DE1696481C - Manufacture of low-reflection glass surfaces, especially for slide cover glasses - Google Patents
Manufacture of low-reflection glass surfaces, especially for slide cover glassesInfo
- Publication number
- DE1696481C DE1696481C DE1696481C DE 1696481 C DE1696481 C DE 1696481C DE 1696481 C DE1696481 C DE 1696481C
- Authority
- DE
- Germany
- Prior art keywords
- ecm
- glass surfaces
- low
- manufacture
- slide cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
Die Erfindung bezieht sich auf die Herstellung von reflexarmen Glasoberflächen, insbesondere für Diapositivdeckgläser, mit schrägliegender Schollenstruk- * tür und abgerundeten Kanten an deren Übergangsstellen, durch Behandlung der gereinigten Glasoberflächen mit einem Flußsäure, Schwefelsäure, Wasser und Ammoniumbifluorid enthaltenden Atzmittel.The invention relates to the production of low-reflection glass surfaces, in particular for slide cover glasses, with sloping clod structure * and rounded edges at their transition points, by treating the cleaned glass surfaces with a hydrofluoric acid, sulfuric acid, water and etchants containing ammonium bifluoride.
Es ist bekannt, Glas durch feine Aufrauhung der Oberfläche reflexfrei zu machen, ohne dem Glas die Durchsichtigkeit zu nehmen. Dies kann z. B. durch feines Sandstrahlen erzielt werden. In anderer Weise kann dies durch Anätzen mittels verdünnter Flußsäure und Alkalifluoriden erreicht werden, bei der eine Mattierung der Glasoberfläche eintritt, die etw;i einer feinkristallinen Struktur entspricht. Obwohl das Glas durchsichtig bleibt, tritt dennoch eine Verminderung des Lichtdurchgangs ein.It is known that glass can be made reflex-free by fine roughening the surface without affecting the glass To take transparency. This can e.g. B. can be achieved by fine sandblasting. In a different way this can be achieved by etching using dilute hydrofluoric acid and alkali fluorides, in which a matting of the glass surface occurs, which corresponds somewhat to a finely crystalline structure. Though that Glass remains transparent, there is still a reduction in the passage of light.
Zur Erzielung einer reflexarmen Oberflächenstruktur mit ineinander übergehenden Mikrowölbungen und -ausnehmungen in unregelmäßiger Verteilung ist ao durch die deutsche Auslegeschrift 1 086 405 bekannt, die Glasoberfläche beim Ätzen mittels Flußsäure durch auf der Glasoberfläche dicht aufliegende, feinstverteilte und in Flußsäure unlösliche Teilchen, z. B. aus Calziumfluorid, Silizium oder Bariumsulfat, as partiell abzudecken.To achieve a low-reflection surface structure with merging micro-curvatures and recesses in irregular distribution is known from the German Auslegeschrift 1 086 405, the glass surface when etching with hydrofluoric acid by lying tightly on the glass surface, finely divided particles insoluble in hydrofluoric acid, e.g. B. from calcium fluoride, silicon or barium sulfate, as to be partially covered.
Die Verwendung von Ammoniumbifluorid als Bestandteil eines Ätzmittels ist durch die USA.-Patentschrift 2 936 554 bekannt. Das Ätzen der Glasoberfläche dient bei dem dort beschriebenen Verfahren der gesteuerten Auflockerung der Glasoberfläche, um das Abtragen der Glaspartikeln beim anschließenden mechanischen Polieren der Glasoberfläche zu erleichtern. The use of ammonium bifluoride as a component of an etchant is disclosed in U.S. Patent 2,936,554 known. The etching of the glass surface is used in the process described there the controlled loosening of the glass surface in order to remove the glass particles during the subsequent to facilitate mechanical polishing of the glass surface.
Versuche haben gezeigt, daß eine Oberflächenstruktur der eingangs erwähnten Art besonders geeignet ist, um bei Verwendung bei Diapositivdeckgläsern das Auftreten der auf Interferenz beruhenden Newtonschen Ringe zu verhindern, ohne einen ungünstigen Einfluß auf die Projektion des Bildes auszuüben. In gleicher Weise ist diese Oberflächenstruktur vorteilhaft, wenn es allein darauf ankommt, das Glas weitgehend reflexarm zu machen, wie dies z. B. bei Verwendung des Glases für Bildverglasungen od. dgl. erwünscht ist.Tests have shown that a surface structure of the type mentioned at the beginning is particularly suitable is to prevent the occurrence of interference based on slide cover glasses when used To prevent Newton's rings without exerting an unfavorable influence on the projection of the image. In the same way, this surface structure is advantageous when it all comes down to the To make glass largely low-reflective, as z. B. when using the glass for picture glazing or the like. Is desired.
Der Erfindung liegt die Aufgabe zugrunde, eine derartige Oberflächenstruktur der Glasoberfläche zu erzielen.The invention is based on the object of providing such a surface structure for the glass surface achieve.
Diese Aufgabe wird dadurch gelöst, daß ein Ätzmittel, bestehend ausThis object is achieved in that an etchant consisting of
100 ecm 70 bis 75%iger Flußsäure,
80 ecm Wasser,100 ecm 70 to 75% hydrofluoric acid,
80 ecm of water,
40 ecm roher Schwefelsäure (66° Be) und
10 g Ammoniumbifluorid40 ecm of crude sulfuric acid (66 ° Be) and
10 g ammonium bifluoride
auf eine Dauer von 4 bis 120 Sekunden und mit einer Temperatur von 10 bis 5O0C, vorzugsweise 25°C, auf die Glasoberfläche zur Einwirkung gebracht wird. * " Der Grad der erzielten Mattierung kann hierbeiin a period of 4 to 120 seconds and at a temperature of 10 to 5O 0 C, preferably 25 ° C, is brought to the glass surface to act. * "The degree of matting achieved can here
55 durch die Wahl der Ätzbedingungen im beanspruch-^ ten Rahmen eingestellt werden. Dieser ist außer von der chemischen Zusammensetzung des Glases auch! von dem Verhältnis zwischen Ätzzeit und Temperatur des Ätzmittels abhängig. Stets wird aber die angestrebte schollenartige Struktur mit verhältnismäßig großen Flächenteilen, deren Kanten an den Übergangsstellen abgerundet sind, erreicht.. 55 can be set within the claimed framework by the choice of the etching conditions. This is also due to the chemical composition of the glass! depends on the relationship between the etching time and the temperature of the etchant. However, the desired clod-like structure with relatively large surface areas, the edges of which are rounded at the transition points, is always achieved.
Weitere Versuche haben erwiesen, daß gewisse Abwandlungen der Anteile der einzelnen Bestandteile des Ätzmittels zugelassen werden können und dann die angestrebte Struktur ebenfalls erreicht wird.Further experiments have shown that certain variations in the proportions of the individual components of the etchant can be allowed and then also achieved the desired structure will.
In weiterer Ausgestaltung der Erfindung wird daher in dem Ätzmittel jeweils nur ein Bestandteil im Rahmen der folgenden Werte abgewandelt:In a further embodiment of the invention, only one component is therefore in each case in the etchant modified within the scope of the following values:
bis 75°/oiger Flußsaure von 70 bis 120 ecm.up to 75% hydrofluoric acid from 70 to 120 ecm.
Wasser von 50 bis 120 ecm,Water from 50 to 120 ecm,
rohe Schwefelsäurecrude sulfuric acid
(66° Be) von 10 bis 70 ecm und(66 ° Be) from 10 to 70 ecm and
Ammoniumbifluorid .... von 3 bis 20 g. -Ammonium bifluoride .... from 3 to 20 g. -
Vorteilhaft ist es, wenn das Ätzmittel beim Ansetzen gut umgerührt wird, und zwar so lange, bis sich das Ammoniumbifluorid vollständig aufgelöst hat.It is advantageous if the etchant is stirred well when it is made up, until the ammonium bifluoride has completely dissolved.
Die Struktur ist bei 100- bis 200facher Vergrößerung gut erkennbar.The structure is at 100 to 200 times magnification good to see.
Claims (2)
Family
ID=