DE1469877A1 - Conductive surface material, in particular a film made of polyvinyl chloride with a content of carbon black and polyethylene glycol ester - Google Patents
Conductive surface material, in particular a film made of polyvinyl chloride with a content of carbon black and polyethylene glycol esterInfo
- Publication number
- DE1469877A1 DE1469877A1 DE19621469877 DE1469877A DE1469877A1 DE 1469877 A1 DE1469877 A1 DE 1469877A1 DE 19621469877 DE19621469877 DE 19621469877 DE 1469877 A DE1469877 A DE 1469877A DE 1469877 A1 DE1469877 A1 DE 1469877A1
- Authority
- DE
- Germany
- Prior art keywords
- carbon black
- polyvinyl chloride
- conductive surface
- polyethylene glycol
- surface material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Leitender Flächenwerkstoff. insbesondere Folie aus Polyvinylchlorid mit einem Gehalt an RuS und Polyäthylenglycolester. Conductive surface material. in particular film made of polyvinyl chloride with a content of carbon black and polyethylene glycol ester.
-----------------------------------------------Elektrisch leitende Fldchenwerkstoffe aus Kunststoff, worunter Gewebefolien, beachichtete-Gewebe, mit Gewebe oder Geflecht bzw. Gewirke armierte Folienplatten u. dgl. verstanden werden, sind in verachiedenen Ausführungsformen bekannt und fUr manche Verwendung, bei der elektrostatische Aufladung zu befürchten ist, vorgeschrieben, So hat man PolyUthylenfolien durch Zusatz verhältnismäßig großer Mengen leitender Substanzen in Pulverform, wie RuB, Metalle, Metallverbindungen, leitend machen kdnnen.----------------------------------------------- Electrically conductive Surface materials made of plastic, including fabric foils, noticeable fabrics, with Woven or braided or knitted reinforced foil sheets and the like are understood, are known in various embodiments and for some use in the Electrostatic charging is mandatory, so you have polyethylene sheeting by adding relatively large amounts of conductive substances in powder form, such as Carbon black, metals, metal compounds, can make them conductive.
Die erreichte Leitfähigkeit liegt in der Größenordnung von 10-8, ohne daß die übrigen Eigenschaften, insbesondere die Festigkeit der Polyäthylenfolie, nachteilig verändert sind.The conductivity achieved is of the order of 10-8 without that the other properties, in particular the strength of the polyethylene film, are disadvantageously changed.
In ähnlicher Weise kann man Gummi und Kunstgummi leitend machen. Auf Polyvinylchlorid jedoch lassen sich die bekannten Maßnahmen merkwErdigerweise nicht Ubertragen.Similarly, rubber and synthetic rubber can be made conductive. on However, the known measures can not be applied to polyvinyl chloride Transfer.
Bei Zumischung der genannten leitenden Substanzen in den bekannten Mengen verlieren Flächenwerkstoffe aus Polyvinylchlorid ihre mechanischen Eigenschaften, insbesondere erfahren sie die Werte der Dehnung und der Zerreißfestigkeit herabsetzende Versprödungen, auch wird die Schweißarbeit erheblich beeinträchtigt. Hochbeanspruchte Schweißnähte, die Zug-und Biegebeanspruchungen aufzunehmen haben, sind bei Flächenwerkstoffen aus Polyvinylchlorid, die die genannten leitenden Substanzen in bekannten Mengen enthalten nicht mehr heratellbar. Soweit man daher durch Zusatz leitender Substanzen versucht hat, unter Beibehaltung tragbarer mechanischer und schweißtechnischer Eigenschaften Polyvinylchlorid und inabesondere Flächenwerkstoffe aus Polyvinylchlorid leitfKhig zu machen, hat man diese leitenden Substanzen in so geringen Mengen zusetzen masen, daß eine den praktischen Anforderungen genUgende, z. B. die elektrostatische Aufladung durch Reibung verhindernde, Leitfähigkeit nicht erreicht werden konnte. Im Ubrigen ist es bekannt, auf Flächenwerkstoffe aus Polyvinylchlorid leitfähige Oberflächenschichten aufzubringen. Auch diese Maßnahme ist jedoch nachteilig, da mit dem verschlieBenden Abtragen der OberflEchenschicht hier offenbar auch die Leitfähigkeit verloren geht, so daß bei Reibungsbeanspruchungen eine dauerhafte Befreiung von einer elektrostatisohen Aufladung auf diese Weise nicht erreichbar ist.When the aforementioned conductive substances are mixed in with the known Large quantities of sheet materials made of polyvinyl chloride lose their mechanical properties, in particular, they experience the values of elongation and tensile strength which reduce them Embrittlement, the welding work is also significantly impaired. Highly stressed Weld seams, which have to absorb tensile and bending loads, are used in flat materials made of polyvinyl chloride containing the aforementioned conductive substances in known quantities no longer contain heratellbar. So much for the addition of conductive substances has tried while maintaining wearable mechanical and welding properties Polyvinyl chloride and in particular sheet materials made of conductive polyvinyl chloride to make, one had to add these conductive substances in such small quantities, that a practical requirement, z. B. the electrostatic charge by preventing friction, conductivity could not be achieved. Besides it is known to apply conductive surface layers to sheet materials made of polyvinyl chloride to raise. However, this measure is also disadvantageous, since with the closing Removal of the surface layer here obviously also the conductivity is lost, so that in the case of frictional stresses a permanent release from an electrostatic Charging is not achievable in this way.
Die Erfindung hat sich die Aufgabe gestellt, einen Flächenwerketoff, inabesondere eine Folie, aus Polyvinylchlorid, so elektisch leitend zu machen, daß der Flichenwerketoff bei hinreichender Leitfähigkeit seine mechanischen Eigenschafton und insbesondere auch seine Schweißbarkeit behält.The invention has the task of providing a surface material, in particular a film made of polyvinyl chloride, see above electrically conductive to make that the Flichenwerketoff its mechanical with sufficient conductivity Properties and in particular its weldability.
Die Erfindung betrifft einen Flächenwerkstoff, insbesondere eine Folie, aus Polyvinylchlorid mit Zueats pulverförmiger leitender Substanzen. Die Erfindung besteht darin, daß eine Grundmasee aus Weiohpolyvinylohlorid bekannter Zusammensetzung ale s beigemischte pulverförmige leitende Substanzen eine Rußkombination und auderdem PolyEthylengly¢oleater enthält.The invention relates to a sheet material, in particular a film, made of polyvinyl chloride with additives of powdery conductive substances. The invention consists in that a basic composition of white polyvinyl chloride of known composition all powdery conductive substances mixed in with a combination of carbon black and more PolyEthylengly ¢ oleater contains.
Nach einer bevorzugten Ausführungsform wird die Rußkombination in Mengen von 5 bis 6 % bezogen auf die Gesamtmasse, dem Werkstoff beigegeben, während der PolySthylengly¢olenter in Mengen von 4 bis 5 %, bezogen auf die Gesamtmasse in dem Werketoff enthalten sein aoll. Der Polyäthylenglycolester kann natürlich durch ein anders Material ersetzt werden, das die gleichen Eigenschaften hat, wie z. B. antistatische Wirkung, schwach hygroskopisch, mechanischen Anlagerungsvermdgen an das PVC-Molekül, also keine feete Verbindung, so daß die Verteilung und Brückenbildung des Rußes damit gegeben ist.According to a preferred embodiment, the carbon black combination is in Quantities of 5 to 6% based on the total mass added to the material during the PolySthylengly ¢ olenter in amounts of 4 to 5%, based on the total mass to be contained in the material. The polyethylene glycol ester can of course be replaced by a different material that has the same properties as z. B. antistatic effect, weakly hygroscopic, mechanical attachment capacity to the PVC molecule, so no fixed connection, so that the distribution and bridging of the soot is thus given.
Die RuBkombination, die bei dem erfindungsgemäßen Flächenwerkstoff verwandt wird, besteht zweckmäßigerweise aus einem Ruß mit großen tröpfchenförmigen Teilchen und einem weiteren Ruß von kleiner kugelförmiger Teilchengröße mit großer rauher, sur Coronabildung neigender Oberfläche. Die Teilchengröße der Rußpartikel eelbst liegt dabei im Rahmen des Gebräuchlichen.The soot combination that occurs in the sheet material according to the invention is used, consists expediently of a soot with large droplet-shaped Particles and another carbon black of small spherical particle size with large rough surface tending to form corona. The particle size of the soot particles eself is within the framework of the usual.
Zweckmäßigerweise verwendet man eine Rußkombination aus 80 % großen Teilchen, Teilchengröße 1200 A, und 20 % RuS mit rauher Oberfläche, Teilchengröße 260 A.It is expedient to use a carbon black combination of 80% large Particles, particle size 1200 Å, and 20% RuS with rough surface, particle size 260 A.
Die Erfindung betrifft auch ein Verfahren zur Herstellung der beschriebenen elektrlsoh leitenden Flächenwerkstoffe, wobei auf einen Träger, beispielsweise ein Gewebe oder auch nur ein grobmaschiges Gewebe, eine Weich-PVC-Paste aufgestrichen und diese durch Anwendung von Wärme geliert wird. Die Erfindung besteht in verfahrensmäßiger Hinsicht darin, zunächst der Weioh-PVC-Paste die Rußkombination und den Polyäthylenglymolester beizumischen und diese Mischung in mehreren Schichten auf den Träger aufzubringen sowie jede Schicht für sich zu gelieren. Die Gelierung erfolgt zweckmäßigerweise bei Temperaturen von etwa 190°C.The invention also relates to a method of making the ones described Elektrlsoh conductive sheet materials, being on a carrier, for example a Fabric or just a wide mesh Fabric, a soft PVC paste and this is gelled by applying heat. The invention exists From a procedural point of view, first the Weioh PVC paste is the carbon black combination and to mix in the polyethylene glycol and this mixture in several layers to apply to the carrier and to gel each layer for itself. The gelation is expediently carried out at temperatures of about 190.degree.
Die durch die Erfindung erreichten Vorteile sind vor allem darin zu sehen, daB der erfindungsgemäße leitende Fläohenwerkstoff durch und durch und nicht nur auf der Oberfläche oder in Oberflächenschichten eine überraschend hohe Leitfähigkeit besitzt. Diese beträgt nämlich weniger 10"Ohm'und ist damit um Großenordnungen besser als bei bekannten leitenden Fldchenwerkstoffen auf Polyvinylchloridbasis. Diese vorteilhafte Durch- und Durch-Leitfähigkeit bei dern erfindungsgemäßen Flächenwerkstoff wird dadurch erklärt, daß sich der Polyäthylenglycolester an das Polyvinylchloridmolekül anlagert und somit die Brückenbildung zwischen den Rußteilchen verstärkt. Darüber hinaus besitzt der erfindungsgemäße Flächenwerkstoff in mechanischer und in schweißtechnischer Hinsicht optimale Eigenschaften, so daß er allen Anforderungen genügt und durch Sohweißen verarbeitet werden kann. Versprodungen werden auch an den Schweißnähten nicht beobachtet.The advantages achieved by the invention are mainly in it see that the conductive surface material according to the invention through and through and not a surprisingly high conductivity only on the surface or in surface layers owns. This is namely less than 10 "ohms" and is therefore orders of magnitude better than with known conductive sheet materials based on polyvinyl chloride. These advantageous through and through conductivity in the planar material according to the invention is explained by the fact that the polyethylene glycol ester attaches to the polyvinyl chloride molecule accumulates and thus strengthens the formation of bridges between the soot particles. About that In addition, the planar material according to the invention has mechanical and welding properties Regarding optimal properties, so that it meets all requirements and through Sohweiß can be processed. The weld seams also become brittle not observed.
Claims (4)