DE1609610B1 - For the erection of walls, an essentially cuboid component made of foamed plastic - Google Patents

For the erection of walls, an essentially cuboid component made of foamed plastic

Info

Publication number
DE1609610B1
DE1609610B1 DE19661609610 DE1609610A DE1609610B1 DE 1609610 B1 DE1609610 B1 DE 1609610B1 DE 19661609610 DE19661609610 DE 19661609610 DE 1609610 A DE1609610 A DE 1609610A DE 1609610 B1 DE1609610 B1 DE 1609610B1
Authority
DE
Germany
Prior art keywords
component
surface layer
walls
erection
foamed plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19661609610
Other languages
German (de)
Inventor
Moog Gerhard Willy
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CONTEMPORARY WALLS Ltd
Original Assignee
CONTEMPORARY WALLS Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CONTEMPORARY WALLS Ltd filed Critical CONTEMPORARY WALLS Ltd
Publication of DE1609610B1 publication Critical patent/DE1609610B1/en
Pending legal-status Critical Current

Description

1 21 2

Die Erfindung betrifft ein zum Errichten von Wänden Material hergestellten, erfindungsgemäßen Formbestimmtes, im wesentlichen quaderförmiges Bau- bausteins liegt zwischen etwa 7 und 31,5kp/cm2. element aus aufgeschäumtem Kunststoff auf der Die harte Oberflächenschicht erhöht wesentlich dieThe invention relates to a shape-determined, essentially cuboidal building block produced for the erection of walls, material according to the invention and lying between approximately 7 and 31.5 kgf / cm 2 . element made of foamed plastic on the The hard surface layer significantly increases the

Basis von verschäumbaren Polymeren, insbesondere Tragfähigkeit des Bauelements. Durch, seine Einvon Urethan-, Phenol-, Styrol- und/oder Epoxypoly- 5 stückigkeit ist die Fertigung vereinfacht, so daß auch meren oder Vorpolymeren, vorzugsweise mit zumindest Kosten eingespart werden.Based on foamable polymers, especially the load-bearing capacity of the component. By, its income Urethane, phenol, styrene and / or Epoxypoly- 5 pieces, the production is simplified, so that too mers or prepolymers, preferably with at least cost can be saved.

einem oben und unten ausmündenden, durchgehenden Da die erfindungsgemäßen Bauelemente eine harte,a top and bottom opening, continuous Since the components according to the invention have a hard,

Hohlraum. glatte Oberfläche aufweisen, kann diese OberflächeCavity. have a smooth surface, this surface can

Quaderförmige Bauelemente aus aufgeschäumtem selbst an Stelle eines Wandverputzes als Sichtfläche Kunststoff sind beispielsweise durch das deutsche io dienen. Wenn der aufschäumbaren Masse vor dem Gebrauchsmuster 1 865 679 bekannt. Diese Bau- Eingießen in die Form verschiedene Farbstoffe beielemente sind jedoch auf Grund ihrer geringen gemengt werden, kann ein mit erfindungsgemäßen Tragfähigkeit primär nur für die Herstellung von Bauelementen errichtetes Gebäude jede gewünschte Zwischenwänden geeignet. Für tragende Wände, Farbe oder Farbkombination haben,
insbesondere bei mehrstöckigen Gebäuden, sind sie 15 In jede Seite des Bauelements können verschiedene deshalb bisher nur zu Isolierzwecken verwendet Muster oder Zeichen, z. B. architektonische Muster, worden, und zwar entweder als Verkleidung und als durchlöcherte Platten, Schrift- oder andere Zeichen, Zwischenschicht für die Wände oder als Schalungs- eingegossen werden.
Cuboid components made of foamed plastic instead of plastering the wall are used, for example, by the German io. If the foamable mass was known before the utility model 1,865,679. These building elements pouring into the form of various dyes are mixed, however, due to their small size, a building constructed with the load-bearing capacity according to the invention primarily only for the production of building elements can have any desired partition walls suitable. For load-bearing walls, have color or color combination,
especially in multi-storey buildings, they are 15. In each side of the building element, different patterns or characters, e.g. B. architectural patterns have been, either as cladding and as perforated panels, writing or other characters, interlayer for the walls or poured as formwork.

körper für Mantelbetonwände, wie es z. B. in dem Mit den durchgehenden Hohlräumen kann esbody for clad concrete walls, such as B. in the with the through cavities it can

deutschen Gebrauchsmuster 1 862 964 beschrieben 20 wahlweise auch als verbleibendes Schalungselement worden ist, bei denen der Ortbeton das tragende für die Mantelbetonweise verwendet werden, wobei Element bildet. auf Grund der höheren Tragfähigkeit der Einzel-German utility model 1 862 964 described 20 optionally also as a remaining formwork element has been, in which the in-situ concrete is used as the load-bearing for the mantle concrete, with Element forms. due to the higher load-bearing capacity of the individual

Aus dem deutschen Gebrauchsmuster 1 938 260 ist elemente vor dem Ausgießen mit Beton erheblich es ferner bekannt, Bauelemente aus tragfähigem höhere Wände errichtet werden können.
Kunststoff zu fertigen und mit einem Kunststoff 25 Es hat sich als zweckmäßig erwiesen, daß das auszuschäumen; jedoch ist die Fertigung solcher verschäumbar Polymer zusätzlich die Entflammung Bauelemente zu einem gewissen Grade umständlich verzögernde Zusatzstoffe enthält,
und daher aufwendig. In der Zeichnung ist die Erfindung in Ausf ührungs-
From the German utility model 1 938 260 elements prior to pouring with concrete it is also known, components can be erected from load-bearing higher walls.
To manufacture plastic and with a plastic 25 It has proven to be useful that the foam; However, the manufacture of such foamable polymer is additionally the inflammation building elements contains to a certain extent cumbersome delaying additives,
and therefore expensive. In the drawing, the invention is in execution

Der Erfindung liegt daher die Aufgabe zugrunde, beispielen dargestellt. Es zeigtThe invention is therefore based on the object, presented examples. It shows

ein Bauelement zu schaffen, das unter Beibehaltung 30 Fig. 1 einen Ausschnitt einer aus Bauelementen seiner guten Isoliereigenschaften sowohl als tragendes nach einem Ausführungsbeispiel der Erfindung beBauelement, z.B. für Hohlwände, als auch in bekannter stehenden Wand mit Eckbauelementen,
Weise als Schalungselement für Mantelbetonwände F i g. 2, 3 und 4 eines der Bauelemente der Wand
to create a building element which, while maintaining 30 Fig. 1, shows a section of a building element made of building elements with its good insulating properties both as a load-bearing element according to an exemplary embodiment of the invention, for example for cavity walls, as well as in a known standing wall with corner building elements,
Way as a formwork element for clad concrete walls F i g. 2, 3 and 4 one of the structural elements of the wall

verwendet werden kann und das zugleich einfach zu nach der Fig. 1 in einer Draufsicht, einer Seiten- und fertigen ist. 35 einer Stirnansicht,can be used and at the same time easy to according to FIG. 1 in a plan view, a side and finished is. 35 a front view,

Diese Aufgabe wird nach der Erfindung bei dem F i g. 5 das Bauelement nach den F i g. 2 bis 4This object is achieved according to the invention in FIG. 5 the component according to FIGS. 2 to 4

quaderförmigen Bauelement der eingangs erwähnten in dem Querschnitt nach der Linie 5-5 in der F i g. 3 Art dadurch gelöst, daß das Bauelement eine einteilig in vergrößertem Maßstab,cuboid component of the initially mentioned in the cross section along the line 5-5 in FIG. 3 Type solved in that the component is a one-piece on an enlarged scale,

mit ihm ausgebildete, d. h. aus dem gleichen Stoff F i g. 6 ein Bauelement nach einem weiterentrained with him, d. H. from the same fabric F i g. 6 shows one component according to another

bestehende glatte Oberflächenschicht und einen Kern 40 Ausführungsbeispiel in parallelperspektivischer Darmit gegenüber der Oberflächenschicht geringerer stellung undexisting smooth surface layer and a core 40 embodiment in parallel perspective Darmit lower position than the surface layer and

Dichte aufweist, daß die Dichte im Kern rund 0,032 F i g. 7 ein weiteres Ausführungsbeispiel des erfin-Density has that the density in the core is around 0.032 F i g. 7 a further embodiment of the inven-

bis 0,064 g/cm3 und in der Oberflächenschicht rund dungsgemäßen Bauelements in parallelperspektivischer 0,16 bis 0,96 g/cm3 beträgt und daß die Dicke der Darstellung.to 0.064 g / cm 3 and in the surface layer around the component according to the invention in parallel perspective 0.16 to 0.96 g / cm 3 and that the thickness of the representation.

Oberflächenschicht etwa 0,40 bis 6,35 mm be- 45 In der F i g. 1 ist eine Wand dargestellt, von der trägt. einige Schichten gezeigt sind und die unter Ver-The surface layer is about 0.40 to 6.35 mm thick. 1 shows a wall from which wearing. some layers are shown and the under

Es ist hierbei an sich nicht neu, Schaumstoffe aus wendung von erfindungsgemäßen Bauelementen 10 Polyesterharz so zu verändern, daß eine weiche, errichtet wurde. Bei der besonderen, hier gezeigten grobporige Schicht kontinuierlich in eine feinporige, Wand sind die Bauelemente 10 durch schichtartiges härtere Schicht übergeht, wodurch jedoch noch kein 50 Versetzen ihrer Stoß- und Lagerflächen derartig ge-Weg zum Erfindungsgegenstand aufgezeigt ist. staltet, daß Nuten und Federn entstehen, die beiIt is not new per se here to use foams from structural elements 10 according to the invention To change polyester resin so that a soft one was built. With the special one shown here coarse-pored layer continuously into a fine-pored wall, the components 10 are layer-like harder layer passes, which, however, does not yet offset their abutment and bearing surfaces in such a way the subject of the invention is shown. so that grooves and tongues are created that contribute to

Das Normalgewicht der verwendeten Schaumstoff- versetzten Bauelementen in den Fugen 11 ineinandermasse entspricht derjenigen Menge, die zur Herstellung greifen. Die in dieser Figur dargestellten Bauelemente der etwa zweieinhalb-bis zehnfachen Menge notwendig 10 besitzen einige oben und unten ausmündende ist, wenn man eine Schaumstoffmasse normaler Dichte 55 Hohlräume 23, die das Bauelement 10 durchqueren, von 0,03204 bis 0,06401 g/cm3 herstellt. Verwendet Die sichtbaren Fugen 13 zwischen den Bauelementen man dieses zusätzliche Gewicht an verschäumbarer können verschieden ausgebildet sein. Zur Verbindung Masse für die Ausformung der erfindungsgemäßen der Bauelemente 10 ist ein Klebemittel, z. B. ein Bauelemente, so erhält man die harte, glatte Oberfläche Epoxyharz, besonders geeignet. Andere Arten der als Teil des Elements. Die derart erhaltene Oberfläche 60 Verbindung der Bauelemente 10 miteinander werden ist glatt, nicht porös, verhältnismäßig dampfundurch- im folgenden erwähnt.The normal weight of the foam-offset construction elements used in the joints 11 in one another corresponds to the amount that is required for production. The components shown in this figure of about two and a half to ten times the amount necessary 10 have some opening at the top and bottom if a foam mass of normal density 55 cavities 23 which traverse the component 10, from 0.03204 to 0.06401 g / cm 3 manufactures. The visible joints 13 between the structural elements and this additional weight of foamable material can be designed in different ways. To connect the mass for the formation of the components 10 according to the invention, an adhesive, for. B. a component, the hard, smooth surface epoxy resin is obtained, which is particularly suitable. Other types of as part of the item. The surface 60 obtained in this way, the connection of the components 10 to one another, is smooth, non-porous, and is relatively impermeable to vapor, as will be mentioned below.

lässig und hat eine relativ gleichförmige Dicke. Diese F i g. 1 zeigt ferner Eckbauelemente 14 und 15.casual and has a relatively uniform thickness. This F i g. 1 also shows corner components 14 and 15.

Dicke variiert normalerweise zwischen 0,397 und Das Eckbauelement 14 besitzt einen langen Schenkel, 6,35 mm. Die Dichte im Kern des Bauelements der sich in der Zeichnung nach links erstreckt, und variiert zwischen etwa 0,03204 und 0,06408 g/cm3, 65 einen kurzen Schenkel, der sich zur senkrecht abwährend die Dichte im Bereich der verdichteten gehenden Seitenwand erstreckt. Beim Eckbauelement Oberflächenschicht etwa 0,1602 bis 0,9612 g/cm3 15 sind die kurzen und langen Schenkel umgekehrt beträgt. Die Druckfestigkeit des aus dem geeigneten angeordnet. Für andere Verbände können Eckbau-Thickness typically varies between 0.397 and The corner component 14 has a long leg, 6.35 mm. The density in the core of the component, which extends to the left in the drawing, and varies between approximately 0.03204 and 0.06408 g / cm 3 , 65 a short leg that extends perpendicularly to the density in the area of the compacted going sidewall . In the case of the corner component, the surface layer is approximately 0.1602 to 0.9612 g / cm 3 , the short and long legs are reversed. The compressive strength of the arranged from the appropriate. For other associations, corner construction

elemente mit gleich langen Schenkeln verwendet werden.elements with legs of the same length can be used.

In den F i g. 2, 3, 4 und 5 ist ein besonderes Ausführungsbeispiel des erfindungsgemäßen Bauelements ähnlich dem in der F i g. 1 gezeigten dargestellt. Durch das Bauelement 20 erstrecken sich zwei oben und unten ausmündende, durchgehende Hohlräume 23. Wie in F i g. 2 dargestellt, trägt die in der Zeichnung linke Stoßfläche des Bauelements 20 einen federartigen Ansatz 22, während in der rechten Stoßfläche eine Nut 21 vorgesehen ist, so daß beidseitig anstoßende, gleichartige Bauelemente nut-feder-artig mit dem Bauelement 20 sich verbinden. Die Bauelemente 20 besitzen ferner einen weiteren federartigen Ansatz 24 und eine Nut 25 an ihren oberen und unteren Lagerflächen. Zum Erleichtern des Einschiebens des Ansatzes 22 in die Nut 21 eines zweiten Bauelements besitzen beide Teile seitlich abgeschrägte Flächen 26.In the F i g. 2, 3, 4 and 5 is a special embodiment of the component according to the invention similar to that in FIG. 1 shown. Two continuous cavities 23 opening out at the top and bottom extend through the component 20. As in Fig. 2, the left abutment surface of the component 20 in the drawing has a spring-like one Approach 22, while in the right abutment surface a groove 21 is provided so that both sides abutting, Similar components are connected to the component 20 in the manner of a tongue and groove. The components 20 have also another spring-like extension 24 and a groove 25 on their upper and lower bearing surfaces. To make it easier to insert the extension 22 into the groove 21 of a second component both parts laterally beveled surfaces 26.

Die Fig. 5 zeigt einen Querschnitt durch das Bauelement20 entlang der Linie 5-5 in der Fig. 3. Die harte, einheitlich ausgebildete, glatte Oberflächenschicht 51 ist einstückig mit dem gesamten Bauelement 20 hergestellt. Der aufgeschäumte Kern 52 von geringerer Dichte ist von der Oberflächenschicht 51 vollständig umschlossen. Die Dicke der Oberflächenschicht 51 beträgt etwa zwischen 0,397 und 6,35 mm; ihre Dichte beträgt etwa 0,1602 bis 0,9612 g/cm3. Die Dichte des Kernes 52 bewegt sich zwischen 0,03204 und 0,06408 g/cm3.FIG. 5 shows a cross section through the component 20 along the line 5-5 in FIG. 3. The hard, uniformly formed, smooth surface layer 51 is produced in one piece with the entire component 20. The foamed core 52 of lower density is completely enclosed by the surface layer 51. The thickness of the surface layer 51 is approximately between 0.397 and 6.35 mm; their density is about 0.1602 to 0.9612 g / cm 3 . The density of the core 52 ranges between 0.03204 and 0.06408 g / cm 3 .

Wie dieses Ausführungsbeispiel in Verbindung mit der F i g. 6 zeigt, können sich Hohlräume 23 in bekannter Weise lotrecht, waagerecht oder in beiden Richtungen durch das Bauelement 20 erstrecken. Diese Hohlräume 23 können nicht nur zur Gewichtserleichterung und/oder als Isolierkammer dienen, sondern auch auf verschiedene Art für weitere Zwecke, wie zum Auffüllen mit Beton zum Vergrößern der Festigkeit und Steifheit einer Wand, ausgenutzt werden; sie können ferner auch Rohrleitungen, Kabel usw. aufnehmen, was ebenfalls bekannt ist.As this exemplary embodiment in conjunction with FIG. 6 shows, cavities 23 in extend vertically, horizontally or in both directions through the component 20 in a known manner. These cavities 23 can not only serve to reduce weight and / or as an insulating chamber, but also in various ways for other purposes, such as filling with concrete to enlarge the Strength and rigidity of a wall, are exploited; you can also use pipelines, Record cables, etc., which is also known.

Das Bauelement 60 ist besonders für die Mantelbetonbauweise geeignet. Zu diesem Zweck weist das in der F i g. 6 dargestellte Bauelement 60 drei oben und unten ausmündende Hohlräume 61 sowie einen sich waagerecht durch das Bauelement 60 erstreckenden, nicht näher gekennzeichneten Hohlraum auf. In diese Hohlräume 61 können in bekannter Weise Bewehrungsstähle 62 od. dgl. vor dem Auffüllen mit Beton eingesetzt sein.The component 60 is particularly suitable for the concrete shell construction. To this end, the in FIG. 6 component 60 shown three above and below opening cavities 61 and one cavity which extends horizontally through the component 60 and is not identified in any more detail. Reinforcing steel 62 or the like can be inserted into these cavities 61 in a known manner before being filled with Be used concrete.

In F i g. 7 ist ein stockwerkshohes, plattenf örmiges Bauelement dargestellt, dessen Mittelteil zum Zweck der klareren Darstellung weggelassen ist. Es kann auch jede andere gewünschte Abmessung besitzen. Solche Bauelemente sind besonders für die Fertigteil-Bauweise auf einem Rastersystem geeignet, wobei ein Streifen 72 das Ausrichten in der Ebene erleichtert. Der Streifen 72 greift beim Versetzen dieser Bauelemente in ihre Nut 71 ein, die an Stelle eines federartigen Ansatzes an der unteren Lagerfläche vorgesehen ist. Die Nut 73 an der oberen Lagerfläche dient zur Aufnahme einer Leiste 74. Ein Verbindungsstab 76 erstreckt sich durch einen Hohlraum 75 und dient zum Befestigen der Leiste 74 entweder an dem Bauelement oder in bekannter Weise zum Zusammenspannen des Streifens 72 mit der Leiste 74.In Fig. 7 a floor-high, plate-shaped component is shown, the middle part of which is for the purpose is omitted for clarity of illustration. It can also have any other desired dimension. Such Components are particularly suitable for prefabricated construction on a grid system, with a strip 72 making it easier to align in the plane. The strip 72 engages in their groove 71 when these components are moved a, which is provided in place of a spring-like projection on the lower bearing surface. The groove 73 on the upper bearing surface is used to receive a bar 74. A connecting rod 76 extends through a cavity 75 and is used to attach the bar 74 either to the component or in for clamping the strip 72 together with the ledge 74 in a known manner.

Hier können die Bauelemente zweckmäßig mittels Klebemittel verbunden sein; sie können aber auch durch Bolzen, Kabel, Druckknopfverschluß, Anschlitzung oder eine Kombination der genannten Verbindungen aneinander befestigt sein.Here, the components can expediently be connected by means of adhesives; but they can too by bolts, cables, snap fasteners, connections or a combination of the above Connections to be attached to each other.

Bei der Fertigung können der Schaumstoffmasse Zusatzstoffe beigemengt werden, so daß das Bauelement feuerfest wird und entflammungsverzögernde Eigenschaften erhält. Zu diesen Zusatzstoffen gehören Phosphor- und/oder halogenhaltige Stoffe, z. B. Tris-/S-chloräthylphosphatjTrisdichlorpropylphosphatjChlorierte Biphenyle und Polyphenyle, Tris-(2,3-dibrompropyl)-phosphate, Tetrabrombisphenol A, Tetrabromphthalsäureanhydrid, Pentabromphenol und andere Polyole auf PhosphatbasisDuring production, additives can be added to the foam mass, so that the component becomes fireproof and acquires flame-retardant properties. These additives include Phosphorus and / or halogenated substances, e.g. B. Tris- / S-chloroethylphosphate / trisdichloropropylphosphate / chlorinated Biphenyls and polyphenyls, tris (2,3-dibromopropyl) phosphates, tetrabromobisphenol A, tetrabromophthalic anhydride, Pentabromophenol and other phosphate-based polyols

Claims (2)

Patentansprüche:Patent claims: 1. Zum Errichten von Wänden bestimmtes, im wesentlichen quaderförmiges Bauelement aus aufgeschäumtem Kunststoff auf der Basis von verschäumbaren Polymeren, insbesondere von Urethan-, Phenol-, Styrol- und/oder Epoxypolymeren oder Vorpolymeren, vorzugsweise mit zumindest einem oben und unten ausmündenden, durchgehenden Hohlraum, dadurch gekennzeichnet, daß das Bauelement (10, 20, 60) eine einteilig mit ihm ausgebildete, d. h. aus dem gleichen Stoff bestehende glatte Oberflächenschicht (51) und einen Kern (52) mit gegenüber der Oberflächenschicht geringerer Dichte aufweist, daß die Dichte im Kern rund 0,032 bis 0,064 g/cm3 und in der Oberflächenschicht rund 0,16 bis 0,96 g/cm3 beträgt und daß die Dicke der Oberflächenschicht etwa 0,40 bis 6,35 mm beträgt.1. For the erection of walls, essentially cuboidal structural element made of foamed plastic based on foamable polymers, in particular urethane, phenolic, styrene and / or epoxy polymers or prepolymers, preferably with at least one continuous cavity opening out at the top and bottom , characterized in that the component (10, 20, 60) has a smooth surface layer (51) formed in one piece with it, ie consisting of the same material, and a core (52) with a lower density than the surface layer, that the density in the core is around 0.032 to 0.064 g / cm 3 and in the surface layer is around 0.16 to 0.96 g / cm 3 and that the thickness of the surface layer is around 0.40 to 6.35 mm. 2. Bauelement nach Anspruch 1, dadurch gekennzeichnet, daß das verschäumbare Polymer zusätzlich die Entflammung verzögernde Zusatzstoffe enthält.2. Component according to claim 1, characterized in that that the foamable polymer additionally contains additives which retard the flammability contains. Hierzu 2 Blatt ZeichnungenFor this purpose 2 sheets of drawings
DE19661609610 1965-07-02 1966-07-04 For the erection of walls, an essentially cuboid component made of foamed plastic Pending DE1609610B1 (en)