DE2104180A1 - Controlled conductivity electrophoretic enamelling bath - by slurry substitution with aluminium hydroxide - Google Patents

Controlled conductivity electrophoretic enamelling bath - by slurry substitution with aluminium hydroxide

Info

Publication number
DE2104180A1
DE2104180A1 DE19712104180 DE2104180A DE2104180A1 DE 2104180 A1 DE2104180 A1 DE 2104180A1 DE 19712104180 DE19712104180 DE 19712104180 DE 2104180 A DE2104180 A DE 2104180A DE 2104180 A1 DE2104180 A1 DE 2104180A1
Authority
DE
Germany
Prior art keywords
slip
bath
aluminium hydroxide
conductivity
slurry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19712104180
Other languages
German (de)
Inventor
Fnedel 4830 Gutersloh Warnke Heinrich 4831 Manenfeld Kaup
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Miele und Cie KG
Original Assignee
Miele und Cie KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Miele und Cie KG filed Critical Miele und Cie KG
Priority to DE19712104180 priority Critical patent/DE2104180A1/en
Publication of DE2104180A1 publication Critical patent/DE2104180A1/en
Pending legal-status Critical Current

Abstract

The conductivity of slurry electrolyte, e.g. Na aluminate in an electroplastic enamelling bath, is controlled by complete or partial substitution of the slurry with Al hydroxide.

Description

"Verfahren zur Regulierung der Schlickerleitfähigkeit" Die Erfindung betrifft ein Verfahren zum elektrophoretischen Beschichten von Gegenständen mit Email. "Method for regulating slip conductivity" The invention relates to a method for the electrophoretic coating of objects with E-mail.

Nachteilig bei diesem bekannten Verfahren ist jedoch, daß bei der elektrophoretischen Beschichtung die Leitfähigkeit im Beschichtungsbad laufend ansteigt.A disadvantage of this known method, however, is that in the electrophoretic coating, the conductivity in the coating bath increases continuously.

Hervorgerufen wird dieser Anstieg der Leitfähigkeit in erster Linie durch Alkaliionen, wie z.B. Natriumionen.This increase in conductivity is primarily caused by alkali ions such as sodium ions.

Die Natriumionen sind im Schlicker bereits durch das Auswaschen von Alkaliionen aus der Fritte während des Naßmahlprozesses und durch die Zugabe von Natriumaluminat oder dergleichen enthalten. Während des elektrophoretischen Beschichtungsprozesses wandern sie auf Grund ihrer positiven Ladung zur Kathode. An der Kathode geben die Natriumionen ihre Ladung ab und reagieren spontan mit dem Wasser. Die Reaktion der Natriumionen mit dem Wasser führt zur Bildung von Natriumhydroxid, welches durch Dissoziation das positiv geladene Natriumion und das negativ geladene Hydroxidion ergibt.The sodium ions are already in the slip after being washed out Alkali ions from the frit during the wet milling process and through the addition of Contain sodium aluminate or the like. During the electrophoretic coating process they migrate to the cathode due to their positive charge. At the cathode they give Sodium ions lose their charge and react spontaneously with the water. The reaction of the Sodium ions with the water leads to the formation of sodium hydroxide, which through Dissociation of the positively charged sodium ion and the negatively charged hydroxide ion results.

Für die elektrophoretische Emailbeschichtung wird anfangs ein Ansatzschlicker gemahlen und in das elektrophoretieche Beschichtungsbad gegeben. Da bei der elektrophoretischen Beschichtung laufend Email verbraucht wird, ist es notwendig, daß ein Nachsatzschlicker zugegeben wird.A batch slip is initially used for the electrophoretic enamel coating ground and placed in the electrophoretic coating bath. As with the electrophoretic Coating enamel is consumed on an ongoing basis, it is necessary that a make-up slip is admitted.

Die Natriumionen aus dem Ansatz- oder Nachsatzschlicker werden nur geringfügig durch Verschleppung aus dem Beschichtungsbad entfernt.The sodium ions from the batch or make-up slip are only slightly removed from the coating bath due to carry-over.

Somit steigt laufend der Gehalt an Natriumionen in dem elektrophoretischen Beschichtungsbad und somit auch die Leitfähigkeit des elektrophoretischen Beschichtungsbades an.Thus the content of sodium ions in the electrophoretic is continuously increasing Coating bath and thus also the conductivity of the electrophoretic coating bath at.

Für die Deionisierung eines elektrophoretischen Beschichtungsbades sind bereits verschiedene Vorschläge gemacht worden.For the deionization of an electrophoretic coating bath various proposals have already been made.

So ist z.B. bekannt, den Schlicker über einen Ionenaustauscher zu deionisieren oder das im Schlicker befindliche Wasser durch deionisiertes Frischwasser zu ersetzen.It is known, for example, to add the slip via an ion exchanger deionize or the water in the slip with deionized fresh water to replace.

Die Anwendung dieser Methoden sind in den meisten Fällen jedoch nicht einfach. Außerdem stören sie einen kontinuierlichen Arbeitsablauf.However, in most cases, these methods are not applied simple. They also disrupt a continuous workflow.

Die Aufgabe der Erfindung ist deshalb, diese bekannten Nachteile zu vermeiden und ein Verfahren zu offenbaren, bei welchem die Leitfähigkeit des Schlickers in einem elektrophoretischen Beschichtungsbad mit einfachen Mitteln reguliert werden kann.The object of the invention is therefore to address these known disadvantages avoid and disclose a method in which the conductivity of the slip can be regulated in an electrophoretic coating bath with simple means can.

Zu diesem Zweck ist die Erfindung dadurch gekennzeichnet, daß die im Schlicker erforderlichen Elektrolyte, wie z.B. das Natriumaluminat gang oder teilweise durch Aluminiumhydroxid ersetzt werden. Ein weiteres Merkmal der Erfindung ist, daß die im Nachsatzschlicker erforderlichen Elektrolyte, wie z.B. das Natriumaluminat ganz oder teilweise durch Aluminiumhydroxid ersetzt werden.To this end, the invention is characterized in that the electrolytes required in the slip, such as the sodium aluminate gang or can be partially replaced by aluminum hydroxide. Another feature of the invention is that the electrolytes required in the make-up slip, such as sodium aluminate be replaced in whole or in part by aluminum hydroxide.

Aluminiumhydroxid bildet in alkalischer Lösung Aluminate. Ersetzt man im Schlicker z.B. das Natriumaluminat durch Aluminiumhydroxid, so bildet es mit den Natriumionen, die im Schlicker durch Auswaschung der Fritte während des Mahlprozesses entstanden sind, Natriumaluminat.Aluminum hydroxide forms aluminates in alkaline solution. Replaces If, for example, the sodium aluminate is formed in the slip by aluminum hydroxide, it is formed with the sodium ions in the slip by washing out the frit during the Grinding process, sodium aluminate.

Damit ist ein bestimmter Gehalt an Natriumaluminat im Schlicker enthalten.This means that the slip contains a certain amount of sodium aluminate.

Ist z.B. bei einem Ansatzschlicker der so gebildete Anteil an Natriumaluminat zu gering, so kann-durch eine zusätzliche Zugabe von Natriumaluminat die Leitfähigkeit des Schlickers reguliert werden. Wenn sich während der elektrophoretischen Beschichtung der Anteil der Natriumionen im Beschichtungsbad erhöht, so kann durch Zusatz eines Nachsatzschlickers, bei welchem das Natriumaluminat ganz oder teilweise durch Aluminiumhydroxid ersetzt ist, die gewünschte Leitfähigkeit wieder eingestellt werden.For example, in the case of a batch slip, this is the proportion of sodium aluminate formed in this way too low, the conductivity can be reduced by an additional addition of sodium aluminate of the slip can be regulated. If during the electrophoretic coating the proportion of sodium ions in the coating bath increases, so can by adding a Make-up slip, in which the sodium aluminate is completely or partially replaced by aluminum hydroxide is replaced, the desired conductivity can be set again.

Die Schlickerleitfähigkeit läßt sich nicht nur durch den Gehalt an Natriumionen verändern, sondern auch durch alle anderen Alkali-oder Erdalkaliionen, welche an der Kathode ihre Ladung verlieren, mit dem Wasser reagieren und dabei Hydroxid bilden.The slip conductivity can not only be determined by the content of Change sodium ions, but also through all other alkali or alkaline earth ions, which lose their charge at the cathode, react with the water and thereby Form hydroxide.

Claims (2)

PatentansprUche: Patent claims: Verfahren zur Regulierung der Schlickerleitfähigkeit bei der elektrophoretischen Emailabscheidung, dadurch gekennzeichnet, daß die in Schlicker erforderlichen Elektrolyte, wie z.B. das Natriumaluminat, ganz oder teilweise durch Aluminiumhydroxid ersetzt werden.Process for regulating the slip conductivity in electrophoretic Enamel deposition, characterized in that the electrolytes required in slip, such as sodium aluminate, completely or partially replaced by aluminum hydroxide will. 2) Verfahren zur regulierung der Schlickerleitfähigkeit bei der elektrophoretischen Emailabscheidung, dadurch gekennzeichnet, daß die im Nachsatzschlicker erforderlichen Elektrolyte, wie z.-B. das Natriumaluminat, ganz oder teilweise durch Aluminiumhydroxid ersetzt werden.2) Procedure for regulating the slip conductivity in the electrophoretic one Enamel deposition, characterized in that those required in the make-up slip Electrolytes, such as the sodium aluminate, in whole or in part with aluminum hydroxide be replaced.
DE19712104180 1971-01-29 1971-01-29 Controlled conductivity electrophoretic enamelling bath - by slurry substitution with aluminium hydroxide Pending DE2104180A1 (en)