DE20319971U1 - Grained leather for footwear is covered by a porous dressing bonded to the leather by adhesion at local points and structured with weakened zones and/or interruptions - Google Patents

Grained leather for footwear is covered by a porous dressing bonded to the leather by adhesion at local points and structured with weakened zones and/or interruptions Download PDF

Info

Publication number
DE20319971U1
DE20319971U1 DE20319971U DE20319971U DE20319971U1 DE 20319971 U1 DE20319971 U1 DE 20319971U1 DE 20319971 U DE20319971 U DE 20319971U DE 20319971 U DE20319971 U DE 20319971U DE 20319971 U1 DE20319971 U1 DE 20319971U1
Authority
DE
Germany
Prior art keywords
leather
leather according
connecting layer
dressing
thickness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE20319971U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE20319971U priority Critical patent/DE20319971U1/en
Publication of DE20319971U1 publication Critical patent/DE20319971U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

The grain side of a grained leather (1) is covered by a dressing (2) which is mainly porous (3). The dressing is secured by a bonding layer (4), which is weakened at points by local thickness reduction and/or interruptions. The bonding layer has the structure of local points, a screen or grid, with a maximum thickness of 0.01-0.05 mm, and with a thickness of 0.002-0.01 mm at the weak points.

Description

Die Erfindung betrifft ein eine feinfaserige Oberfläche aufweisendes Leder, insbesondere ein an seiner die Oberfläche bildenden Narbenseite angeschliffenes Narbenleder, oder ein, Spaltleder mit geschliffener Oberfläche, wobei die Oberfläche über eine Verbindungsschicht mit einer auf einer entfernbaren Unterlage getrennt hergestellten, vorzugsweise aus einer verfestigten, Polyurethan enthaltenden, vernetzten Kunststoffdispersion gebildeten Zurichtung verbunden ist. Die Erfindung ist vor allem auf Rindleder, aber auch auf andere Lederarten, wie beispielsweise Schweine-, Kalb-, Ziegen- oder Schafleder, anwendbar.The invention relates to a fine-fiber surface Leather, in particular a sanded grain on its surface that forms the surface Grain leather, or a split leather with a polished surface, being the surface over a Connection layer separated with a on a removable pad produced, preferably from a solidified, polyurethane containing, crosslinked plastic dispersion formed dressing connected is. The invention is mostly on cowhide, but also on other types of leather, such as pig, calf, goat or sheep leather, applicable.

Unzugerichtete, an ihrer Narbenseite angeschliffene Leder, sowie unzugerichtete Spaltleder weisen bei einer Stärke zwischen 1,1 mm und 2,2 mm je nach Gerbart und Weichheit eine extrem hohe Luftdurchlässigkeit auf, die mit textilen Materialen gleichen Gewichts nahezu vergleichbar ist. Auch die Wasserdampfdurchlässigkeit liegt bei derartigen Ledern, selbst wenn sie hydrophob sind, allgemein über 5 mg/cm2, ermittelt nach DIN 53333. Derartige unzugerichtete Leder weisen jedoch nicht die in der Praxis gewünschten Eigenschaften auf, sodass deren Oberfläche mit einer Zurichtung versehen wird. Dadurch wird die Wasserdampf- und Luftdurchlässigkeit solcher mit einer Zurichtung versehenen Leder wesentlich verringert. So besitzen diese Leder bei einer Dicke der Zurichtung von 0,15 mm keine nennenswerte Luftdurchlässigkeit, und die Wasserdampfdurchlässigkeit beträgt weniger als 0,8 mg/cm2, zumeist weniger als 0, 3 mg/cm2. Außerdem weisen solche mit einer Zurichtung versehenen Leder in Folge des vollflächigen sandwichartigen Schichtaufbaus der kompletten Zurichtung den Nachteil auf, dass sie hart und unflexibel werden, sodass beim Abbiegen keine für hochwertige Narbenleder typische feine Fältelung erfolgt.Undressed leather, sanded on its grain side, as well as undressed split leather, with a thickness between 1.1 mm and 2.2 mm, depending on the grain and softness, have an extremely high air permeability, which is almost comparable to textile materials of the same weight. The water vapor permeability of such leathers, even if they are hydrophobic, is generally above 5 mg / cm 2 , determined according to DIN 53333. However, such undressed leathers do not have the properties desired in practice, so that their surface is provided with a finish. This significantly reduces the water vapor and air permeability of such trimmed leather. Thus, with a finish thickness of 0.15 mm, these leathers have no appreciable air permeability, and the water vapor permeability is less than 0.8 mg / cm 2 , mostly less than 0.3 mg / cm 2 . In addition, as a result of the full-surface sandwich-like layer structure of the complete dressing, such leather provided with a dressing has the disadvantage that it becomes hard and inflexible, so that there is no fine pleating typical of high-quality grain leather when turning.

Die vorliegende Erfindung hat sich zur Aufgabe gestellt, ein mit einer Zurichtung versehenes Leder zu schaffen, bei welchem die erwähnten Nachteile vermieden sind, und welches vor allem eine wesentlich verbesserte Luft- und Wasserdampfdurchlässigkeit aufweist. Zur Lösung dieser Aufgabe schlägt die Erfindung vor, dass die Zurichtung überwiegend porös ausgebildet ist, und dass die Verbindungsschicht Schwachstellen verringerter Dicke und/oder Unterbrechungen aufweist. Dadurch wird gewährleistet, dass Luft und Wasserdampf über die porös ausgebildete Zurichtung und die Schwachstellen verringerter Dicke sowie Unterbrechungen aufweisende Verbindungsschicht praktisch ungehindert durchdringen kann und so beispielsweise bei Verwendung des Leders für Schuhe auftretender Fußschweiß vom Leder aufgenommen und über die Verbindungsschicht und die Zurichtung abgeleitet wird. Bei Verwendung des erfindungsgemäßen Leders für Polstermöbel wird auftretende Feuchtigkeit über die Zurichtung und die Verbindungsschicht zum Leder transportiert und von diesem aufgenommen. Außerdem wird durch die erfindungsgemäße Ausbildung des Leders der Vorteil erzielt, dass die Flexibilität des Leders verbessert wird, sodass beim Abbiegen in der Zurichtung eine feine Lederfältelung mit dem Aussehen eines weichen wertvollen vollnarbigen Leders entsteht.The present invention has been accomplished task, a leather provided with a finish to create, in which the mentioned Disadvantages are avoided, and which one is essential has improved air and water vapor permeability. To solve this Task strikes the invention proposes that the dressing is predominantly porous is, and that the link layer weak spots decreased Has thickness and / or breaks. This ensures that air and water vapor over the porous trained dressing and the weak points of reduced thickness as well as intermittent connection layer practically unimpeded can and so for example when using the leather for shoes occurring foot sweat from the leather recorded and about the compound layer and the dressing is derived. Using of the leather according to the invention for upholstered furniture occurring moisture over the finishing and the connecting layer to the leather transported and taken up by this. Moreover is by the inventive design of the Leather has the advantage that the flexibility of the leather is improved, so that when turning in the dressing a fine leather fold with the appearance of a soft, valuable full-grain leather.

Selbst bei hydrophobierten Ledern mit einer Stärke von mehr als 2 mm wird bei der erfindung gemäßen Ausbildung eine Wasserdampfdurchlässigkeit von mehr als 1,5 mg/cm2 nach DIN 53333 erreicht.Even with hydrophobized leathers with a thickness of more than 2 mm, a water vapor permeability of more than 1.5 mg / cm 2 according to DIN 53333 is achieved with the inventive design.

Eine eventuell vorgenommene imprägnierartige Vorbehandlung des Leders, beispielsweise mit einem dünnen flüssigen Polymer zur Bindung des Schleifstaubes vor dem Aufbringen der Zurichtung beeinflusst die Luftdurchlässigkeit nicht oder kaum.A possibly impregnated Pretreatment of the leather, for example with a thin liquid polymer for binding the grinding dust before the dressing is applied the air permeability not or hardly.

Gemäß einer bevorzugten Ausführungsform der Erfindung weist die Verbindungsschicht eine punkt-, raster- oder gitterartige Struktur auf, bildet somit keine zusammenhängende Schicht, sodass in der Verbindungsschicht Unterbrechungen entstehen, und keine vollflächige, biegesteife Sandwichbauweise gegeben ist, welche die Luft- und Wasserdampfdurchlässigkeit und die Biegefähigkeit ungünstig beeinflusst.According to a preferred embodiment of the Invention, the connection layer has a point, grid or lattice-like structure, does not form a coherent layer, so that there are interruptions in the connection layer, and no full area, rigid sandwich construction is given, which the air and water vapor permeability and the bendability unfavorable affected.

Es genügt aber zur Verbesserung der erwähnten Eigenschaften auch, wenn die Verbindungsschicht eine maximale Dicke zwischen 0,01 mm und 0,05 mm und an ihren Schwach stellen eine Dicke zwischen 0,002 mm und 0,01 mm aufweist, in welchem Fall eine gute Luft und Wasserdampfdurchlässigkeit über diese dünnen Schwachstellen erzielt wird, durch welche auch die Biegefähigkeit des Leders wesentlich verbessert wird.But it is enough to improve mentioned Properties also when the tie layer has a maximum thickness between 0.01 mm and 0.05 mm and at their weak points put a thickness between 0.002 mm and 0.01 mm, in which case good air and Water vapor permeability over this thin Weaknesses are achieved through which also the bendability of the leather is significantly improved.

Dadurch, dass die porös ausgebildete Zurichtung auf einer entfernbaren Unterlage, beispielsweise auf einem geprägtem Trennpapier oder einer Unterlage aus strukturierten Silikonkautschuk, hergestellt wird, bevor sie über die Verbindungsschicht mit der Oberfläche des Leders verbunden wird, ist für die Verbindung nur eine geringe Druckanwendung erforderlich, sodass die poröse Struktur der Zurichtung erhalten bleibt.Because the porous Dressing on a removable surface, for example on an embossed Release paper or a pad made of structured silicone rubber, is made before over the connection layer is connected to the surface of the leather, is for the connection requires only a small amount of pressure so that the porous The structure of the finish is retained.

Vorzugsweise besteht die Verbindungsschicht aus einer elastomeren, verfestigten, Polyurethan enthaltenden, vernetzen Kunststoffdispersion, welche das Entstehen der Schwachstellen und/oder Unterbrechungen begünstigt bzw. sicherstellt. Diese Verbindungsschicht kann kompakt sein, aber auch eine, vorzugsweise Mikrohohlkugeln enthaltende, Schaumstruktur aufweisen, wobei in jedem Fall das Entstehen der Schwachstellen und/oder Unterbrechungen gewährleistet ist.The connection layer is preferably present Crosslink from an elastomeric, solidified, polyurethane-containing Plastic dispersion, which indicates the emergence of weak points and / or interruptions favored or ensures. This connection layer can be compact, however also a foam structure, preferably containing hollow microspheres exhibit, in each case the emergence of the weak points and / or interruptions guaranteed is.

Es hat sich als günstig erwiesen, wenn die Verbindungsschicht ein Flächengewicht zwischen 20 g/m2 und 90g/m2, vorzugsweise zwischen 30 g/m2 und 45 g/m2, aufweist.It has proven to be advantageous if the connecting layer has a weight per unit area between 20 g / m 2 and 90 g / m 2 , preferably between 30 g / m 2 and 45 g / m 2 .

Die Zurichtung kann aus einer Schicht oder aus mehreren Schichten bestehen, wobei auch bei Ausbildung derselben aus mehreren Schichten zumindest eine Vielzahl der Poren der Zurichtung durchgängig sein muss und daher bis zu den Durchbrechungen bzw. Schwachstellen der Verbindungsschicht reichen muss. Es ist daher wesentlich, dass diese Poren in der Zurichtung bei der getrennten Herstellung derselben auf einer entfernbaren Unterlage entstehen und nicht durch Nadeln oder durch eine Laserbehandlung gebildet werden.Dressing can be from one layer or consist of several layers, even if the same is formed from several layers, at least a large number of the pores of the dressing must be continuous and therefore have to extend to the openings or weak points of the connecting layer. It is therefore essential that these pores arise in the dressing when they are produced separately on a removable base and are not formed by needles or by laser treatment.

Gemäß einem weiteren Merkmal der Erfindung kann das Leder an seiner der mit der Zurichtung versehenen Oberfläche gegenüberliegenden Fleischseite eine offenporige dünne Beschichtung aufweisen. Diese Beschichtung kann einen ähnlichen oder gleichen Aufbau wie die Zurichtung an der Oberseite besitzen und über eine gleiche oder eine ähnliche Verbindungsschicht wie jene, über welche die Zurichtung mit der Oberseite verbunden ist, mit der Fleischseite verbunden sein. Es ist in diesem Fall möglich, diese dünne Beschichtung der Fleischseite im selben Verfahrensschritt wie die Zurichtung zeitgleich bzw. nahezu zeitgleich aufzubringen. Insbesondere bei Verwendung des erfindungsgemäßen Leders für Schuhe verfügt in diesem Fall das Leder nicht nur über extrem hohe Komforteigenschaften wegen seiner hohen Luft- und Wasserdampfdurchlässigkeit, die ein Ableiten und Verdunsten des vom Leder aufgenommenen Fußschweißes ermöglicht, es ist aufgrund des einfachen Herstellungsverfahrens auch preiswert.According to another characteristic of Invention can the leather on its provided with the dressing surface opposite side of meat an open pore thin Have coating. This coating can be a similar one or have the same structure as the dressing on the top and over the same or a similar one Link layer like those about which the dressing is connected to the top, to the meat side be connected. In this case it is possible to apply this thin coating the meat side in the same process step as the dressing to apply simultaneously or almost simultaneously. Especially at Use of the leather according to the invention for shoes has in this case, the leather is not only due to extremely high comfort properties its high air and water vapor permeability, which is a drain and evaporation of the foot sweat absorbed by the leather, it is due to the simple manufacturing process also inexpensive.

Eine zusätzliche Verbesserung der Eigenschaften des Leders kann dadurch erfolgen, dass zwischen der Fleischseite und der dünnen Beschichtung ein textiles Vliesmaterial angeordnet ist, dessen Gewicht zweckmäßig maximal 50 % des Ledergewichtes ausmacht und nicht dicker als 3 mm sein soll. Dieses Vliesmaterial kann weiters erfindungsgemäß mit einem dünnen offenzelligen Kunststoftschaummaterial, vorzugsweise durch Nadeln oder mittels eines Wasserstrahles, verbunden sein.An additional improvement in properties of the leather can be done between the meat side and the thin one Coating a textile non-woven material is arranged, the weight of which expediently maximum Accounts for 50% of the leather weight and not be thicker than 3 mm should. According to the invention, this nonwoven material can also be used with a thin open-cell plastic foam material, preferably by needles or connected by a water jet.

Ein besonders günstiges Anwendungsgebiet ist es, wenn das erfindungsgemäß ausgebildete Leder ein Formatzuschnitt mit einer maximalen Größe von 2,4 m2, vorzugsweise von weniger als 1,8 m2, ist, wie er beispielsweise für die Herstellung von Schuhen verwendet wird, da dann Bereiche einer Lederhaut unterschiedlicher Eigenschaften und Stärken optimal Verwendung finden können.It is a particularly advantageous field of application if the leather designed according to the invention is a format blank with a maximum size of 2.4 m 2 , preferably less than 1.8 m 2 , as is used, for example, for the production of shoes, because then Areas of a leather skin of different properties and thicknesses can be optimally used.

In der Zeichnung ist die Erfindung anhand von Ausführungsbeispielen schematisch erläutert. 1 zeigt in stark vergrößertem Querschnitt eine erste Ausführungsform und In the drawing, the invention is explained schematically using exemplary embodiments. 1 shows a greatly enlarged cross section of a first embodiment and

2 in gleichfalls in starker Vergrößerung einen Querschnitt durch eine zweite Ausführungsform eines erfindungsgemäß aufgebauten Leders, welches auf seiner Fleischseite mit einer dünnen offenporigen Beschichtung versehen ist. 2 likewise in a large enlargement, a cross section through a second embodiment of a leather constructed according to the invention, which is provided on its meat side with a thin open-pore coating.

Ein an seiner Narbenseite angeschliffenes Narbenleder 1 oder ein Spaltleder 1 mit geschliffener Oberfläche ist mit einer Zurichtung 2 versehen, welche über ihre ganze Dicke durchgehende Poren 3 aufweist. Die Zurichtung 2 kann ein- oder mehrschichtig ausgebildet sein, besteht vorzugsweise aus einer verfestigten, Polyurethan enthaltenden, vernetzten Kunststoffdispersion und wird getrennt hergestellt, insbesondere dadurch, dass auf einer Unterlage aus geprägtem Trennpapier oder aus mit einer Struktur versehenem Silikonkautschuk eine wässerige Polyurethandispersion, gegebenenfalls in mehreren Schichten hintereinander, aufgesprüht und trocknen gelassen wird, derart, dass in der verfestigten Dispersion die erforderlichen durchgehenden Poren gebildet werden.A grain leather sanded on its grain side 1 or a split leather 1 with ground surface is with a dressing 2 which have continuous pores over their entire thickness 3 having. The dressing 2 can be formed in one or more layers, preferably consists of a solidified, polyurethane-containing, cross-linked plastic dispersion and is manufactured separately, in particular by an aqueous polyurethane dispersion, optionally in several layers in succession, on a base made of embossed release paper or structured silicone rubber , sprayed on and left to dry in such a way that the required continuous pores are formed in the solidified dispersion.

Die so gesondert hergestellte Zurichtung 2 wird unmittelbar nach ihrer Verfestigung über eine auf die Oberseite des Leders 1 aufgebrachte Verbindungsschicht 4 mit dieser Oberseite verbunden. Bei der in 1 dargestellten Ausführungsform weist diese Verbindungsschicht 4 eine punkt-, raster- oder gitterartige Struktur auf, sodass nur an einzelnen Stellen bzw. Punkten eine Verbindung zwischen der Oberseite des Leders und der Zurichtung 2 hergestellt wird und dazwischen Unterbrechungen 5 entstehen, welche mit den Poren in der Zurichtung 2 kommunizieren und dadurch die gewünschte Luft- und Wasserdampfdurchlässigkeit gewährleisten.The dressing so produced separately 2 is immediately after it solidifies on top of the leather 1 applied connection layer 4 connected to this top. At the in 1 illustrated embodiment has this connection layer 4 a point, grid or lattice-like structure, so that only at individual points or points a connection between the top of the leather and the finish 2 is produced and interruptions in between 5 arise which with the pores in the dressing 2 communicate and thereby ensure the desired air and water vapor permeability.

Die Unterbrechungen 5 können eine beliebige Form aufweisen und beispielsweise rund, rechteckig oder linienförmig ausgebildet sein, aber auch jede andere geeignete Form besitzen.The interruptions 5 can have any shape and, for example, be round, rectangular or linear, but also have any other suitable shape.

Bei der in 2 dargestellten Ausführungsform sind nicht nur derartige Unterbrechungen 5 in der Verbindungsschicht 4 vorgesehen, sondern diese weist auch Schwachstellen 6 auf, deren Dicke wesentlich geringer ist als die Gesamtdicke der Verbindungsschicht 4, sodass auch über diese Schwachstellen 6 die Luft- und Wasserdampfdurchlässigkeit wesentlich erhöht und die Biegefähigkeit verbessert wird.At the in 2 embodiment shown are not just such interruptions 5 in the connection layer 4 provided, but this also shows weaknesses 6 whose thickness is significantly less than the total thickness of the connection layer 4 so that even over these vulnerabilities 6 the air and water vapor permeability is significantly increased and the bendability is improved.

Zweckmäßig weist hierbei die Verbindungsschicht 4 eine maximale Dicke zwischen 0,01 mm und 0,05 mm auf, wobei aber die Schwachstellen 6 lediglich eine Dicke zwischen 0,002 mm und 0,01 mm besitzen.The connection layer expediently points here 4 a maximum thickness between 0.01 mm and 0.05 mm, but with the weak points 6 only have a thickness between 0.002 mm and 0.01 mm.

Die Fleischseite 7 des Leders ist bei der in 2 dargestellten Ausführungsform mit einer offenporigen dünnen Beschichtung 8 versehen, wobei zwischen der Fleischseite 7 und der Beschichtung 8 ein textiles Vliesmaterial 9 vorgesehen ist. Vorteilhaft ist es, wenn dieses Vliesmaterial 9 mit einem dünnen, offenzelligen Kunststoffschaummaterial, vorzugsweise durch Nadeln oder mittels eines Wasserstrahles, verbunden ist.The meat side 7 of the leather is in the 2 illustrated embodiment with an open-pore thin coating 8th provided, being between the meat side 7 and the coating 8th a textile non-woven material 9 is provided. It is advantageous if this nonwoven material 9 is connected to a thin, open-celled plastic foam material, preferably by needling or by means of a water jet.

Das luft- und wasserdampfdurchlässige Vliesmaterial 9 ist sowohl mit der Fleischseite 7 als auch mit der offenporigen dünnen Beschichtung 8 über eine Verbindungsschicht 10 verbunden, deren Aufbau und Zusammensetzung jenem bzw. jener der Verbindungsschicht 4 entspricht.The air and water vapor permeable fleece material 9 is both with the meat side 7 as well as with the open-pore thin coating 8th via a connection layer 10 connected, the structure and composition of that or that of the connection layer 4 equivalent.

Eine solche Ausbildung ist vor allem bei Verwendung von aus dem erfindungsgemäßen Leder gebildeten Formatzuschnitten für die Schuhherstellung von Vorteil, da in diesem Fall die offenporige dünne Beschichtung als Futtermaterial dient und eine gesonderte Aufbringung eines solchen Futtermaterials somit nicht erforderlich ist. Bei Schuhen erfolgt infolge der großen Wasserdampfdurchlässigkeit des Leders eine Ableitung des auftretenden Fußschweißes und infolge der großen Luftdurchlässigkeit eine Belüftung des Schuhinnenraums, bei Verwendung des erfindungsgemäßen Leders für Autositze und Polstermöbel eine Aufnahme der auftretenden Feuchtigkeit durch die Zurichtung hindurch vom Leder. Insbesondere bei anderen Verwendungszwecken kann aber die Beschichtung 8 auch entfallen.Such a design is particularly advantageous when using format blanks formed from the leather according to the invention for shoe manufacture, since in this case the open-pore thin coating serves as lining material and a separate application of such lining material is therefore not necessary. In shoes, due to the high water vapor permeability of the leather, the foot sweat that occurs is ventilated and, due to the large air permeability, the interior of the shoe is ventilated. However, the coating can be used in particular for other uses 8th also dropped.

Die in der Zurichtung 2 vorgesehenen durchgehenden Poren 3 sind bei Ausleuchtung bereits bei einer 45-fachen Vergrößerung und einer Dehnung um 25 % deutlich erkennbar. Beim mechanischen oder chemischen Entfernen der Zurichtung 2 von der Verbindungsschicht 4 kann man bereits bei 16-facher Vergrößerung erkennen, dass die Verbindungsschicht 4 sowohl dicke Stellen als auch Schwachstellen aufweist und dass in den Schwachstellen ebenfalls porenförmige Unterbrechungen vorgesehen sind.The one in the dressing 2 provided through pores 3 are clearly visible when illuminated with a 45x magnification and an elongation of 25%. When removing the dressing mechanically or chemically 2 from the connection layer 4 you can already see at 16x magnification that the connection layer 4 has both thick spots and weak spots and that pore-shaped interruptions are also provided in the weak spots.

Die vorliegende Erfindung ist vor allem bei Rindledern, aber auch bei an ihrer Narbenseite geschliffenen Schweine-, Kalb-, Ziegen- und Schafledern anwendbar, insbesondere dann, wenn solche Leder für die Schuhherstellung verwendet werden.The present invention is before especially with cowhide, but also with sanded on their grain side Pig, calf, goat and sheep leather applicable, in particular then when such leather for the shoe manufacturing can be used.

Claims (12)

Eine feinfaserige Oberfläche aufweisendes Leder, insbesondere an seiner die Oberfläche bildenden Narbenseite angeschliffenes Narbenleder, oder Spaltleder mit geschliffener Oberfläche, wobei die Oberfläche über eine Verbindungsschicht (4) mit einer auf einer entfernbaren Unterlage getrennt hergestellten, vorzugsweise aus einer verfestigten, Polyurethan enthaltenden, vernetzten Kunststoffdispersion gebildeten, Zurichtung (2) verbunden ist, dadurch gekennzeichnet, dass die Zurichtung (2) überwiegend porös ausgebildet ist, und dass die Verbindungsschicht (4) Schwachstellen (6) verringerter Dicke und/oder Unterbrechungen (5) aufweist.Leather with a fine-grained surface, in particular grain leather sanded on its grain-forming surface, or split leather with a sanded surface, the surface being connected by a connecting layer ( 4 ) with a finish prepared separately on a removable base, preferably formed from a solidified, polyurethane-containing, crosslinked plastic dispersion ( 2 ), characterized in that the dressing ( 2 ) is predominantly porous, and that the connecting layer ( 4 ) Vulnerabilities ( 6 ) reduced thickness and / or breaks ( 5 ) having. Leder nach Anspruch 1, dadurch gekennzeichnet, dass die Verbindungsschicht (4) eine punkt-, raster- oder gitterartige Struktur aufweist.Leather according to claim 1, characterized in that the connecting layer ( 4 ) has a point, grid or grid-like structure. Leder nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die Verbindungsschicht (4) eine maximale Dicke zwischen 0,01 mm und 0,05 mm und an ihren Schwachstellen (6) eine Dicke zwischen 0,002 und 0,01 mm aufweist.Leather according to claim 1 or 2, characterized in that the connecting layer ( 4 ) a maximum thickness between 0.01 mm and 0.05 mm and at their weak points ( 6 ) has a thickness between 0.002 and 0.01 mm. Leder nach Anspruch 1, 2 oder 3, dadurch gekennzeichnet, dass die Verbindungsschicht (4) aus einer elastomeren, verfestigten, Polyurethan enthaltenden, vernetzten Kunststoffdispersion besteht.Leather according to claim 1, 2 or 3, characterized in that the connecting layer ( 4 ) consists of an elastomeric, solidified, polyurethane-containing, crosslinked plastic dispersion. Leder nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass die Verbindungsschicht (4) kompakt ist.Leather according to one of claims 1 to 4, characterized in that the connecting layer ( 4 ) is compact. Leder nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass die Verbindungsschicht (4) eine, vorzugsweise Mikrohohlkugeln enthaltende, Schaumstruktur aufweist.Leather according to one of claims 1 to 4, characterized in that the connecting layer ( 4 ) has a foam structure, preferably containing hollow microspheres. Leder nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass die Verbindungsschicht (4) ein Flächengewicht zwischen 20 g/m2 und 90 g/m2, vorzugsweise zwischen 30 g/m2 und 45 g/m2, aufweist.Leather according to one of claims 1 to 6, characterized in that the connecting layer ( 4 ) has a basis weight between 20 g / m 2 and 90 g / m 2 , preferably between 30 g / m 2 and 45 g / m 2 . Leder nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass das Leder (1) an seiner der mit der Zurichtung (2) versehenen Oberfläche gegenüberliegenden Fleischseite (7) eine offenporige dünne Beschichtung (8) aufweist.Leather according to one of claims 1 to 7, characterized in that the leather ( 1 ) on his with the dressing ( 2 ) provided surface opposite meat side ( 7 ) an open-pore thin coating ( 8th ) having. Leder nach Anspruch 8, dadurch gekennzeichnet, dass zwischen der Fleischseite (7) und der dünnen Beschichtung (8) ein textiles Vliesmaterial (9) angeordnet ist.Leather according to claim 8, characterized in that between the meat side ( 7 ) and the thin coating ( 8th ) a textile non-woven material ( 9 ) is arranged. Leder nach Anspruch 9, dadurch gekennzeichnet, dass das Vliesmaterial (9) mit einem dünnen offenzelligen Kunststoffschaummaterial, vorzugsweise durch Nadeln oder mittels eines Wasserstrahles, verbunden ist.Leather according to claim 9, characterized in that the nonwoven material ( 9 ) with a thin open-cell plastic foam material, preferably by needling or by means of a water jet. Leder nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass es ein Formatzuschnitt ist.Leather according to one of claims 1 to 10, characterized in that that it is a format cut. Leder nach einem der Ansprüche 1 bis 11, dadurch gekennzeichnet, dass es bei einer Fläche von 100 cm2 und einem Druck von 2 bar einen Luftdurchsatz von mehr als 10 l/min aufweist.Leather according to one of claims 1 to 11, characterized in that it has an air throughput of more than 10 l / min at an area of 100 cm 2 and a pressure of 2 bar.
DE20319971U 2003-12-23 2003-12-23 Grained leather for footwear is covered by a porous dressing bonded to the leather by adhesion at local points and structured with weakened zones and/or interruptions Expired - Lifetime DE20319971U1 (en)