DE202006007596U1

DE202006007596U1 - Construction material for interior fittings on basis of plate-shaped material grade for dry construction, has plate-shaped material with activated charcoal wherein plate-shaped material is building board

Info

Publication number: DE202006007596U1
Application number: DE202006007596U
Authority: DE
Original assignee: Bluecher GmbH
Current assignee: Bluecher GmbH
Priority date: 2006-04-18
Filing date: 2006-05-12
Publication date: 2007-05-31
Anticipated expiration: 2016-05-13

Abstract

Construction material has plate-shaped material which has activated charcoal. The plate-shaped material is a building board e.g. building board made up of gypsum, gypsum cardboard, gypsum fibrous composite materials such as gypsum fiber board, fiber concrete board, glass fiber, carbon fiber, wood, wood fiber, plastic material as well as combination of it. The preferred material is gypsum board gypsum plasterboard e.g. gypsum plasterboard with single or double sided cardboard box and gypsum core layer.

Description

Die vorliegende Erfindung betrifft mit Adsorbentien beaufschlage Plattenmaterialien für den Trockenbau. Insbesondere betrifft die vorliegende Erfindung ein Baumaterial für den Innenausbau auf Basis eines plattenförmigen Werkstoffs für den Trockenbau nach dem Oberbegriff von Anspruch 1.The The present invention relates to adsorbent loaded sheet materials for the Drywall. In particular, the present invention relates to a Building material for the interior design based on a plate-shaped material for drywall after the preamble of claim 1.

Aufgrund eines steigenden Umweltbewußtseins einerseits, aber auch infolge hochempfindlicher Analysenmethoden andererseits rückt die Belastung unserer Umgebung bzw. Umwelt durch Schadstoffe immer mehr ins Licht der Öffentlichkeit. So besteht beispielsweise für den Bereich schad- und/oder geruchsstoffbelasteter Gebäude ein gesteigerter Bedarf, diese mit möglichst wenig Aufwand von Schad- und/oder Geruchsstoffen zu befreien und erforderlichenfalls zu sanieren. Weiterhin besteht ein Bedarf, das Raumklima bzw. die Raumluft in schad- und/oder geruchsstoffbelasteten Räumen entsprechend zu verbessern.by virtue of a rising environmental awareness on the one hand, but also as a result of highly sensitive analytical methods on the other hand moves the pollution of our environment or environment by pollutants always more in the public eye. For example, there is the area of damaged and / or odoriferous buildings increased demand, this with as possible To free little effort from harmful and / or odorous substances and to renovate if necessary. Furthermore, there is a need that Room climate or room air in polluted and / or odorous substances clear to improve accordingly.

Im Rahmen der vorliegenden Erfindung werden als Schadstoffe insbesondere solche Stoffe bezeichnet, die bereits in geringer Menge beim Menschen Irritationen, Allergien oder Krankheiten auslösen können. Hierzu zählen beispielsweise Holzschutzmittel, wie Pentachlorphenol (PCP) und Lindan, Weichmacher, wie polychlorierte Biphenyle (PCB), oder aber auch Formaldehyd. So wurde beispielsweise Formaldehyd in Spanplatten eingesetzt und ist mittlerweile als karzinogen eingestuft. Auch können Kohlenwasserstoffe, die gegebenenfalls aromatisch sind, bzw. deren chlorierte Derivate als Schadstoffe im Sinne der vorliegenden Erfindung beispielsweise aus Lacken, Anstrichen, Klebstoffen oder dergleichen entweichen.in the Within the scope of the present invention are as pollutants in particular such substances are already known in small quantities in humans Irritations, allergies or diseases can cause. These include, for example Wood preservatives, such as pentachlorophenol (PCP) and lindane, plasticizers, such as polychlorinated biphenyls (PCB), or even formaldehyde. For example, formaldehyde was used in chipboard and is now classified as a carcinogen. Also, hydrocarbons, which are optionally aromatic, or their chlorinated derivatives as pollutants in the context of the present invention, for example escape from paints, coatings, adhesives or the like.

Besonders problematische Schadstoffe sind insbesondere die vorgenannten PCB, die beispielsweise als Weichmacher in Fugendichtungsmassen, insbesondere bei der Errichtung von Bauten aus Fertigelementen, eingesetzt wurden. Neuere Erkenntnisse haben gezeigt, daß PCB im Laufe der Zeit aus Dichtungsmassen sowohl in die angrenzenden Betonelemente diffundieren als auch von den Fugendichtungen in die Umgebungsluft abgegeben werden können. Über den Luftaustausch wird dann die mit PCB belastete Luft über das gesam te Gebäude verteilt. Das so von den Fugenabdichtungen freigesetzte PCB schlägt sich in den Räumen teilweise partikelgebunden nieder, löst sich zu einem großen Teil aber auch in Wandfarben und Kunststoffen, was dazu führt, daß nach einiger Zeit der Freisetzung eine Reihe von sogenannten sekundären Emissionsquellen gebildet werden, wobei hier insbesondere gestrichene Wand- und Deckenflächen zu nennen sind. Diese Sekundärquellen enthalten dann im allgemeinen eine derart große Menge an PCB, daß sie eine große Emissionsfläche darstellen, so daß ein alleiniges Entfernen der Fugenabdichtungen kein Absinken der PCB-Konzentrationen in der Raumluft unter die vorgeschriebenen Werte bewirken kann.Especially problematic pollutants are in particular the abovementioned PCB, for example, as plasticizers in jointing compounds, in particular in the construction of prefabricated buildings were used. Recent findings have shown that over time PCBs are made from sealants both diffuse into the adjacent concrete elements as well as from the joint seals can be discharged into the ambient air. On the Air exchange will then transfer the PCB contaminated air over the entire building distributed. The PCB thus released from the joint seals becomes effective in the rooms partially particle-bound, dissolves to a large extent but also in wall paints and plastics, which means that after some Time of release formed a series of so-called secondary emission sources be here, in particular painted wall and ceiling surfaces are called. These secondary sources then contain such a large amount of PCB in general that they have a represent large emission area, so that one only removal of joint seals no decrease in PCB concentrations in the room air below the prescribed values.

Eine weitere Quelle von Schad- und/oder Geruchsstoffen können beispielsweise Teppichböden darstellen. Die Emissionen entstehen z. B. dadurch, daß Ausgangsstoffe dieser Produkte unter dem Einfluß von Feuchtigkeit und/oder unter dem Einfluß von Bestandteilen der Untergrundmaterialien reagieren, so daß der Boden selbst nach dem Entfernen des Bodenbelags weiter Geruchs- und/oder Schadstoffe emittiert, so daß entweder der gesamte Fußboden entfernt oder aber ein Zwischenboden mit Hinterlüftung verlegt werden muß.A another source of pollutants and / or odors, for example carpeting represent. The emissions arise z. B. in that starting materials these products under the influence of moisture and / or under the influence of Components of the substrate materials react, so that the soil even after removal of the flooring further odors and / or pollutants emitted so that either the entire floor removed or a false floor with ventilation must be laid.

Eine weitere Emissionsquelle für unangenehme, manchmal auch gesundheitsschädliche Emissionen sind Zusätze zum Baumaterial selbst. Beispielsweise sind viele Gebäude von Ammoniakausdünstungen betroffen, die auf die Verwendung von Ammoniumsalzen, Harnstoffen oder organischen Aminen im weitesten Sinne als Frostschutzmittel für Beton und Mörtel zurückzuführen sind. Des weiteren ist als Ursache für die Ausdünstung von Aminen bisweilen auch eine vormalige Nutzung eines Raumes z. B. zu Zwecken der Tierhaltung zu nennen, welche dazu führt, daß Bauelemente über einen längeren Zeitraum mit den Schadstoffen aus der Luft beaufschlagt werden. Selbst bei einem Entfernen der Primäremissionsquellen dieser Substanzen, etwa bei einer Umwidmung eines Stallgebäudes zu einem Wohn- oder Geschäftsraum, werden dann diese Schad- und/oder Geruchsstoffe von den Sekundärquellen, nämlich Wand- und Deckenflächen, weiter emittiert.A further emission source for unpleasant, sometimes harmful emissions are additives to the Construction material itself. For example, many buildings are from ammonia fumes affected the use of ammonium salts, ureas or organic amines in the broadest sense as antifreeze for concrete and mortar are attributed. Furthermore, as a cause for the exhalation from amines sometimes also a former use of a room z. B. for purposes of animal husbandry, which leads to components over a longer Be exposed to the pollutants from the air. Even with a removal of the primary emission sources of these substances, for example, when converting a stable building into a living or business space, then these pollutants and / or odors from the secondary sources, namely Wall and ceiling surfaces, continue emitted.

Eine Möglichkeit zur Entfernung von PCB emittierenden Schadstoffquellen in Form von PCB belasteten Fugendichtmassen ist in der DE 40 28 434 A1 vorgesehen. Hierbei wird durch geeignete Maßnahmen die Dichtungsmasse, d. h. nur die Primärquelle, herausgeschnitten und entsorgt. Das Verfahren greift damit aber lediglich auf die Primärquellen zu, so daß eine Dekontaminierung der Sekundärquellen unberücksichtigt bleibt.One way to remove PCB emitting pollutant sources in the form of PCB contaminated joint sealants is in DE 40 28 434 A1 intended. Here, by appropriate measures, the sealant, ie only the primary source, cut out and disposed of. However, the method accesses only the primary sources so that a decontamination of the secondary sources is disregarded.

Weiter ist aus der DE 38 18 993 A1 ein Verfahren zur Sanierung schadstoffbelasteter Räume bekannt, bei dem die schadstoffbelastete Raumluft dadurch gereinigt wird, daß durch geeignete Maßnahmen Luft an Adsorbentien künstlich oder nur durch Eigenzirkulation vorbeigeführt wird. Beispielsweise wird die schadstoffbelastete Luft durch mit Adsorbentien beschickte Adsorptionstürme gepreßt. Eine andere dort beschriebene Möglichkeit besteht darin, die Luft an großflächigen, mit Adsorbentien beladenen Flächengebilden, wie beispielsweise Vorhängen, vorbeizuführen. Dieses Verfahren hat den entscheidenden Nachteil, lediglich auf die bereits belastete Raumluft zurückzugreifen, welche sich immer wieder mit der schadstoffbelasteten Luft vermischt, so daß allenfalls ein Verdünnungseffekt erzielt wird.Next is from the DE 38 18 993 A1 a method for the remediation of polluted rooms known, in which the polluted room air is purified by that art is bypassed by adsorbents by appropriate measures or artificially or only by natural circulation. For example, the polluted air is forced through adsorbent towers charged with adsorbents. Another possibility described therein is to pass the air on large area, with adsorbents loaded fabrics, such as curtains. This procedure has the decisive disadvantage, only resorting to the already contaminated room air, which repeatedly mixed with the polluted air, so that at most a dilution effect is achieved.

Weiterhin sind textile, mit Adsorbentien beaufschlagte, im allgemeinen mit einer wasserundurchlässigen, aber wasserdampfdurchlässigen Beschichtung versehene Flächematerialien bekannt, welche in Abhängigkeit von der Schadstoffquelle als Tapete, Bodenbelag oder dergleichen ausgebildet sind und über die entsprechenden Schad- und/oder Geruchsstoffe emittierenden Quellen aufgebracht werden (vgl. z. B. DE 44 32 834 A1 , DE 44 47 844 C2 , DE 196 07 423 A1 und DE 200 08 162 U1 ). Die dort beschriebenen Materialien eignen sich aber nicht für den Trockenbau, insbesondere nicht als Wand-, Boden- oder Deckenelemente.Furthermore, textile, acted upon with adsorbents, generally provided with a water-impermeable, but water-vapor-permeable coating surface materials are known, which are formed as a function of the pollutant source as wallpaper, flooring or the like and applied via the corresponding pollutants and / or odors emitting sources ( see, for example, DE 44 32 834 A1 . DE 44 47 844 C2 . DE 196 07 423 A1 and DE 200 08 162 U1 ). However, the materials described therein are not suitable for drywall, in particular not as wall, floor or ceiling elements.

Schließlich sind aus der WO 2005/026465 A2 Baumaterialien für den Innenausbau auf Basis von Gipsbauplatten, wie beispielsweise Gipskartonplatten und Gipsfaserplatten, bekannt, welche Zeolithe in Mengen von 1 bis 25 Gew.-% enthalten, und dazu bestimmt sind, Luftschadstoffe in Innenräumen, wie Formaldehyde, Ammoniak, Tabakrauch etc., zu reduzieren. Die dort eingesetzten Zeolithe liefern aber nicht immer das gewünschte Ergebnis, insbesondere aufgrund ihres nicht immer ausreichenden Vermögens, Schad- und/oder Geruchsstoffe aus der Umgebungsluft abzubauen oder zu sorbieren. Da die Zeolithe bei der Herstellung der Gipsplatten in die Gipsmasse eingerührt werden, ist zudem ein großer Teil ihrer Oberfläche nicht für die aufzunehmenden bzw. zu zersetzenden Schad- und Geruchsstoffe frei zugänglich, so daß die Schad- und Geruchsstoffe durch die Gipsmasse hindurch zu den hierin eingelagerten Zeolithen diffundieren müssen. Aus den vorgenannten Gründen müssen relativ große Mengen an Zeolithen eingesetzt werden, was aber die Baumaterialien als solche, insbesondere im Hinblick auf ihren Verbund oder ihre Stabilität, beeinträchtigen kann.Finally are from WO 2005/026465 A2 building materials for interior design based on Plasterboard, such as plasterboard and gypsum fibreboard, known which contain zeolites in amounts of 1 to 25 wt .-%, and to indoor air pollutants, such as formaldehyde, ammonia, Tobacco smoke etc., to reduce. But the zeolites used there deliver not always the desired one Result, in particular due to their insufficient ability to and / or degrade odors from the ambient air or sorb. As the zeolites in the production of gypsum boards in the gypsum compound stirred Becoming, is also a big part their surface not for the pollutants and odors to be absorbed or decomposed freely accessible, So that the Pollutants and odors through the gypsum compound to those herein have to diffuse embedded zeolites. From the aforementioned establish have to relatively large Quantities of zeolites are used, but what the building materials as such, in particular with regard to their composite or their Stability, can affect.

Das der vorliegenden Erfindung zugrundeliegende Problem liegt daher insbesondere in der Bereitstellung von Baumaterialien für den Innenausbau, vorzugsweise auf Basis plattenförmiger Werkstoffe für den Trockenbau, welche die zuvor geschilderten Nachteile des Standes der Technik zumindest weitgehend vermeiden oder aber wenigstens abschwächen.The The problem underlying the present invention is therefore in particular in the provision of building materials for interior work, preferably based on plate-shaped Materials for the drywall, which the previously described disadvantages of the prior art avoid the technology at least largely or at least weaken.

Insbesondere sollen Baumaterialien bzw. Bauplatten mit verbesserten Eigenschaften bereitgestellt werden. Dabei sollen insbesondere für den Innenausbau geeignete Baumaterialien, vorzugsweise in Form von sogenannten Bauplatten, bereitgestellt werden, mit denen sich Geruchs- und/oder Schadstoffe aus der Umgebungsluft effizient reduzieren lassen.Especially are building materials or building boards with improved properties to be provided. It should in particular for the interior suitable building materials, preferably in the form of building boards, be provided with which odors and / or pollutants can be efficiently reduced from the ambient air.

Die Anmelderin hat nun überraschenderweise herausgefunden, daß das zuvor geschilderte Problem dadurch gelöst werden kann, daß man Baumaterialien für den Innenausbau, insbesondere auf Basis sogenannter Bauplatten, mit Aktivkohle versieht bzw. beaufschlagt.The Applicant has now surprisingly found out that the previously described problem can be solved by building materials for the Interior fittings, especially on the basis of so-called structural panels, with Activated carbon provides or impinges.

Gegenstand der vorliegenden Erfindung ist somit ein Baumaterial für den Innenausbau auf Basis eines plattenförmigen Werkstoffs für den Trockenbau, wobei der plattenförmige Werkstoff Aktivkohle aufweist bzw. hiermit versehen und/oder beaufschlagt ist.object The present invention is thus a building material for interior design on the basis of a plate-shaped Material for the dry construction, wherein the plate-shaped material has activated carbon or hereby provided and / or acted upon.

Als plattenförmige Werkstoffe im Sinne der vorliegenden Erfindung können insbesondere sogenannte Bauplatten, vorzugsweise auf Basis von Gips, aber auch auf Basis anderer Materialien, eingesetzt werden. Hierbei kann es sich beispielsweise um Bauplatten aus Gips ("Gipsbauplatten"), Gipskartonbauplatten (z. B. Rigips^®-Platten), Bauplatten aus Gipsfaserverbundstoffen (z. B. Gipsfaserplatten), Bauplatten aus Zementfaserverbundstoffen (z. B. Faserzementplatten, wie Eternit^®-Platten), Bauplatten aus Glasfasern, Bauplatten aus Kohlenstoffasern, Holzbauplatten, Holzfaserbauplatten, Kunststoffbauplatten oder dergleichen sowie Bauplatten aus Kombinationen der vorgenannten Materialien handeln. Erfindungsgemäß bevorzugt sind Gipsbauplatten oder aber Gipskartonbauplatten, insbesondere Gipskartonbauplatten mit ein- oder beidseitiger Kartonageaußenbeschichtung und einer Gipskernschicht.As plate-like materials in the context of the present invention, in particular so-called building boards, preferably based on gypsum, but also based on other materials used. These may, for example, be gypsum plasterboard (plasterboard), gypsum plasterboard (eg ^Rigips® panels), gypsum fiberboard (eg gypsum fiberboard) structural panels, cement fiber composite building panels (eg fiber cement boards such as Eternit ^® boards), structural panels made of glass fibers, building boards made of carbon fibers, wooden building boards, wood fiber boards, plastic boards or the like, as well as building boards made of combinations of the aforementioned materials. Plasterboard or plasterboard building boards, in particular plasterboard building boards with one-sided or two-sided cardboard outer coating and a gypsum core layer, are preferred according to the invention.

Erfindungsgemäß eingesetzte Bauplatten bzw. plattenförmige Werkstoffe haben im allgemeinen Dicken von 0,1 bis 20 cm, insbesondere 0,5 bis 10 cm, vorzugsweise 1 bis 10 cm.Used according to the invention Building boards or plate-shaped Materials generally have thicknesses of 0.1 to 20 cm, in particular 0.5 to 10 cm, preferably 1 to 10 cm.

Die Befestigung der Aktivkohle in und/oder an den plattenförmigen Werkstoffen bzw. Bauplatten kann in vielfältigster Art und Weise erfolgen. Dies ist dem Fachmann an sich geläufig.The Attachment of the activated carbon in and / or on the plate-shaped materials or construction panels can in diverse ways Way done. This is familiar to the person skilled in the art.

Beispielsweise kann die Aktivkohle in den plattenförmigen Werkstoffen bei deren Herstellung eingearbeitet sein (z. B. im Falle von Gips- oder Gipskartonplatten in den Gips eingerührt werden); diese Ausführungsform ist erfindungsgemäß jedoch weniger bevorzugt, da ein Teil der aktiven Oberfläche der Aktivkohle dann mit dem Material der Bauplatte bzw. des Werkstoffs belegt ist und nicht mehr für Adsorptionszwecke zur Verfügung steht.For example can the activated carbon in the plate-shaped materials at their Preparation incorporated (for example, in the case of gypsum plasterboard or plasterboard stirred into the plaster become); this embodiment is according to the invention, however less preferred because part of the active surface of the activated carbon then occupied with the material of the building board or the material and not for anymore Adsorption purposes available stands.

Erfindungsgemäß bevorzugt ist es, wenn der plattenförmige Werkstoff bzw. die Bauplatte an mindestens einer seiner bzw. ihrer beiden Oberflächen mit Aktivkohle versehen und/oder beaufschlagt ist. In erfindungsgemäß bevorzugter Weise ist somit die Aktivkohle nur an der bzw. den Oberfläche(n) des plattenförmigen Werkstoffs fixiert. Dies kann beispielsweise dadurch erfolgen, daß ein Klebstoff auf dem plattenförmigen Werkstoff aufgetragen wird, wobei ein punktförmiger und/oder punktrasterförmiger Klebstoffauftrag bevorzugt ist, und nachfolgend die Aktivkohle hieran zum Haften gebracht wird. Alternativ kann die Aktivkohle aber auch in die Oberfläche(n) des plattenförmigen Werkstoffs bzw. der Bauplatte bei dessen bzw. deren Herstellung eingearbeitet sein, beispielsweise durch Eindrücken in den noch feuchten Gips oder Zementfaserverbundstoff einer entsprechenden Werkstoff- bzw. Bauplatte.According to the invention it is preferred if the plate-shaped material or the building board is provided and / or acted on at least one of its or both surfaces with activated carbon. In accordance with the invention preferably thus is the Activated carbon fixed only on the or the surface (s) of the plate-shaped material. This can be done, for example, that an adhesive is applied to the plate-shaped material, wherein a punctiform and / or punktrasterförmiger adhesive application is preferred, and subsequently the activated carbon is adhered thereto. Alternatively, however, the activated carbon can also be incorporated into the surface (s) of the plate-shaped material or the building board during its production, for example by pressing into the still moist plaster or cement fiber composite of a corresponding material or building board.

Die Fixierung der Aktivkohle an dem plattenförmigen Werkstoff bzw. seine Einarbeitung hieran und/oder hierin erfolgt insbesondere derart, daß minde stens 25%, insbesondere mindestens 30%, vorzugsweise mindestens 40%, besonders bevorzugt mindestens 50%, der Oberfläche der Aktivkohle für zu adsorbierende Schad- und/oder Geruchsstoffe frei zugänglich ist. Wird beispielsweise die Aktivkohle (z. B. in Form von Aktivkohlekörnern, vorzugsweise Aktivkohlekügelchen) mittels eines Klebstoffs an einer oder aber an beiden Oberflächen des plattenförmigen Werkstoffs fixiert, wird vorteilhafterweise die Aktivkohle nicht vollständig in den Klebstoff eingedrückt, so daß sie noch freie Oberfläche in dem vorgenannten Maße aufweist. Entsprechendes gilt beim Einarbeiten in den plattenförmigen Werkstoff bei dessen Herstellung (z. B. bei Gipsplatten durch Eindrücken der Aktivkohle in den noch feuchten Gips).The Fixation of the activated carbon to the plate-shaped material or its Incorporation thereon and / or herein is in particular such that at least 25%, especially at least 30%, preferably at least 40%, especially preferably at least 50%, of the surface of the activated carbon for adsorbing Harmful and / or odorous substances is freely available. For example the activated carbon (eg in the form of activated carbon grains, preferably activated carbon beads) by means of an adhesive on one or both surfaces of the disc-shaped Material fixed, advantageously the activated carbon is not Completely pressed into the glue, so that she still free surface in the aforementioned dimensions having. The same applies when incorporating into the plate-shaped material during its manufacture (eg in the case of gypsum boards by impressing the Activated carbon in the still moist plaster).

Gemäß einer alternativen Ausführungsform kann die Aktivkohle aber auch an einem vorzugsweise flächigen Träger, insbesondere einem textilen Flächengebilde, wie beispielsweise einem Papier, einem Karton, einer Pappe oder dergleichen, fixiert sein, wobei dieser mit Aktivkohle beaufschlagte Träger dann mit dem plattenförmigen Werkstoff verbunden ist, insbesondere mittels Laminierung, Verkleben oder dergleichen.According to one alternative embodiment may the activated carbon but also on a preferably flat carrier, in particular a textile fabric, such as a paper, a cardboard, a cardboard or the like, be fixed, this acted upon by activated carbon Carrier then with the plate-shaped Material is connected, in particular by means of lamination, gluing or like.

Die Menge des plattenförmigen Werkstoffs an Aktivkohle ist derart ausgelegt, daß die durch die Aktivkohle bereitgestellte Adsorptionskapazität ausreicht, um bei der Verwendung des plattenförmigen Werkstoffs aus der Umgebung stammende Emissionen von Schad- und/oder Geruchsstoffen dauerhaft adsorptiv zu binden.The Amount of the plate-shaped Material of activated carbon is designed so that by the activated carbon provided adsorption capacity is sufficient to when using the plate-shaped material from the environment originating emissions of pollutants and / or odors permanently adsorptive to bind.

Die Menge an Aktivkohle kann in weiten Bereichen variieren. Insbesondere enthält der plattenförmige Werkstoff bzw. die Bauplatte nach der vorliegenden Erfindung Aktivkohle in einer Menge, insbesondere Beladungs- und/oder Auflagemenge, von insgesamt 20 bis 750 g/m², insbesondere 25 bis 500 g/m², vorzugsweise 30 bis 400 g/m², besonders bevorzugt 50 bis 300 g/m².The amount of activated carbon can vary widely. In particular, the plate-shaped material or the building board according to the present invention contains activated carbon in an amount, in particular loading and / or amount, of a total of 20 to 750 g / m ² , in particular 25 to 500 g / m ² , preferably 30 to 400 g / m ² , more preferably 50 to 300 g / m ² .

Was die Aktivkohle als solche anbelangt, so kann diese in beliebigen Erscheinungsformen eingesetzt werden.What As regards the activated carbon as such, it may be in any Manifestations are used.

Beispielsweise kann die Aktivkohle entsprechend einer erfindungsgemäß weniger bevorzugten Ausführungsform pulverförmig ausgebildet sein.For example can the activated carbon according to an inventively less preferred embodiment powdery be educated.

Erfindungsgemäß bevorzugt ist es jedoch, wenn die Aktivkohle kornförmig ("Kornkohle"), vorzugsweise kugelförmig ("Kugelkohle"), ausgebildet ist. Dabei weisen die Aktivkohlekörner, vorzugsweise Aktivkohlekugeln, vorteilhafterweise mittlere Teilchendurchmesser im Bereich von 0,01 bis 2,0 mm, insbesondere 0,05 bis 1,0 mm, vorzugsweise 0,1 bis 1,0 mm, auf. Bei dieser Ausführungsform wird die Beladungs- und/oder Auflagemenge vorteilhafterweise derart bemessen, daß die einzelnen Aktivkohlekörner, vorzugsweise Aktivkohlekugeln, einen mittleren Abstand zueinander auf dem plattenförmigen Werkstoff aufweisen, der mindestens der Hälfte, insbesondere mindestens Dreiviertel, vorzugsweise mindestens dem Einfachen, besonders bevorzugt mindestens dem Eineinhalbfachen, des mittleren Teilchendurchmessers der Aktivkohlekörner, vorzugsweise Aktivkohlekugeln, entspricht.According to the invention preferred However, it is when the activated carbon is granular ("grain"), preferably spherical ("ball coal") is formed. The activated carbon grains, preferably activated carbon spheres, advantageously mean particle diameter in the range of 0.01 to 2.0 mm, especially 0.05 to 1.0 mm, preferably 0.1 to 1.0 mm, on. In this embodiment, the loading and / or amount of support advantageously dimensioned such that the individual Activated carbon granules, preferably activated carbon spheres, a mean distance from each other on the plate-shaped Have material that is at least half, in particular at least Three quarters, preferably at least the simple, particularly preferred at least one and a half times, the average particle diameter the activated carbon grains, preferably activated carbon spheres corresponds.

Erfindungsgemäß bevorzugt eingesetzte Aktivkohlekörner, vorzugsweise Aktivkohlekügelchen, weisen einen Berstdruck von mindestens 5 Newton, insbesondere einen Berstdruck im Bereich von 5 Newton bis 20 Newton, pro Aktivkohlekorn bzw. Aktivkohlekügelchen auf.According to the invention preferred activated carbon granules used, preferably activated carbon beads, have a bursting pressure of at least 5 Newton, in particular a bursting pressure in the range of 5 Newton to 20 Newton per activated carbon grain or activated carbon beads on.

Gemäß einer alternativen Ausführungsform kann die Aktivkohle in Form von Aktivkohlefasern vorliegen. Gleichermaßen ist es möglich, eine Aktivkohle einzusetzen, welche eine Mischung aus faserförmiger und kornförmiger, vorzugsweise kugelförmiger, Aktivkohle umfaßt.According to one alternative embodiment may the activated carbon in the form of activated carbon fibers. Equally is it is possible to use an activated carbon, which is a mixture of fibrous and granular, preferably spherical, Activated carbon covers.

Um eine hohe Leistungsfähigkeit des erfindungsgemäßen Baumaterials zu gewährleisten, ist es vorteilhaft, wenn die eingesetzte Aktivkohle eine spezifische Oberfläche (BET) von mindestens 500 g/m², insbesondere mindestens 750 g/m², vorzugsweise mindestens 1.000 g/m², besonders bevorzugt mindestens 1.200 g/m², aufweist. Im allgemeinen weist die erfindungsgemäß eingesetzte Aktivkohle eine spezifische Oberfläche (BET) im Bereich von 500 bis 2.500 g/m², insbesondere 750 bis 2.250 g/m², vorzugsweise 900 bis 2.000 g/m², besonders bevorzugt 1.000 bis 1.750 g/m², auf.In order to ensure high performance of the building material according to the invention, it is advantageous if the activated carbon used has a specific surface area (BET) of at least 500 g / m ² , in particular at least 750 g / m ² , preferably at least 1000 g / m ² , particularly preferred at least 1,200 g / m ² . In general, the activated carbon used according to the invention has a specific surface area (BET) in the range of 500 to 2,500 g / m ² , in particular 750 to 2,250 g / m ² , preferably 900 to 2,000 g / m ² , particularly preferably 1,000 to 1,750 g / m ² , up.

Zur BET-Methode kann beispielsweise verwiesen werden auf Römpp Chemielexikon, 10. Auflage, Georg Thieme Verlag Stuttgart/New York, Stichwort: "BET-Methode", sowie auf die dort referierte Literatur, insbesondere Winnacker-Küchler, 3. Auflage, Band 7, Seiten 93 ff., sowie Z. Annal. Chem. 238, Seiten 187 bis 193 (1968).Reference may be made, for example, to the BET method to Römpp Chemielexikon, 10th edition, Georg Thieme Verlag Stuttgart / New York, keyword: "BET method", and to the literature cited therein, in particular Winnacker-Küchler, 3rd edition, volume 7 , Pages 93 ff., As well as Z. Annal. Chem. 238, p from 187 to 193 (1968).

Um eine hohe Effizienz des erfindungsgemäßen Baumaterials zu ermöglichen, ist es bevorzugt, wenn die eingesetzte Aktivkohle eine Aktivkohle mit einem Adsorptionsvolumen V_ads von mindestens 250 cm³/g, insbesondere mindestens 300 cm³/g, vorzugsweise mindestens 350 cm³/g, besonders bevorzugt mindestens 400 cm³/g, ist. Im allgemeinen wird eine Aktivkohle mit einem Adsorptionsvolumen V_ads von 250 bis 1.000 cm³/g, insbesondere 300 bis 900 cm³/g, vorzugsweise 350 bis 750 cm³/g, eingesetzt.In order to enable a high efficiency of the building material according to the invention, it is preferred if the activated carbon used is an activated carbon having an adsorption _volume V _ads of at least 250 cm ³ / g, in particular at least 300 cm ³ / g, preferably at least 350 cm ³ / g preferably at least 400 cm ³ / g. In general, an activated carbon having an adsorption _volume V _ads of 250 to 1000 cm ³ / g, in particular 300 to 900 cm ³ / g, preferably 350 to 750 cm ³ / g used.

Erfindungsgemäß bevorzugt ist eine Aktivkohle mit einem Gesamtporenvolumen nach Gurvich von mindestens 0,50 cm³/g, insbesondere mindestens 0,55 cm³/g, vorzugsweise mindestens 0,60 cm³/g, besonders bevorzugt mindestens 0,65 cm³/g, ganz besonders bevorzugt mindestens 0,70 cm³/g. Im allgemeinen wird eine Aktivkohle mit einem Gesamtporenvolumen nach Gurvich von 0,50 bis 0,90 cm³/g, insbesondere 0,55 bis 0,85 cm³/g, vorzugsweise 0,60 bis 0,80 cm³/g, besonders bevorzugt 0,65 bis 0,80 cm³/g, ganz besonders bevorzugt 0,70 bis 0,75 cm³/g, eingesetzt.According to the invention, an activated carbon having a total pore volume according to Gurvich of at least 0.50 cm ³ / g, in particular at least 0.55 cm ³ / g, preferably at least 0.60 cm ³ / g, particularly preferably at least 0.65 cm ³ / g , most preferably at least 0.70 cm ³ / g. In general, an activated carbon having a total pore volume according to Gurvich of 0.50 to 0.90 cm ³ / g, in particular 0.55 to 0.85 cm ³ / g, preferably 0.60 to 0.80 cm ³ / g, particularly preferably 0.65 to 0.80 cm ³ / g, very particularly preferably 0.70 to 0.75 cm ³ / g used.

Zu weiteren Einzelheiten bezüglich der Bestimmung des Gesamtporenvolumens nach Gurvich kann beispielsweise verwiesen werden auf L. Gurvich (1915), J. Phys. Chem. Soc. Russ. 47, 805, sowie auf S. Lowell et al., Characterization of Porous Solids and Powders: Surface Area Pore Size and Density, Kluwer Academic Publishers, Article Technology Series, Seiten 111 ff.To for further details For example, the determination of the total pore volume according to Gurvich reference is made to L. Gurvich (1915), J. Phys. Chem. Soc. Soot. 47, 805 and S. Lowell et al., Characterization of Porous Solids and Powders: Surface Area Pore Size and Density, Kluwer Academic Publishers, Article Technology Series, pages 111 ff.

Die Anmelderin hat herausgefunden, daß als Aktivkohle insbesondere eine Aktivkohle mit großem Mikroporenvolumenanteil, bezogen auf das Gesamtporenvolumen der Aktivkohle, geeignet ist. Im Rahmen der vorliegenden Erfindung wird unter dem Begriff des Mikroporenvolumens insbesondere dasjenige Porenvolumen der Aktivkohle verstanden, welches durch Poren mit einem Durchmesser von ≤ 25 Å (2,5 nm), insbesondere ≤ 20 Å (2,0 nm), bereitgestellt wird.The Applicant has found that as activated carbon in particular an activated carbon with a large micropore volume fraction, based on the total pore volume of the activated carbon is suitable. In the context of the present invention, the term of Micro pore volume in particular that pore volume of the activated carbon understood by pores having a diameter of ≤ 25 Å (2.5 nm), in particular ≦ 20 Å (2.0 nm), provided.

Die Anmelderin hat nämlich überraschenderweise herausgefunden, daß die Reduzierung der Schad- und/oder Geruchsstoffkonzentrationen besonders effizient ist, wenn der Mikroporenvolumenanteil der eingesetzten Aktivkohle besonders hoch ist. Ohne sich auf eine bestimmte Theorie festlegen zu wollen, läßt sich die besonders gute Effizienz mit einer Aktivkohle mit besonders großem Mikroporenvolumenanteil darauf zurückführen, daß die Mikroporen aufgrund ihrer nur geringen Größe sozusagen von allen Seiten bzw. Wandungen mit den zu sorbierenden bzw. adsorbierenden Molekülen in Wechselwirkung treten können. Insbesondere wird eine Aktivkohle mit einem Anteil des Mikroporenvolumens, bezogen auf das Gesamtporenvolumen der Aktivkohle, von mindestens 60%, insbesondere mindestens 65%, bevorzugt mindestens 70%, eingesetzt.The Namely, the applicant has surprisingly found out that the Reduction of pollutants and / or odorant concentrations especially is efficient when the micropore volume fraction of the used Activated carbon is particularly high. Without focusing on a specific theory want to set, can be the particularly good efficiency with an activated carbon with especially great Micropore volume fraction attributable to the fact that the micropores due to their only small size so to speak of all sides or walls with those to be sorbed or adsorbed molecules can interact. In particular, an activated carbon with a proportion of the micropore volume, based on the total pore volume of the activated carbon, of at least 60%, in particular at least 65%, preferably at least 70% used.

Insbesondere wird in erfindungsgemäß bevorzugter Weise eine Aktivkohle mit einem aus Poren mit Porendurchmessern von ≤ 25 Å, vorzugsweise ≤ 20 Å, gebildeten Mikroporenvolumenanteil von mindestens 60%, insbesondere mindestens 65%, bevorzugt mindestens 70%, bezogen auf das Gesamtporenvolumen, eingesetzt.Especially is more preferred in accordance with the invention Make an activated carbon with one of pores with pore diameters of ≦ 25 Å, preferably ≦ 20 Å Micropore volume fraction of at least 60%, in particular at least 65%, preferably at least 70%, based on the total pore volume, used.

Eine erfindungsgemäß bevorzugt eingesetzte Aktivkohle weist ein Mikroporenvolumen, d. h. ein aus Poren mit Porendurchmessern von ≤ 25 Å, vorzugsweise ≤ 20 Å, gebildetes Mikroporenvolumen, nach Carbon Black von mindestens 0,40 cm³/g, insbesondere mindestens 0,45 cm³/g, vorzugsweise mindestens 0,50 cm³/g, auf. Im allgemeinen liegt dieses Mikroporenvolumen nach Carbon Black im Bereich von 0,40 bis 0,80 cm³/g, insbesondere 0,45 bis 0,75 cm³/g, vorzugsweise 0,50 bis 0,60 cm³/g.An activated carbon preferably used according to the invention has a micropore volume, ie a micropore volume formed from pores with pore diameters of ≦ 25 Å, preferably ≦ 20 Å, after carbon black of at least 0.40 cm ³ / g, in particular at least 0.45 cm ³ / g , preferably at least 0.50 cm ³ / g, on. In general, this micro pore volume after carbon black is in the range of 0.40 to 0.80 cm ³ / g, in particular 0.45 to 0.75 cm ³ / g, preferably 0.50 to 0.60 cm ³ / g.

Zu weiteren Einzelheiten der Bestimmung der Porenoberfläche nach Carbon Black kann beispielsweise verwiesen werden auf R. W. Magee, Evaluation of the External Surface Area of Carbon Black by Nitrogene Adsorption, Presented at the Meeting of the Rubber Division of the American Chem. Soc., Oktober 1994, z. B. referiert in: Quantachrome Instruments, AUTOSORB-1 AS1 WinVersion 1.50, Operating Manual, P/N 05061, Quantachrome Instruments 2004, Florida, USA, Seiten 71 ff.To further details of the determination of the pore surface after For example, Carbon Black may be referred to R.W. Magee, Evaluation of the External Surface Area of Carbon Black by Nitrogen Adsorption, Presented at the Meeting of the Rubber Division of the American Chem. Soc., October 1994, z. B. Referred to: Quantachrome Instruments, AUTOSORB-1 AS1 WinVersion 1.50, Operating Manual, P / N 05061, Quantachrome Instruments 2004, Florida, USA, pages 71 ff.

Aufgrund der hohen Mikroporosität der erfindungsgemäß bevorzugt eingesetzten Aktivkohle weist diese gleichermaßen einen hohen spezifischen Mikroporenoberflächenanteil auf. Der spezifische Mikroporenoberflächenanteil, d. h. der Oberflächenanteil, der auf Poren mit Porendurchmessern von ≤ 25 Å, vorzugsweise ≤ 20 Å, zurückgeht beträgt mindestens 70%, insbesondere mindestens 75%, bevorzugt mindestens 80%, ganz besonders bevorzugt mindestens 85%, bezogen auf die spezifische Gesamtoberfläche (BET) der Aktivkohle. Insbesondere liegt dieser Mikroporenoberflächenanteil im Bereich von 70 bis 95%, insbesondere 75 bis 95%, vorzugsweise 80 bis 90%.by virtue of the high microporosity the invention preferred used activated carbon, this also has a high specific micropore surface area on. The specific micropore surface area, i. H. the surface fraction, which is due to pores with pore diameters of ≦ 25 Å, preferably ≦ 20 Å, is at least 70%, in particular at least 75%, preferably at least 80%, completely particularly preferably at least 85%, based on the specific total surface (BET) of the activated carbon. In particular, this microporous surface fraction is in the range of 70 to 95%, especially 75 to 95%, preferably 80 to 90%.

Die erfindungsgemäß bevorzugt eingesetzte Aktivkohle weist aufgrund ihrer Mikroporosität gleichermaßen eine große Mikroporenoberfläche auf. Insbesondere liegt die Mikroporenoberfläche nach Carbon Black (d. h. die aus Poren mit Porendurchmessern von ≤ 25 Å, vorzugsweise ≤ 20 Å, gebildete Mikroporenoberfläche) bei mindestens 400 g/m², insbesondere mindestens 800 g/m², vorzugsweise mindestens 1.000 g/m², besonders bevorzugt mindestens 1.200 g/m². Gemäß einer bevorzugten Ausführungsform liegt diese Mikroporenoberfläche im Bereich von 400 bis 1.750 g/m², insbesondere 800 bis 1.500 g/m², vorzugsweise 1.000 bis 1.400 g/m², besonders bevorzugt 1.100 bis 1.300 g/m².The activated carbon preferably used according to the invention likewise has a large micropore surface due to its microporosity. In particular, the microporous surface after carbon black (ie the microporous surface formed from pores with pore diameters of ≦ 25 Å, preferably ≦ 20 Å) is at least 400 g / m ² , in particular at least 800 g / m ² , preferably at least 1000 g / m ² , more preferably at least 1,200 g / m ² . According to a preferred embodiment, this microporous surface lies in the Be ranging from 400 to 1750 g / m ² , in particular 800 to 1500 g / m ² , preferably 1000 to 1400 g / m ² , particularly preferably 1100 to 1300 g / m ² .

Erfindungsgemäß bevorzugt wird als Aktivkohle eine mikroporöse Aktivkohle mit einem mittleren Porendurchmesser (Durchschnittsporendurchmesser) von höchstens 35 Å, vorzugsweise höchstens 30 Å, besonders bevorzugt höchstens 25 Å, eingesetzt. Insbesondere liegt dieser mittlere Porendurchmesser im Bereich von 15 bis 35 Å, insbesondere 15 bis 30 Å, vorzugsweise 15 bis 25 Å.According to the invention preferred is activated carbon as a microporous activated carbon with a medium Pore diameter (average pore diameter) of at most 35 Å, preferably at most 30 Å, most preferably at most 25 Å, used. In particular, this average pore diameter is in the range of 15 to 35 Å, in particular 15 to 30 Å, preferably 15 to 25 Å.

Was die Dichte der erfindungsgemäß bevorzugt eingesetzten Aktivkohle anbelangt, so liegt die Rohdichte der eingesetzten Aktivkohle im allgemeinen im Bereich von 700 bis 975 g/cm³, insbesondere 750 bis 950 g/cm³, vorzugsweise 800 bis 900 g/cm³. Die Schüttdichte der eingesetzten Aktivkohle liegt dagegen im Bereich von 300 bis 900 g/cm³, insbesondere 350 bis 800 g/cm³, vorzugsweise 400 bis 750 g/cm³.As far as the density of the activated carbon preferably used according to the invention is concerned, the apparent density of the activated carbon used is generally in the range from 700 to 975 g / cm ³ , in particular from 750 to 950 g / cm ³ , preferably from 800 to 900 g / cm ³ . By contrast, the bulk density of the activated carbon used is in the range from 300 to 900 g / cm ³ , in particular 350 to 800 g / cm ³ , preferably 400 to 750 g / cm ³ .

Für eine besonders gute Effizienz ist es von Vorteil, wenn die eingesetzte Aktivkohle eine Gesamtporosität von 40 bis 70%, insbesondere 45 bis 65%, vorzugsweise 50 bis 60%, aufweist.For a special good efficiency it is beneficial if the activated carbon used a total porosity from 40 to 70%, in particular 45 to 65%, preferably 50 to 60%, having.

Erfindungsgemäß bevorzugt wird als Aktivkohle eine Aktivkohle mit einem spezifischen Gesamtporenvolumen im Bereich von 0,1 bis 2,5 cm³/g, insbesondere 0,2 bis 2,0 cm³/g, vorzugsweise 0,3 bis 1,5 cm³/g, besonders bevorzugt 0,4 bis 1,0 cm³/g, eingesetzt. Dabei liegt der Anteil an Poren mit Porendurchmessern von ≤ 36 Å bei mindestens 65%, insbesondere mindestens 70%, vorzugsweise mindestens 75%, und kann Werte bis zu 95%, insbesondere bis zu 90%, erreichen.According to the invention, the activated carbon used is preferably an activated carbon having a specific total pore volume in the range from 0.1 to 2.5 cm ³ / g, in particular from 0.2 to 2.0 cm ³ / g, preferably from 0.3 to 1.5 cm ³ / g, more preferably 0.4 to 1.0 cm ³ / g used. The proportion of pores with pore diameters of ≦ 36 Å is at least 65%, in particular at least 70%, preferably at least 75%, and may reach values of up to 95%, in particular up to 90%.

Eine erfindungsgemäß besonders geeignete Aktivkohle, welche die vorgenannten Eigenschaften und Spezifikationen erfüllt, wird beispielsweise von der Blücher GmbH, Erkrath, Deutschland, oder von der AdsorTech GmbH, Premnitz, Deutschland, vertrieben.A particularly according to the invention suitable activated carbon, which have the aforementioned properties and Specifications met, is for example from the Blücher GmbH, Erkrath, Germany, or from AdsorTech GmbH, Premnitz, Germany, distributed.

Zur Steigung der Adsorptionsleistung kann die erfindungsgemäß eingesetzte Aktivkohle mit einer Imprägnierung versehen werden. Dies ist dem Fachmann als solches bekannt.to The slope of the adsorption performance can be used according to the invention Activated carbon with an impregnation be provided. This is known to the skilled person as such.

Eine derartige Imprägnierung kann beispielsweise ausgewählt sein aus der Gruppe von

(i) Metallen, vorzugsweise Kupfer, Silber, Cadmium, Platin, Palladium, Rhodium, Zink, Quecksilber, Titan, Zirkonium, Molybdän und/oder Aluminium, insbesondere deren Ionen und/oder Salzen;
(ii) Enzymen;
(iii) basischen Verbindungen, insbesondere organischen Basen, wie organischen Aminen;
(iv) sauren Verbindungen, insbesondere salz- und schwefelsauren Verbindungen oder freien organischen oder anorganischen Säuren;

sowie Mischungen der vorgenannten Imprägnierungen.Such an impregnation may be selected, for example, from the group of

(i) metals, preferably copper, silver, cadmium, platinum, palladium, rhodium, zinc, mercury, titanium, zirconium, molybdenum and / or aluminum, in particular their ions and / or salts;
(ii) enzymes;
(iii) basic compounds, especially organic bases, such as organic amines;
(iv) acidic compounds, in particular hydrochloric and sulfuric compounds or free organic or inorganic acids;

and mixtures of the aforementioned impregnations.

Für den Fall, daß eine mit einer Imprägnierung versehene Aktivkohle verwendet wird, wird die Imprägnierung im allgemeinen in einer Menge, bezogen auf die Aktivkohle, von 0,01 bis 30 Gew.-%, vorzugsweise 0,1 bis 20 Gew.-%, besonders bevorzugt 1 bis 15 Gew.-%, ganz besonders bevorzugt 1 bis 10 Gew.-%, auf die Aktivkohle aufgebracht.In the case, that one with an impregnation activated charcoal is used, the impregnation generally in an amount, based on the activated carbon, of 0.01 to 30 wt .-%, preferably 0.1 to 20 wt .-%, particularly preferably 1 to 15 wt .-%, most preferably 1 to 10 wt .-%, to the Activated carbon applied.

Die vorgenannten Imprägnierverbindungen ermöglichen zum Teil die katalytische Zersetzung bestimmter Geruchs- und/oder Schadstoffe bzw. deren beschleunigten Abbau bzw. deren beschleunigte Adsorption.The allow the aforementioned impregnation partly the catalytic decomposition of certain odor and / or Pollutants or their accelerated degradation or their accelerated Adsorption.

Das zuvor beschriebene erfindungsgemäße Baumaterial eignet sich insbesondere zu Zwecken der Verwendung zur Beseitigung von Schad- und/oder Geruchsstoffen bzw. zur Beseitigung von Emissionen von Schad- und/oder Geruchsstoffen, insbesondere mittels Adsorption, vorzugsweise in Gebäuden.The previously described building material according to the invention is particularly suitable for purposes of use for disposal of pollutants and / or odors or to eliminate emissions of pollutants and / or odors, in particular by means of adsorption, preferably in buildings.

Die Beseitigung der Emissionen von Schad- und/oder Geruchsstoffen kann zu Zwecken der Entfernung von Schad- und/oder Geruchsstoffen in schad- und/oder geruchsstoffbelasteten Räumen, zu Zwecken der Sanierung schad- und/oder geruchsstoffbelasteter Räume oder zu Zwecken der Raumluftverbesserung bzw. zur Verbesserung des Raumklimas erfolgen. Sie kann aber auch zu Zwecken des Bautenschutzes erfolgen, insbesondere zu Verhinderung der Kontaminierung eines Bauwerks mit in die Raumluft abgegebenen Schad- und/oder Giftstoffen (z. B. bei chemischen Reinigungsbetrieben, chemischen Anlagen, Laboratorien etc.).The Elimination of emissions of pollutants and / or odors may for the purpose of removing pollutants and / or odors in harmful and / or odorous substances rooms for the purposes of renovation damage and / or Odor-contaminated rooms or for the purpose of improving indoor air quality or improving the Room climate done. But it can also for purposes of building protection be carried out, in particular to prevent the contamination of a Building with pollutants and / or toxic substances released into the room air (eg chemical Cleaning plants, chemical plants, laboratories etc.).

Im Rahmen der Verwendung des erfindungsgemäßen Baumaterials wird für den Fall der Entfernung von Schad- und/oder Geruchsstoffen in schad- und/oder geruchsstoffbelasteten Räumen, insbesondere zu Zwecken der Sanierung, die Schad- und/oder geruchsstofffreisetzende Emissionsquelle mit dem erfindungsgemäßen plattenförmigen Werkstoff bzw. mit der erfindungsgemäßen Bauplatte, vorzugsweise mit einer mit Aktivkohle versehenen und/oder beaufschlagten Oberfläche des plattenförmigen Werkstoffs bzw. der Bauplatte, abgedeckt und/oder bedeckt.in the Frame of use of the building material according to the invention is for the case the removal of pollutants and / or odors in harmful and / or odorous substances rooms in particular for sanitation purposes, pollutants and / or odoriferous substances Emission source with the plate-shaped material according to the invention or with the building board according to the invention, preferably with an activated carbon provided and / or acted upon surface of the plate-shaped Material or the building board, covered and / or covered.

Für den Fall, daß das erfindungsgemäße Baumaterial zur Verbesserung der Raumluftverbesserung, beispielsweise zur Entfernung von Schad- und/oder Geruchsstoffen aus der Raumluft (z. B. Tabakrauch), oder aber zu Zwecken des Bautenschutzes eingesetzt wird, wird eine mit Aktivkohle versehene und/oder beaufschlagte Oberfläche des plattenförmigen Werkstoffs der Raumseite zugewandt.In the event that the building material according to the invention for improving the indoor air improvement, for example, for the removal of pollutants and / or odors from the room air (eg tobacco smoke), or for purposes of building protection zes is used, a provided with activated carbon and / or applied surface of the plate-shaped material facing the room side.

Gleichermaßen ist es möglich für den Fall, daß beide Oberflächen des plattenförmigen Werkstoffs mit Aktivkohle beaufschlagt bzw. versehen sind, daß gleichzeitig die Emissionsquelle von Schad- und/oder Geruchsstoffen einerseits bedeckt ist und andererseits auch eine Oberfläche des plattenförmigen Werkstoffs der Raumseite zugewandt ist.Equally is it possible for the Case, that both surfaces of the plate-shaped Material acted upon or provided with activated carbon, that at the same time the emission source of pollutants and / or odors on the one hand is covered and on the other hand, a surface of the plate-shaped material facing the room side.

Im Ergebnis ermöglicht die vorliegende Erfindung somit eine effiziente Beseitigung von Schad- und/oder Geruchsstoffen in Gebäuden bzw. Innenräumen. Die erfindungsgemäßen, für den Trockenbau geeigneten Plattenmaterialien, beispielsweise Gipsplatten, werden mit Adsorbentien auf Aktivkohlebasis versehen, um eine gute Schutzwirkung zu erreichen. So können beispielsweise Giftstoffe, die aus der Wand in den Raum entweichen (z. B. PCB, PCP, Formaldehyd etc.) wirksam entfernt werden. Auch Giftstoffe, die aus dem Raum in das Gemäuer eindringen können (Stichwort: "Bautenschutz"), wie z. B. Isocyanate, können wirksam entfernt werden. Zusätzlich kann durch die Filtrationswirkung der eingesetzten Aktivkohle eine Raumluftverbesserung bzw. eine Verbesserung des Raumklimas erreicht werden.in the Result enabled the present invention thus provides an efficient elimination of Harmful and / or odorous substances in buildings or interiors. The according to the invention, for drywall suitable plate materials, for example plasterboard provided with adsorbents based on activated charcoal, to provide a good protective effect to reach. So can For example, toxins that escape from the wall into the room (eg PCB, PCP, formaldehyde etc.) are effectively removed. Also toxins, from the room into the walls can penetrate (Keyword: "Bautenschutz"), such. For example isocyanates, can effectively removed. additionally can by the filtration effect of the activated carbon used Room air improvement or an improvement of the indoor climate achieved become.

Weitere Ausgestaltungen, Abwandlungen und Variationen der vorliegenden Erfindung sind für den Fachmann beim Lesen der Beschreibung ohne weiteres erkennbar und realisierbar, ohne daß er dabei den Rahmen der vorliegenden Erfindung verläßt.Further Embodiments, modifications and variations of the present invention are for the Person skilled in the reading of the description readily apparent and realizable without him while leaving the scope of the present invention.

Die vorliegende Erfindung wird nachfolgend anhand von Ausführungsbeispielen veranschaulicht, welche die vorliegende Erfindung jedoch keinesfalls beschränken.The The present invention will now be described with reference to exemplary embodiments however, which by no means limit the present invention.

Ausführungsbeispiele:EXAMPLES

Ausführungsbeispiel 1:Embodiment 1

Die Innenwände eines Fertigelementgebäudes, die durch langjährige Beaufschlagung mit PCB-belasteter Raumluft kontaminiert waren, wurden vollständig mit erfindungsgemäßen Gipsbauplatten beaufschlagt, auf deren zur Wand weisenden Oberfläche Aktivkohlekügelchen (mittlerer Durchmesser: 0,8 mm) in einer Auflagemenge von ca. 200 g/m² bei der Herstellung der Gipsplatten eingedrückt waren (freie Oberfläche der Aktivkohlekügelchen: mindestens 50%, BET-Oberfläche: ca. 1.225 g/m², Adsorptionsvolumen Vads: ca. 700 cm³/g; Mikroporenvolumenanteil ≥ 65%; Gesamtporenvolumen nach Gurvich ≥ 0,70 cm³/g; spezifischer Mikroporenoberflächenanteil ≥ 85%; Mikroporenoberfläche nach Carbon Black: ca. 1.250 g/m²; mittlerer Porendurchmesser: < 25 Å; Gesamtporosität: ca. 55%; Berstdruck pro Aktivkohlekugel: ca. 10 Newton).The inner walls of a prefabricated building, which were contaminated by long-term exposure to PCB-contaminated room air, were completely loaded with gypsum plasterboards according to the invention, on their wall-facing surface activated carbon beads (average diameter: 0.8 mm) in a total amount of about 200 g / m ² were pressed in during the production of the gypsum plasterboard (free surface of the activated carbon beads: at least 50%, BET surface area: about 1,225 g / m ² , adsorption volume Vads: about 700 cm ³ / g, micropore volume fraction ≥ 65%, total pore volume according to Gurvich ≥ 0.70 cm ³ / g; specific micropore surface area ≥ 85%; microporous surface after carbon black: about 1250 g / m ² ; mean pore diameter: <25 Å; total porosity: about 55%; bursting pressure per activated carbon ball: about 10 Newton) ,

Die mit Aktivkohle beaufschlagte Oberfläche der Bauplatten wurde zur Wandseite hin angeordnet. Nach Anbringung der erfindungsgemäßen Bauplatten sank die PCB-Raumluftkonzentration von ca. 11.500 ng/m³ auf unter 250 ng/m³ und blieb auch in der Folgezeit (Beobachtungszeitraum: 6 Monate) unter diesem Wert.The treated with activated carbon surface of the building panels was arranged to the wall side. After attachment of the construction boards according to the invention, the PCB indoor air concentration of about 11,500 ng / m ³ dropped to below 250 ng / m ³ and remained in the subsequent period (observation period: 6 months) below this value.

Ausführungsbeispiel 2:Embodiment 2:

Die zuvor beschriebenen Gipsbauplatten nach der vorliegenden Erfindung wurden in einem Raum mit Normalklima ausgelegt, wobei auf 1 m³ Raumvolumen ca. 1,2 m² Gipsplattenfläche kam.The gypsum board according to the present invention described above were laid out in a room with normal climatic conditions, with approximately 1.2 m ^{2 of} gypsum plasterboard surface per 1 m ³ volume of space.

Als Vergleichsgipsbauplatten dienten handelsübliche Gipsbauplatten (Fa. Knauf Gips KG) mit ca. 10 Gew.-% natürlichen Zeolithen (nativ, nicht entwässert) mit einer Korngröße von maximal 200 μm und einem d₅₀-Wert von ca. 40 μm (ebenfalls ca. 1,2 m² Gipsplattenfläche auf 1 m³ Raumvolumen).Commercially available gypsum plasterboards (Knauf Gips KG) with approximately 10% by weight of natural zeolites (native, not dehydrated) with a particle size of at most 200 μm and a d ₅₀ value of approximately 40 μm (also approx. 1.2 m ² plasterboard area to 1 m ³ volume).

In den jeweiligen Räumen wurde durch kontinuierliche Zuführung eines definierten Schadstoffgemisches die jeweilige Schadstoffkonzentration mit den Schadstoffen Formaldehyd und Benzol sowie mit einem Schadstoffgemisch aus Zigarettenrauch eingestellt. Die Luftwechselrate des jeweiligen Gemisches betrugt 0,5 Wechsel/Stunde, so daß das Schadstoffgemisch innerhalb von zwei Stunden komplett ausgetauscht wurde. In dem ausströmenden Schadstoffgemisch wurde der verbleibende Schadstoffwert als Gaskonzentration gemessen.In the respective rooms was by continuous feed a defined pollutant mixture the respective pollutant concentration with the pollutants formaldehyde and benzene and with a pollutant mixture set from cigarette smoke. The air exchange rate of each Mixture was 0.5 changes / hour, so that the pollutant mixture within two hours was completely replaced. In the effluent pollutant mixture the remaining pollutant value was measured as gas concentration.

Durch den Kontakt mit den Bauplatten wurden die Schadstoffe teilweise abgebaut bzw. entfernt, und es stellte sich in dem System eine Schadstoffkonzentration vom Ausgangswert (Einströmungsgemisch) zum Gleichgewichtswert (ausströmendes Gemisch) ein.By the contact with the building boards, the pollutants were partially degraded or removed, and it was in the system a pollutant concentration from the initial value (inflow mixture) to the equilibrium value (outflowing Mixture).

Während bei den Vergleichbauplatten mit den Zeolithen der Formaldehydgehalt von ca. 600 μg/m³ auf ca. 100 μg/m³ und der Benzolgehalt von ca. 45 μg/m³ auf ca. 10 μg/m³ gesenkt werden konnte, konnte er bei den erfindungsgemäßen Bauplatten deutlich stärker gesenkt werden, und zwar im Falle von Formaldehyd von ca. 600 μg/m³ auf ca. 50 μg/m³ und im Fall von Benzol von ca. 45 μg/m³ auf ca. 4 μg/m³.While it was possible to reduce the formaldehyde content of the comparison structural plates with the zeolites from about 600 μg / m ³ to about 100 μg / m ³ and the benzene content from about 45 μg / m ³ to about 10 μg / m ³ in the case of formaldehyde from about 600 μg / m ³ to about 50 μg / m ³ and in the case of benzene from about 45 μg / m ³ to about 4 μg / m ³ .

Bei dem eingeströmten Zigarettenrauch wurde in beiden Fällen eine wesentliche Reduzierung der Geruchsbelästigung durch den Kontakt des Rauches mit den Gipsbauplatten durch Olfaktometrie nachgewiesen, wobei im Fall der erfindungsgemäßen Bauplatten dieser Effekt stärker als im Fall der Vergleichsbauplatten war.In the case of the cigarette smoke which has flowed in, in both cases a substantial reduction in the odor nuisance due to the contact of the smoke with the gypsum plasterboards was detected by olfactometry, in the case of the structural panels according to the invention this effect being stronger than in the case of Comparative building panels was.

Die zuvor geschilderten Ergebnisse belegen, daß die Entfernung von Schad- und/oder Geruchsstoffen durch die erfindungsgemäß vorgesehene Aktivkohle gegenüber handelsüblichen Bauplatten mit Zeolithen deutlich gesteigert werden kann. Dies belegt die Überlegenheit der erfindungsgemäßen Bauplatten gegenüber Bauplatten des Standes der Technik.The previously described results prove that the removal of pollutants and / or odors by the invention provided Activated carbon opposite commercial Building boards with zeolites can be significantly increased. This is proven the superiority the structural panels according to the invention across from Construction panels of the prior art.

Ausführungsbeispiel 3:Embodiment 3

Ausführungsbeispiel 2 wurde wiederholt, jedoch wurde in Abweichung zu der in Ausführungsbeispiel 2 anstelle der mikroporösen Aktivkohle eine Aktivkohle mit geringerem Mikroporenanteil und folglich höherem Meso- und Makroporenanteil (mittlerer Durchmesser der Aktivkohlekugeln: 0,8 mm; freie Oberfläche der Aktivkohlekügelchen: mindestens 50%; BET-Oberfläche: ca. 1.200 g/m²; Adsorptionsvolumen V_ads: ca. 680 cm³/g; Mikroporenvolumenanteil < 40%; spezifischer Mikroporenoberflächenanteil < 30%; mittlerer Porendurchmesser: > 40 Å; Gesamtporosität: ca. 45%).Embodiment 2 was repeated except that instead of the microporous activated carbon in Example 2, an activated carbon having a smaller micropore content and consequently a higher meso and macroporous fraction (mean diameter of the activated carbon spheres: 0.8 mm, free surface of the activated carbon beads: at least 50%; BET surface area: about 1200 g / m ^2; adsorption volume V _ads: about 680 cm ³ / g; micro pore volume fraction <40%; specific micropore surface fraction <30%; average pore diameter:> 40 Å; total porosity: about 45%).

Der Formaldehydgehalt konnte von ca. 600 μg/m³ auf ca. 75 μg/m³ und der Benzolgehalt von ca. 45 μg/m³ auf ca. 8 μg/m³ gesenkt werden. Die erfindungsgemäßen Bauplatten mit der meso-/makroporösen Aktivkohle sind somit gegenüber den zeolithhaltigen Bauplatten des Standes der Technik deutlich effizienter, aber weniger effizient als im Fall der Verwendung mikroporöser Aktivkohle – und dies bei im übrigen im wesentlichen gleichen Parametern mit Ausnahme der Mikroporosität. Durch die Auswahl einer Aktivkohle hoher Mikroporosität läßt sich überraschenderweise die Effizienz deutlich steigern.The formaldehyde content could be reduced from approx. 600 μg / m ³ to approx. 75 μg / m ³ and the benzene content from approx. 45 μg / m ³ to approx. 8 μg / m ³ . The building boards according to the invention with the meso / macroporous activated carbon are thus significantly more efficient than the zeolite-containing building boards of the prior art, but less efficient than in the case of using microporous activated carbon - with otherwise substantially identical parameters with the exception of microporosity. By selecting an activated carbon of high microporosity, surprisingly, the efficiency can be significantly increased.

Auch in bezug auf die meso-/makroporöse Aktivkohle wurde bei dem eingeströmten Zigarettenrauch eine wesentliche Reduzierung der Geruchsbelästigung durch Olfaktometrie nachgewiesen.Also with respect to the meso / macroporous activated carbon was at the streamed Cigarette smoke a significant reduction in odor nuisance detected by olfactometry.

Claims

Building material for interior construction based on a plate-shaped material for dry construction, characterized in that the plate-shaped material has activated carbon.

Building material according to claim 1, characterized that this disc-shaped Material is a building board, in particular a building board made of plaster, from Gypsum plasterboard, of gypsum fiber composite materials, such as gypsum fiber board, cement fiber composite, such as fiber cement board, glass fiber, of carbon fibers, of wood, of wood fibers, of plastic or the like and combination thereof, preferably a gypsum board or a plasterboard, in particular a plasterboard with one- or two-sided cardboard outer coating and a gypsum core layer.

Building material according to claim 1 and / or 2, characterized that the Activated carbon in the plate-shaped Material is incorporated in its production.

Building material according to claim 1 and / or 2, characterized that the disc-shaped Material on at least one of its two surfaces with Activated carbon is provided and / or acted upon.

Building material according to claim 4, characterized that the Activated carbon on the surface (s) of the plate-shaped material fixed, in particular by means of a preferably punctiform and / or dot grid pattern applied adhesive or by incorporation, in particular impressions, in the surface (s) the plate-shaped material during its production.

Building material according to claim 4 or 5, characterized that the Fixation of the activated carbon is such that at least 25%, in particular at least 30%, preferably at least 40%, more preferably at least 50%, the surface of the Activated carbon for to be adsorbed pollutants and / or odors is freely available.

Building material according to claim 1 and / or 2, characterized that the Activated carbon on a preferably flat carrier, in particular a textile or paper sheets, preferably a paper, a cardboard, a cardboard or the like, is fixed and provided with activated carbon carrier with the plate-shaped material is connected, in particular by means of lamination, gluing or like.

Building material according to one or more of the preceding Claims, characterized in that the Amount of activated carbon is designed such that through the activated carbon provided adsorption capacity is sufficient in order to use the disc-shaped Material originating from the environment emissions of harmful and / or Permanently adsorptive bind odors and / or remove.

Building material according to one or more of the preceding claims, characterized in that the plate-shaped material, the activated carbon in an amount, in particular loading and / or Auflagemenge, of a total of 20 to 750 g / m ² , in particular 25 to 500 g / m ² , preferably 30 to 400 g / m ² , particularly preferably 50 to 300 g / m ² .

Building material according to one or more of Claims 1 to 9, characterized in that the activated carbon is powdery.

Building material according to one or more of claims 1 to 9, characterized in that the activated carbon granular, preferably spherical, formed in particular wherein the activated carbon grains, preferably activated carbon spheres, average particle diameter in the range of 0.01 to 2.0 mm, in particular 0.05 to 1.0 mm, preferably 0.1 to 1.0 mm, and / or in particular wherein the individual activated carbon grains, preferably activated carbon spheres, have a mean distance from each other, at least the Half, in particular at least three quarters, preferably at least the simple, be particularly preferably at least one and a half times, the middle Particle diameter of the activated carbon grains, preferably activated carbon beads, equivalent.

Building material according to one or more of claims 1 to 9, characterized in that the activated carbon in the form of activated carbon fibers.

Building material according to one or more of claims 1 to 9, characterized in that the activated carbon a mixture of fibrous and granular, preferably spherical, Activated carbon covers.

Building material according to one or more of the preceding claims, characterized in that the activated carbon has a specific surface area (BET) of at least 500 g / m ² , in particular at least 750 g / m ² , preferably at least 1,000 g / m ² , particularly preferably at least 1,200 g / m ² , and / or that the activated carbon has a specific surface area (BET) of 500 to 2,500 g / m ² , in particular 750 to 2,250 g / m ² , preferably 900 to 2,000 g / m ² , particularly preferably 1,000 to 1,750 g / m ² , has.

Building material according to one or more of the preceding claims, characterized in that the activated carbon is an activated carbon having an adsorption _volume V _ads of at least 250 cm ³ / g, in particular at least 300 cm ³ / g, preferably at least 350 cm ³ / g, particularly preferably at least 400 cm ³ / g, and / or that the activated carbon is an activated carbon having an adsorption _volume V _ads of 250 to 1000 cm ³ / g, in particular 300 to 900 cm ³ / g, preferably 350 to 750 cm ³ / g.

Building material according to one or more of the preceding claims, characterized in that the activated carbon comprises an activated carbon having a total pore volume according to Gurvich of at least 0.50 cm ³ / g, in particular at least 0.55 cm ³ / g, preferably at least 0.60 cm ³ / g, particularly preferably at least 0.65 cm ³ / g, very particularly preferably at least 0.70 cm ³ / g, and / or that the activated carbon is an activated carbon having a total pore volume according to Gurvich of 0.50 to 0.90 cm ³ / g, in particular 0.55 to 0.85 cm ³ / g, preferably 0.60 to 0.80 cm ³ / g, particularly preferably 0.65 to 0.80 cm ³ / g, most preferably 0.70 to 0 , 75 cm ³ / g, is.

Building material according to one or more of the preceding Claims, characterized in that the Activated carbon an activated carbon with a large micropore volume fraction, based on the total pore volume of the activated carbon, is and / or that the Activated carbon an activated carbon with a proportion of the microporous volume, based on the total pore volume of the activated carbon, of at least 60%, in particular at least 65%, preferably at least 70%.

Building material according to one or more of the preceding Claims, characterized in that the Activated carbon an activated carbon with one of pores with pore diameters of ≦ 25 Å, preferably ≦ 20 Å Micropore volume fraction of at least 60%, in particular at least 65%, preferably at least 70%, based on the total pore volume, is.

Building material according to one or more of the preceding claims, characterized in that the activated carbon comprises an activated carbon having a micropore volume, in particular a micropore volume formed from pores with pore diameters of ≤ 25 Å, preferably ≤ 20 Å, after carbon black of at least 0.40 cm ³ / g, in particular at least 0.45 cm ³ / g, preferably at least 0.50 cm ³ / g.

Building material according to one or more of the preceding Claims, characterized in that the Activated carbon an activated carbon with a specific micropore surface fraction, in particular one formed from pores with pore diameters of ≤ 25 Å, preferably ≤ 20 Å specific micropore surface fraction, of at least 70%, in particular at least 75%, preferably at least 80%, especially at least 85%, relative to the specific one total surface (BET) of the activated carbon, is.

Building material according to one or more of the preceding claims, characterized in that the activated carbon comprises an activated carbon having a micro pore surface according to carbon black, in particular a micro pore surface formed of pores with pore diameters of ≤ 25 Å, preferably ≤ 20 Å, of at least 400 g / m ² , in particular at least 800 g / m ² , preferably at least 1,000 g / m ² , more preferably at least 1,200 g / m ² , is.

Building material according to one or more of the preceding Claims, characterized in that the Activated carbon an activated carbon with a mean pore diameter (Average pore diameter) of at most 35 Å, preferably at most 30 Å, most preferably at most 25 Å, is.

Building material according to one or more of the preceding claims, characterized in that the activated carbon comprises an activated carbon having a density in the range from 700 to 975 g / cm ³ , in particular 750 to 950 g / cm ³ , preferably 800 to 900 g / cm ³ , and / or with a bulk density in the range of 300 to 900 g / cm ³ , in particular 350 to 800 g / cm ³ , preferably 400 to 750 g / cm ³ and / or with a total porosity of 40 to 70%, in particular 45 to 65 %, preferably 50 to 60%.

Building material according to one or more of the preceding claims, characterized in that the activated carbon comprises an activated carbon having a specific total pore volume in the range of 0.1 to 2.5 cm ³ / g, in particular 0.2 to 2.0 cm ³ / g, preferably 0.3 to 1.5 cm ³ / g, particularly preferably 0.4 to 1.0 cm ³ / g, in particular wherein the proportion of pores with pore diameters of ≤ 36 Å at least 65%, in particular at least 70%, preferably at least 75%, and up to 95%, in particular up to 90%.

Building material according to one or more of the preceding Claims, characterized in that the Activated carbon an impregnation having.

Building material according to claim 25, characterized that the impregnation selected is the group of (i) metals, preferably copper, silver, cadmium, Platinum, palladium, rhodium, zinc, mercury, titanium, zirconium, molybdenum and / or aluminum, in particular their ions and / or salts; (Ii) enzymes; (iii) basic compounds, especially organic ones Bases, such as organic amines; (iv) acidic compounds, especially salt and sulfuric acid compounds or free organic or inorganic acids; as well as their mixtures and / or combination.

Building material according to claim 25 and / or 26, characterized characterized in that Impregnation, based on the activated carbon, in an amount of 0.01 to 30 wt .-%, preferably 0.1 to 20% by weight, particularly preferably 1 to 15% by weight, most preferably 1 to 10 wt .-%, applied to the activated carbon is.