DE19936464B4 - Colored coating - Google Patents

Colored coating Download PDF

Info

Publication number
DE19936464B4
DE19936464B4 DE19936464A DE19936464A DE19936464B4 DE 19936464 B4 DE19936464 B4 DE 19936464B4 DE 19936464 A DE19936464 A DE 19936464A DE 19936464 A DE19936464 A DE 19936464A DE 19936464 B4 DE19936464 B4 DE 19936464B4
Authority
DE
Germany
Prior art keywords
transparent
color
colored coating
transparent particles
particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE19936464A
Other languages
German (de)
Other versions
DE19936464A1 (en
Inventor
Andreas Dr. Drechsler
Daniel Dr. Neupert
Silke Peil
Guido Dr. Schermann
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Monier Roofing GmbH
Original Assignee
Lafarge Braas GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lafarge Braas GmbH filed Critical Lafarge Braas GmbH
Priority to DE19936464A priority Critical patent/DE19936464B4/en
Priority to AT0125100A priority patent/AT412357B/en
Priority to NL1015865A priority patent/NL1015865C2/en
Publication of DE19936464A1 publication Critical patent/DE19936464A1/en
Application granted granted Critical
Publication of DE19936464B4 publication Critical patent/DE19936464B4/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

Die Erfindung betrifft eine farbige Beschichtung für insbesondere ein plattenförmiges Bauelement (12). DOLLAR A Um die Oberfläche des plattenförmigen Bauelements (12) so zu beschichten, daß dieses in Abhängigkeit vom Blickwinkel eine unterschiedliche Farbe zeigt, wird vorgeschlagen, daß die Oberfläche des plattenförmigen Bauelements (12) eine durchsichtige Partikel (18) enthaltende Beschichtung aus einem transparenten Lack (16) mit einer anderen Farbe als der Farbe der Oberfläche aufweist, wobei der mit einer Monolage der durchsichtigen Partikel (18) beschichtete Anteil der Oberfläche kleiner ist als die gesamte beschichtete Oberfläche und daß die Schichtdicke des transparenten Lackes (16) geringer ist als die Dicke der durchsichtigen Partikel (18).The invention relates to a colored coating for in particular a plate-shaped component (12). DOLLAR A in order to coat the surface of the plate-shaped component (12) so that this shows a different color depending on the viewing angle, it is proposed that the surface of the plate-shaped component (12) comprises a transparent particles (18) containing coating of a transparent lacquer (16) having a different color than the color of the surface, wherein the monolayer of the transparent particles (18) coated portion of the surface is smaller than the entire coated surface and that the layer thickness of the transparent varnish (16) is less than that Thickness of the transparent particles (18).

Description

Die Erfindung betrifft eine farbige Beschichtung für insbesondere ein plattenförmiges Bauelement wie eine Wandverkleidungsplatte, eine Fliese, eine Kachel oder eine Dacheindeckungsplatte.The The invention relates to a colored coating for a particular plate-shaped component like a wallcovering panel, tile, tile or one Roofing plate.

Aus der EP 0 713 557 B1 sind zweifarbige Betondachsteine bekannt, die in zwei nebeneinander liegenden Abschnitten unterschiedlich eingefärbte Oberflächen aufweisen. Eine mehr rustikal wirkende Einfärbung von Betondachsteinen mit mehrfarbig wechselnden streifenförmigen Bereichen ist aus der WO 97/02124 bekannt. Dabei werden der Rohbetonmasse in zufälligem Wechsel drei verschiedene Farben zugesetzt, die nicht vollständig miteinander vermischt werden, so daß sich unterschiedlich eingefärbte Oberflächenbereiche ergeben. Bei den vorstehend genannten Betondachsteinen ist die Farbe im wesentlichen unabhängig vom Blickwinkel, dem Winkel zwischen der Blickrichtung und der Oberfläche des Betondachsteins.From the EP 0 713 557 B1 Two-tone concrete roof tiles are known which have differently colored surfaces in two adjacent sections. A more rustic-looking coloring of concrete roof tiles with multicolored alternating strip-shaped areas is known from WO 97/02124. In this case, the raw concrete mass in random change three different colors are added, which are not completely mixed together, so that there are different colored surface areas. In the concrete roof tiles mentioned above, the color is substantially independent of the viewing angle, the angle between the viewing direction and the surface of the concrete roof tile.

Weiterhin ist eine reflektierende Beschichtung bekannt, bei der in einem transparenten Lack durchsichtige Glaskugeln mit einem Durchmesser von 10 bis 50 μm eingebettet sind ( US 2 963 378 ). Diese Glaskugeln weisen auf einer Hemisphäre eine reflektierende metallische Beschichtung auf, sodass sie stark reflektierend und nicht durchsichtig sind.Furthermore, a reflective coating is known in which transparent glass beads with a diameter of 10 to 50 μm are embedded in a transparent lacquer ( US 2,963,378 ). These glass spheres have a reflective metallic coating on a hemisphere, making them highly reflective and non-translucent.

Bei einer bekannten lichtreflektierenden Folie liegen auf deren Oberfläche Glaskugeln so dicht nebeneinander, dass sie die gesamte Oberfläche bedecken ( US 2 354 018 ). Es ist somit kein Raum für eine Lackschicht, die auf der Folie angeordnet und auch sichtbar ist.In a known light-reflecting film, glass spheres lie on their surface so close to each other that they cover the entire surface ( US 2,354,018 ). There is thus no room for a lacquer layer which is arranged on the foil and also visible.

Schließlich ist auch noch eine Beschichtung bekannt, die transparente sphärische Glasperlen enthält, die einen Durchmesser von 15 bis 75 μm sowie einen Brechungsindex von ungefähr 1,9 haben ( GB 914 413 ). Die Perlenvolumenkonzentration beträgt dabei 65 % bis 75 %. Die Glasperlen sind hierbei jedoch nicht in einen Lack eingebettet, der eine andere Farbe besitzt als die Oberfläche des Körpers, auf welchen der Lack aufgetragen wird.Finally, a coating is also known which contains transparent spherical glass beads which have a diameter of 15 to 75 μm and a refractive index of approximately 1.9 ( GB 914,413 ). The bead volume concentration is 65% to 75%. However, the glass beads are not embedded in a paint that has a different color than the surface of the body on which the paint is applied.

Aufgabe der vorliegenden Erfindung ist es, die Oberfläche eines plattenförmigen Bauelements so zu beschichten, daß dieses in Abhängigkeit vom Blickwinkel eine unterschiedliche Farbe zeigt.task The present invention is thus the surface of a plate-shaped component to coat that dependent on from the point of view shows a different color.

Die Aufgabe wird erfindungsgemäß dadurch gelöst, daß die Oberfläche des plattenförmigen Bauelements eine durchsichtige Partikel enthaltende Beschichtung aus einem transparenten Lack mit einer anderen Farbe als der Farbe der Oberfläche aufweist, wobei der mit einer Monolage der durchsichtigen Partikel beschichtete Anteil der Oberfläche kleiner ist als die. gesamte beschichtete Oberfläche und daß die Schichtdicke des transparenten Lackes geringer ist als die Dicke der durchsichtigen Partikel.The The object is achieved in that the surface of disc-shaped Component containing a transparent particles coating from a transparent varnish of a different color than the color the surface having the monolayer of the transparent particles coated portion of the surface is smaller than that. entire coated surface and that the layer thickness of the transparent Lackes is less than the thickness of the transparent particles.

Bei einem derart beschichteten Bauelement ist die Grundfarbe der Oberfläche durch die durchsichtigen Partikel hindurch sichtbar, während im Bereich der mit transparentem Lack beschichteten Fläche eine Mischfarbe aus Grundfarbe und Lackfarbe erscheint. Es versteht sich, daß die Oberfläche des plattenförmigen Bauelements eine dünne Schicht einer Grundfarbe aufweisen kann.at a component coated in this way is the basic color of the surface the transparent particles visible throughout, while in the area of transparent Paint coated surface a mixed color of base color and paint appears. It understands that the surface of the plate-shaped Component a thin Layer may have a base color.

Bei Blickrichtung in Richtung der Flächennormalen erscheint überwiegend die durch die durchsichtigen Partikel hindurch sichtbare Grundfarbe. Bei schräger Blickrichtung erscheint überwiegend die Mischfarbe, und bei flacher Blickrichtung erscheint überwiegend die Farbe des transparenten Lacks. Es entsteht also eine von der Blickrichtung abhängige changierende Farbwirkung. Insbesondere bei einem Bauelement mit profilierter Oberfläche, beispielsweise bei einer Dachpfanne mit ebenen Wasserläufen und dazwischen angeordneten gerundeten Rippen oder bei einer Dachpfanne mit wellenförmig profilierter Oberfläche, tritt die Oberflächenstruktur aufgrund des unterschiedlichen Farbeindrucks deutlich hervor.at Looking in the direction of the surface normals appears predominantly the base color visible through the transparent particles. At an angle Viewing direction appears predominantly the mixed color, and in a flat line of vision appears predominantly the color of the transparent varnish. So one of the Viewing dependent iridescent Color effect. In particular, in a component with profiled Surface, For example, in a roof tile with flat watercourses and interposed rounded ribs or a roof tile with wavy profiled surface, occurs the surface structure clearly due to the different color impression.

Je nach Wahl der Grundfarbe und der Farbe des transparenten Lacks können beliebige Farbkombinationen erzielt werden. Beispielsweise führt eine rote Grundfarbe und ein blauer transparenter Lack je nach Blickwinkel zu den unterschiedlichsten violetten Farbtönen. Eine rote Grundfarbe und ein rotbrauner transparenter Lack je nach Blickwinkel zu den unterschiedlichsten kastanienfarbenen Farbtönen Die changierende Farbwirkung der Beschichtung ist abhängig von dem mit durchsichtigen Partikeln beschichteten Anteil der Gesamtfläche. Vorteilhafterweise beträgt der mit einer Monolage der durchsichtigen Partikel beschichtete Anteil der Oberfläche zwischen 10% und 50% der gesamten Oberfläche. Es sind also in dem zur Beschichtung verwendeten transparenten Lack nur relativ wenige durchsichtige Partikel enthalten, so daß nicht mehrere durchsichtige Partikel aufeinander zu liegen kommen. Die Bildung von Agglomeraten durchsichtiger Partikel ist vom Beschichtungsverfahren abhängig. Wird die Beschichtung aufgesprüht, so soll der von mit durchsichtigen Partikeln beschichtete rechnerisch ermittelte Anteil der Gesamtfläche nicht über 50% liegen.ever You can choose any of the basic colors and the color of the transparent varnish Color combinations are achieved. For example, a red leads Basic color and a blue transparent varnish depending on the viewing angle to the most different violet colors. A red ground color and a red-brown transparent varnish depending on the angle of view to the most diverse chestnut-colored shades The iridescent color effect of the coating depends on the proportion of the total area coated with transparent particles. advantageously, is coated with a monolayer of transparent particles Proportion of the surface between 10% and 50% of the total surface. So it is in the to Coating used transparent paint only relatively few transparent particles included, so not several transparent particles come to rest on each other. The Formation of agglomerates of transparent particles is from the coating process dependent. If the coating is sprayed on, so should the coated with transparent particles computationally determined proportion of the total area no over 50% lie.

Vorzugsweise sind die durchsichtigen Partikel farblos. Es können jedoch auch eingefärbte durchsichtige Partikel eingesetzt werden, wodurch sich zusätzliche Farbeffekte ergeben.Preferably the transparent particles are colorless. However, it can also be colored transparent Particles are used, resulting in additional color effects.

Eine optimale changierende Farbwirkung wird erreicht, wenn die durchsichtigen Partikel eine im wesentlichen einheitliche Größe aufweisen. Auf diese Weise wird eine gleichmäßige nur vom Blickwinkel abhängige Farbwirkung erreicht.An optimal iridescent color effect is achieved when the transparent particles have a substantially uniform size. On In this way, a uniform color effect dependent only on the viewing angle is achieved.

Eine besonders preiswerte Beschichtung ist möglich, wenn die durchsichtigen Partikel im wesentlichen kugelförmig sind. Hier bietet sich die Verwendung von Glaskugeln bzw. Glasperlen an.A Particularly inexpensive coating is possible when the transparent Particles substantially spherical are. Here is the use of glass beads or glass beads at.

Vorteilhafterweise liegt der Durchmesser der kugelförmigen durchsichtigen Partikel im Bereich zwischen 30 μm und 500 μm. Der Durchmesser der kugelförmigen durchsichtigen Partikel soll nicht mehr als etwa das Dreifache der Dicke der ausgehärteten Lackschicht betragen. Auf diese Weise wird einerseits eine witterungsstabile Einbindung der durchsichtigen Partikel erreicht, andererseits wird nur eine dünne Lackschicht benötigt.advantageously, is the diameter of the spherical transparent particles in the range between 30 microns and 500 microns. The diameter of the spherical transparent Particles should not exceed about three times the thickness of the cured lacquer layer be. In this way, on the one hand, a weather-resistant Integration of the transparent particles achieved, on the other hand only a thin one Lacquer layer needed.

Transparente Lacke im Sinne der Erfindung sind organische oder anorganische Materialen. Organische Materialien sind Polymere, beispielsweise Acrylate oder Styrolacrylate, die als wässerige Acrylat-Dispersionen bzw wässerige Styrolacrylat-Dispersionen aufgebracht werden können. Es versteht sich, daß auch in organischen Lösungsmitteln gelöste Polymere eingesetzt werden können. Auch lösungsmittelfreie Zweikomponenetensysteme wie Polyurethane sind geeignet. Für Anwendungen, bei denen eine besonders hohe Beständigkeit gegen ultraviolette Strahlen erforderlich ist, kann der transparente Lack aus anorganischem Material bestehen. Hierzu eignen sich Systeme auf der Basis von Kieselsol oder Wasserglas besonders gut.transparent Paints according to the invention are organic or inorganic materials. Organic materials are polymers, for example acrylates or Styrene acrylates used as aqueous acrylate dispersions or watery Styrene acrylate dispersions can be applied. It is understood that also in organic solvents dissolved Polymers can be used. Also solventless Two-component systems such as polyurethanes are suitable. For applications, at which a particularly high resistance is required against ultraviolet rays, the transparent Lacquer made of inorganic material. Systems are suitable for this purpose especially good on the basis of silica sol or water glass.

Nachfolgend wird die Ausführung der Erfindung anhand von sieben Ausführungsbeispielen beschrieben.following will be the execution of the invention described with reference to seven embodiments.

Ausführungsbeispiel 1.Embodiment 1.

Auf ein plattenförmiges Bauelement, nämlich einen ausgehärteten Betondachstein mit einer ersten Farbschicht mit einer roten Grundfarbe ist nach dem Aushärten dieser ersten Farbschicht eine Beschichtung aufgebracht worden, die aus einem transparenten Lack mit darin enthaltenen durchsichtigen Partikeln bestand. Als durchsichtige Partikel wurden farblose Glaskugeln eingesetzt. Als transparenter Lack wurden 100 g einer wäßrigen Acrylatdispersion mit einem Feststoffgehalt von 40 Gew.-% eingesetzt, der 10 g einer wässrigen Pigmentsuspension mit einem Gehalt von 5 g blauem Cobalt-Spinell-Pigment zugesetzt waren. Zu 110 g dieser blau pigmentierten Acrylatdispersion wurden 15 g Glaskugeln mit einem Durchmesser von 90 μm ± 20 μm gegeben. Von der fertigen Beschichtungsmischung wurden 115 g/m2 auf den Betondachstein aufgesprüht. Nach dem Aushärten der aufgesprühten Schicht hatte sich zwischen den Glaskugeln eine Lackschicht aus transparentem Lack mit einer mittleren Dicke von etwa 30 μm gebildet, wobei infolge der Kapillarkraft die Dicke angrenzend an die Glaskugeln etwas größer ist, so daß die Glaskugeln witterungsstabil eingebunden sind. In diesem ersten Beispiel bedeckten die Glaskugeln etwa 10 % der beschichteten Oberfläche.On a plate-shaped component, namely a cured concrete roofing tile with a first color layer with a red base color, a coating has been applied after curing of this first color layer, which consisted of a transparent lacquer with transparent particles contained therein. As transparent particles, colorless glass beads were used. 100 g of an aqueous acrylate dispersion having a solids content of 40% by weight, to which 10 g of an aqueous pigment suspension containing 5 g of blue cobalt spinel pigment were added, were used as the transparent paint. To 110 g of this blue-pigmented acrylate dispersion was added 15 g of glass beads having a diameter of 90 μm ± 20 μm. 115 g / m 2 of the finished coating mixture was sprayed onto the concrete roofing tile. After curing of the sprayed layer, a lacquer layer of transparent lacquer with an average thickness of about 30 microns had formed between the glass beads, which is due to the capillary force, the thickness adjacent to the glass beads is slightly larger, so that the glass beads are integrated weather resistant. In this first example, the glass spheres covered about 10% of the coated surface.

Ausführungsbeispiel 2.Embodiment 2.

Auf einen ausgehärteten Betondachstein mit einer ersten Farbschicht mit einer roten Grundfarbe ist nach dem Aushärten dieser ersten Farbschicht eine Beschichtung aufgebracht worden, die aus einem transparenten Lack mit darin enthaltenen farblosen Glaskugeln bestand. Als transparenter Lack wurden 100 g einer wäßrigen Acrylatdispersion mit einem Feststoffgehalt von 40 Gew.-% eingesetzt, der 10 g einer wässrigen Pigmentsuspension mit einem Gehalt von 0,5 g schwarzes Eisenoxid-Pigment (Bayferrox 306) und 4,5 g rotbraune Eisenoxid-Pigment-Mischung (Bayferrox 655) zugesetzt waren. Zu 110 g dieser dunkel rotbraun pigmentierten Acrylatdispersion wurden 45 g Glaskugeln mit einem Durchmesser von 90 μm ± 20 μm gegeben. Von der fertigen Beschichtungsmischung wurden 130 g/m2 auf den Betondachstein aufgesprüht. Nach dem Aushärten der aufgesprühten Schicht hatte sich zwischen den Glaskugeln eine Lackschicht aus transparentem Lack mit einer mittleren Dicke von etwa 40 μm gebildet, wobei infolge der Kapillarkraft die Dicke angrenzend an die Glaskugeln etwas größer ist, so daß die Glaskugeln witterungsstabil eingebunden sind. In diesem zweiten Beispiel bedeckten die Glaskugeln etwa 30 % der beschichteten Oberfläche.On a cured concrete tile with a first color layer with a red base color, a coating has been applied after curing of this first color layer, which consisted of a transparent lacquer with colorless glass beads contained therein. 100 g of an aqueous acrylate dispersion having a solids content of 40% by weight and containing 10 g of an aqueous pigment suspension containing 0.5 g of black iron oxide pigment (Bayferrox 306) and 4.5 g of reddish brown iron oxide were used as the transparent paint. Pigment mixture (Bayferrox 655) were added. To 110 g of this dark red-brown pigmented acrylate dispersion was added 45 g of glass beads with a diameter of 90 μm ± 20 μm. 130 g / m 2 of the finished coating mixture were sprayed onto the concrete roofing tile. After curing of the sprayed layer, a lacquer layer of transparent lacquer with an average thickness of about 40 microns had formed between the glass beads, due to the capillary force, the thickness adjacent to the glass beads is slightly larger, so that the glass beads are integrated weather resistant. In this second example, the glass spheres covered about 30% of the coated surface.

Ausführungsbeispiel 3.Embodiment 3.

Auf einen ausgehärteten Betondachstein mit einer ersten Farbschicht mit einer roten Grundfarbe ist nach dem Aushärten dieser ersten Farbschicht eine Beschichtung aufgebracht worden, die aus einem transparenten Lack mit darin enthaltenen farblosen Glaskugeln bestand. Als transparenter Lack wurden 100 g einer wäßrigen Acrylatdispersion mit einem Feststoffgehalt von 40 Gew.-% eingesetzt, der 2 g einer wässrigen Pigmentsuspension mit einem Gehalt von 1 g blauem Cobalt-Spinell-Pigment zugesetzt waren. Zu 102 g dieser blau pigmentierten Acrylatdispersion wurden 50 g Glaskugeln mit einem Durchmesser von 90 μm ± 20 μm gegeben. Von der fertigen Beschichtungsmischung wurden 46 g/m2 auf den Betondachstein aufgesprüht. Nach dem Aushärten der aufgesprühten Schicht betrug die mittlere Dicke der transparenten Lackschicht etwa 14 μm. Die Glaskugeln bedeckten etwa 12 % der beschichteten Oberfläche.On a cured concrete tile with a first color layer with a red base color, a coating has been applied after curing of this first color layer, which consisted of a transparent lacquer with colorless glass beads contained therein. 100 g of an aqueous acrylate dispersion having a solids content of 40% by weight, to which 2 g of an aqueous pigment suspension containing 1 g of blue cobalt spinel pigment were added, were used as transparent paint. To 102 g of this blue-pigmented acrylate dispersion were added 50 g of glass beads with a diameter of 90 μm ± 20 μm. From the finished coating mixture 46 g / m 2 was sprayed onto the concrete roof tile. After curing of the sprayed layer, the average thickness of the transparent lacquer layer was about 14 microns. The glass spheres covered about 12% of the coated surface.

Ausführungsbeispiel 4.Embodiment 4.

Auf einen ausgehärteten Betondachstein mit einer ersten Farbschicht mit einer roten Grundfarbe ist nach dem Aushärten dieser ersten Farbschicht eine Beschichtung aufgebracht worden, die aus einem transparenten Lack mit darin enthaltenen farblosen Glaskugeln bestand. Als transparenter Lack wurden 100 g einer wäßrigen Acrylatdispersion mit einem Feststoffgehalt von 40 Gew.-% eingesetzt, der 2 g einer wässrigen Pigmentsuspension mit einem Gehalt von 1 g blauem Cobalt-Spinell-Pigment zugesetzt waren. Zu 102 g dieser blau pigmentierten Acrylatdispersion wurden 50 g Glaskugeln mit einem Durchmesser von 90 μm ± 20 μm gegeben. Von der fertigen Beschichtungsmischung wurden 92 g/m2 auf den Betondachstein aufgesprüht. Nach dem Aushärten der aufgesprühten Schicht betrug die mittlere Dicke der transparenten Lackschicht etwa 35 μm. Die Glaskugeln bedeckten etwa 24 % der beschichteten Oberfläche.On a hardened concrete roofing tile with a first coat of paint with a red base color After curing of this first color layer, a coating has been applied which consisted of a transparent lacquer with colorless glass spheres contained therein. 100 g of an aqueous acrylate dispersion having a solids content of 40% by weight, to which 2 g of an aqueous pigment suspension containing 1 g of blue cobalt spinel pigment were added, were used as transparent paint. To 102 g of this blue-pigmented acrylate dispersion were added 50 g of glass beads with a diameter of 90 μm ± 20 μm. 92 g / m 2 of the finished coating mixture were sprayed onto the concrete roofing tile. After curing of the sprayed layer, the average thickness of the transparent lacquer layer was about 35 microns. The glass spheres covered about 24% of the coated surface.

Ausführungsbeispiel 5.Embodiment 5.

Auf einen ausgehärteten Betondachstein mit einer ersten Farbschicht mit einer roten Grundfarbe ist nach dem Aushärten dieser ersten Farbschicht eine Beschichtung aufgebracht worden, die aus einem transparenten Lack mit darin enthaltenen farblosen Glaskugeln bestand. Als transparenter Lack wurden 100 g einer wäßrigen Acrylatdispersion mit einem Feststoffgehalt von 40 Gew.-% eingesetzt, der 2 g einer wässrigen Pigmentsuspension mit einem Gehalt von 1 g blauem Cobalt-Spinell-Pigment zugesetzt waren. Zu 102 g dieser blau pigmentierten Acrylatdispersion wurden 80 g Glaskugeln mit einem Durchmesser von 90 μm ± 20 μm gegeben. Von der fertigen Beschichtungsmischung wurden 61,5 g/m2 auf den Betondachstein aufgesprüht. Nach dem Aushärten der aufgesprühten Schicht betrug die mittlere Dicke der transparenten Lackschicht etwa 25 μm. Die Glaskugeln bedeckten etwa 25 % der beschichteten Oberfläche.On a cured concrete tile with a first color layer with a red base color, a coating has been applied after curing of this first color layer, which consisted of a transparent lacquer with colorless glass beads contained therein. 100 g of an aqueous acrylate dispersion having a solids content of 40% by weight, to which 2 g of an aqueous pigment suspension containing 1 g of blue cobalt spinel pigment were added, were used as transparent paint. To 102 g of this blue-pigmented acrylate dispersion was added 80 g of glass beads with a diameter of 90 μm ± 20 μm. Of the finished coating mixture, 61.5 g / m 2 were sprayed onto the concrete tile. After curing of the sprayed layer, the average thickness of the transparent lacquer layer was about 25 microns. The glass spheres covered about 25% of the coated surface.

Ausführungsbeispiel 6.Embodiment 6.

Auf einen ausgehärteten Betondachstein mit einer ersten Farbschicht mit einer roten Grundfarbe ist nach dem Aushärten dieser ersten Farbschicht eine Beschichtung aufgebracht worden, die aus einem transparenten Lack mit darin enthaltenen farblosen Glaskugeln bestand. Als transparenter Lack wurden 100 g einer wäßrigen Acrylatdispersion mit einem Feststoffgehalt von 40 Gew.-% eingesetzt, der 2 g einer wässrigen Pigmentsuspension mit einem Gehalt von 1 g blauem Cobalt-Spinell-Pigment zugesetzt waren. Zu 102 g dieser blau pigmentierten Acrylatdispersion wurden 80 g Glaskugeln mit einem Durchmesser von 90 μm ± 20 μm gegeben. Von der fertigen Beschichtungsmischung wurden 115,4 g/m2 auf den Betondachstein aufgesprüht. Nach dem Aushärten der aufgesprühten Schicht betrug die mittlere Dicke der transparenten Lackschicht etwa 60 μm. Die Glaskugeln bedeckten etwa 47 % der beschichteten Oberfläche.On a cured concrete tile with a first color layer with a red base color, a coating has been applied after curing of this first color layer, which consisted of a transparent lacquer with colorless glass beads contained therein. 100 g of an aqueous acrylate dispersion having a solids content of 40% by weight, to which 2 g of an aqueous pigment suspension containing 1 g of blue cobalt spinel pigment were added, were used as transparent paint. To 102 g of this blue-pigmented acrylate dispersion was added 80 g of glass beads with a diameter of 90 μm ± 20 μm. From the finished coating mixture 115.4 g / m 2 was sprayed onto the concrete roof tile. After curing of the sprayed layer, the average thickness of the transparent lacquer layer was about 60 microns. The glass spheres covered about 47% of the coated surface.

In der Zeichnung ist schematisch ein erfindungsgemäß beschichtetes Bauelement 10 im Querschnitt dargestellt. Ein plattenförmiges Bauelement 12, hier ein Betondachstein, weist eine erste Farbschicht 14 mit einer roten Grundfarbe auf. Diese erste Farbschicht 14 ist bedeckt mit einer Beschichtung, die aus einem transparenten Lack 16 mit darin enthaltenen durchsichtigen Partikeln 18 besteht. Als durchsichtige Partikel 18 sind hier Glaskugeln eingesetzt.In the drawing, schematically, a device according to the invention coated 10 shown in cross section. A plate-shaped component 12 , here a concrete roof tile, has a first coat of paint 14 with a red base color. This first color layer 14 is covered with a coating that consists of a transparent varnish 16 with transparent particles contained therein 18 consists. As a transparent particle 18 here glass balls are used.

Claims (7)

Farbige Beschichtung mit einem durchsichtige Partikel (18) in einer Monolage enthaltenden transparenten Lack (16), wobei die Schichtdicke des transparenten Lackes (16) geringer ist als die Dicke der durchsichtigen Partikel (18), für insbesondere ein plattenförmiges Bauelement (12), dadurch gekennzeichnet, daß der transparente Lack (16) eine andere Farbe als die Grundfarbe der Oberfläche des plattenförmigen Bauelements (12) aufweist, daß der mit durchsichtigen Partikel (18) beschichtete Anteil der Oberfläche zwischen 10% und 50% der gesamten beschichteten Oberfläche beträgt und daß die Grundfarbe der Oberfläche durch die durchsichtigen Partikel hindurch sichtbar ist.Colored coating with a transparent particle ( 18 ) in a monolayer transparent varnish ( 16 ), wherein the layer thickness of the transparent lacquer ( 16 ) is less than the thickness of the transparent particles ( 18 ), in particular a plate-shaped component ( 12 ), characterized in that the transparent lacquer ( 16 ) a color other than the base color of the surface of the plate-shaped component ( 12 ) that the with transparent particles ( 18 ) coated portion of the surface is between 10% and 50% of the total coated surface and that the base color of the surface is visible through the transparent particles. Farbige Beschichtung nach Anspruch 1, dadurch gekennzeichnet, daß die durchsichtigen Partikel (18) farblos sind.Colored coating according to claim 1, characterized in that the transparent particles ( 18 ) are colorless. Farbige Beschichtung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die durchsichtigen Partikel (18) eine im wesentlichen einheitliche Größe aufweisen.Colored coating according to claim 1 or 2, characterized in that the transparent particles ( 18 ) have a substantially uniform size. Farbige Beschichtung nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die durchsichtigen Partikel (18) im wesentlichen kugelförmig sind.Colored coating according to one of Claims 1 to 3, characterized in that the transparent particles ( 18 ) are substantially spherical. Farbige Beschichtung nach Anspruch 4, dadurch gekennzeichnet, daß der Durchmesser der kugelförmigen durchsichtigen Partikel im Bereich zwischen 30 μm und 500 μm liegt.Colored coating according to claim 4, characterized in that that the Diameter of the spherical transparent particles in the range between 30 microns and 500 microns. Farbige Beschichtung nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß der transparente Lack (16) aus organischem Material besteht wie Acrylat oder Polyurethan.Colored coating according to one of Claims 1 to 5, characterized in that the transparent lacquer ( 16 ) consists of organic material such as acrylate or polyurethane. Farbige Beschichtung nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß der transparente Lack (16) aus anorganischem Material besteht wie Siliciumdioxid oder Silikat.Colored coating according to one of Claims 1 to 5, characterized in that the transparent lacquer ( 16 ) consists of inorganic material such as silica or silicate.
DE19936464A 1999-08-03 1999-08-03 Colored coating Expired - Fee Related DE19936464B4 (en)