DE1136358B - Process for the heat treatment of metallic material in a neutral atmosphere - Google Patents
Process for the heat treatment of metallic material in a neutral atmosphereInfo
- Publication number
- DE1136358B DE1136358B DESCH25795A DESC025795A DE1136358B DE 1136358 B DE1136358 B DE 1136358B DE SCH25795 A DESCH25795 A DE SCH25795A DE SC025795 A DESC025795 A DE SC025795A DE 1136358 B DE1136358 B DE 1136358B
- Authority
- DE
- Germany
- Prior art keywords
- oxygen
- gas mixture
- furnace
- containing gas
- heat treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Verfahren zur Wärmebehandlung von metallischem Gut in einer neutralen Atmosphäre In gas- oder ölbeheizten Industrieöfen ist die Ofenatmosphäre oxydierend, wenn nicht unter Schutzgas gefahren wird. Der Sauerstoff der Atmosphäre bewirkt am Gut einen Abbrand, der mindestens etwa 1,5 bis 1,8D/o beträgt und einen ins Gewicht fallenden Verlust darstellt; darüber hinaus wirkt sich ein so weit gehender Abbrand auf die Qualität der Oberfläche des gewalzten Erzeugnisses negativ aus.Process for the heat treatment of metallic goods in a neutral Atmosphere In gas or oil-fired industrial furnaces, the furnace atmosphere is oxidizing, if not operating under protective gas. The oxygen of the atmosphere causes A burn-up on the property that is at least about 1.5 to 1.8 D / o and one in weight represents falling loss; in addition, such extensive burn-off has an effect on the quality of the surface of the rolled product.
Um diese Nachteile insbesondere bei Edelstählen zu vermeiden, erwärmt man diese in elektrisch beheizten Einsatzöfen, insbesondere Tieföfen, in einer neutralen Atmosphäre.In order to avoid these disadvantages, especially with stainless steels, heated these in electrically heated insert ovens, especially soaking ovens, in a neutral one The atmosphere.
Werden nun in diesen Öfen gegossene Stahlblöcke erwärmt, die nachher gewalzt werden sollen, dann macht sich ein Nachteil bemerkbar, der bei anders beheizten Öfen nicht auftritt: insbesondere im unteren Teil der Blöcke bilden sich beim Gießen durch Spritzer oft Schuppen an der Gutoberfläche, die beim Walzen nicht entfernt werden und zu Ausschuß führen können; auch andere Oberflächenbeschädigungen bleiben bei dieser neutralen Wärmebehandlung bestehen.Are now cast steel blocks in these furnaces heated, the after are to be rolled, then a disadvantage becomes noticeable, that of heated differently Furnaces does not occur: especially in the lower part of the blocks are formed when pouring Often flakes on the surface of the product due to splashes, which are not removed during rolling and can lead to scrap; other surface damage also remains exist in this neutral heat treatment.
Die Erfindung liegt nun in der Erkenntnis, daß eine gezielte Anreicherung der neutralen Atmosphäre von elektrisch beheizten Öfen mit Sauerstoff, zum Zwecke eines gewissen Abbrandes, nicht nur diese Oberflächenschäden beseitigen, sondern das erwärmte Gut auch griffiger für das Einführen in die Walzen gestalten würde.The invention now lies in the knowledge that a targeted enrichment the neutral atmosphere of electrically heated furnaces with oxygen, for the purpose a certain burn, not only remove this surface damage, but the heated material would also make it easier to grip for insertion into the rollers.
Unter gezielter Anreicherung kann verstanden werden der Ort der Einleitung des Sauerstoffes, deren Zeitpunkt in bezug auf die Höhe der Temperatur des Gutes, die Menge des Mediums bzw. die Dauer der Einwirkung auf die Gutoberfläche.Targeted enrichment can be understood as the place of introduction of oxygen, the time of which in relation to the level of the temperature of the goods, the amount of the medium or the duration of the action on the product surface.
Damit kann ein örtlich und in seiner Tiefe begrenzter Abbrand erzielt werden, der gerade das zu Erreichende bewirkt, also gerade die vorhandenen Schuppen abbrennt, oder auf der gesamten Oberfläche des Gutes eine ganz dünne Zunderschicht, also einen Zunderanflug, erzeugt. Dies läßt sich mit entsprechenden Regeleinrichtungen erreichen.In this way, a burn-up that is limited locally and in terms of its depth can be achieved that just causes what is to be achieved, that is, the existing scales burns off, or a very thin layer of scale on the entire surface of the goods, so a hint of tinder generated. This can be done with appropriate control devices reach.
Damit der Sauerstoff an die gewünschten Stellen gelangt, können Einführungen an unterschiedlichen Stellen des Ofens vorgesehen sein. Da sich die eingangs genannten Schuppen bei im Ofen stehendem Gut meist in dessen unterem Teil befinden, wird der Sauerstoff vorzugsweise in den unteren Teil des Ofens eingeleitet, so daß er - je nach der eingeleiteten Menge - mehr oder weniger weit nach oben wirken kann.Introductions can be used to ensure that the oxygen reaches the desired locations be provided at different points of the furnace. Since the aforementioned When the product is in the oven, the scales are mostly in the lower part of the oven Oxygen is preferably introduced into the lower part of the furnace so that he - ever depending on the amount introduced - can work more or less upwards.
Wird er nicht im untersten Teil des Ofens, sondern beispielsweise in der Höhenmitte eingeleitet, dann empfiehlt es sich besonders, ihn im verhältnismäßig kalten Zustand in den Ofen einzuleiten, damit er zum größten Teil nach unten absinkt und den Abbrand im unteren Teil des Gutes bewirkt.It will not be in the lowest part of the oven, but for example initiated in the middle of the altitude, then it is particularly advisable to use it in the proportionately to introduce the cold state into the furnace so that it sinks to the bottom for the most part and causes the burn in the lower part of the property.
Als Medium im Sinne der Erfindung eignet sich reiner Sauerstoff, aber auch Luft usw. Wird ein Gemisch verwendet, dann kann es eine bei einer höheren Temperatur, z. B. über 500' C, oxydierende Sauerstoffverbindung enthalten, insbesondere CO., und/oder Wasserdampf. Gegebenenfalls kann das Behandlungsgas praktisch ganz aus solchen oxydierenden Sauerstoffverbindungen bestehen.Pure oxygen is suitable as a medium for the purposes of the invention, but also air etc. If a mixture is used, it can be one at a higher temperature, z. B. above 500 ° C, contain oxidizing oxygen compounds, especially CO., and / or water vapor. If necessary, the treatment gas can be practically completely turned off such oxidizing oxygen compounds exist.
Durch das Einführen größerer oder kleinerer Mengen Luft od. dgl. sowie durch Regeln der Dauer der Zufuhr kann sowohl die Tiefe oder die Intensität wie die Ausdehnung des hervorgerufenen Abbrandes in vertikaler Richtung geregelt werden. Durch das Einführen einer größeren Menge Luft im Laufe von kurzer Zeit kann auf diese Weise z. B. ein Abbrand begrenzter Intensität bis zu einer verhältnismäßig großen Höhe erzielt werden, während die Zufuhr kleinerer Luftmengen über einen längeren Zeitraum einen stärkeren Abbrand an den unteren Enden der Blöcke zur Folge haben wird.By introducing larger or smaller amounts of air or the like. As well as by regulating the duration of the intake can be both the depth or the intensity like the extent of the burn-off caused can be regulated in the vertical direction. By introducing a larger amount of air in the course of a short period of time you can open this way z. B. a burn of limited intensity up to a proportionate high altitude can be achieved, while the supply of smaller amounts of air over a longer period Period of time, the lower ends of the blocks will burn more intensely will.
Claims (6)