DE202008003183U1 - leveling screed - Google Patents

leveling screed Download PDF

Info

Publication number
DE202008003183U1
DE202008003183U1 DE200820003183 DE202008003183U DE202008003183U1 DE 202008003183 U1 DE202008003183 U1 DE 202008003183U1 DE 200820003183 DE200820003183 DE 200820003183 DE 202008003183 U DE202008003183 U DE 202008003183U DE 202008003183 U1 DE202008003183 U1 DE 202008003183U1
Authority
DE
Germany
Prior art keywords
weight
screed according
leveling screed
leveling
screed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE200820003183
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BTF PRODUKTENTWICKLUNGS und VE
BTF PRODUKTENTWICKLUNGS- und VERTRIEBS-GMBH
Original Assignee
BTF PRODUKTENTWICKLUNGS und VE
BTF PRODUKTENTWICKLUNGS- und VERTRIEBS-GMBH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BTF PRODUKTENTWICKLUNGS und VE, BTF PRODUKTENTWICKLUNGS- und VERTRIEBS-GMBH filed Critical BTF PRODUKTENTWICKLUNGS und VE
Priority to DE200820003183 priority Critical patent/DE202008003183U1/en
Publication of DE202008003183U1 publication Critical patent/DE202008003183U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

Fließestrich, der bei normaler Zimmertemperatur aushärtet und der einen geringen Schwund aufweist. dadurch gekennzeichnet,
dass der Fließestrich folgende Zusammensetzung aufweist:
20–70 Gew-% Silikat,
≤ 30 Gew-% schweren Füllstoff,
≤ 30 Gew-% leichten Füllstoff,
10–70 Gew-% Bindemittel, und
10–60 Gew-% Wasser.Liquid screed, which cures at normal room temperature and has a low shrinkage. characterized,
the screed has the following composition:
20-70% by weight silicate,
≤ 30% by weight heavy filler,
≤ 30% by weight light filler,
10-70% by weight of binder, and
10-60% by weight of water.

Description

Die Erfindung betrifft einen Fließestrich, der bei normaler Zimmertemperatur aushärtet und der einen geringen Schwund aufweist.The Invention relates to a fluid screed, which cures at normal room temperature and a low Has loss.

Estriche können nach ihren Bindemitteln in Zement-, Gussasphalt-, Kunstharz-, Calciumsulfat-, Magnesit- und Fließestriche unterschieden werden. Bei den Fließestrichen handelt es sich um eine Sonderform des Gipsestrichs.screeds can according to their binders in cement, mastic asphalt, synthetic resin, calcium sulphate, magnesite and flow marks be differentiated. The flow screeds are a special form of plaster screed.

Bei den handelsüblichen Estrichen wird auch zwischen Trocken- und Naßestrichen unterschieden. Die Eigenschaften der handelsüblichen Estriche sind jeweils auf bestimmte Anwendungs- bzw. Einsatz-Anforderungen zugeschnitten. So sind bspw. Kunstharzestriche dynamisch hoch belastbar. Anhydridestriche besitzen einen geringen Schwund, so dass sie für relativ große Flächen verwendbar sind. Faserestriche besitzen eine hohe Biegzugfestigkeit. Verbundestriche dienen zur Verbindung mit Rohbeton o. dgl.at the commercial Screeds are also differentiated between dry and wet screeds. The Properties of the commercial Screeds are each tailored to specific application or application requirements. For example, synthetic resin screeds are dynamically highly loadable. Anhydridestriche have a low shrinkage, so they can be used for relatively large areas are. Fiber screeds have a high bending tensile strength. Bonded screeds serve for connection with raw concrete or the like

Der Erfindung liegt die Aufgabe zugrunde, einen Fließestrich der eingangs genannten Art zu schaffen, der – ähnlich wie ein bekannter Anhydridestrich – bei einem guten Fließverhalten einen geringen Schwund besitzt, und der außerdem gute Wärmedämmungseigenschaften und gute Schalldämmungseigenschaften aufweist.Of the Invention is based on the object, a floating screed of the aforementioned To create a kind of - much like a known Anhydridestrich - at a good flow behavior has a low shrinkage, and also good thermal insulation properties and good soundproofing properties having.

Diese Aufgabe wird erfindungsgemäß durch die Merkmale des Anspruches 1, d. h. dadurch gelöst, dass der Fließestrich folgende Zusammensetzung aufweist:
20–70 Gew-% Silikat,
≤ 30 Gew-% schweren Füllstoff,
≤ 30 Gew-% leichten Füllstoff,
10–70 Gew-% Bindemittel, und
10–60 Gew-% Wasser.This object is achieved by the features of claim 1, ie, characterized in that the liquid screed has the following composition:
20-70% by weight silicate,
≤ 30% by weight heavy filler,
≤ 30% by weight light filler,
10-70% by weight of binder, and
10-60% by weight of water.

Der erfindungsgemäße Fließestrich mit einem Anteil von 20 bis 70 Gew-% Silikat weist den Vorteil auf, dass er nicht an einem Verarbeitungs-Werkzeug hängen bleibt, was unter Verarbeitungsgesichtspunkten vorteilhaft ist, und dass er sich homogen verteilt.Of the Flooring according to the invention containing from 20 to 70% by weight of silicate has the advantage that he does not get stuck on a processing tool, which is processing-wise is advantageous, and that it is distributed homogeneously.

Um eine ungewollte bzw. unerwünschte Schimmelbildung zu vermeiden, kann der erfindungsgemäße Fließestrich außerdem 0 bis 1 Gew-% Konservierungsmittel enthalten. Bei dem Konservierungsmittel kann es sich z. B. um Chloracetamid, Thiazolinon- und Isothiazolinon-Derivate und/oder um Bronopol bzw. Mischungen daraus handeln.Around an unwanted or undesirable mold growth In addition, the leveling agent according to the invention can also contain from 0 to 1% by weight of preservative contain. The preservative may be, for. For example, chloroacetamide, Thiazolinone and isothiazolinone derivatives and / or Bronopol Mixtures of these act.

Bei dem Bindemittel des erfindungsgemäßen Fließestrich handelt es sich vorzugsweise um Produkte, welche die Füllstoffe und das Silikat untereinander und – falls es wünschenswert ist – auch mit einem Untergrund wie z. B. einem Rohbeton o. dgl. verbinden. Die Bindemittel binden durch Entzug des Wassers des Fließestrichs, insbesondere durch das Verdunsten des Wassers ab. Für den erfindungsgemäßen Fließstrich sind Film bildende wässrige Polymer-Dispersionen, d. h. Dispersionen von feinteiligen natürlichen und/oder synthetischen Polymeren, geeignet. Bei den Dispersionen handelt es sich vorzugsweise um wässrige Dispersionen von Polymeren wie Natur- und Synthesekautschuk, sowie von Kunstharzen und Kunststoffen; unabhängig von deren Herstellung. Zusätzlich zu den Polymeren können die Dispersionen noch Zusätze von bspw. Netz- und Dispergiermitteln, Entschäumern, Konservierungsstoffen, Füllstoffen und Verdickern enthalten. Desgleichen ist es möglich, Kombinationen verschiedener Polymere, sogenannte Copolymere, zu verwenden.at The binder of the flowing screed according to the invention is preferably about products containing the fillers and the silicate with each other and, if desirable is - too with a background such. B. a raw concrete o. The like. Connect. The binders bind by removing the water of the liquid screed, in particular by the evaporation of the water. For the flow line according to the invention are film-forming watery Polymer dispersions, d. H. Dispersions of finely divided natural and / or synthetic polymers. For the dispersions they are preferably aqueous dispersions of polymers such as natural and synthetic rubber, as well as synthetic resins and plastics; independently of their production. additionally to the polymers can the dispersions still additives from, for example, wetting and dispersing agents, defoamers, preservatives, fillers and thickeners included. Likewise it is possible to combine different Polymers, so-called copolymers to use.

Der erfindungsgemäße Fließestrich ist in vorteilhafter Weise frei von Weichmachern und organischen Lösungsmitteln.Of the Flooring according to the invention is advantageously free of plasticizers and organic Solvents.

Erfindungsgemäß dient das Wasser als Dispersionsmedium, in welchem sich die übrigen Komponenten des Fließestrichs molekular dispers, koloidal dispers oder grob dispers befinden.According to the invention serves the water as a dispersion medium, in which the other components of the liquid screed molecularly dispersed, colloidally dispersed or coarsely dispersed.

Der Wassergehalt sollte möglichst gering sein.Of the Water content should be as possible be low.

Die Füllstoffe beeinflussen die Eigenschaften des Fließestrichs ganz erheblich. Erfindungsgemäß kommen als schwere Füllstoffe insbesondere mineralische Füllstoffe, wie z. B. verschiedene Sande, Tonerden, Kreiden, Eisenoxide, und als leichte Füllstoffe bspw. Hohlkugeln aus Glas, Keramik oder Kunststoff, Fasern aus Zellulose oder aus Kunststoff, Pulver aus Kunststoff und Gummimehl, Bims, Diatomeenerde, Perlite und Korkmehl zum Einsatz. Die Füllstoffe werden so gewählt, dass sowohl zerklüftete, unregelmäßige als auch glatte, runde Partikel in einem solchen Verhältnis verwendet werden, dass sich die verschiedenen Partikel ineinander verhaken.The fillers significantly affect the properties of the liquid screed. Come in accordance with the invention as heavy fillers especially mineral fillers, such as For example, various sands, clays, chalks, iron oxides, and as light fillers For example, hollow spheres made of glass, ceramic or plastic, cellulose fibers or plastic, powder of plastic and rubber powder, pumice, Diatomaceous earth, perlite and cork flour are used. The fillers are chosen that both jagged, irregular as also uses smooth, round particles in such a ratio be that the different particles get caught in each other.

Besonders gute Schall und Wärme dämmende Eigenschaften besitzt der erfindungsgemäße Fließestrich, wenn er Korkmehl mit Perliten und Fasern kombiniert enthält.Especially good sound and heat insulating Properties of the invented liquid screed, if he cork flour contains perlites and fibers combined.

Ein solcher, Korkmehl enthaltender erfindungsgemäßer Fließestrich weist die folgenden Vorteile auf:
Er ist extrem komprimierbar und elastisch, weil die Zellmembranen des Korks sehr flexibel sind.Such cork flour-containing flowable screed according to the invention has the following advantages:
It is extremely compressible and elastic because the cell membranes of the cork are very flexible.

Er ist isolierend und Feuer hemmend, weil Kork keine Flammen verbreitet; es werden während der Verbrennung keine toxischen Gase freigesetzt.He is insulating and fire retardant because cork does not spread flames; it will be during the Combustion releases no toxic gases.

Er ist extrem strapazierfähig und er besitzt einen hohen Reibungskoeffizienten. Durch die wabenförmige Struktur der SUBEROSE Oberfläche entsteht weniger Beeinträchtigung durch Aufprall oder Reibung als bei anderen, bekannten harten Oberflächen.He is extremely durable and he has a high coefficient of friction. Through the honeycomb structure the SUBEROSE surface creates less impairment by impact or friction than other known hard surfaces.

Durch das Vorhandensein von Suberin, bei dem es sich um eine komplexe Mischung aus Fettsäure und einem starken organischen Alkohol handelt, erweist sich Kork als flüssigkeits- und gasundurchlässig.By the presence of suberin, which is a complex Mixture of fatty acid and a strong organic alcohol, cork proves to be as liquid and gas impermeable.

Er ist angenehm fußwarm.He is pleasantly warm.

Er ist quasi unzerstörbar.He is virtually indestructible.

Er weist eine hervorragende Trittschalldämmung auf.He has excellent footfall sound insulation.

Er unterliegt keinen Veränderungen durch hohe Temperaturschwankungen.He is not subject to change due to high temperature fluctuations.

Die positiven Eigenschaften von Kork werden durch seine geringe Leitfähigkeit von Wärme, Schall und Vibration noch erhöht. Das resultiert aus der Tatsache, dass die gasförmigen Elemente in undurchlässigen Kammern versiegelt und durch ein feuchtigkeits-resistentes Material gegeneinander isoliert sind. Infolge dessen besitzt von allen natürlichen Materialien Kork eine der besten isolierenden Eigenschaften – sowohl thermisch als auch akustisch.The The positive properties of cork are due to its low conductivity of heat, sound and vibration still increased. This results from the fact that the gaseous elements in impermeable chambers sealed and by a moisture-resistant material against each other are isolated. As a result possesses of all natural materials Cork one of the best insulating properties - both thermally and acoustically.

Kork nimmt keinen Staub auf und verursacht demzufolge weder Allergien noch stellt er ein Risiko für Asthmatiker dar.cork does not absorb dust and therefore does not cause allergies still he poses a risk for Asthmatic dar.

Die Herstellung des erfindungsgemäßen Fließestriches erfolgt unter Rühren bspw. in einem Schaufelmischer oder in einem Dissolver. Zur Entfernung von Luftblasen aus dem Fließestrich ist es zweckmäßig, wenn während des Mischvorgangs eine Evakuierung der Masse erfolgt.The Production of the flowable screed according to the invention is done with stirring for example in a paddle mixer or in a dissolver. For removal of bubbles from the liquid screed it is useful if while the mixing process an evacuation of the mass takes place.

Der erfindungsgemäße Fließestrich wird üblicherweise aus einem Vorratsbehälter ausgegossen und mit geeigneten Werkzeugen verdichtet und geglättet. Der Fließstrich kann infolge seines geringen Schwundes auch als Abform-, Abguß- oder Formgußmasse zum Nachbilden von Gegenständen verwendet werden.Of the Flooring according to the invention becomes common from a storage container poured out and compacted with suitable tools and smoothed. Of the flow line Due to its low shrinkage, it can also be used as an impression, casting or Formgußmasse to emulate objects be used.

Der erfindungsgemäße Fließestrich härtet durch Trocknung bei normaler Raumtemperatur aus.Of the Flooring according to the invention hardens Drying at normal room temperature.

Zur weiteren Verdeutlichung der Erfindung dienen die nachfolgenden Rezepturbeispiele, wobei es sich versteht, dass die Erfindung nicht auf diese Rezepturbeispiele beschränkt ist.to Further clarification of the invention serve the following recipe examples, it being understood that the invention is not limited to these recipe examples limited is.

Rezepturbeispiel 1:Formulation Example 1

  • 40 Gew-% Aluminiumsilikat,40% by weight of aluminum silicate,
  • 10 Gew-% Kaolin,10% by weight of kaolin,
  • 5 Gew-% Cellulosfasern5% by weight of cellulose fibers
  • 10 Gew-% Styrol-Acrylat Dispersion,10% by weight styrene-acrylate dispersion,
  • 0,2 Gew-% Konservierungsstoff,0.2% by weight of preservative,
  • 34,8 Gew-% Wasser.34.8% by weight of water.

Rezepturbeispiel 2:Formulation example 2:

  • 25 Gew-% Aluminiumsilikat,25% by weight of aluminum silicate,
  • 5 Gew-% Kaolinerde,5% by weight of kaolin earth,
  • 1 Gew-% Cellulosefasern,1% by weight of cellulose fibers,
  • 5 Gew-% Korkmehl,5% by weight cork flour,
  • 5,5 Gew-% Perlite,5.5% by weight of perlite,
  • 15 Gew-% Acrylatdispersion,15% by weight of acrylate dispersion,
  • 5 Gew-% Vinylacetat-Dispersion,5% by weight of vinyl acetate dispersion,
  • 0,2 Gew-% Konservierungsmittel,0.2% by weight preservative,
  • 38,3 Gew-% Wasser.38.3% by weight of water.

Rezepturbeispiel 3:Formulation example 3:

  • 40 Gew-% Aluminiumsilikat,40% by weight of aluminum silicate,
  • 15 Gew-% feinkörniger Sand,15% by weight finer grain Sand,
  • 3 Gew-% Perlite,3% by weight of perlite,
  • 2 Gew-% Korkmehl,2% by weight cork flour,
  • 5 Gew-% Cellulosefasern,5% by weight of cellulose fibers,
  • 12 Gew-% Acrylatdispersion,12% by weight of acrylate dispersion,
  • 0,2 Gew-% Konservierungsmittel,0.2% by weight preservative,
  • 22,8 Gew-% Wasser.22.8% by weight of water.

Claims (11)

Fließestrich, der bei normaler Zimmertemperatur aushärtet und der einen geringen Schwund aufweist. dadurch gekennzeichnet, dass der Fließestrich folgende Zusammensetzung aufweist: 20–70 Gew-% Silikat, ≤ 30 Gew-% schweren Füllstoff, ≤ 30 Gew-% leichten Füllstoff, 10–70 Gew-% Bindemittel, und 10–60 Gew-% Wasser.Liquid screed, which cures at normal room temperature and has a low shrinkage. characterized in that the liquid screed has the following composition: 20-70% by weight of silicate, ≤ 30% by weight heavy filler, ≤ 30% by weight light filler, 10-70% by weight of binder, and 10-60% by weight of water , Fließestrich nach Anspruch 1, dadurch gekennzeichnet, dass der Fließestrich außerdem 0–1 Gew-% Konservierungsmittel enthält.leveling screed according to claim 1, characterized in that the flowing screed Furthermore 0-1% by weight Preservative contains. Fließestrich nach Anspruch 2, dadurch gekennzeichnet, dass das Konservierungsmittel Chloracetamid und/oder Thiazolinon- und Isothiazolinon-Derivate und/oder Bronopal enthält.leveling screed according to claim 2, characterized in that the preservative Chloroacetamide and / or thiazolinone and isothiazolinone derivatives and / or Bronopal. Fließestrich nach Anspruch 1, dadurch gekennzeichnet, dass das Silikat Aluminiumsilikat ist.leveling screed according to claim 1, characterized in that the silicate aluminum silicate is. Fließestrich nach Anspruch 1, dadurch gekennzeichnet, dass der schwere Füllstoff Kaolin, Kaolinerde und/oder feinen Sand enthält.leveling screed according to claim 1, characterized in that the heavy filler Contains kaolin, kaolin soil and / or fine sand. Fließestrich nach Anspruch 1, dadurch gekennzeichnet, dass der leichte Füllstoff Cellulosefasern enthält.leveling screed according to claim 1, characterized in that the light filler Contains cellulose fibers. Fließestrich nach Anspruch 1, dadurch gekennzeichnet, dass der leichte Füllstoff Perlite enthält.leveling screed according to claim 1, characterized in that the light filler Contains perlite. Fließestrich nach Anspruch 1, dadurch gekennzeichnet, dass der leichte Füllstoff Korkmehl enthält.leveling screed according to claim 1, characterized in that the light filler Contains cork flour. Fließestrich nach Anspruch 1, dadurch gekennzeichnet, dass das Bindemittel Acrylatdispersion enthält.leveling screed according to claim 1, characterized in that the binder acrylate dispersion contains. Fließestrich nach Anspruch 9, dadurch gekennzeichnet, dass das Bindemittel Styrol-Acrylatdispersion enthält.leveling screed according to claim 9, characterized in that the binder is styrene-acrylate dispersion contains. Fließestrich nach Anspruch 9, dadurch gekennzeichnet, dass das Bindemittel außerdem Vinylacetat-Dispersion enthält.leveling screed according to claim 9, characterized in that the binder also vinyl acetate dispersion contains.
DE200820003183 2008-03-06 2008-03-06 leveling screed Expired - Lifetime DE202008003183U1 (en)