less than 20 parts by weight of unsaturated bicarboxylic acid per 100 Part by weight of tung oil occur.
6 0 9 8 19/1053 " 5 "6 0 9 8 19/1053 " 5 "
In einigen Fällen ist es notwendig, einen Haftverstärker in einer Druckerfarbe einzuschließen, die die auf Ultraviolettlicht empfindliche Einschlußverbindung aufweist, so daß die Druckerfo.rbe z.B. die für das Tief druckverfahren erforderliche richtige Konsistenz besitzt. Geeignete Haftverstärker sind in der schwebenden Anmeldung 3774-4-/73 aufgeführt und umfassend Poly(vinylmethyläther).In some cases it is necessary to include an adhesion promoter in an ink that is sensitive to ultraviolet light Has sensitive inclusion compound, so that the printer fo.rbe e.g. for the gravure printing process has the required correct consistency. Suitable adhesion promoters are in the pending application 3774-4- / 73 and comprising poly (vinyl methyl ether).
In anderen Fällen weist eine Einschlußverbindung mit der erforderlichen Ultraviolettempfindlichkeit nicht die benötigte Äkalilöslichkeit auf. Es hat sich zur Erhöhung der i.lkalilüslichkeit herausgestellt, daß sich durch die Fithineinnahme einer auf üitraviolettlicht fixierenden Einschlußverbindung d.h. einer Verbindung, die mehr als 20 Gewichtsteile einer ungesättigten Bikarbonsäure ντο 100 Gewichtsteile Tungöl enthält, mit einer auf ultraviolettes Licht ansprechenden Einschlußverbindung einen Trägerstoff ergibt, der sowohl alkalilöslich als auch auf üitraviolettlicht ansprechbar ist.In other cases, an inclusion compound with the required ultraviolet sensitivity will not have the required alkali solubility. In order to increase the alkalinity, it has been found that fithin ingestion of an inclusion compound that fixes on ultraviolet light, i.e. a compound that contains more than 20 parts by weight of an unsaturated bicarboxylic acid ντο 100 parts by weight of tung oil, with an inclusion compound that responds to ultraviolet light results in a carrier, which is both alkali-soluble and responsive to ultraviolet light.
Demzufolge wird erfindungsgemäß ein alkalilöslicher, ultraviolettfixierender Trägerstoff geschaffen, der aus einem Gemisch einer Tfltraviolettlicht nicht fixierenden Einschlußverbindung sowie einer Ultraviolettlich fixierenden Einschlußverbindung aus Tungöl mit einer ungesättigten Bikarbonsäure besteht.Accordingly, the present invention becomes an alkali-soluble, ultraviolet-fixing one Carrier created from a mixture of a Tfltraviolet light non-fixing Inclusion compound and an ultraviolet-fixing inclusion compound of tung oil with an unsaturated one Bicarboxylic acid.
Ein derartiger Trägerstoff stellt gemeinsam mit Pigmenten, Verschnittmillen, Beimengungen und Initiatoren eine ausgezeichnete Druckerfarbe dar, die zufriedenstellend mit den zum Drucken von Banknoten verwendeten Maschinen arbeitet, wobei ein Alkali anstelle des Trichlor-rSuch a carrier material, together with pigments, blends, admixtures and initiators an excellent printing ink which works well with the machines used to print banknotes works, using an alkali instead of the trichloro-r
- 6 609819/1053 - 6 609819/1053
äthylens als Reinigungsmittel zum abwischen der Walzen verwendet wird.Ethylene as a cleaning agent for wiping the rollers is used.
Die Erfindung wird nun anhand der nachstehenden Musterbeispiele beschrieben.The invention will now be described with reference to the following sample examples.
Nicht auf Ultraviolettlicht ansprechende Tungöl-Fumarlackfarbe (A)Tung oil fumaric paint that does not respond to ultraviolet light (A)
1670 Gramm Tungöl und 330 Gramm Fumarsäure wurden in einem rostfreien Stahlgefäß gemischt und in Stickstoffatmosphäre erwärmt. Die Temperatur wurde in einer Stunde auf 190° C angehoben, um hiernach eine Temperatur von 2100O zu erreichen, die dann 15 Minuten lang beibehalten wurde. Hiernach konnte die Temperatur in 15 Hinuten auf 190°0 abfallen.1670 grams of tung oil and 330 grams of fumaric acid were mixed in a stainless steel vessel and heated in a nitrogen atmosphere. The temperature was raised within one hour to 190 ° C in order thereafter to reach a temperature of 210 0 O, which is then maintained for 15 minutes. The temperature was then able to drop to 190 ° 0 in 15 minutes.
Die Lackfarbe (A) stellt einen dickflüssigen Sirup mit einer Viskosität von 235«4- Poisen bei 4-0° 0 dar.The lacquer color (A) is a thick syrup with a viscosity of 235 «4 poises at 4-0 ° 0.
Beispiel 2 Auf Ultraviolettlicht ansprechende Tungöl-Fumarlackfarbe (B)Example 2 Tung oil fumaric lacquer that reacts to ultraviolet light (B)
Dem Beispiel 1 wurde sehr genau gefolgt, ausgenommen, daß nur die Hälfte der Fumarsäure (d.h. 165,0 Gramm) verwendet wurden. Die Viskosität der Lackfarbe lag bei einer Temperatur von 200O bei 49,5 Poise. Die Oberfläche des Films wird bei Aussetzung an ultraviolettes Licht schrumpelig, was anzeigt, daß die Lackfarbe auf Ultraviolettlicht anspricht.Example 1 was followed very closely, except that only half the fumaric acid (ie 165.0 grams) was used. The viscosity of the paint was 49.5 poise at a temperature of 20 0 O. The surface of the film wrinkles upon exposure to ultraviolet light, indicating that the varnish color is responsive to ultraviolet light.
— 7 — 6G9819/1053- 7 - 6G9819 / 1053
Beispiel 5 Alkalilösliche, ultraviolett-fixierende TiefdruckerfarbeExample 5 Alkali-soluble, ultraviolet-fixing gravure ink
Lackfarbe A 4-00 gLacquer color A 4-00 g
Lackfarbe B 400 gLacquer color B 400 g
Lanolin 200 gLanolin 200 g
TrioktylphoSphat 152 gTrioctylphosphate 152 g
Calciumkarbonat 1,200 gCalcium carbonate 1,200 g
Titandioxid 60 gTitanium dioxide 60 g
Chromophtal Braun 5R 110 gChromophtal brown 5R 110 g
Chromophtal Gelb GR 88 gChromophthal yellow GR 88 g
Benzoylperoxid 2,6gBenzoyl peroxide 2.6g
Die sich ergebende Druckerfarbe weist die Viskosität von 171,9 P bei 40°C auf. Sie arbeitet auf modernen Druckmaschinen für Banknoten sehr gut, die mit einer Geschwindigkeit von 5 500 Bögen pro Stunde laufen. Ein 70-Mikrofilm trochnet in weniger als 50 Sekunden, wenn er von einer 125 Watt Hannovia-Lampe bestrahlt wird. Die Druckerfarbe trocknet auch durch Luftoxidierung.The resulting printing ink has a viscosity of 171.9 P at 40 ° C. It works very well on modern banknote printing machines that run at a speed of 5,500 sheets per hour. A 70 microfilm dries in less than 50 seconds when irradiated by a 125 watt Hannovia lamp. The printing ink also dries through air oxidation.
— Patentansprüche -- patent claims -
609819/1053609819/1053
Claims (12)