DE19817883C1 - Plastic cutting wire, used in e.g. rotating brush cutters - Google Patents
Plastic cutting wire, used in e.g. rotating brush cuttersInfo
- Publication number
- DE19817883C1 DE19817883C1 DE1998117883 DE19817883A DE19817883C1 DE 19817883 C1 DE19817883 C1 DE 19817883C1 DE 1998117883 DE1998117883 DE 1998117883 DE 19817883 A DE19817883 A DE 19817883A DE 19817883 C1 DE19817883 C1 DE 19817883C1
- Authority
- DE
- Germany
- Prior art keywords
- thread according
- mowing
- mowing thread
- coating
- monofilament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
Die Erfindung betrifft einen Mähfaden für Freischneidegeräte mit einem Antriebsmotor, wobei der Mähfaden an seinem einen Ende eingespannt und mittels des Antriebsmotors in sehr schnelle Rotationsbewegung mit bis zu 15.000 Umdrehungen je Minute versetzt wird und der Mähfaden der vorherrschenden Fliehkraft folgend sich geradlinig um die Drehachse rotierend erstreckt und Pflanzenhalme oder dergleichen schneidengleich durchtrennt. Die Mähfäden werden üblicherweise aus einem hochfesten Kunststoff, wie Polyamid, Nylon, Polyurethan und Abwandlungen dieser Kunststoffe, hergestellt und sind hochbelastet, so daß ihre Verschleißfestigkeit und Lebensdauer begrenzt ist.The invention relates to a mowing thread for brush cutters with a drive motor, the mowing thread on one Clamped at the end and by means of the drive motor in very fast rotational movement with up to 15,000 revolutions each Minute and the mower thread of the prevailing Following centrifugal force rotating in a straight line around the axis of rotation extends and blades of plants or the like with the same cut severed. The mowing threads are usually made from one high-strength plastic such as polyamide, nylon, polyurethane and Modifications of these plastics are manufactured and are highly stressed so that their wear resistance and durability is limited.
Der Mähfaden ist auf einer Vorratsspule, die in dem Freischneidegerät angeordnet ist, aufgewickelt und es steht jeweils aus der Spule ein Endabschnitt des Mähfadens vor, der aktuell als Mähfaden dient und nach Verschleiß von alleine abbricht bzw. durch Betätigen einer Weiterschaltrichtung abgetrennt und ein neuer Endabschnitt des Mähfadens für den Betrieb zur Verfügung steht.The mowing line is on a supply spool in the Brush cutter is arranged, wound up and it stands from the bobbin in front of an end section of the mowing thread currently serves as a cutting thread and after wear and tear on its own interrupts or by actuating a switching direction severed and a new end section of the mowing line for the Operation is available.
Auf diese Weise wird im Laufe der Zeit der gesamte Mähfaden, der auf der Vorratsspule ist, abschnittsweise benutzt und danach als Abfall weggeworfen, wobei er üblicherweise dort auf der Erde liegenbleibt, wo mit ihm gearbeitet worden war. In this way, the entire mowing line, which is on the supply reel, used in sections and thereafter thrown away as waste, usually ending up there the earth remains where it had been worked.
Der Erfindung liegt die Aufgabe zugrunde, die Abfallbeseitigung der benutzten Mähfadenabschnitte problemlos zu gestalten.The invention is based, which Waste disposal of the used mowing thread sections without problems to design.
Diese Aufgabe wird gemäß dem Vorschlag der Erfindung mit einem monofilen Mähfaden, der in natürlicher Umgebung unter Einwirkung von Mikroorganismen abbaubar ist, hergestellt auf Basis biologisch abbaubarer Polyester durch Extrusion mit nachfolgender Verstreckung erreicht.This object is achieved with a monofilament mowing thread, which is in a natural environment Exposure to microorganisms is degradable, produced on Basis of biodegradable polyester by extrusion with subsequent stretching reached.
Unter den Begriffen biologisch abbaubare Polyester werden im Sinne der Erfindung hieraus hergestellte Mähfaden verstanden, die entsprechend der Prüfung nach DIN 54900 aus dem Entwurf von 1996 die Bioabbaubarkeit testiert bekommen.The terms biodegradable polyesters are used in Understand the cutting thread produced from this, which correspond to the test according to DIN 54900 from the draft from 1996 certified biodegradability.
Als bioabbaubare Polyester für monofile Mähfaden kommen insbesondere hochmolekulare statistische Copolyester in Frage, die unter Verwendung mindestens einer Dihydroxyverbindung, wie aliphatischer Polyole, oder mindestens eines Aminoalkohohls oder deren Mischungen sowie mindestens einer aromatischen Polycarbonsäure oder deren esterbildendem Derivat sowie gleichzeitig einer aliphatischen oder cycloaliphatischen Polycarbonsäure oder deren esterbildendem Derivat als Monomerkomponenten hergestellt sind und die unter Verwendung eines Diisocyanates oder einer Mischung, enthaltend aromatische ein- und mehrkernige Isocyanate, ein- oder zweikernige Diisocyanate und/oder ein- und mehrkernige Isocyanurate als zusätzlicher Monomerkomoponente hergestellt worden sind.Coming as biodegradable polyester for monofilament cutting threads especially high molecular weight statistical copolyesters in question, which using at least one dihydroxy compound, such as aliphatic polyols, or at least one amino alcohol or their mixtures and at least one aromatic Polycarboxylic acid or its ester-forming derivative and an aliphatic or cycloaliphatic at the same time Polycarboxylic acid or its ester-forming derivative as Monomer components are made and using a diisocyanate or a mixture containing aromatic mono- and polynuclear isocyanates, mono- or binuclear diisocyanates and / or mononuclear and multinuclear Isocyanurate produced as an additional monomer component have been.
Für erfindungsgemäße Mähfäden werden insbesondere biologisch abbaubare Polyester mit Molmassen über 100.000 g/mol vorzugsweise über 130.000 g/mol, eingesetzt, deren Schmelzpunkt mindestens 100°C, vorzugsweise mindestens 110°C beträgt.For mowing threads according to the invention are especially biological degradable polyesters with molecular weights over 100,000 g / mol preferably over 130,000 g / mol, whose Melting point at least 100 ° C, preferably at least 110 ° C is.
Erfindungsgemäße Mähfäden können beispielsweise unter Einsatz von biologisch abbaubaren Polyestern, wie sie beispielsweise in der DE 195 32 771 A1 oder der WO 98/12242 beschrieben sind, hergestellt werden.Cutting threads according to the invention can be used, for example of biodegradable polyesters, such as, for example are described in DE 195 32 771 A1 or WO 98/12242, getting produced.
Der erfindungsgemäße Mähfaden aus einem biologisch abbaubaren Polyester wird durch Extrusion und Verstreckung hergestellt, wobei das hergestellte Monofilament ein dem Polyethylen PE-LD vergleichbares Eigenschaftsprofil aufweist. Die erfindungsgemäßen Mähfäden sind reißfest und elastisch, wasserfest und unempfindlich gegen Feuchtigkeitsschwankungen. Sie zeichnen sich durch sehr hohe Zähigkeit und Reißfestigkeit aus. Es werden Zugfestigkeiten nach ISO 527 von 25 N/mm2 und mehr erreicht. Ebenfalls ist die Reißdehnung sehr hoch und beträgt nach ISO 527 mindestens 700% und mehr.The cutting thread according to the invention made of a biodegradable polyester is produced by extrusion and drawing, the monofilament produced having a profile of properties comparable to that of polyethylene PE-LD. The mowing threads according to the invention are tear-resistant and elastic, waterproof and insensitive to moisture fluctuations. They are characterized by very high toughness and tear resistance. Tensile strengths according to ISO 527 of 25 N / mm 2 and more are achieved. The elongation at break is also very high and is at least 700% or more according to ISO 527.
Erfindungsgemäße Mähfaden können bevorzugt aus biologisch abbaubaren Polyestern auf der Basis von 95 bis 99,99 mol-% wenigstens eines Polyesters erstellt werden, der als monomere Komponenten enthält eine Mischung von 20 bis 95 mol-% von mindestens einer aliphatischen oder cycloaliphatischen Dicarbonsäure oder deren esterbildendem Derivat und 5 bis 80 mol-% von mindestens einer aromatischen Dicarbonsäure oder deren esterbildendem Derivat, des weiteren mindestens einer Dihydroxyverbindung oder mindestens ein Aminoalkohol oder deren Mischungen, gegebenenfalls auch noch zusätzlich geringe Mengen 1,6-Hexamethylendiisocyanat und des weiteren 0,01 bis 5 mol-% einer Mischung, enthaltend aromatische ein- oder mehrkernige Isocyanate, ein- oder zweikernige Diisocyanate und/oder ein- oder mehrkernige Isocyanurate.Mowing thread according to the invention can preferably be made from biological degradable polyesters based on 95 to 99.99 mol% at least one polyester can be created as a monomer Components contains a mixture of 20 to 95 mol% of at least one aliphatic or cycloaliphatic Dicarboxylic acid or its ester-forming derivative and 5 to 80 mol% of at least one aromatic dicarboxylic acid or their ester-forming derivative, further at least one Dihydroxy compound or at least one amino alcohol or their mixtures, possibly also additionally small Amounts of 1,6-hexamethylene diisocyanate and a further 0.01 to 5 mol% of a mixture containing aromatic one or multinuclear isocyanates, mononuclear or dinuclear diisocyanates and / or mononuclear or polynuclear isocyanurates.
Als aliphatische Dicarbonsäuren kommen bevorzugt Adipinsäure und/oder Sebacinsäure sowie deren esterbildende Derivate zum Einsatz. Als aromatische Dicarbonsäuren kommt bevorzugt Terephthalatsäure zum Einsatz.Adipic acid are preferred as aliphatic dicarboxylic acids and / or sebacic acid and their ester-forming derivatives for Commitment. Aromatic dicarboxylic acids are preferred Terephthalic acid used.
Als Dihydroxyverbindung kommen bevorzugt Diole in Frage, wie das 1,4-Butandiol oder Mischungen von Diolen. Diols, such as, are preferred as the dihydroxy compound 1,4-butanediol or mixtures of diols.
Als Verbindung mit funktionellen Gruppen, die mit den Säure-, Amino- oder Hydroxyendgruppen der Polyesterkomponente reagieren können, werden bevorzugt Mischungen unterschiedlicher aromatischer Isocyanate und/oder Isocyanurate eingesetzt. Hiermit werden verzweigte Polyester erhalten, die biologisch abbaubar sind und bevorzugt Molekulargewichte (Gewichtsmittelwert) von etwa 100.000 g/mol bis 180.000 g/mol aufweisen.As a connection with functional groups, which with the acid, Amino or hydroxy end groups of the polyester component can react, mixtures are preferred different aromatic isocyanates and / or Isocyanurates used. This makes branched polyesters obtained that are biodegradable and preferred Molecular weights (weight average) of about 100,000 g / mol have up to 180,000 g / mol.
Den biologisch abbaubaren Polyestern können auch gegebenenfalls bereits bei deren Herstellung neben üblichen Katalysatoren Additive zugegeben sein, insbesondere Stabilisatoren, wie Phosphorverbindungen, beispielhaft Organophosphite, phosphorige Säure, phosphonige Säure, Trialkylphosphite, Triphenylphosphit, Trialkylphosphat, Triphenylphosphat, Tocopherol, sowie Füllstoffe, UV- Stabilsatoren, Nukleierungsmittel, Gleit- und Formtrennmittel, wobei hiervon die biologisch verträglichen Mittel bevorzugt sind. Auch für die Einfärbung der Mähfaden werden biologisch verträgliche oder abbaubare Farbmittel verwendet.The biodegradable polyesters can too if necessary, in addition to the usual ones during their manufacture Catalyst additives can be added, in particular Stabilizers, such as phosphorus compounds, are exemplary Organophosphites, phosphorous acid, phosphonous acid, Trialkyl phosphite, triphenyl phosphite, trialkyl phosphate, Triphenyl phosphate, tocopherol, and fillers, UV Stabilizers, nucleating agents, lubricants and mold release agents, of which the biocompatible agents are preferred are. The coloring of the mowing thread is also organic compatible or degradable colorants used.
Darüber hinaus ist es auch möglich, eine Mischung aus verschiedenen biologisch abbaubaren Polyestern oder mit anderen biologisch abbaubaren extrudierbaren Polymerkomponenten für die Mähfaden einzusetzen.In addition, it is also possible to have a mix of various biodegradable polyesters or with other biodegradable extrudable Use polymer components for the cutting thread.
Es wurde überraschenderweise gefunden, daß die aus solchen biologisch abbaubaren Polyestern hergestellten Mähfäden, bei denen der Polyester durch Zusatz von funktionellen Isocyanaten und/oder Isocyanuraten eine Erhöhung der Molmasse erfährt, ausreichende mechanische Eigenschaften insbesondere Reißfestigkeit und Wasserfestigkeit und Zähigkeit erhält, um als Mähfaden eingesetzt zu werden. Zugleich können die beim Einsatz der Mähfaden anfallenden Abfälle problemlos an Ort und Stelle fallengelassen werden, da sie innerhalb kurzer Zeit biologisch durch die Mikroorganismen, die überall vorhanden sind, zersetzt und abgebaut werden und kompostiert werden. It has surprisingly been found that those of such biodegradable polyester mowing threads, at those of the polyester by adding functional isocyanates and / or isocyanurates experience an increase in molecular weight, adequate mechanical properties in particular Tear resistance and water resistance and toughness gets to to be used as a cutting thread. At the same time they can Use of waste thread on site and without problems Spot to be dropped as it is within a short period of time biologically by the microorganisms that are everywhere are decomposed and broken down and composted.
Je nach Einstellung können nach den kontrollierten Kompostierungstest gemäß DIN V 54900 Abbaugrade von 100% bereits in 100 Tagen und weniger erreicht werden. Der Abbaugrad ist vergleichbar dem von Zellulose, wobei der anfängliche Abbaugrad langsamer ansteigt, sich aber dann von Zellulose nähert.Depending on the setting, the controlled Composting test according to DIN V 54900 degrees of degradation of 100% can be achieved in 100 days and less. Of the Degradation is comparable to that of cellulose, with the initial degree of degradation increases more slowly, but then decreases from Cellulose is approaching.
Überraschend ist, daß für eine ausreichende Festigkeit des Mähfadens eine entsprechende große Molmasse eines biologisch abbaubaren Polyesters erforderlich ist, und dennoch der Mähfaden sich durch Mikroorganismen innerhalb einer angemessenen Zeit abbauen läßt.It is surprising that for a sufficient strength of the Mowing thread a correspondingly large molecular weight of a biological degradable polyester is required, and yet the Mowing thread through microorganisms within one reasonable time.
Die erfindungsgemäßen Mähfaden werden aus biologisch abbaubaren Polyestern hergestellt, bei denen der Kondensation der aliphatischen/aromatischen Copolyester 0,1 bis 5 Gew.-%, bevorzugt 0,5 bis 2 Gew.-%, bifunktionelle Isocyanate auf Basis des Polyesters zugegeben werden. Als Diisocyanate lassen sich aliphatische, cycloaliphatische und/oder aromatische Diisocyanate verwenden.The mowing thread according to the invention are made from biological Degradable polyesters made where the condensation the aliphatic / aromatic copolyester 0.1 to 5% by weight, preferably 0.5 to 2% by weight of bifunctional isocyanates Base of the polyester are added. Leave as diisocyanates aliphatic, cycloaliphatic and / or aromatic Use diisocyanates.
Für die biologische Abbaubarkeit von Vorteil ist der Anteil in dem biologisch abbaubaren Polyester, der auf die aromatische Polycarbonsäure als Monomerkomponente zurückgeht, das sind bevorzugt 35 bis 65 mol-%.The proportion in is advantageous for biodegradability the biodegradable polyester, which is based on the aromatic Polycarboxylic acid as a monomer component decreases, that is preferably 35 to 65 mol%.
Beispielsweise kann für den Mähfaden auch ein biologisch abbaubarer Polyester verwendet werden, der hergestellt ist dergestalt, daß der Polyester mit einem aliphatischen Diol, insbesondere C2-6-Diol, vorzugsweise 1,2-Ethandiol, 1,2- Propandiol, 1,3-Propandiol, 1,4-Butandiol, 2,3-Butandiol oder 1,6-Hexandiol, einer aromatischen Dicarbonsäure, vorzugsweise Terephthalsäure, und einer aliphatischen Dicarbonsäure, insbesondere C2-10-Dicarbonsäure, vorzugsweise Adipinsäure oder Sebacinsäure, vorkondensiert und zusätzlich einem Diisocyanat, wie Hexamethylendiisocyanat und/oder einer Mischung, enthaltend unterschiedliche aromatische Isocyanate und/oder Isocyanurate, nachkondensiert bzw. polymerisiert worden ist. For example, a biodegradable polyester can be used for the mowing thread, which is produced in such a way that the polyester with an aliphatic diol, in particular C 2-6 diol, preferably 1,2-ethanediol, 1,2-propanediol, 1,3 -Propanediol, 1,4-butanediol, 2,3-butanediol or 1,6-hexanediol, an aromatic dicarboxylic acid, preferably terephthalic acid, and an aliphatic dicarboxylic acid, in particular C 2-10 dicarboxylic acid, preferably adipic acid or sebacic acid, precondensed and additionally one Diisocyanate, such as hexamethylene diisocyanate and / or a mixture containing different aromatic isocyanates and / or isocyanurates, has been post-condensed or polymerized.
Der Polyester kann dadurch herstellbar sein, daß man den Polyester mit Hilfe von aromatischen Dicarbonsäuren und/oder aliphatischen Dicarbonsäuren in Form ihrer Methylester kondensiert.The polyester can be produced by the Polyester with the help of aromatic dicarboxylic acids and / or aliphatic dicarboxylic acids in the form of their methyl esters condensed.
Dem Polykondensat können die in der Technik üblichen Additive zur Verbesserung der hydrolytischen Stabilität zugesetzt worden sein, insbesondere Phosphorverbindungen.Additives customary in the art can be added to the polycondensate added to improve hydrolytic stability have been, especially phosphorus compounds.
Bei der Herstellung des Mähfadens können den biologisch abbaubaren Polyestern Verarbeitungshilfsmittel und Additive, beispielsweise Nukleierungsmittel, Stabilisatoren oder Gleitmittel sowie auch Farbmittel zugegeben werden.In the production of the mowing thread, the biological degradable polyesters processing aids and additives, for example nucleating agents, stabilizers or Lubricants as well as colorants are added.
Als Nukleierungsmittel können auch sulfonatgruppenhaltige Verbindungen eingesetzt werden, zum Beispiel Alkalimetallsalze der 5-Sulfoisophthalsäure oder deren Mischungen, bevorzugt das Natriumsalz.Sulphonate groups can also be used as nucleating agents Compounds are used, for example alkali metal salts 5-sulfoisophthalic acid or mixtures thereof, preferably that Sodium salt.
Da der Mähfaden, der auf einer Vorratsspule aufgerollt ist und in dem Freischneidegerät untergebracht ist, bei Betrieb des Gerätes und den hohen Umdrehungsgeschwindigkeiten Schwingungen ausgesetzt ist, die zu Relativbewegungen zwischen den Windungen des auf der Vorratsspule aufgewickelten Mähfadens führen, wird hier Reibungshitze erzeugt. Die Erwärmung des Mähfadens, der auf der Vorratsspule ist, kann dabei so stark werden, daß es zu einem Schmelzen bzw. Verschweißen von aufeinanderliegenden Fadenwicklungen kommen kann, wodurch das Abspulen von der Vorratsrolle behindert ist.Because the mowing thread, which is rolled up on a supply spool and is housed in the brush cutter when the Device and the high rotational speed vibrations exposed to relative movements between the Turns of the cutting thread wound on the supply spool friction heat is generated here. The warming of the Cutting thread that is on the supply spool can be so strong be that there is a melting or welding of superimposed thread windings can come, which makes Unwinding from the supply roll is hindered.
Da die biologisch abbaubaren Polyester, aus denen die Mähfaden erfindungsgemäß hergestellt werden, keinen so hohen Schmelzpunkt aufweisen, besteht die Gefahr des Anschmelzens durch Reibungshitze oder Verklebens untereinander.Because the biodegradable polyesters that make up the mowing thread are produced according to the invention, not so high Have melting point, there is a risk of melting due to frictional heat or sticking together.
Um dieses Problem zu lösen, wird erfindungsgemäß vorgeschlagen, den Mähfaden aus biologisch abbaubarem Polyester mit einem Überzug auf Basis eines Fluorpolymeren und/oder eines Aviviermittels zu versehen.To solve this problem, the invention proposed the cutting thread from biodegradable Polyester with a coating based on a fluoropolymer and / or a finishing agent.
Der Überzug aus einem gegebenenfalls ein Aviviermittel enthaltenden Fluorpolymeren verleiht dem Mähfaden eine glattere Oberfläche und erhöht damit auch die Abriebfestigkeit der auf der Vorratsspule den Schwingungen ausgesetzten Fadenwicklungen. Darüber hinaus bietet der Überzug aus Fluorpolymeren auf Grund seiner höheren Schmelzefestigkeit und seines höheren Schmelzpunktes einen verbesserten Schutz gegen das Anschmelzen der Oberfläche auf Grund der entstehenden Reibungswärme, so daß das Verkleben der Fadenwicklungen auf Grund der mit einem Überzug versehen Mähfaden verhindert werden kann.The coating from an optionally a finishing agent containing fluoropolymers gives the mowing thread a smoother surface and thus also increases the abrasion resistance that is exposed to vibrations on the supply spool Thread windings. In addition, the cover offers Fluoropolymers due to its higher melt strength and its higher melting point provides improved protection against the melting of the surface due to the resulting Frictional heat, so that the thread windings stick on The mowing line provided with a coating prevents this can be.
Als Aviviermittel kommen die aus der Textilindustrie für die Behandlung von Garnen und Geweben bekannten glättenden, antistatische und/oder hydrophobierende Eigenschaften aufweisenden Mittel, wie Tenside, in Frage, zum Beispiel auf Basis quartärer Ammoniumverbindungen.The finishing agents come from the textile industry for the Treatment of yarns and fabrics known smoothing, antistatic and / or hydrophobic properties having agents, such as surfactants, in question, for example Based on quaternary ammonium compounds.
Besonders glatte Überzüge werden erreicht, wenn diese aus einer Polymerdispersion des Fluorpolymeren aufgebracht sind. Bevorzugt wird der Überzug aus einer wässrigen Dispersion von feinverteilten Fluorpolymeren aufgebracht.Particularly smooth coatings are achieved when these are made a polymer dispersion of the fluoropolymer are applied. The coating from an aqueous dispersion of finely divided fluoropolymers applied.
Besonders geeignet für den Überzug sind Fluorpolymere mit hoher Schmelzefestigkeit und einer Schmelztemperatur von mindestens 210°C und einer Langzeitgebrauchstemperatur von mindestens 120°C oder mehr.Fluoropolymers with are particularly suitable for the coating high melt strength and a melting temperature of at least 210 ° C and a long term use temperature of at least 120 ° C or more.
Als besonders geeignet für den Überzug auf den erfindungsgemäßen Mähfaden aus biologisch abbaubarem Polyester haben sich die im Anspruch 6 aufgeführten Polymere erwiesen. Dies sind FEP, PFA, E/TFE, E/CTFE, PCTFE oder PTFE-Copolymere.As particularly suitable for the coating on the Mowing thread according to the invention made of biodegradable polyester the polymers listed in claim 6 have proven. These are FEP, PFA, E / TFE, E / CTFE, PCTFE or PTFE copolymers.
Der erfindungsgemäße Mähfaden zeichnet sich auch dadurch aus, daß er aus einem aus einer Formmasse enthaltend biologisch abbaubare Polyester als Monofilament extrudiert wird und nachfolgend bevorzugt um das Vierfache bis Zwölffache verstreckt wird.The mowing thread according to the invention is also characterized by that he is biological from a molding compound containing degradable polyester is extruded as a monofilament and hereinafter preferably four to twelve times is stretched.
Es ist bekannt, daß die mit Mähfaden ausgerüsteten Freischneidegeräte, da sie mit hohen Drehzahlen arbeiten, ein erhebliches Geräusch verursachen, was zu einem Großteil durch Wirbelablösung an dem mit hoher Geschwindigkeit umlaufenden Endabschnitt des Mähfadens bedingt ist.It is known that those equipped with mowing thread Brush cutters because they work at high speeds cause significant noise, which is largely due to Vortex detachment on the rotating at high speed End section of the mowing line is conditioned.
Zur Geräuschreduzierung der Mähfaden ist deshalb bereits vorgeschlagen worden, den Querschnitt des Mähfadens über seine Längserstreckung hin derart zu verändern, daß zusätzliche Abrißkanten am Außenumfang des Mähfadens zur frühzeitigen Wirbelablösung geschaffen werden. Derartige Mähfaden aus Kunststoff mit einem Querschnitt, der eine Geräuschreduzierung bewirkt, sind beispielsweise in der DE 40 05 879 C1 und der WO 97/43469 beschrieben.To reduce noise, the cutting thread is therefore already proposed the cross section of the mower line across its To change longitudinal extension in such a way that additional Tear edges on the outer circumference of the mowing line for early Vortex detachment can be created. Such mowing thread Plastic with a cross section that reduces noise are caused, for example, in DE 40 05 879 C1 and WO 97/43469.
Auch der erfindungsgemäße Mähfaden aus biologisch abbaubarem Polyester kann sowohl einen über seine Längserstreckung hin gleichbleibenden Querschnitt, beispielsweise rund, oval, dreieckig, viereckig, fünfeckig, sechseckig, sternförmig oder kleeblattförmig oder dergleichen aufweisen oder aber mit zusätzlichen Querschnittveränderungen versehen sein. Insbesondere wird der Mähfaden nach dem Extrudieren und Verstrecken durch äußere Einwirkung beispielsweise unter Verkleinerung des Querschnittes bereichsweise verändert, so daß auf diese Weise die gewünschten zusätzlichen Abrißkanten am Umfang des Mähfadens geschaffen werden, um eine frühzeitige Wirbelablösung zu erreichen bzw. die Ausbildung großer Wirbel zu unterdrücken. Die Mähfaden weisen mittlere Durchmesser von 1,5 bis 8 mm je nach Einsatzgebiet auf.The cutting thread according to the invention is also made from biodegradable Polyester can be one along its length constant cross-section, for example round, oval, triangular, quadrangular, pentagonal, hexagonal, star-shaped or have cloverleaf or the like or with additional cross-sectional changes. In particular, the mowing line after extrusion and Stretching due to external influences, for example under Reduction of the cross section changed in some areas, see above that in this way the desired additional tear-off edges on the circumference of the mowing line to be created early To achieve vertebral detachment or the formation of large vertebrae to suppress. The mowing threads have an average diameter of 1.5 to 8 mm depending on the area of application.
Sofern der Mähfaden mit beispielsweise gemäß den Vorschlägen der WO 97/43469 ausgebildeten Querschnitten durch äußere bereichsweise Einwirkung auf das Monofilament versehen ist, wird der Überzug erst nach dem bereichsweisen Verändern der Querschnitte des Monofilamentes aufgebracht.If the mowing line with, for example, according to the suggestions WO 97/43469 formed cross sections by external is affected in some areas on the monofilament, the coating is only changed after changing the area Cross sections of the monofilament applied.
Die bereichsweise Verkleinerung des Querschnittes des Monofilamentes in Längserstreckung desselben ist bevorzugt mindestens einer Schraubenlinie folgend angeordnet.The area-wise reduction of the cross section of the Longitudinal monofilament is preferred arranged following at least one helix.
In der Zeichnung sind beispielhaft Ausführungsformen von verschiedenen Mähfaden dargestellt.In the drawing, exemplary embodiments of different mowing thread shown.
Fig. 1, 2 und 3 zeigen verschiedene Querschnitte von Mähfäden, die über ihre Längserstreckung hin konstant sind. Fig. 1, 2 and 3 illustrate various cross-sections of Mähfäden which are towards constant throughout its longitudinal extent.
Fig. 4, 5 zeigen verschiedene Querschnitte und Ausführungsformen von Mähfäden, deren Querschnitt über die Länge hin durch Verkleinerung bereichsweise verändert ist. Fig. 4, 5 show different cross-sections and embodiments of Mähfäden whose cross-section is varied over the length out by reduction in regions.
In der Fig. 1 ist ein Mähfaden 1 mit rundem Querschnitt dargestellt, dessen Kern 10 aus einem biologisch abbaubaren Polyester gegebenenfalls unter Zusatz von üblichen Additiven hergestellt ist und der nach der Extrusion und Verstreckung um das Siebenfache mit einem Überzug 11 aus einer Polymerdispersion auf Basis eines fluorhaltigen Polymeren versehen ist. Hierbei ist beispielsweise eine wässrige Dispersion von feinverteilten synthetischen Fluorpolymeren, beispielsweise Ethylen-Tetrafluorethylen-Copolymer, wobei die Teilchengröße in der Dispersion unter 5 µm beträgt, hergestellt. Das extrudierte und verstreckte Monofilament wird hierbei durch die wässrige Polymerdispersion hindurchgeführt, wodurch sich ein glatter anhaftender dünner Überzug ergibt, der dem Mähfaden die gewünschte erhöhte äußere thermische Stabilität verleiht. Ein Fluorpolymer, wie E/TFE, weist hierbei eine Schmelztemperatur zwischen 265 bis 270°C auf bei einer langzeitigen Gebrauchstemperatur von mindestens 120°C und kurzzeitig bis 200°C.In FIG. 1, a cutting line 1 is shown with a round cross-section, the core 10 is made of a biodegradable polyester optionally with the addition of customary additives and the one after the extrusion and stretching seven times with a coating 11 of a polymer dispersion based on fluorine-containing polymers is provided. Here, for example, an aqueous dispersion of finely divided synthetic fluoropolymers, for example ethylene-tetrafluoroethylene copolymer, is produced, the particle size in the dispersion being less than 5 μm. The extruded and drawn monofilament is passed through the aqueous polymer dispersion, resulting in a smooth, adherent, thin coating that gives the mowing thread the desired increased external thermal stability. A fluoropolymer, such as E / TFE, has a melting temperature between 265 to 270 ° C with a long-term use temperature of at least 120 ° C and briefly up to 200 ° C.
Der Überzug aus Fluorpolymer hat des weiteren den Vorteil des Antihafteffektes, wodurch ein Ankleben der sich im Betrieb im Freischneidegerät erwärmenden Fadenwicklungen auch an der Spule vermieden wird. Auch die Gefahr, daß der Mähfaden am Ausgang der Spule anhaftet, wird durch den erfindungsgemäßen Überzug aus einem Fluorpolymeren nach Art einer Antihaftbeschichtung verringert.The fluoropolymer coating also has the advantage of Non-stick effect, which makes it sticky when in operation Brush cutter also heating the thread windings on the Coil is avoided. Also the danger that the mowing thread on Output of the coil adheres to the invention A fluoropolymer type coating Non-stick coating reduced.
In der Fig. 2 ist beispielhaft ein Mähfaden mit sternförmigem Querschnitt mit einer Seele 10 aus einem biologisch abbaubaren Polyester mit hoher Schmelztemperatur von beispielsweise 145°C und einem Überzug 11 aus einem Fluorpolymer dargestellt.In FIG. 2, a cutting line with a star-shaped cross-section with a core 10 made of a biodegradable polyester with a high melting temperature such as 145 ° C and a coating 11 is shown of a fluoropolymer exemplified.
Die Fig. 3 zeigt einen Mähfaden im Querschnitt eines gleichseitigen Sechsecks mit Überzug. FIG. 3 shows a cutting line in the cross section of a equilateral hexagon with coating.
In den Fig. 4, 5 sind erfindungsgemäße Mähfäden mit einer Seele 10 aus einem biologisch abbaubaren Polymer und einem Überzug 11 aus einem fluorhaltigen Polymer dargestellt, die zusätzlich mit durch längs Schraubenlinien eingearbeiteter Kerben oder Nuten 12 am Außenumfang Abrißkanten bilden, um die Wirbelablösung und damit die Geräuschminderung zu verbessern.In Figs. 4, 5 Mähfäden according to the invention with a core 10 of a biodegradable polymer and a coating 11 are shown from a fluorine-containing polymer, which additionally form with incorporated by longitudinal helical notches or grooves 12 on the outer circumferential separation edges, to the vortex shedding and improve noise reduction.
Claims (13)