DE2262057A1 - OIL ABSORPTION AGENTS AND METHOD OF MANUFACTURING THEREOF - Google Patents

OIL ABSORPTION AGENTS AND METHOD OF MANUFACTURING THEREOF

Info

Publication number
DE2262057A1
DE2262057A1 DE19722262057 DE2262057A DE2262057A1 DE 2262057 A1 DE2262057 A1 DE 2262057A1 DE 19722262057 DE19722262057 DE 19722262057 DE 2262057 A DE2262057 A DE 2262057A DE 2262057 A1 DE2262057 A1 DE 2262057A1
Authority
DE
Germany
Prior art keywords
peat
oil
fines
fibers
dried
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19722262057
Other languages
German (de)
Inventor
Karl Otto Paul Fischer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fischer Holdings Ltd
Original Assignee
Fischer Holdings Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fischer Holdings Ltd filed Critical Fischer Holdings Ltd
Publication of DE2262057A1 publication Critical patent/DE2262057A1/en
Withdrawn legal-status Critical Current

Description

PatentanwältePatent attorneys

Dipl.-Chem. I. SCHULZE β9 Heidelberg ι 2262057Dipl.-Chem. I. SCHULZE β9 Heidelberg ι 2262057

Gaisbergstraße 3 Dipl.-Ing. E. GUTSCHER Telephon 23269Gaisbergstrasse 3 Dipl.-Ing. E. GUTSCHER telephone 23269

UNSER ZEICHEN:OUR SIGN: Abs. Dipl.-Chem. I. Schulze, Dipl.-Ing. E. Gutscher, Patentanwälte " | IHR ZEICHEN:Abs. Dipl.-Chem. I. Schulze, Dipl.-Ing. E. Gutscher, patent attorneys "| YOUR CHARACTER:

6900 Heidelberg, Gaisbergstraße 36900 Heidelberg, Gaisbergstrasse 3

Anmelder: Fischer Holdings Ltd.,· 219 Riverside Drive, Chilliwack, Britisch Columbien, CanadaApplicant: Fischer Holdings Ltd., 219 Riverside Drive, Chilliwack, British Columbia, Canada

ölabsorptionsmittel und Verfahren zu dessen Herstellung.oil absorbents and processes for their manufacture.

Die Erfindung bezieht sich auf ein (^absorptionsmittel., das auf Wasser schwimmt, und auf ein Verfahren zu dessen Herstellung,The invention relates to an (^ absorbent., The floats on water, and a process for its manufacture,

Das Entfernen von öl, insbesondere von freien Wasseroberflächen ist ein wesentliches Problem, das immer grosser wird mit dem erhöhten Verbrauch von Mineralölen und dergleichen.The removal of oil, especially from exposed water surfaces is a major problem that is increasing with the increased consumption of mineral oils and the like.

309828/0 3 21309828/0 3 21

Es ist bekannt, dass Verschmutzung durch einen Ölfilm erhebliche Schaden für die Lebewesen im Wasser verursacht, da Ölfilme das Eindringen von Sauerstoff in das Wasser hindern und an die Küsten gespültes öl zerstört das Strandleben.It is known that pollution caused by an oil film causes significant damage to living things in the water, since Oil films prevent oxygen from entering the water, and oil washed up on the coast destroys beach life.

Es wurde bereits auf verschiedenen Wegen versucht, den auf Wasser schwimmenden Ölfilm zu entfernen. Eines der erfolgreichsten Verfahren besteht darin, ölabsorbierende Mittel auf den Ölfilm zu streuen, die darauf schwimmen und das öl absorbieren. Anschliessend wird die mit öl vollgesogene Masse gesammelt, und das öl daraus wiedergewonnen oder die Masse verworfen.Attempts have already been made in various ways to remove the oil film floating on water. One of the most successful The method consists in sprinkling oil absorbing agents on the oil film, floating on it and the oil absorb. Then the mass soaked with oil is collected, and the oil or the mass is recovered from it discarded.

Die blabsorblerenden Eigenschaften bestimmter organischer Stoffe, beispielsweise Torf, Textilfasern, Sägemehl und dergleichen sind bekannt. Es muss aber auch immer in Betracht gezogen werden, dass diese Stoffe hydrophil sind, d.h. sie neigen dazu, Wasser zu absorbieren· So nehmen sie neben dem öl von der Wasseroberfläche auch eine gewisse Menge Wasser auf. Aus diesem Grund werden diese organischen Stoffe behandelt und hydrophob gemacht, d.h. im wesentlichen wasserabstossend.The blistering properties of certain organic Substances such as peat, textile fibers, sawdust and the like are known. But it must always be taken into account be drawn that these substances are hydrophilic, i.e. they tend to absorb water so take them next to the oil from the surface of the water also absorbs a certain amount of water. It is for this reason that these organic substances are treated and rendered hydrophobic, i.e. essentially water repellent.

Die US-PS 3 464 920 beschreibt ein Verfahren zum Behandeln von zerkleinertem bzw. pulverisiertem organischen Material mit Organo-Siliciumwasserstoff-Verbindungen, um den organischen Stoffen hydrophobe Eigenschaften zu verleihen.U.S. Patent 3,464,920 describes a method of treating crushed or pulverized organic material with organosilicon hydrogen compounds to the organic To give substances hydrophobic properties.

Die US-PS 3 562 153 bezieht sich auf die Verwendung von kolloiden hydrophoben Metall- oder Metalloidoxiden zum Behandeln von Absorptionsmitteln, um diese hydrophob zu machen.U.S. Patent 3,562,153 relates to the use of colloidal hydrophobic metal or metalloid oxides for treating absorbents to make them hydrophobic.

Eine solche Behandlung ist aber sehr kostspielig und daher unwirtschaftlich, insbesondere da die Stoffe zum Entfernen von öl auf Wasserflächen in grossen Mengen verwendet werden müssen.However, such a treatment is very costly and therefore uneconomical, especially since the substances have to be removed of oil must be used in large quantities on water surfaces.

309828/032 1309828/032 1

— "5 —- "5 -

Aufgabe der Erfindung ist?einen billigen ölabsorbierenden Stoff und ein Verfahren zu dessen Herstellung zu schaffen, das ebenfalls sehr wirtschaftlich ist und dadurch die Verwendung des Absorptionsmittel auf breiter Basis gestattet.The object of the invention is ? to provide an inexpensive oil absorbent material and a process for its manufacture which is also very economical and thereby allows the absorbent to be used on a broad basis.

Es wurde gefunden, dass Torf mit vermindertem Feuchtigkeitsgehalt seine hydrophilen Eigenschaften verliert und weitgehend hydrophob wird«It has been found that peat with reduced moisture content loses its hydrophilic properties and largely becomes hydrophobic "

Erfindungsgemäss wird daher als ©"!absorbierend© Masse ein Torf verwendet, dessen Massergehalt weniger als 10 Gewichts-»^ beträgt.According to the invention, therefore, absorbing means a Peat used, the mass of which is less than 10 weight - »^ amounts to.

Gegenstand der Erfindung ist auch ein Verfahren zum Behandeln und Trennen von Torffaser von Torffeinstoffen vor dem Trocknen.The invention also relates to a method of treatment and separating peat fiber from peat fines prior to drying.

Erfindungsgemäss wird der Wassergehalt von Torf mechanisch bis auf 75 Gewichts-^ verringert. Der Torf wird gesiebt, um ihn in Torffaser und Torffeinstoffe mit einer maximalen Länge von 0,5 mm bis 5 mm zu trennen» Die Torffaser und Torffeinstoffe werden dann gesondert bis auf einen Feuchtigkeitsgehalt von weniger als 10 Gewichts-^ getrocknet.According to the invention, the water content of peat is mechanically up to reduced to 75 weight- ^. The peat is sifted to divide it into peat fiber and peat fines with a maximum length of 0.5 mm to 5 mm to separate »The peat fibers and peat fines are then separately dried to a moisture content of less than 10% by weight.

Um Torf zu einem ölabsorbierenden Mittel zuzubereiten, wird wie ' folgt verfahren· Rohtorf, der direkt vom Torfboden kommt, hat normalerweise einen Wassergehalt von etwa 90 Gewichts-^» Er wird mechanisch in Walzenpressen bis auf einem Wassergehalt von etwa 75 Gewichts-^ getrocknet. Dieser so getrocknete Torf wird dann über vibrierende Siebe geführt, deren Sieböffnungen etwa 0,5 mm bis 5 mm - 1 mm betragen. Solche Siebe haben sich als zweckmässig erwiesen, um den Torf in Torffaser und Torffeinstoffe zu trennen.To make peat an oil-absorbing agent, like ' follows procedure · Raw peat, which comes directly from the peat soil, normally has a water content of about 90% by weight is mechanically dried in roller presses to a water content of about 75% by weight. This so dried peat becomes then passed over vibrating sieves, the sieve openings of which are approximately 0.5 mm to 5 mm - 1 mm. Such sieves have proven to be Proven to be useful for separating the peat into peat fibers and peat fines.

309828/0321309828/0321

Die Torffeinstoffe und Torffasser werden dann gesondert in heisser Luft bei etwa 1000C wärmegetrocknet, bis der Wassergehalt sowohl der Torffaser als auch der Torffeinstoffe zwischen 8 und 10$ des Torfgewichts gesenkt ist. Das getrocknete Material kann, falls es über eine längere Zeitspanne gelagert werden soll, in feuchtigkeitsdichte Behälter gepackt werden, so dass der Torf seine durch das Wärmetrocknen erhaltene Eigenschaften beibehält.The Torffeinstoffe and Torffasser are then separately in hot air heat-dried at about 100 0 C, both the peat fiber until the water content and the Torffeinstoffe 8-10 $ of the Torfgewichts is lowered. If the dried material is to be stored for a longer period of time, it can be packed in moisture-proof containers so that the peat retains the properties obtained by heat drying.

Der mechanisch getrocknete Torf wird vor dem Wärmetrocknen in Paser und Feinstoffe getrennt, da die Torffasern eine viel höhere Wassersättigungskapazität haben als die Feinstoffe. Diese Feinstoffe sind teilweise zerfallene Torfpartikel, die einen grösseren Oberflächenbereich haben als das gleiche Gewicht an Fasern. Wenn daher Fasern und Feinstoffe zusammen in Masse wärmegetrocknet werden, hätten sie einen unterschiedlichen Feuchtigkeitsgehalt.The mechanically dried peat is separated into pas and fines before heat drying, as the peat fibers have a lot have higher water saturation capacity than the fines. These fines are partially decayed peat particles that have a larger surface area than the same weight of fibers. Hence when fibers and fines together in bulk are heat-dried, they would have a different moisture content.

Beide Torfarten, das heisst die Fasern und die Feinstoffe, haben bemerkenswerte hydrophobe Eigenschaften. Wenn sie, also Fasern und Feinstoffe, auf Wasser gestreut werden, schwimmen sie leicht und neigen nicht dazu, sich zu trennen oder Wasser zu absorbieren. Andererseits weisen sowohl die Fasern als auch die Feinstoffe ausgezeichnete ölabsorbierende Eigenschaften auf und sinken nicht unter, wenn sie mit öl vollgesogen sind.Both types of peat, i.e. the fibers and the fines, have remarkable hydrophobic properties. If they, so fibers and fines, scattered on water, float easily and do not tend to separate or absorb water. On the other hand, both the fibers and the fines have excellent oil-absorbing properties and do not sink under when they are soaked with oil.

Die folgenden Beispiele sollen den Erfindungsgegenstand näher erläutern.The following examples are intended to explain the subject matter of the invention in more detail.

Beispiel 1example 1

Auf mit öl bedecktes Wasser wurde 1 Liter Torffeinstoffe gestreut. Verwendet wurde ein Mineralöl mit einem Gewicht von SAE 20. Nach zwei Minuten war der Torf mit öl vollgesogen und bildete eine kompakte, auf dem Wasser schwimmende Masse. Der Wasserspiegel bleib konstant, ein Beweis, dass sehr wenig oder überhaupt kein Wasser absorbiert wurde. Ein Vergleich der Gewichte1 liter of peat fines was sprinkled on water covered with oil. A mineral oil with a weight of SAE 20 was used. After two minutes, the peat was soaked with oil and formed a compact mass floating on the water. The water level remains constant, evidence that very little or no water at all was absorbed. A comparison of the weights

309828/0321309828/0321

des getrockneten Torfes und des mit öl vollgesogenen Torfes zeigte, dass 1 Liter des getrockneten Torfes 1 Liter öl aufgesaugt hatte.of dried peat and peat soaked with oil showed that 1 liter of the dried peat 1 liter of oil had sucked up.

Beispiel 2Example 2

Auf reines Wasser wurde 1 Liter Torffeinstoff gestreut. Diese breiteten sich nicht aus, sondern behielten ihre kompakte Form. Nach einer Stunde wurde die Torfmasse vom Wasser entfernt. Ausser an der Unterseite der Torfmasse haftende Wassertröpfchen war die Masse trocken.1 liter of peat fines was sprinkled on top of pure water. These did not spread, but kept their compact shape. After an hour, the peat mass was removed from the water. Except for water droplets adhering to the underside of the peat mass the mass was dry.

Die obigen Beispiele zeigen, dass Torffeinstoffe, die bis auf einen Wassergehalt von weniger als 10 Gewichts-^ getrocknet sind, im wesentlichen hydrophob und weniger hydrophil sind.The above examples show that peat fines that up to a water content of less than 10 weight ^ dried are essentially hydrophobic and less hydrophilic.

Beispiel 3Example 3

Um die ölabsorbierenden Eigenschaften der Torffeinstoffe mit öl allein zu ermitteln, wurde öl mit einem Gewicht von SAE 20 auf eine saubere Metalloberfläche gegossen und darauf eine gewisse Menge Torffeinstoffe gestreut. Das öl wurde sofort absorbiert und die Metalloberfläche blieb im wesentlichen trocken, d.h. frei von Flüssigkeiten zurück. Die Metalloberfläche zeigte nur ein leicht feuchtes Aussehen, wie es normalerweise bei Metallflächen auftritt, die mit einem Stück öliger Putzwolle gerieben wurden. Der mit öl vollgesogene Torf konnte leicht als eine Masse von der Metallfläche abgehoben werden.To use the oil-absorbing properties of peat fines To determine oil alone, was oil weighing SAE 20 Poured onto a clean metal surface and a certain amount of it Scattered amount of peat fines. The oil was immediately absorbed and the metal surface remained essentially dry, i.e. free of liquids. The metal surface showed just a slightly damp appearance, as usually occurs with metal surfaces that have been covered with a piece of oily cleaning wool were rubbed. The peat soaked with oil could easily be lifted off the metal surface as a mass.

Die ölabsorbierenden hydrophoben Eigenschaften der erfindungsgemäss hergestellten Torffaser werden aus den folgenden Beispielen deutlich.The oil-absorbing hydrophobic properties of the invention The peat fibers produced are clear from the following examples.

309 8 28/032 1309 8 28/032 1

Beispiel 4 Example 4

Der Versuch wurde ähnlich wie in Beispiel 1 durchgeführt, wobei 1 Liter Torffaser verwendet wurde. Die Ergebnisse waren die gleichen wie die mit den Torffeinstoffen erzielten. Die Torffaser hatte ein niedrigeres Schüttgewicht als in der Qualität ähnliche Torffeinstoffe (etwa 70#) und absorbierte etwa 0.7 Liter öl. Daraus war ersichtlich, dass die Torffaser das gleiche Gewicht an öl absorbiert wie die Torffeinstoffe. The experiment was carried out similarly to Example 1, using 1 liter of peat fiber. The results were the same as those obtained with the peat fines. The peat fiber had a lower bulk density than peat fines of similar quality (about 70 #) and was absorbent about 0.7 liters of oil. From this it was seen that the peat fiber absorbs the same weight of oil as the peat fines.

Beispiel 5Example 5

Es wurde ähnlich wie in Beispiel 2 verfahren, wobei jedoch 1 Liter Torffaser verwendet wurde. Auch hier war das Ergebnis das gleiche wie mit Torffeinstoffen gemäss Beispiel 2. Die Beispiele 4 und 5 zeigen, dass die Torffaser so wie die Torffeinstoffe im wesentlichen hydrophob und weniger hydrophil sind.The procedure was similar to that in Example 2, except that 1 liter of peat fiber was used. Here, too, was the result the same as with peat fines according to Example 2. Examples 4 and 5 show that the peat fiber as the Peat fines are essentially hydrophobic and less hydrophilic.

Beispiel 6Example 6

Es wurde ähnlich wie in Beispiel 3 verfahren, wobei jedoch Torffaser verwendet wurde. Die mit öl vollgesogenen Pasern ballen nicht so fest zusammen wie die Masse der Torffeinstoffe und die Metalloberfläche zeigte nicht das im wesentliche ölfilmfreie Aussehen, wie es mit Torffeinstoffen erhalten wurde. Die Wirksamkeit der Torffeinstoffe beim Entfernen von öl von Metallflächen ist auf den grösseren Oberflächenbereich zurückzuführen, dem die zu säuberende Oberfläche ausgesetzt ist. Der freie Oberflächenbereich der Torffaser ist kleiner als bei den Torffeinstoffen.The procedure was similar to that in Example 3, except that Peat fiber was used. The pastes soaked in oil do not clump together as tightly as the bulk of the peat fines and the metal surface did not exhibit the essentially oil film free appearance obtained with peat fines became. The effectiveness of peat fines in removing of oil from metal surfaces is due to the larger surface area that the surface to be cleaned is is exposed. The free surface area of the peat fiber is smaller than that of the peat fines.

Es wurde gefunden, dass die erfindungsgemäss hergestellte Torfmasse ein ausgezeichnetes ölabsorbierendes Mittel ist, da sie hydrophob ist und die vorgeschriebene Schwimmfähigkeit aufweist, wenn sie mit öl vollgesogen ist. AusserdemIt has been found that the peat mass produced according to the invention is an excellent oil-absorbing agent, because it is hydrophobic and has the prescribed buoyancy when it is soaked with oil. Besides that

309828/0321309828/0321

sind die Herstellungskosten sehr gering., da erstens Torf billig ist und dieser nur eine geringe Behandlung s nämlich Sieben und Trocknen erfordert., the manufacturing cost is very low. firstly because peat is cheap and of these only a small treatment s namely requires sieving and drying.

Ferner kann der so behandelte Torf aufgrund seiner ölabsorbierenden Eigenschaften von Metallflächen auch zum Säubern von Schiffen, Lagertanks und dergleichen verwendet werden. Torffeinstoffe können beispielsweise in einen Tank geblasen und dann von den Tankwänden abgestrichen oder durch Vakuum augesaugt werden.Furthermore, the peat treated in this way can be due to its oil-absorbing properties Properties of metal surfaces can also be used for cleaning ships, storage tanks and the like. Peat fines can, for example, be blown into a tank and then wiped off the tank walls or by vacuum be sucked.

309828/0321309828/0321

Claims (8)

PatentansprücheClaims fl./ölabsorptionsmittel, bestehend aus Torf mit einem Wassergehalt von weniger als 10 Gewichts-^.fl./oil absorbent consisting of peat with a water content of less than 10% by weight ^. 2. ölabsorptionsmittel nach Anspruch 1, dadurch gekennzeichnet, dass der Wassergehalt des Torfs zwischen 8 und 10 Gewichts-^ liegt.2. oil absorbent according to claim 1, characterized in that that the water content of the peat is between 8 and 10% by weight. J. ölabsorptionsmittel nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass der Torf eine Faserlänge von zwischen 0,5 bis 5 mm aufweist.J. oil absorbent according to claim 1 or 2, characterized characterized in that the peat has a fiber length of between 0.5 to 5 mm. 4. ölabsorptionsmittel nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass der Torf eine Faserlänge von weniger als 1 mm aufweist.4. oil absorbent according to claim 1 or 2, characterized in that that the peat has a fiber length of less than 1 mm. 5. Verfahren zum Behandeln von Torf zur Herstellung eines ölabsorptionsmittels gemäss den Ansprüchen 1 bis 4, dadurch gekennzeichnet, dass der Torf bis auf einen Wassergehalt von etwa 75 Gewichts-^ mechanisch getrocknet wird, der so getrocknete Torf in Fasern mit einer "^serlange von mehr als 5 mm und in Torffeinstoffe mit einer Faserlänge von kleiner als 5 mm getrennt wird und die Torffasern und die Torffeinstoffe gesondert bis auf einen Wassergehalt von weniger als 10$ bezogen auf das Gewicht des Torfes wärmegetrocknet werden.5. A method for treating peat to produce an oil absorbent according to claims 1 to 4, characterized in that the peat is mechanically dried to a water content of about 75 weight ^ the peat thus dried into fibers with a "^ serlange is separated by more than 5 mm and into peat fines with a fiber length of less than 5 mm and the Peat fibers and peat fines separately except for a water content of less than $ 10 based on weight of the peat are heat-dried. 6. Verfahren nach Anspruch 5, dadurch gekennzeichnet, dass der Torf zum mechanischen Trocknen durch Druckwalzen hindurchgeführt wird.6. The method according to claim 5, characterized in that the peat is passed through pressure rollers for mechanical drying will. 309828/0321309828/0321 — Q -- Q - 7. Verfahren nach Anspruch 5 oder 6, dadurch gekennzeichnet, dass die Torffasern und Torffeinstoffe auf vibrierenden Sieben voneinander getrennt werden. : \ ;: 7. The method according to claim 5 or 6, characterized in that the peat fibers and peat fines are separated from one another on vibrating sieves. : \; : 8. Verfahren nach Anspruch 5 oder 6, dadurch gekennzeichnet, dass die Torffasern und die Torffeinstoffe in einem auf etwa 1000C erwärmten Luftstrom getrocknet werden.8. The method of claim 5 or 6, characterized in that the peat fibers and the Torffeinstoffe are dried in a heated to about 100 0 C air stream. 309828/0321309828/0321 ORlGtNAL INiSPECTEOORlGtNAL INiSPECTEO
DE19722262057 1971-12-29 1972-12-19 OIL ABSORPTION AGENTS AND METHOD OF MANUFACTURING THEREOF Withdrawn DE2262057A1 (en)