DE19725829C1 - Surface coating material for wood used in furniture, wall panels etc. - Google Patents

Surface coating material for wood used in furniture, wall panels etc.

Info

Publication number
DE19725829C1
DE19725829C1 DE1997125829 DE19725829A DE19725829C1 DE 19725829 C1 DE19725829 C1 DE 19725829C1 DE 1997125829 DE1997125829 DE 1997125829 DE 19725829 A DE19725829 A DE 19725829A DE 19725829 C1 DE19725829 C1 DE 19725829C1
Authority
DE
Germany
Prior art keywords
characterized
parts
coating material
surface coating
catalyst
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE1997125829
Other languages
German (de)
Inventor
Dieter Litzcke
Phillip Kahrmann
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ls-Industrielacke Buero-Labor- und Anwendungstechnik 58332 Schwelm De GmbH
Ls Industrielacke Buero L GmbH
Original Assignee
Ls-Industrielacke Buero-Labor- und Anwendungstechnik 58332 Schwelm De GmbH
Ls Industrielacke Buero L GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ls-Industrielacke Buero-Labor- und Anwendungstechnik 58332 Schwelm De GmbH, Ls Industrielacke Buero L GmbH filed Critical Ls-Industrielacke Buero-Labor- und Anwendungstechnik 58332 Schwelm De GmbH
Priority to DE1997125829 priority Critical patent/DE19725829C1/en
Application granted granted Critical
Publication of DE19725829C1 publication Critical patent/DE19725829C1/en
Anticipated expiration legal-status Critical
Application status is Expired - Fee Related legal-status Critical

Abstract

Surface coating material (I), containing (a) 20-50 pts. wt.liquid urea-formaldehyde (UF) resin, (b) 10-25 pts. wt. melamine (MF) resin, (c) 2-3 pts. wt. plasticiser, (d) 5-10 pts. wt. soft resin, (e) 5-10 pts. wt. cellulose fibres, (f) 2-5 pts. wt. anti- settling agent, (g) 2-5 pts. wt. wax or wax dispersion and (h) 5-15 pts. wt. anti-abrasion additive.

Description

Die vorliegende Erfindung betrifft ein verbessertes Oberflächenbeschichtungsmaterial zur Herstellung harter, widerstandsfähiger und wasserfester Oberflächen auf Träger materialien, wie Holzwerkstoffplatten, vergleichbaren Trägerplatten oder Mineralfaser platten, die beispielsweise in Möbeln, Wand- und Deckenpaneelen sowie in Fußboden platten eingesetzt werden können, sowie die Verwendung derartiger Materialien in Ver fahren zur Herstellung beschichteter Oberflächen. The present invention relates to an improved surface coating material for the production of hard, wear-resistant and water-resistant surfaces on support materials such as wood material panels, similar carrier plates or mineral fiber boards, which can be used plates for example in furniture, wall and ceiling panels as well as in floors, and to the use of such materials in United drive for preparing coated surfaces.

Im Stand der Technik wurden bisher UV-härtende und lösungsmittelhaltige Beschichtungs materialien eingesetzt, die jedoch bei der Verarbeitung zum Teil sehr große Mengen an organischen Lösungsmitteln freisetzen oder hautreizende Eigenschaften aufweisen und daher im Hinblick auf ökologische Gesichtpunkte nachteilig sind. UV-curing and solvent-containing coating materials have been used in the prior art, however, that release at the processing in some cases very large amounts of organic solvents or having skin-irritating properties and therefore are disadvantageous with regard to ecological aspects.

Die DE-PS 41 14 518 lehrt die Verwendung einer Zusammensetzung auf Basis von Melamin-Harnstoff-Formaldehyd-Kondensationsprodukten als Oberflächenbeschichtungs materialien, bei der keine organischen Lösungsmittel mehr eingesetzt werden müssen. The DE-PS 41 14 518 teaches the use of a composition based on melamine-urea-formaldehyde condensation products materials as a surface coating, in which no organic solvents have to be used more. Die hier beschriebenen Materialien sind jedoch nicht ausreichend wasserfest und weisen darüber hinaus den Nachteil auf, daß sie für eine Aushärtung in der Presse nicht geeignet sind und somit für hochabriebfesten Glattlackierungen, wie Fußbodenbeschichtungen, nicht in Frage kommen. However, the materials described herein are not sufficiently waterproof and moreover have the disadvantage that they are not suitable for curing in the press and thus highly abrasion-resistant smooth finishes such as floor coatings, are not eligible.

Eine Aufgabe der vorliegenden Erfindung bestand daher darin, eine verbesserte Zusammen setzung bereitzustellen, mit der kostengünstig hochabriebfeste Glattlackierungen bereitge stellt werden können, ohne die Umwelt im wesentlichen zu beeinträchtigen. Therefore, an object of the present invention to provide an improved co-translation, with the cost bereitge highly abrasion-resistant coatings provides Glatt can be without adversely affecting the environment substantially.

Die vorstehende Aufgabe wurde mit einem neuen Beschichtungsmaterial gelöst, das die folgenden Komponenten in den angegebenen Mengen enthält: The above object has been achieved with a new coating material which contains the following components in the amounts indicated:
20-50 Teile eines flüssigen Harnstoff-Formaldehydharzes, 10-25 Teile Melaminharz, 2-3 Teile Weichmacher, 5-10 Teile Weichharz, 5-10 Teile Cellulosefasern, 2-5 Teile Antiabsetzmittel, 2-5 Teile Wachse oder Wachsdispersion und 5-15 Teile eines Antiab riebmittels, jeweils bezogen auf das Gewicht. 20-50 parts of a liquid urea-formaldehyde resin, 10-25 parts of melamine resin, 2-3 parts of plasticizer, 5-10 parts of soft resin, 5-10 parts of cellulose fibers, 2-5 parts anti-settling agent, 2-5 parts waxes or wax dispersion, and 5- 15 parts of a Antiab rubbed by means of, in each case based on the weight.

Das Harnstoff-Formaldehydharz ist in der Zusammensetzung vorzugsweise in einer Menge von 30-40 Gewichtsteilen, am meisten bevorzugt in einer Menge von 35 Gewichtsteilen vorhanden. The urea-formaldehyde resin is preferably present in the composition preferably in an amount of 30-40 parts by weight, most in an amount of 35 parts by weight.

Das Melaminharz ist in der Zusammensetzung vorzugsweise in einer Menge von 15-22 Gewichtsteilen, am meisten bevorzugt in einer Menge von 20 Gewichtsteilen vorhanden. The melamine resin is preferably present in the composition preferably in an amount of 15-22 parts by weight, most in an amount of 20 parts by weight.

Der Weichmacher kann jeder im Stand der Technik bekannte Weichmacher sein, wie bei spielsweise Phthalsäureester, sowie spezielle Alkohole oder Weichmacher auf Basis von Propylen oder Ethylenglycol, sowie Gemische davon. The plasticizer may be any known in the prior art plasticizers, such as phthalic acid esters at play, as well as special alcohols or plasticizers based on propylene or ethylene glycol, and mixtures thereof. Von diesen ist Phthalsäure am meisten bevorzugt. Of these, phthalic acid is most preferred.

Das Weichharz dient zur Elastifizierung und Verhinderung von Spannungsrissen und umfaßt insbesondere Polyurethandiol, sowie spezielle Kunststoff-Dispersionen, z. The soft resin is used for elasticizing and prevention of stress cracks and comprises in particular polyurethane diol, as well as special plastic dispersions, z. B. Vinyl acetat und Acrylsäureester, insbesondere Polyurethandiol. As vinyl acetate and acrylate, in particular polyurethane diol. Es wird vorzugsweise in einer Menge von 6-8 Gewichtsteilen und insbesondere in einer Menge von 7 Gewichtsteilen eingesetzt. It is preferably used in an amount of 6-8 parts by weight and especially in an amount of 7 parts by weight.

Die in der Zusammensetzung verwendeten Cellulosefasern weisen eine Größe im Bereich von 20-1000 µm auf, und sind hauptsächlich als Viskositätsregulator und Träger der schweren Zusatzstoffe gedacht. The cellulose fibers used in the composition have a size in the range of 20-1000 microns, and are intended primarily as a viscosity regulator and support the heavy additives. Die Cellulosefasern werden vorzugsweise in einer Menge von 6-8 Gewichtsteilen in einer Teilchengröße von 30-125 µm, am meisten bevorzugt von 7 Gewichtsteilen in einer Teilchengröße von 30 µm eingesetzt. The cellulose fibers are preferably used in an amount of 6-8 parts by weight with a particle size of 30-125 microns, most preferably from 7 parts by weight in a particle size of 30 microns.

Als Antiabsetzmittel kann jedes im Stand der Technik bekannte Mittel verwendet werden, wobei sich für die Zwecke der Erfindung insbesondere Kieselsäureprodukte als vorteilhaft erwiesen haben, wie Kieselgele, Fällungskieselsäuren, Aerosil, Siliziumdioxide oder Magnesiumsilikate. As anti-settling agent, any known in the prior art means may be used, in particular, have proven to be advantageous for the purposes of the invention, silica products, such as silica gels, precipitated silicas, Aerosil, magnesium silicates or silicas. Am meisten bevorzugt ist Siliziumdioxid in einer Menge von 3 Ge wichtsteilen. Most preferred is silicon dioxide in parts by weight an amount of 3 Ge.

Um der Zusammensetzung eine hohe Oberflächenkratzfestigkeit zu verleihen sind darin Wachse oder Wachsdispersionen enthalten, beispielsweise Polyethylen, Polypropylen, Polyamid, Naturwachs und andere dem Fachmann bekannte Wachse. To the composition to impart a high surface scratch resistance in waxes or wax dispersions contain, for example, polyethylene, polypropylene, polyamide, natural wax, and others known to those skilled waxes. Die Wachse bzw. die Wachsdispersion sind in der Zusammensetzung am meisten bevorzugt in einer Menge von 2 Gewichtsteilen enthalten. The waxes or wax dispersion are preferably present in the composition in an amount of at most 2 parts by weight.

Um der auf dem Trägermaterial aufgebrachten Schicht eine lange Haltbarkeit und Wider standsfähigkeit zu verleihen, weist die Zusammensetzung ein Antiabriebmittel, wie eine Aluminiumverbindung und/oder andere fein gemahlene Minerale mit Härtegraden zwischen Quarz und Diamant, vorzugsweise Aluminiumoxid in jeder Form oder Aluminiumsilikate oder ein Gemisch davon, auf. To the coating applied to the substrate layer to give a long shelf life and cons standing ability, the composition comprises an anti-abrasion agent such as an aluminum compound and / or other finely ground minerals with hardness values ​​between quartz and diamond, preferably aluminum oxide in any form or aluminum silicates or a mixture thereof , on.

Die erfindungsgemäßen Materialien können transparent sein oder nach Wunsch problemlos in allen gewünschten Farben eingefärbt werden. The invention materials may be transparent or easily customized by in all desired colors. So hat sich insbesondere gezeigt, daß durch Zusatz von 5-30 Teilen Farbstoffe, Farbstofflösung, Pigmente oder einem Gemisch davon zu der vorstehend beschriebenen Zusammensetzung die Eigenschaften der erfin dungsgemäßen Zusammensetzungen nicht verschlechtert werden. As has been shown in particular that the properties of the compositions to the invention OF INVENTION are not deteriorated by the addition of 5-30 parts of dyes, dye solution, pigment or a mixture thereof to the composition described above.

Die Verarbeitung der erfindungsgemäßen Zusammensetzung erfolgt zweikomponentig durch Inkontaktbringen der Zusammensetzung mit einer Katalysatorkomponente. The processing of the two-component composition according to the invention is carried out by contacting the composition with a catalyst component.

Als Katalysator kann jeder für diesen Zweck bekannte Katalysator eingesetzt werden, wie beispielsweise Säuren oder Salze, die beim Auflösen einen sauren pH ergeben. As a catalyst, any catalyst known for this purpose can be used, such as acids or salts which give an acidic pH when dissolved. Als Säuren sind insbesondere Maleinsäure, Monobutylphosphorsäure, p-Toluolsulfonsäure, Zitronensäure, sowie ein Gemisch von einer oder mehreren der vorstehenden Säuren geeignet. Suitable acids in particular maleic acid, monobutylphosphoric acid, p-toluenesulfonic acid, citric acid, and a mixture of one or more of the foregoing acids are also suitable. Ebenso sind Aluminiumsulfat, Ammonium chlorid oder Ammoniumsulfat geeignet. Also, aluminum sulfate, ammonium chloride or ammonium sulfate suitable.

Das Inkontaktbringen des Katalysators mit der Zusammensetzung kann durch Unter mischen des Katalysators vor Auftragen der Zusammensetzung auf das Trägermaterial, oder durch separates Auftragen der Katalysatorkomponente auf das Trägermaterial oder auf eine der Lackschichten oder zwischen zwei Lackschichten, wie beispielsweise mittels einer Lackwalze, einer Lackrakelmaschine usw., und anschließendes Überschichten mit der Zusammensetzung erfolgen. The contacting of the catalyst with the composition can be prepared by mixing the catalyst prior to applying the composition to the support material, or by separately applying the catalyst component on the carrier material or one of the coating layers or between two coating layers, such as for example by means of a paint roller, a paint doctor blade machine, etc. take place, and then overlaying with the composition. Es hat sich gezeigt, daß der Katalysator vorteilhaft in einer Menge von 2-5 Gew.-%, bezogen auf das Gesamtgewicht der Zusammensetzung, eingesetzt werden sollte. It has been found that the catalyst should advantageously be used in an amount of 2-5 wt .-%, based on the total weight of the composition.

Die erfindungsgemäße Zusammensetzung ist problemlos mit Wasser verdünnbar und kann in flüssiger Form einschichtig oder sogar mehrschichtig auf die zu beschichtenden Oberflächen aufgetragen werden. The inventive composition is readily dilutable with water and can be applied in liquid form single-layer or even multiple layers on the surfaces to be coated. Zwischen den einzelnen Auftragsschichten können für bestimmte Anwendungszwecke unbeharzte oder vorbeharzte Cellulosepapiere, bzw. Cellulosevliese mit weitergehenden Ausrüstungseigenschaften, wie beispielsweise Korund, oder Harzen, eingelegt werden. Between the individual coating layers can freely treat with resin or vorbeharzte cellulose papers or cellulose webs are inlaid with further equipment properties, such as corundum, or resins for specific applications. Diese Papiere können zudem eingefärbt werden, zur Anpassung des Holzfarbtones bzw. zur Erzielung von Farbeffekten. These papers can also be tinted, for adjusting the wooden shade or to achieve color effects. Die Einfärbung dieser Papiere oder der Vliese kann unmittelbar bei der Zuführung in der Beschichtungsanlage erfolgen oder vor der Beschichtung in einer separaten Anlage. The coloring of these papers or nonwovens can be made directly or indirectly in the supply in the coating system prior to coating in a separate plant.

Die erfindungsgemäßen Zusammensetzungen werden nach Auftragen auf die Träger materialien mit herkömmlichen, im Stand der Technik bekannten Vorrichtungen zum Auftragen von Lacken auf Werkstoffe, einem Härtungsvorgang unterworfen, der bei einem Druck von mindestens 1 kg/cm 2 , einer Temperatur von mindestens 60°C Objekt- Oberflächentemperatur und einer Preßzeit von mindestens 20 Sekunden durchgeführt wird. The compositions according to the invention are after application to the carrier materials by conventional, well-known in the prior art devices for applying coatings on materials subjected to a curing process, at a pressure of at least 1 kg / cm 2, a temperature of at least 60 ° C object - surface temperature and a pressing time is carried out at least 20 seconds. Es ist jedoch klar, daß der Fachmann die Bedingungen aufgrund seines Fachwissens und der zu behandelnden Oberflächen bzw. des eingesetzten Materials entsprechend wählt. It is clear, however, that the skilled man selects in accordance with the conditions because of his expert knowledge and the surfaces to be treated or the material used. Die folgenden Bedingungen habe sich dabei als bevorzugt erwiesen. The following conditions have been found to be preferred. Preßdruck 2-5 kg/cm 2 , mehr bevorzugt 3-4 kg/cm 2 , Preßtemperatur 75-95°C Objekt-Oberflächentemperatur, mehr bevorzugt 80-90°C und eine Preßzeit von 60-240 Sekunden, mehr bevorzugt 180 Sekunden. Pressing pressure 2-5 kg / cm 2, more preferably 3-4 kg / cm 2, press temperature 75-95 ° C object surface temperature, more preferably 80-90 ° C and a press time of 60-240 seconds, more preferably 180 seconds.

Zur Erzielung besonderer Oberflächeneffekte können in den Preßetagen Trennfolien, Ausgleichspolster und/oder Bleche eingesetzt werden, die in der Beschichtungsoberfläche Strukturen bzw. Glanz- oder Matteffekte hervorrufen. To achieve special surface effects release films, compensation pads and / or sheets can be used in the Preßetagen that cause the coating surface structures or glossy or matt effects.

Das Verfahren zum Beschichten von Trägermaterialien wird im allgemeinen derart durch geführt, daß die Trägerplatten auf einer kontinuierlichen Transporteinheit aufgelegt werden und die erfindungsgemäße Zusammensetzung mittels einer herkömmlichen Auftragsstation, beispielsweise mittels Lackwalzen, Lackrakel oder anderen geeigneten Auftragsaggregaten auf die zu beschichtenden Oberflächen aufgetragen wird. The method for coating substrates is generally performed in such a way by that the carrier plates are placed on a continuous conveying unit and the composition of the invention by means of a conventional coating station, for example by means of coating rollers, lacquer doctor blade or other suitable application equipment is applied to the surfaces to be coated. Die wäßrige Zusammensetzung wird je nach Anlage gegebenenfalls 1-30 Minuten abgedunstet bzw. vorgetrocknet. The aqueous composition is optionally flashed 1-30 minutes depending on the plant or predried. Das so beschichtete Trägermaterial wird in die Presse eingefahren und die Schicht bei Wärme ausgehärtet. The thus coated carrier material is inserted into the press, and the layer is cured under heat. Nach Ausfahren aus der Presse kann das beschichtete Material sogleich zur Lagerung abgestapelt oder nach Wunsch weiterverarbeitet werden. After discharge from the press, the coated material can readily be stacked for storage or further processed as desired.

Die folgenden Beispiele erläutern die Anwendung der erfindungsgemäßen Zusammen setzungen beim Beschichten unterschiedlicher Materialien. The following examples illustrate the application of the assembly settlements invention for coating of different materials.

Beispiel 1: Example 1:

Träger-Platten, Oberseite wasserfest verleimt mit Echtholz-Furnier, Unterseite wasserfest verleimt mit imprägniertem Gegenzug-Papier. Carrier plates, top waterproof gluing with real wood veneer, bottom waterproof gluing with return impregnated paper.

Die Platten wurden anhand des folgenden Verfahrens bearbeitet, wobei diese bereits in einer separaten Presseanlage furniert wurden. The plates were processed by the following method, which have already been veneered in a separate press plant.

1.) Stapelzuführung und automatische Beschickung der Platten. 1.) Batch Feeder and automatic loading of the plates.

2.) Furnierschliff und Entstaubung der Oberseite. 2.) veneer grinding and dedusting of the top.

3.) Vorwärmen der Plattenoberfläche von oben. 3.) preheating the plate surface from above.

4.) Auftragswalze für Grundlack von oben. 4.) application roller for base coat from above.

5.) Kaschierstation mit Trennmesser für Cellulosepapier - vorbeharzt und mit Spezial ausrüstung von oben, gefärbt. 5.) laminating with separating knives for cellulose paper - vorbeharzt and with special equipment from the top, dyed.

6.) Auftragswalze für Resistenzlack von oben - kurze Zwischentrocknung. 6.) application roll for resistance paint from above - short intermediate drying.

7.) Auftragswalze für Decklack von oben. 7) application roller for topcoat from above.

8.) Vortrocknung der Beschichtung mit einem Spezialtrockner mit einer Trockenzeit von 7 Minuten. 8.) pre-drying the coating using a special dryer with a drying time of 7 minutes.

9.) Aushärtung in der Presse. 9.) curing in the press.

10.) 4-seitige Besäumung der Papierüberstände. 10) 4-sided trimming of the paper supernatants.

11.) Automatische Abstapelung der fertig beschichteten Platten mit Weitertransport der Stapel zur nachfolgenden Bearbeitung. 11) Automatic stacking of the finished plates coated with further transport of the stack for subsequent processing.

Beispiel 2: Example 2:

Träger-Platten, Oberseite wasserfest verleimt mit imprägnierten Dekorfolien, oder rohe oder vorbehandelte Furniere unterschiedlicher Stärke, Unterseite wasserfest verleimt mit imprägniertem Gegenzug-Papier. Carrier plates, top waterproof gluing with impregnated decorative films, or crude or pre-treated veneers different thickness, bottom waterproof gluing with return impregnated paper.

Hier erfolgt die Verleimung der Dekorfolien, der Furniere und der Gegenzug-Papiere gleichzeitig mit der Aushärtung von LIKAPAL Hydrolaminat in der gleichen Presse. Here, the gluing of the decorative sheets of veneer and the return papers simultaneously with the curing of LIKAPAL Hydro laminate in the same press.

1.) Stapelzuführung und automatische Beschickung der Platten. 1.) Batch Feeder and automatic loading of the plates.

2.) Feinschliff und Entstaubung der Platten-Oberseite. 2.) fine sanding and dedusting of the plate top.

3.) Beidseitige, wasserfeste Beleimung der Platten. 3.) Double-sided, waterproof gluing of the plates.

4.) Kaschierstation mit Trennmesser für Dekorpapiere oben und Gegenzugpapier unten, oder Gegenzugpapier von unten und Furniere von oben. 4.) laminating with separating knife for decorative papers above and below counteracting paper or backing paper from below and from above veneers.

5.) Auftragswalze für Grundlack von oben. 5.) application roller for base coat from above.

6.) Kaschierstation mit Trennmesser für Cellulosepapier - vorbeharzt und mit Spezialausrüstung von oben. 6.) laminating with separating knives for cellulose paper - vorbeharzt and special equipment from the top.

7.) Auftragswalze für Resistenzlack von oben - kurze Zwischentrocknung. 7) application roll for resistance paint from above - short intermediate drying.

8.) Auftragswalze für Decklack von oben. 8.) application roller for topcoat from above.

9.) Vortrocknung der Beschichtung mit einem Spezialtrockner mit einer Trockenzeit von 7 Minuten. 9) pre-drying the coating using a special dryer with a drying time of 7 minutes.

10.) Aushärtung in der Presse. 10.) curing in the press.

11.) 4-seitige Besäumung der Papier- oder Furnierüberstände. 11) 4-sided trimming of paper or veneer supernatants.

12.) Automatische Abstapelung der fertig beschichteten Platten mit Weitertransport der Platten zur nachfolgenden Bearbeitung. 12) Automatic stacking of the finished coated panels with further transport of the plates for subsequent processing.

Beispiel 3: Example 3:

Träger-Platten, Oberseite mit LIKAPAL-Farbgrund und Dekordruck im indirekten Tiefdruck, Unterseite wasserfest verleimt mit imprägniertem Gegenzug-Papier. Support plates with top LIKAPAL-color base and decorative printing in indirect intaglio printing, bottom waterproof gluing with return impregnated paper.

Hier erfolgt die Aushärtung der oberen Beschichtung und die Verleimung des Gegenzug- Papiers gleichzeitig in der gleichen Presse. Here, the curing of the top coat and the gluing of the paper Gegenzug- takes place simultaneously in the same press.

1.) Stapelzuführung und automatische Beschickung der Platten. 1.) Batch Feeder and automatic loading of the plates.

2.) Feinschliff und Entstaubung der Plattenoberseite. 2.) fine sanding and dust removal of the plate surface.

3.) Vorwärmung der Plattenoberfläche von oben. 3) preheating the surface plate from above.

4.) Lackwalze für Farbgrund von oben. 4) paint roller for color ground from above.

5.) Vortrocknung des Farbgrundes in einem Spezialtrockner mit einer Trockenzeit von 30 Sekunden. 5) pre-drying the ground color in a special dryer with a drying time of 30 seconds.

6.) Raster-Druckwerk für Fondfarbe zur Farbegalisierung Oberseite. 6.) raster printing unit for rear color to dye leveling top.

7.) Kurztrocknung der Fondfarbe Oberseite. 7.) Short drying the bottom color top.

8.) Druckwerk für Dekore Oberseite. 8.) printing unit for decors top.

9.) Auftragswalze für Grundlack Oberseite und Leimauftrag Unterseite. 9) application roller for base coat top and bottom glue.

10.) Kaschierstation mit Trennmesser für Cellulosepapier - evtl. vorbeharzt und mit Spezialausrüstung von oben und Gegenzugpapier von unten. 10.) laminating with separating blades for cellulose paper - possibly vorbeharzt and with special equipment from above and backing paper from below.

11.) Auftragswalze Decklack von oben. 11) form roller topcoat from above.

12.) Nach Bedarf Vortrocknung der Beschichtung mit einem Spezialtrockner, oder direkte Beschickung in die Presse Pos. 13.) ohne Vortrocknung. 12.) If necessary, pre-drying of the coating with a special dryer, or direct feeding into the press pos. 13) without pre-drying.

13.) Aushärtung in der Presse. 13.) curing in the press.

14.) 4-seitige Besäumung der Papierüberstände. 14) 4-sided trimming of the paper supernatants.

15.) Automatische Abstapelung der fertig beschichteten Platten mit Weitertransport der Stapel zur nachfolgenden Bearbeitung. 15) Automatic stacking of the finished plates coated with further transport of the stack for subsequent processing.

Die gemäß den vorstehenden Beispielen hergestellten Produkte sind lösungsmittelfrei, und konnten somit emissionsfrei hergestellt werden. The products produced according to the above Examples are solvent-free, and could thus be produced emissions. Dabei ist es möglich bei den gegenwärtig geltenden Grenzwerten für Formaldehyd das Qualitätszeichen "Blauer Engel" zu erreichen. It is possible with the currently applicable limits for formaldehyde the quality mark "Blue Angel" to achieve. Da mit den erfindungsgemäßen Beschichtungsmaterialien eine Vielzahl unterschiedlicher Formen und Materialien behandelt werden können, ist auch die Erfüllung kunden spezifischer Wünsche kostengünstig und problemlos möglich. As with the novel coating materials have a variety of shapes and materials can be treated, including meeting specific customer needs is inexpensive and easily available. Überraschenderweise wurde auch festgestellt, daß mit den erfindungsgemäßen Oberflächenbeschichtungsmaterialien Abriebwerte erzielt werden, die auch die Herstellung furnierter Küchenarbeitsplatten ermöglicht, welche bisher aufgrund von Abriebsfestigkeits-Überlegungen nahezu ausschließlich aus Kunststoff-Melamin gefertigt wurden. Surprisingly, it was also found that abrasion values ​​are achieved with the inventive surface coating materials, which also enables the production of veneered kitchen worktops which have been produced due to abrasion strength considerations almost exclusively of plastic melamine.

Claims (13)

1. Oberflächenbeschichtungsmaterial dadurch gekennzeichnet , daß es 1. Surface coating material characterized in that it
20-50 Teile flüssiges Harnstoff-Formaldehydharz 20-50 parts of liquid urea-formaldehyde resin
10-25 Teile Melaminharz 10-25 parts of melamine resin
2-3 Teile Weichmacher 2-3 parts of plasticizer
5-10 Teile Weichharz 5-10 parts soft resin
5-10 Teile Cellulosefasern 5-10 parts of cellulose fibers
2-5 Teile Antiabsetzmittel 2-5 parts anti-settling agent
2-5 Teile Wachse oder Wachsdispersion 2-5 parts waxes or wax dispersion
5-15 Teile Antiabriebmittel, 5-15 parts antiwear agents,
jeweils bezogen auf das Gewicht, enthält. in each case based on the weight, contains.
2. Oberflächenbeschichtungsmaterial nach Anspruch 1, dadurch gekennzeichnet, daß der Weichmacher Phthalsäure ist. 2. Surface coating material according to claim 1, characterized in that the plasticizer is phthalic acid.
3. Oberflächenbeschichtungsmaterial nach Anspruch 1 oder 2, dadurch gekenn zeichnet, daß das Weichharz Polyurethandiol ist. 3. Surface coating material according to claim 1 or 2, characterized in that the soft resin is polyurethane diol.
4. Oberflächenbeschichtungsmaterial nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß das Antiabsetzmittel Kieselsäureprodukte sind. 4. Surface coating material according to any one of the preceding claims, characterized in that the anti-settling agents are silica products.
5. Oberflächenbeschichtungsmaterial nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß das Antiabriebmittel Aluminiumverbindungen sind. 5. Surface coating material according to any one of the preceding claims, characterized in that the anti-abrasion agents are aluminum compounds.
6. Oberflächenbeschichtungsmaterial nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß es zusätzlich 5-30 Teile Farbstoffe, Farbstofflösungen und/oder Pigmente enthält. 6. Surface coating material according to any one of the preceding claims, characterized in that it additionally contains 5-30 parts of dyes, dye solutions and / or pigments.
7. Verwendung des Materials nach einem der Ansprüche 1 bis 6 in einem Ver fahren zur Herstellung beschichteter Oberflächen, dadurch gekennzeichnet, daß dieses mit einem Katalysator in Kontakt gebracht wird, und die so erhaltene Zusammensetzung auf der zu beschichtenden Oberfläche ausgehärtet wird. 7. Use of the material according to any one of claims 1 to 6 in a drive Ver for preparing coated surfaces, characterized in that this is brought into contact with a catalyst, and the composition thus obtained is cured on the surface to be coated.
8. Verwendung nach Anspruch 7, dadurch gekennzeichnet, daß der Katalysator eine Säure ist. 8. Use according to claim 7, characterized in that the catalyst is an acid.
9. Verwendung nach Anspruch 8, dadurch gekennzeichnet, daß die Säure ausge wählt ist aus Maleinsäure, Monobutylphosphorsäure, p-Toluolsulfonsäure, Zitronen säure oder einem Gemisch davon. 9. Use according to claim 8, characterized in that the acid is selected from maleic acid, monobutylphosphoric acid, p-toluenesulfonic acid lemons or a mixture thereof.
10. Verwendung nach Anspruch 7, dadurch gekennzeichnet, daß der Katalysator Aluminiumsulfat, Ammoniumchlorid oder Ammoniumsulfat ist. 10. Use according to claim 7, characterized in that the catalyst is aluminum sulfate, ammonium chloride or ammonium sulfate.
11. Verwendung nach einem der Ansprüche 7 bis 10, dadurch gekennzeichnet, daß der Katalysator vor dem Auftragen des Materials auf der zu beschichtenden Oberfläche mit dieser vermischt wird. 11. Use according to one of claims 7 to 10, characterized in that the catalyst is mixed on the surface to be coated with this prior to the application of the material.
12. Verwendung nach einem der Ansprüche 7 bis 10, dadurch gekennzeichnet, daß der Katalysator als gesonderter Auftrag vorab auf die zu beschichtende Oberfläche aufgebracht wird. 12. Use according to any one of claims 7 to 10, characterized in that the catalyst is applied as a separate contract in advance on the surface to be coated.
13. Verwendung nach einem der Ansprüche 7 bis 11, bei dem der Härtungsvorgang durchgeführt wird bei den folgenden Bedingungen: 13. Use according to any one of claims 7 to 11, wherein the curing is carried out at the following conditions:
Preßdruck: min 1 Kg/cm 2 Press pressure: min 1 Kg / cm 2
Preßtemperatur: min 60°C Objekt-Oberflächentemperatur Press temperature: 60 ° C min object surface temperature
Preßzeit: 180 Sekunden. Pressing time: 180 seconds.
DE1997125829 1997-06-18 1997-06-18 Surface coating material for wood used in furniture, wall panels etc. Expired - Fee Related DE19725829C1 (en)