DE19631762A1

DE19631762A1 - Fuel briquette

Info

Publication number: DE19631762A1
Application number: DE1996131762
Authority: DE
Inventors: Hans Ruf
Original assignee: Individual
Current assignee: Individual
Priority date: 1996-08-06
Filing date: 1996-08-06
Publication date: 1998-02-12

Abstract

The fuel briquette (1) has at least one grooved section (4), at right angles to its base surface (2), for breaking off. The briquette is composed of compressed hard wood waste, and especially chips and sawdust, together with vegetable matter for aroma and a mineral additive such as clay to slow down combustion.

Description

Die Erfindung betrifft ein Brennstoff-Brikett, insbesondere Grillbrikett, auf Holzbasis, wobei das Brikett im Kasten- oder Strangpreßverfahren geformt ist.The invention relates to a fuel briquette, in particular Barbecue briquette, wood-based, the briquette in the box or Extrusion process is formed.

Derartige Brennstoff-Briketts werden teilweise aus Holzmaterialien, aber auch aus Papierabfällen geformt und gepreßt, wobei die Holzbestandteile, z. B. kleingehäckseltes Restholz in einem Formkasten verpreßt werden. Eine ähnliche Herstellung von Brennstoff-Briketts ist im Strangpreßverfahren möglich, wobei jedoch die Festigkeit relativ gering ist.Such fuel briquettes are partially made Wood materials, but also formed from waste paper and pressed, the wooden components, e.g. B. finely chopped Residual wood can be pressed in a molding box. A similar Production of fuel briquettes is by extrusion possible, but the strength is relatively low.

Hierbei weist das Brennstoff-Brikett eine im wesentliche quaderförmige Form auf, so daß die Grundgröße des Brennstoff- Briketts relativ klein gewählt werden muß, um hier ein günstiges Anbrennverhalten zu erzielen. Dies gilt insbesondere in der Ausführung für Grillbriketts als Holzkohleersatz, da hierbei gegenüber der Verfeuerung in einem geschlossenen Ofen ungünstige Zugbedingungen herrschen. Zudem sind die Außenflächen derartiger kleiner Brennstoff-Briketts zur Erzielung ausreichender Festigkeit relativ hoch verdichtet, so daß das Anbrennverhalten weiterhin ungünstig beeinflußt wird. Von entscheidender wirtschaftlicher Bedeutung ist jedoch, daß aufgrund des schlechten Anbrennverhaltens derartige Brennstoff-Briketts nur mit Kantenlängen von etwa 3 cm × 3 cm ausgeführt werden können, so daß der Maschinenausstoß insgesamt unzureichend ist. Zudem sind derartige Brennstoff-Briketts aufgrund der durch das Anbrennverhalten bedingten kleinen Größe kaum stapelfähig.Here, the fuel briquette essentially has one cuboid shape so that the basic size of the fuel Briquettes must be chosen relatively small in order to be a cheap one To achieve burning behavior. This is especially true in the Version for barbecue briquettes as a charcoal substitute, because of this unfavorable compared to burning in a closed furnace Train conditions prevail. In addition, the outer surfaces are more small fuel briquettes to achieve sufficient Strength compressed relatively high, so that the burning behavior continues to be adversely affected. Of crucial However, economic importance is that due to the poor burning behavior of such fuel briquettes only can be executed with edge lengths of approximately 3 cm × 3 cm, so that the overall machine output is insufficient. In addition are such fuel briquettes due to the Burning behavior due to small size hardly stackable.

Demzufolge liegt der Erfindung die Aufgabe zugrunde ein Brennstoff-Brikett auf Holzbasis zu schaffen, das eine wirtschaftlichere Herstellung und ein verbessertes Anbrennverhalten ermöglicht. Accordingly, the invention is based on the object Wood-based fuel briquette to create one more economical manufacture and an improved one Burning behavior enabled.

Diese Aufgabe wird gelöst durch ein Brennstoff-Brikett gemäß den Merkmalen des Patentanspruches 1.This object is achieved by a fuel briquette according to the Features of claim 1.

Durch die Einformung von wenigstens einer Abbrechnut senkrecht zur Grundfläche des Briketts kann ein relativ großes Brikett von ca. 10-15 cm Kantenlänge (oder mehr) in einem Preßhub bearbeitet werden, so daß der Maschinenausstoß in einer Brikettierpresse erheblich erhöht wird. Die zum Anbrennen erforderliche kleinere Größe kann durch Abbrechen entlang der Nut in einfacher Weise vom Anwender je nach Bedarf durchgeführt werden. Durch die somit gebildete relativ rauhe Bruchkante wird zudem das Anbrennverhalten in diesem Bereich wesentlich verbessert. Darüberhinaus wird durch das Einformen bzw. Einpressen der Abbrechnuten das Holzmaterial auch in Querrichtung verdichtet, so daß die Festigkeit wesentlich erhöht wird. Somit sind derartig große Brennstoff-Briketts sehr gut stapelbar, so daß die Brennstoff-Briketts anstatt als Schüttgut als Palettenware angeboten werden kann. Durch die bei Stapelung als Lüftungsschlitze dienenden Abbrechnuten wird hierbei die Abtrocknung der so gepreßten Brennstoff-Briketts erheblich verbessert, insbesondere wenn Restholz verpreßt wird.By forming at least one break-off groove vertically a relatively large briquette of approx. 10-15 cm edge length (or more) in one press stroke are processed so that the machine output in one Briquetting press is increased significantly. The one to burn required smaller size can be found by canceling along the Groove easily carried out by the user as needed will. Due to the relatively rough breaking edge thus formed the burning behavior in this area is also significant improved. In addition, by molding or Press the break-off grooves into the wood material Transversely compressed, so that the strength increases significantly becomes. Such large fuel briquettes are very good stackable so that the fuel briquettes instead of bulk can be offered as pallet goods. By stacking The break-off grooves serving as ventilation slots are used here Drying of the pressed fuel briquettes considerably improved, especially when residual wood is pressed.

Darüberhinaus eignet sich diese Gestaltung auch sehr gut für das Strangpreßverfahren, da hierbei die Preßmatrize relativ groß gefertigt werden kann und aufgrund des großen Durchlaßquerschnittes Verstopfungen der Preßmatrize entgegengewirkt werden kann. Aufgrund des relativ großen Formquerschnittes können zudem dem Holzbasisstoff Beimengungen zugegeben werden, beispielsweise öl- oder harzhaltige Pflanzenteile als Bindemittel oder Pflanzenteile als Duftstoffzusatz z. B. Lorbeer- oder Wacholderblätter. Im letzteren Fall kann somit das Brennstoff-Brikett auch zur Räucherung oder als spezielles Kaminholz mit starker Duftwirkung verwendet werden. Durch die mögliche Zumischung von Nadeln, Blättern oder Fruchtständen von Bäumen oder Sträuchern ergibt sich durch das darin im allgemeinen enthaltene Harz zudem ein besserer Verbund der Brennstoff-Briketts, so daß bei gleicher Festigkeit der Preßdruck verringert werden kann.In addition, this design is also very suitable for that Extrusion process, since the die is relatively large can be manufactured and because of the large Passage cross-section blockages of the die can be counteracted. Because of the relatively large Cross-sectional shape can also add to the wood base material be added, for example oil or resinous Plant parts as binders or plant parts as Fragrance additive z. B. bay or juniper leaves. in the in the latter case, the fuel briquette can also be used Incense or as a special firewood with a strong fragrance be used. Due to the possible addition of needles, Leaves or fruit stands of trees or shrubs the resin generally contained therein better bond of the fuel briquettes, so that at the same Strength of the pressure can be reduced.

Weiterhin können aufgrund der nun möglichen großen Querschnittsform des Formkastens bzw. der Preßmatrize auch mineralische Zusätze, z. B. Lehm, als Brennverzögerer zugegeben werden oder andererseits ölhaltige pflanzliche Reststoffe, z. B. Schalen von Oliven oder Kokosfasern als Brennbeschleuniger. Somit kann je nach Anwendungszweck des Brennstoff-Briketts, beispielsweise als Grillbrikett oder zur Ofenfeuerung das Abbrennverhalten eingestellt werden. Ebenfalls kann durch solche eingemischten Zusätze eine Anpassung auf die Partikelgröße des Basismaterials, bevorzugt Restholz aus der holzverarbeitenden Industrie, z. B. Hobel-, Fräs- und Sägespäne erfolgen, um so das gewünschte Abbrennverhalten zu erzielen.Furthermore, due to the now possible large Cross-sectional shape of the mold box or the press die also mineral additives, e.g. B. clay, added as a fire retardant are or on the other hand oil-containing vegetable residues, e.g. B. Peel of olives or coconut fibers as a burning accelerator. Depending on the application of the fuel briquette, for example as a grill briquette or for furnace firing Burning behavior can be set. Likewise, through such mixed additives an adjustment to the particle size of the Base material, preferably residual wood from the wood processing Industry, e.g. B. planing, milling and sawdust, so that to achieve the desired burning behavior.

Weitere bevorzugte Ausführungsbeispiele sind Gegenstand der Unteransprüche. Nachfolgend wird ein Ausführungsbeispiel eines Brennstoff-Briketts anhand der Zeichnungen näher erläutert und beschrieben. Hierbei zeigen:Further preferred exemplary embodiments are the subject of Subclaims. An exemplary embodiment of a Fuel briquettes explained in more detail using the drawings and described. Here show:

Fig. 1 eine Seitenansicht eines Brennstoff-Briketts; und Figure 1 is a side view of a fuel briquette. and

Fig. 2 eine zugehörige Draufsicht auf das Brennstoff-Brikett gemäß Fig. 1. FIG. 2 shows an associated top view of the fuel briquette according to FIG. 1.

In Fig. 1 ist ein Brennstoff-Brikett 1 etwa in Originalgröße dargestellt, das eine im wesentliche quaderförmige Grundform aufweist. Das Brikett 1 wird von einer bevorzugt planen Grundfläche 2, einer unterbrochenen Oberseite 3 und vier Seitenflächen 1′ begrenzt. Ausgehend von der Oberseite 3 sind hier zwei Abbrechnuten 4 eingeformt. Die Abbrechnuten 4 haben hierbei bevorzugt eine Tiefe, die größer als die halbe Brikettdicke D ist. Hierdurch wird das Abteilen des Brennstoff-Briketts 1 in drei leisten- oder barrenförmige Teil-Briketts wesentlich erleichtert. Das Abbrechen erfolgt hierbei unter Ausbildung jeweils einer Bruchkante 7, wie dies mit einer Wellenlinie entlang dem Nutengrund 4a der Abbrechnut 4 angedeutet ist. Der Nutengrund 4a ist zudem bevorzugt abgerundet ausgebildet, um die Standzeit der Preßstempels oder der Preßmatrize zu erhöhen. Die Abbrechnut 4 weist hierbei eine im wesentlichen dreieckige Querschnittsform auf, wobei die beiden Flanken 4b der Abbrechnut 4 bevorzugt einen Winkel von 45° einschließen. Hierdurch wird eine zusätzliche Verdichtung in Querrichtung (hier horizontal) erzielt.In Fig. 1, a fuel briquette 1 is shown approximately in original size, which has an essentially cuboid basic shape. The briquette 1 is delimited by a preferably flat base area 2 , an interrupted upper side 3 and four side areas 1 '. Starting from the top 3 , two break-off grooves 4 are formed here. The break-off grooves 4 preferably have a depth that is greater than half the briquette thickness D. This makes it much easier to divide the fuel briquette 1 into three strip-shaped or bar-shaped partial briquettes. The breaking off takes place with the formation of a breaking edge 7 , as is indicated by a wavy line along the bottom 4 a of the break-off groove 4 . The bottom of the groove 4 a is also preferably rounded in order to increase the service life of the ram or the die. The break-off groove 4 has an essentially triangular cross-sectional shape, the two flanks 4 b of the break-off groove 4 preferably enclosing an angle of 45 °. This results in additional compression in the transverse direction (here horizontally).

Zur Erleichterung des Abbrechens der einzelnen Teil-Briketts entlang dem Nutengrund 4a zur Bildung jeweils einer Bruchkante 7 können auch ausgehend von der Grundfläche 2 kleinere Nuten 4′ als Sollbruchstelle eingeformt sein, wie dies in Strichlinien angedeutet ist. Wenn somit derartige Hilfs-Abbrechnuten 4′ eingeformt sind, kann die hier obere Abbrechnut 4 weniger tief ausgebildet sein. Es hat sich jedoch bewährt, daß die obere Abbrechnut 4 tiefer ist als die halbe Brikettdicke D oder insgesamt die Tiefen der sich beiden gegenüberliegenden Abbrechnuten 4 und Hilfs-Abbrechnut 4′ wenigstens die halbe Brikettdicke D einnehmen. Der Verzicht auf derartige Hilfs-Abbrechnuten 4′ ermöglicht jedoch eine einfachere Gestaltung des Preßwerkzeuges.To facilitate the breaking off of the individual partial-briquettes along the groove bottom 4 a to form a respective break edge 7 and starting can be molded as a predetermined breaking point, as indicated in dashed lines from the base 2 smaller grooves 4 '. If such auxiliary break-off grooves 4 'are thus formed, the upper break-off groove 4 here can be made less deep. However, it has been found that the upper break-off groove 4 is deeper than half the briquette thickness D or the depths of the two opposite break-off grooves 4 and auxiliary break-off groove 4 'are at least half the briquette thickness D. Dispensing with such auxiliary break-off grooves 4 ', however, enables a simpler design of the pressing tool.

So kann bei dem Pressen gemäß dem Kastenpreßverfahren der an der Grundfläche 2 angreifende Preßstempel, wie dies durch den Pfeil FP angedeutet ist, plan ausgebildet sein. Es sei jedoch darauf hingewiesen, daß beim Form- bzw. Kastenpreßverfahren der Preßstempel auch an der Oberseite 3 angreifen kann, wodurch dann die Preßform dementsprechend vereinfacht wird. Je nach Angriffsrichtung des Preßstempels kann somit an der Oberseite 3 oder an der Grundfläche 2 ein etwas geringer verdichteter Bereich 5 gebildet werden, wie dies hier punktiert dargestellt wird. An diesem Bereich wird somit das Anbrennverhalten aufgrund seiner niedrigeren Verdichtung ebenfalls verbessert.Thus, in the case of the pressing according to the box pressing method, the pressing die acting on the base surface 2 , as indicated by the arrow FP, can be made flat. However, it should be pointed out that in the case of the molding or box pressing method, the press ram can also act on the upper side 3 , which then simplifies the press mold accordingly. Depending on the direction of attack of the press ram, a slightly less compressed area 5 can thus be formed on the upper side 3 or on the base area 2 , as is shown here in dotted lines. In this area, the burning behavior is also improved due to its lower compression.

In Fig. 2 ist eine Draufsicht auf ein Brennstoff-Brikett 1 gemäß Fig. 1 dargestellt. Für das bevorzugt verwendete Kastenpreßverfahren sind hierbei die Ecken 6 zwischen den Seitenflächen 1′ abgerundet, um die Ausformung zu verbessern. Zudem können hierbei die Abbrechnuten 4 auch schräg, gekrümmt oder sich schneidend ausgebildet sein. Wie angedeutet, kann das vorgeschlagene Brennstoff-Brikett 1 jedoch auch im Strangpreßverfahren geformt werden, indem die Holz-Preßmasse entsprechend dem Pfeil SP durch eine nicht näher dargestellte Preßmatrize mit hohem Druck hindurchgefördert und abgelängt wird. Die Preßmatrize würde in dem Fall den Negativquerschnitt entsprechend Fig. 1 aufweisen. Die Abbrechnuten 4 können somit auch kontinuierlich im Strangpreßverfahren eingeformt werden. FIG. 2 shows a top view of a fuel briquette 1 according to FIG. 1. For the preferably used box pressing process, the corners 6 between the side surfaces 1 'are rounded off in order to improve the shape. In addition, the break-off grooves 4 can also be designed obliquely, curved or intersecting. As indicated, however, the proposed fuel briquette 1 can also be formed in the extrusion process by conveying and cutting the wood molding compound according to arrow SP through a pressing die (not shown in greater detail). In this case, the press die would have the negative cross section corresponding to FIG. 1. The break-off grooves 4 can thus also be continuously molded in the extrusion process.

Die Herstellung des Brennstoff-Briketts erfolgt bevorzugt auf einer Brikettiermaschine gemäß der DE-C-33 33 766 oder EP-B-0 367 859 des Anmelders. In die Preßmasse können hierbei im Bereich der Zuführschnecken gegebenenfalls mit zusätzlichen Mischvorrichtungen zugegeben werden, z. B. ölhaltige Pflanzenteile als Bindemittel oder als Duftstoffzusatz Nadeln oder Blätter eines Baumes oder Strauches. Aufgrund des relativ großen Querschnittes der Preßform ist es auch möglich mineralische Zusätze, die ansonsten sehr verschleißfördernd wären, zuzumischen, da nur ein sehr geringer Anteil dieser mineralischen Zusätze an die Wandungen der Preßform gelangt. So kann beispielsweise Lehm als Bindemittel, aber bevorzugt als Brennverzögerer eingesetzt werden, während z. B. Pflanzenschalen als Brennbeschleuniger zugegeben werden kann. Die Zugabe eines Brennverzögerers bzw. Brennbeschleunigers richtet sich insbesondere nach dem Ausgangsmaterial, beispielsweise der Feinheit des Restholzes aus der Naturholzbearbeitung, z. B. Hobel-, Fräs- und Sägespäne aus Hartholz.The fuel briquette is preferably produced on a briquetting machine according to DE-C-33 33 766 or Applicant's EP-B-0 367 859. In the molding compound can Area of the feed screws with additional if necessary Mixing devices are added, e.g. B. oily Plant parts as a binder or as a fragrance additive needles or leaves of a tree or shrub. Because of the relative large cross section of the mold, it is also possible mineral additives, which are otherwise very wear-promoting would have to be mixed, since only a very small proportion of these mineral additives reaches the walls of the mold. So can, for example, clay as a binder, but preferably as Burn retardants are used while z. B. plant shells can be added as a burning accelerator. The addition of a Burning retarder or burning accelerator is aimed especially according to the starting material, for example the Fineness of the residual wood from natural wood processing, e.g. B. Planing, milling and sawdust made of hardwood.

So können bei relativ grobkörnigem Restholz als Bindemittel und Brennbeschleuniger Schalen von Ölsaaten zugemischt werden, während bei relativ feinen Holzabfall (z. B. aus der Schleifbearbeitung) auf derartige Zusätze im allgemeinen verzichtet werden kann. Vielmehr kann der Einsatz eines Brennverzögerers in Form von einigen Prozenten Lehmzusatz erforderlich sein, um ein zu rasches Abbrennen an der Bruchkante 7 bzw. dem aufgelockerten Bereich 5 zu vermeiden. Es sei darauf hingewiesen, daß entlang der Bruchkante 7 zur Aufteilung des Brennstoff-Briketts 1 in mehrere leisten- oder barrenförmige Teil-Briketts eine relativ rauhe und damit gegenüber der ansonsten glatten Brikettoberfläche für das Anbrennverhalten günstige Zone geschaffen wird. Insbesondere wird jedoch gegenüber den ansonsten kleinen, schüttgutartigen Briketts ein etwa zehnmal so großer Brikett 1 geschaffen, der sehr gut zu stapeln ist und den Maschinenausstoß in ähnlichem Maße erhöht. Das Brikett 1 besteht dabei ausschließlich aus biologischen bzw. pflanzlichen Stoffen, so daß keine Klebstoffe oder dgl. schädliche Kunststoffe verbrannt werden.In the case of relatively coarse-grained residual wood, shells of oilseeds can be mixed in as binders and accelerators, while in the case of relatively fine wood waste (e.g. from grinding work), such additives can generally be dispensed with. Rather, the use of a fire retardant in the form of a few percent addition of clay may be necessary in order to avoid too rapid burning off at the breaking edge 7 or the loosened area 5 . It should be noted that along the breaking edge 7 for dividing the fuel briquette 1 into several strip-shaped or bar-shaped partial briquettes, a relatively rough zone is created which is favorable for the burning behavior compared to the otherwise smooth briquette surface. In particular, compared to the otherwise small, bulk-like briquettes, briquettes 1 are created which are approximately ten times as large and which are very easy to stack and increase the machine output to a similar extent. The briquette 1 consists exclusively of biological or vegetable substances, so that no adhesives or the like. Harmful plastics are burned.

Claims

1. fuel briquette, in particular grill briquette, wood-based, the briquette being shaped in the box or extrusion process, characterized in that at least one break-off groove ( 4 ) is formed perpendicular to the base surface ( 2 ) of the briquette ( 1 ).

2. Fuel briquette according to claim 1, characterized in that the break-off groove ( 4 ) is deeper than half the briquette thickness (D).

3. Fuel briquette according to claim 1 or 2, characterized in that two break-off grooves ( 4 ) are arranged at the same pitch parallel to a side surface ( 1 ') of the fuel briquette ( 1 ).

4. Fuel briquette according to one of claims 1 to 3, characterized in that the groove base ( 4 a) of the break-off groove ( 4 ) is rounded.

5. Fuel briquette according to one of claims 1 to 4, characterized in that the break-off groove ( 4 ) each has a triangular cross-sectional shape.

6. Fuel briquette according to claim 5, characterized in that the flanks ( 4 b) of the break-off groove ( 4 ) enclose an angle of 45 °.

7. Fuel briquette according to one of claims 1 to 6, characterized in that the fuel briquette ( 1 ) is pressed perpendicular to the base ( 2 ).

8. Fuel briquette according to one of claims 1 to 7, characterized in that the base ( 2 ) is square.

9. Fuel briquette according to one of claims 1 to 8, characterized in that the corners ( 6 ) of the fuel briquette ( 1 ) are rounded.

10. Fuel briquette according to one of claims 1 to 9, characterized in that the top ( 3 ) of the fuel briquette ( 1 ) is carried out substantially flat.

11. Fuel briquette according to one of claims 1 to 10, characterized in that the fuel briquette from residual wood, especially planer, Milling and sawdust consists of hardwood.

12. fuel briquette according to claim 11, characterized in that the residual wood as a binder and / or as a fragrance additive Plant parts are added.

13. Fuel briquette according to one of claims 1 to 12, characterized in that mineral additives, especially clay, as Burn retarders are added.