DE1646653C - Method for applying a ceramic protective coating to a pipe which is used for blowing gaseous and / or solid components, in particular oxygen, into or onto molten metal, in particular iron - Google Patents
Method for applying a ceramic protective coating to a pipe which is used for blowing gaseous and / or solid components, in particular oxygen, into or onto molten metal, in particular ironInfo
- Publication number
- DE1646653C DE1646653C DE1646653C DE 1646653 C DE1646653 C DE 1646653C DE 1646653 C DE1646653 C DE 1646653C
- Authority
- DE
- Germany
- Prior art keywords
- pipe
- coating material
- ceramic coating
- molten metal
- wire mesh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Hch zum Einführen des gasförmigen Sauerstoffes in io gleicher Weise (Umhüllung mit einem locker gewebden mit geschmolzenem Eisen gefüllten Konverter ten Stoff oder Drahtgewebe, Aufbringen des keramischen Überzugsmaterials und Trocknung) eine zweite Schutzschicht aufgebracht wird, die ein beHch for the introduction of the gaseous oxygen in the same way (covering with a loosely woven fabric converter filled with molten iron th fabric or wire mesh, applying the ceramic Coating material and drying) a second protective layer is applied, which is a be
sonders gegen Schlacken und Metallschmelzen be-especially against slag and molten metal
(innere) Schutzschicht eignen sich dabei insbesondere Zirkon oder feuerfeste Fasern und für die zweite (äußere) Schutzschicht Korund.The (inner) protective layer is particularly suitable for zirconium or refractory fibers and for the second (outer) protective layer corundum.
Es können für die Schutzschichten aber auch andere keramische Überzugsmaterialien verwendet werden, wie beispielsweise Quarz, Sillimanit oder Schamotte. Als Bindemittel ist beispielsweise Wasserglas geeignst.However, other ceramic coating materials can also be used for the protective layers such as quartz, sillimanite or chamotte. An example of a binding agent is water glass suitable.
Faserverstärkte keramische Werkstoffe sind zwar an sich bekannt, wie sich aus der Zeitschrift »Berichte der Deutschen Keramischen Gesellschaft«, 43 (1966), S. 337 bis 345, sowie der USA.-Patentschrift 3 092 247 ergibt. Die Anwendung von faserverstärk-Fiber-reinforced ceramic materials are known per se, as can be seen from the journal »Reports der Deutschen Keramische Gesellschaft ", 43 (1966), pp. 337 to 345, as well as the USA patent specification 3 092 247 results. The application of fiber reinforced
oder Siemens-Martin-Ofen Eisenrohre verwandt. Zusammen
mit dem gasförmigen Sauerstoff können dabei auch noch feste Bestandteile, wie z. B. Kohlenstoff
und Kalk, eingeblasen werden. Das Verfahren 15 ständigeskeramisches Überzugsmaterial enthält,
kann dabei in der Weise angewandt werden, daß das Als keramisches Oberzugsmaterial für die ersteor Siemens-Martin furnace related iron pipes. Together with the gaseous oxygen, solid components such as. B. carbon and lime, are blown. The method 15 contains permanent ceramic coating material,
can be used in such a way that the As a ceramic covering material for the first
Einblasrohr oberhalb des Flüssigkeitsspiegels der Metallschmelze endet und der Sauerstoff und die übrigen Bestandteile so auf die Metallschmelze geblasen werden, daß sie in dieselbe einzudringen ver- ao mögen und dort die Frischarbeit leisten können. Es ist aber auch möglich, das Einblasrohr von vornherein in die Metallschmelze eintauchen zu lassen, in die dann der Sauerstoff und die übrigen Bestandteile eingeblasen werden. In jedem Falle ist es aber so, daß die dabei verwandten Eirblasrohre infolge von Abbrand und Verzunderung einem sehr schnellen Verschleiß unterworfen sind.Injection pipe above the liquid level the metal melt ends and the oxygen and the other constituents are blown onto the molten metal in such a way that they penetrate into the same and can do the fresh work there. But it is also possible to remove the injection pipe from the start to be immersed in the molten metal, in which then the oxygen and the other components be blown in. In any case, however, it is the case that the Eirblasrohre used as a result are subject to very rapid wear from burn-off and scaling.
Es ist daher bereits bekannt, diese Rohre mitIt is therefore already known to use these pipes
einem Kühlmantel zu versehen und durch Wasser- 30 ten keramischen Überzügen zur" Lösung des
kühlung den Verschleiß hjr tbzusetzen. Diese dungsgemäßen Problems wird jedoch in diesen Ver-Arbeitsweise
hat jedoch den Nachteil, daß beim öffeniiiehungen nicht vorgeschlagen. Das erfindungs-Undichtwerden
des Kühlmantels unkontrolliert gemäße Verfahren wird durch diese Veröffentlichun-Wasserdampf
in die Metallschmelze geblasen wird. gen auch nicht nahegelegt. Dabei ist vor allem auchto be provided with a cooling jacket and by water-thirt ceramic coatings to "dissolve the
cooling to reduce wear and tear. However, this problem according to the invention is in this method of operation has the disadvantage that it is not suggested in the case of opening. The process according to the invention-leakage of the cooling jacket in an uncontrolled manner is blown into the molten metal by this publication. gen also not suggested. Above all, there is also
Es ist auch bereits vorgeschlagen worden (deutsche 35 zu berücksichtigen, daß die weiter oben genannten
Auslegeschrift 1101 468), bei der Kühlung der Ein- drei Anforderungen, die an den Schutzüberzug des
blasrohre an Stelle von Wasser den zum Einblasen Rohres gestellt werden müssen, nur dann befriedidienenden
Sauerstoff selbst zu verwenden. Dabei soll gend erfüllt werden können, wenn der Schutzüberzug
die Entspannung des im allgemeinen mit einem zwei Schutzschichten aufweist und nach dem erfin-Druck
von z. B. 25 Atm angelieferten Sauerstoffes 40 dungsgemäßen Verfahren hergestellt wird,
auf den Betriebsdruck des Einblasrohres im Kühl- Dabei kann der locker gewebte Stoff oder dasIt has also already been proposed (German 35 to take into account that the above-mentioned Auslegeschrift 1101 468), only three requirements that must be placed on the protective coating of the blowpipe instead of water for the blow-in pipe when cooling the inlet then to use satisfactory oxygen himself. It should be able to be met if the protective coating has the relaxation of the generally with a two protective layers and after the inventions pressure of z. B. 25 atm supplied oxygen 40 is produced according to the method,
on the operating pressure of the injection pipe in the cooling. The loosely woven fabric or the
mantel dieses Rohres vorgenommen werden, wobei Drahtgewebe vor dem Aufbringen auf das Rohr mit die Entspannung durch eine entsprechende Bemes- einer Suspension des keramischen Überzugsmaterials sung des Kühlmantels eingestellt werden soll. Es ist getränkt werden und dann auf das Rohr aufgebracht in der Praxis jedoch schwierig, auf diese Art und 45 werden. Das keramische Überzugsmaterial kann aber Weise die Druckverhältnisse den jeweils schwanken- auch als Suspension auf die bereits aufgebrachte den Betriebsbedingungen anzupassen. Außerdem tritt Umhüllung aus locker gewebtem Stoff oder Drahtbeim geringsten Undichtsein des Kühlmantels Sauer- gewebe aufgetragen werden, ζ. Β. durch Aufstreichen, »toff nach außen, der dann — im Gegensatz zum wobei die gewünschte Dicke der Schicht leicht ein-Wasserdanipf — den sofortigen Abbrand des Ein- 50 gestellt werden kann.jacket of this pipe can be made, using wire mesh prior to application to the pipe the relaxation through a corresponding measurement of a suspension of the ceramic coating material solution of the cooling jacket is to be set. It is to be soaked and then applied to the pipe in practice, however, it will be difficult to do so in this way and 45. The ceramic coating material can, however Way the pressure conditions fluctuate in each case - also as a suspension on the already applied adapt to the operating conditions. There is also wrapping made of loosely woven fabric or wire With the slightest leak in the cooling jacket, sour tissue can be applied, ζ. Β. by spreading, »Soak to the outside, which then - as opposed to being the desired thickness of the layer slightly a-dehydrated - the immediate burn-up of the setting 50 can be set.
blasrohres begünstigt. Entscheidend für den Erfolg des erfindungs-blowpipe favored. Crucial for the success of the inventive
Das Ziel der vorliegenden Erfindung war es nun, gemäßen Verfahrens ist, daß die Schutzschichten des •in Verfahren zum Aufbringen eines keramischen Rohres mit einer Umhüllung aus locker gewebtem Schutzüberzuges auf einem derartigen Rohr zu ent- Stoff oder Drahtgewebe versehen sind. Dadurch wird wickeln, durch das die Verschleißbeständigkeit des 55 das Haftvermögen des keramischen Überzugsmate-Rohres wesentlich verbessert wird und gleichzeitig rials auf dem Rohr ganz erheblich verbessert. Außerdem zeigt der Überzug in diesem Falle im getrockneten Zustand eine verbesserte Plastizität. Eingehende Versuche haben nämlich ergeben, daß es 60 zwar auch ohne Verwendung der Umhüllung aus locker gewebtem Stoff oder Drahtgewebe möglich ist, auf das Rohr einen keramischen Überzug mit einer Stärke von etwa 1 bis 3 mm aufzutragen. Das Haftvermögen eines derartigen Überzuges läßt je* The aim of the present invention was, according to the method, that the protective layers of the • in a method for applying a ceramic pipe with a covering of loosely woven protective coating on such a pipe are provided with material or wire mesh. This will wrap, through which the wear resistance of the 55, the adhesion of the ceramic coating material tube is significantly improved and at the same time rials on the tube are significantly improved. In addition, in this case the coating shows improved plasticity in the dried state. Incoming Tests have namely shown that it is 60 even without use of the wrapping of loosely woven cloth or wire mesh possible to apply to the tube a ceramic coating having a thickness of about 1 to 3 mm. The adhesive strength of such a coating can
Die gestellte Aufgabe wird gelöst durch ein Ver- 6g doch sehr zu wünschen übrig, und der so hergestellte fahren zum Aufbringen eines keramischen Schutz- Überzug ist äußerst empfindlich gegen Stoß oderThe problem posed is achieved by a device that leaves a lot to be desired, and the one produced in this way drive to apply a ceramic protective coating is extremely sensitive to impact or
Schlag und neigt sehr zum Brüchigwerden. Für die Herstellung der Umhüllung sind dabeiImpact and is very prone to breakage. For the production of the casing are included
die Nachteile der wasserdampf- bzw. sauerstoffgckühlten Rohre vermieden werden. An den keramischen Schutzüberzug des Rohres sind dabei folgende Anforderungen zu stellen:the disadvantages of the steam or oxygen cooled pipes are avoided. The following requirements must be placed on the ceramic protective coating of the pipe:
1. gute Wärmedämmung,1. good thermal insulation,
2. gute Beständigkeit gegen Schlacken und Metallschmelzen sowie2. Good resistance to slag and molten metal as well
3. gute Haftfähigkeit auf dem Rohr.3. Good adhesion to the pipe.
Überzuges auf einem Rohr, das zum Auf- oder Einblasen von gasförmigen und/oder festen Bestand-Coating on a pipe, which is used to inflate or blow in gaseous and / or solid constituents
locker gewebte Stoffe, wie Mull oder Gaze, aber auch entsprechende Gewebe aus Glaswolle oder Asbest sowie feinmaschige Drahtgewebe geeignet. Diese Gewebe können am zweckmäßigsten in Form einer Binde angewandt werden, die auf das Rohr aufgewickelt wird. Es ist aber natürlich auch möglich, die Gewebe in einem einzigen Stück aef das Rohr aufzuwickeln. Ob man die eine oder andere Methode anwendet, wird in erster Linie von den Dimensionen des Rohres abhängen.but also loosely woven fabrics such as gauze or gauze Appropriate fabrics made of glass wool or asbestos as well as fine-mesh wire mesh are suitable. These tissues can most conveniently be used in the form of a bandage that is wound onto the tube will. But it is of course also possible to wind up the fabric in a single piece aef the tube. Whether one uses one method or the other depends primarily on the dimensions depend on the pipe.
Es liegt auf der Hand, daß die nach dem erfindungsgemäßen Verfahren mit einem keramischen Überzug versehenen Rohre nicht nur für das eingangs beschriebene Frischverfahren eingesetzt werden können, sondern aurh für andere Prozesse, bei denen die Rohre ähnlichen Bedingungen unterworfen werden müssen.It is obvious that the process according to the invention with a ceramic Coated pipes are not only used for the fresh process described above can, but aurh for other processes in which the pipes are subjected to similar conditions Need to become.
In der Abbildung ist ein Querschnitt durch ein Rohr dargestellt, das nach dem erfmejungsgemäßen Verfahren mit einem keramischen Schutzüberzug ao versehen worden ist. Das Bezugszeichen 1 stellt dabei das Rohr dar, auf das als Umhüllung das Mullgewebe 2 aufgewickelt worden ist. Dieses dient der Aufnahme einer aus Zirkon bestehenden Suspension 3. Das Mullgewebe und die Zirkonsuspension as sind dabei innig miteinander verbunden und bilden nach dem Trocknen die innere Schutzschicht des keramischen Schutzüberzuges. Darüber befindet sich wieder eine Umhüllung 4, diesmal aus Drahtgewebe, auf das eine Korund enthaltende keramische Suspension 5 aufgetragen worden ist. Drahtgewebe und Korundsuspension sind ebenfalls innig miteinander verbunden und bilden nach dem Trocknen die äußere Schutzschicht des keramischen Schutzüberzuges.The figure shows a cross section through a tube, which according to the invention Method has been provided with a ceramic protective coating ao. The reference number 1 represents represents the tube on which the gauze 2 has been wound as a cover. This serves the Taking up a suspension consisting of zirconia 3. The gauze fabric and the zirconium suspension as are intimately connected and form the inner protective layer of the after drying ceramic protective coating. Above this there is again a cover 4, this time made of wire mesh, to which a corundum-containing ceramic suspension 5 has been applied. Wire mesh and Corundum suspensions are also intimately connected and form the outer one after drying Protective layer of the ceramic protective coating.
Claims (5)
Family
ID=