DE2064601B2 - ADDITIVE FOR COLLECTOR LUBRICANT - Google Patents

ADDITIVE FOR COLLECTOR LUBRICANT

Info

Publication number
DE2064601B2
DE2064601B2 DE19702064601 DE2064601A DE2064601B2 DE 2064601 B2 DE2064601 B2 DE 2064601B2 DE 19702064601 DE19702064601 DE 19702064601 DE 2064601 A DE2064601 A DE 2064601A DE 2064601 B2 DE2064601 B2 DE 2064601B2
Authority
DE
Germany
Prior art keywords
collector
lubricant
additive
particles
electrical machines
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19702064601
Other languages
German (de)
Other versions
DE2064601A1 (en
DE2064601C3 (en
Inventor
Wolfgang Samen Krebs (Schweiz)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maxon Motor AG
Original Assignee
Interelectric AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Interelectric AG filed Critical Interelectric AG
Priority claimed from DE19702064601 external-priority patent/DE2064601C3/en
Priority to DE19702064601 priority Critical patent/DE2064601C3/en
Priority to AT187371A priority patent/AT325709B/en
Priority to DE19712124425 priority patent/DE2124425A1/en
Priority to NL7116420A priority patent/NL7116420A/xx
Priority to CH1855271A priority patent/CH529455A/en
Priority to JP724083A priority patent/JPS5613983B1/ja
Publication of DE2064601A1 publication Critical patent/DE2064601A1/en
Publication of DE2064601B2 publication Critical patent/DE2064601B2/en
Publication of DE2064601C3 publication Critical patent/DE2064601C3/en
Application granted granted Critical
Expired legal-status Critical Current

Description

Die Erfindung betrifft eine neuartige Verwendung von Schmiermitteln als Kollektorschmiermittel.The invention relates to a novel use of lubricants as collector lubricants.

Es ist bereits die Verwendung von Indium in feinster Verteilung in Lagerschmierölen bekannt Hierdurch wird erreicht, daß die Lagerflächen in Betriebszuständen, in denen sie sich mangels hydrodynamischer Schmierung berühren, durch Gleitreibung unter Wirkung des Indiums aufeinanderlaufen, so daß sie gutes Einlaufverhalten und gute Notlaufeigenschaften haben Sowie wenig zum Fressen neigen.The use of indium in extremely fine distribution in bearing lubricating oils is already known it is achieved that the bearing surfaces in operating states in which they are due to lack of hydrodynamic Touch lubrication, run together by sliding friction under the action of the indium, so that they are good Run-in behavior and good emergency running properties as well as have little tendency to seize.

Es ist ferner bekannt, Lagerschmiermitteln durch Zusatz von Metatiteilchen einen hohen Tropfpunkt sowie hohe Druckfestigkeiten zu verleihen.It is also known to give bearing lubricants a high drop point by adding meta-particles as well as giving high compressive strengths.

Die Anmelderin hat überraschenderweise gefunden, daß die Verwendung von Teilchen einer Größe von unterhalb 100 Mikron aus einem Metall der Gruppen III bis V des periodischen Systems der Elemente mit einem Schmelzpunkt unterhalb 3000C als Zusatz in einem Kollektorschmiermittel für elektrische Maschinen eine wesentliche Erhöhung der Strombelastbarkeit bzw. der Lebensdauer von Kollektoren bei hohen Strombelastungen mit sich bringtThe applicant has surprisingly found that the use of particles below 100 microns in size from a metal from groups III to V of the periodic table of elements with a melting point below 300 ° C. as an additive in a collector lubricant for electrical machines significantly increases the current carrying capacity or the service life of collectors with high current loads

Die Metallteilchen sollten vorzugsweise in einem Größenbereich von 1 bis 20 Mikron liegen. Vorteilhafterweise sind sie dem Kollektorschmiermittel in suspendierter Form zugesetztThe metal particles should preferably range in size from 1 to 20 microns. Advantageously they are added to the collector lubricant in suspended form

Die Erfindung ist im folgenden an einem Ausführungsbeispiel ergänzend beschrieben.The invention is additionally described below using an exemplary embodiment.

Als Flüssigkeit in der die Teilchen aus einem niedrigschmelzenden Metall suspendiert sind, wird ein chemisch passives, wärme- und kältebeständiges, silikonfreies Schmiermittel verwendet das keine organischen und anorganischen Säuren enthält In 100 g dieser Flüssigkeit werden 10 g Zinnteilcher von kugeliger Gestalt mit einer Korngröße im Bereich von 1 bis 15 Mikron suspendiert Der Gewichtsanteil der Teilchen in der Flüssigkeit läßt sich in einem weiten Bereich verändern, ohne daß die Kommutierung ungünstigThe liquid in which the particles of a low-melting metal are suspended is a chemically passive, heat and cold resistant, silicone-free lubricant that does not use organic and inorganic acids contains In 100 g of these 10 g of spherical tin particles with a grain size in the range from 1 to 15 become liquid Micron suspended The weight fraction of the particles in the liquid can be varied within a wide range change without the commutation being unfavorable

ίο beeinflußt wird.ίο is influenced.

Auf den zu behandelnden Kollektor wird das Kollektorschmiermittel in einer solchen Menge aufgetragen, daß der gesamte Kollektor benetzt ist Dabei hat sich gezeigt daß selbst sehr geringe Mengen desThe collector lubricant is applied to the collector to be treated in such an amount that that the entire collector is wetted. It has been shown that even very small amounts of the

iS Kollektorschmiermittels über lange Zeit ihre Wirkung beibehalten. Es scheint daß durch die bei der Kommutierung entstehenden Funken die Zinnteilchen geschmolzen werden und mit der Oberfläche des Kollektors oder der Bürsten verbacken. Versuche mit diesem Kollektorschmiermittel bei einem Kleinmotor mit siebenteiligem Kollektor, der einen Durchmesser von ca. 4 mm und eine Kontaktbürstenbreite von 2 mm aufwies und mit 0,8 Ampere Strom belastet wurde, ergaben eine Lebensdauer von 10 000 Stunden gegenüber einer Lebensdauer von 800 Stunden bei Verwendung der gleichen Schmierflüssigkett, jedoch ohne Zusatz von Zinnteilchen.iS collector lubricant has a long-term effect maintained. It appears that the sparks produced during commutation remove the tin particles melted and baked to the surface of the collector or the brushes. Try with this collector lubricant in a small motor with a seven-part collector, which has a diameter of approx. 4 mm and a contact brush width of 2 mm and was loaded with 0.8 amps of current, gave a life of 10,000 hours versus a life of 800 hours in use the same lubricating liquid chain, but without the addition of tin particles.

Es wurden ferner Versuche mit dem Kollektorschmiermittel gemacht bei Kollektoren und Bürsten aus verschiedenen Metallen und Legierungen, wobei sich zeigte, daß die Wirkung des Kollektorschmiermiitels verhältnismäßig unabhängig ist von der Materialzusammensetzung des Kollektors und der damit zusammenwirkenden Bürsten.Attempts have also been made with the collector lubricant on collectors and brushes various metals and alloys, which showed that the effect of the collector lubricant is relatively independent of the material composition of the collector and the interacting with it To brush.

Nach den bisherigen Untersuchungen beruht die Wirkung der Teilchen aus einem niedrigschmelzenden Material darauf, daß diese Teilchen beim Stromdurchgang schmelzen und dabei praktisch ein flüssiges metallenes Schmiermittel bilden, weiches zu einem sehr geringen Übergangswiderstand führt.According to previous investigations, the effect of the particles is based on a low-melting point Material on the fact that these particles melt when the current passes through and thereby practically a liquid form a metallic lubricant, which leads to a very low contact resistance.

Das Kollektorschmiermittel verringert auch die Materialwanderung zwischen Kollektor und Bürsten.The collector lubricant also reduces material migration between the collector and the brushes.

Diese Wirkungen führen zu einer Lebensdauerverlängerung bis zum Zehnfachen verglichen mit den bisher bekannten Kollektorschmiermitteln.These effects lead to a life extension of up to ten times compared to the previous one known collector lubricants.

Die erfindungsgemäße Verwendung der betreffenden Metallteilchen als Zusatz zu einem Kollektorschmiermittel ist gerade bei Metallbürsten — im Gegensatz zu selbstschmierenden Graphitbürsten — ganz besonders wirkungsvoll.The use according to the invention of the metal particles in question as an additive to a collector lubricant is especially special with metal brushes - in contrast to self-lubricating graphite brushes effective.

Claims (4)

Patentansprüche:Patent claims: L Verwendung von Teilchen einer Größe von unterhalb 100 Mikron aus einem Metall der Gruppen IH bis V des periodischen Systems der Elemente mit einem Schmelzpunkt unterhalb 3000C als Zusatz in einem Kollektorschmiermittel für elektrische Maschinen. L Use of particles below 100 microns in size from a metal from groups IH to V of the periodic table of the elements with a melting point below 300 ° C. as an additive in a collector lubricant for electrical machines. 2. Verwendung von Zinn- und/oder indiumteilchen nach Anspruch 1 als Zusatz in einem Kollektorschmiermittel für elektrische Maschinen.2. Use of tin and / or indium particles according to claim 1 as an additive in one Collector lubricants for electrical machines. 3. Verwendung von Metallteilchen einer Größe von 1 bis 20 Mikron nach den Ansprüchen 1 und 2 als Zusatz in einem Kollektorschmiermittel für elektrische Maschinen.3. Use of metal particles having a size of 1 to 20 microns according to claims 1 and 2 as Additive in a collector lubricant for electrical machines. 4. Verwendung von Metallteilchen in suspendierter Form nach den Ansprüchen 1 bis 3 als Zusatz in einem Kollektorschmiermittel für elektrische Maschinen. 4. Use of metal particles in suspended form according to claims 1 to 3 as an additive in a collector lubricant for electrical machines.
DE19702064601 1970-12-30 1970-12-30 Additive for collector lubricant Expired DE2064601C3 (en)