DE102012018026A1 - Monolithic printing mold for screen printing, has carrier coated with paint layer, and galvanically separated layer made from metal alloy, where galvanically separated layer is higher than paint layer, and completely covers paint layer - Google Patents

Monolithic printing mold for screen printing, has carrier coated with paint layer, and galvanically separated layer made from metal alloy, where galvanically separated layer is higher than paint layer, and completely covers paint layer Download PDF

Info

Publication number
DE102012018026A1
DE102012018026A1 DE201210018026 DE102012018026A DE102012018026A1 DE 102012018026 A1 DE102012018026 A1 DE 102012018026A1 DE 201210018026 DE201210018026 DE 201210018026 DE 102012018026 A DE102012018026 A DE 102012018026A DE 102012018026 A1 DE102012018026 A1 DE 102012018026A1
Authority
DE
Germany
Prior art keywords
layer
lacquer layer
monolithic
printing
printing stencil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE201210018026
Other languages
German (de)
Inventor
Volkmar Zschage
Lutz Engisch
Michael Mäser
Bernd Klebe
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sachsische Walzengravur GmbH
SAECHSISCHE WALZENGRAVUR GmbH
Original Assignee
Sachsische Walzengravur GmbH
SAECHSISCHE WALZENGRAVUR GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sachsische Walzengravur GmbH, SAECHSISCHE WALZENGRAVUR GmbH filed Critical Sachsische Walzengravur GmbH
Priority to DE201210018026 priority Critical patent/DE102012018026A1/en
Publication of DE102012018026A1 publication Critical patent/DE102012018026A1/en
Withdrawn legal-status Critical Current

Abstract

The mold has recesses, and apertures formed in an area of the recesses. A carrier (4) is coated with a paint layer (5), and a galvanically separated layer is made from metal or metal alloy, where the galvanically separated layer is higher than the paint layer, and completely covers the paint layer. Another paint layer is applied on the galvanically separated layer. The paint layers and the carrier are removed such that the mold is realized as the galvanically isolated body made from metal alloy i.e. nickel alloy. An independent claim is also included for a method for manufacturing a monolithic printing mold.

Description

Die Erfindung betrifft monolithische Druckschablonen als galvanisch abgeschiedene Körper und Verfahren zu deren Herstellung.The invention relates to monolithic printing stencils as electrodeposited bodies and to processes for their production.

Druckschablonen und deren Verwendung als Durchdruck sind allgemein bekannt. Der bekannteste Schablonendruck ist der Siebdruck. Die Druckfarbe wird mittels einer Rakel durch die offenen Stellen in Form der Durchbrüche der Schablone auf den zu bedruckenden Gegenstand aufgetragen. Das zu druckende Medium wird durch die Durchbrüche gedruckt.Printing stencils and their use as a through-pressure are well known. The best known stencil printing is screen printing. The ink is applied by means of a doctor blade through the open areas in the form of the breakthroughs of the stencil on the object to be printed. The medium to be printed is printed through the apertures.

Durch die Druckschrift DE 20 2005 007 549 U1 ist eine Druckschablone bekannt. Diese weist mindestens eine Schablonenöffnung für einen Materialdurchtritt eines Druckmediums auf. Die Schablonenöffnung besitzt eine Siebstruktur unter Bildung von stegartigen Strukturbereichen. In die Schablone ist, insbesondere mittels Laserbearbeitung, eine Schablonenöffnung mit einer Siebstruktur eingebracht. Damit ist im Wesentlichen eine Siebdruckform realisiert. Die Schablonenöffnung bestimmt die Menge und die Form des aufzubringenden Druckmediums. Eine Herstellung der Schablone mittels Laserbearbeitung erfordert eine Nachbehandlung, um durch die Bearbeitung hervorgerufene Materialrückstände auf der Schablone zu entfernen.Through the publication DE 20 2005 007 549 U1 a printing stencil is known. This has at least one stencil opening for a material passage of a printing medium. The template opening has a screen structure with the formation of web-like structural areas. In the template, in particular by means of laser processing, a template opening is introduced with a screen structure. This is essentially realized a screen printing form. The template opening determines the amount and shape of the applied print medium. Fabrication of the template by laser processing requires a post-treatment to remove any residual material on the template caused by the processing.

Der in den Patentansprüchen 1 und 12 angegebenen Erfindung liegt die Aufgabe zugrunde, eine Druckschablone mit einer hohen Kanten- und Strukturschärfe zu schaffen.The indicated in the claims 1 and 12 invention has for its object to provide a printing stencil with a high edge and structure sharpness.

Diese Aufgabe wird mit den in den Patentansprüchen 1 und 12 aufgeführten Merkmalen gelöst.This object is achieved with the features listed in the claims 1 and 12.

Die monolithischen Druckschablonen als galvanisch abgeschiedene Körper zeichnen sich insbesondere durch eine hohe Kanten- und Strukturschärfe aus. Dazu weist die monolithische Druckschablone Vertiefungen und Durchbrüche im Bereich der Vertiefungen auf, wobei das eine auf einem Träger mit wenigstens einer entsprechend der Durchbrüche strukturierten Lackschicht höher als die Lackschicht galvanisch abgeschiedene und entsprechend der Vertiefungen bis auf die Lackschicht abgetragene Druckschablone mit entferntem Träger und entfernter Lackschicht ist.The monolithic printing stencils as electrodeposited bodies are characterized in particular by a high edge and structure sharpness. For this purpose, the monolithic printing stencil recesses and openings in the region of the wells, wherein the one on a support with at least one structured according to the apertures lacquer layer higher than the lacquer layer electrodeposited and removed according to the wells down to the lacquer layer stencil printing with removed and removed lacquer layer is.

Die Druckschablone ist damit eine einstückig realisierte Druckschablone. Diese zeichnet sich dadurch aus, dass die Druckschablone Vertiefungen und im Bereich der Vertiefungen angeordnete Durchbrüche aufweist. Die Druckschablone wird dabei so angewandt, dass das Druckmedium über die Durchbrüche in die Vertiefungen und weiter auf den mit dem Druckmedium zu versehenen Gegenstand gelangt. Damit können strukturscharf sehr feine Druckbilder erzeugt werden.The printing stencil is thus an integrally realized printing stencil. This is characterized in that the pressure stencil has depressions and apertures arranged in the region of the depressions. The printing template is thereby applied so that the printing medium passes through the openings in the wells and further on to be provided with the print medium object. This allows very fine print images to be created in a structurally precise manner.

Die Kanten der Druckschablone für die Druckbilder sind dazu strukturscharf und die Abmessungen der Strukturen mit einer Genauigkeit bis einschließlich ±2 μm realisierbar.The edges of the print template for the print images are structurally sharp and the dimensions of the structures can be realized with an accuracy of up to ± 2 μm.

Zur Herstellung einer monolithischen Druckschablone wird nacheinander dazu

  • – ein Träger mit einer ersten Lackschicht beschichtet,
  • – Bereiche der ersten Lackschicht abgetragen, so dass die verbliebene erste Lackschicht die Durchbrüche der Druckschablone sind,
  • – galvanisch eine Schicht aus einem Metall oder einer Metalllegierung abgeschieden, wobei die galvanisch abgeschiedene Schicht höher als die erste Lackschicht ist und die erste Lackschicht vollständig überdeckt,
  • – eine zweite Lackschicht auf die galvanisch abgeschiedene Schicht aufgebracht,
  • – Bereiche der zweiten Lackschicht abgetragen, so dass die verbliebene zweite Lackschicht die Vertiefungen begrenzt,
  • – die durch das Abtragen der zweiten Lackschicht frei liegenden Bereiche der galvanisch abgeschiedenen Schicht geätzt, so dass die verbliebene erste Lackschicht flächig frei geätzt ist, und
  • – sowohl die Lackschichten als auch der Träger entfernt,
so dass die Druckschablone mit Vertiefungen und Durchbrüchen aus der galvanisch abgeschiedenen Schicht als galvanisch abgeschiedener Körper realisiert ist.To produce a monolithic printing stencil is successively thereto
  • A carrier coated with a first lacquer layer,
  • Removed areas of the first lacquer layer, so that the remaining first lacquer layer are the openings of the printing stencil,
  • Galvanically deposited a layer of a metal or a metal alloy, wherein the electrodeposited layer is higher than the first lacquer layer and completely covers the first lacquer layer,
  • A second lacquer layer is applied to the electrodeposited layer,
  • Ablated areas of the second lacquer layer, so that the remaining second lacquer layer delimits the depressions,
  • - etched by the removal of the second lacquer layer exposed areas of the electrodeposited layer, so that the remaining first lacquer layer is free etched surface, and
  • Removing both the lacquer layers and the carrier,
so that the printing stencil with recesses and openings is realized from the electrodeposited layer as a galvanically deposited body.

Die verbliebene nicht geätzte galvanisch abgeschiedene Schicht ist damit die Druckschablone.The remaining non-etched electrodeposited layer is thus the printing stencil.

Vorteilhafte Ausgestaltungen der Erfindung sind in den Patentansprüchen 2 bis 11 und 13 angegeben.Advantageous embodiments of the invention are specified in the claims 2 to 11 and 13.

Nach der Weiterbildung des Patentanspruchs 2 ist die Vertiefung ein Kanal oder eine eine Kontur aufweisende Vertiefung in der Druckschablone zur Realisierung einer aufzubringenden flächigen Schicht. Weiterhin befinden sich im Bereich des Kanalbodens oder des Bodens der eine Kontur aufweisenden Vertiefung beabstandet zueinander angeordnete Durchbrüche zur Zufuhr des die flächige Schicht bildenden Stoffes.According to the embodiment of claim 2, the depression is a channel or a contour having a depression in the printing template for the realization of a flat layer to be applied. Furthermore, located in the region of the channel bottom or the bottom of the contour having a depression spaced from each other arranged openings for the supply of the sheet-forming substance.

Damit wird das Druckmedium in kleinerer Dosis gegenüber einer Öffnung zugeführt, wobei Kanäle oder eine Kontur aufweisende Vertiefungen mit einer Tiefe bis einschließlich 20 μm realisierbar sind. Dementsprechend ist die zu erzielende Strukturhöhe.Thus, the pressure medium is supplied in a smaller dose compared to an opening, wherein channels or a contour having depressions can be realized with a depth up to and including 20 microns. Accordingly, the structure height to be achieved.

Die Vertiefung ist nach der Weiterbildung des Patentanspruchs 3 ein Kanal oder eine eine Kontur aufweisende Vertiefung in der Druckschablone zur Realisierung einer aufzubringenden flächigen Schicht. Wenigstens eine Wand des Kanals oder der Vertiefung weist mindestens bereichsweise wenigstens eine Stufe auf. Weiterhin befinden sich im Bereich des Kanalbodens oder des Bodens der eine Kontur aufweisenden Vertiefung beabstandet zueinander angeordnete Durchbrüche zur Zufuhr des die flächige Schicht bildenden Stoffes. Dadurch besitzt der Kanal oder die eine Kontur aufweisende Vertiefung verschiedene Querschnitte, so dass in ihrer Höhe unterschiedliche Strukturen aufbringbar sind. The recess is according to the embodiment of claim 3, a channel or a contour having depression in the printing template for the realization of a applied sheet-like layer. At least one wall of the channel or the depression has at least one stage at least in regions. Furthermore, located in the region of the channel bottom or the bottom of the contour having a depression spaced from each other arranged openings for the supply of the sheet-forming substance. As a result, the channel or the contour having a recess has different cross sections, so that in height different structures can be applied.

Die Vertiefung ist nach der Weiterbildung des Patentanspruchs 4 anfangs ein Sackloch in der Druckschablone als galvanisch abgeschiedener Körper zur Realisierung eines aufzubringenden Pads. Weiterhin befindet sich im Bereich des Bodens des anfänglichen Sackloches ein Loch als Durchbruch zur Zufuhr des den Pad bildenden Stoffes. Der Durchbruch ist dazu mit einer Querschnittslänge von bis zu einschließlich 50 μm realisierbar.The recess is according to the embodiment of claim 4 initially a blind hole in the stencil as a galvanically deposited body for the realization of an applied pads. Furthermore, located in the region of the bottom of the initial blind hole a hole as a breakthrough for supplying the pad forming substance. The breakthrough can be realized with a cross-sectional length of up to and including 50 μm.

Der Querschnitt des Loches ist nach der Weiterbildung des Patentanspruchs 5 kleiner/gleich dem Querschnitt des anfänglichen Sackloches.The cross section of the hole is according to the embodiment of claim 5 is less than / equal to the cross section of the initial blind hole.

Die Dicke der Druckschablone als galvanisch abgeschiedener Körper ist nach der Weiterbildung des Patentanspruchs 6 gleich/kleiner 100 μm.The thickness of the stencil as a galvanically deposited body is equal to less than 100 microns after the embodiment of claim 6.

Die Dicke der Druckschablone als galvanisch abgeschiedener Körper ist nach der Weiterbildung des Patentanspruchs 7 gleich/größer 50 μm.The thickness of the stencil as a galvanically deposited body is equal to or greater than 50 microns after the embodiment of claim 7.

Die Tiefe des Kanals ist nach der Weiterbildung des Patentanspruchs 8 gleich/kleiner 50 μm.The depth of the channel is equal to less than 50 microns after the embodiment of claim 8.

Der Durchmesser des Loches ist nach der Weiterbildung des Patentanspruchs 9 gleich/größer 5 μm.The diameter of the hole is according to the embodiment of claim 9 equal to / greater than 5 microns.

Die Druckschablone als galvanisch abgeschiedener Körper besteht nach der Weiterbildung des Patentanspruchs 10 aus einem galvanisch abscheidbaren Metall oder einer galvanisch abscheidbaren Metalllegierung, wobei das insbesondere Nickel oder eine Nickellegierung ist.According to the embodiment of claim 10, the stencil as a galvanically deposited body consists of an electrodepositable metal or an electrodepositable metal alloy, in particular nickel or a nickel alloy.

Die Lackschicht ist nach der Weiterbildung des Patentanspruchs 11 eine durch ein Abtragverfahren in Bereichen abgetragene Lackschicht. Das Abtragen erfolgt beispielsweise mittels elektromagnetischer Strahlung. Das kann Laserstrahlung sein.The lacquer layer is according to the embodiment of claim 11 a removed by a removal process in areas paint layer. The removal takes place for example by means of electromagnetic radiation. This can be laser radiation.

Die erste Lackschicht weist nach der Weiterbildung des Patentanspruchs 13 eine Höhe oder wenigstens zwei verschiedene Höhen auf, so dass mittels der Druckschablone Druckschichten einer Höhe oder mindestens zwei Höhen erzeugbar sind.According to the embodiment of claim 13, the first lacquer layer has a height or at least two different heights so that printing layers of a height or at least two heights can be produced by means of the printing stencil.

Ein Ausführungsbeispiel der Erfindung ist in der Zeichnung prinzipiell dargestellt und wird im Folgenden näher beschrieben.An embodiment of the invention is illustrated in principle in the drawing and will be described in more detail below.

Es zeigen dieIt show the

1a bis 1f ein Verfahren zur Herstellung einer monolithischen Druckschablone in schematischen Schnittdarstellungen und 1a to 1f a method for producing a monolithic printing stencil in schematic sectional views and

1g eine schematische Schnittdarstellung einer monolithische Druckschablone. 1g a schematic sectional view of a monolithic printing stencil.

Im nachfolgenden Ausführungsbeispiel werden ein Verfahren zur Herstellung einer monolithischen Druckschablone 1 und eine damit hergestellte monolithische Druckschablone 1 zusammen näher erläutert.In the following embodiment, a method for producing a monolithic printing stencil 1 and a monolithic printing stencil made therewith 1 explained together.

Eine monolithische Druckschablone 1 ist ein galvanisch abgeschiedener Körper mit Vertiefungen 2 und Durchbrüchen 3 im Bereich der Vertiefungen 2.A monolithic print template 1 is a galvanically deposited body with wells 2 and breakthroughs 3 in the area of the depressions 2 ,

Dazu zeigen die
1a bis 1f ein Verfahren zur Herstellung einer monolithischen Druckschablone in schematischen Schnittdarstellungen und
1g eine monolithische Druckschablone jeweils in einer prinzipiellen Darstellung.To show the
1a to 1f a method for producing a monolithic printing stencil in schematic sectional views and
1g a monolithic stencil in each case in a schematic representation.

Die Druckschablone 1 ist eine auf einem Träger 4 mit wenigstens einer entsprechend der Durchbrüche 3 strukturierten ersten Lackschicht 5 höher als die erste Lackschicht 5 galvanisch abgeschiedene und entsprechend der Vertiefungen 2 bis auf die erste Lackschicht 5 abgetragene Schicht 6 als Druckschablone 1 mit entferntem Träger 4 und entfernter erster Lackschicht 5.The printing template 1 is one on a carrier 4 with at least one corresponding to the breakthroughs 3 textured first varnish layer 5 higher than the first lacquer layer 5 electrodeposited and according to the wells 2 except for the first coat of paint 5 worn layer 6 as a printing template 1 with removed carrier 4 and removed first coat of paint 5 ,

Zum Einen ist die Vertiefung 2 ein Kanal 2 oder eine flächige Vertiefung 2 in der Druckschablone 1 zur Realisierung einer aufzubringenden Bahn oder flächigen Schicht mit verschiedenster anwendungsorientierter Kontur. Im Bereich des Bodens der Vertiefung 2 befinden sich beabstandet zueinander angeordnete Durchbrüche 3 zur Zufuhr des die Bahn oder die flächige Schicht bildenden Stoffes.For one thing is the depression 2 a channel 2 or a flat depression 2 in the printing template 1 for the realization of a web to be applied or a flat layer with a wide variety of application-oriented contours. In the area of the bottom of the depression 2 are located spaced apart openings 3 for supplying the material forming the web or the flat layer.

Zum Anderen ist die Vertiefung 2 anfänglich ein Sackloch 2 in der Druckschablone 1 zur Realisierung eines aufzubringenden Pads. Weiterhin befindet sich im Bereich des Bodens des anfänglichen Sackloches 2 ein Loch als Durchbruch 3 zur Zufuhr des den Pad bildenden Stoffes. Der Querschnitt des Loches ist dabei kleiner/gleich dem Querschnitt der Vertiefung 2 in Form de anfänglichen Sackloches 2.The other is the depression 2 initially a blind hole 2 in the printing template 1 for the realization of a pad to be applied. Furthermore, it is located in the area of the bottom of the initial blind hole 2 a hole as a breakthrough 3 for supplying the substance forming the pad. The cross section of the hole is smaller than / equal to the cross section of the recess 2 in the form of the initial blind hole 2 ,

Die Druckschablone 1 weist folgende Abmessungen auf

  • – Dicke der Druckschablone 1 gleich/kleiner 100 μm und geich/größer 50 μm,
  • – Tiefe der Vertiefung 2 gleich/kleiner 50 μm und
  • – Durchmesser des Loches gleich/größer 5 μm.
The printing template 1 has the following dimensions
  • - Thickness of the printing template 1 equal to / less than 100 μm and greater / greater than 50 μm,
  • - Depth of the depression 2 equal to / less than 50 μm and
  • - Diameter of the hole equal to or greater than 5 microns.

Die Druckschablone 1 besteht aus einem galvanisch abscheidbarem Metall oder einer galvanisch abscheidbaren Metalllegierung, wobei das insbesondere Nickel oder eine Nickellegierung ist.The printing template 1 consists of an electrodepositable metal or an electrodepositable metal alloy, which is in particular nickel or a nickel alloy.

Die erste Lackschicht 5 ist eine durch ein Abtragverfahren entsprechend ihrer Struktur Bereiche bildende erste Lackschicht 5. Das Abtragverfahren ist beispielsweise ein Laserabtragverfahren.The first coat of paint 5 is a first paint layer forming by a removal process according to their structure areas 5 , The removal method is, for example, a laser removal method.

Eine Herstellung einer monolithischen Druckschablone 1 erfolgt mit den Schritten:

  • – Beschichten eines Trägers 4 mit einer ersten Lackschicht 5 (Darstellung in der 1a),
  • – Abtragen von Bereichen der ersten Lackschicht 5, so dass die verbliebene erste Lackschicht 5 die Durchbrüche 3 der Druckschablone 1 sind, (Darstellung in der 1b)
  • – galvanisches Abscheiden einer Schicht 6 aus einem Metall oder einer Metalllegierung, wobei die galvanisch abgeschiedene Schicht 6 höher als die erste Lackschicht 5 ist und die erste Lackschicht 5 vollständig überdeckt, (Darstellung in der 1c)
  • – Aufbringen einer zweiten Lackschicht 7 auf die galvanisch abgeschiedene Schicht 6 (Darstellung in der 1d),
  • – Abtragen von Bereichen der zweiten Lackschicht 7, so dass die verbliebene zweite Lackschicht 7 die Vertiefungen begrenzt (Darstellung in der 1e),
  • – Ätzen der durch das Abtragen der zweiten Lackschicht frei liegenden Bereiche der galvanisch abgeschiedenen Schicht 6, so dass die verbliebene erste Lackschicht 5 flächig frei geätzt ist, (Darstellung in der 1f) und
  • – Entfernen sowohl der Lackschichten 5, 7 als auch des Trägers 4, so dass die Druckschablone 1 mit Vertiefungen 2 und Durchbrüchen 3 aus der galvanisch abgeschiedenen Schicht 6 als galvanisch abgeschiedener Körper 1 realisiert ist.
A making of a monolithic print template 1 takes place with the steps:
  • - coating a carrier 4 with a first coat of paint 5 (Presentation in the 1a )
  • - Removal of areas of the first lacquer layer 5 so that the remaining first coat of paint 5 the breakthroughs 3 the printing template 1 are, (representation in the 1b )
  • - Galvanic deposition of a layer 6 of a metal or a metal alloy, wherein the electrodeposited layer 6 higher than the first lacquer layer 5 is and the first coat of paint 5 completely covered, (representation in the 1c )
  • - Apply a second coat of paint 7 on the electrodeposited layer 6 (Presentation in the 1d )
  • - Removal of areas of the second lacquer layer 7 , leaving the remaining second coat of paint 7 the wells limited (representation in the 1e )
  • - Etching the exposed by the removal of the second lacquer layer regions of the electrodeposited layer 6 so that the remaining first coat of paint 5 is free etched surface, (illustration in the 1f ) and
  • - Remove both the paint layers 5 . 7 as well as the carrier 4 so the printing template 1 with depressions 2 and breakthroughs 3 from the electrodeposited layer 6 as a galvanically deposited body 1 is realized.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • DE 202005007549 U1 [0003] DE 202005007549 U1 [0003]

Claims (13)

Monolithische Druckschablone (1) als ein galvanisch abgeschiedener Körper (1) mit Vertiefungen (2) und Durchbrüchen (3) im Bereich der Vertiefungen (2), wobei das eine auf einem Träger (4) mit wenigstens einer entsprechend der Durchbrüche (3) strukturierten Lackschicht (5) höher als die Lackschicht (5) galvanisch abgeschiedene und entsprechend der Vertiefungen (2) bis auf die Lackschicht (5) abgetragene Druckschablone (1) mit entferntem Träger (4) und entfernter Lackschicht (5) ist.Monolithic printing template ( 1 ) as an electrodeposited body ( 1 ) with depressions ( 2 ) and breakthroughs ( 3 ) in the area of the depressions ( 2 ), the one on a support ( 4 ) with at least one corresponding to the breakthroughs ( 3 ) structured lacquer layer ( 5 ) higher than the paint layer ( 5 ) electrodeposited and according to the wells ( 2 ) except for the lacquer layer ( 5 ) ablated printing template ( 1 ) with the carrier removed ( 4 ) and removed paint layer ( 5 ). Monolithische Druckschablone nach Patentanspruch 1, dadurch gekennzeichnet, dass die Vertiefung (2) ein Kanal (2) oder eine eine Kontur aufweisende Vertiefung (2) in der Druckschablone (1) als galvanisch abgeschiedener Körper (1) zur Realisierung einer aufzubringenden flächigen Schicht ist und dass sich im Bereich des Kanalbodens oder des Bodens der eine Kontur aufweisenden Vertiefung (2) beabstandet zueinander angeordnete Durchbrüche (3) zur Zufuhr des die flächige Schicht bildenden Stoffes befinden.Monolithic printing stencil according to claim 1, characterized in that the depression ( 2 ) a channel ( 2 ) or a contoured depression ( 2 ) in the printing template ( 1 ) as a galvanically deposited body ( 1 ) is to realize a flat layer to be applied and that in the region of the channel bottom or the bottom of the contour having recess ( 2 ) spaced from each other breakthroughs ( 3 ) for supplying the sheet-forming substance. Monolithische Druckschablone nach Patentanspruch 1, dadurch gekennzeichnet, dass die Vertiefung (2) ein Kanal (2) oder eine eine Kontur aufweisende Vertiefung (2) in der Druckschablone (1) als galvanisch abgeschiedener Körper (1) zur Realisierung einer aufzubringenden flächigen Schicht ist, dass wenigstens eine Wand des Kanals (2) oder der Vertiefung (2) mindestens bereichsweise wenigstens eine Stufe aufweist und dass sich im Bereich des Kanalbodens oder des Bodens der eine Kontur aufweisenden Vertiefung (2) beabstandet zueinander angeordnete Durchbrüche (3) zur Zufuhr des die flächige Schicht bildenden Stoffes befinden.Monolithic printing stencil according to claim 1, characterized in that the depression ( 2 ) a channel ( 2 ) or a contoured depression ( 2 ) in the printing template ( 1 ) as a galvanically deposited body ( 1 ) for the realization of a surface layer to be applied is that at least one wall of the channel ( 2 ) or the depression ( 2 ) at least partially has at least one step and that in the region of the channel bottom or the bottom of the contour having depression ( 2 ) spaced from each other breakthroughs ( 3 ) for supplying the sheet-forming substance. Monolithische Druckschablone nach Patentanspruch 1, dadurch gekennzeichnet, dass die Vertiefung (2) anfangs ein Sackloch (2) in der Druckschablone (1) als galvanisch abgeschiedener Körper (1) zur Realisierung eines aufzubringenden Pads ist und dass sich im Bereich des Bodens des anfänglichen Sackloches (2) ein Loch (3) als Durchbruch (3) zur Zufuhr des den Pad bildenden Stoffes befindet.Monolithic printing stencil according to claim 1, characterized in that the depression ( 2 ) at first a blind hole ( 2 ) in the printing template ( 1 ) as a galvanically deposited body ( 1 ) is to realize a pad to be applied and that in the region of the bottom of the initial blind hole ( 2 ) a hole ( 3 ) as a breakthrough ( 3 ) for supplying the pad forming substance is. Monolithische Druckschablone nach Patentanspruch 4, dadurch gekennzeichnet, dass der Querschnitt des Loches (3) kleiner/gleich dem Querschnitt des anfänglichen Sackloches (2) ist.Monolithic printing stencil according to claim 4, characterized in that the cross section of the hole ( 3 ) smaller than / equal to the cross section of the initial blind hole ( 2 ). Monolithische Druckschablone nach Patentanspruch 1, dadurch gekennzeichnet, dass die Dicke der Druckschablone (1) als galvanisch abgeschiedener Körper (1) gleich/kleiner 100 μm ist.Monolithic printing stencil according to claim 1, characterized in that the thickness of the printing stencil ( 1 ) as a galvanically deposited body ( 1 ) is equal to / less than 100 μm. Monolithische Druckschablone nach Patentanspruch 1, dadurch gekennzeichnet, dass die Dicke der Druckschablone (1) als galvanisch abgeschiedener Körper (1) gleich/größer 50 μm ist.Monolithic printing stencil according to claim 1, characterized in that the thickness of the printing stencil ( 1 ) as a galvanically deposited body ( 1 ) is equal to / greater than 50 μm. Monolithische Druckschablone nach Patentanspruch 1, dadurch gekennzeichnet, dass die Tiefe des Kanals (2) oder der Vertiefung (2) gleich/kleiner 50 μm ist.Monolithic printing stencil according to claim 1, characterized in that the depth of the channel ( 2 ) or the depression ( 2 ) is equal to / less than 50 μm. Monolithische Druckschablone nach Patentanspruch 4, dadurch gekennzeichnet, dass der Durchmesser des Loches (3) als Durchbruch (3) gleich/größer 5 μm ist.Monolithic printing stencil according to claim 4, characterized in that the diameter of the hole ( 3 ) as a breakthrough ( 3 ) is equal to / greater than 5 μm. Monolithische Druckschablone nach Patentanspruch 1, dadurch gekennzeichnet, dass die Druckschablone (1) als galvanisch abgeschiedener Körper (1) aus einem galvanisch abscheidbaren Metall oder einer galvanisch abscheidbaren Metalllegierung besteht, wobei das insbesondere Nickel oder eine Nickellegierung ist.Monolithic printing stencil according to claim 1, characterized in that the printing stencil ( 1 ) as a galvanically deposited body ( 1 ) consists of an electrodepositable metal or an electrodepositable metal alloy, which is in particular nickel or a nickel alloy. Monolithische Druckschablone nach Patentanspruch 1, dadurch gekennzeichnet, dass die Lackschicht (5, 7) eine durch ein Abtragverfahren in Bereichen abgetragene Lackschicht (5, 7) ist.Monolithic printing stencil according to claim 1, characterized in that the lacquer layer ( 5 . 7 ) a paint layer removed by a removal process in areas ( 5 . 7 ). Verfahren zur Herstellung einer monolithischen Druckschablone (1) als galvanisch abgeschiedener Körper (1) mit den Schritten: – Beschichten eines Trägers (4) mit einer ersten Lackschicht (5), – Abtragen von Bereichen der ersten Lackschicht (5), so dass die verbliebene erste Lackschicht (5) die Durchbrüche (3) der Druckschablone (1) sind, – galvanisches Abscheiden einer Schicht (6) aus einem Metall oder einer Metalllegierung, wobei die galvanisch abgeschiedene Schicht (6) höher als die erste Lackschicht (5) ist und die erste Lackschicht (5) vollständig überdeckt, – Aufbringen einer zweiten Lackschicht (7) auf die galvanisch abgeschiedene Schicht (6), – Abtragen von Bereichen der zweiten Lackschicht (7), so dass die verbliebene zweite Lackschicht (7) die Vertiefungen (2) begrenzt, – Ätzen der durch das Abtragen der zweiten Lackschicht frei liegenden Bereiche der galvanisch abgeschiedenen Schicht (6), so dass die verbliebene erste Lackschicht (5) flächig frei geätzt ist, und – Entfernen sowohl der Lackschichten (5, 7) als auch des Trägers (4), so dass die Druckschablone (1) mit Vertiefungen (2) und Durchbrüchen (3) aus der galvanisch abgeschiedenen Schicht (6) als galvanisch abgeschiedener Körper (1) realisiert ist.Method for producing a monolithic printing stencil ( 1 ) as a galvanically deposited body ( 1 ) comprising the steps of: - coating a carrier ( 4 ) with a first lacquer layer ( 5 ), - removal of areas of the first lacquer layer ( 5 ), so that the remaining first lacquer layer ( 5 ) the breakthroughs ( 3 ) of the printing template ( 1 ), - galvanic deposition of a layer ( 6 ) of a metal or a metal alloy, wherein the electrodeposited layer ( 6 ) higher than the first lacquer layer ( 5 ) and the first lacquer layer ( 5 ) completely covered, - application of a second lacquer layer ( 7 ) on the electrodeposited layer ( 6 ), - removal of areas of the second lacquer layer ( 7 ), so that the remaining second lacquer layer ( 7 ) the depressions ( 2 ), etching the areas of the electrodeposited layer exposed by the removal of the second lacquer layer ( 6 ), so that the remaining first lacquer layer ( 5 ) is free etched surface, and - removing both the paint layers ( 5 . 7 ) as well as the carrier ( 4 ), so that the printing template ( 1 ) with depressions ( 2 ) and breakthroughs ( 3 ) from the electrodeposited layer ( 6 ) as a galvanically deposited body ( 1 ) is realized. Verfahren nach Patentanspruch 12, dadurch gekennzeichnet, dass die erste Lackschicht (5) eine Höhe oder wenigstens zwei verschiedene Höhen aufweist.Method according to claim 12, characterized in that the first lacquer layer ( 5 ) has a height or at least two different heights.
DE201210018026 2012-09-09 2012-09-09 Monolithic printing mold for screen printing, has carrier coated with paint layer, and galvanically separated layer made from metal alloy, where galvanically separated layer is higher than paint layer, and completely covers paint layer Withdrawn DE102012018026A1 (en)