DE1471151A1 - Process for the production of a lightweight building material from slate, slate clay or the like. - Google Patents

Process for the production of a lightweight building material from slate, slate clay or the like.

Info

Publication number
DE1471151A1
DE1471151A1 DE1964F0042377 DEF0042377A DE1471151A1 DE 1471151 A1 DE1471151 A1 DE 1471151A1 DE 1964F0042377 DE1964F0042377 DE 1964F0042377 DE F0042377 A DEF0042377 A DE F0042377A DE 1471151 A1 DE1471151 A1 DE 1471151A1
Authority
DE
Germany
Prior art keywords
slate
rotary kiln
sand
clay
granules
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE1964F0042377
Other languages
German (de)
Inventor
Werner Guentheroth
Kraemer Dipl-Min Hubertus
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fellner and Ziegler GmbH
Original Assignee
Fellner and Ziegler GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fellner and Ziegler GmbH filed Critical Fellner and Ziegler GmbH
Priority to DE1964F0042377 priority Critical patent/DE1471151A1/en
Priority to AT220665A priority patent/AT250846B/en
Priority to NL6503364A priority patent/NL6503364A/xx
Priority to ES0310708A priority patent/ES310708A1/en
Priority to CH386165A priority patent/CH442123A/en
Priority to FR10011A priority patent/FR1434462A/en
Priority to GB1199865A priority patent/GB1093792A/en
Publication of DE1471151A1 publication Critical patent/DE1471151A1/en
Pending legal-status Critical Current

Description

H. SEILER, J. PFENNING . H. STEHMANNH. SEILER, J. PFENNING. H. STEHMANN

DIPLOM-INGENIEURE . DIPLOM-INGENIEURDIPLOMA IN ENGINEERS. GRADUATE ENGINEER

ι Berlin« PATENTANWÄLTE es Nürnberg 2ι Berlin «PATENTANWÄLTE es Nürnberg 2

OLDENBURGALLEE 10 ■ ' ESSENWEINSTRASSE 4-iOLDENBURGALLEE 10 ■ 'ESSENWEINSTRASSE 4-i

TELEFON: 945521/22 TELEFON: 203727TELEPHONE: 945521/22 TELEPHONE: 203727

TELEGRAMM-ADRESSE: SEILWEHRPATENT TELE G R A MM-A DR E S S E: STE H P ATETELEGRAM ADDRESS: SEILWEHRPATENT TELE G R A MM-A DR E S S E: STE H P ATE

BANKKONTO: . -■ BANKKONTEN:BANK ACCOUNT:. - ■ BANK ACCOUNTS:

BERLINER BANK A.-G., / BERLIN19 ^**" ' DEUTSCHE BANK A.G. NÜRNBERG NR. U BERLINER BANK A.-G., / BERLIN19 ^ ** "' DEUTSCHE BANK AG NUREMBERG NR. U

DEP.-KASSE A4, GIROKONTO NR. 97256 _^—"*"^' , . ν ι i VOLKSBANK FORTH/BAY., KONTO-NR. A DEP.-KASSE A4, GIRO ACCOUNT NO. 97256 _ ^ - "*" ^ ',. ν ι i VOLKSBANK FORTH / BAY., ACCOUNT NO. A.

POSTSCHECK-KONTO: BERLIN-W 5938 --—"^ V*"** V . POSTSCHECK-KONTO: NÜRNBERG i7lPOST CHECK ACCOUNT: BERLIN-W 5938 --— "^ V *" ** V. POST CHECK ACCOUNT: NUREMBERG i7l

■*""** Nürnberg, den 20.5.64 12/51■ * "" ** Nuremberg, May 20th, 64 12/51

Pa.Fellner & Ziegler G.m.b.H., Frankfurt/Main-West IjJPa.Fellner & Ziegler G.m.b.H., Frankfurt / Main-West IjJ

Kreuznacherstr. 29Kreuznacherstr. 29

Verfahren zur Herstellung eines Leichtbaustoffes aus SchieferProcess for the production of a lightweight building material from slate

ton
Schiefer/od.dergl.volume
Slate / or the like.

Die Herstellung von Leichtbaustoffen, insbesondere Schiefer, Schieferton od.dergl. durch Erhitzen des Materials auf die zur Auslösung des Blähvorganges erforderliche Temperatur und Zeit geschieht nach dem bisher bekannten Verfahren einerseits im Schwebebett und andererseits im Drehrohrofen. Als wirtschaftlichstes Verfahren hat sich für die Erzeugung eines derartigen Leichtbaustoffes das Drehofenverfahren erwiesen. Nachteilig zeigte sich hierbei jedoch, daß das dem Drehofen aufzugebende Gut bei der Erzielung der für den Blähvorgang erforderlichen Temperaturen und Zeiten im Drehrohrofe t^. zum Anbacken an den Wandungen oder zur Zusammenballung zuThe production of lightweight building materials, in particular slate, slate clay or the like. by heating the material the temperature and time required to initiate the swelling process is done according to the previously known method on the one hand in the floating bed and on the other hand in the rotary kiln. As the most economical process has been found for the production the rotary kiln process has proven such a lightweight construction material. However, it was found to be disadvantageous that the Rotary kiln goods to be given up in order to achieve the temperatures and times required for the expansion process in the rotary kiln t ^. to stick to the walls or to agglomerate

o) größeren Klumpen neigt. Zur Vermeidung dieser Nachteile ist ■^· es vorgeschlagen worden, die Drehzahl des Ofens zu erhöh.en un ^ den Ofen gleichzeitig mit Einbauten zum Anheben des Materials o) Tends to larger lumps. To avoid these disadvantages, it has been proposed to increase the speed of rotation of the furnace and to increase the furnace at the same time with internals for lifting the material

o zu. versehen. Ferner ist vorgeschlagen worden, durch Einbauo to. Mistake. It has also been suggested by incorporation

einer entsprechenden Kratz- und Kämmvorrichtung das Anbackena corresponding scraping and combing device the caking

COPY -2-COPY -2-

des Materials an den Wandungen des Ofens zu vermeiden.of the material on the walls of the furnace.

Es ist weiterhin bekannt, daß durch einen homogenen Zusatz bestimmter chemischer Mittel die Blähfähigkeit derartiger Materialien erhöht, und dadurch der Ablauf des Blähvorganges bereits bei einer relativ niedrig liegenden Temperatur ablaufen kann, bei welcher mit Anbackungen noch nicht zu rechnen ist. Dieses Verfahren ist aber nicht bei stückig aufgegebenem Gut möglich.It is also known that by a homogeneous addition certain chemical agents increase the ability of such materials to expand, and thereby the expansion of the expansion process can take place at a relatively low temperature at which caking is not yet to be expected is. However, this process is not possible with goods that are sent in pieces.

Der Erfindung liegt die Aufgabe zugrunde, den Blähvorgang in einem üblichen Drehrohrofen ohne besondere Einbauten durchzuführen, ohne daß hierbei die üblichen Drehzahlen für den Antrieb des Drehofens geändert zu werden brauchen. Trotzdem soll e3 erreicht werden, daß das zu blähende Gut nicht an der Ofenwandung anhaftet und nicht zur Klumpenbildung neigt.The invention is based on the object of the expansion process in a conventional rotary kiln without special internals perform without the need to change the usual speeds for driving the rotary kiln. Nevertheless e3 should be achieved so that the material to be expanded does not adhere to the furnace wall and does not tend to form clumps.

Zur Lösung dieser Aufgabe besteht die Erfindung in erster Linie darin, daß zur Herstellung eines Leiohtbaustoffee aus Schiefer, Schieferton od.dergl. im Drehrohrofen diesem neben dem Blähsohiefer, Schieferton od.dergl. zusätzlich Sand am Einlaufende des Ofens zugegeben wird. Dieser Lehre liegt die Überlegung zugrunde, daß .das Aufblähen des Materials in Gegenwart von Stoffen vorgenommen werden soll, deren Schmelztemperatur weit über der des zu blähenden Stoffes liegt. Die zuzusetzenden Stoffe sollten unter Berücksichtigung der herrschenden Betriebsbedingungen in chemischer Hinsicht gegenüber der sich bildenden Schmelze und dem Ofenfutter inert sein bzw. mit der Schmelze möglichst nur unter Erhöhung der Schmelztemperatur an der Oberfläche reagieren. In diesemTo solve this problem, the invention consists primarily in the fact that for the production of a loan building toffee Slate, slate clay or the like. in the rotary kiln this in addition to the expanded pine, slate clay or the like. additionally sand on The inlet end of the furnace is added. This teaching is based on the idea that the expansion of the material in the presence to be made of substances whose melting temperature is far above that of the substance to be expanded. the Substances to be added should take into account the prevailing operating conditions from a chemical point of view be inert to the melt that is being formed and the furnace lining or, if possible, only to increase the melt with the melt Melting temperature on the surface react. In this

809811/0987 "5"809811/0987 " 5 "

Sinne kann der erfindungsgemäß zuzusetzende Sand auch durch andere Stoffe mit den vorgenannten Eigenschaften ersetzt werden. The sand to be added according to the invention can also pass through other substances with the aforementioned properties are replaced.

Die sich aufblähenden Teilchen werden durch die Drehbewegung des Ofens mit dem inerten Material z.B. Sand umhüllt und dadurch ihr Zusammenbacken bzw. ihr Ankleben an dem Putter des Drehrohrofens vermieden. Die Drehbewegung des Ofens bewirkt weiterhin durch das Abrollen der Körner eine Abrundung sowie Schließung der Kornoberflächen, so daß als Endprodukt ein Material entsteht, das zwar in seinem Inneren den gewünschten porösen Aufbau besitzt, jedoch von einer festen geschlossenen Oberfläche umgeben 1st. Es wird als besonders zweckmäSlg empfohlen, den Schiefer, Schieferton od.dergl« in einer Körnung von etwa 1 bis 20 iron dem Drehrohrofen aufzugeben. Hierbei kann der gleichzeitig dem Drehrohrofen am Einlaufende zugeführte Sand in einer Körnung Anwendung finden von etwa 1 bis 2 mm. Hierbei kann der gleichzeitig dem Drehrohrofen am Einlaufende zugeführt« Sand In einer Körnung bis zu 2 mm Anwendung finden· The swelling particles are enveloped with the inert material, for example sand, as a result of the rotary movement of the furnace, thereby preventing them from sticking together or sticking to the putter of the rotary kiln. The rotation of the furnace also causes the grains to roll off and close, so that the end product is a material that has the desired porous structure inside, but is surrounded by a solid, closed surface. It is particularly advisable to add slate, slate clay or the like in a grain size of about 1 to 20 iron to the rotary kiln. The sand that is simultaneously fed to the rotary kiln at the inlet end can be used in a grain size of about 1 to 2 mm. Here, the sand that is simultaneously fed to the rotary kiln at the inlet end can be used with a grain size of up to 2 mm.

DIt Durchführung des Verfahrene gemäß der Erfindung kann aber auoh in der Welse erfolgen« daß der Blähschiefer, Blähton oder dergl· fein zerkleinert tu Granallen verarbeitet wird und diese Granalien können zusammen mit dem Sand dem Drehrohrofen zugeleitet werden. Hierbei kann man zusätzlich auch In der Welse vorgehen, daß die Granallen In ihrem feuchten Zustand noch mit dem Sand gepudert werden, so daß also der Sand auf 4er pberf lache der einzelnen Oranalien anhaftet.The method according to the invention can be carried out but also in the catfish take place «that the expanded slate, expanded clay or the like finely comminuted tu granals is processed and these granules can be fed to the rotary kiln together with the sand. You can also use the Catfish proceed that the granules in their moist state still be powdered with the sand, so that the sand adheres to the surface area of the individual oranges.

80Μ11/0Θ6780Μ11 / 0Θ67

BADORlClNAt4-BADORlClNAt 4 -

Wenn man für die Durchführung des Verfahrensals Ausgangs* gut ein gebrochenes Material des zu blähenden Stoffes verwendet, so entstehen beim Zerkleinern des Schiefers, Schieferton od.dqgl Fein- und Feinstanteile des Ausgangsstoffes. Es 1st nun sehr wirtschaftlich und für die Durchführung des Verfahrens sehr zweckdienlich, daß man die Fein- und Feinstanteile, wie sie beim Zerkleinern des Ausgangsgutes anfallen, zu Granalien verarbeitet und daß dann diese Granalien zusammen mit der Grobkörnung des Ausgangsgutes und mit dem Sandanteil dem Drehrohrofen aufgegeben werden.If you are required to carry out the procedure as exit * well used a broken material of the fabric to be inflated, so arise when crushing the slate, slate clay or the like Fine and fine fractions of the raw material. It is now very economical and very useful for carrying out the process It is expedient to convert the fine and fine fractions, as they arise when the starting material is crushed, into granules processed and that then these granules together with the coarse grain size of the starting material and the sand content Rotary kiln are abandoned.

Um die Festigkeit der Granalien zu vergrößern, kann, wie es übrigens an sich bekannt ist, auch so vorgegangen werden, daß die GAaIien vor ihrer Aufgabe in den Drehrohrofen mittels der Drehofenabgase einer Vortrocknung unterworfen werden.In order to increase the strength of the granules can, as is known per se, incidentally, also possible to proceed so, since the ß GAaIien before their task in the rotary kiln by the rotary kiln exhaust gases from a predrying subjected.

Die Wirtschaftlichkeit des Verfahrens ist besonders auch dadurch gewährleistet, daß der beigegebene inerte Stoff, also z.B. der Sand, der an dem geblähten Material nur in loser Form punktförmig anhaftet, während und nach dem KühlVorgang naoh bekannten Methoden zurückgewonnen werden kann. Dieser inerte Stoff steht damit praktisch immer wieder für die Durchführung des Verfahrene zur Verfugung. Man wird hierbei eine solche Menge an Sand oder dergl. verwenden, daß bei den Aufblähvorgang die aufzublähenden Stoffe ausreichend mit dem Sand in Berührung kommen, um jeder Gefahr eines Zusaneenbackens oder Zusammenkluepens des Blähmaterials von vornherein vorzubeugen. Diese für den Blähvorgang zweckmäßigerweise anzuwendende Menge von Sand wird hierbei im praktischen BetriebThe economic efficiency of the process is particularly guaranteed by the fact that the added inert substance, For example, the sand, which only loosely adheres to the expanded material at points, during and after the cooling process can be recovered using known methods. This inert substance is thus practically always available for carrying out the process. You become a Use such an amount of sand or the like. That the substances to be inflated sufficiently with the inflation process Sand come into contact to avoid any risk of caking or clumping of the intumescent material to prevent. This expediently for the bloating process The amount of sand to be used is here in practical operation

. BAD ORIGINAL · "5". BATHROOM ORIGINAL · " 5 "

809811/0987809811/0987

entsprechend ausprobiert.tried accordingly.

Als Ausführungsbeispiel mag erwähnt werden: 80# blähfähiger Schiefer mit einer Körnung von 3 bis 20 mm und 20$ Sand, und zwar zweckmäßigerweise als Quarzsand mit einer Körnung bis 2 mm. Nach dem Durchführen des Aufblähvorganges und nach dem Heinigen des aufgeblähten Gutes von dem Sand durch Abrollen bzw. Absieben des Sandes z.B. in einer entsprechenden Trommel ergeben sich gutgerundete aufgeblähte Körner mit einer dichten Oberfläche, die eine unter sich unterschiedliche Körnung aufweisen können. Wird mit solchen verschiedenen Körnungen ein Beton aufgebaut, so ergeben diese festen Körnungen der Zuschlagstoffe auch bei einem geringen Betongemisch eine besonders gute Festigkeit, die weit über den Rahmen der bisher für derartige Leichtbaustoffe erhaltenen Festigkeiten hinausgeht und sich deshalb vorzugsweise für Konstruktionsbeton eignet.As an exemplary embodiment, it may be mentioned: 80 # more expandable Slate with a grain size of 3 to 20 mm and $ 20 sand, and although expediently as quartz sand with a grain size of up to 2 mm. After performing the inflation process and after Keeping the inflated material from the sand by rolling or sieving the sand, e.g. in a suitable drum well-rounded puffed up grains with a dense surface, which have a different grain size can. If a concrete is built with such different grain sizes, these solid grain sizes result in the aggregate a particularly good strength even with a small concrete mix, which is far beyond the scope of the previous for such Lightweight building materials goes beyond the strengths obtained and is therefore preferably suitable for structural concrete.

AnsprücheExpectations 1/098 71/098 7

Claims (5)

-fc--fc- 1. Verfahren zur Herstellung eines Leichtbaustoffes aus Schiefer, Schieferton od.dergl. unter Verwendung eines Drehrohrofens, dadurch gekennzeichnet, daß den dem Drehrohrofen aufzugebenden Schiefer, Schieferton od.dergl. Sand hinzugefügt wird.1. Process for the production of a lightweight building material from slate, slate clay or the like. using a rotary kiln, characterized in that the slate, slate clay or the like to be given to the rotary kiln. Sand added will. 2. Verfahren nach Anspruch 1 dadurch gekennzeichnet, daß Schiefer, Schieferton od.dergl. in einer Körnung von etwa 1 - 20 mm sowie Sand in einer Körnung bis zu 2mm dem Drehrohrofen aufgegeben werden.2. The method according to claim 1, characterized in that slate, slate clay or the like. in a grain size of about 1 - 20 mm and sand with a grain size of up to 2 mm can be fed into the rotary kiln. 3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß Schiefer, Schieferton od.dergl. fein zerkleinert zu Granalien verarbeitet werden, die zusammen mit Sand dem Drehrohrofen aufgegeben werden.3. The method according to claim 1, characterized in that Slate, slate clay or the like. finely chopped into granules, which are processed together with sand in the rotary kiln to be abandoned. 4. Verfahren nach Anspruch 3, dadurch gekennzeichnet, daß die Granalien mit dem Sand gepudert dem Drehrohrofen aufgegeben werden.4. The method according to claim 3, characterized in that the Granules powdered with the sand are fed into the rotary kiln. 5. Verfahren nach Anspruch 1 bis 4, dadurch gekennzeichnet, daß die beim Zerkleinern des Schiefers, Schiefertones od.dergl. entstehenden Fein- und Peinstanteile zu Granalien verarbeitet werden und daß diese Granalien mit der Grobkörnung des Schiefers, Schiefertones od.dergl. zusammen mit dem Sandanteil dem Drehrohrofen aufgegeben werden.5. The method according to claim 1 to 4, characterized in that the od.dergl when crushing the slate, slate clay. resulting fine and fine parts are processed into granules and that these granules with the coarse grain of the slate, Slate or the like. be given to the rotary kiln together with the sand. .. 6'. Verfahren nach Anspruch 3 bis 5* dadurch gekennzeichnet, daß die Granalien vor ihrer Aufgabe In den Drehrohrofen in.. 6 '. Process according to Claims 3 to 5 *, characterized in that the granules are in -2-809811/0987 -2- 80981 1/0987 -'■- 1471161- '■ - 1471161 an sich bekannter Welse mittels der Drehofenabgase einer Vortrocknung unterworfen werden.known catfish by means of the rotary kiln exhaust gases of a pre-drying be subjected. 809811/0987809811/0987
DE1964F0042377 1964-03-21 1964-03-21 Process for the production of a lightweight building material from slate, slate clay or the like. Pending DE1471151A1 (en)