DE2034180C

DE2034180C - Process for masking objects for surface treatments

Info

Publication number: DE2034180C
Authority: DE
Inventors: Seinosuke Nagoya Horiki (Japan)
Original assignee: Nagoya Yukagaku Kogyo K K , Tokai, Aichi (Japan)
Publication date: 1972-08-10

Description

, Die Erfindung bezieht sich auf ein Verfahren zum als eine Anpassungsschicht, welche Ungleichmäßig-, The invention relates to a method for as a matching layer, which unevenly-

Ί Maskieren von Gegenständen für Oberflächenbehand- keiten auf den Oberflächen, auf welchen die Schablo- Ί Masking of objects for surface treatments on the surfaces on which the template

{ ' lungen, insbesondere Oberflächenbehandlungen mit 30 nenelementeanzubringensind, ausgleicht. Als Material einem Wärmebehandlungsarbeitsgang, bei dem eine für die untere Gummischicht kommt entsprechend der ' bestimmte, von einem Überzug bzw. einer Beschichtung USA.-Patentschrift 2 363 842 natürlicher oder syn-{'lungs, in particular surface treatments with 30 elements are to be applied, compensates. As a material a heat treatment process in which one comes for the lower rubber layer according to the 'certain, from a coating or a coating USA.-Patent 2 363 842 natural or syn-

oder Plattierung freizuhaltende Teilfläche eines Gegen- thetischer Gummi oder Gummischwamm in Frage.or plating the part of the surface to be kept free of a counter-thetic rubber or rubber sponge in question.

Standes mit einem Abdeckelement aus Kunstharz- Synthetischer Gummi ist jedoch mit Kunstharz nicht schaum maskiert wird. 35 gleichzusetzen. Das Verhalten von natürlichem undStand with a cover made of synthetic resin - Synthetic rubber, however, does not work with synthetic resin foam is masked. 35 equate. The behavior of natural and

Um eine oder mehrere Teilflächen bei Oberflächen- synthetischem Gummi oder Gummischwamm ist [' behandlungen wie Überziehen bzw. Beschichten oder grundsätzlich sehr ähnlich und unterscheidet sich hin-Around one or more sub-areas in the case of surfaces - synthetic rubber or rubber sponge is ['treatments such as coating or coating or basically very similar and differs from

Galvanisieren der Oberflächen von Gegenständen von sichtlich Struktur und Temperaturverhalten und dem Überzug bzw. der Plattierung freizuhalten, Schrumpfungsverhalten ebenso grundsätzlich von den ! wurden bisher Schutzabdeckungen aus Papierstreifen, 40 sogenannten Kunstharzen. Die aus der USA.-Patent-Electroplating of the surfaces of objects with visible structure and temperature behavior and To keep the coating or the plating free, the shrinkage behavior also basically from the ! So far, protective covers were made from strips of paper, 40 so-called synthetic resins. The one from the USA.

!.' Kunstharzbeschichtungen u.dgl. verwendet. Wie die schrift 2 363 842 bekannten Schablonenelemente kön-!. ' Resin coatings and the like are used. As the template elements known from script 2 363 842 can

zu maskierenden Teilflächen jedoch in Bohrungen oder nen verwendet werden, um bestimmte Muster auf Ausnehmungen liegen, befriedigen solche gebrauch- Oberflächen von Gegenständen mit Farbe anzubringen, liehe Abdeckungen aus Papier u.dgl. nicht, da ihre Diese Schablonenelemente müssen jedoch nach dem Anbringung schwierig sowie kompliziert und eine 45 Aufbringen der Farbe abgenommen werden und sind wirksame Maskierung kaum erzielbar ist. zu einer Verwendung in Überzugsverfahren, wo eineHowever, partial areas to be masked can be used in bores or holes to create certain patterns Recesses are found to satisfy such usable surfaces of objects with paint, Borrowed covers made of paper and the like. Not because their stencil elements must be after Installation is difficult as well as complicated and an application of the paint can be removed effective masking can hardly be achieved. to use in coating processes where a

Daher wurden bisher für solche Zwecke zum, Ver- Wärmebehandlung des Überzugsmaterials nach dem stopfen der Bohrungen oder Ausnehmungen geeignete Auftragen erforderlich ist, nicht geeignet. Ein Abgeformte Gummistopfen verwendet. Beispielsweise decken von Bohrungen oder anderen Ausnehmungen wurden beim elektrophoretischen Lackieren eines 50 in Gegenständen vor dem Auftragen eines Überzugs unteren Lenkers der vorderen Radaufhängung eines ist mit diesen bekannten Schablonenelementen eben-Kraftwagens die Innenflächen der zur Aufnahme der falls nicht möglich. Die Verwendung der bekannten Lagerbuchsen bestimmten öffnungen, an denen der Schablonenelemente ist auf die Verwendung als ein-Auflrag von Lack nicht erwünscht ist, mittels in die fache »Malerschablone« zum raschen Aufbringen von öffnung getriebener Gummistopfen abgedeckt. Wenn 55 Mustern auf Oberflächen beschränkt. Für eine Verbei diesem Verfahren der lackierte oder plattierte Wendung zum Abdecken von Flächen von Gegen-Gegenstand jedoch nach der Oberflächenbehandlung ständen in der Massenproduktion sind die bekannten erhitzt wird, stellt sich bei dem Gummistopfen schnell Schablonenelemente ebenfalls nicht geeignet, da ihr Alterung und Zerfall auf Grund der Wärmeeinwirkung Aufsetzen und ihr Wiederabnehmen sehr viel Mühe ein, so daß sich die Passung zwischen Stopfen und 60 und Zeit erfordern. Insgesamt gesehen sind die beÖffnung verschlechtert und entweder die Stopfen kannten Schablonenelemente in ihrem Anwendungswährend der Behandlung abfallen oder das Überzugs- gebiet sehr beschränkt und zum Abdecken von Ausmalerial auf die Innenflächen der öffnung(en) gelangt. nehmungen und Bohrungen und anderen Oberflächen, Somit s;nd auf diese Weise befriedigende Ergebnisse insbesondere in Überzugsverfahren, bei denen dem nicht erzielbar. Darüber hinaus sind derartige Gummi- 65 Aufbringen des Überzugs eine Wärmebehandlung stopfen nach höchstenszehnmaliger Verwendung bereits nachfolgt, vollständig ungeeignet,
verbraucht, wodurch sich die Kosten eines solchen Ver- Aus der USA.-Patentschrift 2 388 835 sind Maskenfahrens beträchtlich erhöhen. Schließlich müssen die elemente bekannt, welche zum Abdecken von Bohrun-Therefore, for such purposes for heat treatment of the coating material after the bores or recesses have been plugged, suitable applications have not been suitable. A molded rubber stopper used. For example, bores or other recesses were covered by the electrophoretic painting of a 50 in objects before applying a coating to the lower arm of the front suspension of a motor vehicle with these known template elements, the inner surfaces of the to accommodate the if not possible. The use of the known bearing bushes has certain openings at which the stencil element is not desired to be used as a layer of varnish, covered by means of rubber stoppers driven into the “painter's stencil” for rapid application of the opening. When 55 patterns are limited to surfaces. For this method of lacquered or clad turning to cover surfaces of counter-objects, however, after the surface treatment stands in mass production, the known ones are heated, stencil elements quickly turn out to be unsuitable for rubber stoppers, as their aging and decay are due the application of heat and their removal again take a lot of effort, so that the fit between the plug and 60 and require time. Viewed overall, the opening is worsened and either the stoppers knew template elements fall off during the treatment or the coating area is very limited and reaches the inner surfaces of the opening (s) to cover painting. Recesses and bores and other surfaces, thus s; nd in this way satisfactory results, especially in coating processes, in which this is not achievable. In addition, such rubber is completely unsuitable, after it has been used a maximum of ten times, it is completely unsuitable,
This increases the cost of such a mask process considerably. Finally, the elements must be known which are used to cover drilling

gen und Ausnehmungen in Gegenständen, weiche an Ihrer Außenseite mit einem Überzug versehen werden sollen, verwendet werden sollen. Diese Maskenelemente werden wie .Stöpsel in die abzudeckenden Ausnehmungen eingeführt. Als Material für diese bekannten stopfenartifeen Maskenelemente ist Gummi oder Gummizusammensetzungen angegeben. Diese bekannten Gummistopfen haben Nachteile, die im Hinblick auf einen ähnlichen Stand der Technik vorslehend bereits dargelegt wurden. Selbst wenn die Mas- 10 kenelemente gemäß der USA.-Patentschrift 2388 835 äieh während des Auftragens dss Überzugs, beispielsweise während eines elektrophoretischen Auftragens, nicht lockern, verbleibt das Problem, diese Gummieine schnelle Volumenvcrkleinerung erfährt. Geeignete Kunstharzschaumstoffe sind Polystyrolschaum, Polyäthylenschaum, Polypropylenschaum, Polyacrylharzschaum sowie Schaumstoffe aus Vinylpolymeren ein-5 schließlich Vinylhomopolymere oder -mischpoiymere u.dgl.genes and recesses in objects that are provided with a coating on their outside should be used. These mask elements are like .Plugs in the to be covered Recesses introduced. The material used for these known plug-type mask elements is rubber or rubber compositions. These known rubber stoppers have disadvantages that are imposed in the With regard to a similar state of the art, provisionally have already been set out. Even if the Mas- 10 elements according to U.S. Patent 2,388,835 See the coating during application, for example during electrophoretic application, not loosening, the problem remains with these gums experiences rapid volume reduction. Suitable synthetic resin foams are polystyrene foam, polyethylene foam, Polypropylene foam, polyacrylic resin foam and foams made from vinyl polymers a-5 finally vinyl homopolymers or mixed polymers etc.

In der nachstehenden Tabelle sind einige in Versuchen ermittelte Daten äes Schrumpfverhaltens verschiedener polymerer Schaumstoffe angeführt.In the table below, some of the data on the shrinkage behavior determined in experiments are various polymer foams listed.

Bezeichnung des Polymersdesignation of the polymer

Polypropylen
I lethacrylharzPolypropylene
I methacrylic resin

Grad derdegree of

AufschlämmungSlurry

40 bis 60
20 bis 40
20 bis 40
20 bis 4040 to 60
20 to 40
20 to 40
20 to 40

SchrumpftemperaturShrinkage temperature

⁰C ⁰ C

95 bis 120 105 bis 130 110 bis 140 110 bis 14095 to 120 105 to 130 110 to 140 110 to 140

Verformungs-,Deformation,

temperaturtemperature

"C"C

65 bis 90 40 bis 50 60 bis 75 70 bis 9065 to 90 40 to 50 60 to 75 70 to 90

Der Ausdruck »Schrumpftempcratur« bezeichnet die Temperatur, bei der das Schrumpfen einsetzt. Diese liegt gewöhnlich beträchtlich über der Verformnngstemperatur des Polymers, jedoch unter der Einbrenntemperatur gebräuchlicher Beschichtungsmittel. JeThe term "shrinkage temperature" denotes the temperature at which shrinkage begins. This is usually well above the deformation temperature of the polymer, but below the stoving temperature of conventional coating agents. Ever

stopfen nach dem Auftragen des Überzugs zu ent- 15 Polystyrolstopper after applying the coating to remove 15 polystyrene

fernen. Dies muß in mühsamer Weise von Hand ge- Polyäthylen ijhehen. Diese bekannten Gummistopfen sind daher für eine Verwendung in einer Massenprouuktion nicht eeignet.distant. This has to be done laboriously by hand. Polyethylene ijhehen. These known rubber stoppers are therefore not suitable for mass production suitable.

Der Erfindung liegt die Aufgabe zugrunde, ein so
Maskierverfahren der eingangs erläuterten Art zu
schaffen, welches einfach und wirtschaftlich ist und
c-'ne zuverlässige Abdeckung Jer vor¹ Überzug freizuhaltenden Flächen während der Oberflächenbehand- , _o _ .The invention is based on the object of such
Masking method of the type explained at the beginning
create which is simple and economical and
c-'ne reliable covering Jer in front of ¹ coat of areas to be kept clear during the surface treatment-, _o _.

Iv.ng gewährleistet und ein rasches und se.bsttätiges »5 stärker ein Material aufgeschäumt ist, um so niedriger Entfernen der Abdeckung nach der Oberflächenbehand- liegt seine Schrumpf temperatur. Beispielsweise setzt jung ermöglicht. bei einem Polystyrolschaum mit einem Aufschau-Diese Aufgabe wird erfindungsgemäß dadurch ge- mungsgrad bzw. Vergrößerungsfaktor von 80 das löst, daß der mit einem bei Wärmebehandlung Schrumpfen sehr viel früherem, beispielsweise bei schrumpfenden Kunstharzschaumabdeckelement ver- 30 einer Temperatur von etwa 90⁰C. sehene Gegenstand nach dem Beschichten bis zum Bei der Auswahl des Materials für die erfindungsge-Schrumpfen des Abdeckelements erwärmt wird. mäßen Abdeckelemente ist zu beachten, daß dieses Das erfindungsgemäße Verfahren hat gegenüber nicht durch irgendwelche Bestandteile des zu ^verwendem Stand der Technik wesentliche Vorteile. Durch die denden Auftragsmaterials oder galvanischen Bades Verwendung von Kunstharzschaum als Abdeckungs- 35 angegriffen wird, da die Abdeckelemente ja wahrend material ist es möglich, die Abdeckung in großen Men- der Oberflächenbehandlung an Ort und Stelle bleiben gen rasch und mit sehr geringen Kosten herzustellen. sollen. Somit ist die Art des zu verwendenden K-unst-Die Kunstharzschaumabdeckuni, 1 lassen sich auch harzschaumstoffes in Abhängigkeit von der Zusamleitht handhaben und rasch in den abzudeckenden mensetzung des anzuwendenden Auftragsmatenais Ausnehmungen an Gegenständen oder auf abzu- 40 oder galvanischen Bades auszuwählen. Beim ^^lektr0" deckende Flächen von Gegenständen anbringen. Die phoretischen Auftragen von Melaminharz, Alkydnarz Abdeckungen können auf einfache Weise mit dem oder Akrylharz ist beispielsweise Polystyrolscnaum jeweils erforderlichen Unter- oder Übermaß hergestellt ungeeignet, da er durch die Ester, Ketone oder arowerden und gewährleisten eine zuverlässige und exakte matische Kohlenwasserstoffe enthaltenden Losungs-Abueckung der zu schützenden Flächen während des 45 mittel dieser Stoffe gelöst würde., Dagegen ist oei jeweiligen Oberflächenbehandlungsverfahrens. Nach dieser Behandlungsart Polyäthylenschaum am besten Beendigung der Oberflächenbehandlung müssen die für die Abdckelemente geeignet. Fur das; ^el<*^tr°- Abdeckungen nicht in mühsamer Weise einzeln von phoretische Auftragen von wasserlöslichen AlKyanarz-Hand von den Gegenständen abgenommen werden, Überzugsverbindungen eignet sich andererseits Poiysondern schrumpfen bei einer nachfolgenden Wärme- 50 styrolschaum hervorragend; er ergibt ausgezeicnnete behandlung auf einen Bruchteil ihres ursprünglichen Ergebnisse. . Volumens zusammen und fallen dabei selbsttätig von Die erfindungsgemäßen Abdeckelemente sine vor den Gegenständen, an denen sie bestimmte Flächen der Oberflächenbehandlung von Gegenstanden, oeiabgedeckt hatten, ab. Das erfindungsgemäße Verfahren spielsweise vor dem Lackieren oder Galvanisieren ist insbesondere zur Verwendung in der Massenferti- 55 durch einfaches Eintreieen in Ausnehmungen imu gung wo eine Vielzahl von Teilen oberflächenbe- Bohrungen oder durch Aufziehen auf bestimmte iuihandelt werden solle, geeignet. Die Abdeckungen flächen des Gegenstandes mühelos aufbringbar, müssen nur einmal verwendet werden, so daß sich Die angestellten Versuche ergaben, dall die in der zeitraubende und unwirtschaftliche Wartungs- und vorstehenden Tabelle angeführten Schaumstoffe tür Abnahmearbeit erübrigt. Insgesamt gesehen ist das 60 das erfindungsgemäße Verfahren besonders geeignet erfindungsgemäße Verfahren zuverlässig und wirt- sind. (,«„„»„ schaftlich ^{Durch das} erfindungsgemaße Verfahren können Dererfindungsgemäßve?wendbareKun*tharzschaum nicht nur Ausnehmungen oder Bohrungen in Gegen-, für die Abdeckelemente kann irgendein thermo- ständen beim Uckieren oder Galvanisieren geschiizt Dlastischer Kunstharzschaum sein, soweit dieser bei 65 werden, sondern auch solche Teilflachen wieGew.nde-Normaltemperatur genügende Elastizität und keineilei teile von Schrauben oder ADscnniue oer ^uc.mvnv Schrumpfung aufweist, dafür jedoch bei Erwärmung von Stangen oder Rohren, über eine bestimmte Temperatur, beispielsweise 90⁰C, Iv.ng is guaranteed and a material is foamed up quickly and automatically, the lower the removal of the cover after surface treatment, the lower its shrinkage temperature. For example, young allows. in a polystyrene foam having a Aufschau-This object is inventively overall mung degree or magnification factor released from 80 the that of a upon heat treatment shrink much earlier, comparable for example in shrinking Kunstharzschaumabdeckelement 30 a temperature of about 90 ⁰ C. provided The object after coating is heated until the selection of the material for the inventive shrinkage of the cover element. MAESSEN cover members is to be noted that this process of the invention has the opposite not limited by any of the components essential to ^ver wendem prior art advantages. The use of synthetic resin foam as a cover is attacked by the application material or the galvanic bath, since the cover elements are indeed possible during the material, the cover can remain in place in large quantities and the surface treatment can be produced quickly and at very low cost. should. Thus, the type of K-unst-Die Kunstharzschaumabdeckuni, 1 can also be handled resin foam depending on the composition and quickly selected in the composition of the application material to be covered, recesses on objects or on removed or electroplated baths. ^Apply covering surfaces of objects when applying. The phoretic application of melamine resin, alkyd resin coverings can be made in a simple manner with the or acrylic resin is, for example, polystyrene reliable and accurate matic hydrocarbons containing Losungs-Abueckung the protected areas during the 45 middle of these substances would be solved contrast oei respective surface treatment process after this type of treatment polyethylene foam best completion of the surface treatment for the Abdckelemente Available for need that;... ^el < * ^tr ° - covers cannot be removed from the objects in a laborious manner individually by the phoretic application of water-soluble alkyan resin by hand; it gives excellent treatment at a fraction of its original results. . The cover elements according to the invention fall off in front of the objects on which they have covered certain surfaces of the surface treatment of objects. The method according to the invention, for example, before painting or electroplating, is particularly suitable for use in mass production by simply entering into recesses where a large number of parts are to be surface-drilled or drawn onto certain objects. The cover surfaces of the object can be applied effortlessly, only have to be used once, so that the experiments made showed that the foams listed in the time-consuming and uneconomical maintenance table and the above table for acceptance work are unnecessary. Viewed overall, the method according to the invention is particularly suitable, the method according to the invention is reliable and economical. (, """""Economically ^{By means of the} method according to the invention, the synthetic resin foam that can be used according to the invention can not only have recesses or bores in counterparts, for the cover elements any thermostats can be protected during plating or electroplating. but also such partial surfaces as thread normal temperature sufficient elasticity and no parts of screws or ADscnniue oer ^ uc.mvnv shrinkage, but when rods or tubes are heated above a certain temperature, for example 90 ⁰ C,

Zum Maskieren von Ausnehmungen oder BohrungenFor masking recesses or bores

werden vorzugsweise aus Kunststoffschaum bestehende deckelemente-von Hand entfällt. Ein weiterer wich-Abdeckclemente in Form von Walzen, Ringwülsten, 'tiger Vorteil des ernndungsgemiißen Vof arjrens 'beKugeln, Zylindern, Prismen, Würfeln u. dgl/ in Ab- steht darin, daß das Maskieren mit sehr niedrigen hängigkeit von der Form oder Umrißgestalt der zu ;Kosten erfolgen kann, da der erfindungsgemäß vermaskierenden Ausnehmungen oder Bohrungen ver- 5 wendete Kunstharzschaum äußerst billjgjst.;'
wendet- Diese Abdeckelemente sind zweckmäßig so " Weitere Vorteile und Merkmale der Erfindung erbemessen, daß ihre.Querschnittsfläche,^etwas größer geben sich aus der folgenden Beschreibung von Ausist als die der Ausnehmungen oderiBohrungen, so.daß _#führungsbeispielen an Hand der Zeichnung. In dieser sie nur unter gewisser Gewaltanwendung in diese 'istcover elements made of plastic foam are preferably omitted by hand. Another advantage of the different covering elements in the form of rollers, annular beads, of the design according to the specification of spheres, cylinders, prisms, cubes and the like is that the masking is very little dependent on the shape or outline shape of the at; costs can occur, since the synthetic resin foam used according to the invention to mask recesses or bores is extremely inexpensive; '
These cover elements are wendet- heritage measure expediently "Further advantages and features of the invention that ihre.Querschnittsfläche, ^ something to give greater from the following description of the recesses is OFF when the oderiBohrungen so.daß, _# exemplary embodiments with reference to the drawing. In this it is only with a certain use of force in this'

einführbar sind und während des Lackierens oder io F i g. 1 eine Schrägansicht des unteren Lenkers derare insertable and during painting or io F i g. 1 is an oblique view of the lower link of FIG

Galvanisieren dicht und passend an der innenfläche Vorderradaufhängung eines Kraftwagens mit darinElectroplating tightly and fittingly on the inner surface of the front wheel suspension of a motor vehicle with it

der Ausnehmungen bzw. Bohrungen anliegen. eingesetzten erfindungsgemäßen Schaumstoffstopfen,the recesses or bores are in contact. used foam stopper according to the invention,

Für das Maskieren von Gewinde-Endstücken von F i g. 2 eine Schnittansicht eines Teiles des unteren Schrauben oder Abschnitten der Mantelflächen von Lenkers nach F i g. 1 nach einer Warmbehandlung Stangen oder Rohren eignen sich Abdeckelemente in 15 sowie des geschrumpften und abgelösten Schaumstoff-Form von Nippeln oder Muffen mit wenigstens einem teils,For masking threaded end pieces of FIG. Fig. 2 is a sectional view of part of the lower one Screws or sections of the lateral surfaces of the handlebar according to FIG. 1 after a heat treatment Rods or tubes are suitable cover elements in 15 as well as the shrunk and detached foam form of nipples or sleeves with at least one part,

sich zumindest über drei Viertel der Dicke des Ma- F i g. 3 eine Schrägansicht einer Stange mit einemis at least three quarters of the thickness of the dimensions. 3 is an oblique view of a rod with a

terials von der Außenseite einwärts erstreckenden erfindungsgemäßen muffenförmigen Abdeckelement,terials sleeve-shaped cover element according to the invention extending inward from the outside,

Einschnitt. F i g. 4 eine entsprechende Ansicht der gleichenIncision. F i g. 4 is a corresponding view of the same

Solche Schaumsiofi-Abdeckeiemente in Form von so Stange nach der Warmbehandlung sowie des geNippeln oder Muffen sollten zweckmäßig einen Innen- schrumpften Schaumteils,Such Schaumsiofi cover elements in the form of a rod after the heat treatment as well as the nipple or sleeves should expediently have an internally shrunk foam part,

durchmesser aufweisen, der etwas kleiner ist als der F ί g. 5 eine Schrägansicht eines Teiles einerhave a diameter that is slightly smaller than the F ί g. 5 is an oblique view of part of a

Außendurchmesser der Stange oder des Rohrs, um Schraube mit einem erfindungsgemäßen nippelförmi-Outside diameter of the rod or tube to screw with a nipple-shaped according to the invention

einen dichten Sitz zwischen der Stange bzw. dem Rohr gen Abdeckelement unda tight fit between the rod or the tube and cover element

und dem Abdeckelement zu gewährleisten. as F i g. 6 eine entsprechende Ansicht der gleichenand to ensure the cover element. as F i g. 6 is a corresponding view of the same

In der Anwendung des erfindungsgemäßen Verfah- Schraube nach der Warmbehandlung, mit dem ge-In the application of the inventive method screw after the heat treatment, with the ge

rens werden zunächst die gegen einen Auftrag oder schrumpften Schaumteil.rens are initially the against an order or shrunk foam part.

Galvanisieren zu maskierenden Ausnehmungen, Boh- B e i s ρ i e 1 1 '
rungen oder Teilflächen eines Gegenstandes mittelsElectroplating recesses to be masked, Boh- B eis ρ ie 1 1 '
stanchions or partial areas of an object by means of

der vorstehend beschriebenen Abdeckeiemente ver- se Das Beispiel bezieht sich auf den nach dem erfin-of the above-described cover elements. The example relates to the according to the invention

stopft oder abgedeckt. Darauf wird der Gegenstand dungsgemäßen Verfahren behandelten unteren Lenkerstuffs or covered. The subject of the method according to the invention is then treated lower link

mit einem gebräuchlichen Oberzugsmaterial behandelt nach F i g. 1 und 2.treated with a customary cover material according to FIG. 1 and 2.

oder galvanisiert. Versuche haben ergeben, daß Der untere Lenker 4 besteht aus Stahlblech und Flächen, an denen der Schaumstoff anlag, vollkommen weist drei kreisförmige Öffnungen 1, 2, 3 auf, mit vor dem Auftragsmaterial oder dem Galvanisieren 35 Durchmessern zwischen 26 und 40 mm. In die drei geschützt waren. Beim anschließenden Erhitzen des kreisförmigen öffnungen 1, 2, 3 sind aus Polystyrol-Gegenstandes auf eine zu seiner Warmbehandhiag er- schaum mit einem Aufschäumungsgrad von 50 beforderliche Temperatur schrumpften die Abdeckele- stehende, zylindrische Abdeck- oder Maskierungsmente ohne Festkleben an der Oberfläche des Gegen- elemente 5, 6, 7, deren Durchmesser jeweils um etwa Standes auf etwa ein Zehntel ihres AuEgasgsvoiumens 40 0,5 bis 2 mm größer sind als die der Öffnungen, ge- und ließen sich ohne die bei Gummistopfen auftre- waltsam eingetrieben und dichtend darin gehalten,
tenden Schwierigkeiten entfernen. . Der so vorbereitete Lenker wurde in ein wasserlös-or galvanized. Tests have shown that the lower link 4 consists of sheet steel and surfaces on which the foam was applied, completely has three circular openings 1, 2, 3, with 35 diameters between 26 and 40 mm before the application material or electroplating. In which three were protected. When the circular openings 1, 2, 3 are subsequently heated, the polystyrene object is at a temperature required for its heat-treatment foam with a degree of foaming of 50, the cylindrical cover or masking elements shrink without sticking to the surface of the counterpart. elements 5, 6, 7, the diameters of which are 0.5 to 2 mm larger than those of the openings by about a tenth of their AuEgasgsvoliumens 40, and could be forcefully driven in and held tightly in them without the rubber stoppers ,
remove any difficulties. . The handlebar prepared in this way was put into a water-soluble

Erfindungsgemäße Abdeckelemente in Nippel- oder Üches Alkydharz-Auftragsmaterial enthaltendes BadCovering elements according to the invention in a bath containing nipple or alkyd resin application material

Muffenform schrumpfen bei der Warmbehandlung eingetaucht und zur Bildung einer Beschichtung 8 aufThe socket shape shrinks during the heat treatment and is dipped open to form a coating 8

des lackierten oder galvanisierten Gegenstandes schnell 4S den nicht bedeckten Flächen einem gebräuchlichenof the lacquered or galvanized object quickly 4S the uncovered areas in use

auf sehr kleine Abmessungen zusammen, wobei sie elektrophoretischen Überzugsverfahren unterzogen,to very small dimensions, being subjected to electrophoretic coating processes,

an den Einschnitten aufrissen, so daß sich das ge- Der auf diese Weise beschichtete Gegenstand wurdetorn open at the incisions, so that the object coated in this way was

schrumpfte Abdeckelement mühelos von dem be- anschließend in einen Heißluft-Trockenofen gebrachtThe shrunk cover element was effortlessly removed from it and then placed in a hot air drying oven

treffenden Gegenstand entfernen üeß. und zum Einbrennen der Beschichtung während 60 Mi-remove the hit object. and for baking the coating for 60 minutes

Die vor dem Lackieren oder Galvanisieren zu 50 nuten auf 190⁰C erhitzt. Während des Erhitzens ^{The heated to 190 0} C for 50 slots before painting or electroplating. During heating

schützende Fläche kann vorbereitend mit geeigneten, schrumpfen die Abdeckelemente schnell ein und das Festkleben verhindernden Mitteln bestrichen fielen von selbstausdenöffnungen, deren Innenflächen,protective surface can be prepared with suitable, the cover elements quickly shrink and the sticking agents coated fell from self-opening openings, the inner surfaces of which,

werden, beispielsweise mit Maschinenöl, Silikonöl mit denen die Abdeckelemente während der Behand-are used, for example with machine oil, silicone oil, with which the cover elements are

od. dgl., die das Ablösen des geschrumpften Schaum- lung in Anlage wp unbeschichtet blieben F i g. (2).od. The like. The detachment of the shrunk foam remained uncoated in the plant wp F i g. (2).

teils von dem Gegenstand erleichtern. SS r ' ' 1 ?partly relieve of the object. SS r " 1?

Somit werden bei Anwendung des erfindungsge- Beispiel l Thus, when using the invention example l

mäßen Verfahr <..& dazu bestimmte Ausnehmungen Eine Stahlstange 9 mit einem Durchmesser vonmoderate traversing <.. & for this purpose recesses A steel rod 9 with a diameter of

oder Bohrungen eines einer Oberflächenbehandlung zu 15 mm ist in eine aus Methacrylharzschaum mit einem unterziehenden Gegenstandes durch formschlüssiges Aufschäumungsgrad von 35 hergestellte Muffe 10 mitor holes of a surface treatment of 15 mm is in one made of methacrylic resin foam with a subject subject by positive foaming of 35 sleeve 10 produced with

Einpassen von aus Kunstharzschaum bestehenden 60 einem Innendurchmesser von 14 mm und einem Außen-Fitting of 60 made of synthetic resin foam with an inner diameter of 14 mm and an outer

Abdeckelementen gegen eine Oberflächenbehandlung, durchmesser von 30 mm eingeführt. Von der Außenbeispielsweise Lackieren oder Galvanisieren, zuver- seite der Muffe 10 her erstreckt sich ein Einschnitt 11 lässig geschützt. Bei der nachfolgenden Warmbehand- von 12 mm Tiefe radial einwärts (F i g. 3).Covering elements against a surface treatment, diameter of 30 mm introduced. From the outside, for example Painting or electroplating, an incision 11 extends towards the sleeve 10 casually protected. In the subsequent heat treatment from a depth of 12 mm radially inwards (Fig. 3).

lung schrumpfen die Abdeckelemente sehr schnell Die mit der Muffe 10 versehene Stakstange 9 wird zusammen und fallen dabei von selbst aus den Aus- 65 durch elektrostatischen Auftrag mit einem Lack 12treatment, the cover elements shrink very quickly. The rod 9 provided with the socket 10 becomes and fall out of their own accord by electrostatic application with a lacquer 12

nehmungen oder Bohrungen heraus, so daß das bei beschichtet und dann während 30 Minuten bei 180⁰Crecesses or bores out, so that the coated at and then at 180 ⁰ C for 30 minutes

' den gebräuchlichen, Gummistopfen verwendenden eingebrannt. Während der Warmbehandlung riß die Maskierverfahren erforderliche Entfernen der Ab- Muffe 10 am Einschnitt 11 auf, schrumpfte auf etwa'Branded in' the common, rubber stopper. The tore during the heat treatment Masking process required removal of the socket 10 at the incision 11, shrunk to about

ein Zehqtcl des ursprünglichen Volumens und fiel von der Stange ab. Die durch die Schaumstoffmuffe maskierte Teilfläche blieb frei von jeglichem Überzugsfmatcrial (Fig.;4).a tenth qtcl of the original volume and fell from off the pole. The partial area masked by the foam sleeve remained free of any coating material (FIG. 4).

Beispiel 3Example 3

■ Das Gewindeende 13 einer Schraube 14 mit einem Durchmesser von 10 mm wurde mittels eines aus PoIyithylenschaum mit einem Aufschäumungsgrad von 35 gefertigten Nippels 15 mit einem Innendurchmesser■ The threaded end 13 of a screw 14 with a A diameter of 10 mm was measured by means of a polyethylene foam with a degree of expansion of 35 manufactured nipple 15 with an inner diameter von 9 mm und einem 7 mm tiefen Einschnitt 16 mas-¹" kiert. ' * · ;v;of 9 mm and a 7 mm deep incision 16 mas ¹ kiert "'*·;.v;

Die mittels des Nippels maskierte Schraube wurde &_; galvanisch ,mit Chrom17 überzogen.: Die gllyaniscii;f verchromte Schraube wurde anschließend auf etwa 16O⁰C erwärmt. Dabei riß der maskierende. Nippel .am Einschnitt auf, schrumpfte schnell zusammen; und, , ififiel Yon/der^&hraube^bVpabeiiblieb^idas^öwin^The screw masked by the nipple was &_; galvanically coated with Chrom17 .: The gllyaniscii; f chrome screw was then heated to about 16O ⁰ C. The masking one tore. Nipple at the incision, quickly shrunk; and, ififiel Yon / the ^ & ^ hraube bVpabeiiblieb ^ ^ idas öwin ^

ende der Schraube frei von jeglicher galvanischer Beschichtung.end of the screw free of any galvanic coating.

Hierzu 1 Blatt Zeichnungen1 sheet of drawings

909iS33/434909iS33 / 434

Claims

Rubber stopper after treatment has ended

Claims: can be removed individually by hand, so that this Ver

driving is time-consuming in this respect too.

1, method for masking objects From the US Pat. No. 2,363,842, templates for surface treatments, in particular tops, are known, soft as a composite body with a surface treatment with a heat treatment - relatively thin plate-shaped mask plate and a ventilation process in which a certain, are provided with a thicker layer provided underneath, a cover or a coating or the partial surface of a counter surface to be kept free, for example from synthetic rubber sponge plating. This thick lower layer can either be covered with a cover element made of synthetic resin or a large part of the lower surface of the mask plate is masked, thereby identified, or it can be arranged in the form of stripes that the with a heat treatment along the Run along the edges on the underside of the shrinking synthetic resin foam cover mask plate! The article provided with stencil elements after coating according to US Pat. No. 2,163,842 further have suction cups, heated until the cover element shrinks, which are used to attach the ^w ' ^rc i. Template element on the surface of a counter

2. The method according to claim 1, characterized by the stand. The actual mask plate has records that a cover element in the form of a recess, the contours of which correspond to the patterns

E nipple or a sleeve talk to at least one who with the help of the mask plate on one

: radial incision is used and is to be applied to ao object by means of paint,

-: a rod-shaped or tubular object by applying the paint to the through the recesses in

is postponed. of the mask plate uncovered surface of the counter

Γ stands is applied. The one from the USA.

,; Scripture 2 3ύ3 842 are known template elements

'·; -. 25 designed for repeated use. The lower one

' _f . thicker ones made of rubber or rubber sponge

Layer is used in this known stencil element