DE1558016C3 - Process for the production of cold-rolled profiles from metal, preferably steel, strip - Google Patents
Process for the production of cold-rolled profiles from metal, preferably steel, stripInfo
- Publication number
- DE1558016C3 DE1558016C3 DE19661558016 DE1558016A DE1558016C3 DE 1558016 C3 DE1558016 C3 DE 1558016C3 DE 19661558016 DE19661558016 DE 19661558016 DE 1558016 A DE1558016 A DE 1558016A DE 1558016 C3 DE1558016 C3 DE 1558016C3
- Authority
- DE
- Germany
- Prior art keywords
- cold
- strip
- production
- metal
- preferably steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
i 5b8 016i 5b8 016
Bei der Herstellung von kaltgewalzten Profilen aus Metall-, vorzugsweise Stahlband entsteht zwangläufig in den unmittelbaren Verformungsbereichen, also an den abgewinkelten Stellen, eine Werkstoffverfestigung.In the production of cold-rolled profiles from metal, preferably steel strip, this inevitably arises In the immediate deformation areas, i.e. at the angled points, material hardening.
Bekannterweise wurde bereits vorgeschlagen, die bei der Formgebung eines Profils keinen nennenswerten Formänderungen unterliegenden Teile durch eine oder mehrere Walzvorgänge, beispielsweise durch Balligformen in einer Arbeitsstufe und anschließendem Wiederglattwalzen in einer nachfolgenden Arbeitsstufe zusätzlich kaltzuverfestigen. Diesem Verfahren haftet jedoch der Nachteil an, daß auf der Oberseite der so behandelten Profilteile die Spuren des besagten Walzens kenntlich bleiben.As is well known, it has already been proposed that when shaping a profile, no significant Parts subject to changes in shape due to one or more rolling processes, for example by crowning in one work step and subsequent smooth rolling in a subsequent one Work stage additionally work hardened. However, this method has the disadvantage that the traces of said rolling remain recognizable on the upper side of the profile parts treated in this way.
Um dies zu vermeiden, wird erfindungsgemäß ein neuer Weg beschatten. Hierbei wurde erkannt, daß auf eine Kaltverfestigung der beim Profilieren keiner nennenswerten Kaltverfestigung unterliegenden Teile verzichtet werden kann, wenn durch »In-die-Kanten-Stauchen« von Bandmaterial während des Profiliereiis eine gezielte Kaltverfestigung an den Kanten vorgenommen wird.In order to avoid this, a new way is shadowed according to the invention. It was recognized that on strain hardening of the parts that are not subject to any significant strain hardening during profiling can be dispensed with if the strip material is "compressed into the edges" during profiling targeted work hardening is carried out on the edges.
Es läßt sich nach diesem Verfahren der Grad der Kaltverfestigung durch die Menge des zugegebenen Bandmaterials zum Zwecke des »In-die-Kanten-Stauchens« wunschgemäß in seiner Größe leicht festlegen. Hierbei ist es beispielsweise ohne weiteres möglich, das »Mehr« an Bandmaterial ,derart zu bemessen, daß praktisch scharfkantige ; Ecken entstehen. Die bei Durchführung des Verfahrens erzielbare Erhöhung des Gesamtwiderstandsmoments wirkt sich in jeder Weise vorteilhaft aus.According to this method, the degree of strain hardening can easily be determined in terms of its size as required by the amount of tape material added for the purpose of "upsetting into the edges". Here it is, for example, easily possible to measure the "excess" of tape material in such a way that practically sharp-edged ; Corners arise. The increase in the total drag torque that can be achieved when the method is carried out has an advantageous effect in every way.
Nach dem besagten Verfahren hergestellte Profile, ίο beispielsweise C-Profile, eignen sich, insbesondere dann, wenn sie in dem nicht kaltverfestigten Bereich mit Ausstanzungen oder Löchern versehen sind, als Armierungsträger für Stahlbetonbauten, wobei der Vorteil in der günstigen statischen Wirkung liegt.Profiles produced by the aforementioned method, for example C-profiles, are particularly suitable then, if they are provided with punchings or holes in the non-work-hardened area, as Reinforcement beams for reinforced concrete structures, the advantage of which is the favorable static effect.
Claims (1)