DE102013201742A1 - Process for the treatment of silicon-containing fine-grained material in the production of chlorosilanes - Google Patents
Process for the treatment of silicon-containing fine-grained material in the production of chlorosilanes Download PDFInfo
- Publication number
- DE102013201742A1 DE102013201742A1 DE201310201742 DE102013201742A DE102013201742A1 DE 102013201742 A1 DE102013201742 A1 DE 102013201742A1 DE 201310201742 DE201310201742 DE 201310201742 DE 102013201742 A DE102013201742 A DE 102013201742A DE 102013201742 A1 DE102013201742 A1 DE 102013201742A1
- Authority
- DE
- Germany
- Prior art keywords
- fine
- silicon
- grained material
- production
- chlorosilanes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Gegenstand der Erfindung ist ein Verfahren zur Aufbereitung feinkörnigen Materials bei der Herstellung von Chlorsilanen, das dadurch gekennzeichnet ist, dass das feinkörnige Material zu Körpern erhöhter Dichte gepresst wird.The invention relates to a method for processing fine-grained material in the production of chlorosilanes, which is characterized in that the fine-grained material is pressed into bodies of increased density.
Description
Die Erfindung betrifft ein Verfahren zur Aufbereitung Silizium-haltigen feinkörnigen Materials, das bei der Herstellung von Chlorsilanen anfällt, durch Pressen, sowie das verfahrensgemäß erhaltene Kompaktat.The invention relates to a process for the preparation of silicon-containing fine-grained material obtained in the production of chlorosilanes by pressing, and the compacted material obtained according to the method.
Silizium-haltiges Material mit hohen Silizium-Anteilen, typischerweise über 80 %, beispielsweise 84 %, ist ein sehr wertvoller Rohstoff. Er eignet sich auf Grund seines Siliziumgehaltes zur Herstellung von Silizium-Verbindungen, zum Beispiel von Chlorsilanen in einem Festbett- oder Rührbettreaktor. Chlorsilane wiederum stellen eine wichtige Stoffklasse mit einem breiten Anwendungsgebiet dar. Diese werden eingesetzt als Rohstoff zur Herstellung von SiO2, dem sogenannten fumed silica, als Ausgangsmaterial für Organosilane und Kieselsäureester sowie als Edukte für Lichtwellenleiter und Halbleiter- bzw. Solar-Silizium. Es ist daher von höchster technischer und wirtschaftlicher Bedeutung, Chlorsilane in großer Menge kostengünstig und sicher herstellen zu können.Silicon-containing material with high silicon contents, typically over 80%, for example 84%, is a very valuable raw material. It is suitable on the basis of its silicon content for the production of silicon compounds, for example of chlorosilanes in a fixed bed or stirred bed reactor. Chlorosilanes in turn represent an important class of substances with a wide range of applications. These are used as raw materials for the production of SiO 2 , the so-called fumed silica, as starting material for organosilanes and silicic acid esters and as reactants for optical waveguides and semiconductor or solar silicon. It is therefore of the highest technical and economic importance to be able to produce chlorosilanes in large quantities in a cost-effective and safe manner.
In einem Wirbelschicht-, Festbett- oder Rührbettreaktor werden Silizium (Si) und Chlorwasserstoff (HCl) und/oder Chlor (Cl) umgesetzt, wodurch sich anorganische Chlorsilane wie SiCl4 und/oder HSiCl3 und/oder H2SiCl2 oder Gemische daraus bilden und als Produktgase den Reaktor verlassen und anschließend weiter behandelt werden.In a fluidized bed, fixed bed or stirred bed reactor, silicon (Si) and hydrogen chloride (HCl) and / or chlorine (Cl) are reacted to form inorganic chlorosilanes such as SiCl 4 and / or HSiCl 3 and / or H 2 SiCl 2 or mixtures thereof form and leave the reactor as product gases and then treated further.
Die Produktgase enthalten produktionsbedingt Feststoffe wie zum Beispiel Pulver, Stäube und/oder feine Körner enthaltend Silizium, Eisen, Eisenchlorid und/oder Aluminiumchlorid. Eisenchlorid und Aluminiumchlorid sind Reaktionsnebenprodukte, die davon herrühren, dass das eingesetzte Roh-Silizium diese Metalle in geringen Mengen als Kontaminationen enthält, die nach der Verflüssigung der Produktgase, der sogenannten Brüden, in der Flüssigphase zurückbleiben und sich im Behälter für die Flüssigphase absetzen. Dadurch können sie aus dem gebildeten Chlorsilangemisch abgetrennt werden.The product gases contain solids due to production such as, for example, powders, dusts and / or fine grains containing silicon, iron, iron chloride and / or aluminum chloride. Ferric chloride and aluminum chloride are reaction by-products which result from the fact that the raw silicon used contains these metals in small amounts as contaminants which, after the liquefaction of the product gases, the so-called vapors, remain in the liquid phase and settle in the container for the liquid phase. As a result, they can be separated from the chlorosilane mixture formed.
Die in den Produktgasen enthaltenen Feststoffe, die in Form von Pulver, Staub, und/oder in Form feiner Körner auftreten, werden im Rahmen der Erfindung unter den Begriff „feinkörniges Material“ zusammengefasst. The solids contained in the product gases, which occur in the form of powder, dust, and / or in the form of fine grains are summarized in the context of the invention by the term "fine-grained material".
Die Partikel dieses feinkörnigen Materials verlassen den Reaktor, ohne umgesetzt worden zu sein, da das Material wiederum feinkörnig ausgetragen wird. The particles of this fine-grained material leave the reactor without having been reacted, since the material is again discharged in fine-grained.
Die Patentschrift
Eine weitere Möglichkeit, die oben genannten Feststoffe wieder zu größeren Aggregaten bzw. Stücken zu verbinden, besteht darin, diese zu schmelzen oder zu sintern. Dabei ist allerdings der aufgrund der hohen Schmelztemperaturen notwendige Energieaufwand nachteilig.Another way to reconnect the above solids to larger aggregates or pieces is to melt or sinter them. However, the energy required due to the high melting temperatures is disadvantageous.
Es bestand daher die Aufgabe, das feinkörnige Silizium-haltige Material in eine Form zu bringen, in welcher es in die Reaktoren zur Silan-Herstellung, zum Beispiel der Chlorsilanherstellung in einem Festbett-Reaktor, eingebracht werden kann.It was therefore the object to bring the fine-grained silicon-containing material in a form in which it can be introduced into the reactors for silane production, for example, the Chlorsilanherstellung in a fixed-bed reactor.
Die Aufgabe wird gelöst durch ein Verfahren zur Aufbereitung des feinkörnigen Materials und durch die gemäß diesem Verfahren erhaltenen verdichteten Körper. The object is achieved by a method for the preparation of the fine-grained material and by the compacted body obtained according to this method.
Gegenstand der Erfindung ist ein Verfahren zur Aufbereitung feinkörnigen Materials bei der Herstellung von Chlorsilanen, welches dadurch gekennzeichnet ist, dass das feinkörnige Material zu Körpern erhöhter Dichte gepresst wird. Im Rahmen der Erfindung werden die gemäß dem Verfahren der Erfindung erhaltenen Körper „Kompaktate“ genannt.The invention relates to a process for the preparation of fine-grained material in the production of chlorosilanes, which is characterized in that the fine-grained material is pressed into bodies of increased density. In the context of the invention, the bodies obtained according to the process of the invention are called "compactates".
Der Vorteil des beanspruchten Verfahrens ist vor allem darin zu sehen, dass man nach der Durchführung des Verfahrens Kompaktate erhält, die auf einfachere Art und Weise in den Herstellprozess von Chlorsilanen zurück geführt werden können, ohne wie sonst üblich, stark staubendes Pulver oder Asche handhaben zu müssen. Zum Beispiel können die erfindungsgemäß erhaltenen Kompaktate mittels Transportbänder oder Container gehandhabt und in den Chlorsilanherstellprozess zurück geführt werden. Ein Luftabschluss, der eine gefährliche Verwirbelung feinkörniger Feststoffe unterbindet, oder eine aufwendige Absaugung mit Filtervorrichtungen ist mit der Durchführung des erfindungsgemäßen Verfahrens überflüssig.The advantage of the claimed method is to be seen in the fact that after the implementation of the method Kompaktate receives that can be performed in a simpler manner in the production process of chlorosilanes without, as usual, handle heavily dusting powder or ash have to. For example, the Kompaktate obtained according to the invention by means of Transport belts or containers are handled and returned to the chlorosilane production process. An air seal, which prevents dangerous turbulence of fine-grained solids, or a complex extraction with filter devices is superfluous with the implementation of the method according to the invention.
Im Folgenden wird die Erfindung näher erläutert.The invention will be explained in more detail below.
Als feinkörniges Material kann in dem erfindungsgemäßen Verfahren Silizium-Asche, Silizium-Pulver, Silizium-Staub, Heißgasfilterasche, oder ein Gemisch dieser Materialien eingesetzt werden.As a fine-grained material, silicon ash, silicon powder, silicon dust, hot gas filter ash or a mixture of these materials can be used in the process according to the invention.
In dem erfindungsgemäßen Verfahren kann es vorteilhaft sein, das feinkörnige Material in einer Stempelpresse zu pressen. Stempelpressen sind dem Fachmann bekannt. Es können zum Beispiel handelsübliche hydraulisch oder ölhydraulisch arbeitende Stempelpressen, jeweils mit vorgebbarer Presskraft, Pressgeschwindigkeit, Entlastungsposition und Haltezeit, eingesetzt werden.In the method according to the invention, it may be advantageous to press the fine-grained material in a stamping press. Stamp presses are known in the art. For example, commercially available hydraulic or oil hydraulic punch presses, each with a predefinable pressing force, pressing speed, unloading position and holding time, can be used.
Das erfindungsgemäße Verfahren wird vorzugsweise mit einer Presskraft von 2000 bis 8000 N und einer Haltezeit von 25 bis 40 Sekunden, bevorzugt von 30 Sekunden durchgeführt. The inventive method is preferably carried out with a pressing force of 2000 to 8000 N and a holding time of 25 to 40 seconds, preferably of 30 seconds.
Die Haltezeit ist im Rahmen der Erfindung die Zeitdauer, während der das feinkörnige Material der Presskraft ausgesetzt wird, gleichbedeutend mit von der Stempelpresse auf das feinkörnige Material ausgeübten Kraft. The holding time is in the context of the invention, the period during which the fine-grained material is subjected to the pressing force, equivalent to force exerted by the punch press on the fine-grained material.
Da der Stempel der erfindungsgemäß eingesetzten Stempelpresse eine definierte Fläche aufweist, die mit dem feinkörnigen Material in Kontakt gebracht wird, lässt sich der Quotient aus Presskraft und dieser Fläche errechnen und als Druck angeben, der auf das Material während der Ausübung der Presskraft wirkt. Dieser Druck, der im Rahmen der Erfindung Pressdruck genannt wird, wird, beispielsweise mittels Vorgabe der Presskraft, vorzugsweise auf einen Wert von 2 bis 18 kN/cm2 eingestellt, um Kompaktate zu erhalten. Besonders bevorzugt kann ein Pressdruck von 2,3 bis 9,1 kN/cm2 eingestellt werden, um Kompaktate zu erhalten, die fest genug sind, um sie in den Chlorsilanherstellprozess zurückführen zu können, beispielsweise über ein Transportband oder in Gebinden. Since the punch of the stamping press according to the invention has a defined surface, which is brought into contact with the fine-grained material, the quotient of pressing force and this surface can be calculated and given as the pressure acting on the material during the exertion of the pressing force. This pressure, which is called pressing pressure in the context of the invention, is set to a value of 2 to 18 kN / cm 2 , for example by means of presetting the pressing force, in order to obtain compactates. Particularly preferably, a compacting pressure of 2.3 to 9.1 kN / cm 2 can be set in order to obtain compacts which are strong enough to be able to return them to the chlorosilane production process, for example via a conveyor belt or in containers.
Bevorzugt wird beim Auffüllen der Vakanz der erfindungsgemäß eingesetzten Stempelpresse mit dem feinkörnigen Material die auf das Material ausgeübte Kraft allmählich bis zur Presskraft erhöht, um Luft bzw. eingeschlossenes Gas entweichen zu lassen. Da währenddessen das Volumen des feinkörnigen Materials abnimmt, lässt sich ein Quotient aus der Weglänge des die Presskraft übertragenden Stempels und der Zeitdauer definieren, während der die Presskraft von Null beginnend aufgebaut wird. Ist die Presskraft erreicht, hat der Stempel die Weglänge von Null bis zu seiner Endposition auf dem feinkörnigen Material zurückgelegt. Der Quotient wird im Rahmen der Erfindung Pressgeschwindigkeit genannt. Bevorzugt wird eine Pressgeschwindigkeit von 1 bis 20 mm/min gewählt.When filling the vacancy of the stamping press used according to the invention with the fine-grained material, the force exerted on the material is preferably increased gradually to the pressing force in order to allow air or entrapped gas to escape. Meanwhile, as the volume of the fine-grained material decreases, a quotient of the path length of the pressing-force-transmitting punch and the period of time during which the pressing force is established starting from zero can be defined. When the pressing force is reached, the punch has traveled the path length from zero to its final position on the fine-grained material. The quotient is called press speed in the context of the invention. Preferably, a pressing speed of 1 to 20 mm / min is selected.
Je geringer die Größen der Partikel des feinkörnigen Materials aber sind, desto länger dauert es, bis eingeschlossene Luft bzw. Gas entwichen ist. Die ausgewählte Haltezeit führt zu Kompaktaten mit größerer Festigkeit. However, the smaller the sizes of the particles of the fine-grained material are, the longer it takes for trapped air or gas to escape. The selected hold time results in compact data of greater strength.
Nach der Durchführung des beanspruchten Verfahrens liegen die Kompaktate in Form von Tabletten oder Pellets vor. Vorzugsweise werden diese unter Inertgas und/oder verminderter Feuchtigkeit, bevorzugt unter Stickstoff, gelagert. Dies hat den Vorteil, dass die erfindungsgemäß erhaltenen Kompaktate stabil bleiben, gleichbedeutend damit, dass die Kompaktate mindestens während einer Zeitdauer von 60 min bis 10 Tagen beim Lagern nicht zerbrechen. Werden solche Kompaktate unter Stickstoff gelagert, zeigen diese auch nach mehreren Tagen weder Risse, noch Brüche. After carrying out the claimed process, the compacts are in the form of tablets or pellets. Preferably, these are stored under inert gas and / or reduced humidity, preferably under nitrogen. This has the advantage that the compactates obtained according to the invention remain stable, synonymous with the fact that the compacts do not break during storage for a period of at least 60 minutes to 10 days. If such compactates are stored under nitrogen, they will not show cracks or fractures even after several days.
Wird ein Pressdruck im Bereich von mehr als 9,1 kN/cm2, bevorzugt von 10 bis 14 kN/cm2 eingestellt, sind die dann erhaltenen Kompaktate derart fest, dass diese einen Sturz aus 2 m Höhe auf harten Boden überstehen, ohne dass aus mehreren Kompaktaten Stücke abplatzen. Das Abplatzen von Stücken verringert sich mit steigendem Pressdruck, und bei einem eingesetzten Pressdruck von 12 bis 14 kN/cm2 findet man bei den erfindungsgemäß erhaltenen Kompaktaten kaum noch abgeplatzte Stücke.If a pressing pressure in the range of more than 9.1 kN / cm 2 , preferably adjusted from 10 to 14 kN / cm 2 , then the Kompaktate then obtained are so strong that they survive a fall from 2 m height on hard ground, without flake off pieces of several compact pieces. The chipping of pieces decreases with increasing pressing pressure, and at an applied pressing pressure of 12 to 14 kN / cm 2 , hardly any chipped pieces are found in the compactates obtained according to the invention.
Das erfindungsgemäß aufbereitete feinkörnige Material kann bereits dann ohne das Anfallen von feinen Körnern in den Chlorsilanherstellprozess zurückgeführt werden, wenn ein Pressdruck von 10 bis 12 kN/cm2 aufgewandt wurde.The fine-grained material prepared according to the invention can be returned to the chlorosilane production process without the precipitation of fine grains even if a compacting pressure of 10 to 12 kN / cm 2 has been used.
Wird ein Pressdruck von 14 bis 18 kN/cm2 eingesetzt, können die erhaltenen Kompaktate sogenannte Lagen bilden. Solche Lagen sind Zonen mit erhöhtem Dichtegradienten, die quer, längs oder in jeder anderen Richtung innerhalb des Volumens des Kompaktates und bezogen auf die Wirkungsrichtung des Pressdruckes ausgedehnt sein und eine vliesen- oder linsenartige Gestalt haben können. Wird die Lagenbildung vermieden, können die Presslinge besonders einfach in den Reaktor zurückgeführt werden, nämlich, ohne feine Körner oder abgeplatzte Stücke handhaben zu müssen.If a pressing pressure of 14 to 18 kN / cm 2 is used, the resulting compacts can form so-called layers. Such layers are zones of increased density gradients which may be extended transversely, longitudinally or in any other direction within the volume of the compact and in relation to the direction of action of the pressing pressure and may have a non-woven or lenticular shape. If the layer formation is avoided, the compacts can be particularly easily returned to the reactor, namely, without having to handle fine grains or chipped pieces.
In einer weiteren Ausprägung des erfindungsgemäßen Verfahrens können dem feinkörnigen Material auch Bindemittel hinzugefügt werden. Bevorzugt können anorganische Bindemittel eingesetzt werden, vorzugsweise Kieselsäuren, Aluminate, Zirkonate, Calciumoxid, Calciumhydroxid, Zement, Calziumsulfat, organische Verbindungen enthaltende Bindemittel, zum Beispiel Kieselsäureester, oder ein Gemisch dieser Bindemittel. Auch Silizium-Pulver selbst ist als Bindemittel geeignet, falls es zuvor bereits erfindungsgemäß gepresst worden ist. Besonders bevorzugt wird Silizium-Pulver mit einem Anteil von 5 bis 10 % eingesetzt. In a further embodiment of the method according to the invention, it is also possible to add binders to the fine-grained material. Preference is given to using inorganic binders, preferably silicic acids, aluminates, zirconates, calcium oxide, calcium hydroxide, cement, calcium sulfate, binders containing organic compounds, for example silicic acid esters, or a mixture of these binders. Also, silicon powder itself is suitable as a binder, if it has been previously pressed according to the invention. Particular preference is given to using silicon powder in a proportion of 5 to 10%.
Unerwartet werden damit Kompaktate erhalten, die mindestens während einer Zeitdauer von 60 min bis 10 Tagen beim Lagern weder Risse zeigen, noch zerbrechen.Unexpectedly, compacts are obtained which, during storage for at least 60 minutes to 10 days, do not crack or break during storage.
Deshalb ist ebenfalls Gegenstand der Erfindung das erfindungsgemäß erhaltene Kompaktat, das dadurch gekennzeichnet ist, dass das Kompaktat im Anschluss an die Durchführung des Verfahrens während einer Zeitdauer von 60 min bis 10 Tagen weder Risse zeigt, noch zerbricht.Therefore, the invention also relates to the compactate obtained according to the invention, which is characterized in that the compactate after the implementation of the method for a period of 60 minutes to 10 days, neither cracks, nor breaks.
Falls organische Bindemittel eingesetzt werden, muss der organische Anteil in einem Kalzinierungsschritt vor Einsatz bei der Chlorsilanherstellung entfernt werden. Der Einsatz eines Bindemittels oder eines Gemisches oben genannter Bindemittel hat den Vorteil eines alkalischen pH-Wertes. Denn die Feststoffe aus der Chlorsilanherstellung enthalten aufgrund der vorherrschenden Reaktionsbedingungen im Chlorsilanherstellprozess HCl und hydrolysierbare Silizium-Halogen-Bindungen, die an den Feststoffen anhaften, welche somit einen sauren pH-Wert aufweisen. Dieser wird durch das oder die Bindemittel neutralisiert. Die unangenehme Eigenschaft der Kompaktate, Chlorwasserstoff freizusetzen, kann damit also mindestens teilweise aufgehoben werden.If organic binders are used, the organic portion must be removed in a calcination step prior to use in chlorosilane production. The use of a binder or a mixture of the above-mentioned binder has the advantage of an alkaline pH. Because the solids from the chlorosilane production contain due to the prevailing reaction conditions in Chlororsilanherstellprozess HCl and hydrolyzable silicon-halogen bonds, which adhere to the solids, which thus have an acidic pH. This is neutralized by the binder (s). The unpleasant property of the compacts to liberate hydrogen chloride can thus be at least partially offset.
Das erfindungsgemäße Verfahren wird im Folgenden anhand eines Beispiels näher erläutert.The method according to the invention is explained in more detail below with reference to an example.
Beispiel 1.Example 1.
Das feinkörnige Material aus der Chlorsilanherstellung war Silizium-Asche aus einem Wirbelschichtreaktor.The fine-grained material from chlorosilane production was silicon ash from a fluidized bed reactor.
Es wurde eine hydraulische Stempelpresse eingesetzt. Für jede Pressung wurde an dem Gerät ein Pressdruck aus dem Bereich von 2,3 bis 9,1 kN/cm2 eingestellt, sowie eine Pressgeschwindigkeit von 10 mm/min und eine Entlastungsposition von 10 mm vorgegeben. Die Haltezeit wurde mit 30 Sekunden gewählt, während der der jeweilige Pressdruck ausgeübt wurde.It was used a hydraulic punch press. For each pressing, a pressing pressure of 2.3 to 9.1 kN / cm 2 was set on the device, and a pressing speed of 10 mm / min and a relief position of 10 mm were specified. The holding time was chosen to be 30 seconds during which the respective pressing pressure was exerted.
Die erhaltenen Tabletten wurden unter Stickstoff gelagert und zeigten nach 7 Tagen keine Risse. Somit wiesen diese Kompaktate eine genügend gute Festigkeit auf, um sie in den Reaktor zurückführen zu können.The resulting tablets were stored under nitrogen and showed no cracks after 7 days. Thus, these compactates had sufficient strength to recycle them into the reactor.
ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION
Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.
Zitierte PatentliteraturCited patent literature
- DE 102009037155 B3 [0007] DE 102009037155 B3 [0007]
- DE 102009020143 A1 [0008] DE 102009020143 A1 [0008]
Claims (4)