DE1918288A1 - Cords - Google Patents
CordsInfo
- Publication number
- DE1918288A1 DE1918288A1 DE19691918288 DE1918288A DE1918288A1 DE 1918288 A1 DE1918288 A1 DE 1918288A1 DE 19691918288 DE19691918288 DE 19691918288 DE 1918288 A DE1918288 A DE 1918288A DE 1918288 A1 DE1918288 A1 DE 1918288A1
- Authority
- DE
- Germany
- Prior art keywords
- cord
- twisted
- strands
- wire
- cord according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
KORDECORDS
Die Erfindung betrifft Verstärkungskorde für Gegenstände aus Kautschuk und insbesondere, jedoch nicht ausschließlich, ReifenkordeThe invention relates to reinforcing cords for articles made of rubber and particularly, but not exclusively, tire cords
Es ist bekannt, Luftreifen mit Hilfe von Stahldrahtkorden zu verstärken.
Derartige Stahldrahtkorde bestehen im allgemeinen aus
einer Anzahl von Litzen, die wiederum aus einer Anzahl von Stahldrähten
bestehen, die auf einer Verseilvnaschine umeinander gelegt
sind. Es wurde nun festgestellt, daß Drahtkorde, bei denen die
Litzen aus Drahtbündeln zusammengesetzt sind, auf wirtschaftliche Weise hergestellt werden können. Im folgenden wird unter"Bündel"
eine Vielzahl von im wesentlichen parallelen Drähten verstanden.It is known to reinforce pneumatic tires with the aid of steel wire cords. Such steel wire cords are generally made of
a number of strands, which in turn consist of a number of steel wires that are laid around one another on a stranding machine. It has now been found that wire cords in which the
Strands are composed of wire bundles, can be manufactured in an economical manner. In the following, a “bundle” is understood to mean a multiplicity of essentially parallel wires.
909843/1287909843/1287
Bei den erfindungsgemäßen Korien behalten die Drähte über die Länge des Kordes gegenüber der Achse der Litze nicht die gleiche relative Lage bei. Dadurch weichen sie von gebräuchlichen Litzen ab, die durch Zusammenlegen der einzelnen Drähte gebildet sind.In the case of the coria according to the invention, the wires retain their length of the cord with respect to the axis of the strand does not have the same relative position. As a result, they deviate from common strands, which are formed by merging the individual wires.
Ein erfindungsgemäßer Kord umfaßt wenigstens zwei Litzen, bei denen Jede Litze ein Bündel aus Metalldrähten enthält. Der Durchmesser jedes Drahtes liegt unter~0,25 mm (0,010 inch).A cord according to the invention comprises at least two strands, in which Each strand contains a bundle of metal wires. The diameter of each wire is less than ~ 0.25 mm (0.010 inch).
In einer weiteren Ausführungsform umfaßt der erfindungsgemäße Kord wenigstens zwei Litzen, bei denen.jede Litze ein Bündel aus Metalldrähten enthält, wobei der Durchmesser jedes Drahtes weniger ■als etwa 0,25 mm (0,010 inch), jedoch nicht weniger als etwa 0,05 mm (0,002 inch) beträgt.In a further embodiment, the invention comprises Cord at least two strands, in which each strand contains a bundle of metal wires, the diameter of each wire less ■ as about 0.25 mm (0.010 inch) but not less than about 0.05 mm (0.002 inch).
In einer weiteren Ausführungsform umfaßt der erfindungsgemäße Kord wenigstens zwei Litzen, von denen jede ein Bündel Metalldrähte enthält, wobei der Durchmesser jedes Drahtes weniger als etwa 0,18 mm (0,007 inch), jedoch nicht weniger als etwa 0,075 nun. (0,003 inch) beträgt.In a further embodiment, the invention comprises Cord at least two strands, each of which is a bundle of metal wires wherein the diameter of each wire is less than about 0.18 mm (0.007 inches) but not less than about 0.075 now. (0.003 inch).
Gemäß der Erfindung enthält ein verstärkter Gegenstand aus Kautschuk eine Verstärkung, dia wenigstens einen der oben beschriebenen Korde enthält.According to the invention, a reinforced article made of rubber includes a reinforcement containing at least one of the cords described above.
Ein Ausführungsbeispiel der Erfindung ist in der beigefügten Zeichnung dargestellt.An embodiment of the invention is shown in the attached Drawing shown.
Fig. 1 zeigt die Seitenansicht eines gedoppelten Kordes, Fig. 2 einen Schnitt durch diesen Kord.Fig. 1 shows the side view of a doubled cord, Fig. 2 shows a section through this cord.
Aus den Figuren ist zu-erkennen, daß die beiden Litzen leicht abgeflacht sind, und daß die Einzeldrähte innerhalb der Litzen.willkürlich verteilt sind. It can be seen from the figures that the two strands are slightly flattened and that the individual wires are randomly distributed within the strands.
9098437128790984371287
BAD ORIGINALBATH ORIGINAL
Gemäß der Erfindung wird ein Kord aus Metalldrähten mit einem Durchmesser von weniger als etwa 0,25 min (0,010 inch) so hergestellt, daß wenigstens zwei Drahfbündel zusammengefügt werden, daß die Drahtbündel einzeln in einer Drillrichtung verdrillt werden, und daß die verdrillten Bündel' entgegen der Drillrichtung verdrillt werden.In accordance with the invention, a cord is made from metal wires having a diameter of less than about 0.25 min (0.010 inch) so that that at least two wire bundles are put together, that the wire bundles are twisted individually in a twisting direction, and that the twisted bundles are twisted against the twisting direction.
Die Metalldrähte sind gegebenenfalls mit einem anderen Metall, einem keramischen Material, einem Polymerisat, einem Haftbeschleuniger oder einem anderen Material überzogen. Vorzugsweise bestehen die Metalldrähte jedoch aus Stahldrähten oder aus mit einem anderen Metall, wie beispielsweise Messing, überzogenen Stahldrähten. Die Metalldrähte besitzen vorzugsweise einen Durchmesser von weniger als etwa 0,1 mm (0,004 inch).The metal wires are optionally coated with another metal, a ceramic material, a polymer, an adhesion accelerator or coated with another material. Preferably, however, the metal wires consist of steel wires or with another metal, such as brass, coated steel wires. The metal wires preferably have a diameter less than about 0.1 mm (0.004 inch).
Im allgemeinen haben die Metalldrähte einen im wesentlichen -kreisförmigen Querschnitt. Es können jedoch auch Drähte mit einem anderen Querschnitt verwendet werden, z. B. streifenförmige Drähte-, vorausgesetzt, daß die größte Abmessung des Querschnitts, d.h. der maximale Durchmesser innerhalb des vorher erwähnten Durchmesserbereiches liegt.In general, the metal wires are substantially circular in shape Cross-section. However, wires with a different cross-section can also be used, e.g. B. strip-shaped wires, provided that the largest dimension of the cross-section, i.e. the maximum diameter, is within the aforementioned diameter range lies.
Jede Litze kann aus einem verdrillten Drahtbündel bestehen, wobeiEach strand can consist of a twisted wire bundle, whereby
das Drahtbündel als Bündel um seine eigene Achse verdrillt ist,the wire bundle is twisted as a bundle around its own axis,
oder die Litzen können einfach aus unverdrillten Drahtbündeln bestehen.or the strands can simply consist of untwisted wire bundles.
Der erfindungsgemäße Kord kann aus einem Kabel bestehen, das aus einer Anzahl von Litzen besteht, die umeinander oder um eine Seele gelegt sind. Die Verdrillung kann verhältnismäßig niedrig _ -Steigungswinkel θ etwa 14° - oder größer- Steigungswinkel etwa 20° bis 30e-sein. Die Litzen können auf einer herkömmlichenThe cord according to the invention can consist of a cable which consists of a number of strands which are laid around one another or around a core. The twist may be relatively low _ -Steigungswinkel θ about 14 ° - or greater-pitch angle is about 20 ° to 30 -his e. The strands can be on a conventional
Verseilmaschine zu Kabeln verarbeitet werden.Stranding machine can be processed into cables.
909843/1287909843/1287
Der erfindungsgemäße Kord kann auch aus einem gedoppelten oder einem gefachten Kord bestehen, wobei er aus zwei oder mehreren gezwirnten Litzen besteht, so daß diese spiralförmig verschlungen*' sind. Dabei ist der Steigungswinkel θ für/jede Litze Vorzugs- V weise gleich. Die gedoppelten Korde können auf einer herkömmlichen lextil-Zwirnmaschine hergestellt sein, insbesondere dann, -. .- ·■> wenn die Litzen aus sehr feinen Drähten*, d. h. Drähten mit einem. Durchmesse^ von weniger als·0,1 mm, bestehen. ■ . - : The cord according to the invention can also consist of a doubled or a plied cord, whereby it consists of two or more twisted strands so that these are twisted spirally * '. The pitch angle θ is preferably the same for / each strand. The doubled cords can be made on a conventional lextile twisting machine, in particular -. .- · ■> if the strands are made of very fine wires *, i. H. Wires with one. Diameter of less than 0.1 mm. ■. - :
Die erfindugsgemäßen Korde können schwach oder stark verdrillt sein. Im allgemeinen gilt,'daß die Dehnbarkeit der "Corde um so;.. ... größer ist, ;)e stärker sie verdrillt sind. Je feiner die einzelnen Drähte in den Litzen sind, um so leichter wird es, eine . \ \; starke Verdrillung des Kordes zu erzielen und, bei gegebener Kord-Verdrillung,wird die Kord-Flexibilität um so größer.The cords according to the invention can be weakly or strongly twisted. In general, the following applies: the stretchability of the "cords is so; .. ... greater,;) e more strongly they are twisted. The finer the individual wires are in the strands, the easier it is to create a. \ \"; to achieve strong twisting of the cord and, given a given cord twist, the cord flexibility is all the greater.
Die erfindungsgemäßen Korde sind gegebenenfalls mit einem Metalldraht oder einem Textil-Faden oder -Garn umsponnen«, Die erfindungsgemäßen Drahtkorde können vor- und nachgeformt werden, und zwar in Verfahren, die der in der Drahtverseilung üblichen Entkräuselung und Entspannung entsprechen. ' ·The cords according to the invention are optionally wound with a metal wire or a textile thread or yarn Wire cords can be pre-formed and post-formed using processes that are common in wire stranding Corresponding to de-curling and relaxation. '·
Anhand der im folgenden aufgeführten Beispiele wird die Erfindung nähp"1" erläutert.The invention is illustrated near " 1 " on the basis of the examples given below.
Eine Litze aus einem Bündel von 10 vermessingten Stahldrähten mit einem Durchmesser von 3e etwa 0,17 mm (0,0069 inch) wurde mit etwa 2"Drehungen/ cm Litzenlänge (4,75 Drehungen/inch)A strand of a bundle of 10 brass-plated steel wires 3 e about 0.17 mm (0.0069 inch) in diameter was twisted at about 2 "turns / cm of strand length (4.75 turns / inch).
in um seine eigene Achse gedrillt.-Darauf wurden drei solcher Litzen entgegengesetzter Drillrichtung miteinander verdrillt, wobei der so gebildete Kord mit etwa 0,8 Drehungen/cm Kordlänge (2 Drehungen/inch) verdrillt war, die verbleibende Verdrillung in den Litzen betrug etwa 1 Drehung/cm Litzenlänge (2,75 Drehungen/inch).Twisted in around its own axis.-Thereupon three such strands were made opposite twist direction twisted together, the cord thus formed with about 0.8 turns / cm cord length (2 turns / inch) was twisted, the remaining twist in the strands was about 1 turn / cm of strand length (2.75 turns / inch).
909 8 43/128 7909 8 43/128 7
Die Dehnungseigenschaften dieses Kordes wurden gemessen, die Ergebnisse dieser Messung, sind in Tabelle I aufgeführt.The elongation properties of this cord were measured Results of this measurement are shown in Table I.
9 /** 1 0 L
9 / **
Diese Messungen wurden an der Instron-Universal-TestmaschineThese measurements were made on the Instron Universal Test Machine
durchgeführt, wobei sich die bewegliche Einspannvorrichtung mit einer konstanten Geschwindigkeit von 5 cm/min bewegte.with the movable jig moving at a constant speed of 5 cm / min.
Für jeden Test wurde der Kord an seinen Enden in Araldit eingebet tet, um den Kord zu schützen und Brüche in der Einspannvorrichtung der Testmaschine zu vermeiden. Die Versuche wurden jeweils an zwei "Sätzen von Korden, durchgeführt, wobei die freie Testlänge einmal 10 cm, das andere Mal 30 cm betrug.For each test, the cord was embedded in araldite at its ends, to protect the cord and prevent breakage in the jig of the test machine. The trials were each on two "sets of cords, performed, being the free test length once 10 cm, the other time 30 cm.
Bei den in Tabelle I angegebenen Werten handelt es sich um Mittelwerte aus den Versuchen an den beiden Kordsätzen. Die Dehnbarkeit wurde aus der Differenz der jeweiligen Dehnungen der 30 bzw. 10 cm langen Korde ermittelt. Auf diese Weise wurde die Korddehnung frei von Einwirkungen der Einspannvorrichtung und des Araldits auf der Basis einer Kordlänge von 20 cm ermittelt.The values given in Table I are mean values from the experiments on the two sets of cords. The extensibility was determined from the difference between the respective elongations of the 30 resp. 10 cm long cords determined. In this way, the cord elongation became free from the effects of the jig and the Araldits determined on the basis of a cord length of 20 cm.
Eine Litze aus einem Bündel von 40 vermessingten Stahldrähten mit einem Durchmesser-von je etwa 0,075 mm (0,003 inch) wurde durch Drehung des Drahtbündels um seine eigene Achse mit etwa 0,8 Drehungen /cm Litzenlänge (2 Drehungen/inch) verdrillt. Zwei"derartige Litzen wurden darauf in entgegengesetzter Drillrichtung miteinander verdrillt, der so gebildete Kord wies eine Verdrillung von etwa 0,8 Drehungen/cm Kordlänge (2 Drehungen/inch) auf·, die in den Litzen verbliebene Verdrillung war praktisch gleich Null.A strand made from a bundle of 40 brass-plated steel wires each about 0.075 mm (0.003 inch) in diameter was made by rotating the wire bundle about its own axis with about 0.8 turns / cm strand length (2 turns / inch) twisted. Two such strands were then twisted in opposite directions twisted together, the cord formed in this way had a Twist of about 0.8 turns / cm of cord length (2 turns / inch) on ·, the twist left in the strands was practical equals zero.
'909843/128?'909843/128?
Weiter wurde ein ähnlicher Kord hergestellt, ausgenommen daß die
Litzen aus mit etwa 2,5 Drehungen/cm Litzenlänge (6 Drehungen/
inch) verdrillten Drahtbündeln bestanden, und daß zwei derartiger Litzen mit etwa 2,5 Drehungen/cm Kordlänge in entgegengesetzter
Drillrichtung miteinander verdrillt waren. Die bleibende.Verdrillung in den Litzen war ebenfalls praktisch Null. Ferner wurde
ein ähnlicher Kord hergestellt, dessen Drahtbündel jedoch anfänglich mit etwa 4 Drehungen/cm (10 Drehungen/inch) verdrillt war und
bei dem die Verdrillung des daraus gebildeten Kordes 4 Drehungen/ cm Kordlänge betrug.A similar cord was also made except that the strands were made from approximately 2.5 turns / cm of strand length (6 turns /
inch) twisted wire bundles, and that two such strands were twisted with about 2.5 turns / cm cord length in opposite twisting direction. The permanent twisting in the strands was also practically zero. Furthermore, was
A similar cord was made, but the bundle of wires was initially twisted at about 4 turns / cm (10 turns / inch) and the twist of the cord formed therefrom was 4 turns / cm of cord length.
Die mit diesen Korden gewonnenen Meßergebnisse sind in der folgenden Tabelle II angegeben.The measurement results obtained with these cords are as follows Table II given.
0,8 Dreh/cm 2,5 Dreh/cm 4 Dreh/cm0.8 turn / cm 2.5 turn / cm 4 turn / cm
Bruchlast - 101 kg 87 kg 49 kg
Bruchdehnung 1,7 # 2,8 % 3,8 % Breaking load - 101 kg 87 kg 49 kg
Elongation at break 1.7 # 2.8 % 3.8 %
Dehnung bei halber
Bruchlast 0,7 % 1,2 % 1,7 % Stretching at half
Breaking load 0.7 % 1.2 % 1.7 %
Korddurchmesser **Ό,91 mm ~0,94 mm ~1 mmCord diameter ** Ό, 91mm ~ 0.94mm ~ 1mm
(0,036 inch) (0,037 inch) (0,040 inch)(0.036 inch) (0.037 inch) (0.040 inch)
Drei Litzen bestehend aus je einem Bündel von 62 vermessingten
Stahldrähten mit einem Durchmesser von je etwa 0,13 mm (0,005
inch) wurden zunächst einzeln mit etwa 0,55 Drehungen/cm (1,4
Drehungen/lnch) verdrillt. Diese drei Litzen wurden, dann mit etwa
0,55 Drehungen/cm in der entgegengesetzten Richtung zu einem Kord verdrillt. ■Three strands each consisting of a bundle of 62 brass-plated
Steel wires with a diameter of about 0.13 mm (0.005
inch) were initially turned individually at about 0.55 turns / cm (1.4
Turns / inch) twisted. These three strands were then twisted into a cord at about 0.55 turns / cm in the opposite direction. ■
9098 4 371289098 4 37128
Die physikalischen Eigenschaften dieses Kordes sind in Tabelle III angegeben. Er eignet sich als Verstärkungskord für Reifen mit großem Durchmesser, beispielsweise- als großer Radial-Reifen für Erdbewegungs-Fahrzeuge.The physical properties of this cord are shown in Table III specified. It is suitable as a reinforcement cord for tires with a large diameter, for example as a large radial tire for Earthmoving vehicles.
Bruchlast ' . " 589 kgBreaking load '. "589 kg
Bruchdehnung ~ 1,65 % Elongation at break ~ 1.65 %
Dehnung bei halber Bruchlast 0,70 % Elongation at half breaking load 0.70 %
Kord durchmess er ^2,3 m (0,090- inch)Cord diameter ^ 2.3 m (0.090- inch)
Drei Litzen, bestehend aus je einem Bündel von 119 vermessingten Stahldrähten mit einem Drahtdurchmesser von etwa 0,05 mm (0,002 inch) wurden zunächst einzeln mit etwa einer Drehung/cm (2·^ Drehung/inch) in einer Richtung verdrillt. Diese Litzen wurden-darauf mit etwa einer Drehung/cm in entgegengesetzter Richtung zu einem Kord verdrillt.Three strands, each consisting of a bundle of 119 brass-plated Steel wires with a wire diameter of about 0.05 mm (0.002 inch) were initially individually with about one turn / cm (2 ^ turn / inch) twisted in one direction. These strands were-on twisted into a cord with about one twist / cm in the opposite direction.
Die physikalischen Eigenschaften dieses Kordes sind in Tabell IVThe physical properties of this cord are given in Table IV
anger3ben. Er eignet sich als Verstärkungskord für LKW-Radial-Reifen. to tan. It is suitable as a reinforcement cord for truck radial tires.
' Tabelle IV ' Table IV
Bruchlast . 134 kgBreaking load. 134 kg
Bruchdehnung 1,4$Elongation at break 1.4 $
Dehnung bei halber Bruchlast 0,6 % Elongation at half breaking load 0.6 %
Korddurchmesser ^ 1,1 mm (0,42 inch)Cord diameter ^ 1.1 mm (0.42 inch)
909843/1287909843/1287
Claims (15)