ANLAGE 1 zur Gebrauchsmusteranmeldung Gm 297 Gereckte netzartige Formkörper
aus Thermoplasten
.
<9 6
n d r A A n/7 n ~ o~
F 1 447/30 a mi
Gegenstand des GebrauchsmustersAsind gereckte durchbrochene
C>
Gitterwerke aus Kunststoffen, die nach dem für Metallbleche
bekannten Streckziehverfahren hergestellt werden, dadurch gekennzeichnet, daß man
Kunststoff-Folien oder-Platten aus hochpolymeren Thermoplasten mit kristallinem
und amorphem Gefügeanteil verwendet, wie Polyolefine, z. B. Polyäthylen, Polypropylen,
sowie Polyamide, Polymerisate fluorhaltiger ungesättigter Verbindungen u. a. Thermoplasten
mit kristallinem und amorphem Gefüge zur Herstellung der gereckten Gitterwerke verwendet.APPENDIX 1 to the utility model registration Gm 297 Stretched, reticulated moldings made from thermoplastics .
<9 6
ndr AA n / 7 n ~ o ~
F 1 447/30 a mi
The subject of the utility model is stretched openwork
C>
Latticework made of plastics, according to the one for sheet metal
known stretch-drawing processes are produced, characterized in that plastic films or sheets made of high-polymer thermoplastics with crystalline and amorphous structural content are used, such as polyolefins, e.g. B. polyethylene, polypropylene, and polyamides, polymers of fluorine-containing unsaturated compounds, including thermoplastics with crystalline and amorphous structure are used to produce the stretched latticework.
Gemäß dem älteren Vorschlag erfolgt die Reckung nur um geringere Beträge
ohne Anwendung von Wärme.According to the older proposal, the stretching is done only by smaller amounts
without applying heat.
Es wurden nun gereckte netzartige Fornkörper aus, nakromolekularen
Stoffen, die nach dem Streckziehverfahren hergestellt
sind, gefunden, die dadurch gekennzeichnet sind, daß man die
gereckten netzartigen Formkörper aus makromolekularen Stoffen
\',
vorzugsweise Niederdruckpolyäthylen herstellt, wobei man
die Reckung des Gittewerkes am Schmelzpunkt oder\bis zu 50
vorzugsweise
unterhalb des Sch'ielzpunktesder kristallenen Gefüßeanteile
durchführt. Die erfinungsgemäß durchgeführte Reckung kann
sowohl in als auch senkrecht zur Stanzrichtung der Gitter-
werke um Beträge von 300 bis über 1000 j durchgeführt werden.
,
Vorzugsweise läßt sich die erfindungsgo'mä3e Reckuni in
einem Bereich, der um 0, 5 bis 200 unterhalb des Schmelzpunktes
\
der kristallinen Gefügeanteile liegt, durchführen.
I
Nürde man die Reckung um hohe Beträge bei Zimmertemperatur
oder etwas darüber durchführen, so werden die Gitterwerke
geschädigt wie auo Abbildung 1 auo der mit oinom Pfoil be-
oiohnoton Stelle hprhj An dieser Stelle würde bei einer
weiteren Reckung des Gitterwerkes die Brücke zwischen den
entsprechenden Rauten abreißen.
Die genannten gereckten netzartigen GitterwerKe aus Kunst-
stoffen zeichnen sich durch ein sehr ansprechendes gleich-
mäßiges Muster sowie eine hohe Festigkeit in den Gitterbrücken
aus.
Es zeigte sich überraachenderweise, da3 beim Verstrecken in
Stanzrichtung der Streckgitter die Gitterbrücken beim Ver-
strecken bei Temperaturen nahe unterhalo des Schmelzpunktes
der kristallinen Gefügeanteile selbst bei sehr hohen Ver-
streckungs-raden von über 1000 Ao nicht aufreißen, sondern
gleichmäßig ausgezogene, etwa rechteckig ausgebildete Knoten-
bereiche im Netzwerk bilden, die nach dem Abkühlen unerwartet
hohe Festigkeiten aufweisen. s-u-2).
Seim Verstrecken senkrecht zur Stanzrichtung des Streckgitter
entstehen ebenfalls sehr schöne gleichmäßig ausgezogene
Netzwerke, die sich aber sowohl in der äußeren Form als auch
in den Eigenschaften charakteristisch von den Netzwerken unter-
scheiden, die durch Verstrecken der Streckgitter in Stanzrich-
tung entstehen. a. Abbildung 3)-Beim Heißverstrecken senk-
recht zur Stanzrichtung der 3treckgitter ziehen sich auch die Brücken
in der gleichen Richtung wie die Gitterstäbe bzw. die Netzfäden aus. Die Fäden zeichnen
sich durch besonders hohe Festigkeit aus, während die Brücken-bzw. Knotenpunkte
des Netzes nur geringe Festigkeit besitzen und relativ leicht aufgerissen werden
können. Für dekorative Zwecke erscheinen diese Netze aber trotzdem recht interessant.
Durch gleichzeitiges Ausrecken in und senkrecht zur Stanz-
richtung der Streckgitter kann man Netzwerke erhalten, die
in
CD 1
ihrem Aussehen und auch in den Eigenschaften zwischen den
Netzen entsprechend Abbildung 2 un4 5 liegen. Durch biaxiale
Ausreckung der Streckgitter bei Temperaturen unterhalb des
Schmelzpunktes der kristallinen Anteile können Netze mit be-
sonders hoher Festigkeit in den Knotenpunkten erhalten werden.Stretched, reticulated molded bodies were now made from nacromolecular materials that were produced by the stretch drawing process are found, which are characterized in that the
Stretched reticulated shaped bodies made from macromolecular substances
\ ',
preferably produces low-pressure polyethylene, wherein one
the stretching of the lattice at the melting point or \ up to 50
preferably
below the focus point of the crystalline vessel parts
performs. The stretching carried out according to the invention can
both in and perpendicular to the punching direction of the grid
works by amounts from 300 to over 1000 j.
,
Preferably, the inventive Reckuni can be in
a range that is 0.5 to 200 below the melting point
\
of the crystalline structure is to be carried out.
I.
If one would draw large amounts at room temperature
or do something about it, so will the latticework
damaged as auo Figure 1 auo the one with oinom Pfoil
oiohnoton place hprhj At this point would be a
further stretching of the latticework, the bridge between the
tear off the corresponding diamonds.
The above-mentioned stretched, net-like latticework made of art
fabrics are characterized by a very attractive,
moderate pattern and high strength in the lattice bridges
the end.
It was surprisingly found that when stretching in
Punching direction of the expanded mesh the lattice bridges when
stretch at temperatures close to below halo of the melting point
of the crystalline structure even with very high levels of
Do not tear open stretch lines of over 1000 Ao, but rather
evenly drawn out, roughly rectangular knot
Form areas in the network that are unexpected after cooling
have high strengths. su-2).
When stretching perpendicular to the punching direction of the expanded metal
there are also very beautiful, evenly drawn out ones
Networks, which are however both in the external form and
characteristic of the networks in terms of properties
separate, which by stretching the expanded metal in punched
tion arise. a. Figure 3) -When hot stretching, lower-
right to the punching direction of the stretched lattice, the bridges also extend in the same direction as the lattice bars or the net threads. The threads are characterized by particularly high strength, while the bridge or. Nodes of the network have little strength and can be torn open relatively easily. For decorative purposes, however, these nets appear quite interesting. By simultaneously stretching in and perpendicular to the punching in the direction of the expanded metal, networks can be obtained that are in
CD 1
their appearance and also in the properties between the
Nets as shown in Figure 2 and 4 5. By biaxial
Stretching the expanded metal at temperatures below the
The melting point of the crystalline parts, networks with
especially high strength in the nodes can be obtained.
Durch Variation des Ausreckungsgrades in und senkrecht zur Stanzrichtung
@ann man sowohl Aussehen als auch die mechanische Festigkeit der Netze in den Knotenstellen
beeinflussen.
Wie urch Versuche nachgewiesen wurde, läßt sich die erfin-
dungsgemäße Heißverstreckung in kontinuierlichem Durchlaufverfahren durchführen.
Es ist sogar möglich, die Folien-oder Plattenherstellung mit Hilfe der Breitschlitzdüse,
die Her-
stellung der Streckgitter aus diesen Folieh und die anschließen-
ID
de Heißverstreckung dieser Gitter hintereinander im kontinuierlichen Verfahren durchzuführen.By varying the degree of extension in and perpendicular to the punching direction, one can influence both the appearance and the mechanical strength of the nets in the nodes. As has been proven by experiments, the invented
Carry out proper hot stretching in a continuous process. It is even possible to produce the film or sheet with the help of the slot die, the position of the expanded metal from this film and the subsequent
ID
de hot stretching of these grids one after the other to be carried out in a continuous process.
'nsonders Vorteilhaft lassen sich nach dem erfindungsgemäßen herfahren
Polyäthylene verwenden, die nach dem sogenannten @iederdruckverfahren hergestellt
sind. Die genannten Niederdruckverfahren sind bei Raff Allison "Polyethylene", Seite
72ff nsbesondere Seite 80, 1. Absatz, sowie Seite 81, Absatz 2, @, 4 und 5, beschrieben.It is particularly advantageous to use the method according to the invention
Use polyethylene that is manufactured according to the so-called low pressure process
are. The low-pressure processes mentioned are at Raff Allison "Polyethylene", p
72ff, especially page 80, 1st paragraph, as well as page 81, paragraph 2, @, 4 and 5, are described.
Nach dem geschilderten Verfahren können grundsätzlich auch nrrno,'laste,
die nicht sieicnzeitig kristalline und amorphe enteile besitzen, sondern nur aus
rein amorphem Gefüge bestehen, wie Polyvinylchlorid, Polystyrol usw., zu Netzwerken
verarbeitet
werden. In diesen Falle muß jedoch die Herstel-
lun7 des Streckgitter vor der Heißverstrecun zum Netzwerk
n u
bereits bei erhöhten Temperaturen durchgeführt werden. Bei den Thermoplasten, die
einen rein amorphen Gefügeaufbau besitzen, muß die Heißverstreckung zum Netzwerk
im Temperaturbereich des viskoelastischen Zustandes des verwendeten Thermoplasten
durchgeführt werden und zwar möglichst um mindestens 500 über der Einfriertemperatur.According to the process described above, loads that do not have crystalline and amorphous components at the moment but only consist of a purely amorphous structure, such as polyvinyl chloride, polystyrene, etc., can be processed into networks. In this case, however, the manufacturer lun7 of the expanded metal before the heat stretch to the network
nu
can be carried out at elevated temperatures. In the case of thermoplastics, which have a purely amorphous structure, the hot stretching to form the network must be carried out in the temperature range of the viscoelastic state of the thermoplastic used, preferably by at least 500 above the freezing temperature.