DE1696244A1 - Paper-plastic film for refining sheet-like materials - Google Patents
Paper-plastic film for refining sheet-like materialsInfo
- Publication number
- DE1696244A1 DE1696244A1 DE19661696244 DE1696244A DE1696244A1 DE 1696244 A1 DE1696244 A1 DE 1696244A1 DE 19661696244 DE19661696244 DE 19661696244 DE 1696244 A DE1696244 A DE 1696244A DE 1696244 A1 DE1696244 A1 DE 1696244A1
- Authority
- DE
- Germany
- Prior art keywords
- paper
- plastic
- film
- plastic film
- chipboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
HÖ©ER - STELLRECHT - Θ Rl ESS BACH - HÄECKERHÖ © ER - LAW - Θ Rl ESS BACH - HÄECKER
PATENTANWÄLTE IN STUTTSARTPATENT LAWYERS IN STUTTSART
A 35 353A 35 353
w - 123
6.1Ο»19ββ w - 123
6.1Ο »19ββ
18962U18962U
PAPXIRMBEIK SCHlUi1SLBIPAPXIRMBEIK SCHLUi 1 SLBI
73117311
Papier-Kunststoff -Polie zur edeluttg plattonf'ormlg&s WerkstoffePaper-plastic film for edeluttg plattonf 'ormlg & s materials
Die Erfindung betrifft eine Papiei^Kunststoff-^olie siar Ver edeluag platteöförmiger Werkstoffe sowie ein ?eirfatoea «um Herstellen einer solchenThe invention relates to a paper ^ plastic ^ olie siar Ver edeluag plate-shaped materials as well as a? eirfatoea "um Manufacture of such a
Ea ist toeSsairot, platteuförroig© Werkstoff®* S9B9 Ea is toeSsa red, platteuforroig © Material® * S 9 B 9
oder SgsQPAslsplatteis» iöro^ Aiäfteii3g@a eineror SgsQPAslsplatteis »iöro ^ Aiäfteii3g @ a one
BADORIQINAI.BADORIQINAI.
A 35 355 roA 35 355 ro
6. 10. 1966 - jf - - . -. October 6, 1966 - jf - -. -.
Dekorschicht au veredeln-. So werden beispielsweise Spanplat ten gegenwärtig auf folgende Weise veredelt?Refine the decorative layer. For example, chipboard are currently refined in the following way?
1. Auf ein® Spanplatte wird mit Hilfe eines Polyv&tiylalkohol-Elebers od.dgl. eine Sdiicntstoffplatte mit Dekorscliicnt aufgeklebt. Seeignete ten sind ζ.B9 unter den Bezeichnungen loriBica- oder Ultrapas-Platten im Handel«1. On a chipboard with the help of a Polyv & tiylalkohol-Elebers or the like. a plastic plate glued on with decorative clips. Sea lignites are ζ.B 9 under the names loriBica or Ultrapas plates in the trade «
2m Auf eine Spanplatte wird direkt ein mit Melaiainforiaaldenydaarz getränktes Dekorpapier heiß aufgepreßt· 2 m A decorative paper soaked with Melaiainforiaaldenydaarz is pressed hot directly onto a chipboard
Die oben unter 1. angegebene Veredelung erfordert zunächst die separate Herstellung einer Schichtstoff platte, was durch Zusammenpressen eines Stapels aus behalten Papieren bei etwa 140 - 1500O und etwa 150 kp/cm erfolgen kann. Der zu verpressende Stapel kann dabei folgendermaßen aufgebaut sein (von unten nach oben) ι Mit Melaittiaharz getränktes Gegenzugpapier (unbedrucktes Dekorpapier), mehrere mit Phenolfonaal=' dehydharg getränkte Kraftpapiere (Kernpapiere) 9 mit MelaiBim« \axz getränktesj meist weißes Untsrlagenpapier (Barriere«The refinement given above under 1. first requires the separate production of a laminate board, which can be done by compressing a stack of retained papers at about 140-150 0 O and about 150 kp / cm. The to be compressed stack can be constructed as follows (from bottom to top) ι By Melaittiaharz soaked balancer paper (unprinted decorative paper), several (with Phenolfonaal = 'dehydharg impregnated kraft paper (core papers) 9 MelaiBim "\ AXZ getränktesj mostly white Untsrlagenpapier barrier"
BAD ORIQiNAtBAD ORIQiNAt
BJ - 123 .BJ - 123.
6.10.1966 Λ T-Zr. October 6, 1966 Λ T-Zr.
oder Underlaypapier), mit Melaminhars getränktes.» bedrucktes oder unbedrucktes Dekorpapier, mit Melaminhare getränktes Overlaypapier. Die so gewonnene Schichtstoffplatte kann auf eine oder beide Oberflächen der Spanplatte aufgeklebt werden.or underlay paper), soaked with melamine resin. " printed or unprinted decor paper, soaked with melamine hair Overlay paper. The laminated board obtained in this way can be placed on one or both surfaces of the chipboard are glued on.
Die oben unter 2. genannte Veredelung einer Spanplatte erfolgt dadurch, daß ein mit Melaiainforiaaldehydharz getränktes, einfarbiges oder bedrucktes Dekorpapier- sehr saugfähiges, opakes Papier - bei etwa 1450O und einem Druck von etwaThe above under 2. refinement of a chipboard takes place in that a single-colored or printed decorative paper impregnated with Melaiainforiaaldehydharz - very absorbent, opaque paper - at about 145 0 O and a pressure of about
2 ? 2 ?
10-25 kp/cm» vorzugsweise 15-20 kp/cm , auf eine o$er beide Seiten einer Spanplatte aufgepreßt wird.10-25 kp / cm »preferably 15-20 kp / cm, on one o $ er both sides of a chipboard is pressed on.
Die nach den bekannten Verfahren veredelten Flatten sind, verhältnismäßig teuer, weil das auf einer Papiermaschine gefertigte Dekorpapier in einem besonderen Arbeitsgang auf einer Imprägniermaschine mit etwa 100 - 130 Gew.^ (bezogen auf das Papiergewicht) beharzt werden muß, wobei die Leistung der Ioprägnieismaschine meist nur etwa 6 - 12 m Papierbahn pro Minute beträgt· Außerdem sind die so beharzten Papiere und die verpreßten Platten spröde und brüchig, so daß bei der Fertigung und Verarbeitung ein beträchtlicher Ausschuß entsteht» Bei dennaen dem zweiten Verfahren veredelten Span-The flattened according to the known processes are, relatively expensive because it was made on a paper machine Decor paper in a special process an impregnation machine with about 100 - 130 wt on the weight of the paper), whereby the performance of the Iopregnation machine is usually only about 6 - 12 m paper web per minute · In addition, the resin-coated papers and the pressed plates are brittle and fragile, so that at a considerable scrap arises during production and processing.
4 s-4 s-
1Q-9&4.7./-JQL3JB21Q-9 & 4.7 ./- JQL3JB2
BAD ORiÖflNAL" "BAD ORiÖflNAL ""
m - 123 > ■m - 123> ■
6.10ο 1966 ., -Abentstehe« außerdem in der Wärme oder bei trockener Atmosphäre auf den veredelten Seiten leicht Spannungsrisee, was auf das jeweils unterschiedliche Verhalten oder "Arbeiten" der Spanplatte bzw. der raelaminbeharzten Dekorschicht zurückgeht.6.10ο 1966., -Desist "also in the warmth or when it is dry Atmosphere on the refined pages slightly tense rises, which indicate the different behavior or "work" the chipboard or the decorative layer coated with raelamin resin is decreasing.
Die Erfindung geht von der Aufgabe aus9 eine Papier^Kuaststoff=* Folie vorzuschlagen9 mit deren Hilfe sich unter Einsparung von Arbeit und Zeit billigere und bessere Schichtwerkstoffe herstellen lassen. The invention is based on the task of 9 proposing a paper plastic film 9 with the help of which cheaper and better layer materials can be produced while saving work and time.
Gemäß der Erfindung zeichnet sich eine für die Lösung der gestellten Aufgabe geeignete Folie dadurch aus, daß ein flächiger Körper aus Papiermasse mit einer Kunststoffdispersion ge« füllt ist und auf wenigstens einer Oberfläche einen - insbesondere heißsiegelfähigen - Kunststoff-PiIm aufweist.According to the invention is characterized for the solution of Set task suitable film in that a flat body made of paper pulp with a plastic dispersion ge « is filled and on at least one surface one - in particular heat-sealable - plastic PiIm.
Eine solche Papier-Kunststoff-Polie läßt sich erfindungsgemäß dadurch herstellen, daß zu einem üblichen, für die Papierherstellung geeigneten, Zellulosefaeern enthaltenden Stoffbrei 20 - 40 Gew.# (bezogen auf die Pasermenge) eines thermoplastischen, fein dispergieren, polymeren Kunststoffes Bugegeben werden, daß dieser Stoff in einer Papiermaschine in an eichSuch a paper-plastic sheet can be used according to the invention manufacture by that to a common, for paper production suitable pulp containing cellulose fibers 20 - 40 wt. # (based on the amount of Paser) of a thermoplastic, Finely disperse, add polymeric plastic be that this substance in a paper machine in at calibration
109-847/0382 BADORlGINAt 109-847 / 0382 BADORlGINAt
A 35 353 πι
m - 123
6.10.1966A 35 353 πι
m - 123
October 6, 1966
bekannter Weise zu einer kunststoff gefüllten Bahn verarbeitet wird, und daß auf wenigstens eine Seite der nahezu trockenen Bahn ein Kunststoff«Film aufgetragen wird.processed in a known way to a plastic-filled web will, and that on at least one side of the nearly dry Bahn a plastic film is applied.
Me fertige Papier-Kunststofffolie kann gemäß einer bevor-! äugten Ausführungsform der Erfindung weiterhin auf wenigstens einer Seite bedruckt werden.Me finished paper-plastic film can according to a pre-! ugly embodiment of the invention can also be printed on at least one side.
Ss wurde gefunden, daß die Veredelung von Spanplatten mit der srfindungegemäßen, in der Papiermaschine herstellbaren Folie überraschend einfach und - da die Folie nicht spröde und brüchig ist - praktisch ohne Ausschuß durchführbar ist. Ferner hat sich ergeben, daß eine erfindungsgemäß veredelte Spanplatte frei von Rißbildung infolge Wärme oder Austrocknung ist.It was found that the finishing of chipboard with the according to the invention, which can be produced in the paper machine Surprisingly simple and - since the film is not brittle and fragile is - practically feasible without waste. It has also been found that a chipboard refined according to the invention is free from cracking due to heat or drying out.
Sie nachstehende Beschreibung bevorzugter Ausführungsformen der Erfindung dient im Zusammenhang mit der beiliegenden Zeich«» nung und mehreren Beispielen der weiteren Erläuterung.See the description of preferred embodiments below the invention is used in conjunction with the accompanying drawings and several examples for further explanation.
Eine für die Veredelung von Spanplatten, Faserplatten, Sperrholzplatten od.dgl. geeignete Papier-Kunststoff-Folie läßt sich erfindungegemäß folgendermaßen herstellen:One for the finishing of chipboard, fiberboard, plywood or the like. suitable paper-plastic film produce according to the invention as follows:
109847/0382 BAD109847/0382 BATH
A 35 353 KJ m - 123 6.10.1966 A 35 353 KJ m - 123 October 6, 1966
oder .or .
Kurze und/lange Zellulosefasern werden im üblichen Mischungsverhältnis zusammen mit Weiß«» und/oder Buntpigmenten, die der Erzielung der gewünschten Opazität und Farbe dlensa, in bekannter Weise vermählen. Vor oder nach dem Mahlen wird ein Uaßverfestigungsmittel zugegeben. Nach dem Mahlen werden 20 ~ 40 Gew.^vorzugsweise ?5 - 35 Gew.^, bezogen auf die eingesetzte Paserstoffmenge, eines thermoplastischen, polymeren Kunststoffs in feiner Dispersion zugefügt und achlisßlieh noch die .rtetentionsmitte^ür die Pigmente beigegeben 9 worauf der pH-Wert des Stoffbreies mittels Alüminiumtriformiat-, Aluminiumsulfat- oder Säurelösung auf die gewünschte Sfcufe9 z.B. auf S,8, eingestellt und automatisch geregelt wird.Short and long cellulose fibers are ground in the usual mixing ratio together with white "" and / or colored pigments, which are used to achieve the desired opacity and color. A solidifying agent is added before or after grinding. After grinding, 20 ~ 40% by weight, preferably 5 - 35% by weight, based on the amount of fiber used, of a thermoplastic, polymeric plastic are added in a fine dispersion and finally the retention agent for the pigments is added 9 whereupon the pH- The value of the pulp by means of aluminum triformate, aluminum sulfate or acid solution is set to the desired level 9, e.g. to S, 8, and is automatically regulated.
Nach dem lauf des Stoffes über Stoffauflauf, Sieb, Uaßpreeeen und Trockenzylinder einer üblichen Papiermaschine wird auf die nahezu trockene Papierbahn entweder noch in der Papiermaschine oder in einer besonderen Streichmaschine mittels einer herkömmlichen Auftrags- oder Streicheinrichtung einseitig oder beidseitig ein vorzugsweise heißsiegelfähiger Kunststoff-Pilro aufgetragen, wobei der Film entweder unter Verwendung einer Kunstatoffdiapereion oder als Kunststoffschmelze unter Verwendung eines Extruders oder auf eine andere After the material has run over the headbox, wire, Uaßpreeeen and drying cylinder of a conventional paper machine, a preferably heat-sealable plastic pilro is applied to one or both sides of the almost dry paper web either in the paper machine or in a special coating machine using a conventional application or coating device, the film using either a plastic diaperion or as a plastic melt using an extruder or another
geeignete Weise aufgebracht wird.is applied in a suitable manner.
109847/0382109847/0382
A 35 353 roA 35 353 ro
ι» - 123ι »- 123
6.10.1966 — - -10/6/1966 - - -
Die so hergestellte Folie kann nun'bedruckt werden, wobei der Druck entweder auf die mit dem Film überzogene Seite oder auf die filmfreie Papierseite aufgebracht werden kann. Pabei sind die Druckeigenschrften wegen der Elastizität der Füllung des Papierss mit einer Kunststoffdispersion überraschend gut.The film produced in this way can now be printed, with the pressure either on the side covered with the film or can be applied to the film-free paper side. The compressive properties are due to the elasticity of the Filling of the paper with a plastic dispersion is surprising Well.
Die erfindungsgemäße Folie kann - bedruckt oder unbedruckt im Zusammenhang mit der Herstellung von veredelten Dekorplat*- ten auf verschiedene Weise verwendet werden.The film according to the invention can be printed or unprinted in Connection with the production of refined decorative plates * - can be used in a number of ways.
1«, Die Papier-Kunststoff-Folie kann auf ihrer den Kunststoff» Film tragenden Seite mit einer - z.B. transparenten Kunststoff-Folie, insbesondere aus Polyvinylchlorid, beispielsweise durch Aufkaschieren in einem KaTa-nder unter Erwärmung veredelt werden. Der so erhaltene Werkstoff kann durch einen Kleber mit der papierähnlichen Rück* seite z.B. auf Spanplatten aufgebracht werden. Vor dem Aufkaschieren der Kunststoff-Folie kann die Papier«« Kunststoff-Folie auf der Filmseite bedruckt werden.1 «, the paper-plastic film can on its the plastic» Film-bearing side with a - e.g. transparent plastic film, in particular made of polyvinyl chloride, for example by lamination in a KaTa-changer be refined under heating. The material obtained in this way can be glued to the paper-like back * side can be applied to chipboard, for example. Before the Laminating the plastic film can make the paper «« Plastic foil can be printed on the film side.
2. Die Papier-Kunststoff-Folie kann unbedruckt gelassen oder auf der papierähn-lichen, filmfreien Seite bedruckt2. The paper-plastic film can be left unprinted or printed on the paper-like, film-free side
- 8 10 98 4 7/0382 - 8 10 98 4 7/0382
BADBATH
A 35 355 m
a - 123
6.10.1966A 35 355 m
a - 123
October 6, 1966
und dann mit Hilfe der heißsiegelfähigen Filmseite auf eine Spanplatte od.dgl. aufkaschiert werden. Dieser Fall ist auf der schematischen Zeichnung dar- · gestellt. Bas Bezugszeichen 1 bezeichnet die mit einem Kunststoff-PiIiB 2 beschichtete, auf der papierähnlichen Rückseite 3 mit einer Holzmaserung bedruckte Papier-Kunststoff -Polie, die im Innern mit Kunststoff 4 gefüllt und mittels der heißsiegelfähigen Filmseite auf eine Holzspanplatte 5 aufgebracht ist .and then using the heat sealable film side on a chipboard or the like. be laminated. This case is shown on the schematic drawing posed. The reference number 1 denotes the one coated with a plastic PiIiB 2, on the paper-like Back 3 paper-plastic film printed with a wood grain, the inside filled with plastic 4 and is applied to a chipboard 5 by means of the heat-sealable film side.
!Die so veredelte Spanplatte kann als solche verwendet werden. Sie kann aber auch durch lackieren mit Polyester-, Nitro- oder einen: anderen in der Möbelindustrie gebräuchlichen, farblosen oder farbig getönten Lack weiterveredelt werden. Dabei ist es überraschend günstig, daß die Opazität einer so behandelten Folie besser ist, als die eines mit etwa 100$ Melaminharz getränkten und verpreßten Dekorpapiers.The chipboard finished in this way can be used as such. However, it can also be further refined by painting with polyester, nitro or another colorless or color-tinted varnish commonly used in the furniture industry. It is surprisingly beneficial that the opacity of a film treated in this way is better than that of a decorative paper impregnated with about 100 $ melamine resin and pressed.
3. Die Papier-Kunststoff-Folie kann unbedruckt oder auf der papierähnlichen, filmfreien Seite bedruckt mit3. The paper-plastic film can be unprinted or printed with on the paper-like, film-free side
10 9847/038210 9847/0382
A 35 353 m A 35 353 m
id - 123 - 'id - 123 - '
6.10.1966 ■-October 6, 1966 ■ -
Hilfe der heißsiegelfähigen Filmssite auf eine. Spanoder Hartfaserplatte oder auch auf eine Lage mit Phenolformaidehydhars getränkter„ saugfähiger Kernpapiere (Matronkraftpapiere) aufgepreßt werden. Dabei wird außerdem zur Erzielung einer mechanisch sehr wi~ derstandfähigen Oberfläche ein auf die Oberseite der Papier-Kunststoff-Folie aufgelegtes melaminformaldehydbeharztes Overlaypapier (nicht pigmentiertes, nach dem Beharzen und Vorpressen transparent werdendes Paper niedrigen Flächengewichte) mit aufgepreßt. Das Vorpressen erfolgt unter den üblichen Bedingungen, wie sie dem Fachmann bei der Herstellung dekorativer laminatplatten bekannt sind.Help the heat sealable film site on a. Spanoder Hardboard or on a layer with Phenolformaidehydhars soaked "absorbent core papers (Matron Kraft papers) are pressed on. In addition, to achieve a mechanically very wi ~ the stable surface on top of the Paper-plastic film applied melamine-formaldehyde resin Overlay paper (non-pigmented paper that becomes transparent after resinating and prepressing low grammage). The pre-pressing takes place under the usual conditions, such as the expert in the production of decorative laminate panels are known.
Eine mit Weiß- und Farbpigmenten versehene Zellstoffaufschläm·=· mung, wie sie bei der Dekorpapierherstellung üblich ist, wird unter Zusatz eines Naßverfestigungsmittels, z.B. Nadavin der Farbwerke Bayer Leverkusen, in bekannter Weise mit Holländern oder Refinern gemahlen. Der erhaltenen wässrigen AufschlämmungA pulp slurry provided with white and colored pigments = as is customary in the manufacture of decorative paper with the addition of a wet strength agent, e.g. Nadavin from Farbwerke Bayer Leverkusen, in a known manner with Dutch or refined. The obtained aqueous slurry
- 10 -- 10 -
10 984 7/0382 SAD10 984 7/0382 SAD
A 35 353 ro
m - 123
6.10o1966A 35 353 ro
m - 123
6.10o1966
werden 20 - 40 #, vorzugsweise 25 ·» 35 $ einer wässrigen Dispersion eines thermoplastischen, polymeren Kunststoffs, z.B. Lutofan (ein Polyvinylchlorid-Misehpolyinezisat), zugegeben, wobei die Prozentzahlen den Feststoffgehalt der Kunststoff-Dispersion bezogen auf 100 Teile Zellstoff in absolut trockenem Zustand bedeuten. Nach dem Mahlen werden Retentionsmittel, ZoB. Polyacrylsäureamid (Retaroinol), Galaktoraannan (Polygal), Natriumaluminat od.dgl. zugegeben und der gewünschte pH-Wert mit Aluminiumsulfat, Aluminiumtriformiat oder einer Säure, z.B. auf den Wert 6, 8, eingestellt. Hierauf wird die Stoffauf schlämmung in bekannter Weise durch den Stoffauflauf auf ein Papiermaöchienensieb geleitet und die auf dem Sieb entstandene Papierbahn über die Naßpressen uM Trockenzylinder der Papiermaschine geführt. Danach wird auf der Ober·=* und/oder Unterseite der Bahn ein Kunststoffilm aufgebracht, wae durch den Auftrag einer wäßrigen Kunststoffdispersion, z.B. eines Polyvinylchlorid-Butyleater-MischpolyraeiSsätes oder einer Kunststofflösung mit Hilfe einer an eich bekannten Auftragseinrichtungen (z.B. Leimpresse, Luftbürste, Rollenauftrag, Rackelauftrag) erfolgen kann. Das Aufbringen des Kunststoffilms erfolgt entweder während dea Laufs der Bahn auf der Papiermaschine oder mit Hilfe einer besonderen Streichmaschine nach der Fertigung der Papierbahn.20-40 #, preferably 25x35 $, of an aqueous dispersion of a thermoplastic, polymeric plastic, e.g. Lutofan (a polyvinyl chloride mixed polyinezate), added, whereby the percentages represent the solids content of the plastic dispersion based on 100 parts of pulp in an absolutely dry state. After grinding, retention aids, ZoB. Polyacrylic acid amide (Retaroinol), Galaktoraannan (Polygal), Sodium aluminate or the like. added and the desired pH with aluminum sulfate, aluminum triformate or an acid, e.g. to the value 6, 8. Then the fabric is on slurry in a known manner through the headbox a paper machined sieve and the resultant on the sieve Paper web over the wet press and drying cylinder the paper machine. Then on the upper · = * and / or A plastic film is applied to the underside of the web, wae through the application of an aqueous plastic dispersion, e.g. one Polyvinylchloride-Butyleater-MischpolyraeiSätes or a plastic solution with the help of an application device known from calibration (e.g. size press, air brush, roller application, knife application) can be done. The plastic film is applied either while the web is running on the paper machine or with the help of a special coating machine the manufacture of the paper web.
- 11 -- 11 -
109847/a382109847 / a382
ro - 123ro - 123
Es wird entsprechend Beispiel I eine Papier-Kunststoff-Folie hergestellt, wobei als Kunststoffdispersion für die Papierfüllung eine Dispersion eines Styrol-Butadien-Mischpolymerisats und für die einseitige Befilmung ebenfalls eineStyrol-Butadien-Mischpolymeraat-Dispersion verwendet wird.According to Example I, a paper-plastic film is used produced, with as a plastic dispersion for the paper filling a dispersion of a styrene-butadiene copolymer and also a styrene-butadiene copolymer dispersion for one-sided filming is used.
Man-verfährt entsprechend Beispiel I, verwendet jedoch als Kunststoff«Dispersion ein Acrylsäurebutylester-Vinylazetat-MißchpolymeiSsat. Proceed as in Example I, but used as Plastic dispersion of an acrylic acid butyl ester-vinyl acetate-MisschpolymeiSat.
Man verfährt entsprechend Beispiel I, verwendet jedoch als Kunststoff-Dispersion ein Methacrylsäurebutylester-Methacryleäure· äthylester-Mischpolymerisat.The procedure is as in Example I, but used as Plastic dispersion a butyl methacrylate methacrylic acid ethyl ester copolymer.
Man verfährt entsprechend Beispiel I, verwendet jedoch als Kunststoff-Dispersion ein Vinylpropionatpolymerisat.The procedure is as in Example I, but used as a plastic dispersion a vinyl propionate polymer.
~ 12 109847/0382 ~ 12 109847/0382
A 35 355 βA 35 355 β
α - 123α - 123
6.10.1966 -10/6/1966 -
Man verfährt entsprechend Beispiel Ϊ, verwendet jedoch als Kunststoff-Dispersion ein Vinylazetat-Vinylpalmitat-Misehpolymerisat. Proceed as in example Ϊ, but use as Plastic dispersion a vinyl acetate-vinyl palmitate mixed polymer.
Man verfährt entsprechend Beispiel I, verwendet jedoch als Haßverfestigungsmittel anstelle von Haöavin Melaminforiaaldehydharz, welches erst nach dem Mahlproseß zugegeben wird.The procedure is as in Example I, but used as Hate strengthening agent instead of Haöavin melaminforiaaldehyde resin, which is only added after the grinding process.
Beispiel VIIIExample VIII
Eine nach einem der Beispiele I - VII hergestellte Papier-Kunststoff -Folie, deren eine Seite Papier- und deren andere Seite Kunststoff Charakter hat, wird auf der Filmseite bedruckt und auf dieser Seite in bekannter Weise mit einer transparenten farblosen oder farbigen Kunststoff -Folie, z.B· einer Polyvinylchlorid-Folie versehen, was z.B. durch Aufkalandrieren erfolgen kann.A paper plastic produced according to one of Examples I-VII Foil, one side of which is paper and the other side plastic, is printed on the film side and on this side in a known manner with a transparent, colorless or colored plastic film, e.g. a polyvinyl chloride film provided, which can be done e.g. by calendering can.
Das so erhaltene Material ist aufrollbar und kann gemäß einer weiteren Ausgestaltung der Erfindung unter Verwendung einesThe material obtained in this way can be rolled up and according to one further embodiment of the invention using a
- 13 109BA7/0382 - 13 109BA7 / 0382
6.10.1966October 6, 1966
Λ 3 Λ 3
Klebers ait der Papierseite auf eine Span-, Faser-,Metall- oder Holzplatte aufgebracht werden, wodurch dekorative-» billige Platten, z.B. für die ,Möbelherstellung erhalten werden.Glue ait the paper side on a chipboard, fiberboard, metal or wooden panel, making decorative »cheap Panels, e.g. for furniture production.
Beispiel IX ίExample IX ί
Eine nach einem der Beispiele I - VII hergestellt3-Papier-Kunststoff-Folie wird erfinduntggeiaäß auf der Papierseite z.B. mit Holzdessin bedruckt und mit der heißaiegalfähigen Filmseite unter Druck und Wärme auf eine Span-, Paser- oder Holzplatte aufgepreßt.A 3-paper-plastic film produced according to one of Examples I - VII is invented on the paper side E.g. printed with a wood design and with the hot-eye-compatible Film side pressed onto a chipboard, Paser board or wood board under pressure and heat.
Man erhält auf diese W©ise Dekorplattenf deren Oberfläche
allerdings nicht besonders kratzfest ist» die aber durch
lackieren mit einem üblichen Kunstharzlack, z.B. Möbel-, ™
Boots-, Nitro» oder dgl. lack weiterveredelt werden können
und so furnierten Platten ähnlich werden. Für die Möbelindustrie bietet sich dabei der Vorteil, daß durch Wahl eines
z.B. farbig getönten Lackes der Farbton der Plattenoberfläche passend eingestellt werden kann.
This gives W © ise decorative panels but not for the surface superior scratch resistance is "but by
varnishing with a conventional synthetic resin varnish, for example furniture, boat, nitro or similar varnish can be further refined and thus become similar to veneered panels. For the furniture industry, this has the advantage that the color of the panel surface can be adjusted to match by choosing, for example, a color-tinted varnish.
~ 14 -~ 14 -
109*47/0382109 * 47/0382
ro - 123ro - 123
6.10.1966 ~ 14 ~ October 6, 1966 ~ 14 ~
Eine Bach einem der Beispiele X - VII hergestellte Papier-Kunststoff -Folie wird gemäß einsr weiteren Auaführungsforra der Erfindung auf der Papierseite bedruckt, auf der bedruckten Papierseite mit einem Melamiaformaldebydharsegetrankteu Over« laypapier bedeckt und dann mit der lieißsisgelfähigen Film-= seite bei etwa 20 kp/cm Druck und 150 C auf eine Span 9 Faser- oder Holzplatte aufgepreßt, wobei je nach Verwendung hochglänzener oder satter, verchromter Metallpreßplatt en glänzende oder matte, kratzfeste, veredelte Platten erhalten werden.A paper-plastic film produced by Bach one of Examples X - VII is printed on the paper side according to a further embodiment of the invention, covered on the printed paper side with a melamiaformaldebydharsegetrankteu overlay paper and then covered with the lissisgel-capable film side at about 20 kp / cm pressure and 150 C on a chipboard 9 fibreboard or wood board, with glossy or matt, scratch-resistant, refined boards being obtained depending on the use of high-gloss or rich, chrome-plated metal press plates.
Eine nach einem der Beispiele I ~ VII hergestellte Papier-Kunststoff -Folie wird auf der Papieraeite bedruckt, auf der bedruckten Papierseite mit einem njelaminformaldehydharzgetränkten Overlaypapier bedeckt und dann mit der heißsiegelfähigen Filmseite unter etwa 100-kp/on Druck und bei 150 C auf eine lage phenolformaldehydharzgetränkter Kernpapiere (Natronkraftpapiere), unter denen noch ein melaminformaldehydharzgetränktes Dekorpapier (Gegenzugpapier) liegen kann, aufgepreßt. Die Verpressung erfolgt zwischen verchromtenA paper plastic produced according to one of Examples I ~ VII -Film is printed on the paper side, on the printed paper side with a njelaminformaldehyde resin impregnated Overlay paper covered and then covered with the heat sealable Film side under about 100 kp / on pressure and at 150 ° C on a layer of phenol-formaldehyde resin-impregnated core papers (Soda kraft papers), including a melamine-formaldehyde resin soaked Decorative paper (backing paper) can lie, pressed on. The pressing takes place between chrome-plated
- 15— 109847/0382 - 15-109847/0382
BADBATH
in - 123
6.10.1966in - 123
October 6, 1966
Platten oder zwischen Trennpapieren. Es entstehen kratzfeste, glänzende oder matte Dekorationsplatten.Plates or between release papers. The result is scratch-resistant, glossy or matt decorative panels.
Die hier in Betracht gezogenen Papier-Kunststoff-Folien bzw. die gemäß der Erfindung aus ihnen gewonnenen Laminatplatten besitzen folgende ,Vorteile:The paper-plastic films or plastic films considered here the laminate panels obtained from them according to the invention have the following advantages:
Die Papier-Kunststoff-Folien enthalten ihren Kunststoffgehalt bereits auf der schnell laufenden Papiermaschine, brachen also nicht mehr in besonderen, sehr langsam laufenden Maschinen beharzt werden. Die Folien besitzen eine sehr lange, praktisch unbegrenzte lagerfähigkeit, während eaie üblichen, mit Melaminformaldehydharz getränkten Dekorpapiere infolge der fortschreitenden Polykondensation des Harzes nur sehr beschränkt lagerfähig sind- Weiterhin lassen sich die erfindungsgemäßen Folien sehr gut rollen, bedrucken und verarbeiten. Im Gegensatz hierzu sind die üblichen, mit Melarainformaldehydharz getränkten Dekorpapiere spröd und brechen leicht.The paper-plastic films contain their plastic content already on the fast-running paper machine, broke So no longer have to be treated in special, very slowly running machines. The films have a very long, practically unlimited shelf life, while the usual, with Melamine-formaldehyde resin impregnated decorative papers as a result of the progressive polycondensation of the resin can only be stored to a very limited extent Roll, print and process foils very well. In contrast, the usual ones are impregnated with melara formaldehyde resin Decorative papers are brittle and break easily.
Zum Zwecke der Herstellung veredelter Platten können die erfindungsgemäßen Papier-Kunststoi'f-Folien mit solchen Kunststoffen hergestellt werden, die das geBirchtete "Durchbluten" For the purpose of producing refined panels, the paper / plastic films according to the invention can be produced with plastics that allow the "bleeding"
- 16 -- 16 -
109847/0382109847/0382
BADOMtMAt.BADOMTMAt.
A55353. 16962UA 55353 . 16962U
πι - 123 ' πι - 123 '
6.10.1966October 6, 1966
des Phenolformaldehydharzes verhindern. Der gemäß der Erfindung eingelagerte Kunststoff bildet nämlich für das Phenolhara eine Sperre« Auf diese Weise läßt sich auch ein besonders» Barrierepapier einsparen. Bei der Herstellung von Ieminatpltit- e* ten ist weiterhin bei Verwendung der .erfindungsgeEiäßen Folien weniger Kunststoff erforderlich als s.B. bei raelaminforiaalde= hydbeharzten Dekorpapieren. Somit ist bei erfindungsgemäß gewonnenen Iiaminatplatten auch die Opazität günstiger als bei Verwendung melaminbeharzter Dekorpapiere. Schließlich können, worauf bereits hingewiesen wurde, mit Hilfe der erfindungsgemäßen Papier-Kunststoff-Folie Dekorplatten und veredelte Platten, *^Β. veredelte Spanplatten, billiger hergestellt werden als nach den bisher gebräuchlichen Verfahren.prevent the phenol-formaldehyde resin. The plastic stored according to the invention forms a barrier for the phenolic resin. "In this way it is also possible to save a special" barrier paper. In the production of Ieminatpltit- e * th with the use of the inventive foils, less plastic is required than, for example, with raelaminforiaalde = hydresinated decorative papers. Thus, in the case of laminate panels obtained according to the invention, the opacity is also more favorable than when using melamine-resinated decorative papers. Finally, as has already been pointed out, decorative panels and refined panels, * ^ Β, can be used with the paper-plastic film according to the invention. refined chipboard, can be produced more cheaply than with the previously common processes.
- 17 -- 17 -
109BA7/0382109BA7 / 0382
Claims (5)