DE2049144A1

DE2049144A1 - Sandwiched insulating panel - with filled polyester resin and methacrylic resin layers

Info

Publication number: DE2049144A1
Application number: DE19702049144
Authority: DE
Inventors: Hans Peter 2800 Bremen. E04c 2-36 Liebegott
Original assignee: DS-Chemie GmbH & Co KG, 2800 Bremen
Priority date: 1970-10-07
Filing date: 1970-10-07
Publication date: 1972-06-15

Abstract

Heat, sound and damp insulating wall panel consists of two layers of different materials, one of which is a hardened, unsaturated polyester foam (I) whilst the other material is a methacrylic resin which is combined with (I) before hardening and then set together with it. Pref. the materials both contain fillers, with expanded clay particles in the polyester and sand in the methacrylic resin.

Description

Verbundplatte Die Erfindung bezieht sich auf eine Verbundplatte, bestehend aus wenigstens zwei Werkstoffen ait voneinander abweichenden Materialeigenschaften. Composite panel The invention relates to a composite panel, consisting of at least two materials with material properties that differ from one another.

Verbundplatten dieser Art sind in mannigfachen Ausführungsformen bekannt. Dabei stehen wenigstens zwei Schichten aus unterschiedliches Material in inniger Verbindung. Insbesondere haben derartige Verbundplatten als Baumaterial erhebliche Bedeutung, wobei sUnw Beispiel eine Schicht eine besonders gute Wärme- und Schallisolationswirkung haben muß, wohingegen eine andere Schicht etwa besonders gute Festigkeitseigenschaften besitzen soll.Composite panels of this type are known in various forms. At least two layers of different materials are intimately connected Link. In particular, such composite panels have significant building material Meaning, where sUnw example a layer has a particularly good heat and sound insulation effect must have, whereas another layer has particularly good strength properties should own.

Gegenstand der Erfindung ist die Schaffung einer derartigen Verbundplatte mit einerseits einem besonders vorteilhaften Isolationsvermögen für Wärme und Schall und andererseits einer hinreichend großen Oberflächenhärte, so daß man sie für Bauzwecke, zum Beispiel als Wandelemente, unmittelbar verwenden kann. Dabei soll zugleich gewährleistet sein, daß ein Eindringen von Feuchtigkeit weitgehend vermieden wird.The object of the invention is to create such a composite panel with, on the one hand, particularly advantageous insulation properties for heat and sound and on the other hand a sufficiently high surface hardness so that they can be used for building purposes, to the Example as wall elements, can be used immediately. At the same time, it should be guaranteed be that a penetration of moisture is largely avoided.

Dies wird erfindungsgemäß bei einer Verbundplatte der einleitend beschriebenen Art dadurch erreicht, daß der eine Werkstoff eine an sich bekannte Schaumstruktur aus gehärtetem, umgesättigtem Polyesterharz ist, und daß der andere Werkstoff ein mit dem Ausgangsmaterial der Schaumstruktur in ungehärteten Zustand in Verbindung gebrachtes und mit diesem gemeinsam gehärtetes Methacrylatharz ist.According to the invention, this is described in the introduction for a composite panel Kind achieved in that one material has a foam structure known per se from hardened, unsaturated polyester resin, and that the other material is a in connection with the starting material of the foam structure in the uncured state brought and with this jointly hardened methacrylate resin.

Bei der an sich bekannten Schaumstruktur handelt es sich um ein ungesättigtes, zum Beispiel durch Zusatz von Benzoylperoxid gehärtetes Material, dem zuvor ein Treibmittel zugesetzt wurde.The foam structure known per se is an unsaturated, for example by adding benzoyl peroxide hardened material, which was previously a Propellant was added.

Dabei kann es sich zum Beispiel um Kohlensäuredialkylester-Anhydrid und insbesondere um ein Kohlensäurediäthylester-Anhydrid handeln. Auf diese Weise wird im Polyester von seiner Erhärtung ein Treibgas abgespalten. Da die Härtung mit Wärmeabgabe verbunden ist, kommt as gleichzeitig zur Härtung des Methacrylatharzes, dessen Ausgangsmaterial ein monomeres Methylmetacrylat in üblicher Mischung mit Benzoylperoxid ist. Die für die Aushärtung dieses Materials erforderliche Wärme entsteht also bei der Aushärtung des Polyesterharzes und braucht nicht in irgendeiner anderen Form zugeführt werden. Dieser Vorgang hat erhebliche praktische Bedeutung, weil sich sonst vor allem große Flächen nur schwer mit hinreichender Gleichmäßigkeit erwärmen lassen würden. Die Verbindung zwischen den beiden Harzen ist besonders innig.This can be, for example, dialkyl carbonate anhydride and in particular a carbonic acid diethyl ester anhydride. In this way a propellant gas is split off from the hardening of the polyester. Because the hardening is associated with the release of heat, the methacrylate resin cures at the same time, whose starting material is a monomeric methyl methacrylate in a conventional mixture Is benzoyl peroxide. The heat required to cure this material so arises during the curing of the polyester resin and does not need in any be fed to another form. This process is of considerable practical importance, because otherwise large areas in particular would be difficult to achieve with sufficient uniformity would warm up. The connection between the two resins is special intimate.

während die Schaumstruktur aus Polyesterharz eine ungewöhnlich niedrige Wärmeleitfähigkeit hat und somit hervorragend für Bauzwekce der erwähnten Art geeignet ist, verleiht die Methacrylatschicht der Verbundplatte eine beachtliche äußere Härte.while the polyester resin foam structure is unusually low Has thermal conductivity and is therefore ideally suited for building purposes of the type mentioned is, the methacrylate layer gives the composite panel considerable external hardness.

Wenn auch die Schaumstruktur aus Polyesterharz an sich eine hinreichende Druckfestigkeit hat, so ist die Oberflächenhärte dennoch zu gering, um hieraus bestehende Platten unmittelbar zu verwenden. Durch dis Methacrylatharzschicht wird dieser Nachteil jedoch behoben. Zugleich wird dadurch gewährleistet, daß in die Schaumstrukturschicht keine Flüssigkeit von der mit Methaorylatharz verbundenen Seite her eindringen kann.Even if the foam structure made of polyester resin is sufficient in itself Has compressive strength, the surface hardness is still too low to consist of it Plates immediately to use. Through the methacrylate resin layer however, this disadvantage is remedied. At the same time, this ensures that in the foam structure layer does not have any liquid from that associated with methaorylate resin Can penetrate side.

Man kann die genannte Seite der Verbundplatte mithin so gar der freien Wtterung aussetzen, was besonders fUr Leichtbauzwecke von großer Bedeutung ist.The said side of the composite panel can therefore even be the free one Expose to the weather, which is particularly important for lightweight construction purposes.

Zu einer weitergehenden Steigerung der beabsichtigten Materialeigenschaften und Senkung des Herstellungsaufwandes kommt man, wenn sowohl das Polyesterharz als auch das Methacrylatharz Füllstoffe enthalten. Diese Füllstoffe sind zweckmäßig so gewählt, daß sie beim Polyesterharz dessen Wärme- und Schallisolationswirkung steigen, wohingegen sie beim Methacrylatharz dessen Härte erhöhen. Demnach kann man für das Polyesterharz mit Vorteil Blähtonkörper verwenden, die in das noch flüssig Ausgangsmaterial eingebracht werden. Für das Methacrylatharz kommt demgegenüber als Füllstoff insbesondere Sand in Betracht.To a further increase in the intended material properties and lowering the manufacturing cost is achieved when both the polyester resin as the methacrylate resin also contain fillers. These fillers are useful chosen so that the heat and sound insulation effect of the polyester resin increase, whereas they increase the hardness of methacrylate resin. So can it is advantageous to use expanded clay bodies for the polyester resin, which are still liquid in it Starting material are introduced. For the methacrylate resin on the other hand sand is particularly suitable as filler.

Ein besondere für Bauzwecke geeignete Verbundplatte erhält man dadurch, daß ihre eine Außenschicht aue reinem Methacrylatharz besteht, der sich eine dickere Schicht aus mit Füllstoff vermischtem Methacrylatharz anschließt, die ihrerseits mit der Schaumstruktur aus Polyesterharz in Verbindung steht.A special composite panel suitable for building purposes is obtained by that their one outer layer consists of pure methacrylate resin, which is thicker A layer of methacrylate resin mixed with filler adjoins, which in turn is in connection with the foam structure made of polyester resin.

Die Außenschicht aus reinem Methacrylatharz gewährleistet dabei nicht nur eine sehr hohe Oberflächenhärte, sondern zugleich einen völlig dichten Abschluß. Die nun folgende, zum Beispiel mit Sand vermischte Methacrylatharzschicht ist zwar infolge ihres Füllstoffes auch von beträchtlicher Oberflächenhärte, jedoch insgesamt nicht so dicht wie die aus reinem Methacrylatharz bestehend Außenschicht. Die sodann folgende Schicht aus Polyesterharz besitzt bei noch befriedigender Druckfestigkeit vor allem die gewünschten Isolationswirkungen.The outer layer made of pure methacrylate resin does not guarantee this only a very high surface hardness, but at the same time a completely tight seal. The methacrylate resin layer that follows, for example mixed with sand, is due to their filler also of considerable surface hardness, but overall not as dense as the outer layer consisting of pure methacrylate resin. The then The following layer of polyester resin still has satisfactory compressive strength above all the desired insulation effects.

Eine Verbundplatte der beschriebenen Art wird zweckmäßig daduroh hergestellt, daß zunächst eine Form mit einer Schicht aus reines monomerem Methylmethacrylat, dem Benzoylperoxid in üblicher Menge zugesetzt ist, ausgestrichen wird. Diese Außen- oder Deckschicht kann nan dadurch härten, daß man hierauf Infrarotstrahler einwirken läßt. Sodann wird die Zwischenschicht aufgegossen, die aus monomerem Methylmethacrylat mit mineralischen Füllstoffen, wie insbesondere mit 86 Gewichtsprozent Sand, besteht und gleichfalls Benzoylperoxid enthält. Die Zwischenschicht ist zweckmäßig ein bis mehrere Millimeter stark. Es ist jedoch nicht erforderlich, daß man diese Zwischenschicht gleichfalls durch zusätzliche Wärmeeinwirkung zur Aushärtung bringt. Vielmehr wird auf die Zwischenschicht du in der erwähnten Weise schäumbare Polyesterharz zuss-en mit Blähton aufgebracht und in der Form belassen, bis es unter Wärmentwicklung zum Aufschäumen und Aushärten kommt. Die Wärmentwicklung reicht dann ebenfalls dazu aus, die Methylmethacrylatschicht zum Harz auszuhärten.A composite panel of the type described is expediently produced daduroh, that first a form with a layer from pure monomeric methyl methacrylate, the benzoyl peroxide is added in the usual amount, is spread out. This exterior or the top layer can be hardened by infrared emitters acting on it leaves. Then the intermediate layer, made of monomeric methyl methacrylate, is poured on with mineral fillers, such as in particular with 86 weight percent sand and also contains benzoyl peroxide. The intermediate layer is expediently a to several millimeters thick. However, it is not necessary to have this intermediate layer also brings about hardening through the action of additional heat. Rather, it will On the intermediate layer you pour foamable polyester resin in the manner mentioned applied with expanded clay and left in the form until it develops under heat Foaming and hardening comes. The heat development is then also sufficient from curing the methyl methacrylate layer to the resin.

Soweit es aus optischen Gründen zweckmäßig ist, kann man die luscrrr, Methacrylatharzschicht in an sich bekannter Weise beliebig einfärben.As far as it is expedient for optical reasons, one can use the luscrrr, Color the methacrylate resin layer as desired in a known manner.

Falls die neue Verbundplatte der Gefahr ausgesetzt ist, daß aber ihre sämtlichen Seiten Flüssigkeit eindringen kann, ist es schließlich noch angebracht, sie so auszubilden, daß ihre sämtlichen Außenschichten aus Methacrylatharz bestehen. Eine derartige Verbundplatte ist vollständig gegen das Eindringen von Flüssigkeit versiegelt und besitzt zugleich bei sämtlichen Seiten eine hinreichende Oberflächenhärte.If the new composite panel is exposed to the risk that your liquid can penetrate all sides, it is still advisable to to train them so that all of their outer layers are made of methacrylate resin. Such a composite panel is completely against the ingress of liquid sealed and at the same time has sufficient surface hardness on all sides.

Zur weiteren Veranschaulichung der Erfindung sei auf die schematischen, sich auf ein Ausführungsbeispiel beziehende Zeichnung Bezug genommen.To further illustrate the invention, refer to the schematic, Reference is made to an exemplary embodiment drawing.

Bei der ausschnittweise dargestellten Verbundplatte erkennt man drei Schichten. Die äußere Schicht 1 besteht aus reinem Methacrylatharz. In inniger Verbindung an die Außenschicht 1 schließt sich die Zwischenschicht 2 an, die aus Methacrylatharz mit 85 Gewichtsprozent Sand hergestellt ist. Auf diese Zwischenschicht folgt die aus Polyesterharz bestehende Schaumstruktur 3, in die Blähtonkörper 4 eingebunden sind. Die Schaumporen sind, wenngleich sie zeichnerisch nicht dargestellt wurden} in der gesamten Schaumstruktur 3 vorhanden, wohingegen die Schichten 1 und 2 vollständig dicht sind.The composite panel shown in detail shows three Layers. The outer layer 1 consists of pure methacrylate resin. In close connection the outer layer 1 is followed by the intermediate layer 2, which is made of methacrylate resin is made with 85 weight percent sand. To this Intermediate layer This is followed by the foam structure 3 made of polyester resin, into the expanded clay body 4 are involved. The foam pores are, although they are not shown in the drawing } were present in the entire foam structure 3, whereas the layers 1 and 2 are completely tight.

Claims

PATENT CLAIMS

1. Composite panel, consisting of at least two materials with each other deviating material properties, characterized by the fact that the one material a known foam structure made of hardened, unsaturated polyester resin is, and that the other: material one with the starting material of the foam structure in the unhardened state associated and hardened together with this Is methacrylate resin.

2. composite panel according to claim 1, characterized in that both the polyester resin and the methacrylate resin contain fillers.

3. Composite panel according to claims 1 and 2, characterized gekennzeicnet, that the polyester resin has expanded clay body (4) as filler.

4. Composite panel according to claims 1 to 3, characterized in that that the methacrylate resin (2) contains sand as a filler.

5. Composite panel according to claims 1 to 4, characterized in that that their one outer layer (1) consists of pure methacrylate resin, constitutes one thicker intermediate layer of methacrylate resin (2) mixed with filler, which in turn is connected to the foam structure (3) made of polyester resin.

6. Composite panel according to claims 1 to 5, characterized in that that its outer layer (1) consisting of methacrylate resin is colored.

7. Composite panel according to claims 1 to 6, characterized in that that all outer sides have layers of methacrylate resin.