DE1170099B - Organopolysiloxane-based lubricating grease - Google Patents

Organopolysiloxane-based lubricating grease

Info

Publication number
DE1170099B
DE1170099B DEG32115A DEG0032115A DE1170099B DE 1170099 B DE1170099 B DE 1170099B DE G32115 A DEG32115 A DE G32115A DE G0032115 A DEG0032115 A DE G0032115A DE 1170099 B DE1170099 B DE 1170099B
Authority
DE
Germany
Prior art keywords
organopolysiloxane
radical
hours
formula
methyl hydrogen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DEG32115A
Other languages
German (de)
Inventor
John Harold Wright
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General Electric Co
Original Assignee
General Electric Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Co filed Critical General Electric Co
Publication of DE1170099B publication Critical patent/DE1170099B/en
Pending legal-status Critical Current

Description

BUNDESREPUBLIK DEUTSCHLANDFEDERAL REPUBLIC OF GERMANY

DEUTSCHESGERMAN

PATENTAMTPATENT OFFICE

AUSLEGESCHRIFTEDITORIAL

Internat. Kl.: ClOmBoarding school Kl .: ClOm

Deutsche KL: 23 c-1/04German KL: 23 c-1/04

Nummer: 1 170 099Number: 1 170 099

Aktenzeichen: G 32115 IV c / 23 cFile number: G 32115 IV c / 23 c

Anmeldetag: 24. April 1961Filing date: April 24, 1961

Auslegetag: 14. Mai 1964Opening day: May 14, 1964

Es ist bekannt, Organopolysiloxane als Schmiermittel zu verwenden. Sie zeichnen sich besonders durch gute Wärmebeständigkeit, wasserabstoßende, isolierende und niederviskose Eigenschaften (auch bei hohen Temperaturen) aus. Ihre Konsistenz kann man bekanntlich durch Zusatz von organischen oder anorganischen Fettverdickern verändern. Weiterhin ist es bereits bekannt, ein Gemisch zweier verschiedener Siloxane unter Zusatz von Fettverdickern auf anorganischer oder organischer Basis als Schmiermittel einzusetzen.It is known to use organopolysiloxanes as lubricants to use. They are particularly characterized by good heat resistance, water-repellent, insulating and low-viscosity properties (even at high temperatures). Your consistency can is known to change by adding organic or inorganic fat thickeners. Farther it is already known to use a mixture of two different siloxanes with the addition of fat thickeners to use on an inorganic or organic basis as a lubricant.

Schmierfette auf Organopolysiloxanbasis werden häufig auch zum Schmieren von metallischen Teilen verwendet. Zwar werden durch derartige Schmierfette die metallischen Teile selbst nicht angegriffen, es hat sich jedoch herausgestellt, daß derartige Schmierfette metallische Teile nicht gegen die Korrosionseinwirkung einer oxydierenden Atmosphäre in der gewünschten Weise schützen. Dies ist besonders bei aus Kupfer, Kupferlegierungen oder Stahl bestehenden Teilen der Fall. Zur Beseitigung dieses Mangels wurden bisher diesen Schmierfetten korrosionshemmend wirkende Zusätze einverleibt. Diese Zusätze wirken sich jedoch ungünstig auf die sonstigen günstigen Eigenschaften, insbesondere die Wärmebeständigkeit, der Organopolysiloxane aus.Organopolysiloxane-based greases are also often used to lubricate metallic parts used. Although the metallic parts themselves are not attacked by such lubricating greases, However, it has been found that such lubricating greases do not protect metallic parts against the effects of corrosion protect from an oxidizing atmosphere in the desired manner. This is special This is the case with parts made of copper, copper alloys or steel. To eliminate this For lack of corrosion-inhibiting additives have been incorporated into these lubricating greases. These However, additives have an unfavorable effect on the other favorable properties, in particular the Heat resistance, made of organopolysiloxanes.

Die Erfindung macht sich daher zur Aufgabe, ein aus einem Gemisch zweier verschiedener Siloxane unter Zusatz von Fettverdickern auf organischer oder anorganischer Basis bestehendes Schmierfett zu schaffen, das die günstigen Eigenschaften der bekannten Siloxane besitzt und darüber hinaus beim Aufbringen auf metallische Oberflächen, beispielsweise aus Kupfer oder Stahl, diese vor Korrosion schützt.The object of the invention is therefore to produce a mixture of two different siloxanes existing lubricating grease with the addition of organic or inorganic-based grease thickeners to create that has the favorable properties of the well-known siloxanes and beyond when applied to metallic surfaces, for example made of copper or steel, they protect against corrosion protects.

Diese Aufgabe wird nun bei einem Schmierfett der vorstehend genannten Art erfindungsgemäß dadurch gelöst, daß ein aus folgenden Verbindungen bestehendes Siloxangemisch verwendet wird:This object is now achieved according to the invention with a lubricating grease of the type mentioned above solved by using a siloxane mixture consisting of the following compounds:

(1) ein an sich bekanntes flüssiges Organopolysiloxan der Formel(1) a known liquid organopolysiloxane the formula

in der R" gleich oder verschieden ist und einen einwertigen Halogenkohlenwasserstoffrest, einen einwertigen Kohlenwasserstoffrest oder einen Cyanalkylrest darstellt und η 2,004 bis 2,4 ist;in which R "is the same or different and represents a monovalent halohydrocarbon radical, a monovalent hydrocarbon radical or a cyanoalkyl radical and η is 2.004 to 2.4;

(2) 0,1 bis 2 Gewichtsprozent, bezogen auf (1) eines bekannten Methylwasserstoffpolysiloxans der Schmierfett auf Organopolysiloxanbasis(2) 0.1 to 2 percent by weight, based on (1) a known methyl hydrogen polysiloxane of Organopolysiloxane-based lubricating grease

Anmelder:Applicant:

General Electric Company, Schenectady, N. Y.
(V. ?l. A.)
General Electric Company, Schenectady, NY
(V? L. A.)

Vertreter:Representative:

Diplrlng. M. Licht,Diplrlng. M. light,

München 2, Sendlinger Str. 55Munich 2, Sendlinger Str. 55

und Dr. R. Schmidt, Oppenau (Renchtal),and Dr. R. Schmidt, Oppenau (Renchtal),

PatentanwältePatent attorneys

Als Erfinder benannt:Named as inventor:

John Harold Wright, Waterford, N. Y. (V. St. A.)John Harold Wright, Waterford, N.Y. (V. St. A.)

Beanspruchte Priorität:Claimed priority:

V. St. v. Amerika vom 16. Mai 1960 (29 186) —V. St. v. America of May 16, 1960 (29 186) -

Formelformula

(R)2(ROSiO(R) 2 (ROSiO

- Si — O\—Si(R)2(R')
CH3
- Si - O \ —Si (R) 2 (R ')
CH 3

in der R und R' einen Methyl- oder einen Phenylrest darstellen, wobei R und R' gleich oder verschieden sein können, R' außerdem Wasserstoff bedeuten kann und α eine ganze Zahl von 10 bis 500 ist.in which R and R 'represent a methyl or a phenyl radical, where R and R' can be identical or different, R 'can also mean hydrogen and α is an integer from 10 to 500.

Es hat sich nämlich herausgestellt, daß der Zusatz einer geringen Menge eines bekannten Methylwasserstoffpolysiloxans dem Schmierfett Korrosion und Metallteilen verhindernde Eigenschaften verleiht, ohne daß die anderen wertvollen Eigenschaften des Schmierfettes beeinträchtigt werden.It has been found that the addition of a small amount of a known methyl hydrogen polysiloxane gives the grease corrosion and metal parts preventing properties without affecting the other valuable properties of the grease may be impaired.

Methylwasserstoffpolysiloxane der obenstehenden Formel (2) sind an sich bekannt. Weiterhin sind flüssige Organopolysiloxane der obenstehenden Formel (1) bekannt Das Radikal R" in der Formel (1) kann als einwertigen Kohlenwasserstoffrest einen Alkylrest, Arylrest, Aralkylrest, Alkenylrest oder einen cycloaliphatischen Rest, als Halogenkohlenwasserstoffrest einen Halogenalkyl- oder -arylrest enthalten. Methyl hydrogen polysiloxanes of the above formula (2) are known per se. Furthermore are liquid organopolysiloxanes of the above formula (1) known The radical R "in the formula (1) can be an alkyl radical, aryl radical, aralkyl radical, alkenyl radical or as a monovalent hydrocarbon radical contain a cycloaliphatic radical, as halohydrocarbon radical a haloalkyl or -aryl radical.

409 589/411409 589/411

Bei der bevorzugten Durchführung der Erfindung sind die flüssigen Organopolysiloxane der Formel (1) solche, in denen wenigstens 50% der organischen Reste, die an das Silicium gebunden sind, Methylreste sind. Die Viskosität dieses flüssigen Organopolysiloxans ist abhängig von dessen Molekulargewicht und der Art der siliciumgebundenen, organischen Reste. Obwohl jedes flüssige Organopolysi'oxan der Formel (1) erfindungsgemäß verwendet werden kann, werden Flüssigkeiten mit einer Viskosität zwischen etwa 10 und lOOOOOcSt bei 25QC bevorzugt.In the preferred practice of the invention, the liquid organopolysiloxanes of formula (1) are those in which at least 50% of the organic radicals bonded to the silicon are methyl radicals. The viscosity of this liquid organopolysiloxane depends on its molecular weight and the type of silicon-bonded organic residues. Although any liquid Organopolysi'oxan of formula (1) can be used in the invention are preferably liquids having a viscosity between about 10 and lOOOOOcSt at 25 Q C.

Diese flüssigen Organopolysiloxane können gleiche oder verschiedene Siloxaneinheiten von unterschiedlicher Art und Zusammensetzung enthalten, z. B. Triorganosiloxan- oder Diorganosiloxaneinheiten allein oder in Verbindung mit Monoorganosiloxaneinheiten. Beispielsweise können diese Organopolysiloxane als Siloxaneinheiten, Trimethylsiloxan-, Methylphenylsiloxan-, Diphenylsiloxan-, Triphcnyl- ao siloxan-, Methyl-jö-xyanoäthylsiloxan-, Methylsiloxan-, Phenylsiloxan- oder ß-Cyanäthylsiloxaneinheiten enthalten.These liquid organopolysiloxanes can contain the same or different siloxane units of different types Type and composition included, e.g. B. triorganosiloxane or diorganosiloxane units alone or in conjunction with monoorganosiloxane units. For example, these can be organopolysiloxanes as siloxane units, trimethylsiloxane, methylphenylsiloxane, diphenylsiloxane, triphenyl ao siloxane, methyl-jö-xyanoäthylsiloxan-, Methylsiloxan-, Phenylsiloxane or ß-cyanoethylsiloxane units contain.

Erfindungsgemäß können als Fettverdicker alle diese Verdickungsmittel auf organischer oder anorganischer Basis verwendet werden. Die Beschaffenheit (Konsistenz) der erfindungsgemäßen Schmierfette hängt von der Menge und Art des verwendeten Verdickungsmittels des jeweils verwendeten flüssigen Organopolysiloxans der Formel (1) und des jeweils verwendeten Methylwasserstoffpolysiloxans (2) ab. Beispiele für geeignete Verdickungsmittel sind unter anderem die Metallsalze der Fettsäuren mit wenigstens 8 Kohlenstoffatomen, wobei das Metall der Salze aus Aluminium, Blei, Zink, Mangan, Lithium, Natrium, Kalium, Calcium, Barium, Strontium, Kupfer, Quecksilber, Wismut, Chrom, Eisen, Cobalt, Nickel bestehen kann. Die Verwendung vieler solcher Metallsalze wird in den USA.-Patentschriften 2 456 642 und 2 599 984 beschrieben. Metallsalze mit Fettsäuren einer kürzeren Kette, z. B. mit 2 bis 6 Kohlenstoffatomen, und mit Oxyfettsäuren bzw. Oxyfettsäureglyceriden, die in den USA.-Patentschriften 2 551 931 und 2 508 741 beschrieben werden, können ebenfalls als Verdickungsmittel eingesetzt werden.According to the invention, all these organic or inorganic thickeners can be used as fat thickeners Base can be used. The nature (consistency) of the lubricating greases according to the invention depends on the amount and type of thickener used and the particular liquid used Organopolysiloxane of the formula (1) and the methyl hydrogen polysiloxane (2) used in each case. Examples of suitable thickeners include the metal salts of fatty acids with at least 8 carbon atoms, whereby the metal of the salts consists of aluminum, lead, zinc, manganese, lithium, Sodium, potassium, calcium, barium, strontium, copper, mercury, bismuth, chromium, iron, cobalt, Nickel can exist. The use of many such metal salts is described in U.S. patents 2,456,642 and 2,599,984. Metal salts with fatty acids of a shorter chain, e.g. B. with 2 to 6 carbon atoms, and with oxyfatty acids or oxyfatty acid glycerides, which are described in the U.S. Patents 2,551,931 and 2,508,741 can also be used as thickeners will.

Andere besondere Metallsalze, die erfindungsgemäß als Verdickungsmittel verwendet werden können, sind Lithium-2-äthylhexoat, Lithiumoxystearat, Lithiummyristat und Lithiumcaproat. Auch Phthalocyanin ist ein geeignetes Verdickungsmittel.Other particular metal salts used as thickeners in accordance with the invention are lithium 2-ethylhexoate, lithium oxystearate, lithium myristate and lithium caproate. Even Phthalocyanine is a suitable thickening agent.

Außer den Metallsalzen kann man als Verdickungsmittel für die Schmierfette nach der Erfindung feinzerteilte, neutrale Oxyde von Metallen und Metalloiden verwenden, z. B. Siliciumdioxyd, Aluminiumdioxyd, Eisenoxyd, Titandioxyd und Zinkoxyde. Wird Siliciumdioxyd als Verdickungsmittel benutzt, dann empfiehlt sich die Anwendung in Form eines Aerogels; man kann aber auch sublimiertes oder ausgefälltes Siliciumdioxyd oder Diatomeenerde zusetzen.In addition to the metal salts, one can use as a thickener for the lubricating grease according to the invention use finely divided, neutral oxides of metals and metalloids, e.g. B. silicon dioxide, Aluminum dioxide, iron oxide, titanium dioxide and zinc oxides. Used silica as a thickener used, then the application in the form of an airgel is recommended; but one can also be sublimated or add precipitated silica or diatomaceous earth.

Außerdem können im Rahmen der Erfindung komplexe Metallseifen verwendet werden, z. B. Aluminiumbenzoatstearat nach der USA.-Patentschrift 2 599 553; Acylureate, z. B. Octadecanoylureat nach der USA.-Patentschrift 2 698 300 und Phenylendiamide, z. B. Acetylstearoyl-p-phenylendiamide nach der USA.-Patentschrift 2 709 157.In addition, complex metal soaps can be used within the scope of the invention, e.g. B. Aluminum benzoate stearate in U.S. Patent 2,599,553; Acylureates, e.g. B. Octadecanoylureate according to U.S. Patent 2,698,300 and phenylenediamides, e.g. B. Acetylstearoyl-p-phenylenediamide according to U.S. Patent 2,709,157.

Eine weitere besonders vorteilhafte Gruppe von Verdickungsmitteln besteht aus Ureaten mit aromatischen Substituenten.Another particularly advantageous group of thickeners consists of ureas with aromatic Substituents.

Obwohl, wife oben erläutert wurde, die zugesetzte Menge des Verdickungsmittels in den Fettmassen nach der Erfindung nicht entscheidend ist und in weiten Grenzen variiert werden kann (in Abhängigkeit von der gewünschten Beschaffenheit des Enderzeugnisses), hat man herausgefunden, daß die Menge gewöhnlich zwischen etwa 2 und 25 Gewichtsprozent, ausgehend von dem Gewicht des Organopolysiloxans der Formel (1), betragen soll. Entscheidender ist jedoch die verwend >te Menge des Methylwasserstoffpolysiloxans (1), das als Hemmstoff gegen die Korrosion verwendet wird. Um eine befriedigende Korrosionsfestigkeit zu erzielen, muß das Methylwasserstoffpolysiloxan etwa 0,1 bis 2 Gewichtsprozent, ausgehend vom Gewicht des flüssigen Organopolysiloxans der Formel (1), betragen. Werden weniger als 0,1 Gewichtsprozent flüssiges Methylwasserstoffpolysiloxan verwendet, dann ist die Korrosionsverhütung gegen Kupfer, Kupferlegierungen und Stahl unzureichend. Beträgt der Anteil des Methylwasserstoffpolysiloxans mehr als 2 Gewichtsprozent, z. B. 3 Gewichtsprozent, dann verursacht das Methylwasserstoffpolysiloxan selbst eine Korrosion der Kupfer-, Kupferlegierungs- oder Stahlflächen. Although, as discussed above, the amount of thickener added in the fat masses according to the invention is not critical and can be varied within wide limits (depending on of the desired quality of the end product), it has been found that the Amount usually between about 2 and 25 weight percent based on the weight of the Organopolysiloxane of the formula (1) should be. However, the amount of the used is more decisive Methyl hydrogen polysiloxane (1), which is used as an inhibitor against corrosion. To a To achieve satisfactory corrosion resistance, the methyl hydrogen polysiloxane must be about 0.1 to 2 percent by weight, based on the weight of the liquid organopolysiloxane of the formula (1). Will If less than 0.1 percent by weight of liquid methylhydrogen polysiloxane is used, then the corrosion prevention is used insufficient against copper, copper alloys and steel. If the proportion of methyl hydrogen polysiloxane is more than 2 percent by weight, z. B. 3 weight percent, then the methyl hydrogen polysiloxane itself causes corrosion the copper, copper alloy or steel surfaces.

Die Schmierfette nach der Erfindung können in herkömmlicher Weise hergestellt werden, indem man lediglich das Methylwasserstoffpolysiloxan der Formel (2), das Organopolysiloxan der Formel (1) und das Verdickungsmittel in einer der üblichen Misch- oder Mahlvorrichtungen vermischt. Besonders gute Ergebnisse wurden erzielt, wenn die Masse in einer der üblichen Färb- oder Kolloidmühlen gemischt wurde.The greases according to the invention can be prepared in a conventional manner by only the methyl hydrogen polysiloxane of the formula (2), the organopolysiloxane of the formula (1) and the thickening agent is mixed in one of the usual mixing or grinding devices. Particularly Good results have been obtained when the mass is in one of the usual dye or colloid mills was mixed.

Falls gewünscht, können weitere übliche Zusätze den Schmierfetten nach der Erfindung beigegeben werden.If desired, further conventional additives can be added to the lubricating greases according to the invention will.

In den nachfolgenden Beispielen wurde das Schmierfett durch Vermischen des flüssigen Methylwasserstoffpolysiloxans (1), des flüssigen Organopolysiloxans der Formel (2) und des Verdickungsmittels in einer Farbmühle bereitet. Die Mischung wurde solange gemahlen, bis ein gleichförmiges Erzeugnis erhalten wurde. Die Korrosionsfestigkeit jedes Schmierfettes wurde durch Auftragen eines Überzugs aus der Masse auf einen frisch gereinigten, geschmirgelten und polierten Kupferstreifen ermittelt, der nachfolgend in Wasser getaucht wurde und bei einer Temperatur von 700C so lange im Wasser verblieb, bis eine Korrosion zu beobachten war. Die Korrosion zeigte sich dadurch an, daß der Kupferstreifen, verglichen mit dem frischen Kupferstreifen, sich merklich verfärbt hatte. Wurde ein Kupferstreifen ohne jeglichen Fettüberzug in Wasser getaucht, dann verfärbte er sich nach 4 Stunden.In the examples below, the grease was prepared by mixing the liquid methyl hydrogen polysiloxane (1), the liquid organopolysiloxane of formula (2) and the thickener in a paint mill. The mixture was milled until a uniform product was obtained. The corrosion resistance of each grease was determined by applying a coating of the composition on a freshly cleaned, sanded and polished copper strip was immersed in water below and as long remained at a temperature of 70 0 C in the water, was observed to corrosion. The corrosion was indicated by the fact that the copper strip had noticeably discolored compared with the fresh copper strip. If a copper strip was immersed in water without any grease coating, it became discolored after 4 hours.

Beispiel 1example 1

Es wird ein Anzahl von Schmierfetten bereitet, indem man ein Dimethylpolysiloxan mit gestoppter Kette (durch Trimethylsiiyl) mit einer Viskosität von 30OcSt bei 25 0C als Basisflüssigkeit verwendet, die jeweils 10 Gewichtsprozent, ausgehend vom Gewicht der genannten Flüssigkeit, feinzerteiltes Siliciumdioxydaerogel als Verdickungsmittel enthält. Ein Teil dieses Schmierfettes wird ohne ZusatzA number of lubricating greases are prepared by using a dimethylpolysiloxane with a stopped chain (by trimethylsiiyl) with a viscosity of 30OcSt at 25 0 C as the base liquid, each containing 10 percent by weight, based on the weight of the liquid mentioned, of finely divided silicon dioxide aerogel as a thickener. Part of this grease is made without any additive

eines Hemmstoffes zum Vergleich zurückbehalten. Dem übrigen Teil werden unterschiedliche Anteile eines flüssigen Methylwasserstoffpolysiloxans (2) mit einer Viskosität von etwa 20 cSt bei 25 0C, das eine durch Trimethylsilyl gestoppte Kette und durchschnittlich etwa 40 Dimethylwasserstoffsiloxaneinheiten je Molekül enthält, zugesetzt. In der nachstehenden Tabelle werden die verschiedenen Schmierfette und ihre Prüfungsergebnisse (nach dem beschriebenen Prüfungsverfahren) angeführt.of an inhibitor retained for comparison. The remaining part be a liquid methylhydrogenpolysiloxane (2) having a viscosity of about 20 cSt at 25 0 C, which contains a stopped by trimethylsilyl chain and an average of about 40 Dimethylwasserstoffsiloxaneinheiten per molecule, were added different amounts. The table below lists the various greases and their test results (according to the test procedure described).

Tabelle ITable I.

Versuch
Nr.
attempt
No.
Methyl-
wasserstoff-
polysiloxan-
Zusatz in
Gewichtsprozent
Methyl-
hydrogen-
polysiloxane
Addition in
Weight percent
ErgebnisResult
11 ohne Zusatzwithout addition verfärbt nach 18 Stundendiscolored after 18 hours 22 0,050.05 verfärbt nach 24 Stundendiscolored after 24 hours 33 0,10.1 rein nach 100 Stundenpurely after 100 hours 44th 0,50.5 rein nach 100 Stundenpurely after 100 hours 55 1,01.0 rein nach 100 Stundenpurely after 100 hours 66th 2,02.0 rein nach 100 Stundenpurely after 100 hours 77th 3,03.0 verfärbt nach 48 Stundendiscolored after 48 hours 88th 5050 verfärbt nach 30 Stundendiscolored after 30 hours 99 9898 verfärbt nach 30 Stundendiscolored after 30 hours

Wie die vorstehende Tabelle I zeigt, verfärbt sich das Schmierfett ohne Methylwasserstoffpolysiloxan innerhalb von 18 Stunden. Die Masse mit einem Zusatz von 0,05 Gewichtsprozent Methylwasserstoffpolysiloxan zeigt demgegenüber keine nennenswerte Verbesserung, da sie sich nach 24 Stunden verfärbt. Im Gegensatz zu diesen Prüfungsergebnissen sind die Schmierfette nach der Erfindung, welche 0,1 und 0,5 Gewichtsprozent Methylwasserstoffpolysiloxan enthalten, noch nach 100 Stunden einwandfrei. Wurde eine größere Menge Methylwasserstoffpolysiloxan zugesetzt, dann zeigt sich ein erheblicher Rückgang der Korrosionsfestigkeit. Werden andere übliche Hemmstoffe für die Korrosion an Stelle des Methylwasserstoffpolysiloxans zugesetzt, dann sind die Ergebnisse ebenfalls unbefriedigend. Wird beispielsweise ein Nonylphenyl zugesetzt, dann verfärbt sich der Kupferstreifen innerhalb von 72 Stunden. Bei Zusatz einer der nachstehend genannten, bisher als Hemmstoff für die Korrosion verwendeten Verbindungen verfärben sich die Kupferstreifen in weniger als 50 Stunden: Äthylendiamintetraessigsäure, deren Di-, Tri- und Tetranatriumsalze, 2,6-Di-tert.-butylhydrochinon, Anthrachinon, 2-Aminoanthrachinon, 2,3-Dichlor-l,4-naphthochinon, Dichlorhydrochinon, 3,5-Dimethylphenol und Zinknaphthenat.As shown in Table I above, the grease discolored without methyl hydrogen polysiloxane within 18 hours. The mass with an addition of 0.05 percent by weight methyl hydrogen polysiloxane In contrast, shows no appreciable improvement, since it changes color after 24 hours. In contrast to these test results, the greases of the invention are which Containing 0.1 and 0.5 percent by weight methyl hydrogen polysiloxane, still flawless after 100 hours. If a larger amount of methyl hydrogen polysiloxane was added, then a significant amount was found Decrease in corrosion resistance. Will be other common inhibitors to corrosion Added instead of the methyl hydrogen polysiloxane, then the results are also unsatisfactory. For example, if a nonylphenyl is added, the copper strip changes color within 72 hours. With the addition of one of the following, previously used as a corrosion inhibitor The compounds used change the color of the copper strips in less than 50 hours: ethylenediaminetetraacetic acid, their di-, tri- and tetrasodium salts, 2,6-di-tert-butylhydroquinone, anthraquinone, 2-aminoanthraquinone, 2,3-dichloro-1,4-naphthoquinone, dichlorohydroquinone, 3,5-dimethylphenol and Zinc naphthenate.

Beispiel 2Example 2

Zu einem flüssigen Methylchlorphenylpolysiloxan der Formel (1), das durchschnittlich 2,22-Methylreste je Siliciumatom und 0,03 Chlorphenylreste (3 bis 4 Chloratome je Phenylrest) je Siliciumatom enthält und eine Viskosität von etwa 70 cSt bei 25° C aufweist, werden 15 Gewichtsprozent, bezogen auf das Polysiloxan, Lithium-2-äthylhexoat und unterschiedlichen Mengen eines Methylwasserstoffpolysiloxans der Formel (2), das durchschnittlich 1000 Methylwasserstoffsiloxaneinheiten je Molekül enthält und eine Viskosität von 1000 cSt bei 25 0C aufweist, gegeben. Die nachstehende Tabelle II gibt die Prüfergebnisse dieser Schmierfette an.15 contains by weight percent, based on the polysiloxane, lithium-2-ethylhexoate and different amounts of a methylhydrogenpolysiloxane of formula (2), the average of 1,000 methylhydrogensiloxane units per molecule and having a viscosity of 1000 cSt at 25 0 C was added. Table II below gives the test results for these greases.

Tabelle IITable II

Versuch
Nr.
attempt
No.
Methyl
wasserstoff
polysiloxan in
Gewichtsprozent
methyl
hydrogen
polysiloxane in
Weight percent
ErgebnisResult
1010 ohne Zusatzwithout addition verfärbt nach 12 Stundendiscolored after 12 hours 1111 0,050.05 verfärbt nach 18 Stundendiscolored after 18 hours 1212th 0,10.1 rein nach 100 Stundenpurely after 100 hours 1313th 1,01.0 rein nach 100 Stundenpurely after 100 hours 1414th 2,02.0 rein nach 100 Stundenpurely after 100 hours 1515th 3,03.0 verfärbt nach 24 Stundendiscolored after 24 hours

Werden die Schmierfette der Versuche 10 und 13 auf eine schmiedeeiserne Platte aufgetragen, dann zeigt sich bei der mit dem Schmierfett Nr. 10 überzogenen Platte nach 30 Stunden unter den beschriebenen Versuchsbedingungen eine Verfärbung, während die mit dem Schmierfett Nr. 13 überzogene Platte auch nach 100 Stunden noch einwandfrei ist.If the greases of tests 10 and 13 are applied to a wrought iron plate, then shows in the plate coated with the grease No. 10 after 30 hours below those described Experimental conditions discoloration while that coated with No. 13 grease Plate is still flawless even after 100 hours.

Beispiel 3Example 3

Als Basis wird ein flüssiges Methyl phenylpolysiloxan eingesetzt, das ein Mischpolymerisat aus Dimethylsiloxan- und Methylphenylsiloxaneinheiten mit durch Trimethylsilyl abgestoppter Kette darstellt, in welchem das Verhältnis von Dimethylsiloxanzu Methylphenylsiloxaneinheiten 3 : 1 und die Viskosität der Flüssigkeit 50OcSt bei 25 0C ist. Das Schmierfett wird durch ■ Vermischen dieser Flüssigkeit mit 10 Gewichtsprozent eines Ureats mit aromatischen Substituenten (4,4'-Bis-[3-p-toluylurcid]) als Verdickungsmittel und mit unterschiedlichen Prozentsätzen, ausgehend vom Gewicht der Flüssigkeit, des Methylwasserstoffpolysiloxans der Formel (2) bereitet. Die Prüfergebnisse dieser unterschiedlich zusammengesetzten Schmierfette ähneln denen der Beispiele 1 und 2. Nach 100 Stunden wird keine Verfärbung der Probestreifen beobachtet, wenn der Methylwasserstoffpolysiloxangehalt zwischen 0,1 und 2 Gewichtsprozent beträgt, während eine Verfärbung in weniger als 50 Stunden eintritt, wenn weniger oder mehr als diese Menge Methylwasserstoffpolysiloxan zugesetzt wird.A liquid methyl phenyl polysiloxane is used as the base, which is a copolymer of dimethylsiloxane and methylphenylsiloxane with abgestoppter by trimethylsilyl chain, in which the ratio of Dimethylsiloxanzu methylphenylsiloxane 3: 1, and the viscosity of the liquid 50OcSt at 25 0 C. The grease is made by ■ mixing this liquid with 10 percent by weight of a urea with aromatic substituents (4,4'-bis- [3-p-toluylurcid]) as a thickener and with different percentages, based on the weight of the liquid, of the methyl hydrogen polysiloxane of the formula ( 2) prepares. The test results of these differently composed lubricating greases are similar to those of Examples 1 and 2. After 100 hours, no discoloration of the test strips is observed if the methyl hydrogen polysiloxane content is between 0.1 and 2 percent by weight, while discoloration occurs in less than 50 hours, if less or more when this amount of methyl hydrogen polysiloxane is added.

Beispiel 4Example 4

Die Basisflüssigkeit ist ein Mischpolymerisat aus 10 Molprozent Methyl-ß-cyanoäthylsiloxaneinheiten, 80 Molprozent Dimethylsiloxaneinheiten und 10 Molprozent Diphenylsiloxaneinheiten mit durch Trimethylsilyl gestoppter Kette, die eine Viskosität von 25 cSt bei 25 0C besitzt. Bei Schmierfetten, die durch Zusatz von 25 Gewichtsprozent, ausgehend vom Gewicht der Basisflüssigkeit, Siliciumdioxyd (als Aerogel) und unterschiedlichen Mengen des Methylwasserstoffpolysiloxans von Beispiel 2 erhalten werden, werden mit den vorausgegangenen Beispielen vergleichbare Ergebnisse bei der Prüfung erzielt. Außerdem ergeben weniger als 0,1 Gewichtsprozent Methylwasserstoffpolysiloxangehalt in diesen Schmierfetten bei der Prüfung auf einem schmiede-The base liquid is a copolymer of 10 mol percent methyl-ß-cyanoethylsiloxane units, 80 mol percent dimethylsiloxane units and 10 mol percent diphenylsiloxane units with a chain stopped by trimethylsilyl and which has a viscosity of 25 cSt at 25 ° C. In the case of lubricating greases which are obtained by adding 25 percent by weight, based on the weight of the base liquid, silicon dioxide (as airgel) and different amounts of the methyl hydrogen polysiloxane from Example 2, results comparable to the previous examples are achieved in the test. In addition, less than 0.1 percent by weight methyl hydrogen polysiloxane content in these greases when tested on a forge

eisernen Streifen eine Verfärbung nach weniger als 50 Stunden. Beträgt der Zusatz von Methylwasserstoffpolysiloxan zwischen 0,1 und 2 Gewichtsprozent, ausgehend vom Gewicht der Basisflüssigkeit, dann ist auch nach Ablauf von 100 Stunden das Eisen einwandfrei.iron stripes discolour after less than 50 hours. Is the addition of methyl hydrogen polysiloxane between 0.1 and 2 percent by weight based on the weight of the base liquid, then the iron is flawless even after 100 hours.

Die vorstehenden Ausführungsbeispiele haben einige Möglichkeiten der Erfindung veranschaulicht. Darüber hinaus ist die Erfindung in weitem Rahmen anwendbar auf Schmierfette, welche mit Methylwasserstoffpolysiloxanen der Formel (2) in einer Beimischung von 0,1 bis 2 Gewichtsprozent, ausgehend vom Gewicht des Organopolysiloxans, bereitet werden. Das jeweilig verwendete flüssige Organopolysiloxan der Formel (1), das als Schmierfettbasis verwendet wird, kann von beliebiger Art sein. In gleicher Weise können alle bekannten Verdickungsmittel für die Herstellung der Schmierfette verwendet werden, wobei deren Anteil lediglich von der gewünschten Konsistenz des Enderzsugnisses abhängt.The above exemplary embodiments have illustrated some possibilities of the invention. In addition, the invention is broadly applicable to lubricating greases made with methyl hydrogen polysiloxanes of formula (2) in an admixture of 0.1 to 2 percent by weight, based on the weight of the organopolysiloxane will. The respective liquid organopolysiloxane of the formula (1) used as the grease base used can be of any type. All known thickeners can be used in the same way are used for the production of the lubricating greases, the proportion of which is only depends on the desired consistency of the final product.

Claims (3)

Patentansprüche:Patent claims: 1. Schmierfett auf Organopolysiloxanbasis, bestehend aus einem Gemisch zweier verschiedener Siloxane unter Zusatz von Fettverdickern auf anorganischer oder organischer Basis, dadurch gekennzeichnet, daß das SiI-oxangemisch aus folgenden Verbindungen besteht: 1. Organopolysiloxane-based lubricating grease, consisting of a mixture of two different types Siloxanes with the addition of fat thickeners on an inorganic or organic basis, characterized in that the SiI-oxane mixture consists of the following compounds: (1) einem an sich bekannten flüssigen Organopolysiloxan der Formel(1) a known liquid organopolysiloxane of the formula einen einwertigen Kohlenwasserstoffrest, einen einwertigen Halogenkohlenwasserstoffrest oder einen Cyanoalkylrest darstellt und «2,004 bis 2,4 ist;a monovalent hydrocarbon radical, a monovalent halohydrocarbon radical or represents a cyanoalkyl radical and is 2.004 to 2.4; (2) 0,1 bis 2 Gewichtsprozent bezogen auf (1) eines bekannten Methylwasserstoffpolysiloxans der Formel(2) 0.1 to 2 percent by weight based on (1) a known methyl hydrogen polysiloxane the formula (R)2(ROSiO(R) 2 (ROSiO Si — Of— Si(R)2(R')Si - Of - Si (R) 2 (R ') CH3 CH 3 in der R und R' einen Methyl- oder einen Phenylrest darstellen, wobei R und R' gleich oder verschieden sein können, R' außerdem Wasserstoff bedeuten kann und a eine ganze Zahl von 10 bis 500 ist.in which R and R 'represent a methyl or a phenyl radical, where R and R' can be identical or different, R 'can also mean hydrogen and a is an integer from 10 to 500. 2. Schmierfett nach Anspruch 1, dadurch gekennzeichnet, daß (1) ein flüssiges Dimethylpolysiloxan mit durch Trimethylsilyl gestoppter Kette und (2) ein Methylwasserstoffpolysiloxan mit durch Trimethylsilyl gestoppter Kette ist.2. Lubricating grease according to claim 1, characterized in that (1) a liquid dimethylpolysiloxane with chain terminated by trimethylsilyl and (2) a methyl hydrogen polysiloxane with chain stopped by trimethylsilyl. 3. Schmierfett nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß das Verdickungsmittel ein Siliciumdioxyd-Aerogel ist.3. Lubricating grease according to claim 1 or 2, characterized in that the thickener is a Silica airgel is. In Betracht gezogene Druckschriften:Considered publications: 'n SiO4-* 'n SiO 4 - * USA.-Patentschriften Nr. 2 595 890, 2 642 395, 35 2 771422, 2 913 473;
z französische Patentschrift Nr. 1 099 659;
U.S. Patent Nos. 2,595,890, 2,642,395, 35,2771422, 2,913,473;
z French patent specification No. 1,099,659;
in der R" gleich oder verschieden ist und schweizerische Patentschrift Nr. 300 602.in which R "is the same or different and Swiss Patent No. 300 602. 409 589/411 5.64 Θ Bundesdruckerei Berlin409 589/411 5.64 Θ Bundesdruckerei Berlin
DEG32115A 1960-05-16 1961-04-24 Organopolysiloxane-based lubricating grease Pending DE1170099B (en)