DE19530508A1 - Dry peelable, breathable, tear-proof and strong laminated wall covering - Google Patents
Dry peelable, breathable, tear-proof and strong laminated wall coveringInfo
- Publication number
- DE19530508A1 DE19530508A1 DE19530508A DE19530508A DE19530508A1 DE 19530508 A1 DE19530508 A1 DE 19530508A1 DE 19530508 A DE19530508 A DE 19530508A DE 19530508 A DE19530508 A DE 19530508A DE 19530508 A1 DE19530508 A1 DE 19530508A1
- Authority
- DE
- Germany
- Prior art keywords
- wallpaper
- wallpaper according
- polyethylene
- layer
- visible side
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die Erfindung betrifft eine mehrschichtige Tapete, deren sichtseitige Schicht aus Polyethylen besteht, welche mit einer Trägerschicht verbunden ist. Die Trägerschicht kann aus Papier oder anderen, überwiegend Cellulosefasern ent haltenden Flächengebilden bestehen.The invention relates to a multi-layer wallpaper, the visible layer made of polyethylene, which with a carrier layer is connected. The backing layer can from paper or other, mainly cellulose fibers holding flat structures exist.
Durch die genannten Merkmale gekennzeichnete Tapeten sind bereits bekannt und werden z. B. in den DE-Gebrauchs mustern 86 00 174 und 94 02 973 in verschiedener Ausfüh rung beschrieben.Wallpapers characterized by the features mentioned are already known and z. B. in DE use samples 86 00 174 and 94 02 973 in different versions tion described.
Bekanntlich weisen Tapeten, die an ihrer Oberseite eine Kunststoffschicht tragen, eine Reihe von Vorteilen gegen über reinen Papiertapeten auf. Wegen ihrer Unempfindlich keit gegenüber Wasser sind sie abwaschbar und daher leicht zu reinigen. Infolge der Festigkeit, Elastizität und Geschlossenheit ihrer Oberfläche resultiert eine re lativ hohe Stabilität gegenüber mechanisch einwirkenden Kräften sowohl bei der Verarbeitung als auch im Gebrauch.As is well known, wallpapers have one on the top Wear plastic layer, a number of advantages against over pure paper wallpaper. Because of their insensitivity They are washable against water and therefore easy to clean. Due to the strength, elasticity and the unity of its surface results in a re relatively high stability against mechanically acting Powers both in processing and in use.
Unter den Kunststoffen, die für die Tapeten-Deckschichten bisher bekannt sind und praktisch eingesetzt werden, nimmt Polyethylen eine besondere Stellung aufgrund seiner chemischen Eigenschaften ein. Es erweist sich gegenüber zahlreichen Lösungsmitteln wesentlich weniger empfindlich als z. B. Polyacrylate ("Acryltapete") oder Polyvinyl chlorid ("Vinyltapete"). Während letztgenanntes im Falle eines Brandes giftige Gase (Chlorwasserstoff) entwickelt, verbrennt Polyethylen rückstandslos zu den auch in der Natur vorkommenden Stoffen Wasser und Kohlendioxid. Hin sichtlich der Herstellung, Verarbeitung und Entsorgung gehört Polyethylen zu den hygienisch unbedenklichsten und umweltfreundlichsten Kunststoffen.Among the plastics used for the wallpaper cover layers are known and used in practice so far takes a special position due to its polyethylene chemical properties. It turns out to be numerous solvents much less sensitive as z. B. polyacrylates ("acrylic wallpaper") or polyvinyl chloride ("vinyl wallpaper"). While the latter in the case of a fire develops toxic gases (hydrogen chloride), burns polyethylene without residue to those in the Naturally occurring substances water and carbon dioxide. There with regard to production, processing and disposal Polyethylene is one of the most hygienically safe and most environmentally friendly plastics.
Bei den Tapeten nach DE-Gebrauchsmuster 86 00 174 wird Polyethylen in Form von Folien mit relativ niedrigen Flä chenmassen eingesetzt, die auch mattiert, in Substanz ge färbt, oberflächlich aufgerauht und gegebenenfalls auch bedruckt sein können. Allerdings wird wegen der be grenzten Haftungsfähigkeit der Druckfarben auf der glat ten Folienoberfläche das Bedrucken der Papierträger schicht empfohlen. Wegen der Verschleierung des Druck bildes verbieten sich dann aber offensichtlich mattierte und gefärbte Folien. Um bei den vorgeschlagenen Tapeten das Durchdringen von Farbflecken aus dem Untergrund zu vermeiden, werden schwere, mehrlagige Papierträgerschich ten mit Flächenmassen bis zu 230 Gramm pro Quadratmeter verwendet. Damit können zwar relativ tiefstrukturierte Prägungen erzielt werden, jedoch bereiten die karton ähnlich steifen Endprodukte bei der Verarbeitung er fahrungsgemäß Schwierigkeiten.For the wallpaper according to DE utility model 86 00 174 Polyethylene in the form of films with a relatively low area masses used, also matted, in substance colors, roughened on the surface and possibly also can be printed. However, because of the be limited the adhesiveness of the inks on the glat printing on the paper carrier layer recommended. Because of the concealment of the print picture then obviously prohibit matted and colored foils. To the proposed wallpaper the penetration of color spots from the underground avoid heavy, multi-layer paper carrier layer with masses of up to 230 grams per square meter used. This can be relatively deeply structured Embossing can be achieved, however, prepare the cardboard similarly rigid end products during processing Difficulties due to driving.
Diese Nachteile sollen Tapeten nach DE-Gebrauchsmuster 94 02 973 vermeiden, bei denen Deckschichten aus geschäumtem Polyethylen eingesetzt werden, welche die Trägerschichten aus leichteren, aber ebenfalls mehrlagigen Papieren in ihrer Dicke erheblich übertreffen. Die Polyethylenschicht kann auch hier farblos oder gefärbt, bedruckt und durch Prägung oder Aufrauhung strukturiert sein. Allerdings er fordert die Aufbringung der Polyethylen-Deckschicht durch direkte Extrusion spezielle technische Vorrichtungen, wie auch die alternativ vorgeschlagene Verarbeitung vorge schäumter Polyethylenfolien auf herkömmlichen Maschinen der Papiertapetenfertigung nicht ohne weiteres möglich ist.These disadvantages are said to be wallpaper according to DE utility model 94 Avoid 02 973 where the top layers are made of foamed Polyethylene are used, which are the backing layers from lighter, but also multilayered papers in significantly exceed their thickness. The polyethylene layer can also be colorless or colored, printed and through Textured embossing or roughening. However he did demands the application of the polyethylene cover layer direct extrusion special technical devices, such as also the alternative processing proposed foamed polyethylene films on conventional machines the paper wallpaper production not easily possible is.
Aus bauphysikalischer Sicht mangelt es den bisher vorge schlagenen Polyethylen-Deckschichten und den damit herge stellten Tapeten an Atmungsaktivität infolge unzureichen der Gasdurchlässigkeit.From the building physics point of view, there is a shortage of the ones previously described beaten polyethylene cover layers and the provided wallpapers with insufficient breathability as a result the gas permeability.
Die Verlegung von Tapeten der vorgenannten Art erfordert wegen ihres kompakten Aufbaus und ihrer hohen Flächenmas sen meistens die Anwendung spezieller, verstärkter Klebe mittel, z. B. Dispersionskleber, die bei der Trocknung zur wasserfesten Verbindung von Tapete und Untergrund führen. Infolge der geschlossenen Oberfläche einerseits und der Festigkeit der Verklebung mit dem Untergrund andererseits ist die Wiederentfernung der Tapeten sehr erschwert und kostenaufwendig.The laying of wallpapers of the aforementioned type requires because of their compact design and their large area mostly use special, reinforced adhesive medium, e.g. B. dispersion adhesive, which is used for drying waterproof connection of wallpaper and surface. Due to the closed surface on the one hand and the Strength of the bond to the substrate on the other hand the removal of the wallpaper is very difficult and expensive.
Der Erfindung liegt die Aufgabe zugrunde, eine Tapete der eingangs gekennzeichneten Art ohne Verzicht auf die be kannten, sich aus der Verwendung von Polyethylen-Deck schichten ergebenden Vorteile, weiterzuentwickeln und so auszubilden, daß bei Gewährleistung einer hohen Stabili tät die Flächenmasse der Trägerschicht vermindert werden kann und daß eine atmungsaktive und nach der Verarbeitung trocken spaltbare Tapete resultiert.The invention has for its object a wallpaper initially identified type without waiving the be knew from the use of polyethylene deck resulting benefits, evolve and so train that while ensuring high stabili the mass per unit area of the carrier layer can be reduced can and that is breathable and after processing dry fissile wallpaper results.
Erfindungsgemäß wird diese Aufgabe dadurch gelöst, daß die Sichtseitenschicht aus einem thermisch-mechanisch verfestigtem Faservlies aus Polyethylen (PE)-Endlosfasern besteht (Anspruch 1). Derartige Faservliese sind sowohl trocken als auch naß bilateral hochfest und unter praxis üblichen Beanspruchungen unzerreißbar. Ihre mikroporöse Feinstruktur ermöglicht es, Tapeten der eingangs gekenn zeichneten Art so auszubilden, daß ohne Verzicht auf den Schutz des Untergrundes gegen Wasser die angestrebte At mungsaktivität als bauphysikalisch wertvolle Eigenschaft erzielt wird. Infolge der mehrfachen Lichtbrechung zwi schen den PE-Feinfasern und der eingeschlossenen Luft be sitzen die Faservliese ohne zusätzliche Mattierungsmittel eine hohe Opazität, die einen erheblichen Beitrag zur op tischen Untergrundabdeckung erbringt. Zusätzlich wirkt, insbesondere bei nicht bedruckten und schwach geprägten Tapeten, das arteigene Faserwirbelbild. Als Polyethylen (PE) wird Hochdruck-Polyethylen (HDPE) bevorzugt.According to the invention this object is achieved in that the visible side layer from a thermal-mechanical Consolidated nonwoven made of continuous polyethylene (PE) fibers exists (claim 1). Such non-woven fabrics are both dry and wet bilaterally high strength and under practice usual stresses are unbreakable. Your microporous Fine structure makes it possible to identify wallpapers of the beginning traced kind so that without giving up the Protection of the underground against water the desired At activity as a building physically valuable property is achieved. Due to the multiple light refraction between the PE fine fibers and the enclosed air the non-woven fabrics sit without additional matting agents a high opacity, which makes a significant contribution to the op table provides underground coverage. In addition, especially for non-printed and slightly embossed Wallpaper, the species' own fiber swirl pattern. As polyethylene (PE), high pressure polyethylene (HDPE) is preferred.
Vorteilhafterweise beträgt die Flächenmasse der PE- oder HDPE-Faservliese 35 Gramm pro Quadratmeter oder mehr (Anspruch 2). Technisch und wirtschaftlich besonders zweckmäßig sind Deckschichten dieser Art mit Flächen massen zwischen 40 und 60 Gramm pro Quadratmeter, ohne jedoch die Erfindung darauf zu beschränken (Anspruch 3).The basis weight of the PE or is advantageously HDPE nonwovens 35 grams per square meter or more (Claim 2). Technically and economically special Cover layers of this type with surfaces are expedient measure between 40 and 60 grams per square meter without however, to limit the invention to this (claim 3).
Die PE-Faservliese können zwecks Variation der Ober flächenbeschaffenheit beständig coronabehandelt sein (Anspruch 4), was sich vor allem für die weitere Ver edlung vorteilhaft erweist.The PE non-woven fabrics can be used to vary the upper surface texture be corona treated (Claim 4), which is especially for the further Ver noble proves advantageous.
Das Laufverhalten auf Maschinen und die Handhabung der Tapeten bei der Verarbeitung kann durch eine antistati sche Ausrüstung der PE-Faservliese verbessert werden (Anspruch 5); insbesondere wird dadurch auch die Attrak tion von Verunreinigungen während der Herstellung und beim Gebrauch der Tapeten minimiert.The running behavior on machines and the handling of the Wallpaper during processing can be done by an antistati equipment of PE nonwovens can be improved (Claim 5); in particular this also makes the Attrak tion of impurities during manufacture and minimized when using the wallpaper.
Es hat sich überraschenderweise gezeigt, daß PE-Faser vliese mit lösungsmittelfreien, wasserbasierten Pigment farben einwandfrei wisch- und wasserfest bedruckbar und damit die an Tapeten gestellten Anforderungen erfüllbar sind (Anspruch 6). Somit können umweltverträgliche Druck farben verwendet werden und es entfällt die Ein schränkung, die Farbgebung auf der Trägerschicht ausfüh ren zu müssen.It has surprisingly been found that PE fiber fleeces with solvent-free, water-based pigment colors perfectly printable and smudge-proof and waterproof so that the requirements placed on wallpaper can be met are (claim 6). Thus, environmentally friendly printing colors are used and there is no one limitation, the coloring on the carrier layer need to.
Weiterhin war die Feststellung überraschend, daß ein er findungsgemäßer Kaschierverbund von PE-Faservlies und ei ner Trägerschicht, vorzugsweise einer Papierträgerschicht zu einer Tapete führt, die nach der Verlegung an der Ka schierschicht trocken spaltbar ist (Anspruch 7). Hierbei ist es vorteilhaft, die Tapete mit Hilfe eines wasserfest trocknenden Dispersionsklebers zu verlegen.Furthermore, it was surprising to find that he Laminating composite of PE fiber fleece and egg according to the invention ner backing layer, preferably a paper backing layer leads to a wallpaper that after laying on the Ka shear layer is dry fissile (claim 7). Here it is advantageous to use a waterproof wallpaper drying dispersion adhesive.
Bei beabsichtigter Erneuerung der Wandbekleidung kann beispielsweise die PE-Deckschicht (nach örtlich eng be grenzter mechanischer Lockerung am Tapetenrand) durch vertikal von der Wand weggerichteten kräftigen Zug in ganzer Bahn von der Papierschicht abgetrennt werden, wo bei letztere fest mit dem Untergrund verbunden bleibt. Diese Trennung von Polyethylen und Papier erleichtert ei nerseits die Entsorgung des Polyethylenabfalls in Form eines nahezu sortenreinen recycelbaren Materials und an dererseits bildet das an der Wand verbleibende Papier ge meinsam mit der stabilen Kleberschicht eine den Unter grund gut abschirmende Makulatur für die Neutapezierung.If the wallcovering is intended to be replaced For example, the PE top layer (according to closely limited mechanical loosening at the edge of the wallpaper) strong pull vertically away from the wall whole web are separated from the paper layer where the latter remains firmly connected to the subsurface. This separation of polyethylene and paper makes it easier on the other hand, the disposal of the polyethylene waste in the form an almost pure recyclable material and on the other hand, the paper remaining on the wall forms ge together with the stable adhesive layer one the sub reasonably well shielded waste for new upholstery.
Als Trägerschichten kommen vorzugsweise Flächengebilde zum Einsatz, bei denen Cellulosefasern den überwiegenden Bestandteil bilden, wie Papiere oder vliesartige Gebilde. Es eignen sich bereits einfache Unterbahnpapiere mit Flä chenmassen vorzugsweise bis zu 130 Gramm pro Quadrat meter, ebenso aber auch mehrlagige Papiere, ohne daß die erfindungsgemäßen Tapeten hinsichtlich ihrer Papier- Träger-Schichten auf bestimmte Flächenmassen beschränkt sind (Ansprüche 8, 9 und 10).Flat structures are preferably used as carrier layers used in which cellulose fibers predominate Form part, such as papers or non-woven structures. Simple underlayer papers with flä are already suitable chenmassen preferably up to 130 grams per square meters, but also multi-layer papers, without the wallpapers according to the invention with regard to their paper Backing layers limited to certain masses are (claims 8, 9 and 10).
Allgemein, vorzugsweise jedoch bei der Verwendung ein facher Unterbahnpapiere für die Trägerschichten, erweist sich die Beimischung anorganischer Weißpigmente wie Titandioxid zum Kaschiermittel vorteilhaft für das opti sche Erscheinungsbild der Tapeten (Anspruch 15).Generally, but preferably when using one fold underlayer papers for the backing layers, proves the admixture of inorganic white pigments such as Titanium dioxide to the lamination agent advantageous for the opti cal appearance of the wallpaper (claim 15).
Die erfindungsgemäßen Tapeten eignen sich besonders in der Ausführung als geprägte Tapeten (Anspruch 11) mit ei ner gegenüber reinen Papiertapeten verbesserten Präge stabilität.The wallpapers of the invention are particularly suitable in the execution as embossed wallpaper (claim 11) with egg improved embossing compared to pure paper wallpaper stability.
Die nachfolgenden Beispiele sollen die Erfindung erläu tern, ohne sie darauf zu beschränken.The following examples are intended to explain the invention without limiting it to them.
Ein verfestigtes, beständig coronabehandeltes und anti statisch ausgerüstetes Faservlies aus Hochdruck-Poly ethylenendlosfasern mit einer Flächenmasse von ca. 42,5 Gran pro Quadratmeter wird mit wasserbasierten Pigment farben, wie sie zum Bedrucken von Papiertapeten üblich sind, im Tiefdruckverfahren in bekannter Weise bedruckt, getrocknet und aufgerollt. In einem zweiten Arbeitsgang wird diese bedruckte Polyethylenbahn auf einer Kaschier- Präge-Anlage mit Hilfe eines wäßrigen Kaschierklebers auf Basis von Polyvinylacetat, der 9,5 Masseprozent Titandioxid enthält, mit einer Unterbahn aus Papier der Flächenmasse 120 Gramm pro Quadratmeter verbunden und un mittelbar anschließend kalt geprägt, getrocknet und wie üblich konfektioniert.A solidified, constantly corona-treated and anti statically equipped nonwoven made of high pressure poly continuous ethylene fibers with a basis weight of approx. 42.5 Gran per square meter is made with water-based pigment colors as usual for printing on paper wallpaper are printed in a known manner using the gravure printing process, dried and rolled up. In a second step is this printed polyethylene web on a laminating Embossing system with the help of an aqueous laminating adhesive based on polyvinyl acetate, the 9.5 mass percent Contains titanium dioxide, with a paper base Area mass 120 grams per square meter connected and un indirectly cold stamped, dried and how usually assembled.
Im Ergebnis erhält man einen an der Oberfläche farbig ge musterten, durch Prägung stabil strukturierten zwei lagigen Schichtverbund, der als Wandbekleidung (Tapete) verwendbar ist und die in der Beschreibung aufgeführten vorteilhaften Eigenschaften besitzt.The result is a colored surface eyed, two structurally structured by embossing layered layered composite, which is used as wall covering (wallpaper) is usable and those listed in the description possesses advantageous properties.
Ein Flächengebilde aus Polyethylen der gleichen Art wie in Beispiel 1, jedoch mit einer Flächenmasse von ca. 55 Gramm pro Quadratmeter, wird ohne vorherige Bedruckung in gleicher Weise wie in Beispiel 1 mit einer Unterbahn aus Papier, deren Flächenmasse 100 Gramm pro Quadratmeter be trägt, kaschiert, geprägt und fertiggestellt. Der Ka schierkleber enthält 8 Masseprozent Titandioxid. Im Ergebnis erhält man ein analoges Erzeugnis wie in Bei spiel 1, jedoch in Gestalt einer einheitlich weißen, nur durch den Prägeeffekt strukturierten Tapete.A sheet of polyethylene of the same type as in Example 1, but with a basis weight of approx. 55 Grams per square meter, is without prior printing in same way as in Example 1 with a sub-web Paper, the basis weight of which is 100 grams per square meter carries, conceals, embossed and finished. The Ka schier adhesive contains 8% by mass of titanium dioxide. in the The result is a product similar to that in Bei game 1, however in the form of a uniform white, only textured wallpaper through the embossing effect.
Claims (16)