DE112416C - - Google Patents
Info
- Publication number
- DE112416C DE112416C DENDAT112416D DE112416DC DE112416C DE 112416 C DE112416 C DE 112416C DE NDAT112416 D DENDAT112416 D DE NDAT112416D DE 112416D C DE112416D C DE 112416DC DE 112416 C DE112416 C DE 112416C
- Authority
- DE
- Germany
- Prior art keywords
- carbon
- acetylene
- compounds
- carbides
- carbonic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
KAISERLICHESIMPERIAL
PATENTAMT.PATENT OFFICE.
KLASSE 12 i. CLASS 12 i.
Die Herstellung von Kohlenstoff aus Acetylen vermittelst Oxydation des Wasserstoffes des Äcetylens ist bekannt (vergl. die Patentschrift 92801 und die englische Patentschrift 23957 vom Jahre 1897). Die hierbei angewendeten Oxydationsmittel, wie Sauerstoff der Luft oder Wasserstoffsuperoxyd, haben aber den Nachtheil, dafs ihre Einwirkung auf das Acetylen nicht geregelt werden kann und man deshalb bei ihrer Anwendung nur mangelhafte und ungleiche Resultate erhält. Aufserdem gestatten sie nur die Anwendung von freiem Acetylen, nicht aber von Carbiden. Es wurde gefunden, dafs man eine regelmäfsige theilweise Oxydation des Acetylene erzielt, wenn man als Oxydationsmittel Kohlenoxyd oder Kohlensäure anwendet. Hierbei wird nicht nur der Kohlenstoff des Acetylene abgeschieden, sondern auch der Kohlenstoff des angewendeten Oxydationsmittels, was eine Vergrößerung der Ausbeute zur Folge hat; aufserdem gestattet auch die Anwendung dieser Oxydationsmittel die Verwendung von Carbiden an Stelle des freien Acetylens.The production of carbon from acetylene by means of oxidation of the hydrogen of the acetylene is known (see patent specification 92801 and English patent specification 23957 from the year 1897). The oxidizing agents used here, such as oxygen in the air or hydrogen peroxide, but have the disadvantage that their action on the acetylene is not regulated can and therefore only inadequate and uneven results are obtained when using them. In addition, they only allow the use of free acetylene, but not carbides. It has been found that regular partial oxidation of the acetylene is obtained if carbon dioxide or carbonic acid is used as the oxidizing agent. This will not only the carbon of the acetylene is deposited, but also the carbon of the applied Oxidizing agent, which leads to an increase in the yield; also permitted also the application of these oxidizing agents the use of carbides in place of the free acetylene.
Die Zersetzung von Acetylen oder acetylenhaltigen Gemischen unter Abscheidung von Kohlenstoff findet statt, wenn man sie mit Kohlensäure, Kohlenoxyd oder diese Verbindungen enthaltenden Gasen mischt und dieses Gemisch durch erhitzte Röhren leitet, oder unter Druck der Einwirkung des elektrischen Funkens unterwirft. Unter diesen Umständen reagiren die Gase auf einander nach den GleichungenThe decomposition of acetylene or acetylene-containing mixtures with the separation of Carbon takes place when you carbonate it, carbon dioxide or these compounds containing gases mixes and this mixture passes through heated tubes, or under the pressure of the action of the electric Subordinates spark. Under these circumstances the gases react to one another according to the Equations
C2 H2 + C O = H2 O + 3 C. 2 C2 H2 + C O2 = 2 H2 O + 5 C.C 2 H 2 + CO = H 2 O + 3 C. 2 C 2 H 2 + CO 2 = 2 H 2 O + 5 C.
C2H2 + 3 C O = H2O + C O2 + 4 C. C2 H2 + CO2 = H2O + CO + 2 C. C 2 H 2 + 3 C O = H 2 O + C O 2 + 4 C. C 2 H 2 + CO 2 = H 2 O + CO + 2 C.
Anstatt Acetylen kann man auch mit Vortheil dessen Metallverbindungen, besonders die der alkalischen Erden oder andere Carbide, z. B. Aluminiumcarbid oder diese Verbindungen enthaltende Gemische, verwenden. Leitet man z. B. über Calciumcarbid bei erhöhter Temperatur Kohlenoxyd, Kohlensäure oder diese Verbindungen enthaltende Gase, so tritt Kohlenstoffabscheidung ein, und zwar hauptsächlich nach den ReactionenInstead of acetylene one can also use its metal compounds with advantage, especially those of the alkaline earths or other carbides, e.g. B. aluminum carbide or these compounds containing mixtures. If one leads z. B. via calcium carbide at elevated temperature Carbon dioxide, carbonic acid, or gases containing these compounds, then carbon deposition occurs a, and that chiefly after the reactions
CaC2+ CO = CaO + 3 C. CaC 2 + CO = CaO + 3 C.
Ca C2 + 3 C O = Ca C O3 + 4 C. Ca C 2 + 3 C O = Ca C O 3 + 4 C.
2 Ca C2 + C O2 = 2 Ca O + 5 C. 2 Ca C 2 + CO 2 = 2 Ca O + 5 C.
2 Ca C2 + 3 C O2 = 2 Ca C O3 + 5 C.2 Ca C 2 + 3 CO 2 = 2 Ca CO 3 + 5 C.
Der Kohlenstoff scheidet sich hierbei je nach der angewendeten Temperatur und der Dauer der Einwirkung in mehr oder minder feiner Vertheilung oder in krystallinischer Form ab. Als Beispiel sei angeführt die Herstellung von feinst vertheiltem Kohlenstoff aus Calciumcarbid. In einer Retorte, Röhre oder sonstigem Apparat wird fein zerkleinertes Calciumcarbid auf 200 bis 2500 erhitzt und der Einwirkung von Kohlenoxyd so lange unterworfen, bis keine Absorption mehr eintritt. Die erhaltene Reactionsmasse wird sehr fein gemahlen, mit Wasser geschlämmt und der abgeschlämmte Theil, wenn nothwendig, durch Behandlung mit geeigneten Lösungsmitteln von anhaftendem Kalk befreit.Depending on the temperature used and the duration of the action, the carbon is deposited in a more or less fine distribution or in a crystalline form. An example is the production of finely divided carbon from calcium carbide. In a retort, tube or other apparatus, finely ground calcium carbide is heated to 200 to 250 0 and subjected to the action of carbon oxide until no more absorption occurs. The reaction mass obtained is ground very finely, slurried with water, and the slurried part, if necessary, freed from adhering lime by treatment with suitable solvents.
Das so erhaltene Kohlenstoffpulver ist frei von allen theerigen Bestandtheilen und in so feiner Vertheilung, dafs es mit Vortheil zur Fabrikation bester Druckerschwärze und als Ersatz für chinesische Tusche verwendet werden kann.The carbon powder thus obtained is free from all herbal constituents and in such a way fine distribution, that it is advantageous for the manufacture of the best printing ink and as a Can be used as a substitute for Chinese ink.
Leitet man Kohlenoxyd, Kohlensäure oder diese Gase enthaltende Gemische bei hoher Temperatur oder unter Druck ein, so scheidet sich Kohlenstoff in graphitischer Form ab. Der auf diese Weise erhaltene Graphit ersetzt den natürlichen Graphit in allen seinen Verwendungsarten. If one conducts carbon dioxide, carbonic acid or mixtures containing these gases at high At temperature or under pressure, carbon is deposited in graphitic form. Of the Graphite obtained in this way replaces natural graphite in all of its uses.
Die Abscheidung des Kohlenstoffs aus Carbiden bezw. Acetylen durch Kohlensäure, Kohlenoxyd oder diese Verbindungen enthaltende Gase kann mit Vortheil dort angewendet werden, wo es darauf ankommt, fein vertheilten Kohlenstoff für chemische Zwecke anzuwenden. Hierbei werden zweckmäfsig beide Processe, nämlich der Procefs der Kohlenstoffabscheidungund Kohlenstoffbindung, vereinigt. So z. B. findet dieser Procefs bei Kohlung von Metallen vortheilhaft Anwendung.The deposition of carbon from carbides BEZW. Acetylene by carbonic acid, Carbon dioxide or gases containing these compounds can be used there with advantage where it is important to use finely divided carbon for chemical purposes. This will be expedient both processes, namely the process of carbon deposition and carbon sequestration, united. So z. B. This process finds advantageous application in the carbonization of metals.
Beim Cementiren von Eisen z. B. bringt man das zu cementirende Metall in geeigneter Weise mit den Carbiden in Berührung und leitet bei hoher Temperatur darüber Kohlenoxyd, Kohlensäure oder diese Verbindungen enthaltende Gemische mit oder ohne Zusatz von Acetylen. Bei Anwendung von Acetylen kann natürlich die Anwesenheit von Carbiden fortfallen.When cementing iron, for. B. one brings the metal to be cemented in a suitable manner in contact with the carbides and, at high temperatures, conducts carbon dioxide and carbonic acid over them or mixtures containing these compounds with or without the addition of acetylene. When using acetylene can of course the presence of carbides is omitted.
Eine andere Verwendungsart dieser Kategorie ist das sogenannte Oxydiren des Silbers. Silberne Gegenstände werden mit Carbidpulver belegt und bei 150 bis 2000 der Einwirkung von Kohlenoxyd unterworfen. Der sich hierbei abscheidende Kohlenstoff brennt sich im Silber ein und verleiht diesem das beliebte oxydische Aussehen.Another use of this category is the so-called oxidation of silver. Silver objects are coated with carbide powder and subjected to the action of carbon oxide at 150 to 200 0. The carbon that is deposited in the process burns itself into the silver and gives it the popular oxidic appearance.
Claims (1)