DE202011110323U1 - Functionalized latex-based foam - Google Patents

Functionalized latex-based foam Download PDF

Info

Publication number
DE202011110323U1
DE202011110323U1 DE201120110323 DE202011110323U DE202011110323U1 DE 202011110323 U1 DE202011110323 U1 DE 202011110323U1 DE 201120110323 DE201120110323 DE 201120110323 DE 202011110323 U DE202011110323 U DE 202011110323U DE 202011110323 U1 DE202011110323 U1 DE 202011110323U1
Authority
DE
Germany
Prior art keywords
foam
additive
latex
layer
latex foam
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE201120110323
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Latexco NV
Original Assignee
Latexco NV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Latexco NV filed Critical Latexco NV
Priority to DE201120110323 priority Critical patent/DE202011110323U1/en
Publication of DE202011110323U1 publication Critical patent/DE202011110323U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Einstückiger Latexschaum, umfassend eine erste Schicht aus Latexschaum und eine zweite und/oder nachfolgende Schicht aus Latexschaum, dadurch gekennzeichnet, dass die erste Schicht einen Zusatzstoff enthält, der in Form einer Lösung, Emulsion oder Dispersion aufgebracht wird und wobei die erste Schicht eine Dicke von 0,01 bis 9 mm aufweist.One-part latex foam comprising a first layer of latex foam and a second and / or subsequent layer of latex foam, characterized in that the first layer contains an additive which is applied in the form of a solution, emulsion or dispersion and wherein the first layer has a thickness of 0.01 to 9 mm.

Description

Technisches GebietTechnical area

Die vorliegende Erfindung betrifft latexbasierte Schäume, insbesondere betrifft die vorliegende Erfindung funktionalisierte Latexschäume zur Verwendung in Bett- oder Sitzprodukten, wobei der Schaum mit einem oder mehreren Zusatzstoffen imprägniert ist.The present invention relates to latex-based foams, in particular, the present invention relates to functionalized latex foams for use in bedding or seating products wherein the foam is impregnated with one or more additives.

Die vorliegende Erfindung stellt ebenfalls ein Verfahren für die Erstellung von Latexschaum bereit, einschließlich des Schrittes der Imprägnierung der Oberfläche des Latexschaumes mit einem Zusatzstoff, wobei der Zusatzstoff in Form einer Lösung, Emulsion oder Dispersion aufgebracht wird und die Imprägnierung mithilfe einer Sprühtechnik erfolgt.The present invention also provides a process for the production of latex foam, including the step of impregnating the surface of the latex foam with an additive, wherein the additive is applied in the form of a solution, emulsion or dispersion and the impregnation is carried out by means of a spraying technique.

Allgemeiner Stand der TechnikGeneral state of the art

Der Markt ist übersättigt mit geschäumten Produkten, die versuchen, Stützstrukturen Komfort zu verleihen. Zum Beispiel werden Matratzen- und Kissenauflagen häufig verwendet, um zusätzlichen Komfort zu liefern und um die Nutzungsdauer einer Matratze oder eines Kissens zu verlängern. Derartige Auflagen werden auf der Oberseite der Matratze oder des Kissens angeordnet und können aus dünnerem Schaum als die Matratze bestehen und flächengleich mit der Länge und Breite der Matratze oder des Kissens sein. Die Dicke der Auflage kann je nach von einem Benutzer gewünschtem Grad der Stützung und Polsterung gewählt werden. Die Auflage sorgt für eine zusätzliche Polsterung auf der Matratze oder dem Kissen und schützt die Matratze oder das Kissen vor Verschmutzung.The market is oversaturated with foamed products trying to give comfort to support structures. For example, mattress and cushion pads are often used to provide extra comfort and extend the useful life of a mattress or pillow. Such pads are placed on top of the mattress or pad and may be made of thinner foam than the mattress and coextensive with the length and width of the mattress or pad. The thickness of the overlay may be selected according to the degree of support and padding desired by a user. The pad provides extra padding on the mattress or pillow and protects the mattress or pillow from soiling.

Eine Vielfalt von Zusatzstoffen sind bekannt, die den geschäumten Produkten zugegeben werden. Derartige funktionale Wirkstoffe werden im Allgemeinen angewendet, um zu versuchen, das geschäumte Endprodukt mit wesentlich neuen Funktionalitäten zu versehen. Während derartige Wirkstoffe vorteilhaft sein können, kann es bei manchen Anwendungen auch zu unerwünschten Wirkungen in Bezug auf die ursprünglichen Eigenschaften des Schaumproduktes kommen.A variety of additives are known which are added to the foamed products. Such functional agents are generally used to try to provide the final foamed product with substantially new functionalities. While such agents may be beneficial, in some applications undesirable effects on the original properties of the foam product may also result.

Ein Beispiel für einen derartigen Zusatzstoff sind Latentwärmespeichermaterialien (PCM). Je nach Aufbaumaterial verfügen viele Matratzen und Kissen über eine geringe Wärmeableitung, was für den Benutzer beim Schlafen unangenehm ist. Folglich weisen manche Stützstrukturen Lüftungslöcher, extra Materialschichten, anpassbare Luftblasen und dergleichen auf, um zu versuchen, die Wärmeableitung zu verbessern.An example of such an additive is latent heat storage materials (PCM). Depending on the construction material many mattresses and pillows have a low heat dissipation, which is uncomfortable for the user when sleeping. Thus, some support structures have vent holes, extra layers of material, adjustable air bubbles, and the like to try to improve heat dissipation.

Während es wünschenswert ist, Schaumprodukte mit guten thermischen Eigenschaften bereitzustellen, ist es schwierig, effiziente thermische Eigenschaften zu erzielen und gleichzeitig die ursprünglichen Grundeigenschaften des Schaumes aufrechtzuerhalten.While it is desirable to provide foam products with good thermal properties, it is difficult to achieve efficient thermal properties while maintaining the original basic properties of the foam.

US 2009/0288259 beschreibt einen Latexschaum, der in einem angemessenen Grad die – manchmal widersprüchlichen – festgesetzten Anforderungen widerspiegelt. Darüber hinaus ist die Wärmeregulierung des bekannten Schaumes weiterhin nicht vollends zufriedenstellend, da die Wärmeregulierung des Schaumes, wie sich herausgestellt hat, auf Kosten der Wärmeregulierung oder auf Kosten der Schaumeigenschaften, wie etwa der Gleichmäßigkeit der Zellstruktur des Schaumes, erzielt wird. US 2009/0288259 describes a latex foam which, to a reasonable degree, reflects the - sometimes contradictory - stipulated requirements. In addition, heat regulation of the prior art foam is still not entirely satisfactory because heat regulation of the foam has been found to be achieved at the expense of heat regulation or at the expense of foam properties such as the uniformity of the cell structure of the foam.

Die Aufgabe der vorliegenden Erfindung besteht darin, wenigstens teilweise wenigstens einem der oben genannten Nachteile abzuhelfen oder andernfalls eine brauchbare Alternative bereitzustellen.The object of the present invention is to remedy, at least in part, at least one of the above-mentioned disadvantages or else to provide a viable alternative.

Gemäß dem Verfahren der vorliegenden Erfindung hat man überraschend festgestellt, dass, falls das geschäumte Produkt Latexschaum ist, die Leistung und Aktivität der funktionalisierten Partikel selbst aufrechterhalten bleiben und die Schaumeigenschaften, wie etwa Luft-/Feuchtigkeitsregulierung und Atmungsaktivität, nicht nachteilig beeinträchtigt werden. Man hat ebenfalls festgestellt, dass die Schäume eine verbesserte Leistung des funktionalen aktiven Wirkstoffes liefern.According to the process of the present invention, it has surprisingly been found that if the foamed product is latex foam, the performance and activity of the functionalized particles themselves are maintained and the foam properties, such as air / moisture control and breathability, are not adversely affected. It has also been found that the foams provide improved performance of the functional active agent.

Die vorliegende Erfindung betrifft Schäume, auf die Zusatzstoffe gesprüht werden. Die Schäume sind dadurch gekennzeichnet, dass sie die aktiven funktionalen Wirkstoffe in einer bestimmten Teilchengröße, einem bestimmten Teilchenabstand und Abdeckungswert innerhalb einer spezifischen Oberschicht des Schaumes aufweisen.The present invention relates to foams onto which additives are sprayed. The foams are characterized by having the active functional agents in a particular particle size, particle spacing and coverage within a specific top layer of the foam.

Gemäß der vorliegenden Erfindung gibt es zahlreiche Vorteile in Zusammenhang mit Schaumprodukten, die funktionale Teilchen nur auf der Oberfläche des Produktes enthalten, die vom Benutzer berührt wird, im Gegensatz zu Teilchen, die in der gesamten Struktur des Schaumes verteilt sind.In accordance with the present invention, there are numerous advantages associated with foam products that contain functional particles only on the surface of the product that is touched by the user, as opposed to particles dispersed throughout the structure of the foam.

Neben den wirtschaftlichen Vorteilen in Zusammenhang mit der Verwendung von weniger Teilchen gibt es auch Vorteile in Zusammenhang mit Schäumen, die funktionalisierte Teilchen enthalten, wobei das Teilchen im Schäumgemisch während der Schaumherstellung nicht vorhanden ist und stattdessen in einem Nachschäumschritt hinzugefügt wird. Das Vorhandensein der Teilchen im Schäumgemisch kann das Schäumverfahren beeinflussen und erfordert Anpassungen an die unterschiedlichen Parameter, die beim Schäumen angewendet werden.In addition to the economic benefits associated with the use of fewer particles, there are also advantages associated with foams containing functionalized particles, where the particle is not present in the foaming mixture during foam production and instead is added in a post-foaming step. The presence of the particles in the foaming mixture can affect the foaming process and requires adjustments to the different parameters used in foaming.

Demzufolge ist es ebenso eine weitere Aufgabe der Erfindung, funktionalisierten Latexschaum mit wenigen oder keinen Anpassungen an die herkömmlichen Schäumproduktionsschritte bereitzustellen. Accordingly, it is also a further object of the invention to provide functionalized latex foam with little or no adaptation to the conventional foam production steps.

Es ist eine weitere Aufgabe der Erfindung, eine dünne funktionalisierte Matratze bereitzustellen, von der Art, die als Auflage für eine herkömmliche Matratze verwendet werden kann. Insbesondere ist es eine Aufgabe der Erfindung, eine funktionalisierte Auflage mit einer Dicke von 2 bis 20 cm bereitzustellen, die die Fläche einer herkömmlichen Matratze aufweist. Diese Auflagenmatratze wird über einer herkömmlichen Matratze angeordnet und verwendet, um den Komfort von Latexschaum ohne den teuren Austausch der herkömmlichen Matratze zu liefern, wodurch die hierin genannten Vorteile geboten werden.It is a further object of the invention to provide a thin functionalized mattress of the type that can be used as a support for a conventional mattress. In particular, it is an object of the invention to provide a functionalized overlay with a thickness of 2 to 20 cm having the surface of a conventional mattress. This overlay mattress is placed over a conventional mattress and used to provide the comfort of latex foam without the costly replacement of the conventional mattress, thereby providing the advantages mentioned herein.

Die Auflage der vorliegenden Erfindung ist für die Verwendung auf der Oberseite einer vorhandenen herkömmlichen Matratze bestimmt, um den Komfort der Matratze zu erhöhen und gleichzeitig eine vorhandene herkömmliche Matratze zu verwenden. Die Auflage kann als Aftermarket-Produkt verwendet und auf einer Matratze angeordnet werden.The overlay of the present invention is intended for use on top of an existing conventional mattress to increase the comfort of the mattress while using an existing conventional mattress. The overlay can be used as an aftermarket product and placed on a mattress.

Auflagen für die Verwendung in Bett- oder Sitzprodukten sind bekannt. Diese Auflagen erstrecken sich über die gesamte Breite und Länge des jeweiligen Bett- oder Sitzproduktes. Ist das jeweilige Bett- oder Sitzprodukt eine Matratze, wird üblicherweise eine derartige Auflage auf einer Seite der Matratze und eine zweite Auflage auf der gegenüberliegenden Seite der Matratze angeordnet, wobei die Matratze gewissermaßen „sandwichartig” dazwischengeschoben wird. Diese Kombination wird dann üblicherweise mit einem Polsterstoffbezug bedeckt.Pads for use in bedding or seating products are known. These requirements extend over the entire width and length of the respective bed or seat product. If the respective bed product or seat product is a mattress, such a support is usually arranged on one side of the mattress and a second support on the opposite side of the mattress, the mattress being pushed in a manner of "sandwiching". This combination is then usually covered with a upholstery fabric cover.

Auflagen wurden bislang so ausgeführt, dass sie unterschiedliche Festigkeits- oder Härtegrade bieten. Insbesondere umfasst die Auflage in einer Bettstruktur, die eine Federkernmatratze und eine Auflage aufweist, Schaum, der geklebt oder gegossen ist.Editions have been made so far that they offer different levels of strength or hardness. In particular, the support in a bed structure comprising a spring mattress and a support comprises foam which is glued or cast.

Alternativ dazu kann die Auflage gemäß der vorliegenden Erfindung auf einer unfertigen Matratze (entweder einer herkömmliche Matratze mit Stahlfedern oder einer Schaummatratze) angeordnet werden und die Auflage und die Matratze werden dann mit Stoff bezogen.Alternatively, the overlay according to the present invention may be placed on an unfinished mattress (either a conventional steel spring mattress or a foam mattress) and the overlay and mattress are then fabric covered.

Diese und andere bevorzugte Aspekte der Erfindung werden im Folgenden noch genauer beschrieben und aus der detaillierten Beschreibung, einschließlich der Zeichnung, besser zu verstehen sein.These and other preferred aspects of the invention will be described more fully hereinafter and will be better understood from the detailed description, including the drawing.

Detaillierte Beschreibung der ErfindungDetailed description of the invention

Die vorliegende Erfindung betrifft die folgenden Ausführungsformen:
Einen einstückigen Latexschaum, umfassend eine erste Schicht aus Latexschaum und eine zweite und/oder nachfolgende Schicht aus Latexschaum, dadurch gekennzeichnet, dass die erste Schicht einen Zusatzstoff enthält, der in Form einer Lösung, Emulsion oder Dispersion aufgebracht wird und wobei die erste Schicht eine Dicke von 0,01 bis 9 mm aufweist.The present invention relates to the following embodiments:
A one-piece latex foam comprising a first layer of latex foam and a second and / or subsequent layer of latex foam, characterized in that the first layer contains an additive which is applied in the form of a solution, emulsion or dispersion and wherein the first layer has a thickness from 0.01 to 9 mm.

Den einstückigen Latexschaum, wobei der Latexschaum mit dem Zusatzstoff imprägniert ist.The one-piece latex foam, wherein the latex foam is impregnated with the additive.

Den einstückigen Latexschaum, wobei der Kern des Schaumes im Wesentlichen frei von dem Zusatzstoff ist. Der Kern ist hierin definiert als jener Teil der einstückigen Schaumstruktur, der sich, senkrecht auf die äußere Oberfläche gemessen, in einem Abstand von 9 mm zu der äußeren Oberfläche der Schaumstruktur, befindet.The one-piece latex foam, wherein the core of the foam is substantially free of the additive. The core is defined herein as that part of the one-piece foam structure which is located at a distance of 9 mm from the outer surface of the foam structure, measured perpendicular to the outer surface.

Den einstückigen Latexschaum, umfassend eine dritte Schicht mit einem Zusatzstoff, wobei der Zusatzstoff in Form einer Lösung, Emulsion oder Dispersion aufgebracht wird und wobei die dritte Schicht eine Dicke von 0,01 bis 9 mm aufweist.The one-piece latex foam comprising a third layer with an additive, wherein the additive is applied in the form of a solution, emulsion or dispersion and wherein the third layer has a thickness of 0.01 to 9 mm.

Den einstückigen Latexschaum, wobei der Zusatzstoff aus der Gruppe gewählt wird, bestehend aus i) Latentwärmespeichermaterial, ii) feuerhemmendem Mittel, iii) einem antibakteriellen aktiven Wirkstoff, iv) einem Antipilzmittel und Kombinationen, die wenigstens eines der Vorhergehenden umfassen.The one-piece latex foam, wherein the additive is selected from the group consisting of i) latent heat storage material, ii) fire retardant, iii) an antibacterial active ingredient, iv) an antifungal agent, and combinations comprising at least one of the foregoing.

Den einstückigen Latexschaum, wobei der Zusatzstoff ein Latentwärmespeichermaterial ist.The one-piece latex foam, wherein the additive is a latent heat storage material.

Den einstückigen Latexschaum, wobei die erste Schicht und/oder dritte Schicht farbig sind.The one-piece latex foam, wherein the first layer and / or third layer are colored.

Den einstückigen Latexschaum, wobei das Aufbringen durch eine Sprühtechnik erfolgt.The one-piece latex foam, wherein the application is carried out by a spray technique.

Ein Bettprodukt, umfassend einen Latexschaum gemäß der vorliegenden Erfindung.A bed product comprising a latex foam according to the present invention.

Das Bettprodukt, wobei das Produkt eine Matratzenauflage ist.The bed product wherein the product is a mattress overlay.

Die Matratzenauflage, wobei die Auflage eine Dicke von 2 bis 20 cm aufweist.The mattress pad, the pad has a thickness of 2 to 20 cm.

Ein Verfahren zur Herstellung eines einstückigen Latexschaumes gemäß der vorliegenden Erfindung, wobei das Verfahren folgende Schritte umfasst:

  • a. Gießen von Latexschaum
  • b. Vulkanisieren des gegossenen Latexschaumes
  • c. dosiertes Zuführen eines Zusatzstoffes zum vulkanisierten Latexschaum, wobei der Zusatzstoff in Form einer Lösung, Emulsion oder Dispersion dosiert zugeführt wird.
A process for producing a one-piece latex foam according to the present invention, the process comprising the steps of:
  • a. Pouring latex foam
  • b. Vulcanizing the cast latex foam
  • c. metered feeding of an additive to the vulcanized latex foam, wherein the additive is metered in the form of a solution, emulsion or dispersion.

Das Verfahren zur Herstellung eines einstückigen Latexschaumes gemäß der vorliegenden Erfindung, wobei das dosierte Zuführen durch eine Sprühtechnik erfolgt.The method for producing a one-piece latex foam according to the present invention, wherein the metered feeding is done by a spraying technique.

Ein Teileset eines Latexschaumes und ein Aufbringungsset, umfassend eine Lösung, Emulsion oder Dispersion eines Zusatzstoffes, der auf der Oberfläche der Schaumschicht aufzubringen ist.A set of latex foam and application kit comprising a solution, emulsion or dispersion of an additive to be applied to the surface of the foam layer.

Das Teileset, wobei der Zusatzstoff aus der Gruppe gewählt wird, bestehend aus i) Latentwärmespeichermaterial, ii) feuerhemmendem Mittel, iii) einem antibakteriellen aktiven Wirkstoff, iv) einem Antipilzmittel, v) einem Duftstoff und Kombinationen, die wenigstens eines der Vorhergehenden umfassen.The kit of parts wherein the additive is selected from the group consisting of i) latent heat storage material, ii) fire retardant, iii) an antibacterial active ingredient, iv) an antifungal agent, v) a fragrance, and combinations comprising at least one of the foregoing.

Latexschaum:Latex foam:

„Latex” ist hierin definiert als eine Dispersion von Polymerteilchen in einer kontinuierlichen Phase, wobei die Polymerteilchen vorzugsweise eine Größe in einem Bereich von 10 bis 1000 nm aufweisen. Der Latexschaumstoff kann aus Naturkautschuklatex oder aus einem oder mehreren solcher synthetischer Latizes, wie etwa Styrol-Polybutadien-Latex, Acrylnitril-Polybutadien-Latex, Polychloropren-Latex und dergleichen oder aus einer Mischung von Naturkautschuklatex und einem oder mehreren solcher synthetischer Latizes erstellt werden. Der Latexschaum umfasst herkömmlichen Latexschaum ebenso wie viskoelastischen Latexschaum."Latex" is defined herein as a dispersion of polymer particles in a continuous phase, wherein the polymer particles preferably have a size in a range of 10 to 1000 nm. The latex foam may be made of natural rubber latex or one or more of such synthetic latexes such as styrene-polybutadiene latex, acrylonitrile-polybutadiene latex, polychloroprene latex and the like, or a blend of natural rubber latex and one or more such synthetic latexes. The latex foam includes conventional latex foam as well as viscoelastic latex foam.

Der Feststoffgehalt geeigneter wässriger Latizes beträgt 20 bis 75 Gew.-%. Bevorzugte Latizes haben einen Feststoffgehalt von 50 bis 75 Gew.-%.The solids content of suitable aqueous latices is from 20 to 75% by weight. Preferred latexes have a solids content of 50 to 75 wt .-%.

Geeignete Polymerlatizes sind alle Dispersionen, in denen der Feststoff in einer flüssigen Phase verteilt ist, und diese Phase bildet wiederum eine Emulsion mit einer weiteren flüssigen Phase. Beispiele sind Latizes aus Polymeren, bestehend aus Dienen oder olefinisch ungesättigten Monomeren und Copolymeren daraus, wie etwa Polystyrol-Butadien-Latex, Polybutadien-Latex, Polyisopren-Latex, Naturkautschuklatex, Acrylnitril-Butadien-Latex, Polychloropren-Latex, Polydichlorbutadien-Latex, Latex aus einem Copolymer von Chloropren und Dichlorbutadien, Polyisopren-Latex, Latex aus chloriertem Polyisopren oder (Meth)acrylat-Latex. Polyurethandispersionen oder sonstige Dispersionen, in denen Polymere mithilfe von Emulgatoren oder Dispersionsmedien in Wasser verteilt werden, sind jedoch ebenso geeignet.Suitable polymer latices are all dispersions in which the solid is distributed in a liquid phase, and this phase in turn forms an emulsion with a further liquid phase. Examples are latexes of polymers consisting of dienes or olefinically unsaturated monomers and copolymers thereof, such as polystyrene-butadiene latex, polybutadiene latex, polyisoprene latex, natural rubber latex, acrylonitrile-butadiene latex, polychloroprene latex, polydichlorobutadiene latex, latex from a copolymer of chloroprene and dichlorobutadiene, polyisoprene latex, chlorinated polyisoprene latex or (meth) acrylate latex. However, polyurethane dispersions or other dispersions in which polymers are dispersed in water by means of emulsifiers or dispersion media are also suitable.

Bevorzugte Latizes umfassen Latizes aus Naturkautschuk, Styrol-Butadien-Kautschuk (SBR), wobei der SBR einen geringen Styrolgehalt (bis zu 27%) aufweist, Nitrilkautschuk (NBR), Isopren-Kautschuk, Neopren-Kautschuk, Polybutadien-Kautschuk, Isobutylen-Isopren-Kautschuk (IIR), Copolymere aus Acrylnitril, Methacrylnitril, Acrylaten, Methacrylaten, Vinylpyridin mit Butadien oder 2-Chlor-1,3-butadien und chloriertem Polyethylen oder Mischungen aus diesen.Preferred latexes include latexes of natural rubber, styrene-butadiene rubber (SBR), the SBR having a low styrene content (up to 27%), nitrile rubber (NBR), isoprene rubber, neoprene rubber, polybutadiene rubber, isobutylene-isoprene Rubber (IIR), copolymers of acrylonitrile, methacrylonitrile, acrylates, methacrylates, vinylpyridine with butadiene or 2-chloro-1,3-butadiene and chlorinated polyethylene or mixtures thereof.

Besonders bevorzugt sind Latizes aus Naturkautschuk, Styrol-Butadien-Kautschuk, Nitrilkautschuk, Polybutadien-Kautschuk, Isopren-Kautschuk oder Copolymere, die Acrylate umfassen.Particularly preferred are latexes of natural rubber, styrene-butadiene rubber, nitrile rubber, polybutadiene rubber, isoprene rubber or copolymers comprising acrylates.

Polymerhaltige Latizes, wie zum Beispiel SBR (Styrol-Butadien-Kautschuk) oder NBR (Acrylnitril-Butadien-Kautschuk), Polychloropren, Polybutadien, Polyisopren, Naturkautschuklatex, Polyvinylchlorid, (Meth)acrylat-Dispersionen oder Dispersionen aus Copolymeren daraus, sind normalerweise im Handel mit Feststoffkonzentrationen von über 50% erhältlich. Diese Konzentrationen können zum Beispiel durch Erhöhen der Konzentration von niedrigkonzentrierten Polymerlatizes erzielt werden. Die Konzentration von Naturkautschuklatex wird beispielsweise von 30% auf 60% Feststoffe erhöht.Polymer-containing latexes such as SBR (styrene-butadiene rubber) or NBR (acrylonitrile-butadiene rubber), polychloroprene, polybutadiene, polyisoprene, natural rubber latex, polyvinyl chloride, (meth) acrylate dispersions or dispersions of copolymers thereof are usually commercially available available with solids concentrations of over 50%. These concentrations can be achieved, for example, by increasing the concentration of low-concentration polymer latexes. For example, the concentration of natural rubber latex is increased from 30% to 60% solids.

Weitere bevorzugte Latizes sind Kombinationen von synthetischem Latex und Naturlatex. Bevorzugte Verhältnisse von Naturlatex zu synthetischem Latex können von 1:4 bis 6:4 variieren. Besonders bevorzugte Verhältnisse von Naturlatex zu synthetischem Latex liegen bei über 1:1.Other preferred latexes are combinations of synthetic latex and natural latex. Preferred ratios of natural latex to synthetic latex can vary from 1: 4 to 6: 4. Particularly preferred ratios of natural latex to synthetic latex are over 1: 1.

Die Verhältnisse sollten entsprechend dem verwendeten Latex optimiert werden.The conditions should be optimized according to the latex used.

Verfahren zur Herstellung von Latexschaum können solche sein, wo Latex in eine geschlossene Form gegossen wird, die mit Aluminiumstiften versehen ist, um eine gute Wärmeleitung sicherzustellen, und anschließend vulkanisiert, gewaschen und in ein Endprodukt getrocknet wird. Als Ergebnis aus dem Vorhandensein der Aluminiumstifte in der geschlossenen Form umfasst die Matratze vertikale, durchgängige Vertiefungen, die eine ordentliche Belüftung der Matratze sicherstellen. Gemäß diesem Verfahren können Matratzen mit einer Dicke von bis zu 20 cm hergestellt werden, wobei die Dicke hauptsächlich durch die Geschwindigkeit beschränkt wird, mit der die Wärme in den Kern des Latexmaterials geleitet werden kann. Ein alternatives Verfahren zur Herstellung von Latexschaum besteht darin, Latexschaum auf ein Endlosförderband zu gießen, gefolgt von Vulkanisieren, Waschen und abschließendem Trocknen. Die maximale Höhe der aus Latexschaum erzeugten Matratze beträgt ungefähr 6 cm, weil Wärme nicht schnell genug in den Kern des Latexmaterials geleitet werden kann, da auf dem Förderband keine Aluminiumstifte vorhanden sind. Folglich hat die erzeugte Latexplatte aufgrund des Fehlens von Aluminiumstiften auf dem Förderband keinerlei vertikale, durchgängige Kanäle.Processes for producing latex foam may be those where latex is poured into a closed mold provided with aluminum posts to ensure good thermal conduction and then vulcanized, washed and dried into a final product. As a result of the presence of the aluminum pins in the closed mold, the mattress includes vertical, continuous recesses which ensure proper ventilation of the mattress. According to this method, mattresses can be made with a thickness of up to 20 cm, the thickness being limited mainly by the speed with which the heat can be conducted into the core of the latex material. An alternative method of making latex foam is to cast latex foam on an endless belt followed by vulcanization, washing and final drying. The maximum height of the mattress made of latex foam is about 6 cm, because heat can not be conducted fast enough into the core of the latex material because there are no aluminum pins on the conveyor belt. As a result, the latex plate produced has no vertical, continuous channels due to the absence of aluminum posts on the conveyor belt.

Die vorliegende Erfindung betrifft latexbasierte Schäume, insbesondere betrifft die vorliegende Erfindung funktionalisierte Latexschäume für die Verwendung in einem Bett- oder Sitzprodukt, wobei der Schaum mit einem oder mehreren Zusatzstoffen imprägniert ist.The present invention relates to latex-based foams, more particularly, the present invention relates to functionalized latex foams for use in a bedding or sitting product wherein the foam is impregnated with one or more additives.

Mit „einstückig” ist gemeint, dass der Latexschaum ein einzelnes, durchgängiges Schaumprodukt mit einer durchgängigen Schaumstruktur ist.By "unitary" is meant that the latex foam is a single, continuous foam product having a continuous foam structure.

Zusatzstoff:Additive:

Ein kennzeichnendes Merkmal der Erfindung ist die Tatsache, dass die Oberfläche des Latexschaumes mit einem Zusatzstoff imprägniert ist.A distinguishing feature of the invention is the fact that the surface of the latex foam is impregnated with an additive.

Vorzugsweise weist der Schaum die Zusatzwirkstoffe in Form von Teilchen auf. Insbesondere ist die Schicht 1 enthaltende Oberfläche in einer Ebene im Längsquerschnitt zu wenigstens 1% der Oberfläche mit Teilchen bedeckt. Vorzugsweise umfasst die Zusatzstoff enthaltende Schicht wenigstens 0,001 g/m2 Teilchen, besonders bevorzugt jedoch 0,1 bis 1000 g/m2, am meisten bevorzugt 50–450 g/m2.Preferably, the foam has the additive active ingredients in the form of particles. In particular, the layer is 1 containing surface in a plane in longitudinal cross section to at least 1% of the surface covered with particles. Preferably, the additive-containing layer comprises at least 0.001 g / m 2 of particles, more preferably 0.1 to 1000 g / m 2 , most preferably 50-450 g / m 2 .

Vorzugsweise weist die Zusatzstoff enthaltende Schicht eine Dicke von 0,01–9 mm auf. Als Ergebnis aus der vorgeschlagenen Dicke und Partikelmenge ist der erfindungsgemäße Latexschaumstoff besonders geeignet für die Wärme- und Luft-/Feuchtigkeitsregulierung, die notwendig ist. Bei normalem Gebrauch des Latexschaumes erfährt der Schaum eine bestimmte Wärmeentwicklung und mechanische Beanspruchung. Die festgestellte Dicke und die Bereitstellung des Zusatzstoffes können dem Schaum die gewünschte Elastizität, Rückstellungsfähigkeit und Atmungsaktivität und Wärmeregulierung verleihen und somit zahlreiche Anforderungen erfüllen, die materialtechnisch widersprüchlich sind.Preferably, the additive-containing layer has a thickness of 0.01-9 mm. As a result of the proposed thickness and amount of particulate, the latex foam of the invention is particularly suitable for heat and air / moisture control which is necessary. With normal use of the latex foam, the foam undergoes certain heat and mechanical stress. The determined thickness and provision of the additive can provide the foam with the desired elasticity, resilience and breathability and thermal control, and thus meet many requirements that are materially contradictory.

Zum Zwecke der Wirtschaftlichkeit und Effektivität hat man es als vorteilhaft erachtet, funktionalisierte Teilchen, wenn verwendet, in die Oberflächenschicht 1 einzuschließen. Da die Oberflächenschicht 1 verglichen mit der übrigen Schicht des Schaumes 2 relativ dünn ist, ermöglicht das Anordnen derartiger Wirkstoffe in Schicht 1 den Einsatz einer geringeren Gesamtmenge der Teilchen, um verglichen mit dickeren Schichten ähnliche wirksame Konzentrationen zu erzielen und dadurch Kosten in Verbindung mit den Teilchen zu senken. Zudem wird durch das Anordnen derartiger Teilchen in der Oberflächenschicht 1 sichergestellt, dass die Wirkstoffe in der äußersten Schaumschicht, das heißt, den Körper berührenden Zonen, und nicht in vom Benutzer entfernten Zonen angeordnet sind, was die Wirksamkeit der Teilchen fördern kann.For the sake of economy and effectiveness, it has been found advantageous to incorporate functionalized particles, when used, into the surface layer 1 include. Because the surface layer 1 compared with the remaining layer of the foam 2 is relatively thin, allows arranging such agents in layer 1 the use of a lower total amount of particles to achieve similar effective concentrations as compared to thicker layers, thereby reducing costs associated with the particles. In addition, by arranging such particles in the surface layer 1 ensures that the active ingredients are located in the outermost foam layer, that is, the body contacting zones, rather than in user-removed zones, which may promote the effectiveness of the particles.

Geeignete funktionale Zusatzstoffklassen umfassen: i) Latentwärmespeichermaterialien ii) Pigmente iii) antibakterielle Wirkstoffe und Antipilzmittel iv) Hautbehandlungswirkstoffe (zum Beispiel Befeuchtungsmittel, einschließlich gemischte und okklusive), sonstige Hautgefühlswirkstoffe, Feuchtigkeitsmittel, Hautreparaturstoffe, einschließlich Wirkstoffe zur Vorbeugung, Verzögerung und/oder Bekämpfung von Hautfurchen, Falten oder Atrophie, die Haut beruhigende und/oder heilende Wirkstoffe v) Duftstoffe vi) feuerhemmende Mittel und Mischungen davon.Suitable functional additive classes include: i) latent heat storage materials ii) pigments iii) antibacterial agents and antifungal agents iv) skin treatment agents (e.g., moisturizers, including mixed and occlusive), other skin feel agents, moisturizers, skin repair agents, including active ingredients for the prevention, retardation and / or control of cutaneous fissures , Wrinkles or atrophy, the skin soothing and / or curative active ingredients v) fragrances vi) fire retardants and mixtures thereof.

Eine besondere Klasse funktionalisierter Zusatzstoffe umfasst ein Latentwärmespeichermaterial (PCM).A special class of functionalized additives includes a latent heat storage material (PCM).

Ein Beispiel für ein PCM ist Paraffin. Im Fall einer Energieabgabe oder -entladung im Bereich des Schmelzpunktes des PCM hält das Material seine Schmelztemperatur während des Phasenübergangs von einem festen in einen flüssigen Zustand oder umgekehrt aufrecht. Erst nach dem Phasenübergang wird die Temperatur weiter ansteigen oder andernfalls sinken. Dieser Effekt wird verwendet, um die Temperatur des Materials zu regulieren, dem das PCM hinzugefügt wird. Dies ermöglicht es, die Temperatur innerhalb der Oberfläche des Latexschaumes auf einer konstanten Temperatur zu halten. Wenn ein Schaumprodukt, wie etwa eine Matratze oder Auflage, gemäß der vorliegenden Erfindung hergestellt wird, ist es vorteilhafterweise möglich, eine effiziente Wärmeverwaltung des Schaumes sicherzustellen. Folglich ist es möglich, den Schaum daran zu hindern, zu warm zu werden, ihn aber ebenso daran zu hindern, eine unzureichende Isolierung bereitzustellen. Ein mögliches Latentwärmespeichermaterial kann phasenwechselnde Mikrokapseln (erhältlich unter der Produktbezeichnung Outlast) umfassen, die Materialien enthalten, die bei naher Körpertemperatur Phasenwechsel vollziehen können. Als Ergebnis kann Wärmeenergie in der Barriereschicht gespeichert werden, wodurch ein Produkt entsteht, das ein kühles oder warmes Gefühl bewirken kann.An example of a PCM is paraffin. In the case of energy release or discharge in the region of the melting point of the PCM, the material maintains its melting temperature during the phase transition from a solid to a liquid state or vice versa. Only after the phase transition, the temperature will continue to increase or otherwise decrease. This effect is used to regulate the temperature of the material to which the PCM is added. This makes it possible to keep the temperature within the surface of the latex foam at a constant temperature. When a foam product, such as a mattress or pad, is made in accordance with the present invention, it is advantageously possible to ensure efficient heat management of the foam. Consequently, it is possible to prevent the foam from becoming too warm, but also to prevent it from providing insufficient insulation. A potential latent heat storage material may include phase change microcapsules (available under the product name Outlast) which contain materials that can phase change at near body temperature. As a result, heat energy can be stored in the barrier layer, creating a product that can cause a cool or warm feeling.

Vorzugsweise umfasst die PCM-enthaltende Schicht eine kristallisierbare organische Substanz als PCM. Dies kann zum Beispiel ein n-Paraffin mit einem Schmelzpunkt zwischen –10°C und 65°C (n-Docaden bis n-Octacosan) sein. Das Paraffin kann eine an eine poröse Struktur gebundene Form aufweisen, kann aber auch in mikroverkapselter Form in eine Polymerdispersion eingebracht werden. Das Polymer kann zum Beispiel zur Gruppe der Acrylate, Polyurethane, Styrol-Butadien-Latizes, Silikone oder Polymermischungen dieser Art gehören.Preferably, the PCM-containing layer comprises a crystallizable organic substance as PCM. This may be, for example, an n-paraffin having a melting point between -10 ° C and 65 ° C (n-docaden to n-octacosan). The paraffin may have a form bound to a porous structure, but may also be incorporated in microencapsulated form into a polymer dispersion. The For example, polymer may be included in the group of acrylates, polyurethanes, styrene-butadiene latexes, silicones or polymer blends of this type.

In einer bevorzugten Ausführungsform des erfindungsgemäßen geschäumten Produkts wird das PCM in Form von Mikrokapseln aufgebracht.In a preferred embodiment of the foamed product according to the invention, the PCM is applied in the form of microcapsules.

Insbesondere ist die Substratschicht 1 aus Latexschaum mit einer Dicke von 2–20 cm hergestellt, die mit 50–450 g/m2 PCM versehen ist.In particular, the substrate layer 1 Made of latex foam with a thickness of 2-20 cm, which is provided with 50-450 g / m 2 PCM.

Bevorzugte PCM-Materialien umfassen jene, die in den Patentschriften WO 01/06054 ; WO 01/62376 ; US 2002/055560 und WO 2006/013165 erläutert werden. Hochbevorzugte PCM sind jene, die in WO 2006/117702 beschrieben sind.Preferred PCM materials include those described in patents WO 01/06054 ; WO 01/62376 ; US 2002/055560 and WO 2006/013165 be explained. Highly preferred PCMs are those that are in WO 2006/117702 are described.

Beispiele für im Handel erhältliche PCMs umfassen Mikrathermic G Soft; Micracat B; Micra EF und Micrafix (von DEVAN Chemicals).Examples of commercially available PCMs include Mikrathermic G Soft; Micracat B; Micra EF and Micrafix (from DEVAN Chemicals).

Gemäß einer weiteren Klasse von Zusatzstoffen kann die Zusatzstoff enthaltende Schicht auch antibakterielle Substanzen und Antipilzmittel umfassen.According to another class of additives, the additive-containing layer may also comprise antibacterial substances and antifungal agents.

In einer weiteren veranschaulichenden Ausführungsform kann die Oberflächenschicht 1 einen aktiven Wirkstoff wie etwa Probiotika und/oder Silber umfassen, um die Entstehung von Pilzen, Bakterien und/oder Parasiten zu minimieren oder zu verhindern. Eine mögliche Oberflächenschicht 1, die einen solchen aktiven Wirkstoff umfasst, ist Vacuflex 18411AG, erhältlich bei Omniflex, Inc. Solch aktiver Wirkstoff kann in Produkten, wie etwa Matratzen und/oder Auflagen, wie oben erwähnt, wünschenswert sein.In a further illustrative embodiment, the surface layer 1 include an active ingredient such as probiotics and / or silver to minimize or prevent the formation of fungi, bacteria and / or parasites. A possible surface layer 1 containing such an active ingredient is Vacuflex 18411AG available from Omniflex, Inc. Such active ingredient may be desirable in products such as mattresses and / or pads as mentioned above.

Gemäß einer weiteren Klasse von Zusatzstoffen kann die Zusatzstoff enthaltende Schicht auch Pigmente umfassen.According to another class of additives, the additive-containing layer may also comprise pigments.

Die Verwendung eines Pigments als Zusatzstoff kann eine farbige oder gemusterte Schicht 1a, 1b (zum Beispiel eine farbige und/oder gemusterte Oberflächenschicht) bereitstellen, optional in Kombination mit einem PCM, wodurch ein farbiges oder gemustertes Schaumprodukt, wie etwa eine Matratze oder Auflage, bereitgestellt wird. Somit kann ein Artikel mit viel mehr Farbvariationen geschaffen werden als durch die bloße Verwendung von farbigem oder pigmentiertem Gel möglich wäre. Die Verwendung eines pigmentierten PCM oder sonstige Variationen im Erscheinungsbild der Substratschicht 1a, 1b können dem geschäumten Produkt dieses Erscheinungsbild verleihen, während sie gleichzeitig dem Endverbraucher einen Hinweis auf die Funktionalität des PCM liefern. In einer bevorzugten Ausführungsform weist das mit PCM imprägnierte, geschäumte Produkt ebenso ein blau/rotes Aussehen auf, was die Wärmeregulierungsfähigkeit des geschäumten Produkts widerspiegelt.The use of a pigment as an additive can be a colored or patterned layer 1a . 1b (for example, a colored and / or patterned surface layer), optionally in combination with a PCM, to provide a colored or patterned foam product, such as a mattress or overlay. Thus, an article with much more color variations can be created than would be possible by the mere use of colored or pigmented gel. The use of a pigmented PCM or other variations in the appearance of the substrate layer 1a . 1b can give the foamed product this appearance while at the same time providing an indication to the end user of the functionality of the PCM. In a preferred embodiment, the PCM impregnated foamed product also has a blue / red appearance, reflecting the heat-regulating ability of the foamed product.

Gemäß einer weiteren Klasse von Zusatzstoffen kann die Zusatzstoff enthaltende Schicht auch so genannte Polymermikropartikel umfassen, die häufig in Körperpflege- und Pharmarezepturen verwendet werden, um die Freisetzung eines aktiven Inhaltsstoffes auszudehnen, um den aktiven Inhaltstoff vor dem Abbau in einer Zusammensetzung zu schützen und/oder um die Rezeptierung des aktiven Inhaltsstoffes in einer Zusammensetzung aufgrund von Schwierigkeiten, wie etwa Löslichkeit oder Rezepterscheinungsbild, zu ermöglichen.According to another class of additives, the additive-containing layer may also include so-called polymer microparticles, which are often used in personal care and pharmaceutical formulations to extend the release of an active ingredient, to protect the active ingredient from degradation in a composition, and / or to facilitate formulation of the active ingredient in a composition due to difficulties such as solubility or prescriptive appearance.

Polymermikropartikel umfassen diskrete, frei fließende Partikel, die einen aktiven Wirkstoff in einer Polymermatrix absorbieren, adsorbieren, einschließen oder in sonstiger Weise festhalten können. Derartige Mikropartikel können eine kontrollierte Freisetzung des aktiven Wirkstoffes im Lauf der Zeit bereitstellen, entweder durch Aufbrechen der Mikropartikel, wobei der aktive Wirkstoff freigesetzt wird, wenn ausreichend Druck oder Scherbeanspruchung auf die Mikropartikel ausgeübt wird, oder die Mikropartikel können halbdurchlässig oder porös sein, wodurch der aktive Wirkstoff aus dem Partikel diffundieren kann. In manchen Ausführungsformen liefern die Polymermikropartikel selbst, ohne geladenen aktiven Wirkstoff, einen gewünschten Nutzen. Darüber hinaus können die Mikropartikel neben sich selbst mehrere aktive Wirkstoffe befördern.Polymer microparticles include discrete, free-flowing particles that can absorb, adsorb, entrap, or otherwise hold an active agent in a polymer matrix. Such microparticles may provide controlled release of the active agent over time, either by disrupting the microparticles, releasing the active agent when sufficient pressure or shear is applied to the microparticles, or the microparticles may be semipermeable or porous, thereby rendering the microparticles porous active ingredient can diffuse out of the particle. In some embodiments, the polymer microparticles themselves, without charged active agent, provide a desired benefit. In addition, the microparticles can carry several active ingredients in addition to themselves.

Gemäß einer weiteren Klasse von Zusatzstoffen kann die Zusatzstoff enthaltende Schicht auch funktionalisierte Teilchen mit einem aktiven Wirkstoff umfassen, der entweder direkt verwendet oder auf Teilchen geladen werden kann, umfassend, aber nicht beschränkt auf: Hautaufheller, Wirkstoffe gegen Akne, Antipilzmittel, botanische Extrakte, Mineralien, Pflanzenextrakte, Pflanzenextraktkonzentrate (zum Beispiel Aloe Vera), Weichmacher, Feuchtigkeitsmittel, Hautberuhigungsstoffe (zum Beispiel Talk), Farbstoffe, Duftstoffe und dergleichen. Die Mengen solch vorhandener aktiver Wirkstoffe sind ausreichend, um ihre vorgesehene Funktion zu erfüllen, ohne die Eigenschaften oder Nutzen anderer im geschäumten Produkt vorhandenen Inhaltstoffe nachteilig zu beeinflussen.According to another class of additives, the additive-containing layer may also comprise functionalized particles having an active ingredient which may either be used directly or loaded onto particles, including, but not limited to, skin whitening agents, anti-acne agents, antifungals, botanical extracts, minerals , Plant extracts, plant extract concentrates (for example, aloe vera), plasticizers, moisturizers, skin tranquilizers (for example, talc), dyes, perfumes, and the like. The amounts of such active agents present are sufficient to perform their intended function without adversely affecting the properties or benefits of other ingredients present in the foamed product.

Besonders bevorzugt kann ein funktionalisierter Zusatzstoff einer oder eine Mischung aus einem kosmetischen Stoff, einem medizinischen Aktivstoff, einem in der Kosmetik und Körperpflege verwendeten Stoff oder jeder sonstige Stoff sein, der für eine topische Anwendung nützlich ist. Solch topisch aktive Wirkstoffe umfassen, sind aber nicht beschränkt auf Hautpflegestoffe, Pflanzenextrakte, Antioxidantien, Insektenschutzmittel, Gegenreizmittel, Vitamine, Steroide, antibakterielle Stoffe, Antipilzmittel, entzündungshemmende Stoffe, Sonnenschutzmittel, optische Aufheller und sonstige kosmetische und medizinische topisch wirksame Stoffe.More preferably, a functionalized additive may be one or a mixture of a cosmetic, a medical active, a substance used in cosmetics and personal care, or any other substance useful for topical application. Such topically active agents include, but are not limited to skin care, plant extracts, antioxidants, insect repellents, Anti-irritants, vitamins, steroids, antibacterial substances, antifungals, anti-inflammatory agents, sunscreens, optical brighteners and other cosmetic and medical topically active substances.

Zusatzstoffzusammensetzung:Additive Composition:

(A) Trägerkomponente(A) Carrier component

Die Zusammensetzungen, aus denen die Zusatzstoff enthaltenden Schichten gebildet sind, umfassen einen oder mehrere Zusatzstoffe, die in einem Träger verteilt sind, der eines oder mehrere flüssige Verdünnungsmittel umfasst. Geeignete flüssige Verdünnungsmittel können flüchtig oder nichtflüchtig und polar oder unpolar sein. Eine Vielfalt solcher Träger ist dem Fachmann bekannt und ist allgemein dafür bekannt, eines oder mehrere kompatible Verdünnungsmittel, Streckmittel und dergleichen zu umfassen.The compositions of which the additive-containing layers are formed comprise one or more additives distributed in a carrier comprising one or more liquid diluents. Suitable liquid diluents may be volatile or nonvolatile and polar or nonpolar. A variety of such carriers are known to those skilled in the art and are generally known to include one or more compatible diluents, diluents, and the like.

Die Art des in der vorliegenden Erfindung verwendeten Trägers hängt von der Art des gewünschten Produkts ab. Die für den Erfindungsgegenstand nützlichen Zusammensetzungen können in einer breiten Vielfalt von Produktarten vorliegen, einschließlich flüssiger oder halbflüssiger Formen. Diese umfassen, aber sind nicht beschränkt auf Lotionen, Cremes, Gels, Sprays, Salben und Pasten. Für die Erfindung nützliche Zusammensetzungen können zum Beispiel eine Lösung aus Materialien umfassen, in der der Zusatzstoff verteilt ist, oder sie können eine Emulsion umfassen, in der der Zusatzstoff verteilt ist. Die Wahl der Trägerkomponente und die Mengen hängen von der gewünschten Produktart ab und sind dem Durchschnittsfachmann bekannt.The type of support used in the present invention depends on the type of product desired. The compositions useful for the subject invention may be in a wide variety of product types, including liquid or semi-liquid forms. These include, but are not limited to lotions, creams, gels, sprays, ointments and pastes. For example, compositions useful in the invention may comprise a solution of materials in which the additive is distributed, or they may comprise an emulsion in which the additive is distributed. The choice of carrier component and amounts depend on the type of product desired and are known to one of ordinary skill in the art.

Die Zusammensetzungen umfassen üblicherweise etwa 0,1% bis etwa 35% Zusatzstoff und etwa 5% bis etwa 90% flüssigen Träger. Die Zusammensetzungen umfassen im Allgemeinen etwa 5% bis etwa 90% flüssiges Verdünnungsmittel. Die Zusammensetzungen weisen vorzugsweise eine Viskosität von etwa 10 bis etwa 50.000 mPa·s bei 10 sec–1 auf (bei 25°C unter Verwendung von parallelen 60 mm-Platten mit 0,5 mm Spalt bei einer Rate von 10 sec–1).The compositions typically comprise from about 0.1% to about 35% additive and from about 5% to about 90% liquid carrier. The compositions generally comprise from about 5% to about 90% liquid diluent. The compositions preferably have a viscosity of from about 10 to about 50,000 mPa · s at 10 sec -1 (at 25 ° C using 60 mm parallel plates with 0.5 mm gap at a rate of 10 sec -1 ).

Diese Materialien sind dem Fachmann wohl bekannt und im Handel erhältlich. Die Wahl der jeweiligen Art und des Niveaus eines bestimmten Zusatzstoffmaterials für den jeweiligen Zweck in einem bestimmten Produkt unterliegt der fachmännischen Kenntnis des Handwerkers.These materials are well known to those skilled in the art and are commercially available. The choice of the particular type and level of a particular additive material for the particular purpose in a particular product is subject to the skill of the artisan.

In einer weiteren Ausführungsform ist die Zusammensetzung als kosmetische Zusammensetzung rezeptiert. Wie hernach verwendet, bezieht sich der Ausdruck „kosmetische Zusammensetzung” auf ein flüssiges oder halbflüssiges Hautkosmetikprodukt, das Lotionen, Cremes, Gels, Pasten und dergleichen umfasst, aber nicht darauf beschränkt ist.In a further embodiment, the composition is formulated as a cosmetic composition. As used hereinafter, the term "cosmetic composition" refers to a liquid or semi-liquid skin cosmetic product which includes, but is not limited to lotions, creams, gels, pastes, and the like.

Zusammensetzungen, die unter Verwendung der vorliegenden Erfindung erzeugt werden sollen, sind vorzugsweise im Allgemeinen von flüssiger Form. Jegliche Zusatzmaterialien, die vorhanden sind, können bei Raumtemperatur flüssig, fest oder halbfest sein, doch sollten sie so gewählt werden, dass die Imprägnierung der Zusammensetzung ermöglicht wird, um die Zusatzstoff enthaltende Schicht 1 zu bilden.Compositions to be produced using the present invention are preferably generally of liquid form. Any adjunct materials that are present may be liquid, solid or semi-solid at room temperature, but they should be chosen to allow impregnation of the composition around the additive-containing layer 1 to build.

Für ein verbessertes Sprühen haben bevorzugte Zusammensetzungen einen Feststoffgehalt von etwa 60 Gew.-% oder weniger. Diesbezüglich bezieht sich „Feststoffe” auf Zusatzstoffe, die in der Zusammensetzung nicht löslich oder mischbar sind.For improved spraying, preferred compositions have a solids content of about 60% by weight or less. In this regard, "solids" refers to additives that are not soluble or miscible in the composition.

Besonders bevorzugte Zusatzstoffe umfassen feuerhemmende Mittel, wärmeregulierende Zusatzstoffe, wie etwa PCMs; geruchsüberdeckende oder – neutralisierende Zusatzstoffe; Febreze®; Duftstoffe; aromatische Zusatzstoffe, wie etwa Kamille, Vanille, Eukalyptus; Ag-Nanopartikel, Au-Nanopartikel, ätherische Öle (Aloe Vera); Probiotika; Mückenschutz, Iod; Magnesium; Calcium; Talk; Antipilzzusatzstoffe; Antialgenzusatzstoffe; Bakterizide; biokeramische Füllstoffe; Härter; Teeextrakte (grüner Tee); Antistaubmilben-Zusatzstoffe; wasserabweisende Stoffe.Particularly preferred additives include fire retardants, heat regulating additives such as PCMs; odor masking or neutralizing additives; Febreze ®; Fragrances; aromatic additives such as chamomile, vanilla, eucalyptus; Ag nanoparticles, Au nanoparticles, essential oils (aloe vera); probiotics; Mosquito repellent, iodine; Magnesium; calcium; Talk; Antifungal additives; Anti algae additives; bactericides; bioceramic fillers; Harder; Tea extracts (green tea); Anti dust mites additives; water repellent fabrics.

Der funktionalisierte Zusatzstoff kann auf das Latexschaumsubstrat 1 durch jedes geeignete Verfahren aufgebracht werden. Nichteinschränkende Beispiele umfassen direktes Aufbringen des Polymerpartikelabgabesystems auf das Substrat durch beispielsweise Besprengen, Bestäuben oder Besprühen. Bevorzugte Verfahren umfassen das Verteilen des Zusatzstoffes in einer wässrigen oder nichtwässrigen Flüssigkeit oder Mischung von Flüssigkeiten, dann das Aufbringen der Dispersion auf das Substrat. Die Dispersion kann durch Sprühen, Beschichten, Eintauchen, Aufgießen oder anderweitig auf den Latexschaum aufgebracht werden. Bevorzugt werden Sprühtechniken.The functionalized additive can be applied to the latex foam substrate 1 be applied by any suitable method. Non-limiting examples include direct application of the polymer particle delivery system to the substrate by, for example, sprinkling, dusting or spraying. Preferred methods include distributing the additive in an aqueous or nonaqueous liquid or mixture of liquids, then applying the dispersion to the substrate. The dispersion can be applied to the latex foam by spraying, coating, dipping, pouring or otherwise. Preference is given to spraying techniques.

Das Herstellungsverfahren des Schaumes gemäß der vorliegenden Erfindung umfasst das Imprägnieren des Schaumes mit einem Zusatzstoff. Das Verabreichen des Zusatzstoffes kann das Gießen einer Menge (zum Beispiel Volumen, Gewicht und/oder Dicke) einer Gelvorstufe umfassen, die ausreichend ist, um in die Schaumschicht bis zu einer gewünschten Tiefe einzudringen, die je nach Produkt und/oder Anwendung unterschiedlich sein kann.The production process of the foam according to the present invention comprises impregnating the foam with an additive. Administering the additive may involve pouring a quantity (e.g., volume, weight, and / or thickness) of a gel precursor sufficient to penetrate the foam layer to a desired depth, which may vary depending on the product and / or application ,

Aus praktischen Zwecken kann es aufgrund des Gewichts des funktionalen Zusatzstoffes nützlich sein, die Eindringtiefe des Materials in den Schaum zu minimieren und gleichzeitig die gewünschten Eigenschaften des Endprodukts auszuwägen, zum Beispiel Atmungsaktivität, Weichheit, Gesamtgewicht und dergleichen. Zum Beispiel kann es für Produkte wie Matratzenauflagen wünschenswert sein, das Gesamtgewicht der Auflage zu minimieren. Das Anpassen der Eindringtiefe des Zusatzstoffes in die Schaumschicht kann somit die gewünschte Weichheit liefern und gleichzeitig den Beitrag des Zusatzstoffes zum Gesamtgewicht der Auflage minimieren.For practical purposes, it may be useful, due to the weight of the functional additive, to increase the penetration depth of the material into the foam while at the same time weighing the desired properties of the final product, for example breathability, softness, total weight and the like. For example, for products such as mattress pads, it may be desirable to minimize the total weight of the overlay. Adjusting the depth of penetration of the additive into the foam layer can thus provide the desired softness while minimizing the contribution of the additive to the total weight of the overlay.

Zum Beispiel kann es für eine Matratzenauflage mit 2 cm Dicke wünschenswert sein, eine funktionalen Zusatzstoff enthaltende Schicht von etwa 0,1 mm bis etwa 1 mm zu umfassen, und eine derartige Tiefe kann durch Aufbringen von etwa 50 g/m2 Zusatzstoff auf die Oberfläche der Schaumschicht erzielt werden, was die Zusatzstoffschicht 1 definiert. Das Imprägnieren des Zusatzstoffes in die Schaumschicht 1 kann von Hand erfolgen oder das Verfahren kann automatisch ausgeführt werden. Zum Beispiel kann der Zusatzstoff auf der Schaumschicht 1 mithilfe vielfältigster Techniken angeordnet werden, wie etwa, aber nicht nur beschränkt auf eine Walz-, Gieß-, Sprüh- oder Vakuumtechnik und/oder dergleichen.For example, it may be desirable for a mattress with 2 cm thickness, a functional additive to include layer containing from about 0.1 mm to about 1 mm, and such a depth, by applying from about 50 g / m 2 additive on the surface the foam layer can be achieved, which is the additive layer 1 Are defined. The impregnation of the additive in the foam layer 1 can be done by hand or the procedure can be performed automatically. For example, the additive may be on the foam layer 1 be arranged by a variety of techniques, such as, but not limited to, a rolling, casting, spraying or vacuum technique and / or the like.

Der Schaum kann jeden natürlichen oder synthetischen Schaum umfassen, sowohl als Platte als auch gegossen. Die Schäume sind offenzellig. Der Schaum kann auch recycelten Schaum, schaumimprägnierte Fasermatten oder mikrozellularen Elastomerschaum umfassen. Darüber hinaus kann der Schaum organische und/oder anorganische Füllstoffe umfassen. Ferner können zusätzliche Zusatzstoffe in die Schaumzusammensetzung eingegliedert werden, wie etwa, aber nicht nur beschränkt auf feuerhemmende Mittel, Beschlagschutzmittel, Ultraviolettabsorber, Wärmestabilisatoren, Pigmente, Farbstoffe, Geruchskontrollstoffe, Duftstoffe und dergleichen.The foam may comprise any natural or synthetic foam, both as a plate and cast. The foams are open-celled. The foam may also comprise recycled foam, foam-impregnated fiber mats or microcellular elastomeric foam. In addition, the foam may include organic and / or inorganic fillers. Further, additional additives can be incorporated into the foam composition, such as, but not limited to, fire retardants, antifoggants, ultraviolet absorbers, heat stabilizers, pigments, dyes, odor control agents, perfumes, and the like.

1 zeigt eine Querschnittsansicht eines Querschnitts einer Ausführungsform eines beispielhaften einstückigen Latexschaums gemäß der vorliegenden Offenbarung, umfassend gegenüberliegende obere und untere Schichten 1a, 1b. Der einstückige Latexschaum, umfassend eine erste Schicht 1 und eine zweite Schicht 2 und eine Zusatzstoff enthaltende Schaumschicht 1, die angrenzend an die Schaumschicht 2 angeordnet ist. 1 FIG. 12 is a cross-sectional view of a cross-section of one embodiment of an exemplary one-piece latex foam according to the present disclosure, including opposing top and bottom layers. FIG 1a . 1b , The one-piece latex foam comprising a first layer 1 and a second layer 2 and an additive-containing foam layer 1 , which is adjacent to the foam layer 2 is arranged.

In manchen Ausführungsformen kann eine optionale Materialschicht in und/oder zwischen jeder der vorhergehenden Schichten angeordnet sein, die Farbe, Text und/oder Grafiken, Kennzeichnungen, wie etwa Etiketten, Prägungen und dergleichen umfassen kann.In some embodiments, an optional layer of material may be disposed in and / or between each of the preceding layers, which may include color, text and / or graphics, indicia, such as labels, embossments, and the like.

Die vorliegende Erfindung betrifft ferner ein Teileset eines Latexschaums und ein Aufbringungsset, umfassend eine Lösung, Emulsion oder Dispersion eines Zusatzstoffes, der auf einer Oberfläche der Schaumschicht aufzubringen ist. Der Zusatzstoff wird aus der Gruppe gewählt, bestehend aus i) Latentwärmespeichermaterial, ii) feuerhemmendem Mittel, iii) einem antibakteriellen aktiven Wirkstoff, iv) einem Antipilzmittel, v) einem Duftstoff und Kombinationen, die wenigstens eines der Vorhergehenden umfassen.The present invention further relates to a latex foam part set and an application set comprising a solution, emulsion or dispersion of an additive to be applied to a surface of the foam layer. The additive is selected from the group consisting of i) latent heat storage material, ii) fire retardant, iii) an antibacterial active ingredient, iv) an antifungal agent, v) a perfume, and combinations comprising at least one of the foregoing.

Verfahren:Method:

Die vorliegende Erfindung betrifft ein Verfahren zur Herstellung eines einstückigen Latexschaumes wie oben beschrieben, wobei das Verfahren folgende Schritte umfasst:

  • a. Gießen von Latexschaum;
  • b. Vulkanisieren des gegossenen Latexschaumes;
  • c. Imprägnieren des vulkanisierten Latexschaumes mit einem Zusatzstoff, wobei der Zusatzstoff in Form einer Lösung, Emulsion oder Dispersion aufgebracht wird;
  • d. und vorzugsweise Trocknen des imprägnierten Latexschaumes.
The present invention relates to a process for producing a one-piece latex foam as described above, the process comprising the following steps:
  • a. Casting latex foam;
  • b. Vulcanizing the cast latex foam;
  • c. Impregnating the vulcanized latex foam with an additive, wherein the additive is applied in the form of a solution, emulsion or dispersion;
  • d. and preferably drying the impregnated latex foam.

Die Imprägnierung erfolgt vorzugsweise durch eine Sprühtechnik.The impregnation is preferably carried out by a spray technique.

Ein Verfahren zur Erzeugung von Latexschaum ist das Gießen des Latexschaumes auf ein Endlosförderband, gefolgt von Vulkanisieren, Waschen und abschließendem Trocknen.One method of producing latex foam is by casting the latex foam onto an endless belt followed by vulcanization, washing and final drying.

Ein zweites Merkmal der Erfindung wird durch eine Anlage zur Herstellung von Latexschaumprodukten mit unbegrenzter Länge dargestellt, die zur Bildung von Matratzen, Kissen und dergleichen vorgesehen sind. Die Anlage umfasst Gießmittel, wie etwa Gieß-, Sprühtechniken für Latexschaumstoff, der in einer ersten und zweiten und/oder nachfolgenden Gießstationen angeordnet wird, Mittel zum Legen des Latexschaumstoffes, die jeweils mit einer Legeebene vorausbestimmter Größe versehen sind oder via Förderband, eine oder mehrere Vulkanisationsstationen, Betriebsmittel für die Legemittel, Entfernungsmittel der vulkanisierten ersten Schicht, die in einer zweiten und/oder nachfolgenden Gießstation anzuordnen ist.A second feature of the invention is represented by an installation for the production of latex foam products of indefinite length intended for the formation of mattresses, cushions and the like. The plant comprises pouring means, such as casting, latex foam spraying techniques, placed in a first and second and / or subsequent casting stations, means for laying the latex foam, each provided with a laying plane of predetermined size or via conveyor belt, one or more Vulcanization stations, equipment for the laying means, vulcanized first layer removing means to be arranged in a second and / or subsequent casting station.

Alternativ dazu können dem Latexschaum der vorliegenden Erfindung unterschiedliche Schichten hinzugefügt werden, die abwechselnde Schichten, bestehend aus Latexschaum und Schaum, gewählt aus Polyolefin, Polyurethan, Polystyrol oder Polyester oder viskoelastischem Latex oder Mischungen davon, sind.Alternatively, various layers may be added to the latex foam of the present invention which are alternating layers consisting of latex foam and foam selected from polyolefin, polyurethane, polystyrene or polyester or viscoelastic latex or mixtures thereof.

Latexschaum verfügt von Natur aus über eine höhere unabhängige Stützeigenschaft als Schäume, wie etwa Polyurethan- oder Urethanschäume. Dieser Unterschied ist auf Unterschiede in der Zusammensetzung zwischen den Materialien zurückzuführen und wird wenigstens zum Teil in den typischen Lastverformungskurven für jeden Materialtyp widergespiegelt. Eine Lastverformungskurve ist normalerweise eine Kurve der Kraft in lbs, die notwendig ist, um eine flache Scheibe mit 50 Quadratzoll (8'' Durchmesser) in den Schaum oder sonstiges zu testendes Material für einen bestimmten Durchbiegungsprozentsatz hineinzudrücken.Latex foam inherently has a higher independent support property than foams, such as polyurethane or urethane foams. This difference is due to differences in the Due to the composition between the materials and is reflected at least in part in the typical load-deflection curves for each type of material. A load-deflection curve is typically a force-in-lbs curve necessary to force a 50-square inch (8 "diameter) flat disk into the foam or other material to be tested for a given percent deflection.

Latexschaum ist üblicherweise dadurch gekennzeichnet, dass er einen eher allmählichen Anstieg im unteren Teil der Kurve aufweist, nämlich in einem Bereich von 5–10%, der normalerweise im oberen Teil der Kurve steiler wird, nämlich in einem Bereich von 50–70%.Latex foam is usually characterized as having a more gradual increase in the lower part of the curve, namely in a range of 5-10%, which normally steepens in the upper part of the curve, namely in a range of 50-70%.

Erfindungsgemäße Schäume können Perforationen aufweisen. Kombinationen von Perforationen unterschiedlicher Größen können ebenfalls angewendet werden. Die Größen der Perforationen betragen zwischen 0,5 und 2 cm. Die Perforationen, in Kombination mit dem erfindungsgemäßen Verbundschaum, verschaffen dem Benutzer des Verbundschaumes einen höheren Komfortgrad. Erfindungsgemäße Schäume können Profile aufweisen. In Kombination mit den erfindungsgemäßen Verbundschäumen verbessern die Profile, die in bestimmten Zonen auf der Oberseite der oberen Schicht des Verbundschaumes vorhanden sind, den Schlafkomfort des Benutzers, weil sich das Bettprodukt, wenn es mit dem erfindungsgemäßen Verbundschaum gestaltet ist, in diesen Zonen weicher anfühlt, je nach Form und Abmessungen der Profile.Foams of the invention may have perforations. Combinations of perforations of different sizes can also be used. The sizes of the perforations are between 0.5 and 2 cm. The perforations, in combination with the composite foam according to the invention, give the user of the composite foam a higher degree of comfort. Foams of the invention may have profiles. In combination with the composite foams of the invention, the profiles present in certain zones on top of the top layer of the composite foam improve the sleeping comfort of the user, because the bed product, when designed with the composite foam of the invention, feels softer in these zones, depending on the shape and dimensions of the profiles.

Der erfindungsgemäße Schaum kann ebenfalls mit weiteren Schichten zusätzlich zum Latexschaum verbunden werden. Unterschiedliche Schichten können hinzugefügt werden, die abwechselnde Schichten aus Latexschaum und Schaum sind, der gewählt wird aus Polyolefin, Polyurethan, Polystyrol oder Polyester oder viskoelastischem Latex oder Mischungen daraus.The foam according to the invention can likewise be combined with further layers in addition to the latex foam. Different layers may be added, which are alternating layers of latex foam and foam selected from polyolefin, polyurethane, polystyrene or polyester or viscoelastic latex or blends thereof.

Beispiel 1 (A bis F):Example 1 (A to F):

Eine flüssige Latexschaumschicht wird hergestellt. Das Latexschaumgemisch kann aus natürlichem Latex oder synthetischem Latex, wie Intex 2720 oder Intex 2731 (im Handel erhältlich bei Polimeri Europa), oder jedem sonstigen erhältlichen Schaumlatex oder Gemisch bestehen. Die Oberseite des Latexschaumes kann in unterschiedlichen Zonen während des Härtungsverfahrens des Latexschaumes mit Profilen versehen werden. Der Schaum absolviert das gesamte Verfahren auf der kontinuierlichen Produktionsanlage in den verschiedenen Schritten: Vorwärmen, Vulkanisieren, Waschen, Pressen, Trocknen. Vor dem Trocknungsschritt wird die Schaumschicht (auf der Oberseite, der Unterseite und/oder den Seitenflächen und Kombinationen davon) mit einem oder mehreren Zusatzstoffen imprägniert, die gewählt werden aus (A) PCM, wie etwa Mikrathermic G Soft (beladen mit 50–450 g/m2); Mikracat B; Mikra EF; Mikrafix; (B) Farbstoffen, wie etwa Helizarin® blau RT (Konzentration 1 g/1000 l bis 100 g/1000 l); (C) Duftstoff; (D) feuerhemmendem Mittel, wie etwa Finifire Pro® (beladen mit 600 g/m2); (E) Antipilzmittel; (F) Bakteriziden.A liquid latex foam layer is produced. The latex foam mixture may consist of natural latex or synthetic latex, such as Intex 2720 or Intex 2731 (commercially available from Polimeri Europa), or any other available foam latex or blend. The top of the latex foam may be profiled in different zones during the curing process of the latex foam. The foam completes the entire process on the continuous production line in the various steps: preheating, vulcanization, washing, pressing, drying. Prior to the drying step, the foam layer (on top, bottom and / or side surfaces and combinations thereof) is impregnated with one or more additives selected from (A) PCM such as Mikrathermic G Soft (loaded at 50-450 g / m 2 ); Mikracat B; Mikra EF; Mikrafix; (B) dyes, such as Helizarin Blue ® RT (concentration 1 g / 1000 l to 100 g / 1000 l); (C) fragrance; (D) fire retardant, such as Finifire Pro ® (loaded with 600 g / m 2); (E) antifungal agents; (F) Bactericides.

Schließlich wird das Schaumprodukt (Matratzenauflage) in die richtige Länge und Breite geschnitten und kann in Platten oder Rollen gefertigt werden. Der Schaum zeigt eine ausgezeichnete Leistung der Zusatzstoffe, während die Schaumeigenschaften nicht nachteilig beeinflusst werden und die Gleichmäßigkeit der Zellstruktur des Schaumes aufrechterhalten bleibt (REM-Analyse).Finally, the foam product (mattress overlay) is cut to the correct length and width and can be made into sheets or rolls. The foam exhibits excellent performance of the additives while not adversely affecting the foam properties and maintaining the uniformity of the cell structure of the foam (SEM analysis).

Der erfindungsgemäße Schaum kann in zahlreichen anderen Anwendungen verwendet werden. Hauptanwendungsbereich ist die Bettproduktindustrie.The foam of the invention can be used in numerous other applications. Main application area is the bed product industry.

Man wird verstehen, dass jede spezifische Anwendung ihre eigenen Ansprüche an die zu verwendenden Bettprodukte stellt. Wichtige Eigenschaften in diesem Zusammenhang sind Dichte, Härte, Rückstellvermögen und Dämpfungsverhalten des Bettproduktes und um für jede Anwendung geeignet zu sein, sollten diese Eigenschaften optimal ausgewogen und angepasst sein.It will be understood that each specific application makes its own demands on the bed products to be used. Important properties in this context are the density, hardness, resilience and damping behavior of the bed product and in order to be suitable for every application, these properties should be optimally balanced and adapted.

Der vorliegende Latexschaum verfügt über ein antibakterielles/geruchsbekämpfendes Merkmal, was bei Anwendungen in Sportausrüstungen, Möbeln und Matratzenschonern vorteilhaft ist; und die vorliegenden Schäume verfügen über eine im Wesentlichen wasserundurchlässige Oberfläche, was sehr nützlich sein kann, zum Beispiel in Produkten, wo Inkontinenz ein Problem ist (zum Beispiel Matratzenschoner, Rollstuhlkissen und dergleichen).The present latex foam has an antibacterial / odor control feature, which is beneficial in sports equipment, furniture and mattress protector applications; and the present foams have a substantially water-impermeable surface, which may be very useful, for example, in products where incontinence is a problem (e.g., mattress protectors, wheelchair cushions, and the like).

Weitere geeignete Anwendungen sind solche, wo Wärmeenergieverwaltung erforderlich ist. Ferner kann der erfindungsgemäße Schaum organische und/oder anorganische Füllstoffe umfassen. Des Weiteren können weitere Zusatzstoffe in die Innenstruktur des Schaumes eingegliedert werden, wie etwa, aber nicht beschränkt auf feuerhemmende Mittel, Beschlagschutzmittel, Ultraviolettabsorber, Wärmestabilisatoren, Pigmente, Farbstoffe, Geruchskontrollstoffe und dergleichen.Other suitable applications are those where thermal energy management is required. Furthermore, the foam according to the invention may comprise organic and / or inorganic fillers. Further, other additives can be incorporated into the interior structure of the foam, such as, but not limited to, fire retardants, antifoggants, ultraviolet absorbers, heat stabilizers, pigments, dyes, odor control agents, and the like.

In einer weiteren Ausführungsform der vorliegenden Erfindung kann eine kundenspezifische Anpassung des Schaumes für seine Verwendung als Bettprodukt von einem potenziellen Benutzer durchgeführt werden, der einen Fragebogen ausfüllt, um die Analyse des „Schlaffunktionalitäten”-Profils dieses Benutzers zu unterstützen. Das Schlafkomfortprofil bewertet Funktionalitäten wie die Vorliebe des Benutzers für Funktionalitäten, wie etwa Intensität und Auswahl von aktiven Wirkstoffen, umfassend Duft, Lotionen und dergleichen. Eine Festigkeitsempfehlung wird berechnet, entweder in Form eines Drucks für unterschiedliche Zonen einer „Testmatratze”, die eine Luftblase enthält, oder in Form einer Schaumart und -dichte für jede Zone. Darüber hinaus wird eine Oberflächenempfehlung basierend auf den Antworten des Benutzers auf einen Oberflächenempfehlungsfragebogen erstellt und die Schäume der vorliegenden Erfindung werden dann gemäß den Verbraucherbedürfnissen zugeschnitten.In another embodiment of the present invention, customization of the foam for its use as a bed product may be performed by a prospective user filling out a questionnaire to analyze the "sleep functionalities" profile to support this user. The sleep comfort profile evaluates functionalities such as the user's preference for functionalities, such as intensity and selection of active agents, including fragrance, lotions, and the like. A strength recommendation is calculated, either in the form of a pressure for different zones of a "test mattress" containing an air bubble, or in the form of a foam type and density for each zone. In addition, a surface recommendation is made based on the user's responses to a surface recommendation questionnaire, and the foams of the present invention are then tailored according to consumer needs.

In einer weiteren Ausführungsform kann die erste Schicht als eine Seitenfläche der Matratze oder Matratzenauflage definiert sein, das heißt, die Seiten senkrecht zur Stützfläche der Matratze. Gemäß der vorliegenden Erfindung können sowohl die vier Seitenflächen und/oder die Oberseite und/oder Unterseite der Matratze oder Matratzenauflage mit einem Zusatzstoff imprägniert sein.In another embodiment, the first layer may be defined as a side surface of the mattress or mattress overlay, that is, the sides perpendicular to the support surface of the mattress. According to the present invention, both the four side surfaces and / or the top and / or bottom of the mattress or mattress pad may be impregnated with an additive.

In einer bevorzugten Ausführungsform, in der der Kern des Schaumes im Wesentlichen zusatzstofffrei ist, versteht sich, dass mit Kern jener Teil der einstückigen Schaumstruktur definiert ist, der 9 mm von der äußeren Oberfläche der Schaumstruktur beabstandet ist, wenn senkrecht zur äußeren Oberfläche gemessen wird und wie in 1c mit Bezugszeichen 2 dargestellt ist.In a preferred embodiment, in which the core of the foam is substantially additive-free, it will be understood that the core defines that portion of the one-piece foam structure which is 9 mm from the outer surface of the foam structure when measured perpendicular to the outer surface as in 1c with reference number 2 is shown.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • US 2009/0288259 [0007] US 2009/0288259 [0007]
  • WO 01/06054 [0056] WO 01/06054 [0056]
  • WO 01/62376 [0056] WO 01/62376 [0056]
  • US 2002/055560 [0056] US 2002/055560 [0056]
  • WO 2006/013165 [0056] WO 2006/013165 [0056]
  • WO 2006/117702 [0056] WO 2006/117702 [0056]

Claims (13)

Einstückiger Latexschaum, umfassend eine erste Schicht aus Latexschaum und eine zweite und/oder nachfolgende Schicht aus Latexschaum, dadurch gekennzeichnet, dass die erste Schicht einen Zusatzstoff enthält, der in Form einer Lösung, Emulsion oder Dispersion aufgebracht wird und wobei die erste Schicht eine Dicke von 0,01 bis 9 mm aufweist.One-part latex foam comprising a first layer of latex foam and a second and / or subsequent layer of latex foam, characterized in that the first layer contains an additive which is applied in the form of a solution, emulsion or dispersion and wherein the first layer has a thickness of 0.01 to 9 mm. Einstückiger Latexschaum nach Anspruch 1, wobei der Latexschaum mit dem Zusatzstoff imprägniert ist.A one-piece latex foam according to claim 1, wherein the latex foam is impregnated with the additive. Einstückiger Latexschaum nach Anspruch 1, wobei der Kern des Schaumes im Wesentlichen frei von dem Zusatzstoff ist.The one-piece latex foam of claim 1, wherein the core of the foam is substantially free of the additive. Einstückiger Latexschaum nach Anspruch 1, umfassend eine dritte Schicht mit einem Zusatzstoff, wobei der Zusatzstoff in Form einer Lösung, Emulsion oder Dispersion aufgebracht wird und wobei die dritte Schicht eine Dicke von 0,01 bis 9 mm aufweist.A one-part latex foam according to claim 1, comprising a third layer with an additive, wherein the additive is applied in the form of a solution, emulsion or dispersion and wherein the third layer has a thickness of 0.01 to 9 mm. Einstückiger Latexschaum nach Anspruch 1, wobei der Zusatzstoff aus der Gruppe gewählt ist, bestehend aus i) Latentwärmespeichermaterial, ii) feuerhemmendem Mittel, iii) einem antibakteriellen aktiven Wirkstoff, iv) einem Antipilzmittel und Kombinationen, die wenigstens eines der Vorhergehenden umfassen.A one-piece latex foam according to claim 1, wherein the additive is selected from the group consisting of i) latent heat storage material, ii) fire retardant, iii) an antibacterial active ingredient, iv) an antifungal agent, and combinations comprising at least one of the foregoing. Einstückiger Latexschaum nach Anspruch 1, wobei der Zusatzstoff ein Latentwärmespeichermaterial ist.A one-piece latex foam according to claim 1, wherein the additive is a latent heat storage material. Einstückiger Latexschaum nach einem der vorhergehenden Ansprüche, wobei die erste Schicht und/oder dritte Schicht farbig sind.One-piece latex foam according to one of the preceding claims, wherein the first layer and / or third layer are colored. Einstückiger Latexschaum nach Anspruch 1, wobei die Imprägnierung durch eine Sprühtechnik erfolgt.One-piece latex foam according to claim 1, wherein the impregnation is effected by a spraying technique. Bettprodukt, umfassend einen Latexschaum nach Anspruch 1.Bed product comprising a latex foam according to claim 1. Bettprodukt nach Anspruch 9, wobei das Produkt eine Matratzenauflage ist.The bedding product of claim 9, wherein the product is a mattress overlay. Matratzenauflage nach Anspruch 10, wobei die Auflage eine Dicke von 2 bis 20 cm aufweist.A mattress overlay according to claim 10, wherein the overlay has a thickness of 2 to 20 cm. Teileset eines Latexschaumes und Aufbringungsset, umfassend eine Lösung, Emulsion oder Dispersion eines Zusatzstoffes, der auf einer Oberfläche der Schaumschicht aufzubringen ist.A set of latex foam and application kit comprising a solution, emulsion or dispersion of an additive to be applied to a surface of the foam layer. Teileset nach Anspruch 12, wobei der Zusatzstoff aus der Gruppe gewählt ist, bestehend aus i) Latentwärmespeichermaterial, ii) feuerhemmendem Mittel, iii) einem antibakteriellen aktiven Wirkstoff, iv) einem Antipilzmittel, v) einem Duftstoff und Kombinationen, die wenigstens eines der Vorhergehenden umfassen.The kit of claims 12, wherein the additive is selected from the group consisting of i) latent heat storage material, ii) fire retardant, iii) an antibacterial active, iv) an antifungal agent, v) perfume, and combinations comprising at least one of the foregoing ,
DE201120110323 2010-09-07 2011-09-07 Functionalized latex-based foam Expired - Lifetime DE202011110323U1 (en)