DE1817690C3 - Foil for the production of printing forms - Google Patents
Foil for the production of printing formsInfo
- Publication number
- DE1817690C3 DE1817690C3 DE1817690A DE1817690A DE1817690C3 DE 1817690 C3 DE1817690 C3 DE 1817690C3 DE 1817690 A DE1817690 A DE 1817690A DE 1817690 A DE1817690 A DE 1817690A DE 1817690 C3 DE1817690 C3 DE 1817690C3
- Authority
- DE
- Germany
- Prior art keywords
- hydroxyphenyl
- printing forms
- weight
- bis
- foil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
soso
Gegenstand der Erfindung ist eine Folie für die Herstellung von Druckformen oder Vorlagen für Druckformen mit einem nichttransparenten Schicht- *5 träger aus pigmentiertem Polycarbonat.The invention relates to a film for the production of printing forms or templates for Printing forms with a non-transparent layer * 5 pigmented polycarbonate support.
Für die Herstellung von Aufsichtvorlagen für Druckformen wurden bisher photographische Schichten auf Schichtträgern aus Papier, die durch Verleimung mit Kunststoff- oder Metallfolien maßhaltig ge- macht wurden, verwendet. Es wurde auch versucht, mit Weißpigment gefüllte CeHulosetriacetatträger zn verwenden (DE-AS 1 003 036). Es ist jedoch schwierig, solche Schichtträger so herzustellen, daß sie eine gleichmäßige Opazität aufweisen. Außerdem genügen « diese Materialien nicht den technischen Anforderungen, weil entweder die Oberflächenglätte oder die Maßhaltigkeit nicht ausreicht.For the production of reflective templates for Up to now, printing forms have been photographic layers on paper substrates, which are dimensionally accurate by gluing with plastic or metal foils. power were used. Attempts have also been made to use CeHulosetriacetatträger filled with white pigment use (DE-AS 1 003 036). However, it is difficult to make such supports so that they can be have uniform opacity. In addition, «these materials do not meet the technical requirements, because either the surface smoothness or the Dimensional accuracy is not enough.
Extrudierte pigmentierte Folien aus maßhaltigen Kunststoffen sind für diesen Zweck nicht einsatzbar, w weil sie sich nicht genügend stark oder gleichmäßig pigmentieren lassen. Die Beschichtung maßhaltiger Unterlagen mit einer pigmentierten Schicht befriedigt, abgesehen von dem aufwendigen Herstellungsverfahren, wegen zu geringer Dichte und oft ungenügender Haftung und Maßhaltigkeit nicht.Extruded pigmented films made of dimensionally stable plastics cannot be used for this purpose, w because they cannot be pigmented sufficiently or evenly. The coating is more accurate Documents with a pigmented layer satisfied, apart from the complex manufacturing process, because of insufficient density and often insufficient Liability and dimensional accuracy are not.
Aus der DE-AS 1 060710 sind Schichtträger für phototechnische Filme bekannt, die aus hochmolekularen thermoplastischen Polycarbonaten* 2.B. auf der Basis von 4,41-Di-(moriooxyafyl)-älkäfien, bestehen ω und die gegebenenfalls Farbstoffe oder Pigmente enthalten.DE-AS 1 060710 discloses layer supports for phototechnical films which are made from high molecular weight thermoplastic polycarbonates * 2.B. on the basis of 4,4 1 -Di- (moriooxyafyl) -älkäfien, consist ω and which optionally contain dyes or pigments.
Die Einarbeitung von Pigmenten in die Lösungen oder Schmelzen der genannten Polycarbonate ist jedoch insofern mit Schwierigkeiten verbunden, als es bi nicht ohne weiteres möglich ist, gleichmäßig pigmentierte opake Filme zu erhalten. Selbst dann, wenn es gelingt, das Pigment vor der Formgebung des Materials in der Lösung oder Schmelze gleichmäßig zu verteilen, beginnt das Pigment nach kurzer Zeit zu agglomerieren, so daß schließlich ein streifiger Film mit unterschiedlicher Opazität entsteht Dazukommt, daß durch die Agglomeration des Pigmentes die vor dem Vergießen der Gießlösungen notwendige Filtration erheblich behindert wird.The incorporation of pigments into the solutions or melts of the polycarbonates mentioned is associated with difficulties insofar as it is bi it is not readily possible to obtain uniformly pigmented opaque films. Even if there is if it is possible to distribute the pigment evenly in the solution or melt before shaping the material, the pigment begins to agglomerate after a short time, so that finally a streaky film is formed different opacity arises In addition, the agglomeration of the pigment before the Pouring the casting solutions necessary filtration is significantly hindered.
Der Erfindung liegt deshalb die Aufgabe zugrunde, einen gleichmäßig opaken, maßhaltigen Schichtträger zu entwickeln.The invention is therefore based on the object to develop a uniformly opaque, dimensionally stable substrate.
Diese Aufgabe wird gelöst mit einer Folie für die Herstellung von Druckformen oder Vorlagen für Druckformen mit einer gegebenenfalls lichtempfindlichen Schicht auf einem maßhaltigen weißpigmentierten Schichtträger aus einem Polycarbonat auf der Basis von Bis-(4-hydroxyphenyI)-alkanen) das dadurch gekennzeichnet ist, daß der Schichtträger ein Alkydharz als Dispergierungsmittel und 10 bis 20 Gew.-% Titandioxid bezogen auf das Gesamtgewicht der im Schichtträger enthaltenen Polymerisate enthält.This object is achieved with a film for the production of printing forms or templates for printing forms with an optionally light-sensitive layer on a dimensionally stable white-pigmented layer support made of a polycarbonate based on bis (4-hydroxyphenyl) alkanes ) which is characterized in that the The support contains an alkyd resin as a dispersing agent and 10 to 20% by weight of titanium dioxide based on the total weight of the polymers contained in the support.
Die in der erfindungsgemäßen Weise zu verwendenden Kohlensäureester leiten sick: von Bis-(4-hydroxyphenyO-alkanen ab, wobei die Phenylgruppen, z. B. durch einwertige, geradkettige oder verzweigte Alkylreste mit bis zu 5 Kohlenstoffatomen, oder durch einwertige Cycloalkyl-oder Arylreste substituiert sein können, und wobei unter »Alkanenc auch Cycloalkane verstanden werden. Als besonders geeignet erweist sich der von 2,2-Bis-(4-Hydroxyphenyl)-propan abgeleitete polymere Kohlensäureester, vorzugsweise solche Produkte die in geringen Mengen bis zu etwa 10 Mol-% bezogen auf das gesamte Phenolalkan l,l-Bis-(4-Hydroxyphenyl)-Cyclohexan enthalten.The carbonic acid esters to be used in the manner according to the invention derive from: bis- (4-hydroxyphenyO-alkanes, the phenyl groups, z. B. by monovalent, straight-chain or branched alkyl radicals with up to 5 carbon atoms, or by monovalent cycloalkyl or aryl radicals can be substituted, and "alkanes" also mean cycloalkanes. That of 2,2-bis (4-hydroxyphenyl) propane has proven to be particularly suitable derived polymeric carbonic acid esters, preferably those products in small amounts up to about 10 mol%, based on the total phenol alkane, contain 1,1-bis (4-hydroxyphenyl) cyclohexane.
Die in der erfindungsgemäßen Weise zu verwendenden polymeren Kohlensäureester können in bekannter Weise hergestellt werden aus den genannten Dihydroxyverbindungen durch Umsetzung mit aliphatischen oder aromatischen Diestern der Kohlensäure oder mit Phosgen oder mit Bischlorkohlensäureestern aromatischer Dihydroxyverbindungen nach Verfahren wie sie beispielsweise in den folgenden deutschen Patentschriften: 959497, 1020184, 1024710,1026958,1031512,1046311 oder in den belgischen Patentschriften 532546 beschrieben werden.The polymeric carbonic acid esters to be used in the manner according to the invention can be prepared in a known manner from the aforementioned Dihydroxy compounds by reaction with aliphatic or aromatic diesters of carbonic acid or with phosgene or with bischlorocarbonic acid esters of aromatic dihydroxy compounds Process as described, for example, in the following German patents: 959497, 1020184, 1024710,1026958,1031512,1046311 or in the Belgian patents 532546 are described.
Dte Herstellung des Schichtträgers erfolgt nach dem üblichen Gießverfahren auf einer Band- öder Trommelmaschine aus Titandioxidptgment enthaltenden Lösungen von Polycarbonat in niedrigsiedenden Lösungsmitteln. Die Lösungen können noch Weichmacher, Farbstoffe oder optische Aufheller enthalten.Dte production of the support takes place after the usual casting process on a belt or drum machine from solutions of polycarbonate containing titanium dioxide in low-boiling solvents. The solutions can still Contain plasticizers, dyes or optical brighteners.
Das Pigment wird dem Gießlösungsansatz zwecktnäßigerwefee in Form einer Paste zugegeben. Zur Erzielung eines gleichmäßig pigmentierten Filmes hoher Dichte und guten Glanzes hat es sieh als vorteilhaft herausgestellt, wenn die Korngröße des Pigmentes kleiner als 1 um ist, und die Paste so stabil ist, daß nach 2 Stunden noch keine Sedimentation nach Verdünnung der Paste mit Methylenchlorid im Verhältnis 1:20 beobachtet wird.The pigment is expediently added to the casting solution in the form of a paste. To achieve a uniformly pigmented film higher It has proven to be advantageous if the grain size of the pigment is dense and glossy is smaller than 1 µm, and the paste is so stable that after 2 hours there is still no sedimentation after the paste has been diluted with methylene chloride in proportion 1:20 is observed.
Diese Eigenschaften der Paste erreicht man, wenn man das Pigment in Gegenwart eines Alkydharzes eines Lösungsmittels und gegebenenfalls eines Weichmachers mechanisch bearbeitet. Der Zusatz des Alkydharzes verhindert die Agglomeration des Pigmentes und setzt die Viskosität der Paste herab. DerThese properties of the paste are achieved when the pigment is mechanically processed in the presence of an alkyd resin, a solvent and, if appropriate, a plasticizer. The addition of the alkyd resin prevents agglomeration of the pigment and reduces the viscosity of the paste. Of the
Verhinderung der Agglomeration des Pigmentes kommt besonders Bedeutung zu, denn einmal wird dadurch die vor dem Verguß der Gießzusammensetzung notwendige Filtration ermöglicht und zum anderen bleibt das Pigment in der Gießzusammensetzung vollkommen homogen verteilt Eine Agglomeration des Pigmentes in der Gießzusammensetzung führt zu Schichtträgern, die Streifen unterschiedlicher Opazität und eine verminderte Oberflächenglätte aufweisen. Prevention of agglomeration of the pigment is of particular importance, because once it is before the casting of the casting composition allows the necessary filtration and, on the other hand, the pigment remains in the casting composition distributed completely homogeneously An agglomeration of the pigment in the casting composition leads to Substrates that have stripes of different opacity and reduced surface smoothness.
Als besonders geeignet haben sich Alkydharze bestehend aus Phthalsäure, einem mehrwertigen Alkohol (z. B. Glycerin, Triraethylolpropan, Pentaerythrit) einerseits und Ricinen- oder Sojaölfettsäure andererseits, die als 60%ige Lösungen in organischen Lösungsmitteln im Handel sind, in einer Konzentration von 4 bis 8 Gew.-% (entsprechend 1,8 bis 4,8 Gew.-% Fesistoff) bezogen auf Titandioxid erwiesen.Alkyd resins consisting of phthalic acid, a polyhydric alcohol, have proven particularly suitable (e.g. glycerine, triraethylolpropane, pentaerythritol) on the one hand and ricinic or soybean oil fatty acid on the other hand, which are commercially available as 60% solutions in organic solvents, in one concentration from 4 to 8% by weight (corresponding to 1.8 to 4.8% by weight of solids) based on titanium dioxide.
Als Weichmacher und Dispergiermittel verwendet man vorzugsweise- ein kurzkettiges Kondensationsprodukt aus Phthalsäure und Äthylenglykol vorzugsweise mit einem Molgewicht bis zu 10000 in einer Konzentration von 3 bis 6 Gew.-% bezogen auf das Gesamtgewicht des im Schichtträger enthaltenen Polymeren. The plasticizer and dispersant used are preferably a short-chain condensation product of phthalic acid and ethylene glycol with a molecular weight up to 10,000 in a concentration of 3 to 6 wt .-% based on the Total weight of the polymer contained in the substrate.
Auf dem pigmentierten Schichtträger aus dem Po-Iycarbonat wird in an sich bekannter Weise eine Haftschicht aufgebracht, die die Haftung zwischen der hydrophoben Unterlage und gegebenenfalls hydrophilen Schicht, z.B. einer SUberhalogenidgelatineemulsionsschkht vermitteln soll.On the pigmented polycarbonate support an adhesive layer is applied in a manner known per se, the adhesion between the hydrophobic Support and optionally hydrophilic layer, e.g. a superhalide gelatin emulsion layer should convey.
Dies geschieht beispielsweise durch Behandeln des Trägers mit einer Lösung, die ein Mischacetal aus Polyvinylalkohol und Aldehyden rest wasserlöslich machenden Gruppen und Aldehyden ohne wasserlöslich machende Gruppen enthält. Dieses Mischacetal ist in organischem Lösungsmittel löslich und hat gegenüber Wasser ein starkes Quellvermögen.This is done, for example, by treating the carrier with a solution containing a mixed acetal made from polyvinyl alcohol and aldehydes, which makes it water-soluble Contains groups and aldehydes without water-solubilizing groups. This mixed acetal is in soluble in organic solvents and has a strong swelling capacity in relation to water.
Die Mischacetale können nach üblichen Verfahren erhalten Werden, z. B. indem man die Komponenten mehrere Stunden lang in methanolischer Lösung mit Schwefelsäure als Katalysator erhitzt. Beispiele für Aldehyde mit wasserlöslich machenden Gruppen sind Aldehyde, die im aromatischen Kern Sulfo·, Carboxy- oder Hydroxygruppen enthalten, z. B. 4-Sülfobenzaldehyd und 4-Hydröxybenzaldehyd. Beispiele für Aldehyde ohne wasserlöslich machende Gruppen sind aromatische, araliphatische und altphatische Aldehyde, z. B. Benzaldehyd, Tolylaldehyd, 4-Chlorbenzaldehyd und Hydrozimtaldehyd.The mixed acetals can be obtained by conventional methods, e.g. B. by moving the components Heated for several hours in methanolic solution with sulfuric acid as a catalyst. examples for Aldehydes with water-solubilizing groups are aldehydes that contain sulfo, carboxy- or contain hydroxyl groups, e.g. B. 4-sulphobenzaldehyde and 4-hydroxybenzaldehyde. Examples of aldehydes without water-solubilizing groups are aromatic, araliphatic and oldphatic aldehydes, z. B. benzaldehyde, tolylaldehyde, 4-chlorobenzaldehyde and hydrocinnamaldehyde.
Zur Verbesserung der Haftwirkung können dem Mischacetal kleine Mengen eines teilweise verseiften Mischpolymerisates aus Vinylchlorid und einem organischen Vinylester, z. B. Vinylacetat, Vinylpropionat, Vinylbutyrat, z. B. eines teilweise verseiften Mischpolymerisates aus Vinylchlorid und Vinylacetat züge* setzt werden. Diese teilweise verseiften Mischpolymerisate werden nach bekannten Verfahren durch Verseifung in Methanol mit Schwefelsäure als Katalysator hergestellt, wobei ledigikh die organischen Estergruppen teilweise verseift werden. Geeignete verseifte Mischpolymerisate enthalten ungefähr 45-70 Gew.-% Vinylchlorid, 5-30 Gew.-% Vinylalkohol und 10-40 Gew.-% Vinylester. Es kommen auch Mischpolymerisate aus Vinylchlorid und a, ßungesättigten Carbonsäuren, bzw. teilweise verseifte Mischpolymerisate aus Vinylchlorid und Estern der vorgenannten Säure für den vorliegenden Anwendungszweck in Frage,To improve the adhesive effect, small amounts of a partially saponified copolymer of vinyl chloride and an organic vinyl ester, e.g. B. vinyl acetate, vinyl propionate, vinyl butyrate, e.g. B. a partially saponified copolymer of vinyl chloride and vinyl acetate trains * are set. These partially saponified copolymers are produced by known processes by saponification in methanol with sulfuric acid as a catalyst, only the organic ester groups being partially saponified. Suitable saponified copolymers contain approximately 45-70% by weight vinyl chloride, 5-30% by weight vinyl alcohol and 10-40% by weight vinyl ester. There are also copolymers of vinyl chloride and α, ß unsaturated carboxylic acids, or partially saponified copolymers of vinyl chloride and esters of the aforementioned acid in question for the present application,
Weiterhin wirken sich Zusätze von Vemetzungsmitteln günstig auf die Haftwirkung aus. Als Vernetzungsmittel können lineare Mischpolymerisate von ungesättigten Säureanhydriden mit anderen polymerisierbaren Monomeren eingesetzt werden, wie z. B, in der deutschen Patentschrift 1183369 beschrieben. Als besonders günstig erweisen sich Mischpolymerisate aus Vinylacetat und Maleinsäureanhydrid mit ei-Additions of crosslinking agents also have an effect has a positive effect on the adhesive effect. Linear copolymers of unsaturated acid anhydrides are used with other polymerizable monomers, such as. B, described in German patent specification 1183369. Copolymers of vinyl acetate and maleic anhydride with a
nem Säureanhydridgehalt von 40-50 Molprozent, bezogen auf das Copolymere.nem acid anhydride content of 40-50 mol percent, based on the copolymer.
Zur Erzeugung der Haftschicht wird das Mischacetal im Gemisch mit dem vorgenannten Mischpolymerisat und gegebenenfalls mit Vernetzungsmitteln im Tauch- oder Antragsverfahren auf die Polycarbonatzwischenschicht aufgebracht. Als Lösungsmittel eignen sich organische Lösungsmittel, bevorzugt jedoch Gemische aus Aceton und Methanol.The mixed acetal is used to produce the adhesive layer in a mixture with the aforementioned copolymer and optionally with crosslinking agents im Dip or application process applied to the polycarbonate interlayer. Suitable as a solvent organic solvents, but preferably mixtures of acetone and methanol.
Der so hergestellte Schichtträger kann für die Her-The substrate produced in this way can be used for the
stellung von Druckformen auf photomechanischem Wege benutzt werden, ferner mit lichtempfindlicher Sflberhalogenid-Emulsion verseben für die Herstellung von Aufsichtvorlagen, wie sie für die Herstellung von Tiefdruckformen auf photomechanischem Wege notwendig sind.position of printing forms can be used photomechanically, also with light-sensitive Sverhalide emulsion for the production of reflective templates, such as those used for manufacturing of rotogravure forms by photomechanical means are necessary.
40 g Titandioxid40 g titanium dioxide
11 kg eines Kondensationsproduktes von Phthaljo säure und Äthylengiyltol (Mol. Gew. 6400)11 kg of a condensation product of phthaljo acid and ethylene glycol (mol. wt. 6400)
2,4 kg einer 60%igen Lösung in Xylot eines mit Rkinensäure modifizierten AJkydharzes aus Phthalsäure und Trimethylolpropan2.4 kg of a 60% solution in xylot one with Rkinenic acid modified alkyd resin from phthalic acid and trimethylol propane
47 kg Methylenchlorid47 kg of methylene chloride
werden in einer Schwingmühle mehrere Stunden vermählen. Von dieser Paste werden 44 kg zusammen mit 100 kg Polycarbonat auf der Basis von Bis-(4-Hydroxyphenyl)-2,2-propan mit einem Anteil von 5% l,l-Bis-(4-Hydroxyphenyl)-Cyclohejt« in 438 kg Methylenchlorid gelöstare ground in a vibrating mill for several hours. 44 kg of this paste are added together with 100 kg of polycarbonate based on bis (4-hydroxyphenyl) -2,2-propane with a share of 5% l, l-bis (4-hydroxyphenyl) -Cyclohejt «in 438 kg Dissolved methylene chloride
Diese Lösung läßt sich einwandfrei filtrieren. Die filtrierte Lösungwird durch Erwärmen auf 40° C luftfrei gemacht und nach Beruhigung der Lösung zu einem Film von 0,2 mm Stärke vergossen. Nach dem Tauchverfahren wird anschließend auf beiden Seiten eine Haftschicht nach Beispiel 1 der deutschen Patentschrift 1183396 aufgetragen.This solution can be filtered properly. The filtered solution becomes air-free by warming to 40 ° C made and after the solution has settled down, cast into a film 0.2 mm thick. After this The immersion process is then followed by an adhesive layer according to Example 1 of the German patent on both sides 1183396 applied.
Nach dem Antrag der Lösung für die Haftschicht wird die Folie bei 100-130° C getrocknet. Der Restlösungsmittelgehalt beträgt dann 0,4%. Der Film hat folgende Eigenschaften:After applying the solution for the adhesive layer the film is dried at 100-130 ° C. The residual solvent content is then 0.4%. The film has the following properties:
längsalong
queracross
Die Unterlage wird nun mit einer lichtempfindlichen Silberhalogenidemulsion für die Herstellung von Aufsichtsdruckvorlagen versehen.The base is now coated with a light-sensitive silver halide emulsion for the production of Provide reflective print templates.
50 kg Titandioxid50 kg of titanium dioxide
233 kg Triphenylphosphat233 kg triphenyl phosphate
1,5 kg der 60%igen Lösung des Alkylharzes nach Beispiel I1.5 kg of the 60% solution of the alkyl resin Example I.
25 kg Chloroform25 kg of chloroform
werden in einer Schwingmühle mehrere Stunden vermählen. Von dieser Paste werden 35 kg zusammen mit 100 kgPolycarbonat auf der Basis von Bis-(4-Hydroxy!phenyl)-2,2-propan mit einem Anteil von 5% l,l-Bis-(4-Hydroxyphenyl)-CycIohexan in 447 kg Methylenchlorid gelöst.are ground in a vibrating mill for several hours. 35 kg of this paste are added together with 100 kg of polycarbonate based on bis (4-hydroxyphenyl) -2,2-propane with a proportion of 5% 1,1-bis- (4-hydroxyphenyl) -cyclohexane in 447 kg Dissolved methylene chloride.
Die Herstellung der Folie sowie das Aufbringen der Haftschicht erfolgt nach Beispiel 1. Der Schichtträger wird nun mit Gelatine^chicht, in der fein verteiltes Silber enthalten ist (Schwarzschicht) begossen und direkt für die Herstellung von Druckformen auf photpmechanischem Wege benutzt.The film is produced and the adhesive layer is applied according to Example 1. The support is now coated with gelatine, in the finely divided silver is included (black layer) and poured directly for the production of printing forms on photpmechanical Paths used.
Beispiel 3 (Vergleichsbeispiel)Example 3 (comparative example)
50 kg Titandioxid50 kg of titanium dioxide
234 kg Triphenylphosphat234 kg triphenyl phosphate
25 kg Chloroform25 kg of chloroform
werden in einer Schwingmühle mehrere Stunden vermählen. Von der so hergestellten Paste werden 34^ kg zusammen mit 100 kg Polycarbonat auf der Basis von Bis-(4-hydroxyphenyl)-2,2-propan mit einem Anteil von 5% 1,1 Bis-(4-hydroxyphenyI)-cycIohexan in 438 kg Methylenchlorid gelöst.are ground in a vibrating mill for several hours. Of the paste produced in this way, 34 ^ kg together with 100 kg of polycarbonate on the Base of bis (4-hydroxyphenyl) -2,2-propane with a Share of 5% 1,1 bis (4-hydroxyphenyl) cyclohexane dissolved in 438 kg of methylene chloride.
Die Lösung wird durch eine Filterpresse, die aus gepreßter Watte und Mako bestehende Filter enthältThe solution is passed through a filter press containing filters made from pressed cotton and Mako
(Filterfläche 0,35 m?), filtriert.(Filter area 0.35 m ? ), Filtered.
In gleicher Weise werden die entsprechend den Beispielen 1 und 2 erhaltenen Lösungen filtriert.The solutions obtained according to Examples 1 and 2 are filtered in the same way.
Während von den erfindungsgemäßen Lösungen gemäß Beispiel 1 und 2 1000 I durch die Filterpresse geschickt werden können, ohne daß das Filter undurchlässig wird, verstopft das Filter bereits nach einem Durchsatz von etwa 501 der Lösung gemäß Beispiel 3,While of the solutions according to the invention according to Examples 1 and 2 1000 l through the filter press can be sent without the filter becoming impermeable, the filter clogs after a throughput of about 50 l of the solution according to the example 3,
Die Herstellung der Filme aus den drei Lösungen sowie das Aufbringen der Haftschichten geschieht wie in Beispiel 1 angegeben.The production of the films from the three solutions and the application of the adhesive layers are carried out in the same way given in example 1.
Der Film entsprechend Beispiel 3 zeigt eine schon mit bloßem Auge erkennbare ungleichmäßige Pigmentierung und zwar in Gießrichtung verlaufende Streifen.The film according to Example 3 shows uneven pigmentation which can be recognized with the naked eye namely strips running in the casting direction.
Die entsprechend Beispiel 1 und 2 hergestellten Filme weisen dagegen eine vollkommen homogene Pigmentierung und außerdem einen höheren Glanz auf.The films produced according to Examples 1 and 2, on the other hand, are completely homogeneous Pigmentation and also a higher gloss.
Eine subjektive Beurteilung <k.s Oberflächenglanzes der Proben nach Beispiel 1,2 una 3 liefert folgendes Ergebnis:A subjective assessment <k.s surface gloss the samples according to Example 1, 2 and 3 provide the following Result:
Probe 1 stark glänzend 1-0,5Sample 1 very glossy 1-0.5
Probe 2 stark glänzend 1-0,5Sample 2 very glossy 1-0.5
Probe 3 schwach glänzend 2-2,5.Sample 3 slightly glossy 2-2.5.
Für die zahlenmäßige Bewertung des Oberflächenglanzes wurde ein Hilfsgerät zur Bestimmung der Streureflexion verwendet.For the numerical evaluation of the surface gloss, an auxiliary device was used to determine the Diffuse reflection used.
Claims (4)