DE202011110262U1 - Textile structure surface - Google Patents

Textile structure surface Download PDF

Info

Publication number
DE202011110262U1
DE202011110262U1 DE202011110262U DE202011110262U DE202011110262U1 DE 202011110262 U1 DE202011110262 U1 DE 202011110262U1 DE 202011110262 U DE202011110262 U DE 202011110262U DE 202011110262 U DE202011110262 U DE 202011110262U DE 202011110262 U1 DE202011110262 U1 DE 202011110262U1
Authority
DE
Germany
Prior art keywords
thread
knitted
special
textile
special thread
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE202011110262U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE202011110262U priority Critical patent/DE202011110262U1/en
Publication of DE202011110262U1 publication Critical patent/DE202011110262U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Textile Strukturfläche für Bekleidung, Bekleidungszubehör und Technische Textilien aus Gewebe, Gewirke, Gestrick oder Geflecht, gekennzeichnet dadurch, dass der Kett-, Schuss-, Strick- oder Flechtfaden ein Spezialfaden aus Natur-, Chemie- oder Anorganischen Faserstoffen ist, wobei der Spezialfaden einen viereckigen Querschnitt hat, die Fasern oder Filamente wirr bis quer zur Fadenlängsachse angeordnet sind, zwischen den Faser- oder Filamentteilen lokale Verbindungsstellen in Form von Klebpunkten aus faserstoffeigenen oder zusätzlich eingebrachten Polymer oder in Form von Verschlingungspunkten in Ausführung als Pfropfen, Knäuel oder Maschen sind und dass der Spezialfaden eine Feinheit von mindestens 200 tex aufweist.Textile structure surface for clothing, clothing accessories and technical textiles made of woven, knitted, knitted or woven fabric, characterized in that the warp, weft, knitted or braided thread is a special thread of natural, chemical or inorganic fibers, the special thread a quadrangular cross-section, the fibers or filaments are arranged confused to transverse to the longitudinal axis of the thread, between the fiber or filament parts local joints in the form of adhesive dots of fibper own or additionally introduced polymer or in the form of Verschlingungspunkten in execution as a plug, ball or mesh and that the special thread has a fineness of at least 200 tex.

Description

Die Erfindung betrifft eine textile Strukturfläche, wobei die textile Strukturfläche ein Fadenstoff, wie Gewebe, Gewirke, Gestrick oder Geflecht ist und für Oberbekleidung, Wäsche, Täschnerwaren oder für technische Anwendungen, wie als Sport-, Bau-, Mobil-, Schutz-, Medizintextil o. ä. eingesetzt wird.The invention relates to a textile structure surface, wherein the textile structure surface is a thread material, such as woven, knitted fabric or knit fabric and for outerwear, linen, Täschnerwaren or for technical applications, such as sports, construction, mobile, protective, medical textile o. Ä. Is used.

Die Herstellung von Fadenstoff, wie Gewebe, Gewirke, Gestrick oder Geflecht und der Einsatz solcher Fadenstoffe für Oberbekleidung, Wäsche, Täschnerwaren oder für technische Anwendungen ist bekannt. Als Fäden für die Herstellung dieser Fadenstoffe finden vorwiegend Faser- oder Filamentgarne Einsatz. Diese Faser- oder Filamentgarne sind gekennzeichnet durch parallel zur Fadenlängsachse angeordnete Fasern oder Filamente, die umeinander für den Faden festigkeitsgebend verdreht sind, sie weisen einen kreisrunden Querschnitt auf mit den in diesem Querschnitt angeordneten Fasern oder Filamenten. Ein Faden aus einem Filament wird als Monofilamentgarn bezeichnet, ein solcher aus vielen Filamenten wird als Multifilamentgarn benannt. Diese Fäden sind im Fadenstoff für die Festigkeit, die Oberflächenstruktur, die Oberflächenbeständigkeit und für die Optik und Haptik verantwortlich. Vorteile der Fadenstoffe allgemein sind die hohen Festigkeits- und Abriebseigenschaften, die vielfältigen Mustermöglichkeiten und der Einsatz von hinsichtlich Farbe, Feinheit, Festigkeit, Faserstoffzusammensetzung sehr variablen Fadenmaterial.The production of yarn material, such as woven, knitted, knitted or braided and the use of such thread materials for outerwear, laundry, bagging or technical applications is known. As threads for the production of these yarn materials are mainly fiber or filament yarn use. These fiber or filament yarns are characterized by fibers or filaments arranged parallel to the yarn longitudinal axis, which are twisted around each other in terms of strength for the yarn, they have a circular cross section with the fibers or filaments arranged in this cross section. A filament yarn is referred to as a monofilament yarn, and a filament yarn is named multifilament yarn. These threads are responsible in the thread material for the strength, the surface structure, the surface resistance and for the look and feel. Advantages of the yarn materials in general are the high strength and abrasion properties, the diverse pattern possibilities and the use of very variable thread material in terms of color, fineness, strength, fiber composition.

Es ist weiterhin bekannt, für den Einsatz in Oberbekleidung, Wäsche, Täschnerwaren oder für technische Anwendungen als Technisches Textil Vliesstoffe zu verwenden. Die Vliesstoffe sind textile Flächengebilde, die unter Umgehung des Fadenherstellungsprozesses direkt durch flächige Ablage von Fasern oder Filamenten zum Vlies und anschließenden mechanischem, chemischen oder thermischen Verfestigen dieses Vlieses entstehen.It is also known to use nonwovens for use in outerwear, underwear, bagging or for technical applications as a technical textile. The nonwovens are textile fabrics which, circumventing the yarn production process, are produced directly by laminar deposition of fibers or filaments to the nonwoven and subsequent mechanical, chemical or thermal solidification of this nonwoven.

Bekannt sind seit langem viele Möglichkeiten, verfahrenstechnisch die Herstellungstechniken von Fadenstoffen und Vliesstoffen miteinander zu kombinieren, um textile Flächengebilde wirtschaftlich mit neuen Eigenschaften oder mit verbesserten Eigenschaften bezogen auf eine dieser beiden Stoffgruppen zu fertigen. Beispiele sind das Übernähen von Vliesstoffen im inne einer Festigkeitserhöhung, das Vernadeln von Fadenstoffen zur Ereichung einer dreidimensionalen Struktur und das lokale oder flächige Verkleben von Vliesstoffen mit Fadenstoffen.For a long time, many possibilities have been known for procedurally combining the production techniques of yarn materials and nonwovens to produce textile fabrics economically with new properties or with improved properties based on one of these two groups of substances. Examples are the over-stitching of nonwovens in the context of an increase in strength, the needling of thread materials to provide a three-dimensional structure and the local or surface bonding of nonwovens with filaments.

Auch der Einsatz von anderen Rohstoffaufmachungen statt Fasern oder Fäden zur Fertigung von textilen Flächengebilden ist bekannt. Sogenannte Florofol-Nähgewirke werden nach DD 84061 durch die flächige Vorlage einer Flachfolie zu einer speziellen Kettenwirkmaschine erhalten, wobei beim verfestigenden Übernähen der Folie mit Fäden die Folie durch die Wirkung der durchstechenden Schiebernadeln in Foliebändchen aufgesplittert wird. Es gibt auch Foliebändchengewebe, wobei eine Folie einer Webmaschine vorgelegt wird, die Folie wird zu schmalen Bändern geschnitten und diese werden als Kettfäden verwebt.The use of other raw material applications instead of fibers or threads for the production of textile fabrics is known. So-called Florofol-Nähgewirke become after DD 84061 obtained by the flat presentation of a flat film to a special warp knitting machine, wherein the film is splintered by the action of the piercing needles in Foliebändchen when consolidating over stitching the film with threads. There are also Foliebändchengewebe, wherein a film is presented to a loom, the film is cut into narrow bands and these are woven as warp threads.

Auch in DE 24 40 338 wird die Herstellung einer textilen Fläche aus Foliestreifen beschrieben. Folie als Fläche und Foliestreifen weisen in der daraus hergestellten textilen Fläche keine textilen Eigenschaften, wie Weichheit, Optik und Haptik auf.Also in DE 24 40 338 the production of a textile surface made of film strips is described. Film as a surface and film strips have no textile properties such as softness, appearance and feel in the textile surface produced therefrom.

In WO 03/002796 A1 werden Verfahren und Einrichtung zur Herstellung eines Fadens aus gering verfestigten Spinnvliesstreifen beschrieben. Diese Spinnvliesbändchen werden zum Zwecke der Herstellung eines zu textilen Flächen weiter verarbeitbaren Fadens verstreckt und stark verdreht. Dieser Faden hat durch die Festigkeitsverleihende starke Verdrehung einen runden Querschnitt und durch die hohe Verstreckung eine Fadenfeinheit von höchstens 100 tex und feiner. Mit solch einem Fadenmaterial kann keine textile Fläche mit grober Oberflächenstruktur hergestellt werden. Durch die relativ feine und runde Fadenstruktur sind auch keine funktionellen Eigenschaften im Sinne der Optik und Haptik erreichbar.In WO 03/002796 A1 describes a method and apparatus for producing a thread of low-strength spun-bonded nonwoven strip. These spunbonded tapes are stretched and strongly twisted for the purpose of producing a thread which can be further processed into textile surfaces. This thread has by the strength distribution end strong twist a round cross section and the high draw a yarn count of at most 100 tex and finer. With such a thread material, no textile surface with a coarse surface structure can be produced. Due to the relatively fine and round thread structure also no functional properties in the sense of appearance and feel can be achieved.

Im Sinne dieser Zielstellung wurde eine textile Fläche entwickelt, die die Struktur eines groben Fadenstoffes mit der wirtschaftlichen Herstellung von Vliesstoffen und deren Kombinationsmöglichkeiten von Rohstoff, Vliesbildung und Vliesverfestigung zu neuen Eigenschaftsmodifikationen miteinander verbindet.For the purposes of this aim, a textile surface has been developed which combines the structure of a coarse yarn material with the economic production of nonwovens and their combination possibilities of raw material, web formation and web consolidation to new property modifications.

Überraschenderweise wurde festgestellt, dass solche Eigenschaften eines textilen Flächengebildes wie zum Beispiel

  • – geringes Gewicht bei hoher Flächenbedeckung,
  • – grobe Oberflächenstruktur,
  • – hautangenehme Haptik,
  • – weicher Griff,
  • – gute Drapierfähigkeit,
  • – hohe Flexibilität,
  • – gute Verformbarkeit,
  • – kein Ausfasern bei Gebrauchs- und Reinigungsbeanspruchungen,
erreicht werden können, indem aus thermisch, chemisch oder mechanisch verfestigten Vliesstoff durch Schneiden desselben in Streifen daraus entstehende Spezialfäden verwebt, verstrickt, verwirkt oder verflochten werden.Surprisingly, it has been found that such properties of a textile fabric as, for example
  • - low weight with high area coverage,
  • - rough surface structure,
  • - skin-friendly feel,
  • - soft handle,
  • - good drape ability,
  • - high flexibility,
  • - good deformability,
  • - no fraying during use and cleaning stresses,
can be achieved by interweaving thermally, chemically or mechanically consolidated nonwoven fabric by cutting it into strips resulting from special threads, entangled, forfeited or interwoven.

Aufbauend auf die DE 10 2010 031 049.2 , wo Gewebestreifen aus Polyethylen hoher Dichte zu einer textilen Fläche verstrickt werden, werden für die erfindungsgemäße textile Strukturfläche Spezialfäden verarbeitet, die folgende Konstruktion und Struktur und daraus resultierende Eigenschaften aufweisen:

  • 1.; Der Spezialfaden kann aus allen zur Vliesstoffherstellung einsetzbaren Faserstoffen, wie Natur-, Chemie- oder Anorganischen Faserstoffen bestehen.
  • 2.: Der Spezialfaden hat einen viereckigen Querschnitt, wobei größenmäßig eine Seite durch die Dicke des Vliesstoffes und die andere Seite durch die Schnittbreite, mit der der Vliesstoff in Streifen geschnitten wird, bestimmt werden.
  • 3.: Der Spezialfaden hat eine große Querschnittsfläche und damit eine hohe Feinheit, bestimmt durch die Flächenmasse des Vliesstoffes, aus dem der Spezialfaden durch Schneiden hergestellt ist und der Schnittbreite.
  • 4.: Im Spezialfaden sind die Fasern oder Filamente, ausgehend vom Vliesbildungsprinzip des als Ausgangsmaterial dienenden Vliesstoffes, quer bis wirr zur Fadenlängsachse angeordnet. Diese Anordnung verleiht dem Spezialfaden eine druckelastische, voluminöse, hohlraumreiche Struktur.
  • 5.: Zwischen den Fasern oder Filamenten des Vliesstoffes und damit auch des daraus hergestellten Spezialfadens sind lokale Verbindungsstellen angeordnet, die dem Spezialfaden hohe Festigkeit und hohe Widerstandskraft gegen Scheuer- und Reibbeanspruchungen verleihen und auch verhindern, das bei Verarbeitung zur textilen Strukturfläche und deren gebrauch Faser- oder Filamentteile aus der Oberfläche des Spezialfadens heraustreten. Diese lokalen Verbindungsstellen zwischen benachbarten Fasern oder Filamenten sind abhängig vom Vliesstoffverfestigungsprinzip und haben folgende Bezeichnung und Struktur:

– Klebstelle: An den Berührungsstellen von Faser- oder Filamentteilen verbindend wirkende Klebefläche aus dem faserstoffeigenen Polymer, aus bei der Vliesbildung zugemischten thermoplastischen Bindefasern bei der thermischen Vliesstoffverfestigung oder aus zusätzlichen Klebstoffen bei der chemischen Vliesstoffverfestigung.
– Faserpfropfen: Partielle Faserbündelung in vertikaler Vliesstoffebene durch Vernadelung zum Nadel-Vliesstoff entstanden, damit streng quer zur Fadenlängsachse angeordnete Faserbündel.
– Fasermasche: Partielle Faserbündelung und horizontale Umformung zur Masche beim Vermaschen zum Nähwirk-Vliesstoff Malivlies, Kunit oder Multiknit entstanden, damit diagonal bis quer zur Fadenlängsachse angeordnete Faserbündelung.
– Faserknäuel: Partielle Faserzusammenballung mit horizontaler und vertikaler Anordnung als Knäuel im Vliesstoffquerschnitt beim Wasserstrahlverfestigen zum Vliesstoff entstanden, damit diagonal, längs und quer zur Fadenlängsachse angeordnete Faserbündelung.Building on the DE 10 2010 031 049.2 where fabric strips of high density polyethylene too are entangled a textile surface, special threads are processed for the textile structure surface according to the invention, which have the following construction and structure and resulting properties:
  • 1.; The special thread can consist of all fibrous materials that can be used for nonwoven fabric production, such as natural, chemical or inorganic fibers.
  • 2: The special thread has a quadrangular cross-section, wherein one side in size by the thickness of the nonwoven fabric and the other side by the cutting width, with which the nonwoven fabric is cut into strips, determined.
  • 3 .: The special thread has a large cross-sectional area and thus a high fineness, determined by the basis weight of the nonwoven fabric from which the special thread is made by cutting and the cutting width.
  • 4 .: In the special thread, the fibers or filaments, starting from the web-forming principle of the nonwoven fabric serving as starting material, are arranged transversely to the yarn longitudinal axis. This arrangement gives the special thread a pressure-elastic, voluminous, cavity-rich structure.
  • 5: Between the fibers or filaments of the nonwoven fabric and thus the special thread made therefrom local joints are arranged, which give the special thread high strength and high resistance to scuffing and rubbing stresses and also prevent the processing of the textile structure surface and their use fiber - or filament parts emerge from the surface of the special thread. These local joints between adjacent fibers or filaments are dependent on the nonwoven bonding principle and have the following designation and structure:

Adhesive point: Adhesive surface of the fiber-owning polymer which binds at the points of contact of fiber or filament parts, of thermoplastic binder fibers admixed during web formation during thermal nonwoven consolidation or of additional adhesives in chemical nonwoven bonding.
- Faserpfropfen: Partial fiber bundling in vertical nonwoven fabric level by needling to needle-nonwoven fabric, thus strictly transverse to the yarn longitudinal axis arranged fiber bundles.
- Fiber mesh: Partial fiber bundling and horizontal forming into a mesh during meshing with the stitchbonded nonwoven fabric Malivlies, Kunit or Multiknit, thus fiber bundling arranged diagonally to transversely to the longitudinal axis of the thread.
- fiberballs: Partial Faserzusammenbaubung with horizontal and vertical arrangement as a ball in the nonwoven cross-section during hydroentanglement to the nonwoven fabric, thus diagonal, longitudinal and transverse to the longitudinal axis of the fiber arranged fiber bundling.

Der Begriff der textilen Strukturfläche kennzeichnet die Erscheinung der erfindungsgemäßen Fläche, die durch die hohe Feinheit des verarbeiteten Spezialfadens bei geringer Faden- und Maschendichte eine hohe Flächenmasse und grobe Oberfläche hat.The term of the textile structure surface characterizes the appearance of the surface according to the invention, which has a high basis weight and rough surface due to the high fineness of the processed special thread with low thread and mesh density.

Die Feinheit von Fäden wird allgemein in tex angegeben und bezeichnet die Masse in g, die ein Faden der Länge von 1000 m hat. Hohe tex-Werte bedeuten grobe Fäden und geringe tex-Werte feine Fäden. Allgemein haben Fäden aus Chemiefaserstoffen bei der Verarbeitung zu Oberbekleidungsstoffen eine Feinheit zwischen 17 und 100 tex.The fineness of threads is generally indicated in tex and denotes the mass in g, which has a thread of the length of 1000 m. High tex values mean coarse threads and low tex values mean fine threads. In general, threads made of man-made fibers have a fineness of between 17 and 100 tex when being processed into outerwear fabrics.

Die Feinheit des erfindungsgemäßen Spezialfadens errechnet sich nach der Beziehung T(SF) = M(V) × B(SF) × 10, wobei sind
T(SF) = Feinheit des Spezialfadens in tex, M(V) = Flächenmasse des Vliesstoffes in g/m2; B(SF) = Schnittbreite, mit der der Vliesstoff streifenförmig geschnitten wird, in cm.The fineness of the special thread according to the invention is calculated according to the relationship T (SF) = M (V) × B (SF) × 10, where are
T (SF) = fineness of the special thread in tex, M (V) = basis weight of the nonwoven fabric in g / m 2 ; B (SF) = cutting width at which the nonwoven fabric is cut in strips, in cm.

Die Fertigung der erfindungsgemäßen textilen Strukturfläche mit der charakteristischen Oberflächenstruktur einschließlich spezieller Optik und Haptik umfasst allgemein folgende 3 Stufen:

  • 1. Auswahl eines Faser- oder Filamentvliesstoffes aus Natur-, Chemie- oder Anorganischen Faserstoffen mit zwischen den Faser- oder Filamentteilen angeordneten lokalen Verbindungsstellen in Form von Klebpunkten aus faserstoffeigenen oder zusätzlich eingebrachten Polymer oder mit zwischen Fasern oder Filamenten angeordneten Verschlingungen derselben in Form von Pfropfen, Knäuel oder Maschen sowie in spezieller Flächenmasse und Dicke;
  • 2. Herstellen des Spezialfadens durch Längsschneiden des Vliesstoffes in spezieller Breite als Einzel- oder Mehrfachschnitt und Aufwicklung des oder der Spezialfäden;
  • 3. Verarbeitung des Spezialfadens oder der Spezialfäden als Kett- und Schußfaden zum Gewebe, als Kett- und Maschenfaden zum Gewirke, als Strickfaden zum Gestrick und als Flechtfaden zum Geflecht mit spezieller Faden-, Maschendichte und Bindung.
The production of the textile structural surface according to the invention with the characteristic surface structure including special optics and haptics generally comprises the following 3 stages:
  • 1. Selection of a fiber or filament nonwoven fabric from natural, chemical or inorganic fibers with arranged between the fiber or filament parts local joints in the form of adhesive dots of fibrous own or additionally introduced polymer or arranged between fibers or filaments entanglements thereof in the form of plugs , Balls or loops and in special basis weight and thickness;
  • 2. Production of the special thread by longitudinal cutting of the nonwoven fabric in a specific width as a single or multiple cut and winding of the special thread or threads;
  • 3. Processing of special thread or special threads as a warp and weft thread to the fabric, as a warp and knitted thread to the knitted fabric, as a knitting thread to the knit and as a braiding thread to the braid with special thread, stitch density and binding.

Erfindungsgemäss wird die Aufgabe der umfassenden Struktur- und Anforderungserfüllung an eine textile Strukturfläche durch die in Anspruch 1 aufgezeigten Merkmale gelöst. Vorteilhafte Ausführungen sind in den Unteransprüchen enthalten.According to the invention, the object of comprehensive structural and requirements fulfillment of a textile structural surface is achieved by the features indicated in claim 1. Advantageous embodiments are contained in the subclaims.

Der Vorteil der Erfindung ist darin zu sehen, dass in einer an sich bekannten textilen Flächengebildekonstruktion wie Gewebe, Gewirke, Gestrick oder Geflecht durch den Einsatz eines neuartigen Spezialfadens eine neuartige Oberflächenstruktur mit speziellen optischen und haptischen Effekten und neuen Funktionseigenschaften erreicht wird. Solche Effekte können sein Leichtheit der Fläche mit hohem Auftriebseffekt im Wasser oder in anderen Flüssigkeiten, angenehmes Hautempfinden in Form einer Verringerung der Hautempfindlichkeit z. B. im Vergleich zu Wolle, Beständigkeit gegen Besiedelung mit Keimen, Mikroorganismen, Algen, hohe Druckelastizität, hohe Abriebfestigkeit, gutes Drapierverhalten. The advantage of the invention is the fact that a novel surface structure with special optical and haptic effects and new functional properties is achieved in a known textile fabric structure such as fabric, knitted fabric or knitted fabric by the use of a novel special thread. Such effects may be lightness of the surface with high buoyancy effect in the water or in other liquids, pleasant skin sensation in the form of a reduction of the skin sensitivity z. B. compared to wool, resistance to colonization with germs, microorganisms, algae, high compressive elasticity, high abrasion resistance, good drape behavior.

Hinzu kommen durch die erfindungsgemäße Flächenkonstruktion hohe Beständigkeiten derselben gegen intensive Verarbeitungs-, Gebrauchs- oder Reinigungsbeanspruchungen.In addition, by the surface construction according to the invention high resistances of the same against intensive processing, service or cleaning stresses.

Im folgenden wird die Erfindung anhand von 2 Ausführungsbeispielen kurz beschrieben.In the following the invention will be briefly described with reference to 2 embodiments.

Im 1. Ausführungsbeispiel wird als Ausgangsmaterial für den Spezialfaden ein thermisch verfestigter Filamentvliesstoff aus 100% Polyethylen mit einer Flächenmasse von 40 g/m2 und einer Dicke von 0,3 mm verwendet. Aus diesem Vliesstoff wird durch Einzelschnitt mit einer Schnittbreite von 6 mm ein Spezialfaden mit einer Querschnittsfläche von 0,3 × 6 mm und einer Fadenfeinheit von 240 tex erhalten. Dieser Spezialfaden wird auf einen Fadenträger, wie einer Hülse, aufgewickelt. Der Spezialfaden wird nachfolgend mit leichter Drehungserteilung für den Faden im Bereich von 20 Drehungen je m Fadenlänge auf einer Strickmaschine zur textilen Strukturfläche verstrickt, wobei in Querrichtung 2 Maschen je cm und in Längsrichtung 3 Maschen je cm sind. Es entsteht eine erfindungsgemäße textile Strukturfläche mit einer Flächenmasse von 600 g/m2 und einer je m2 enthaltenen Länge des Spezialfadens von 2500 m.In the first embodiment, a thermally bonded filament nonwoven made of 100% polyethylene having a basis weight of 40 g / m 2 and a thickness of 0.3 mm is used as the starting material for the special thread. From this nonwoven fabric is obtained by a single cut with a cutting width of 6 mm, a special thread with a cross-sectional area of 0.3 × 6 mm and a thread count of 240 tex. This special thread is wound on a thread carrier, such as a sleeve. The special thread is subsequently entangled with a slight twist pitch for the thread in the range of 20 turns per m thread length on a knitting machine to the textile structure surface, in the transverse direction 2 stitches per cm and in the longitudinal direction 3 stitches per cm. The result is a textile structure surface according to the invention with a basis weight of 600 g / m 2 and a per m 2 contained length of the special thread of 2500 m.

Dieses grobe Gestrick wird für Oberbekleidungsgegenstände eingesetzt und weist als erfindungsgemäße textile Strukturfläche gegenüber vergleichbaren Gestricken aus Naturfasergarnen folgende Vorteile auf:

  • – geringes Gewicht,
  • – weiches und hautfreundliches Trageempfinden,
  • – Verbindungsnähte zur Konfektionierung eines Oberbekleidungsgegenstandes können unter Nutzung der thermoplastischen Eigenschaften des Faserstoffes Polyethylen durch Thermoschweißen hergestellt werden,
  • – durch den Rohstoff und die lokalen Klebepunkte des Spezialfadens gibt es kein Ausfasern, Ausfransen, Pillingbildung,
  • – atmungsaktive und dermatologisch unbedenkliche Oberfläche,
  • – einfache und wirtschaftliche Herstellung.
This coarse knit fabric is used for outerwear articles and, as a textile structural surface according to the invention, has the following advantages over comparable natural fiber yarn knits:
  • - low weight,
  • - soft and skin-friendly wearing sensation,
  • Connecting seams for finishing an outerwear article can be produced by thermal welding using the thermoplastic properties of the pulp polyethylene,
  • - there is no fraying, fraying, pilling, due to the raw material and the local sticking points of the special thread
  • - breathable and dermatologically harmless surface,
  • - simple and economical production.

Im 2. Ausführungsbeispiel wird als Ausgangsmaterial für den Spezialfaden ein thermisch verfestigter Faservliesstoff aus 100% Polypropylen mit einer Flächenmasse von 85 g/m2 und einer Dicke von 0,8 mm verwendet. Aus diesem Vliesstoff wird durch Einzelschnitt mit einer Schnittbreite von 12 mm ein Spezialfaden mit einer Querschnittsfläche von 0,8 × 12 mm und einer Fadenfeinheit von 1020 tex erhalten. Dieser Spezialfaden wird auf einen Fadenträger, wie einer Hülse, aufgewickelt. Der Spezialfaden wird nachfolgend auf einer Webmaschine zur textilen Strukturfläche verwebt. Die Bindung ist Leinwand 1/1 und die Fadendichte in Kette und Schuß je 10 Fäden/dm. Es entsteht eine erfindungsgemäße textile Strukturfläche mit einer Flächenmasse von 820 g/m2 und einer je m2 enthaltenen Länge des Spezialfadens von 804 m.In the second embodiment is used as starting material for the special thread, a thermally bonded nonwoven fabric made of 100% polypropylene with a basis weight of 85 g / m 2 and a thickness of 0.8 mm. From this nonwoven fabric is obtained by single cut with a cutting width of 12 mm, a special thread with a cross-sectional area of 0.8 × 12 mm and a thread count of 1020 tex. This special thread is wound on a thread carrier, such as a sleeve. The special thread is subsequently woven onto the textile structure surface on a weaving machine. The binding is canvas 1/1 and the thread density in warp and weft 10 threads / dm. The result is a textile structural surface according to the invention with a basis weight of 820 g / m 2 and per m 2 contained length of the special thread of 804 m.

Dieses grobe Gewebe wird für die oberflächliche Abdeckung von Badebecken, Pools u. ä. eingesetzt. Sie weist gegenüber vergleichbar eingesetzten beschichteten Polyestergeweben folgende Vorteile auf:

  • – um bis zu 300% geringeres Gewicht, durch dieses und die spezifische Faserstoffdichte um 0,9 g/cm3 liegt das Abdeckgewebe ohne zusätzliche Befestigung auf der Wasseroberfläche auf,
  • – luftdurchlässig, kein Bewuchs mit Keimen, Algen o. ä.,
  • – Verbindungsnähte zur Konfektionierung abgepasster Abdeckungen können unter Nutzung der thermoplastischen Eigenschaften des Faserstoffes Polyethylen durch Thermoschweißen hergestellt werden,
  • – durch den Rohstoff und die Klebpunkte des Spezialfadens gibt es kein Ausfasern, Ausfransen, Pillingbildung,
  • – einfache und wirtschaftliche Herstellung.
This coarse fabric is used for the superficial coverage of bathing pools, pools, etc. Ä. Used. It has the following advantages over similarly used coated polyester fabrics:
  • - By up to 300% lower weight, by this and the specific fiber density of 0.9 g / cm 3 , the cover fabric is without additional attachment to the water surface,
  • - permeable to air, no vegetation with germs, algae or similar,
  • Connecting seams for the manufacture of fitted covers can be produced by thermal welding using the thermoplastic properties of the pulp polyethylene,
  • - there is no fraying, fraying, pilling, due to the raw material and the glue points of the special thread
  • - simple and economical production.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • DD 84061 [0005] DD 84061 [0005]
  • DE 2440338 [0006] DE 2440338 [0006]
  • WO 03/002796 A1 [0007] WO 03/002796 Al [0007]
  • DE 102010031049 [0010] DE 102010031049 [0010]

Claims (3)

Textile Strukturfläche für Bekleidung, Bekleidungszubehör und Technische Textilien aus Gewebe, Gewirke, Gestrick oder Geflecht, gekennzeichnet dadurch, dass der Kett-, Schuss-, Strick- oder Flechtfaden ein Spezialfaden aus Natur-, Chemie- oder Anorganischen Faserstoffen ist, wobei der Spezialfaden einen viereckigen Querschnitt hat, die Fasern oder Filamente wirr bis quer zur Fadenlängsachse angeordnet sind, zwischen den Faser- oder Filamentteilen lokale Verbindungsstellen in Form von Klebpunkten aus faserstoffeigenen oder zusätzlich eingebrachten Polymer oder in Form von Verschlingungspunkten in Ausführung als Pfropfen, Knäuel oder Maschen sind und dass der Spezialfaden eine Feinheit von mindestens 200 tex aufweist.Textile structure surface for clothing, clothing accessories and technical textiles made of woven, knitted, knitted or woven fabric, characterized in that the warp, weft, knitted or braided thread is a special thread of natural, chemical or inorganic fibers, the special thread a quadrangular cross-section, the fibers or filaments are arranged confused to transverse to the longitudinal axis of the thread, between the fiber or filament parts local joints in the form of adhesive dots of fibper own or additionally introduced polymer or in the form of Verschlingungspunkten in execution as a plug, ball or mesh and that the special thread has a fineness of at least 200 tex. Textile Strukturfläche für Bekleidung, Bekleidungszubehör und Technische Textilien aus Gewebe, Gewirke, Gestrick oder Geflecht nach Anspruch 1, gekennzeichnet dadurch, dass die textile Strukturfläche eine Flächenmasse von mindestens 200 g/m2 aufweist und dass diese Fläche eine Länge an Spezialfaden von mindestens 1000 m je m2 enthält.Textile structural surface for clothing, clothing accessories and technical textiles made of woven, knitted, knitted or woven fabric according to claim 1, characterized in that the textile structural surface has a basis weight of at least 200 g / m 2 and that this surface has a length of special thread of at least 1000 m each contains m 2 . Textile Strukturfläche für Bekleidung, Bekleidungszubehör und Technische Textilien aus Gewebe, Gewirke, Gestrick oder Geflecht nach Anspruch 1 und 2, gekennzeichnet dadurch, dass die textile Strukturfläche neben dem Spezialfaden einen Effekt- oder Funktionsfaden mit einem Masseanteil von höchstens 20% enthält.Textile structural surface for clothing, clothing accessories and technical textiles made of woven, knitted, knitted or braided according to claim 1 and 2, characterized in that the textile structure surface in addition to the special thread contains an effect or functional thread with a mass fraction of at most 20%.
DE202011110262U 2010-07-07 2011-07-04 Textile structure surface Expired - Lifetime DE202011110262U1 (en)