DE102014103962A1 - Feumurkomponente a hip joint prosthesis and method for producing a femoral component of a hip joint prosthesis - Google Patents
Feumurkomponente a hip joint prosthesis and method for producing a femoral component of a hip joint prosthesis Download PDFInfo
- Publication number
- DE102014103962A1 DE102014103962A1 DE102014103962.9A DE102014103962A DE102014103962A1 DE 102014103962 A1 DE102014103962 A1 DE 102014103962A1 DE 102014103962 A DE102014103962 A DE 102014103962A DE 102014103962 A1 DE102014103962 A1 DE 102014103962A1
- Authority
- DE
- Germany
- Prior art keywords
- shaped
- shaft
- titanium
- metal structures
- titanium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Die Erfindung betrifft eine Femurkomponente (20) einer Hüftgelenkprothese aus einer geschmiedeten Titanlegierung, mit einem zur zementfreien Verankerung im Femur eines Menschen oder Tiers bestimmten Schaft (21), der in einem proximalen Schaftbereich (24) eine poröse, metallische, durch Sintern und/oder Verschmelzen hergestellte Oberfläche (25). Der proximale Schaftbereich (24) des Schafts (21) ist mit einer unter Maß hergestellten Außenoberfläche (28) versehen, die mit mittels eines Laserstrahls aufgesinterten und/oder verschmolzenen, stegförmigen und/oder bandförmigen und/oder hinterschnittenen oder Hinterschnitte aufweisenden Metallstrukturen (31) aus Titan oder aus einer Titanlegierung versehen ist, die nach außen offene Poren (32) zur Unterstützung des Femuranbaus und/oder der Osseointegration begrenzen. Die Erfindung betrifft auch ein Verfahren zur Herstellung einer Femurkomponente einer Hüftgelenkprothese.The invention relates to a femoral component (20) of a hip joint prosthesis made of a forged titanium alloy, with a shaft (21) intended for cementless anchoring in the femur of a human or animal, which in a proximal shaft region (24) has a porous, metallic, by sintering and / or Fusion produced surface (25). The proximal shank region (24) of the shank (21) is provided with an outer surface (28) which has been made to measure and which has metal structures (31) which have been sintered and / or fused by means of a laser beam, web-shaped and / or band-shaped and / or undercut or undercuts. is made of titanium or of a titanium alloy, which define outwardly open pores (32) to support femoral growth and / or osseointegration. The invention also relates to a method for producing a femoral component of a hip joint prosthesis.
Description
Die Erfindung betrifft eine Femurkomponente einer Hüftgelenkprothese aus einer geschmiedeten Titanlegierung, mit einem ein distales Schaftende und ein proximales Schaftende aufweisenden, zur zementfreien Verankerung im Femur eines Menschen oder Tiers bestimmten Schaft, der in einem, vorzugsweise proximalen, Schaftbereich eine poröse, metallische, durch Sintern und/oder Verschmelzen hergestellte Oberfläche aufweist, um einen Femuranbau und eine Osseointegration bzw. um ein Knochenwachstum des Femurs und einen Eingriff des Femurs bzw. mit dem Femur zu fördern. Die Erfindung betrifft auch ein Verfahren zur Herstellung einer zementfrei implantierbaren bzw. zu implantierenden Femurkomponente einer Hüftgelenkprothese. The invention relates to a femoral component of a forged hip joint prosthesis with a distal shaft end and a proximal shaft end intended for cementless anchoring in the femur of a human or animal, which in a, preferably proximal, shaft region a porous, metallic, by sintering and / or fusing surface to promote femur construction and osseointegration, or bone growth of the femur and femur or femur engagement. The invention also relates to a method for producing a cementless implantable or to be implanted femoral component of a hip joint prosthesis.
Hüftgelenkprothesen sind auch unter der Bezeichnung Hüftendoprothesen bekannt. Diese weisen acetabulare Komponenten und femurale bzw. femorale Komponenten auf, die auch mit Femurkomponenten bezeichnet werden. Die Femurkomponenten können unterschieden werden in mittels eines Zements implantierbare bzw. zu implantierende Hüftgelenkprothesen, die auch als zementierte Komponenten bezeichnet werden und in zementfrei implantierbare bzw. zu implantierende Hüftgelenkprothesen, die auch als zementfreie Komponenten bezeichnet werden. Die Erfindung bezieht sich auf zementfrei implantierbare bzw. zu implantierende Hüftschäfte. Derartige Hüftschäfte bestehen aus Metall und können insbesondere durch Gießen oder Schmieden, insbesondere durch Gesenkschmieden, hergestellt werden. Aufgrund ihrer besonderen mechanischen und bioverträglichen Eigenschaften und wegen ihres zugleich minimalen Gewichts werden Femurkomponenten bzw. Schäfte von Hüftgelenkprothesen aus einer Titanlegierung besonders bevorzugt. Hip joint prostheses are also known as hip endoprostheses. These have acetabular components and femoral or femoral components, which are also referred to as femoral components. The femoral components can be distinguished in hip-joint prostheses which can be implanted or implanted by means of a cement, which are also referred to as cemented components, and in cementless implantable or hip-joint prostheses which are also referred to as cement-free components. The invention relates to cementless implantable or to be implanted Hüftschäfte. Such Hüftschäfte are made of metal and can be produced in particular by casting or forging, in particular by drop forging. Because of their particular mechanical and biocompatible properties and because of their minimal weight at the same time, femoral components or shanks of hip joint prostheses made of a titanium alloy are particularly preferred.
Üblicherweise werden Schmiede-Rohteile über Maß gefertigt, durch Reinigungsstrahlen entzundert und dann durch eine spanende Fertigung, insbesondere durch Fräsen, auf endkonturnahe Abmessungen bzw. auf Maß gebracht. Durch die Zerspanung werden eher glatte Oberflächen mit einer vergleichsweise geringen Rautiefe im Bereich weniger Mikrometer erreicht. Usually, forged blanks are made over measure, descaled by cleaning jets and then brought by a machining production, in particular by milling, on close to final dimensions or to measure. The cutting achieves rather smooth surfaces with a comparatively small roughness in the range of a few micrometers.
Um eine dauerhafte Fixation im Femur bzw. im Oberschenkelknochen zu erzielen, kommt es insbesondere bei den zementfrei implantierten Hüftgelenkprothesen auf eine sehr gute Primärstabilität an. Um den Knochenanbau und die Osseointegration zu unterstützen bzw. zur Föderung des Knochenwachstum des Femurs und des Femureingriffs, können insbesondere in einem proximalen Schaftbereich des Schafts bzw. in einem Bereich, in dem eine Knochenbefestigung an dem Implantat gewünscht ist, Oberflächenrauhigkeiten, vorzugsweise in Form einer porösen Außenoberfläche, vorgesehen sein. In diesem Zusammenhang kann man auch von texturierten Bereichen sprechen. Dort soll der Knochen möglichst frühzeitig und gut einwachsen, damit der Patient das Implantat möglichst bald belasten kann. In order to achieve a permanent fixation in the femur or in the thighbone, a very good primary stability is required, in particular in the cementless implanted hip joint prostheses. In order to support the bone cultivation and the osseointegration or to promote bone growth of the femur and the femur engagement, in particular in a proximal shaft region of the shaft or in a region in which a bone attachment to the implant is desired, surface roughness, preferably in the form of a porous outer surface, be provided. In this context, one can also speak of textured areas. There the bone should grow in as early and well as possible so that the patient can load the implant as soon as possible.
Es sind diverse Verfahren zur Herstellung derartiger poröser Oberflächen bekannt geworden. Unter diesen Verfahren sind insbesondere das so genannte Plasmaspritzverfahren oder das Aufbringen von aus Metallkurzfasern aus Titan komprimierten Metallfasergeweben bekannt geworden. Es werden auch gesinterte poröse Überzüge aus Metallpartikeln eingesetzt. Derartige Verfahren bzw. damit hergestellte Implantate sind beispielsweise aus der
Aus der
Eine optimale Porengröße, Porosität und Biokompatibilität der porösen Oberflächen unterstützt den Knochenanbau und die Osseointegration, was für eine langanhaltende Stabilität der Implantate erforderlich ist. Optimum pore size, porosity and biocompatibility of the porous surfaces support bone attachment and osseointegration, which is required for long-term stability of the implants.
Es ist eine Aufgabe der Erfindung, eine Femurkomponente einer Hüftgelenkprothese der eingangs genannten Art zur Verfügung zu stellen, die einen verbesserten Knochenanbau und eine verbesserte Osseointegration ermöglicht und die vorteilhafte Möglichkeiten für Poren begrenzende bzw. ausbildende Metallstrukturen bietet, die nach dem Einwachsen des Knochengewebes in die Poren nicht nur Scherkräfte entlang des Schafts aufnehmen können, sondern die auch Zug- bzw. Biegekräfte sicher aufnehmen können. Es ist ferner eine Aufgabe der Erfindung ein Verfahren zur Verfügung zu stellen, das besonders flexible und erweiterte Möglichkeiten zur Herstellung einer poröse Oberflächenstrukturen aufweisenden Femurkomponente einer Hüftgelenkprothese bietet, welche die vorstehenden erwähnten Vorteile aufweist. It is an object of the invention to provide a femoral component of a hip joint prosthesis of the type mentioned in the introduction, which permits improved bone cultivation and improved osseointegration and which offers advantageous possibilities for pore-limiting metal structures which after bone ingrowth into the bone tissue Pores can not only absorb shear forces along the shaft, but can also safely absorb tensile or bending forces. It is a further object of the invention to provide a method which offers particularly flexible and expanded possibilities for producing a porous surface structure femoral component of a hip joint prosthesis, which has the aforementioned advantages.
Die auf die Vorrichtung bezogene Aufgabe wird insbesondere durch die Merkmale des Anspruches 1 gelöst und die auf das Verfahren bezogene Aufgabe wird insbesondere durch die Merkmale des Anspruches 7 gelöst. The object related to the device is in particular solved by the features of claim 1 and the task related to the method is in particular solved by the features of
Demgemäß betrifft die Erfindung insbesondere eine zementfrei implantierbare bzw. zementfrei zu implantierende Femurkomponente einer Hüftgelenkprothese aus einer geschmiedeten Titanlegierung, mit einem ein distales Schaftende und ein proximales Schaftende aufweisenden, zur zementfreien Verankerung im Femur eines Menschen oder Tiers bestimmten Schaft, der in einem, vorzugsweise proximalen, Schaftbereich eine poröse, metallische, durch Sintern und/oder durch Verschmelzen hergestellte Oberfläche zur Unterstützung eines Femuranbaus und einer Osseointegration bzw. zur Förderung von Knochenwachstum des Femurs und eines Eingriffs des Femurs bzw. mit dem Femur aufweist, wobei ein Schaftbereich des Schafts, insbesondere der proximale Schaftbereich des Schafts, mit einer unter Maß hergestellten Außenoberfläche versehen ist, die mit aufgesinterten und/oder aufgeschmolzenen, stegförmigen und/oder bandförmigen und/oder hinterschnittenen bzw. Hinterschnitte aufweisenden Metallstrukturen aus Titan oder aus einer Titanlegierung versehen ist, die nach außen offene Poren zur Unterstützung des Femuranbaus und/oder der Osseointegration bzw. zur Förderung von Knochenwachstum des Femurs und eines Eingriffs des Femurs bzw. mit dem Femur begrenzen. Accordingly, the invention relates in particular to a cementless implantable or cementless femoral component of a forged titanium alloy having a distal shaft end and a proximal shaft end intended for cementless anchoring in the femur of a human or animal, which is in one, preferably proximal Shank region has a porous, metallic, by sintering and / or by fusing surface for supporting femur cultivation and osseointegration or to promote bone growth of the femur and an engagement of the femur or with the femur, wherein a shaft portion of the shaft, in particular the proximal shaft region of the shaft is provided with an outer surface produced under dimension, which has metal structures a sintered and / or fused, rib-shaped and / or band-shaped and / or undercut or undercut Titanium or titanium alloy is provided to limit the externally open pores to support the femoral culture and / or osseointegration or to promote bone growth of the femur and an intervention of the femur or with the femur.
Gemäß einer ganz besonders bevorzugten Ausgestaltung kann vorgesehen sein, dass die unter Maß hergestellte Außenoberfläche mit mittels eines Laserstrahls bzw. mittels Lasersintern aufgesinterten und/oder aufgeschmolzenen, stegförmigen und/oder bandförmigen und/oder hinterschnittenen bzw. Hinterschnitte aufweisenden Metallstrukturen aus Titan oder aus einer Titanlegierung versehen ist, die die nach außen offenen Poren begrenzen. Dadurch werden flexible und auch neue Möglichkeiten für noch bessere Hüftgelenkprothesen zum Wohle der betroffenen Patienten geschaffen. Dies gilt vor allem dann, wenn die aufgesinterten Metallstrukturen hinterschnitten sind bzw. Hinterschnitte aufweisen. Denn dann können sich nach dem Einwachsen des Knochens in die Hinterschnitte bzw. in die hinterschnittenen Bereiche der Metallstrukturen formschlüssige Verbindungen zwischen dem Knochen und dem Implantat derart ausbilden, dass auch senkrecht zu der jeweiligen Außenoberfläche des Implantats wirkende Zugkräfte, vor allem aber Biegekräfte wirksam übertragen werden können. Dadurch wird eine ganz besonders gute und über lange Zeit sichere Fixierung des Implantats in dem Knochen bzw. Femur erreicht. According to a very particularly preferred embodiment it can be provided that the outer surface produced under measure with sintered by means of a laser beam or by laser sintering and / or molten, web-shaped and / or band-shaped and / or undercut or undercut metal structures of titanium or of a titanium alloy is provided, which limit the pores open to the outside. This creates flexible and new opportunities for even better hip joint prostheses for the benefit of the affected patients. This is especially true when the sintered metal structures are undercut or have undercuts. Because then, after ingrowth of the bone into the undercuts or into the undercut areas of the metal structures, form-fitting connections between the bone and the implant can be formed in such a way that tensile forces, but in particular bending forces, acting perpendicular to the respective outer surface of the implant are effectively transferred can. This achieves a particularly good and long-term secure fixation of the implant in the bone or femur.
Gemäß einer Weiterbildung kann vorgesehen sein, dass die Metallstrukturen, in einer Draufsicht betrachtet, sich bogenförmig und/oder buchstabenförmig und/oder V-förmig und/oder U-förmig und/oder S-förmig und/oder f-förmig und/oder F-förmig und/oder L-förmig und/oder t-förmig und/oder T-förmig und/oder sternförmig und/oder X-förmig und/oder ringförmig über die unter Maß hergestellte Außenoberfläche erstrecken bzw. dass die Metallstrukturen, in einer Draufsicht betrachtet, bogenförmig und/oder buchstabenförmig und/oder V-förmig und/oder U-förmig und/oder S-förmig und/oder f-förmig und/oder F-förmig und/oder L-förmig und/oder t-förmig und/oder T-förmig und/oder sternförmig und/oder X-förmig und/oder ringförmig ausgebildet sind. According to a development, it can be provided that the metal structures, seen in a plan view, are arcuate and / or letter-shaped and / or V-shaped and / or U-shaped and / or S-shaped and / or F-shaped and / or F -shaped and / or L-shaped and / or T-shaped and / or T-shaped and / or star-shaped and / or X-shaped and / or annular over the outer surface produced under dimension or that the metal structures, in a plan view considered, arcuate and / or letter-shaped and / or V-shaped and / or U-shaped and / or S-shaped and / or F-shaped and / or F-shaped and / or L-shaped and / or T-shaped and / or T-shaped and / or star-shaped and / or X-shaped and / or annular.
Alternativ oder zusätzlich kann vorgesehen sein, dass die Metallstrukturen, in einer parallel oder tangential zu der unter Maß hergestellten Außenoberfläche des Schafts verlaufenden Schnittebene betrachtet, einen bogenförmigen und/oder einen buchstabenförmigen, insbesondere V-förmigen und/oder U-förmigen und/oder S-förmigen und/oder f-förmigen und/oder F-förmigen und/oder L-förmigen und/oder t-förmigen und/oder T-förmigen und/oder X-förmigen, und/oder einen sternförmigen und/oder einen ringförmigen Querschnitt aufweisen. Alternatively or additionally, it may be provided that the metal structures, viewed in a sectional plane running parallel or tangentially to the outer surface of the shaft produced under dimension, have an arcuate and / or letter-shaped, in particular V-shaped and / or U-shaped and / or S -shaped and / or F-shaped and / or F-shaped and / or L-shaped and / or T-shaped and / or T-shaped and / or X-shaped, and / or a star-shaped and / or an annular cross-section exhibit.
Alternativ oder zusätzlich kann vorgesehen sein, dass die Metallstrukturen in einem quer oder senkrecht zu der unter Maß hergestellten Außenoberfläche verlaufenden Schnittebene betrachtet einen rechteckförmigen und/oder länglichen und/oder langgestreckten und/oder konkaven und/oder V-förmigen und/oder U-förmigen und/oder t-förmigen und/oder T-förmigen und/oder pilzförmigen und/oder kegelförmigen und/oder doppelkegelförmigen Querschnitt aufweisen. Vorzugsweise dann, wenn die Metallstrukturen einen kegelförmigen Querschnitt aufweisen, sind sie mit Wandteilen gebildet, die sich zu der unter Maß hergestellten Außenoberfläche hin verjüngen. Vorzugsweise dann, wenn die Metallstrukturen einen doppelkegelförmigen Querschnitt aufweisen, sind sie mit zwei kegelförmigen Wandteilen gebildet, die sich in Richtung zueinander kegelförmig verjüngen. Alternatively or additionally, it may be provided that, in a sectional plane running transversely or perpendicular to the outer surface produced under dimension, the metal structures have a rectangular and / or oblong and / or elongated and / or concave and / or V-shaped and / or U-shaped and / or T-shaped and / or T-shaped and / or mushroom-shaped and / or conical and / or biconical cross-section. Preferably, when the metal structures have a tapered cross-section, they are formed with wall portions that taper toward the outer surface made to dimension. Preferably, when the metal structures have a double-cone-shaped cross-section, they are formed with two conical wall parts, which taper conically in the direction of each other.
Alternativ oder zusätzlich kann vorgesehen sein, dass der, vorzugsweise proximale, Schaftbereich des Schafts mit einer, beispielsweise als ein Fach oder eine Tasche ausgebildeten, Ausnehmung versehen ist, die teilweise oder vollumfänglich von einem Ausnehmungsrand des Schafts begrenzt ist und die von einem die unter Maß hergestellte Außenoberfläche aufweisenden Ausnehmungsboden des Schafts begrenzt ist. Alternatively or additionally, it may be provided that the, preferably proximal, shaft portion of the shaft is provided with a recess formed, for example, as a pocket or a pocket, which is partially or fully bounded by a recess edge of the shaft and that of the lower produced outer surface having recess bottom of the shaft is limited.
Die Erfindung betrifft insbesondere auch ein Verfahren zur Herstellung der Femurkomponente, insbesondere nach einem der Ansprüche 1 bis 6, oder zur Herstellung einer Femurkomponente einer Hüftgelenkprothese aus einer Titanlegierung, die einen zur zementfreien Verankerung im Femur eines Menschen oder Tiers bestimmten, ein distales Schaftende und ein proximales Schaftende aufweisenden Schaft aus einem geschmiedeten Schaftwerkstoff enthält, wobei entweder von einem einen Schaft enthaltenden geschmiedeten Rohling der Femurkomponente ausgegangen wird, oder ein einen Schaft enthaltender Rohling der Femurkomponente durch Schmieden, vorzugsweise durch Warmschmieden, insbesondere durch Gesenkschmieden, hergestellt wird, wonach in einem, vorzugsweise proximalen, Schaftbereich des geschmiedeten Schafts der geschmiedete Schaftwerkstoff teilweise, vorzugsweise spanabhebend, beispielsweise durch Fräsen, auf unter Maß unter Ausbildung einer Außenoberfläche abgetragen wird, wonach auf die Außenoberfläche, ein Metallpulver, vorzugsweise in Form einer Schicht oder mehrerer Schichten, aus Titan oder aus einer Titanlegierung aufgebracht und gleichzeitig oder anschließend mittels eines Laserstrahls bzw. mittels Lasersintern, vorzugsweise bei Umgebungsdruck bzw. bei nicht erhöhten Drücken, insbesondere frei von erhöhten Drücken, derart auf die Außenoberfläche des Schaft aufgesintert und/oder in die Außenoberfläche des Schaft eingeschmolzen wird bzw. mit der Außenoberfläche des Schafts verschmolzen wird, dass sich dort nach außen offene Poren begrenzende Metallstrukturen aus Titan oder aus einer Titanlegierung zur Unterstützung eines oder des Femuranbaus und einer oder der Osseointegration bzw. zur Förderung von Knochenwachstum des Femurs und eines Eingriffs des Femurs bzw. mit dem Femur ausbilden. The invention also relates in particular to a method for producing the femoral component, in particular according to one of claims 1 to 6, or for producing a femoral component of a hip joint prosthesis made of a titanium alloy, which has a cementless anchorage in the femur of a human or animal, a distal shaft end and a Proximal shank end containing shaft of a forged stock material, either from a one shaft or a shank-containing blank of the femoral component is produced by forging, preferably hot forging, in particular swaging, whereby in a, preferably proximal, shank region of the forged stem the forged stem material is partially, preferably machined, for example by milling to a degree to form an outer surface is removed, after which applied to the outer surface, a metal powder, preferably in the form of one or more layers of titanium or a titanium alloy and simultaneously or subsequently by means of a laser beam or by laser sintering, preferably at ambient pressure or at non-elevated pressures, in particular free from elevated pressures, so sintered onto the outer surface of the shaft and / or is melted into the outer surface of the shaft or with the outside fused to the outside surface of the stem, there are titanium or titanium alloy metal structures, open to the outside, to support femurs and / or osseointegration or to promote bone growth of the femur and femur or femur engagement form.
Gemäß einer besonders bevorzugten Ausführungsvariante kann vorgesehen sein, dass auf die Außenoberfläche des Schafts eine erste Pulverschicht eines oder des Metallpulvers aus Titan oder aus einer oder der Titanlegierung aufgebracht wird, das gleichzeitig oder anschließend mittels eines Laserstrahls auf die Außenoberfläche des Schafts aufgesintert und/oder in die Außenoberfläche des Schafts eingeschmolzen bzw. mit der Außenoberfläche des Schafts verschmolzen wird, so dass sich dort über die Außenoberfläche erhebende Metallstrukturen ausbilden, wonach wenigstens eine weitere Pulverschicht eines oder des Metallpulvers aus Titan oder aus einer oder der Titanlegierung auf die Metallstrukturen aufgetragen wird, das gleichzeitig oder anschließend mittels eines Laserstrahls derart auf die Metallstrukturen aufgesintert und/oder in die Metallstrukturen eingeschmolzen bzw. mit den Metallstrukturen verschmolzen wird, dass sich die nach außen offene Poren begrenzenden Metallstrukturen aus Titan oder aus der Titanlegierung ausbilden. According to a particularly preferred embodiment, provision may be made for a first powder layer of titanium powder or titanium alloy or titanium alloy to be applied to the outer surface of the shaft, which is simultaneously or subsequently sintered onto the outer surface of the shaft by means of a laser beam and / or the outer surface of the stem is fused or fused with the outer surface of the stem to form elevational metal structures over the outer surface, after which at least one further powder layer of one or the titanium or titanium alloy metal powder is applied to the metal structures at the same time or subsequently sintered onto the metal structures by means of a laser beam and / or melted into the metal structures or fused to the metal structures such that the metal structures opening outward open pores from titanium or from the titanium alloy.
Gemäß einer besonders bevorzugten Ausführungsvariante kann vorgesehen sein, dass das Metallpulver aus Titan oder aus der Titanlegierung mittels eines Laserstrahls bzw. mittels Lasersintern derart aufgesintert und/oder eingeschmolzen wird, dass die Metallstrukturen stegförmig und/oder bandförmig ausgebildet sind und/oder hinterschnitten sind bzw. Hinterschnitte aufweisen. According to a particularly preferred embodiment, it can be provided that the metal powder of titanium or of the titanium alloy is sintered and / or melted by means of a laser beam or by laser sintering such that the metal structures are web-shaped and / or band-shaped and / or undercut or Have undercuts.
Alternativ oder zusätzlich kann vorgesehen sein, dass das Metallpulver aus Titan oder aus der Titanlegierung mittels eines Laserstrahls bzw. mittels Lasersintern derart aufgesintert und/oder eingeschmolzen wird, dass sich die Metallstrukturen, in einer Draufsicht betrachtet, bogenförmig und/oder einen buchstabenförmig und/oder V-förmig und/oder U-förmig und/oder S-förmig und/oder f-förmig und/oder F-förmig und/oder L-förmig und/oder t-förmig und/oder T-förmig und/oder sternförmig und/oder X-förmig und/oder ringförmig über die Außenoberfläche erstrecken. Alternatively or additionally, it may be provided that the metal powder of titanium or of the titanium alloy is sintered and / or melted by means of a laser beam or by laser sintering such that the metal structures, seen in a plan view, arcuate and / or a letter-shaped and / or V-shaped and / or U-shaped and / or S-shaped and / or F-shaped and / or F-shaped and / or L-shaped and / or T-shaped and / or T-shaped and / or star-shaped and or extend X-shaped and / or annular over the outer surface.
Alternativ oder zusätzlich kann vorgesehen sein, dass das Metallpulver aus Titan oder aus der Titanlegierung mittels eines Laserstrahls bzw. mittels Lasersintern derart aufgesintert und/oder eingeschmolzen wird, dass die Metallstrukturen, in einer parallel oder tangential zu der Außenoberfläche verlaufenden Schnittebene betrachtet, einen bogenförmigen und/oder einen buchstabenförmigen und/oder einen V-förmigen und/oder einen U-förmigen und/oder einen S-förmigen und/oder einen f-förmigen und/oder einen F-förmigen und/oder einen L-förmigen und/oder einen t-förmigen und/oder einen T-förmigen und/oder einen sternförmigen und/oder einen X-förmigen und/oder einen ringförmigen Querschnitt aufweisen. Alternatively or additionally, it can be provided that the metal powder of titanium or of the titanium alloy is sintered and / or melted by means of a laser beam or laser sintering such that the metal structures, viewed in a direction parallel or tangent to the outer surface cutting plane, an arcuate and / or a letter-shaped and / or a V-shaped and / or a U-shaped and / or an S-shaped and / or an F-shaped and / or an F-shaped and / or an L-shaped and / or a T-shaped and / or have a T-shaped and / or a star-shaped and / or an X-shaped and / or an annular cross-section.
Alternativ oder zusätzlich kann vorgesehen sein, dass das Metallpulver aus Titan oder aus der Titanlegierung mittels eines Laserstrahls bzw. mittels Lasersintern derart aufgesintert und/oder eingeschmolzen wird, dass die Metallstrukturen in einem quer oder senkrecht zu der Außenoberfläche verlaufenden Schnittebene betrachtet einen rechteckförmigen und/oder länglichen und/oder langgestreckten und/oder konkaven und/oder V-förmigen und/oder U-förmigen und/oder t-förmigen und/oder T-förmigen und/oder pilzförmigen und/oder kegelförmigen und/oder doppelkegelförmigen Querschnitt aufweisen. Alternatively or additionally, it may be provided that the metal powder of titanium or of the titanium alloy is sintered and / or melted by means of a laser beam or laser sintering such that the metal structures in a transverse or perpendicular to the outer surface extending cutting plane considered a rectangular and / or elongate and / or elongate and / or concave and / or V-shaped and / or U-shaped and / or T-shaped and / or T-shaped and / or mushroom-shaped and / or conical and / or biconical cross-section.
Alternativ oder zusätzlich kann vorgesehen sein, dass der geschmiedete Schaftwerkstoff in dem, vorzugsweise proximalen, Schaftbereich des Schafts unter Ausbildung einer, beispielsweise als ein Fach oder eine Tasche ausgebildeten, Ausnehmung, vorzugsweise spanabhebend, beispielsweise durch Fräsen, abgetragen wird, die teilweise oder vollumfänglich von einem Ausnehmungsrand des geschmiedeten Schafts begrenzt ist und die von einem die Außenoberfläche aufweisenden Ausnehmungsboden des Schafts begrenzt ist, wonach das Metallpulver aus Titan oder aus der Titanlegierung auf die Außenoberfläche bzw. auf die Metallstrukturen der Ausnehmung mittels eines Laserstrahls bzw. mittels Lasersintern aufgesintert und/oder in die Außenoberfläche der Ausnehmung bzw. in die in der Ausnehmung angeordneten Metallstrukturen eingeschmolzen wird. Alternatively or additionally, it may be provided that the forged shaft material in the, preferably proximal, shaft portion of the shaft to form a, for example as a pocket or a pocket formed, recess, preferably machined, for example, by milling, which partially or completely from a recess edge of the forged shaft is limited and which is bounded by a recess having the outer surface of the shaft, after which the metal powder of titanium or titanium alloy on the outer surface or on the metal structures of the recess by means of a laser beam or sintered by laser sintering and / or is melted into the outer surface of the recess or in the arranged in the recess metal structures.
Es versteht sich, dass die vorstehenden Merkmale und Maßnahmen im Rahmen der Ausführbarkeit der Erfindung beliebig kombiniert werden können. It is understood that the above features and measures may be combined as desired within the scope of the invention.
Weitere Merkmale, Vorteile und Gesichtspunkte der Erfindung ergeben sich aus den Ansprüchen und den Zeichnungen sowie aus dem nachfolgenden Beschreibungsteil, in dem ein bevorzugtes Ausführungsbeispiel der Erfindung anhand von Figuren beschrieben ist. Further features, advantages and aspects of the invention will become apparent from the claims and the drawings and from the following description part, in which a preferred embodiment of the invention with reference to figures.
Es zeigen: Show it:
Die
Der Schaft
Die
Die
Die in der
Zur Herstellung der Femurkomponente
Entweder kann man von einem aus einer Titanlegierung bestehenden, einen Schaft enthaltenden, geschmiedeten Rohling einer bzw. für eine Femurkomponente einer Hüftgelenkprothese ausgehen oder kann zunächst ein einen Schaft enthaltender Rohling einer bzw. für eine Femurkomponente einer Hüftgelenkprothese durch Schmieden aus einer Titanlegierung hergestellt werden. Als Schmiedeverfahren kann bevorzugt Warmschmieden und Gesenkschmieden angewandt sein bzw. werden. For making the
Either one may start from a forged titanium alloy stem for a femoral component of a hip joint prosthesis, or first a stem containing a stem for or for a femoral component of a hip joint prosthesis may be made by forging a titanium alloy. As a forging method, hot forging and drop forging can be preferably used.
Anschließend wird zunächst in einem bzw. in dem proximalen Schaftbereich
Daran anschließend wird auf die durch den Materialabtrag gebildete Außenoberfläche
Gleichzeitig oder anschließend wird das Metallpulver dieser ersten Pulverschicht mittels eines nicht gezeigten Laserstrahls bzw. mittels Lasersintern bei Umgebungsdruck, also frei von erhöhten Drücken, bei durch den Laserstrahl stark erhöhten Temperaturen, auf die Außenoberfläche
Anschließend wird wenigstens eine weitere Pulverschicht eines oder des Metallpulvers aus Titan oder aus einer oder der Titanlegierung auf die ersten Metallstrukturen aufgetragen. Subsequently, at least one further powder layer of one or of the metal powder made of titanium or of one or the titanium alloy is applied to the first metal structures.
Gleichzeitig oder anschließend wird das Metallpulver dieser weiteren Pulverschicht mittels eines nicht gezeigten Laserstrahls bzw. mittels Lasersintern bei Umgebungsdruck, also frei von erhöhten Drücken, bei durch den Laserstrahl stark erhöhten Temperaturen, derart auf die ersten Metallstrukturen aufgesintert und/oder in die Metallstrukturen eingeschmolzen, dass sich nach außen offene Poren
Dabei kann das Metallpulver mittels des Laserstrahls bzw. mittels Lasersintern derart auf die besagte vertiefte bzw. unter Maß hergestellte Außenoberfläche
BezugszeichenlisteLIST OF REFERENCE NUMBERS
- 2020
- Femurkomponente/Hüftgelenkprothese Femoral / acetabular prosthesis
- 2121
- Schaft shaft
- 2222
- distales Schaftende distal shaft end
- 2323
- proximales Schaftende proximal shaft end
- 2424
- proximaler Schaftbereich proximal shaft area
- 2525
- Oberfläche surface
- 2626
- Hals neck
- 2727
- Kopf head
- 2828
- Außenoberfläche outer surface
- 2929
- Ausnehmung recess
- 30.130.1
- Ausnehmungsrand recess edge
- 30.230.2
- Ausnehmungsrand recess edge
- 30.330.3
- Ausnehmungsboden recess bottom
- 3131
- Metallstruktur metal structure
- 31.131.1
- Metallstruktur metal structure
- 31.231.2
- Metallstruktur metal structure
- 31.331.3
- Metallstruktur metal structure
- 31.431.4
- Metallstruktur metal structure
- 31.531.5
- Metallstruktur metal structure
- 31.731.7
- Metallstruktur metal structure
- 31.731.7
- Metallstruktur metal structure
- 3232
- Poren pore
ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION
Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.
Zitierte PatentliteraturCited patent literature
- DE 3527136 A1 [0005] DE 3527136 A1 [0005]
- US 3906550 [0005] US 3906550 [0005]
- US 3605123 [0005] US 3605123 [0005]
- DE 69630933 T2 [0006] DE 69630933 T2 [0006]
Claims (13)