DE2201067C3 - - Google Patents
Info
- Publication number
- DE2201067C3 DE2201067C3 DE19722201067 DE2201067A DE2201067C3 DE 2201067 C3 DE2201067 C3 DE 2201067C3 DE 19722201067 DE19722201067 DE 19722201067 DE 2201067 A DE2201067 A DE 2201067A DE 2201067 C3 DE2201067 C3 DE 2201067C3
- Authority
- DE
- Germany
- Prior art keywords
- paper
- fibers
- cellulose
- celluloses
- soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Die Erfindung bezieht sich auf ein Verfahren zur Herstellung eines in wäßrigen alkalischen Lösungen löslichen Spezialpapiers mit einer ausgezeichneten Bedruckbarkeit aus alkalilöslichen Cellulosefasern.The invention relates to a process for the preparation of an aqueous alkaline solution soluble special paper with excellent printability made from alkali-soluble cellulose fibers.
Papier ist im wesentlichen aus einem verwickelten Geflecht von Cellulosefascrn aufgebaut und kann nicht dispergiert oder gelöst werden, wenn es nicht speziellen Behandlungen, wie z. B. in einer konzentrierten wäßrigen Lösung von Zinkchlorid mit mehr als 40% bei etwa 1000C oder mit Cuprammonium in einigen Fällen in Abhängigkeit vom Gebrauchszweck unterworfen wird, während es hingegen günstig wäre, wenn die Bestandteile des Papiers so einfach als möglich dispergiert oder gelöst werden könnten.Paper is essentially made up of an entangled braid of cellulose fiber and cannot be dispersed or dissolved unless it is subjected to special treatments, e.g. B. in a concentrated aqueous solution of zinc chloride with more than 40% at about 100 0 C or with cuprammonium in some cases depending on the intended use, while it would be beneficial if the constituents of the paper dispersed or dissolved as easily as possible could become.
In der US-Patentschrift 30 34 922 ist ein Schreibpapier beschrieben, das im Wasser in seine einzelnen Bestandteile zerfällt und das durch Imprägnieren eines Textilfaservlieses mit einer wäßrigen Dispersion, das ein wasserunlösliches Füllmaterial und einen wasserlöslichen Filmbildner als Bindemittel enthält, Trocknen der so erhaltenen Struktur, erneutes Anfeuchten des trockenen Gebildes bis auf einen Feuchtigkeitsgehalt von 3 bis 10% und Glätten auf einem erhitzten Kalander erhalten wird.In US Pat. No. 3,034,922 there is a writing paper described, which breaks down into its individual components in water and that by impregnating a Textile fiber fleece with an aqueous dispersion containing a water-insoluble filler material and a water-soluble one Contains film former as a binder, drying the structure thus obtained, rewetting the dry structure down to a moisture content of 3 to 10% and smoothing on a heated calender is obtained.
Ferner beschreibt auch die US-Patentschrift 34 31 166 ein wasserlösliches Papier, das durch Erhitzen einer Papierbahn aus Cellulose-Glykolsäure-Fasern mit einem Substitutionsgrad von 0.1 bis 0,8 während einer solchen Zeit und bei einer solchen Temperatur, daß die Papierbahn bei einer nachfolgenden Alkaliimprägnierung nicht gelöst wird oder zerfällt, Imprägnieren der hitzebehandelten Bahn mit einer wäßrigen Alkalilösung in einer das Neutraüsierungsäquivalent, bezogen auf die Cellulose-Glykolsäure, übersteigenden Gewichtsmenge und Erhitzen der imprägnierten Papierbahn erhalten wird.Furthermore, US Pat. No. 3,431,166 describes a water-soluble paper which, by heating a paper web made of cellulose-glycolic acid fibers with a degree of substitution of 0.1 to 0.8 during such a time and at such a temperature that the paper web in a subsequent alkali impregnation does not dissolve or disintegrates, impregnating the heat-treated sheet with an aqueous alkali solution in one that exceeds the neutralization equivalent, based on the cellulose glycolic acid Weight amount and heating of the impregnated paper web is obtained.
Aufgabe der Erfindung ist demgegenüber die Schaffung eines Verfahrens zur Herstellung eines Spezialpapiers, das zur Anwendung als Etiketten von wiederverwendbaren Flaschen, brauchbar ist, das nicht reißt oder durch Benetzung mit Wasser während des Gebrauchs beschädigt wird, das jedoch sehr leiehl entfernt werden kann, wenn es in eine wäßrige alkalische Lösung eingebracht wird, so daß sich eine erhebliche Verbesserung der Arbeitswirksamkeit ergibt. Ferner soll das erfindungsgemäß hergestellte Papier auch zur Anwendung für Geheimdokumente geeignet sein, die unter beliebigen Witterungsbedingungen ihre Brauchbarkeit beibehalten, jedoch erforderlichenfalls innerhalb weniger Sekunden durch Einbringung in eine verdünnt» wäßrige alkalische Lösung dispergiert werden.In contrast, the object of the invention is to create a method for producing a special paper, that is suitable for use as labels of reusable bottles, that does not tear or damaged by wetting with water during use, but it is very easy to remove can, if it is placed in an aqueous alkaline solution, so that there is a considerable improvement the work effectiveness results. Furthermore, the paper produced according to the invention should also be used be suitable for secret documents that retain their usefulness under any weather conditions, but if necessary within a few seconds by introducing it into a dilute aqueous solution alkaline solution to be dispersed.
Nachdem festgestellt worden war, daß ein aus einer Papiermasse, die Fasern von Celluloseäthern enthält, die in einer wäßrigen alkalischen Lösung löslich, jedoch nicht in Wasser löslich sind, gefertigtes Papier die Eigenschaft besitzt, leicht in einer wäßrigen alkalischen Lösung gelöst oder dispergiert zu werden, wurden diese Untersuchungen weiter ausgedehnt. Dabei wurde das Verfahren gemäß der Erfindung aufgefunden.After it was found that a paper pulp containing fibers of cellulose ethers, which are soluble in an aqueous alkaline solution but not soluble in water, manufactured paper the Has a property of being easily dissolved or dispersed in an aqueous alkaline solution, they have become Investigations further expanded. The method according to the invention was found here.
Das Verfahren zur Herstellung eines in wäßrigen alkalischen Lösungen löslichen Spezialpapiers mit einer ausgezeichneten Bedruckbarkeit aus alkalilöslichen Cellulosefasern ist dadurch gekennzeichnet, daß man eine Bahn aus alkalilöslichen, wasserunlöslichen Celluloseätherfasern oder einem Gemisch von wenigstens 0,2 Gewichtsteilen dieser Celluloseätherfasern mit 1 Gewichtsteil üblicher Papierherstellungsfasern, mit einem alkalischen, wäßrigen Oberflächenbehandlungsmittel, das eine trockenfilmbildende Substanz, bestehend aus dem teilweisen Verseifungsprodukt von Polyvinylacetat, einem Äthylen/Acrylsäure-Copolymerisat, Kasein od^r Gemischen hiervon, enthält, beschichtet und danach die Bahn sofort trocknet.The process for making an in aqueous alkaline Solutions of soluble special paper with excellent printability from alkali-soluble Cellulose fibers are characterized in that a web of alkali-soluble, water-insoluble cellulose ether fibers is used or a mixture of at least 0.2 parts by weight of these cellulose ether fibers with 1 Part by weight of conventional papermaking fibers, with an alkaline, aqueous surface treatment agent, which consists of a dry film-forming substance from the partial saponification product of polyvinyl acetate, an ethylene / acrylic acid copolymer, Casein or mixtures thereof, contains, coated and then the web dries immediately.
Bei dem Verfahren gemäß der Erfindung wird zunächst eine Faserbahn in üblicher Weise gebildet, wobei als Fasermaterial entweder Celluloseätherfasern, die in wäßrigen alkalischen Lösungen löslich, jedoch in Wasser nicht löslich sind, oder ein Gemisch von mindestens 0,2 Gewichtsteilen der vorstehenden Celluloseätherfasern und 1 Gewichtsteils eines üblichen Papierfasermaterials, wie natürlichen Fasern, organischen Fasern, anorganischen Fasern, regenerierten Fasern, Linters, Bastfasern, Strohfasern od. dgl. verwendet werden, und dabei die Fasern erforderlichenfalls zusammen mit Hilfsmittel, wie Leimungs- oder Schlichtemittel oder Farbstoffe zur Anwendung gelangen.In the method according to the invention, a fiber web is first formed in the usual manner, wherein as fiber material either cellulose ether fibers, which are soluble in aqueous alkaline solutions, but in Are not soluble in water, or a mixture of at least 0.2 parts by weight of the above cellulose ether fibers and 1 part by weight of a common paper fiber material, such as natural fibers, organic fibers, inorganic fibers, regenerated fibers, linters, bast fibers, straw fibers or the like can be used, and, if necessary, the fibers together with auxiliaries such as sizing or sizing agents or Dyes are used.
Die hierbei verwendeten Celluloseätherfasern bestehen aus Cellulosederivaten, die in solchem Ausmaß veräthert wurden, daß sie in einer wäßrigen alkalischen Lösung löslich sind, jedoch nicht in Wasser. Zu derartigen Cellulosederivaten gehören Carboxyalkylcellulosen, wie saure Carboxymethylcellulose, mehrwertige Metallsalze hiervon, beispielsweise die Al-, Sn-, Zn- und Fe-Salze, Hydroxyalkylcellulosen wie Hydroxyäthylcellulose, Alkylcellulosen wie Äthylcellulose, Cyanoalkylcellulosen wie Cyanoäthylcellulose, Carbamylalkylctllulosen wie Carbamyläthylcellulosen und Sulfoalkylcellulosen wie Sulfoäthylcellulose.The cellulose ether fibers used here consist of cellulose derivatives, which are etherified to such an extent were found to be soluble in an aqueous alkaline solution but not in water. To such Cellulose derivatives include carboxyalkyl celluloses, such as acidic carboxymethyl cellulose, polyvalent Metal salts thereof, for example the Al, Sn, Zn and Fe salts, hydroxyalkyl celluloses such as hydroxyethyl cellulose, Alkyl celluloses such as ethyl cellulose, cyanoalkyl celluloses such as cyanoethyl cellulose, carbamyl alkyl cellulose such as carbamylethyl celluloses and sulfoalkyl celluloses such as sulfoethyl cellulose.
Die wie vorstehend beschrieben hergestellte Bahn unterscheidet sich kaum von der üblichen Bahn in Aussehen und Form und kann in diesem Zustand zur Beschriftung und zum Druck verwendet werden. Gewöhnlich ist jedoch bei den Papieren, die die Celluloseätherfasern enthalten, die Dichte dieses Papieres relativ gering, d. h. es ist relativ porös. Da dieses Papier somit beim Druck eine unnötig große Menge an Druckfarbe und weiterhin in ungleichmäßiger Weise absorbiert,The sheet prepared as described above hardly differs in appearance from the usual sheet and shape and can be used in this state for lettering and printing. Usually however, in the case of papers containing the cellulose ether fibers, the density of this paper is relative low, d. H. it is relatively porous. Because this paper thus uses an unnecessarily large amount of printing ink when printing and continues to absorb in an uneven manner,
22 Ol22 Ol
kann seine Druckfähigkeit nicht als zufriedenstellend betrachtet werden.its printability cannot be considered satisfactory.
Zur Erzielung von Bahnen mit einer guten Druckfähigkeit, wobei die Druckfähigkeit ohne Verschlechterung der Fähigkeit der Auflösung oder Dispergierung in einer wäßrigen alkalischen Lösung verbessert werden kann, wird die Bahn mit einem alkalilöslichen wäßrigen Oberflächenbehandlungsmittel beschichtet und anschließend getrocknet, wobei das Aufbringen des Oberflächenbehandlungsmittels unter Anwendung der Pigmentbeschichtungstechnik oder einer Arbeitsweise, wie sie bei Oberflächenbehandlungen von gewöhnlichen Papieren ausgeführt wird, aufgebracht wird. Es ist dabei notwendig, die Bahn vor dem Auftreten einer Reaktion zwischen dem Celluloseäther und dem in dem Überzug vorhandenen Alkali zu trocknen.To achieve webs with good printability, wherein the printability without deteriorating the ability of dissolving or dispersing in an aqueous alkaline solution can be improved, the web is with an alkali-soluble aqueous Surface treatment agent coated and then dried, the application of the Surface treatment agent using the pigment coating technique or a working method, as it is carried out in the surface treatment of ordinary papers. It is It is necessary to check the web before a reaction occurs between the cellulose ether and that in the Coating existing alkali to dry.
Gemäß der Erfindung ist es erforderlich, daß sich die Bahn mit dem aufgetragenen Oberflächenbehandlungsmittel in einer wäßrigen alkalischen Lösung löst oder dispergiert. Dadurch ergibt sich eine Beschränkung hinsichtlich der alkalilöslichen wäßrigen Oberflächenbehandlungsmittel, die verwendet werden können. Das Oberflächenbehandlungsmittel muß eine Substanz enthalten, die einen trockenen Filmüberzug bildet, welcher in einer wäßrigen alkalischen Lösung löslich ist, jedoch in Wasser nicht löslich ist. Beispiele für derartige Substanzen sind partiell verseifte Polyvinylacetate, Äthylen-Acrylsäure-Copolymere, Äthylacrylat-Methylacrylsäure-Copolymere, 2-Äthylhexylacrylat-Methacrylsäure-Copolymere, Casein, Celluloseether und Gemische von derartigen Substanzen. Verseiftes Polyvinylacetat, Natnumalginat. Gummi arabicum, modifizierte Stärken und Copolymere vom Acrylesterlyp können ebenfalls zusammen mit den vorstehend aufgeführten Substanzen verwendet werden. Es können auch Pigmente, wie Tone, Calciumcarbonat, Kaolin, Titandioxyd, Talk und Zinkoxyd, wie sie in den üblichen Pigmentuberzügen verwendet werden, und die in den klaren Überzügen verwendeten Färbungsmittel als Bestandteile in dem vorstehend beschriebenen wäßrigen Oberflächenbehandlungsmittel vorhanden sein.According to the invention it is necessary that the The web with the applied surface treatment agent dissolves in an aqueous alkaline solution or dispersed. This results in a restriction with regard to the alkali-soluble aqueous surface treatment agents, which can be used. The surface treatment agent must contain a substance which forms a dry film coating which is soluble in an aqueous alkaline solution, however is not soluble in water. Examples of such substances are partially saponified polyvinyl acetates, ethylene-acrylic acid copolymers, Ethyl acrylate-methacrylic acid copolymers, 2-ethylhexyl acrylate-methacrylic acid copolymers, Casein, cellulose ethers and mixtures of such substances. Saponified polyvinyl acetate, Sodium alginate. Gum arabic, modified starches and copolymers of acrylic ester glycol can also be used can be used together with the substances listed above. It can also use pigments, such as Clays, calcium carbonate, kaolin, titanium dioxide, talc and zinc oxide, as they are in the usual pigment coatings are used, and the coloring agents used in the clear coatings as ingredients in the aqueous surface treatment agents described above may be present.
Die Celluloseäther, die gemäß der Erfindung zur Anwendung gelangen, werden durch Veretherung von Cellulosederivaten in solchem Ausmaß, daß sie in einer wäßrigen alkalischen Lösung löslich werden, jedoch nicht in Wasser, erhalten. Das geeignete Ausmaß der " Verätherung kann nicht allgemein angegeben werden, da dessen Bereich in Abhängigkeit von den einzelnen Cellulosederivaten variiert, jedoch sind, um Beispiele anzugeben, die folgenden Bereiche günstig: ein Veräilici ungsgrad im Bereich von 0,1 bis 1,0 im Fall von Carboxymethylcellulose und deren mehrwertiger Metallsalze, von 0,17 bis 0,5 im Fall von Hydroxyäthylcellulose, von 0,2 bis 0,5 im Fall von Äthylcellulose, von 0,1 bis 0,4 im Fall von Methylcellulose und von 0,08 bis 0,18 im Fall von Sulfoäthylcellulose.The cellulose ethers that are used according to the invention are by etherification of Cellulose derivatives to such an extent that they become soluble in an aqueous alkaline solution, however not in water. The appropriate degree of "etherification" cannot generally be stated however, since the range thereof varies depending on the individual cellulose derivatives, these are examples indicate the following areas favorable: a Veräilici degree of efficiency in the range of 0.1 to 1.0 in the case of Carboxymethyl cellulose and its polyvalent metal salts, from 0.17 to 0.5 in the case of hydroxyethyl cellulose, from 0.2 to 0.5 in the case of ethyl cellulose, from 0.1 to 0.4 in the case of methyl cellulose and from 0.08 to 0.18 in the case of sulfoethyl cellulose.
Die folgenden Beispiele dienen zur weiteren Erläuterung der Erfindung. Die Prozentsätze sind in den Beispielen in jedem Fall auf das Gewicht bezogen.The following examples serve to further illustrate the invention. The percentages are in the examples in each case based on weight.
60 Beispiel 1 60 Example 1
Zu einem Verätherungsgrad von 0,45 verätherte Fasern von Carboxymethylcellulose wurden bis zu 35° SR geschlagen oder gemahlen und anschließend zu einem Hochqualitätspapier von 55 g/m2 auf einer Fourdrinier-Papiermaschine verarbeitet. Obwohl dieses Papier für Zwecke wie Beschriftung, Maschinenbeschriftung und Druck verwendet werden konnte, waren die aulgedruckten Buchstaben undeutlich. Es war deshalb nicht für Druckzwecke geeignetFibers of carboxymethyl cellulose etherified to a degree of etherification of 0.45 were beaten or ground up to 35 ° SR and then processed to a high quality paper of 55 g / m 2 on a Fourdrinier paper machine. Although this paper could be used for purposes such as lettering, machine lettering, and printing, the printed letters were indistinct. It was therefore unsuitable for printing
Eine wäßrige alkalische Lösung, die als Substanzen zur Bildung des trockenen Filmes 5% eines teilweise verseiften Produktes von Polyvinylacetat und 10% Casein enthielt, wurde zu einem Gemisch aus 90 Teilen Kaolin und 10 Teilen Titandioxid in solcher Menge zugesetzt, daß der Feststoffgehalt 30% betrug. Das Oberflächenbehandlungsmittel wurde auf das vorstehend genahnte Papier nach dem Walzenauftragsverfahren in einer Menge von 15 g/m2 aufgetragen und getrocknet Das beschichtete Papier wurde durch einen 5stufigen Superkalander, der bis zu 20 kg/cm2 Druck hatte, geführt An aqueous alkaline solution containing, as substances for forming the dry film, 5% of a partially saponified product of polyvinyl acetate and 10% of casein was added to a mixture of 90 parts of kaolin and 10 parts of titanium dioxide in such an amount that the solids content was 30% . The surface treatment agent was applied to the above-mentioned paper by the roller application method in an amount of 15 g / m 2 and dried. The coated paper was passed through a 5-stage supercalender which had a pressure of up to 20 kg / cm 2
Wenn das erhaltene Papier nach dem Offset-Druckverfahren bedruckt wurde, war es kaum von einem üblichen Druckpapier hinsichtlich der Druckfähigkeit zu unterscheiden und es wurde ein klarer Druck erhalten. Wenn dieses Papier als Etikett für eine Flasche verwendet wurde und im Zustand der Fixierung an der Flasche in eine wäßrige NaOH-Lösung mit 2% Konzentration von Raumtemperatur eingebracht wurde, quoll das etikett in 20 bis 30 Sekunden und begann sich nach 60 Sekunden aufzulösen, und war nach 120 Sekunden vollständig gelöst, so daß keinerlei Anzeichen für seine ursprüngliche Form mehr festgestellt werden konnten.When the obtained paper was printed by the offset printing method, it was hardly of a conventional one Printing paper was distinguished in terms of printability, and a clear print was obtained. If this paper has been used as a label for a bottle and is in the state of being fixed to the Bottle was placed in an aqueous NaOH solution with 2% concentration at room temperature, the label swelled in 20 to 30 seconds and began to dissolve in 60 seconds, and was after 120 seconds completely dissolved, so that no more signs of its original shape can be found could.
Ein gemischtes Bahnmaterial aus 20% Rayonfasern, 40% Cyanoäthylcellulosefasern mit einem Verätherungsgrad von 0,25 und Methylcellulosefasern mit einem Verätherungsgrad von 0,3 wurden auf 20° SR gemahlen und anschließend zu einem Hochqualitätspapier von 60 g/m2 unter Anwendung einer Zylinderpapiermaschine verarbeitet.A mixed web of 20% rayon fibers, 40% cyanoethyl cellulose fibers with an etherification degree of 0.25 and methyl cellulose fibers with an etherification degree of 0.3 were ground to 20 ° SR and then processed into a high quality paper of 60 g / m 2 using a cylinder paper machine.
Eine wäßrige alkalische Lösung, die als Substanzen zur Bildung des trockenen Filmes 10% eines teilweise verseiften Produktes von Polyvinylacetat und 10% oxidierte Stärke enthielt, d.h. Substanzen, die in einer wäßrigen alkalischen Lösung löslich sind, jedoch nicht in Wasser, wurde zu einem Pigmentgemisch aus 50 Teilen Ton und 50 Teilen Titandioxid in solcher Menge zugegeben, daß der Feststoffgehalt 35% betrug. Dadurch wurde das Oberflächenbehandlungsmittel hergestellt, welches auf das vorstehende Papier mit dem Luftmesserauftragsverfahren in einer Menge von 20 g/m2 aufgetragen wurde, worauf getrocknet und anschließend, wie in Beispiel 1, mit einem Superkalander behandelt wurde.An aqueous alkaline solution containing, as substances for forming the dry film, 10% of a partially saponified product of polyvinyl acetate and 10% of oxidized starch, ie substances which are soluble in an aqueous alkaline solution but not in water, was made into a pigment mixture 50 parts of clay and 50 parts of titanium dioxide were added in such an amount that the solids content was 35%. Thereby, the surface treatment agent was prepared, which was applied to the above paper by the air knife application method in an amount of 20 g / m 2 , followed by drying and then, as in Example 1, treated with a supercalender.
Das erhaltene Papier hatte das Aussehen von Kunstpapier und wenn es nach dem Photogravurverfahren bedruckt wurde, wurde ein klarer Druck erhalten.The paper obtained had the appearance of art paper and when it was photo-engraved was printed, a clear print was obtained.
Wenn dieses Papier als Etikett von Glaswaren für den klinischen Gebrauch in einem Krankenhaus verwendet wurde und nach dem Gebrauch in eine 3%ige wäßrige NaOH-Lösung vom Raumtemperatur mit fixiertem Etikett eingebracht wurde, quoll das Etikett, wie in Beispiel 1, und löste sich unter Dispergierung der Bestandteile und der Einzelfasern leicht auf.When this paper is used as a label of glassware for clinical use in a hospital and after use in a 3% aqueous NaOH solution from room temperature with fixed Label was applied, the label swelled as in Example 1 and came off to disperse the Components and the individual fibers easily.
Ein gemischtes Bahnmaterial aus 70% Kraftzellstoff und 30% Äthylcellulosefasern mit einem Verätherungsgrad von 0,3 wurde auf 35° SR gemahlen und dann mitA mixed sheet material of 70% kraft pulp and 30% ethyl cellulose fibers with a degree of etherification from 0.3 was ground to 35 ° SR and then with
10% Ton, bezogen auf das Gesatntgewicht, versetzt, worauf das Gemisch zu einem feinen Papier mit 55 g/m2 auf einer Yankee-Papiermaschine verarbeitet wurde.10% clay, based on the total weight, was added, whereupon the mixture was processed into a fine paper with 55 g / m 2 on a Yankee paper machine.
Dann wurde die Oberfläche des erhaltenen Papieres mit einer 5%igen wäßrigen Ammoniumcarboxynethylcelluloselösung nach dem Messerstreichverfahren in solcher Menge überzogen, daß ein Auftrag von 7 g/m2 erhalten wurde. Anschließend wurde getrocknet, das Papier kalandriert und aufgewickeltThen the surface of the paper obtained was coated with a 5% aqueous ammonium carboxyethyl cellulose solution by the knife coating method in such an amount that an application of 7 g / m 2 was obtained. It was then dried, and the paper was calendered and wound up
Das erhaltene Papier hatte das Aussehen eines feinen Papieres und seine Druckfähigkeit war ausgezeichnet Falls dieses Papier in eine wäßrige Natriumsilicatlösung mit einer Konzentration von 6% von 400C eingebracht wurde, quoll es in 60 Sekunden und 2 Minuten später war es vollständig in die Einzelnem aufgelöst, die die Bestandteife des Papieres bildeten.The paper obtained had the appearance of fine paper and its printability was excellent. If this paper was placed in an aqueous sodium silicate solution having a concentration of 6% at 40 ° C., it swelled in 60 seconds and 2 minutes later it was completely dissolved that made up the constituent parts of the paper.
Ein gemischtes Bahnmaterial aus 50% Aluminium-Carboxymethylcellulosefasern und 50% Unters wurde verwendet und Papier mit 52 g/m2 hieraus mittels einer Papiermaschine hergestelltA mixed sheet of 50% aluminum-carboxymethyl cellulose fibers and 50% under was used, and paper of 52 g / m 2 was made therefrom by means of a paper machine
Dann wurden beide Seiten dieses Papieres mit einem wäßrigen Oberflächenbehandlungsmittel beschichtet, das als Substanzen zur Bildung des trockenen Filmes 2^% eines Äthylen-Acrylsäure-Copolymeren und 2,5% oxidierte Stärke enthielt, wobei die Auftragung nach der Doppelbeschichtungstechnik erfolgte. Das Papier wurde dann getrocknet und superkalandriertThen both sides of this paper were coated with an aqueous surface treatment agent, that as substances for the formation of the dry film 2 ^% of an ethylene-acrylic acid copolymer and 2.5% contained oxidized starch, the application using the double coating technique. The paper was then dried and supercalendered
Das erhaltene Papier hat eine hervorragende Druckfähigkeit. Dieses Papier löste sich innerhalb 120 Sekunden in einer wäßrigen l,5%igen NaOH-Lösung bei 40° C und trennte sich in die Einzelfasern des Unters auf.The obtained paper has excellent printability. This paper came off within 120 seconds in an aqueous 1.5% NaOH solution at 40 ° C and separated into the individual fibers of the bottom on.
Claims (2)