DE1522526A1 - Process for the production of a liquid pair suitable for printing purposes - Google Patents

Process for the production of a liquid pair suitable for printing purposes

Info

Publication number
DE1522526A1
DE1522526A1 DE19661522526 DE1522526A DE1522526A1 DE 1522526 A1 DE1522526 A1 DE 1522526A1 DE 19661522526 DE19661522526 DE 19661522526 DE 1522526 A DE1522526 A DE 1522526A DE 1522526 A1 DE1522526 A1 DE 1522526A1
Authority
DE
Germany
Prior art keywords
resin
polymerizable compound
liquid
lighting
polymerization catalyst
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19661522526
Other languages
German (de)
Inventor
Lodewikjk Jansen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gebr Stork and Companies Apparatenfabriek NV
Original Assignee
Gebr Stork and Companies Apparatenfabriek NV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Gebr Stork and Companies Apparatenfabriek NV filed Critical Gebr Stork and Companies Apparatenfabriek NV
Publication of DE1522526A1 publication Critical patent/DE1522526A1/en
Pending legal-status Critical Current

Description

Verfahren zur Herstellung eines für drucktechnische Zwecke geeigneten flussigen Präparats.Process for the production of a suitable for printing purposes liquid preparation.

Die Erfindung bezieht sich auf ein Verfahren zur Herstellung eines für drucktechnische Zwecke geeigneten flussigen Präparats, das sich insbesondere für die Herstellung von Schablonen für Siebdruck eignet und mindestens eine durch Beleuchtung polymerisierbare Verbindung enthalt, gegebenenfalls bei Anwendung eines geeigneten Beschleunigers.The invention relates to a method of making a liquid preparation suitable for printing purposes, in particular suitable for the production of stencils for screen printing and at least one through Contains lighting polymerizable compound, optionally when using one suitable accelerator.

Ein derartiges aus einer wasserigen émulsion bestehendes Präparat, dessen Lichtempfindlichkeit durch EinzuSügung eines in Wasser löslichen Bichromats beschleunigt wird, ist allgemein bekannt. Als wasserige Emulsion verwendet man oft wasserige Polyvinylalkohollosungen. deren Feststoffgehalt mindestens 10 bis 2% betragt, Ausseptlem Nachteil einer mangelhaften Haftung an der Oberflache) die gegebenenfalls durch Aetzen des beim Siebdruck verwendeten Siebprodukts verbessert werden kann tritt noch das Problem auf, dass durch den niederen Feststoffgehalt nach Verdampfen des Wassers die aufgetragene Schicht von z. B.Such a preparation consisting of a watery emulsion, its sensitivity to light by adding a water-soluble bichromate is accelerated is well known. It is often used as an aqueous emulsion aqueous polyvinyl alcohol solutions. whose solids content is at least 10 to 2%, Except for the disadvantage of inadequate adhesion to the surface) can be improved by etching the screen product used in screen printing The problem still arises that due to the low solids content after evaporation of the water the applied layer of z. B.

0. 05 mm schliesslich nur einen Film von 0, 005 bis 0. 01 mm ergibt. In den Durchlocherungen des Schablonenmaterials bleiben demzufolge schliesslich sehr dünne Membranen von z. B. 0. 01 bis 0. 25 mm übrig. Ausserdem treten beim Eintrocknen der polymerisierbaren Verbindung sehr hohe Zugspannungen in der Durchlöcherung gebildeten Schicht auf, wodurch beim Vorhandensein sehr kleiner Luftblasen in der aufgetragenen Emulsion das Auftreten sehr kleiner Locher nach Trocknen bezw. Backen der Deckschicht nicht zu vermeiden ist.0.05 mm ultimately only results in a film of 0.005 to 0.01 mm. As a result, they ultimately remain in the perforations in the template material very thin membranes of e.g. B. 0. 01 to 0.25 mm left. Also occur when drying up the polymerizable compound formed very high tensile stresses in the perforation Layer on, eliminating the presence of very small air bubbles in the applied Emulsion, the appearance of very small holes after drying BEZW. Baking the top layer cannot be avoided.

Man hat zwar versucht) diesen Nachteil dadurch zu beseitigen, dass die wasserige Emulsion in mehreren Schichten übereinander vorgesehen wird, was in der Tat wohl eine gewisse Verbesserung, aber andererseits keine hinreichende Behebung der itsängel bedeutet, da wahrend der Beleuchtung ungenügend Licht in der ersten aufgetragenen Schicht erhalten wird, wodurch diese Schicht nicht hinreichend fixiert wird und demzufolge bei dem weiteren Entwicklungsvorgang, welcher das Weichen bezw. Spülen mit Wasser umfasst, die ungenügend beleuchteten Teile herausgespult werden.Attempts have been made to eliminate this disadvantage by the aqueous emulsion is provided in several layers on top of one another, which is shown in in fact a certain improvement, but on the other hand not a sufficient remedy The fault means that there is insufficient light in the first during the lighting applied Layer is obtained, whereby this layer is not is sufficiently fixed and consequently in the further development process, which the switch resp. Rinsing with water includes spooling out the insufficiently lit parts will.

Auch hat man schon vorgeschlagen, Um die mechanischen und chemischen Eigenschaften der Deckschicht und eine Erhöhung des Feststoffgehalts durch Zusatz von teilweise polymerisierten Produkten z. B. Phenolformaldehydharzen zu erreichen, die nach der Beleuchtung, Entwicklung und Trocknung durch einen Erwarmungsprozess gehartet werden. Diese sogenannten Vorpolymere sind jedoch nicht lange haltbar, sodass die Emulsion innerhalb einem gewissen Zeitabschnitt verbraucht werden soll. Ein anderer Nachteil besteht darin, dass die Polymerisation dieser Vorpolymere nach Hinzufügung der erforderlichen Bichromatmenge sehr beschleunigt wird, sodass es-notwendig ist die mit einer lichtempfindlichen Emulsionschicht versehenen Schablonen möglichst rasc1l und bei einer möglichst niederen Temperatur zu trocknen und zu beleuchten. Demzufolge ist die Anwendung von eines BeleuchtungsgerAtsmit einem guten Beluftungssystem erforderlich em damitYDetailverlust des aufzutragenden Husters wegen unerwünschter Polymerisation der Vorpolymere in den nicht beleuchteten Teilen vermieden wird. Durch die erregte Polymerisation wird der obige Prozess noch beschleunigt.It has also been suggested to get the mechanical and chemical Properties of the top layer and an increase in the solids content through addition of partially polymerized products e.g. B. to achieve phenol-formaldehyde resins, those after lighting, developing and drying through a heating process to be hardened. However, these so-called prepolymers do not last long, so that the emulsion should be used up within a certain period of time. Another disadvantage is that the polymerization of these prepolymers after Addition of the required amount of bichromate is very accelerated, making it necessary the stencils provided with a light-sensitive emulsion layer are ideal Rasc1l and to dry and illuminate at the lowest possible temperature. Hence the use of a lighting fixture with a good ventilation system required em thereby loss of detail of the cough to be applied due to undesired Polymerization of the prepolymers in the unlit parts is avoided. The above process is accelerated by the excited polymerization.

Ausserdem hat es sich herausgestellt, dass die in dieser Weise hergestellten Schablonen bei Anwendung neuzeitlicher Druckpappen mit chemisch aktiven Komponenten, wie Hydroxyde, Carbonates Sauren und Phenole) rasch angegriffen werden, wodurch man nur geringe Langen bedrucken kann. Dies ist von besonderer Bedeutung da man zur Zeit über sogenannte rotierende Filmdruckmaschinen verfugt, wobei z. B. aus dunner Nickelfolie hergestellte, fein durchlöcherte-Hohlzylinder Anwendung finden, mit denen Ait einer sehr hohen Geschwindigkeit von 30 bis 50 m je Minute Textil bedrucken kannt Bedeutende Beschädigungen der Deckschicht können von auf den Geweben vorhandenen und vorspringenden Faserteilchen verursacht werden.It has also been found that those manufactured in this way Stencils when using modern printing cardboard with chemically active components, such as hydroxides, carbonates, acids and phenols) are quickly attacked, causing you can only print short lengths. This is of particular importance as one currently has so-called rotating film printing machines, with z. B. off Finely perforated hollow cylinders made of thin nickel foil are used, with which ait a very high speed of 30 to 50 m per minute textile can print Significant damage to the top layer can occur on the fabric existing and protruding fiber particles are caused.

Der Erfindung liegt die Augabe zugrunde diese nachteile zu beseitigen und sie gründet sich auf das Erkenntnis dass in die lichtempfindliche, haltbare Emulsion eine bestimmte) unter dem Einfluss eines Harzpolymerisationskatalysators aushartende Harzkomponente aufgenommen werden soll, welcher Polymerisationskatalysator erst spater nach der Beleuchtung und Entwicklung an die Harzkomponente hinzugefugt wird.The invention is based on the task of eliminating these disadvantages and it is based on the knowledge that in the light-sensitive, durable Emulsion a certain) under the influence of a resin polymerization catalyst hardening resin component is to be included, which polymerization catalyst added to the resin component only later after lighting and development will.

Erfindungsgemass ist das neue Verfafiren dadurch gekennzeichnet, u dass in das Preparat eine Harzkomponente aufgenommen wird, die ohne Harzpolymerisationskatalysator nicht chemisch auf die polymerisierbare Verbindung reagiert, wahrend nach der Beleuchtung und Trocknung das erhaltene Skelett der polymerisierbaren em Verbindung genügend durchlässig ist) um ein/flüssigew oder in ein flussiges Mittel eingeführter Harzpolymerisationskatalysator auf die Harzkomponente reagieren zu lassen. Vorzugsweise findet als Harzkomponente ein Epoxyd-und/oder Polyesterharz Anwendung, da diese Harze bei Aushärtung ausserordentlich harte Schichten ergeben, wahrend die Haftung an verschiedenen Materialien und die chemische Beständigkeit im allgemeinen sehr gut ist. Anstelle der erwähnten Harzarten kann man selbstver- standlich auchKdíe obigen Anforderungen erfüllenden Harze verwenden.According to the invention, the new method is characterized in that a resin component is included in the preparation which does not react chemically to the polymerizable compound without a resin polymerization catalyst, while the resulting skeleton of the polymerizable compound is sufficiently permeable after lighting and drying or reacting resin polymerization catalyst introduced in a liquid agent to the resin component. An epoxy and / or polyester resin is preferably used as the resin component, since these resins produce extremely hard layers when cured, while the adhesion to various materials and the chemical resistance are generally very good. Instead of the types of resin mentioned, you can You can also use Kdíe resins that meet the above requirements.

Indem diese Harzkomponente ohne Katalysator in eine Emulsion einer durch Beleuchtung polymerisierbaren Verbindung aufgenommen wird) kann man, falls die Harzkomponente flussig ist, den Feststoffgehalt der aufzutragenden Emulsionschicht nötigenfalls auf einem Wert von 50% hinauftreiben, wodurch die Starie des auf und in den Durchlöcherungen der Schablone erhaltenen Filmes sehr vergrossert wird. Ausserdem ist nach der Beleuchtung und Entfernung der nicht beleuchteten Teile der polymerisierbaren Verbindung die Harzkomponente noch flussig in ein Skelett der polymerisierbaren Verbindung, meistens in Form von Polyvinylalkohol, eingebettet, wodurch der vorhandene Film besonders plastisch ist und bei Temperatursteigerung durch kapillare Wirkung in die Durchlöcherungen hineingezogen wird) was wieder eine verbesserte Auffüllung der Durchlöcherungen an den erwünschten Stellen herbeiführt, wodurch die Gefahr der Bildung von Lochern und Rissen in der Deckschicht auf ein Mindestmass beschrankt ist.By converting this resin component into an emulsion without a catalyst polymerizable compound is added by lighting) one can, if the resin component is liquid, the solids content of the emulsion layer to be applied if necessary drift up to a value of 50%, whereby the starie of the and The film obtained in the perforations of the stencil is greatly enlarged. Besides that is polymerizable after lighting and removal of the non-illuminated parts Connection of the resin component still liquid in a skeleton of the polymerizable Compound, most often in the form of polyvinyl alcohol, embedded, eliminating the existing Film is particularly plastic and when the temperature rises due to capillary action is drawn into the perforations) which again improves filling which creates perforations at the desired locations, thereby reducing the risk of education of holes and cracks in the top layer to a minimum is restricted.

Vorzugsweise findet als eine durch Beleuchtung polymerisierbare Verbindung ein Polyvinylalkohol Anwend. der-durch teilweise Hydrolyse eines eine genügend grosse Kettenlange aufweisenden Polyvinylazetats erhalten wird, wodurch dieser Stoff sowohl für Lichtempfanger als auch für Emulgatoren geegient ist.Preferably found as a compound polymerizable by illumination a polyvinyl alcohol application. der-by partial hydrolysis of a sufficiently large one Chain-length polyvinyl acetate is obtained, which makes this substance both is suitable for light receivers as well as for emulsifiers.

An Stelle eines Stoffes) der eine kombinierte Wirkung aufweist und als Emulgator und durch Beleuchtung polymerisierbare Verbindung dienen kann, kann man nach einer bestimmten Ausfuhrungsweise der Erfindug einen Emulgator hinzufügen) der wenigstens nicht chemisch auf die Harzkomponente reagiert es sei den7 dass ein Harzpolymerisationskatalysator hinzugefugt wird.Instead of a substance) that has a combined effect and can serve as an emulsifier and polymerizable compound by lighting, can you add an emulsifier according to a certain embodiment of the invention) who at least does not react chemically to the resin component Resin polymerization catalyst is added.

Die Erfindung umfasst auch ein Verfahren zur Herstellung einer Schablone, wie bei für Siebdruck geeignetem Masterial, durch Beleuchtung eines Präparats in dem sich eine unter dem Einfluss von Beleuchtung polymerisierbare Verbindung in einem flussigen Medium befindet, welcher Verbindung auf ilunsch ein geeigneter Beschleuniger hinzugefugt werden kann, welches Verfahren sich erfindungsgemass dadurch auszeichnetp dass man ein Praparat, wie bei Anwendung des erfindungsgemassen Verfahrens erhalten, nach Mischen mit einem Beschleuniger, wie Bichromstt, auf das Siebmaterial auftragt und nach Beleuchtung und Entfernung der nicht umgewandelten polymerisierbaren Verbindung mit einem Harzpolymerisationskatalysator in flüssigem Sustand, oder in einem flüssigen Medium, behandelt, wonach durch Erhöhung der Temperatur das Harz aushartet.The invention also includes a method for producing a stencil, as in the case of a masterial suitable for screen printing, by illuminating a specimen in in which a compound polymerizable under the influence of lighting a liquid medium, which compound, if desired, a suitable accelerator can be added, which method is characterized according to the invention p that a preparation is obtained as when using the method according to the invention, after mixing with an accelerator such as Bichromstt, applied to the sieve material and after lighting and removing the unconverted polymerizable compound with a Resin polymerization catalyst in liquid state, or in a liquid medium, after which, by increasing the temperature, the resin hardens.

Die-abschliessende Anwendung eines Harzpolymerisationskatalysators bei der Herstellung der Schablone ist dadurch vorteilhaft, dass die in den Durchlöcherungen angebrachten Deckschichtmenge oinigormassen vergrossert wird.The final application of a resin polymerization catalyst in the production of the stencil it is advantageous that the holes in the The amount of top layer applied is increased oinigormassen.

Das der verwendeten Harzkomponente zugehörige Hartungsmittel wird vorzugsweise in einem Losungsmittel gelost, das in das Skelett der polymerisierbaren Verbindung in Form von z. B.The hardening agent associated with the resin component used is preferably dissolved in a solvent that is in the skeleton of the polymerizable Connection in the form of z. B.

Polyvinylalkohol eindringt und durch Spritzen, Untertauchen oder ein sonstiges, beliebigest Verfahren auf der Schablone angebracht wird. Die Einwirkung des Hartungsmittels oder Harzpolymerisationskatalysators ist an einer gewissen Schwellung des aufgetragenen Films spur-bar. Bei diesem Verfahren haben sich insbesondere die Harze als sehr vorteilhaft erwiesen deren Harzpolymerisationskatalysator in Wasser löslich ist.Polyvinyl alcohol penetrates and by splashing, immersion or a any other process is attached to the template. The impact of the curing agent or resin polymerization catalyst is at some swelling of the applied film. In this process, the Resins have been found to be very useful as their resin polymerization catalyst in water is soluble.

Nach Einwirkung des Harzpolymerisationskatalysators wird das Uebermass durch Abblasen mit Luft, Absaugen durch einen Ansaugekopf oder, falls das Losungsmittel genügend fluchtig ist, durch einfaches Verdampfen entfernt. Nach etwaiger Trocknung können die Schablonen einer Warmebehandlung unterzogen werden die der für das verwendete Harz erforderliche Zeit-Temperaturkombination entspricht.After exposure to the resin polymerization catalyst, the excess becomes by blowing off with air, suction through a suction head or, if the solvent is sufficiently volatile, removed by simple evaporation. After any drying the stencils can be subjected to a heat treatment similar to that used for the Resin corresponds to the required time-temperature combination.

Es hat sich herausgestellt, dass in sehr vorteilhafter Weise ein organischer Farbstoff in die Losung des Harzpolymerisationskatalysators aufgenommen werden kann, der bei der zum Einbacken des Harzes erforderlichen Temperatur zersyetzt wird. Einerseits wird dadurch der auf die Schablonen aufgetragene Film durch Färbung besser ersichtlich und kann die spätere Entfernung des Uebermasses an Harzpolvmersiationskaltastor besser überwacht werden. wahrendrdie Zersetzung des Farbstoffs in zuverlässiger Weise darstellt ob die erforderliche Temperatur vrirklich erreicht ist.It has been found that an organic dye can be included in the solution of the resin polymerization catalyst in a very advantageous manner, which is decomposed at the temperature required for baking the resin. On the one hand, this makes the film applied to the stencils more visible through coloring and the later removal of the excess of resin polarization cold can be better monitored. while the dye decomposes in a reliable manner represents whether the required temperature has actually been reached.

Die Erfindung wird nachstehend an Hand einer Anzahl von Ausfuhrungsbeispielen erläutert wobei noch mehrere vorteilhaft anzuwendende Einzelheiten hervorgehoben werden.The invention is explained below with reference to a number of exemplary embodiments explained whereby several advantageous details to be used are highlighted will.

Beispiel 1 Zur Bereitung eines für drucktechnische Zwecke geeigneten, flüssigen, Praparats wird 100 g Polyvinylalkohol in 1000 cm3, Nasser suspendiert.Example 1 For the preparation of a suitable for printing purposes, liquid, preparation, 100 g of polyvinyl alcohol is suspended in 1000 cm3 of water.

Nach völliger Lösung wird der erhaltenen émulsion 500 g Epoxydharz hinzugefü gt, wobei zwecks Erhalts einer homogenen Suspension sorgfältig gerührt wird. Die schliesslich erhaltene Suspension ist eine viskose Flüssigkeit, die bei Aufbewahrung sehr stabiel bleibt.After complete dissolution, the emulsion obtained becomes 500 g of epoxy resin added, stirring carefully to obtain a homogeneous suspension will. The suspension that is finally obtained is a viscous liquid which Storage remains very stable.

<' Als Polyvinylalkohol wird ein Proparat benutzt) das durch teilweise Hydrolyse des eine genügend hohe Viskosität aufweisenden Polyvinylazetats erhalten wird. Zur Verbesserung der Emulgierung q des Harzes im Preparat kann noch ein Emulgator z. B. in Form von 1 g Natriumsalz von Diisopropylnaphthalinsulfonsaure hinzugefugt werden. <'A proparate is used as polyvinyl alcohol) by partially Hydrolysis of the polyvinyl acetate, which has a sufficiently high viscosity obtain will. An emulsifier can also be used to improve the emulsification q of the resin in the preparation z. B. added in the form of 1 g of the sodium salt of diisopropylnaphthalenesulfonic acid will.

Sur Herstellung einer Schablone, wie bei für Siebdruck geeignetem Material in Form eines durchlöcherten Nickelzylinders, verfahrt man in folgender meise. To produce a stencil, as in the case of material suitable for screen printing in the form of a perforated nickel cylinder, proceed as follows.

500 g der obenerwähnten Emulsion wird mit 50 g einer 20 ; 0 Bichromatlosung gemischt wodurch die Emulsion lichtempfindlich gemacht wrid. Die lichtempfindliche Emulsion wird mittels einer Rakel auf der Schablone angebracht. Die neue achablone wird zwecks der Entfernung etwaiger Luftblasen einige Minuten in einer Vakuumkammer gehalten. Die Entfernung der Luftblasen ist insbesondere zu empfehlen, da dieselben zu einer erheblichen Verringerung der Festigkeit der aufgetragenen Deckschicht in den Durchlöcherungen führen kann. 500 g of the above-mentioned emulsion is mixed with 50 g of a 20; 0 dichromate solution mixed making the emulsion photosensitive. The light sensitive Emulsion is applied to the stencil using a squeegee. The new template is placed in a vacuum chamber for a few minutes to remove any air bubbles held. The removal of the air bubbles is particularly recommended because the same to a significant reduction in the strength of the applied top layer in can lead to the perforations.

Darauf wird das Ganze bei einer Temperatur von 30 bis 50° C getrocknet lveiter wird mit einer Rakel eine zweite émulsionschicht aufgetragen) die nach etwaiger Entfernung von Luftblasen wieder getrocknet wird. Danach wird die Schablone beleuchtet, wobei das Licht nurydie Teile der Schablone fillt wo die. The whole thing is then dried at a temperature of 30 to 50 ° C In addition, a second layer of emulsion is applied with a squeegee Removal of air bubbles is dried again. Then the stencil is illuminated, with the light only filling the parts of the stencil where the.

Durchlöcherungen abgeschlossen werden sollet. Darauf werden die nicht beleuchteten Teile durch Spulen mit Wasser herausgespult und wird die Schablone aufs neue getrocknet, wonach dieselbe für unbestimmte Zeit zur weiteren Abarbeitung aufbewahrt werden kann. Perforations should be completed. They won't care the illuminated parts are spooled out by spooling with water and the stencil is used dried again, after which the same for an indefinite period of time for further processing can be kept.

Dies bieste den Verteil, dass die Herstellung von Schablonen mitels der Beluechtungsmaschine jetzt ununterborchen vor sich gehen kann und dass die späteren Bearbeitungen bis auf einen spateren Zeitpunkt aufgeschoben werden können.This beasts the distribution that the production of stencils means the lighting machine now uninterrupted in front of you can go and that the later edits were postponed until a later date can be.

Nach etwaiger Retusche erfolgt die Trocknung und wird durch Untertauchen, Spritzen, oder Auftragen mittels biner Rakel eine Losung des Harzpolymerisationskatalysators, im vorliegenden Fall eine 20% Losung in Wasser, aufgestrichen. Nach Einwirkung wahrend einer Viertelstunde wird das Uebermass der Losung durch Absaugen und Abblasen entfernt, wodurch das Nasser verdunstet. Darauf wird bei ungefähr 60 C die Schablone erwärmt und getrocknet, wobei das Hartungsmittel oder der Harzpolymerisationskatalysator sich in dem noch flussigen Harz lost. Diese Erwärmung ist mit einer weiteren Auffüllung der Durchlöcherungen verknüpft, da die flussige Masse wegen der viskosen Eigenschaften dazu neigt sich darin anzuhäufen.After any retouching, drying takes place and is achieved by immersion, Spraying or applying a solution of the resin polymerization catalyst using a doctor blade, in the present case a 20% solution in water, painted on. After exposure while a quarter of an hour the excess of the solution is removed by suction and blowing off, whereby the water evaporates. The stencil is then heated to around 60 ° C and dried, wherein the curing agent or the resin polymerization catalyst dissolves in the still liquid resin. This warming is with one more replenishment of the perforations linked as the liquid mass because of the viscous properties tends to accumulate in it.

Schliesslich härtet man die erhaltene Kunststoffschicht durch Erwarmen während einer 6tune bei einer Temperatur von 120°C.Finally, the plastic layer obtained is hardened by heating during a 6tune at a temperature of 120 ° C.

Es ist angezeigt, der obenerwähnten wasserigen Losung des Harzpolymerisationskatalysators 0. 5% eines an sich bekannten Anzeigerstoffs in Form eines organischen Farbstoffs hinzuzufugen der sich bei der erwunschten Hartungstemperatur der benutzten Harzkomponente zersfetzt. Hinzufugung dieses Farbstoffs an das wasserige Gemisch des Harzpolymerisationskatalysators bietet ausserdem den Orteil dass die geschlossenen Durchlöcherungen in dem Siebzylinder gefärbt werden und also die Möglichkeit gegeben ist. in einfacher Weise festzustellen ob sich noch offene Stellen in dem Muster befinden beziehungsweise ob das Muster die erwünschte Form ausfwist.The above-mentioned aqueous solution of the resin polymerization catalyst is indicated 0.5% of an indicator substance known per se in the form of an organic dye to be added at the desired hardening temperature of the resin component used decomposed. Adding this dye to the aqueous mixture of the resin polymerization catalyst also offers the advantage that the closed perforations in the screen cylinder be colored and so the possibility is given. in a simple manner whether there are still vacancies in the pattern or whether the pattern Execute the desired shape.

Beispiel 2 Dieselben Bearbeitungen wie in Beispiel 1 werden wiederholt, jedoch wird anstelle des Epoxydharzes eine Menge von 400 g Polyesterharz hinzugefugt ; dem Polyesterharz ist die benotigte Beschleunigermenge in Form von Kobaltnaphtenat beigegeben'wahrend als Harzpolymerisationskatalysator eine Losung von Methylathylketonperoxyd in Dimethylphtalat verwendet wird.Example 2 The same operations as in Example 1 are repeated, however, an amount of 400 g polyester resin is added instead of the epoxy resin ; the polyester resin is the required amount of accelerator in the form of cobalt naphtenate added'wahrend as resin polymerization catalyst a solution of methyl ethyl ketone peroxide is used in dimethyl phthalate.

Beispiel 3 Herstellung von Photoschablonen Auf eine sehr glatte Oberflache wird ein Prtiparat, wie im Beispiel 1 beschrieben, aufgetragen, wonach bestimmte, dem erwünschten Muster entsprechende Teile beleuchtet werden. Nach Herausspulen der nicht beleuchteten Teile und Hinzufugung des Harzpolymersiations. katalysators, wie im Biespiel 1, erfolgt die Aushartung. Hierauf wird in einem elektrolytischen Bad eine Nickelachicht auf der Walze ahgeolen bracht. Schliesslich wird die gebildeter Hohlzylinder aus Nickel in bekannter Weise von der Walze abgehoben.Example 3 Production of photographic stencils on a very smooth surface a preparation, as described in Example 1, is applied, after which certain, parts corresponding to the desired pattern are illuminated. After rewinding of the unlit parts and addition of resin polymerization. catalyst, as in example 1, hardening takes place. This is followed by an electrolytic Bad brings a nickel layer on the roller ahgeolen. Eventually, the more educated Hollow cylinder made of nickel lifted off the roller in a known manner.

Auch ist es möglich, nach der Härtung die Walzenoberflache zu atzen und in dieser Weise einen Druckzylinder mit dem erwünschten Muster herzustellen. bedrucken von Papier, Textilien, Kunststoffen u. s. w. It is also possible to etch the roller surface after hardening and in this way to produce a printing cylinder with the desired pattern. printing on paper, textiles, plastics, etc.

Auf einer Breite des zu bedruckenden Materials wird ein mit o einem Farbstoff gemischtes Prparat angebracht, worauf man die erwünschten Teile beleuchtet und nach den übrigen Behandlungen der Harzpolymerisationskaralysator einwirken lasst. On a width of the material to be printed a with o a Dye-mixed preparation attached, whereupon the desired parts are illuminated and after the other treatments, leave the resin polymerization catalyst to act.

Claims (5)

Patent-Ansprüche Verfahren zur Herstellung eines für drucktechnische Zwecke geeigneten flüssigen Proparats, das sich insbesondere für die Herstellung von Schablonen fur Siebdruck eignete, und mindestens eine durch Beleuchtung polymerisierbare Verbindung enthalt, gegebenenfalls bei Anwendung eines geeigneten Beschleunigers, d a d u r c h u g e k e n n z e i c h e t, dass in das Praparat eine Harzkomponente aufgenommen wird, die wenigstens ohne Harzpolymerisationskatalysator nicht chemisch auf die polymerisierbare Verbindung reagiert, währed nach der Beleuchtung und d Trockung das erhaltene Skelett der polymerisierbaren Verbindung genügend druchlässig sit, um einen flüssigen oder in ein flussiges Mittel eingefuhrter Harzpolymerisationskatalysator auf die Harzkomponente reagieren zu lassez* Patent claims method for producing one for printing Purpose of suitable liquid Proparats, which is particularly suitable for the production of stencils suitable for screen printing, and at least one that can be polymerized by lighting Contains compound, if necessary with the use of a suitable accelerator, it is noted that there is a resin component in the preparation is added, which at least not chemically without resin polymerization reacts to the polymerizable compound while after lighting and d Drying the resulting skeleton of the polymerizable compound is sufficiently permeable sit to a liquid or introduced into a liquid agent resin polymerization catalyst to react to the resin component to lassez * 2. Verfahren nach Anspruch 1 oder 2, d a d u r c h g e k e n nz eichne t, dass als Harzkomponente ein Epoxydharz und/oder Polyesterharz Anwendung findet.2. The method according to claim 1 or 2, d u r c h e k e n n nz e ts that the resin component is an epoxy resin and / or Polyester resin is used. 3. Verfahren nach Anspruch 1 oder 2, d a d u r c h g e k e n nz e i c h n e t, dass als eine durch-Beleuchtung polymerisierbare Verbindung ein Polyvinylalkohol Anwendung findet) der durch teilweise Hydrolyse eines eine genügend grosse Kettenlange aufweisenden Polyvinylazetats erhalten wird.3. The method according to claim 1 or 2, d a d u r c h g e k e n nz e i n e t that as a through-lighting polymerizable compound a polyvinyl alcohol Is used) which by partial hydrolysis of a sufficiently large chain length having polyvinyl acetate is obtained. 4. Verfahren nach den Ansprüchen 1 bis 3, d a d u r c h g e-'/ k e n n z e i c h n e t, dass in das flüssige Praparat ein Emulgator aufgenommen wird der wenigstens nicht chemisch auf die Harzkomponente reagiert, es sei denn dass ein Harzpolymerisationskatalysator hinzuge0gt w 1522526 4. The method according to claims 1 to 3, d a d u r c h g e - '/ k e Note that an emulsifier is included in the liquid preparation which at least does not react chemically to the resin component, unless that a resin polymerization catalyst is added 1522526 5. Verfahren zur Herstellung einer Schablone, wie bei für Siebdruck geeignetem Material, durch Beleuchtung eines Preparats in dem sich eine unter dam Einfluss von Beleuchtung polymerisierbare Verbin- dungtauf Wunsch ein geeigneter Beschleuniger hinzugefugt werden kann' d a du r c h g e k e n n z e i c h n e t, dass man ein nach dem u Verfahren nach einem oder mehreren der Anspruche erhaltenes Preparat, wie beis Answendung des erfindungsgemässen Verfahrens erhalten, nach Mischen mit einem Beschleuniger, wie Bichromate auf das Siebmaterial aufstreicht und nach Beleuchtung und Entfernung der nicht umgewandelten polymerisierbaren Verbindung mit einem Harzpolymerisationskatalysator in flussigem Zustand, oder in einem flussigen Medium, behandelt, wonach durch Erhöhung der Temperatur das Harz aushärtet.5. A method for producing a stencil, as in the case of material suitable for screen printing, by illuminating a preparation in which a compound that can be polymerized under the influence of illumination is If desired, a suitable accelerator can be added because you indicate that a preparation obtained by the method according to one or more of the claims, as obtained by using the method according to the invention, is spread onto the sieve material after mixing with an accelerator such as bichromate and after illuminating and removing the unconverted polymerizable compound, treated with a resin polymerization catalyst in a liquid state, or in a liquid medium, after which the resin is hardened by increasing the temperature. 6. Verfahren zur Herstellung von Photoschablonen, d a d ur c h g e k e n n z e i c h n e t, dass man ein nach dem Verfahren nach einem oder mehreren der Anspruche 1 bis 4 erhaltenes Verfahren nach Mischen mit einem Beschleuniger, wie Bichromat, auf die Walzenoberflache auftfägt und nach Beleuchtung und Entfernung der nicht umgewandelten polymerisierbaren Verbindung mit einem Harzpolymerisations. katalysator in flussigem Zustand, oder in einem flussigen Medium, behandelt, wonach man durch Erhöhung der Temperatur das Harz haret, und schlisessilich eine Metallschicht sich ablagernlasst.6. Process for the production of photographic stencils, d a d ur c h g e it is not indicated that one can get one according to the method according to one or more of claims 1 to 4 obtained process after mixing with an accelerator, like bichromate, on the roller surface and after lighting and removal the unconverted polymerizable compound with a resin polymerization. catalyst in the liquid state, or in a liquid medium, treated, after which the resin is hardened by increasing the temperature, and finally a metal layer deposited. 7. Verfahren zur Herstellung von Druckwalzen, d a d u r c h g e k e n n z e i c h n e t, dass aman ein anch einem oder mehrern der Ansprüche 1 bis 4 erhaltens Praprat, anch Michen mit eiem Bescheuniger, wie Bichromat, auf die Walzenoberflache aufstreicht und nach Beleuchtung und Entfernung der nicht umgewandelten polymerisierbaren Verbindung mit einem Harzpolymerisationskatalysator in fluseigem Zustand. oder in einem flüssigen Medium, behandelt und nach AuthSrtunK druch Temperatusteigeurung die nicht ageschirmten atzt, 8* Verfahren zum Bedrucken von Papier, Textilien, Kunstatoffen u. s. w. d a d u r c h g e k e n n z e i c h n e t, dass man ein nach einem oder mehreren der Ansprüche 1 bis 4, erhaltenes Präparat, nach Mischen mit einem Beschleuniger, wie Bichromat, auf das zu bedruckende Material aufstreicht und nach Beleuchtung und Entfernung der nicht umgewandelten polymerisierbaren Verbindung mit einem Harzpolymerisationskatalysator in flussigem Zustand, oder in einem flussigen Medium behandelt und schliesslich durch Temperaturerhöhung das harz Härtet.7. A method for the production of printing rollers, characterized in that aman one or more of the claims 1 to 4 obtained product, including mixing with an accelerator such as dichromate, spreads on the roller surface and after lighting and removal of the unconverted polymerizable compound with a resin polymerization catalyst in a fluffy state. or in a liquid medium, treated and according to AuthSrtunK By increasing the temperature, which is not shielded, processes for printing paper, textiles, plastics, etc. are characterized in that a preparation obtained according to one or more of claims 1 to 4 is added after mixing with an accelerator such as dichromate imprinting material and after lighting and removal of the unconverted polymerizable compound treated with a resin polymerization catalyst in the liquid state, or in a liquid medium, and finally the resin cures by increasing the temperature. 9. Verfahren nach den Anspruchen 5 bis 8, d a d u r c h g e k e n n z e i c h n e t, dass der bei der verwendeten Harzkomponente Anwendung findende Harzpolymerisationskatalysator in einem in das Skelett der polymerisierbaren Verbindung durchdricingenden Lösungsmittle gelost wird.9. The method according to claims 5 to 8, d a d u r c h g e k e n It does not indicate that the resin component used is applicable Resin polymerization catalyst in one in the skeleton of the polymerizable compound penetrating solvents is dissolved. 10. Verfahren nach Anspruch 9, d a d u r c h g e k e n nz e i c h n e t, dass bei Verwendung eines Epoxydharzes in Wasser losliche Harzpolymerisationskatalysatoren, wie Aminen, Anwendung finden.10. The method according to claim 9, d a d u r c h g e k e n nz e i c h n e t that when an epoxy resin is used, resin polymerization catalysts that are soluble in water, such as amines, find application. 11. Verfahren nach den Anspruchen 9 und 10, d a d u r c h g e k e n n z e i c h e t. dass in die Losung des Harzpolymerisations-Bt katalysators ein organischer Farbstoffa ufgeommen ist, der bei der zum Einbacken des Harzes erforderlichen Temperatur auflöste11. The method according to claims 9 and 10, dadurchgeke nnzeiche t. that in the solution of the resin polymerization Bt catalyst an organic dye is absorbed, which dissolved at the temperature required to bake the resin
DE19661522526 1965-01-28 1966-01-13 Process for the production of a liquid pair suitable for printing purposes Pending DE1522526A1 (en)