DE10302949A1 - Flowable polymer composition, useful in hobby and craft work, comprises a PVC or a PVC copolymer binding agent and 2,2,4-trimethyl-1,3-pentanediyl dibenzoate plasticizer - Google Patents

Flowable polymer composition, useful in hobby and craft work, comprises a PVC or a PVC copolymer binding agent and 2,2,4-trimethyl-1,3-pentanediyl dibenzoate plasticizer Download PDF

Info

Publication number
DE10302949A1
DE10302949A1 DE2003102949 DE10302949A DE10302949A1 DE 10302949 A1 DE10302949 A1 DE 10302949A1 DE 2003102949 DE2003102949 DE 2003102949 DE 10302949 A DE10302949 A DE 10302949A DE 10302949 A1 DE10302949 A1 DE 10302949A1
Authority
DE
Germany
Prior art keywords
pvc
weight
plastic mass
trimethyl
plasticizer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE2003102949
Other languages
German (de)
Other versions
DE10302949B4 (en
Inventor
Heidi Dr. Hummel
Heinrich Schnorrer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JS Staedtler GmbH and Co KG
Original Assignee
JS Staedtler GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JS Staedtler GmbH and Co KG filed Critical JS Staedtler GmbH and Co KG
Priority to DE2003102949 priority Critical patent/DE10302949B4/en
Publication of DE10302949A1 publication Critical patent/DE10302949A1/en
Application granted granted Critical
Publication of DE10302949B4 publication Critical patent/DE10302949B4/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

A flowable polymer composition (I) comprising a binding agent, plasticizer and optionally other additives is characterized in that the binding agent is PVC or a PVC copolymer and the plasticizer is a 2,2,4-trimethyl-1,3-pentanediyl dibenzoate.

Description

Die Erfindung betrifft eine fließfähige Kunststoffmasse sowie deren Verwendung im Hobby und Künstlerbereich.The invention relates to a flowable plastic mass as well as their use in the hobby and artist area.

Fließfähige Kunststoffmassen sind prinzipiell bekannt. So ist beispielsweise ein flüssiges Kunststoffmittel bekannt, das als Überzugsmittel, Malfarbe und Kleber eingesetzt wird.Flowable plastic masses are known in principle. For example, a liquid plastic agent known as a coating agent, Paint and glue is used.

Das Mittel besteht im wesentlichen aus PVC bzw. PVC-Copolymeren und Weichmachern. Bei Temperaturen um 130°C werden derartige Mittel bei einer maximalen Schichtdicke von 6 mm ausgehärtet. Als Weichmacher finden in derartigen Mitteln nach dem Stand der Technik Gemische aus Phatalsäureester Verwendung.The mean is essentially made of PVC or PVC copolymers and plasticizers. At temperatures around 130 ° C such agents are used in a maximum layer thickness of 6 mm hardened. Find as a plasticizer in such agents according to the prior art mixtures of phthalic acid esters Use.

Die so hergestellten formstabilen Überzüge und dergleichen können dann mechanisch bearbeitet werden.The dimensionally stable coatings and the like thus produced can then machined.

Nachteilig bei derartigen Mitteln ist es, dass die damit hergestellten Überzüge und Schichten eine mangelhafte Transparenz aufweisen und nach ihrer Durchhärtung eine sehr hohe Bruchempfindlichkeit an den Tag legen.A disadvantage of such means it is that the coatings and layers produced with it are defective Have transparency and after curing through a very high sensitivity to breakage lay the day.

Aufgabe der Erfindung ist es daher, eine fließfähige Kunststoffmasse für den Hobby und Künstlerbedarf zu schaffen, die die eingangs genannten Nachteile nicht aufweist und die insbesondere nach dem Härtevorgang weiterhin elastisch bzw. flexibel bleibt und so eine Bruchgefahr praktisch ausgeschlossen werden kann. Weiter ist es Aufgabe der Erfindung, dass das erfindungsgemäße Mittel nach dem Härten eine hohe Transparenz aufweist und damit ein dekoratives und hochwertiges Erscheinungsbild der damit behandelten Objekte oder hergestellten Formen oder Gegenstände sichergestellt bleibt.The object of the invention is therefore a flowable plastic mass for the Hobby and art supplies to create, which does not have the disadvantages mentioned above and especially after the hardening process remains elastic or flexible and thus a risk of breakage can be practically excluded. Another object of the invention is that the agent according to the invention after hardening has a high transparency and thus a decorative and high quality Appearance of the objects treated or manufactured with it Shapes or objects remains ensured.

Diese Aufgaben werden mit den in den Ansprüchen 1 und 6 umfassten Merkmalen gelöst.These tasks are carried out with the in the claims 1 and 6 included features solved.

Vorteilhafte Ausgestaltungen und Weiterbildungen der erfindungsgemäßen Massen sind in den weiteren Ansprüchen umfasst.Advantageous configurations and Further developments of the masses according to the invention are in the others Claims included.

Die besonderen Vorteile der erfindungsgemäßen Kunststoffmasse liegen in seiner universellen Einsetzbarkeit, wie beispielsweise als Lack bzw. Überzug, Kleber, Schreibflüssigkeit oder Gießmasse. Die gehärtete Kunststoffmasse zeichnet sich durch eine leichte mechanische Bearbeitbarkeit, wie Schmirgeln, Schaben oder Fräsen aus.The particular advantages of the plastic composition according to the invention lie in its universal applicability, such as as a varnish or coating, Glue, writing fluid or casting compound. The hardened Plastic mass is characterized by easy mechanical workability, such as sanding, scraping or milling out.

Die Konsistenz des Mittels ist bei normaler Umgebungstemperatur vor dem Härten flüssig und härtet bei offener Lagerung auch über längere Zeiträume nicht aus. Wichtig ist es, dass die Konsistenz vor dem Härten nicht gummiartig ist, d.h. dass sich bei der Verarbeitung keine langen Fäden bilden und ziehen, damit auf leichte und einfache Art und Weise eine Verarbeitung möglich ist.The consistency of the agent is at normal ambient temperature before hardening liquid and does not harden with open storage even over longer periods out. It is important that the consistency is not before hardening is rubbery, i.e. that the processing does not take long Form threads and pull, so that processing is easy and simple possible is.

Durch diese Beschaffenheit der Konsistenz ist das Mittel sogar aus Plastikflaschen mit Spitzen oder Spitzendüsen mit kleine Öffnungen verschreib- oder auftragbar, wobei in allen Fällen der Verwendung keine Blasenbildung auftritt. Weiche Plastikflaschen sind zur leichten Dosierung des Flusses von Vorteil.Because of this consistency the agent even from plastic bottles with tips or tip nozzles small openings can be prescribed or applied, with no blistering in all cases of use occurs. Soft plastic bottles are for easy dosing of the River is an advantage.

Als ein weiterer Vorteil der erfindungsgemäßen Masse kann es angesehen werden, dass sehr leicht Farbmittel eingemischt werden können.As a further advantage of the mass according to the invention it can be seen that colorants are mixed in very easily can be.

Es hat sich des weiteren als vorteilhaft herausgestellt, dass beim Härtevorgang, bei einer Temperatur von etwa 130°C keine Blasenbildung auftritt und die Masse voll transparent und glasklar bleibt.It has also proven advantageous emphasized that during the hardening process, at a temperature of about 130 ° C No blistering occurs and the mass is fully transparent and remains crystal clear.

Die Masse härtet durch Wärmeeinwirkung aus, wobei es sich dabei um einen Gelierprozess handelt, in welchem sich unter Wärmeeinwirkung der Weichmacher zwischen die Makromoleküle des Bindemittels einlagert.The mass hardens through exposure to heat, which is a gelling process in which under the influence of heat the plasticizer is embedded between the macromolecules of the binder.

Erreicht werden diese vorteilhaften Eigenschaften des Mittels durch den Einsatz eines speziellen Weichmachers. Dieser Weichmacher ist ein 2,2,4-Trimethyl-1,3-Pentanediyl Dibenzoat.These advantageous are achieved Properties of the agent through the use of a special plasticizer. This plasticizer is a 2,2,4-trimethyl-1,3-pentanediyl dibenzoate.

Der Kunststoffmasse können als Zusatz (ZS) geringe Mengen an Stabilisatoren beigefügt sein. Beispiele für mögliche Stabilisatoren sind beispielsweise Zinkethylhexanoad, Zinkcarboxylat und/oder Calciumstearat.The plastic mass can as Additive (ZS) small amounts of stabilizers can be added. Examples for possible stabilizers are, for example, zinc ethyl hexanoad, zinc carboxylate and / or calcium stearate.

Als Farbmittel (FM) können Ölfarben Verwendung finden. Unter Ölfarben versteht man definierte Anstrichfarben. Der Anteil an Ölfarbe in der Kunststoffmasse kann bis 10 Gew.-% betragen.Oil paints can be used as colorants (FM) Find use. Under oil paints one understands defined paints. The proportion of oil paint in the plastic mass can be up to 10% by weight.

Zur Einfärbung der Kunststoffmasse können auch Pigmente in reiner Form, beispielweise in Pulverform eingesetzt werden. Der Gewichtsanteil an Pigmenten in der Masse sollte 5 Gew.-% nicht überschreiten. Als eine Auswahl einer Vielzahl von möglichen Farbpigmenten seien Pigment Blue 15, Pigment Yellow 3 und Pigment White 6 genannt.You can also use it to color the plastic mass Pigments in pure form, for example in powder form become. The weight fraction of pigments in the mass should be 5% by weight. do not exceed. As a selection of a variety of possible color pigments Pigment Blue 15, Pigment Yellow 3 and Pigment White 6.

Durch die Zugabe dieser Farbmittel erhält die Kunststoffmasse ein brillantes Aussehen.By adding these colorants receives the plastic mass has a brilliant appearance.

Alternativ zu den Pigmenten können verlackte Farbstoffe eingesetzt werden. Beispiele für verlackte Farbstoffe sind Chinolingelb Lack E 104, Indigotin Lack E 132 und Ponceau 4R Lack E 124.As an alternative to the pigments, lacquered Dyes are used. Examples of lacquered dyes are Quinoline yellow lacquer E 104, indigotine lacquer E 132 and Ponceau 4R lacquer E 124.

Es ist zu beachten, dass der Gehalt an Farbmitteln vorzugsweise einen Gehalt von 10 Gew.-% an der Gesamtmischung nicht überschreiten sollte, denn in diesem Anteilsbereich wird die Konsistenz durch die Zugabe von Farbmitteln (FM) nicht bzw. nicht maßgeblich verändert.It should be noted that the salary of colorants preferably a content of 10% by weight of the total mixture do not exceed should, because the consistency is achieved in this proportion the addition of colorants (FM) not or not significantly changed.

Durch die Zugabe von feinem Metallglitter, feinem Glitzerpulver oder Glitzerplättchen kann zudem ein besonderer optischer Effekt erzielt werden.By adding fine metal glitter, fine Glitter powder or flakes a special optical effect can also be achieved.

Unterschiedlich eingefärbte Kunststoffmassen können zudem beliebig miteinander vermengt bzw. vermischt werden, wodurch Marmorierungseffekte erzielt werden. Flächen sehen aus wie emailliert und bekommen so einen hochwertiges Erscheinungsbild. Hierbei ist anzumerken, dass auch eingefärbte Massen glasklar bleiben und wirken.Different colored plastic masses can can also be mixed or mixed as desired, whereby Marbling effects can be achieved. Areas look like enamelled and get a high quality appearance. It should be noted here that also colored Masses remain crystal clear and effective.

Die Erfindung soll anhand eines Rahmenbeispiel sowie einigen Rezepturbeispielen näher dargestellt werden.The invention is based on a framework example as well as some recipe examples.

Rahmenbeispiel 1 für eine fließfähige Kunststoffmasse;Framework example 1 for a flowable plastic mass;

  • 30 – 60 Gew.- % Bindemittel (BM)30-60 % By weight of binder (BM)
  • 40 – 70 Gew.- % Weichmacher (WM)40-70 % By weight plasticizer (WM)
  • 0 – 10 Gew.- % Farbmittel (FM)0-10 % By weight of colorant (FM)
  • 0 – 5 Gew.- % sonstige Zusätze (ZS)0 - 5 % By weight of other additives (ZS)

Rezepturbeispiel 1 – farblose MasseRecipe example 1 - colorless Dimensions

  • 44 Gew.- % PVC oder PVC-Copolymerisat (BM)44% by weight of PVC or PVC copolymer (BM)
  • 56 Gew.- % Weichmacher (WM)56% by weight plasticizer (WM)

Rezepturbeispiel 2 – farblose MasseRecipe example 2 - colorless Dimensions

  • 50 Gew.- % PVC oder PVC-Copolymerisat (BM)50% by weight PVC or PVC copolymer (BM)
  • 49 Gew.- % 2,2,4-Trimethyl-l,3-Pentanediyl Dibenzoate (WM)49% by weight 2,2,4-trimethyl-l, 3-pentanediyl dibenzoate (WM)
  • 1 Gew.- % Stabilisator (ZS)1% by weight stabilizer (ZS)

Rezepturbeispiel 4 – blaue MasseRecipe example 4 - blue Dimensions

  • 44 Gew.- % PVC-Copolymer (BM)44% by weight PVC copolymer (BM)
  • 55 Gew.- % 2,2,4-Trimethyl-l,3-Pentanediyl Dibenzoate (WM)55% by weight 2,2,4-trimethyl-l, 3-pentanediyl dibenzoate (WM)
  • 1 Gew.- % Pigment Blue 15 (FM)1% by weight of Pigment Blue 15 (FM)

Rezepturbeispiel 3 – eingefärbte MasseRecipe example 3 - colored mass

  • 55 Gew.- % PVC oder PVC-Copolymerisat (BM)55% by weight PVC or PVC copolymer (BM)
  • 3 Gew.- % 2,2,4-Trimethyl-l,3-Pentanediyl Dibenzoate (WM)3% by weight 2,2,4-trimethyl-l, 3-pentanediyl dibenzoate (WM)
  • 1 Gew.- % Calciumstearat (ZS)1% by weight calcium stearate (ZS)
  • 1 Gew.- % Ölfarbe (FM)1% by weight oil paint (FM)

Die Konsistenz der Kunststoffmasse kann problemlos durch die Variation der Gehalte von Bindemittel und Weichmacher eingestellt werden.The consistency of the plastic mass can be easily achieved by varying the binder content and plasticizers can be set.

Verwendung findet die erfindungsgemäße Kunststoffmasse im Hobby- und Künstlerbereich.The plastic mass according to the invention is used in the hobby and artist area.

Speziell werden die Kunststoffmassen bei der Herstellung von Überzugsschichten, zur Veredelung oder Schutz von Oberflächen eingesetzt. Derartige Objekte können dann als Wandschmuck, Untersetzer usw. Verwendung finden.The plastic masses are special in the production of coating layers, used for finishing or protecting surfaces. such Objects can then used as wall decorations, coasters, etc.

Häufige Verwendung ist auch die Verzierung oder Beschriftung von Windlichtern oder Lampenschirme.Common It is also used to decorate or label lanterns or lampshades.

Weitere Verwendungen liegen in der Erstellung von Reliefs, dem Einsatz als Schreibmittel in Spritzflaschen mit Spritzdüsen zum Dekorieren von Glasflächen an Flaschen oder Fenstern.Further uses are in the Creation of reliefs, use as writing materials in wash bottles with spray nozzles for decorating glass surfaces on bottles or windows.

Weiter kann die Kunststoffmasse auch zur Erzeugung von Buntglaseffekten oder Fensterbildern eingesetzt werden. Ein weiteres Beispiel für die Vielfalt der Verwendung ist die einer Übertragungstechnik, fast wie „Abziehbilder", von Offset gedruckten Abbildungen, Schwarz/Weiß- sowie Farbkopien und Buntstiftzeichnungen.The plastic mass can also used to create stained glass effects or window pictures become. Another example of the variety of uses is that of a transfer technique, almost like "decals", of offset printed images, Black-and-white- as well as color copies and colored pencil drawings.

Claims (7)

F1ießfähige Kunststoffmasse bestehend aus Bindemittel, Weichmachern sowie ggf. weiteren Zusatzstoffen, wobei das Bindemittel PVC oder ein PVC-Copolymerisat ist dadurch gekennzeichnet, dass der Weichmacher (WM) ein 2,2,4-Trimethyl-l,3-Pentanediyl Dibenzoate ist.Pourable plastic mass consisting of binders, plasticizers and possibly other additives, the binder PVC or a PVC copolymer being characterized in that the plasticizer (WM) is a 2,2,4-trimethyl-1,3-pentanediyl dibenzoate. Kunststoffmasse nach Anspruch 1, dadurch gekennzeichnet, dass der Gehalt an Weichmacher (WM) in der Masse zwischen und 40 und 70 Gew.-% liegt.Plastic mass according to claim 1, characterized in that the plasticizer (WM) content in the mass between and 40 and 70% by weight. Kunststoffmasse nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass sich die Masse aus 30 – 60 Gew.- % Bindemittel (BM) 40 – 70 Gew.- % Weichmacher (WM) 0 – 10 Gew.- % Farbmittel (FM) 0 – 5 Gew.- % Stabilisator (Z5) zusammensetzt.Plastic mass according to claim 1 or 2, characterized in that crowd out 30 - 60% by weight of binder (BM) 40-70% by weight % Plasticizer (WM) 0-10 % By weight of colorant (FM) 0 - 5 Wt% stabilizer (Z5) composed. Kunststoffmasse nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Masse als Zusatzstoff ein Farbmittel (FM) aufweist.Plastic mass according to one of the preceding claims, characterized characterized that the mass as an additive is a colorant (FM) having. Kunststoffmasse nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Masse als Zusatzstoff einen Stabilisator (ZS) aufweist.Plastic mass according to one of the preceding claims, characterized characterized that the mass as an additive is a stabilizer (ZS) has. Verwendung einer fließfähigen Kunststoffmasse nach einem der vorhergehenden Ansprüche, als Arbeitsmittel im Hobby- und Künstlerbereich.Use of a flowable plastic mass after any of the preceding claims, as a tool in the hobby and Artist area. Verwendung einer fließfähigen Kunststoffmasse nach einem der vorhergehenden Ansprüche, wobei die Kunststoffmasse als Beschichtungs- oder Überzugsmittel, als Schreibmittel, als Klebstoff oder als Gießmasse eingesetzt oder verwendet wird.Use of a flowable plastic mass after any of the preceding claims, the plastic mass as a coating or coating agent, used or used as a writing medium, as an adhesive or as a casting compound becomes.
DE2003102949 2003-01-24 2003-01-24 Use of a flowable plastic mass Expired - Fee Related DE10302949B4 (en)