DE102010018110A1 - Multi-layer material for use in composite construction for panels and moldings, has carrier layer of consolidated froth, which comprises two side surfaces - Google Patents

Multi-layer material for use in composite construction for panels and moldings, has carrier layer of consolidated froth, which comprises two side surfaces Download PDF

Info

Publication number
DE102010018110A1
DE102010018110A1 DE102010018110A DE102010018110A DE102010018110A1 DE 102010018110 A1 DE102010018110 A1 DE 102010018110A1 DE 102010018110 A DE102010018110 A DE 102010018110A DE 102010018110 A DE102010018110 A DE 102010018110A DE 102010018110 A1 DE102010018110 A1 DE 102010018110A1
Authority
DE
Germany
Prior art keywords
layer
multilayer material
fabric
coating
resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE102010018110A
Other languages
German (de)
Inventor
Marno Matthäs
Jörg J. Hoffmann
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEMA INVEST GmbH
Original Assignee
BEMA INVEST GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BEMA INVEST GmbH filed Critical BEMA INVEST GmbH
Priority to DE102010018110A priority Critical patent/DE102010018110A1/en
Publication of DE102010018110A1 publication Critical patent/DE102010018110A1/en
Ceased legal-status Critical Current

Abstract

The multi-layer material (1) has a carrier layer (2) of consolidated froth, which comprises two side surfaces, where each of side surfaces is laminated with the fabric layers (3,3'). One fabric layer is provided as decoration layer. The outer surface of the matrix (4) is coated with a transparent coating layer (5).

Description

Die Erfindung betrifft ein Mehrschichtmaterial in Verbundbauweise für Platten und Formkörper nach Oberbegriff des Hauptanspruchs.The invention relates to a multilayer composite material for plates and moldings according to the preamble of the main claim.

Derartige Mehrschichtmaterialien sind in vielfachen Ausführungsformen bekannt und werden beispielsweise zur Herstellung von Fußbodenbelägen, Arbeitsflächen, Decken- und Wandverkleidungen, sowie für Möbel verwendet.Such multilayer materials are known in many embodiments and are used for example for the production of floor coverings, work surfaces, ceiling and wall coverings, as well as for furniture.

Das besagte Mehrschichtmaterial weist eine stabile Trägerschicht auf, die zum Beispiel aus Holzplatten, Spanplatten, Faserplatten oder verdichtetem Schaum bestehen kann. Insbesondere zu Verkleidungs- oder Verlegezwecken ist die Trägerschicht mit großflächig ausgebildeten oberen und unteren Seitenflächen flach ausgeformt. Die Seitenflächen können mit einer zum Beispiel aus Papier, Folie oder Gewebe gebildeten Dekorationsschicht belegt sein, welche mittels einer durchsichtigen Matrix, zum Beispiel aus Harz, auf die Seitenflächen auf laminiert wird. Für die Dekorationsschicht bildet die Matrix zum einen mit ihrer äußeren Oberfläche eine Sichtfläche und zum anderen eine schützende Deckschicht.The said multilayer material has a stable carrier layer, which may consist of, for example, wood panels, chipboard, fiberboard or compressed foam. In particular, for cladding or laying purposes, the carrier layer is formed flat with large area formed upper and lower side surfaces. The side surfaces may be covered with a decorative layer formed, for example, from paper, foil or fabric, which is laminated to the side surfaces by means of a transparent matrix, for example of resin. For the decorative layer, the matrix forms on the one hand with its outer surface a visible surface and on the other a protective cover layer.

Die DE 20 2004 003 214 U1 beschreibt hierzu ein Mehrschichtmaterial, dessen Trägerschicht zumindest einseitig mit einer Gewebeschicht aus Kohlefasern versehen ist, welche mittels einer Kunststoffmatrix auf die Trägerschicht laminiert ist. Hierdurch wird eine durchsichtige Deckschicht zur Präsentation der Gewebeschicht erzeugt, die mittels des besagten Gewebes verstärkt wird, so dass die Deckschicht zusätzlich zur schützenden Funktion eine tragende und festigende Funktion übernimmt. Als Gewebeart können beispielsweise Leinwand-, Köper-, oder Atlasbindungen verwendet werden, die jeweils eine unterschiedliche Optik bieten und der gebildeten Deckschicht einen 3D-Effekt verleihen.The DE 20 2004 003 214 U1 describes for this purpose a multi-layer material, the carrier layer is provided at least on one side with a fabric layer of carbon fibers, which is laminated by means of a plastic matrix on the carrier layer. As a result, a transparent cover layer for presenting the fabric layer is produced, which is reinforced by means of said fabric, so that the cover layer assumes a supporting and fastening function in addition to the protective function. As a type of fabric, for example, can be used canvas, twill, or satin weave, each offering a different look and give the cover layer formed a 3D effect.

Die Aufgabe der Erfindung besteht darin, die funktionellen Eigenschaften der Deckschicht zu verbessern.The object of the invention is to improve the functional properties of the cover layer.

Diese Aufgabe löst die Erfindung mit den Merkmalen des Hauptanspruchs.This object is achieved by the invention with the features of the main claim.

Die Erfindung sieht vor, eine als Dekorationsschicht vorgesehene Gewebeschicht mit einer durchsichtigen Matrix zu versiegeln, deren äußere Sichtfläche mit einer durchsichtigen Überzugsschicht beschichtet ist, welche gegen äußere Einwirkung, insbesondere gegen Strahlungs- und/oder Flüssigkeitseinwirkung, abweisungsfähig ist.The invention provides for sealing a layer of fabric provided as a decorative layer with a transparent matrix whose outer visible surface is coated with a transparent coating layer which is resistant to external influences, in particular to radiation and / or liquid.

Erfindungsgemäß kann die Überzugsschicht beispielsweise gegen UV-Licht beständig sein und eine imprägnierte Oberfläche aufweisen. Mit der erfindungsgemäßen Überzugsschicht wird zusammen mit der Matrix ein Sichtlaminat geschaffen, welches die Gewebeschicht beispielsweise gegen Wettereffekte in verbesserter Weise schützt.According to the invention, the coating layer can be resistant to UV light, for example, and have an impregnated surface. With the coating layer according to the invention, a visual laminate is created together with the matrix, which protects the fabric layer in an improved manner, for example against weather effects.

So kann zum Beispiel die Gewebeschicht insbesondere mit Farbmitteln getönt bzw. lackiert werden, die ohne UV-Schutz schnell ausbleichen würden, mit der erfindungsgemäßen Überzugsschicht aber ihre Farben auch bei starker UV-Strahlung dauerhaft beibehalten können. Zusätzlich kann die äußere Oberfläche der Überzugsschicht beispielsweise eine nach dem Lotuseffekt strukturierte hydrophobe Oberflächenarchitektur aufweisen, wodurch insbesondere die Haftung von Schmutz- und Wasserpartikel minimiert wird.Thus, for example, the fabric layer can be tinted or painted in particular with colorants which would rapidly fade without UV protection, but which can permanently retain their colors even with strong UV radiation with the coating layer according to the invention. In addition, the outer surface of the coating layer may, for example, have a lotus-effect structured hydrophobic surface architecture, thereby minimizing the adhesion of soil and water particles in particular.

Erfindungsgemäß wird eine Sichtfläche für eine zu Dekorativzwecken laminierte Gewebeschicht erzeugt, die gegenüber Wettereinflüssen, wie zum Beispiel starke Sonneneinstrahlung, staubhaltige Winde, Regen usw., einen abweisenden Charakter aufweist, so dass die Gewebeschicht insbesondere länger neu und unverschmutzt erscheint.According to the invention, a visible surface for a decorative layer laminated fabric layer is generated, which against weather influences, such as strong sunlight, dusty winds, rain, etc., has a repellent character, so that the fabric layer appears new and unpolluted especially longer.

Die erfindungsgemäß versiegelte Gewebeschicht kann witterungsbeständig und dauerhaft bei gleich bleibender Optik präsentiert werden.The inventively sealed fabric layer can be weather-resistant and permanently presented with the same appearance.

Vorzugsweise ist die Trägerschicht mit großflächig ausgebildeten gegenüberliegenden Seitenflächen flach ausgeformt.Preferably, the carrier layer is formed flat with large area formed opposite side surfaces.

Jede Seitenfläche ist mit einer Gewebeschicht laminiert. Hierbei wird vorgeschlagen, dass die Gewebeschichten von gleicher Webart sind und gleiche Flächengewichte aufweisen. Hierdurch wird insbesondere ein Mehrschichtmaterial für Verkleidungs- oder Verlegezwecke geschaffen, welches in gleicher Weise beidseitig durch die Gewebeschichten verstärkt werden kann.Each side surface is laminated with a fabric layer. It is proposed that the fabric layers are of the same weave and have the same basis weights. As a result, in particular, a multi-layer material for cladding or laying purposes is created, which can be reinforced in the same way on both sides by the fabric layers.

Wahlweise kann zum Beispiel die äußere Oberfläche einer laminierten Gewebeschicht als Sichtfläche vorgesehen werden, wobei auf der äußeren Oberfläche der anderen laminierten Gewebeschicht ein Abreißgewebe aufgebracht ist. Das Abreißgewebe kann von Hand entfernt werden, sobald die der Sichtfläche gegenüberliegende Rückseite des Mehrschichtmaterials als Verlegeseite genutzt werden soll.Optionally, for example, the outer surface of a laminated fabric layer may be provided as a visible surface with a tear-off fabric applied to the outer surface of the other laminated fabric layer. The tear-off fabric can be removed by hand as soon as the rear face of the multilayer material opposite the visible surface is to be used as the laying side.

Zusätzlich wird das Abreißgewebe erfindungsgemäß genutzt, um beim Trocknungsvorgang ein Verziehen der Trägerschicht auf der gegenüberliegenden Seite zu verhindern. Durch diese Maßnahme kann insbesondere eine plane Oberfläche zum Aufbringen der erfindungsgemäßen Überzugsschicht sichergestellt werden. Die Überzugsschicht kann daher vor oder nach dem Verdichten des Schaums aufgebracht werden.In addition, the tear-off fabric is used according to the invention to prevent warping of the carrier layer on the opposite side during the drying process. By this measure, in particular a flat surface for applying the coating layer according to the invention can be ensured. The coating layer can Therefore, be applied before or after the compression of the foam.

Durch die Erfindung entsteht nach Art einer Sandwichbauweise eine Struktur, die aus einem zentralen formgebendem Bestandteil aus verdichtetem Schaum besteht, welches auf der einen Großfläche durch das Abreißgewebe und auf der anderen Großfläche durch die als Dekorationsschicht dienende Gewebeschicht beschichtet ist.As a result of the invention, a structure is created in the manner of a sandwich construction, which consists of a central shaping component of compressed foam, which is coated on one large surface by the tear-off fabric and on the other large surface by the fabric layer serving as a decorative layer.

Der zentrale verdichtete Schaumkern kann in an sich üblicher Weise zum Beispiel aus den Bestandteilen Polyol und Isozyanat zu Polyurethan extrudiert werden, welches in geeigneter Weise zu Platten weiterverarbeitet wird.The central compressed foam core can be extruded in a conventional manner, for example, from the components polyol and isocyanate to polyurethane, which is suitably processed into plates.

Entsprechende Verfahren gibt es zum Beispiel bei der Herstellung von Trittschall-Dämmplatten oder im Modellbau.Corresponding methods exist, for example, in the production of impact sound insulation boards or in model making.

Diese Platten sind auch unter der Bezeichnung Microbalanceplatten an sich bekannt.These plates are also known as microbalance plates per se.

Alternativ zu den oben genannten Ausgangsmaterialien zur Herstellung von Polyurethanschaum kommt auf Styrodur oder ähnliches in Betracht.As an alternative to the above-mentioned starting materials for producing polyurethane foam, Styrodur or the like can be used.

In jedem Fall ist das so entstehende Sandwichmaterial ausgestattet mit einem formgebenden Stützstoff aus verdichtetem Hartschaum, wobei die Verdichtung des Schaums entweder vor dem Laminieren erfolgt oder auch gleichzeitig mit dem Laminieren, sozusagen wie bei einem „Nass in Nass”-Laminat, erfolgen kann.In any case, the resulting sandwich material is equipped with a forming support made of compressed rigid foam, wherein the compression of the foam either before lamination takes place or at the same time with the lamination, as in a "wet in wet" laminate can take place.

Vorzugsweise wird für den Schaum der Trägerschicht ein Hartschaum verwendet. Die Herstellung des Mehrschichtmaterials kann beispielsweise erfolgen, indem die Trägerschicht, die Gewebeschichten, welche beispielsweise mit Harz und Härter vorgetränkt sein können, und das Abreißgewebe zusammen verdichtet werden.Preferably, a rigid foam is used for the foam of the carrier layer. The production of the multilayer material can be carried out, for example, by compacting the carrier layer, the fabric layers, which may be pre-soaked with resin and hardener, and the tear-off fabric, for example.

Das erfindungsgemäße Mehrschichtmaterial soll insbesondere zur Bildung von Wand- und Bodenplatten im Innen- und Außenbereich eingesetzt werden. Das Mehrschichtmaterial kann beispielsweise zur Bildung von Fliesen, Türen, Arbeitsplatten verwendet werden. Im Besonderen eignet sich das Mehrschichtmaterial auch zum Fliesen von Bad- und Feuchträumen.The multilayer material according to the invention should be used in particular for the formation of wall and floor panels in the interior and exterior. The multi-layer material can be used, for example, to form tiles, doors, worktops. In particular, the multi-layer material is also suitable for tiling bath and wet rooms.

Das erfindungsgemäße Mehrschichtmaterial eignet sich beispielsweise auch zum Beschichten von Möbelstücken, Arbeitsplatten, Toilettensitzen, Blumenkübeln, Türverkleidungen, Zargen, Sockelleisten, Treppenstößen, Wandplatten, Badewannenverkleidungen, rutschfeste Badewannen- sowie Duscheinlagen, Fensterbänken, Innenverkleidungen für Aufzüge sowie insbesondere zur Bildung von hygienischen, sterilen und fugenlosen Wandbeschichtungen im medizinischen Bereich.The multilayer material of the invention is also suitable, for example, for coating furniture, countertops, toilet seats, flower tubs, door panels, frames, baseboards, stairs, wall panels, bathtub coverings, non-slip bath and shower liners, window sills, interior linings for elevators and in particular for the formation of hygienic, sterile and seamless wall coatings in the medical field.

Das Mehrschichtmaterial kann auch auf bereits verlegte herkömmliche Boden- sowie Wandplatten aufgebracht werden bzw. auf verschiedenste Materialien wie zum Beispiel Leder, Tapeten, Keramik, Beton oder Naturstein unlösbar aufgebracht werden.The multi-layer material can also be applied to already laid conventional floor and wall panels or applied to various materials such as leather, wallpaper, ceramics, concrete or natural stone insoluble.

Insbesondere zur Bildung von ebenen Wand- und Bodenplatten, sowie zur Verkleidung von flachen Objektseiten, wird vorgeschlagen, dass das Mehrschichtmaterial zur Bildung von dünnwandigen und ebenen Platten vorgesehen wird, welche eine Dicke von 1 mm bis 8 mm vorzugsweise eine Dicke von 2 mm bis 5 mm, aufweisen.In particular, for the formation of flat wall and floor panels, as well as for covering flat object sides, it is proposed that the multi-layer material is provided for the formation of thin-walled and flat plates having a thickness of 1 mm to 8 mm, preferably a thickness of 2 mm to 5 mm, have.

Die Schmalseiten der dünnwandigen Platten können beispielsweise abgesetzt sein, so dass die Platten spaltfrei aneinander gelegt werden können. Weiterhin können die Platten auf ihren abgesetzten Seiten Bohrungen aufweisen, um die Platten als Wand- oder Bodenplatten auf entsprechende Unterlagen aufschrauben zu können.The narrow sides of the thin-walled plates can be discontinued, for example, so that the plates can be placed against one another gap-free. Furthermore, the plates may have on their remote sides holes in order to screw the plates as wall or floor panels on appropriate documents can.

Die Überzugsschicht kann aus ein- oder mehrlagig aufgebrachten Beschichtungen bestehen. Vorzugsweise ist zumindest eine Beschichtung gegen UV-Licht beständig und die äußere Oberfläche der äußersten Beschichtung nach dem Lotuseffekt hydrophob strukturiert. Jede Schicht kann unterschiedliche gegen äußere Einwirkungen abweisungsfähige Eigenschaften aufweisen, die sich in der erfindungsgemäßen Überzugschicht ergänzen.The coating layer may consist of coatings applied in one or more layers. Preferably, at least one coating is resistant to UV light and the outer surface of the outermost coating after the lotus effect hydrophobic structured. Each layer may have different properties that can be rejected against external influences, which complement each other in the coating layer according to the invention.

So kann beispielsweise für wenigstens eine Beschichtung Klarlack verwendet werden, der gegenüber UV-Licht beständig ist. Als übergeordnete letzte Beschichtung kann ergänzend hierzu eine Lotusbeschichtung vorgesehen werden. Für einen besonders starken UV-Schutz wird vorgeschlagen, dass zumindest drei Beschichtungen der Überzugschicht mit dem UV-Licht beständigem Klarlack hergestellt werden. Zusätzlich kann für die Matrix der Sichtfläche auch ein Harz verwendet werden, das gegenüber UV-Licht beständig ist.Thus, for example, for at least one coating clear coat can be used, which is resistant to UV light. As a superordinate last coating, a lotus coating can additionally be provided for this purpose. For a particularly strong UV protection, it is proposed that at least three coatings of the coating layer be produced with the UV light-resistant clearcoat. In addition, for the matrix of the visible surface, a resin which is resistant to UV light can also be used.

Vorzugweise bestehen die Gewebeschichten aus Glasfasergewebe. Hierbei ist vorgesehen, dass die jeweilige Gewebeschicht aus miteinander verwobenen Schuss- und Kettenfäden besteht, die jeweils von einer Vielzahl flachgelegter und zueinander parallel verlaufender Filamente gebildet werden.Preferably, the fabric layers are made of glass fiber fabric. In this case, it is provided that the respective fabric layer consists of interwoven weft and warp threads which are each formed by a multiplicity of flattened filaments running parallel to each other.

Das Glasfasergewebe ist vorzugsweise farblich getönt bzw. spinndüsengefärbt oder farblich lackiert. Wie auch ein Kohlefasergewebe erfüllt das Glasfasergewebe eine tragende und festigende Funktion. Jedoch kann bezogen auf ein Kohlefasergewebe durch Einsatz des Glasfasergewebes der Materialaufwand wesentlich verringert werden. Das Glasfasergewebe kann beispielsweise derart eingefärbt werden, dass eine dreidimensionale Tiefenwirkung entsteht, die einem Kohlefasergewebe aus flachgelegten Filamenten nahe kommt. Durch die erfindungsgemäße Überzugschicht wird ein Ausbleichen des eingefärbten Gewebes verhindert und durch ihre Selbstreinigungsfähigkeit kann zudem leichter die Sichtfläche der verwendeten Gewebeschicht vor Verschmutzung freigehalten werden.The glass fiber fabric is preferably colored or spinneret dyed or painted. Like a carbon fiber fabric, the glass fiber fabric fulfills a supporting and firming function. However, based on a Carbon fiber fabric by using the fiberglass fabric material costs are significantly reduced. By way of example, the glass fiber fabric can be colored in such a way that a three-dimensional depth effect is produced which approximates a carbon fiber fabric made of flattened filaments. By means of the coating layer according to the invention, bleaching of the dyed fabric is prevented, and its self-cleaning capability also makes it easier to keep the visible surface of the fabric layer used from being contaminated.

Im Folgenden wird die Erfindung anhand von Ausführungsbeispielen näher erläutert.In the following the invention will be explained in more detail by means of exemplary embodiments.

Es zeigen:Show it:

1: die Sichtfläche eines erfindungsgemäßen Mehrschichtmaterials; 1 : the visible surface of a multilayer material according to the invention;

1a: eine Seitenansicht des Mehrschichtmaterials gem. 1 im Vollschnitt; 1a : a side view of the multilayer material acc. 1 in full section;

2: eine schematisch dargestellte Laminiervorrichtung für das Mehrschichtmaterial; 2 a schematically illustrated laminating device for the multilayer material;

3: eine verlegbare Platte aus dem erfindungsgemäßen Mehrschichtmaterial; 3 : a layable plate of the multilayer material according to the invention;

4: ein Verlegebeispiel der Platte gem. 3; 4 : a laying example of the plate acc. 3 ;

5: die Seitenansicht des Verlegebeispiels gem. 4; 5 : the side view of the laying example gem. 4 ;

6: ein weiteres Anwendungsbeispiel für eine Platte aus erfindungsgemäßem Mehrschichtmaterial. 6 : Another application example of a plate made of multilayer material according to the invention.

Sofern im Folgenden nichts anderes gesagt ist, gilt die folgende Beschreibung stets für alle Figuren.Unless otherwise stated below, the following description applies to all figures.

Die Figuren zeigen ein erfindungsgemäßes Mehrschichtmaterial 1 in Verbundbauweise für Platten und Formkörper. Das Mehrschichtmaterial 1 weist eine Trägerschicht 2 aus verdichtetem Schaum auf. Die Trägerschicht 2 weist zwei großflächig ausgebildete obere und untere Seitenflächen auf und ist flach ausgeformt. Die Seitenflächen sind jeweils mit einer oberen und einer unteren Gewebeschicht 3, 3' laminiert. Dies wird insbesondere in 1a gezeigt.The figures show a multilayer material according to the invention 1 in composite construction for plates and moldings. The multi-layer material 1 has a carrier layer 2 made of compressed foam. The carrier layer 2 has two large trained upper and lower side surfaces and is formed flat. The side surfaces are each with an upper and a lower fabric layer 3 . 3 ' laminated. This is especially true in 1a shown.

Die oberen und unteren Gewebeschichten 3, 3' sind jeweils mit einer oberen und einer unteren Matrix 4, 4' versiegelt. In dem gezeigten Beispiel ist die obere Gewebeschicht 3 als Dekorationsschicht vorgesehen und zu diesem Zweck ist zumindest die obere Matrix 4 durchsichtig. Die Matrizen 4, 4' bestehen aus einem Harz, insbesondere aus Polyesterharz. Die durchsichtige obere Matrix 4 bildet mit ihrer äußeren Oberfläche eine Sichtfläche 14. Die Matrizen 4, 4' sind mit den oberen und unteren Gewebeschichten 3, 3' verstärkt, wobei die Gewebeschichten 3, 3' jeweils von gleicher Webart sind und – hier – gleiche Flächengewichte aufweisen. Hierdurch kann das Mehrschichtenmaterial 1 in gleicher Weise beidseitig tragende und festigende Funktionen übernehmen.The upper and lower tissue layers 3 . 3 ' are each with an upper and a lower matrix 4 . 4 ' sealed. In the example shown, the top fabric layer is 3 provided as a decorative layer and for this purpose is at least the upper matrix 4 transparent. The matrices 4 . 4 ' consist of a resin, in particular polyester resin. The transparent upper matrix 4 forms with its outer surface a visible surface 14 , The matrices 4 . 4 ' are with the upper and lower tissue layers 3 . 3 ' reinforced, the tissue layers 3 . 3 ' are each of the same weave and - here - have the same basis weights. This allows the multilayer material 1 in the same way take on both sides carrying and strengthening functions.

Die Matrizen 4, 4' bilden eine Deckschicht, welche die jeweils darunter liegende Gewebeschicht 3, 3' gegen zerstörerische Wirkungen von Außen schützt. Erfindungsgemäß werden die funktionellen Eigenschaften der Deckschicht verbessert, in dem die Sichtfläche 14 der oberen Matrix 4 mit einer durchsichtigen Überzugsschicht 5 beschichtet wird, die gegen äußere Einwirkung, insbesondere gegen Strahlung- und/oder Flüssigkeitseinwirkung, abweisungsfähig ist.The matrices 4 . 4 ' form a cover layer which covers the underlying tissue layer 3 . 3 ' protects against destructive effects from outside. According to the invention, the functional properties of the cover layer are improved, in which the visible surface 14 the upper matrix 4 with a transparent coating layer 5 is coated, which is resistant to external influences, especially against radiation and / or liquid exposure.

Die Überzugsschicht kann beispielsweise gegen UV-Licht beständig sein und eine imprägnierte Oberfläche aufweisen. Die obere Gewebeschicht 3 ist mit einem Färbemittel farblich getönt. Die Gewebeschicht 3 wird durch den UV-Schutz der Überzugsschicht 5 gegen Ausbleichen geschützt. Zusätzlich ist die äußere Oberfläche der Überzugsschicht 5 nach dem Lotuseffekt hydrophob strukturiert, wodurch die Überzugsschicht 5 selbstreinigungsfähig ist. Sowohl UV-Licht als auch Schmutz bzw. Wasserpartikel werden von der Überzugsschicht 5 abgewiesen. Die als Dekorationsschicht vorgesehene Gewebeschicht 3 kann daher dauerhafter bei gleich bleibender Optik präsentiert werden und erscheint länger neuwertig.The coating layer may, for example, be resistant to UV light and have an impregnated surface. The upper fabric layer 3 is tinted with a colorant. The fabric layer 3 is due to the UV protection of the overcoat layer 5 protected against fading. In addition, the outer surface of the coating layer 5 structured according to the lotus effect hydrophobic, whereby the coating layer 5 is self-cleaning. Both UV light and dirt or water particles are from the coating layer 5 rejected. The intended as a decorative layer fabric layer 3 can therefore be presented more permanently with the same appearance and appears longer as new.

Weiterhin zeigt insbesondere 1a, dass auf der äußeren Oberfläche der mit der unteren Matrix 4' laminierten Gewebeschicht 3' ein Abreißgewebe 6 aufgebracht ist. Das Abreißgewebe 6 kann von Hand entfernt werden, sobald diese Seite des Mehrschichtmaterials 1 als Befestigungsseite genutzt werden soll.Furthermore, it shows in particular 1a that on the outer surface of the lower matrix 4 ' laminated fabric layer 3 ' a tear-off fabric 6 is applied. The tear-off fabric 6 Can be removed by hand as soon as this side of the multi-layer material 1 to be used as a mounting side.

Insbesondere in 2 wird ein Ausführungsbeispiel zur Herstellung des Mehrschichtmaterials 1 gezeigt. Die in 1a gezeigten unterschiedlichen Schichten des Mehrschichtmaterials 1 werden in der in 2 gezeigten Laminiervorrichtung 10, z. B. eine Breitschlitzdüse oder ein Rakel, wie folgt eingelegt:
Als erstes wird das Abreißgewebe 6 rücklagig eingelegt, dann folgt die untere Gewebeschicht 3', welche mit dem bereits vorverdichteten Schaum der Trägerschicht 2 überdeckt wird, welcher abschließend mit der oberen Gewebeschicht 3 überdeckt wird. Die jeweiligen Gewebeschichten 3, 3' sind bereits mit der jeweiligen Matrix 4', 4 vorgetränkt, welche jeweils aus einem Harz mit einer oder zwei Komponenten besteht und z. B. bei einem Einkomponentenharz mit einem Härter versehen ist. Mittels der Laminiervorrichtung 10 werden dann die jeweils aufgezählten Schichten des Mehrschichtenmaterials 1 zusammen etwas verdichtet.In particular in 2 is an embodiment for producing the multi-layer material 1 shown. In the 1a shown different layers of the multilayer material 1 be in the in 2 shown laminating device 10 , z. B. a slot die or a doctor blade, inserted as follows:
First, the tear-off fabric 6 inserted in the back, then follows the lower fabric layer 3 ' , which with the already pre-compressed foam of the carrier layer 2 is covered, which concludes with the upper fabric layer 3 is covered. The respective fabric layers 3 . 3 ' are already with the respective matrix 4 ' . 4 pre-soaked, each consisting of a resin with one or two components and z. B. is provided with a hardener in a one-component resin. By means of the laminator 10 then become the enumerated layers of the multilayer material 1 compressed something together.

Hierbei wird erfindungsgemäß das Abreißgewebe 6 genutzt, um beim Trocknungsvorgang ein Verziehen der Trägerschicht 2 zu verhindern. Durch diese Maßnahme kann die erfindungsgemäße Überzugsschicht 5 vor oder nach dem Verdichten aufgebracht werden, da sich insbesondere die Sichtfläche 14 der oberen Matrix 4 beim Trocknen der Trägerschicht 2 nicht verzieht.In this case, according to the invention, the tear-off fabric 6 used to warping the carrier layer during the drying process 2 to prevent. By this measure, the coating layer according to the invention 5 be applied before or after the compression, as in particular the visible surface 14 the upper matrix 4 during drying of the carrier layer 2 do not forgive.

Für den Schaum der Trägerschicht 2 wird vorzugsweise ein Hartschaum verwendet, um dem erfindungsgemäßen Mehrschichtmaterial 1 bei geringem Eigengewicht eine stabile Struktur zu verleihen.For the foam of the carrier layer 2 a rigid foam is preferably used to the multi-layer material according to the invention 1 to give a stable structure at low dead weight.

Die Figuren zeigen, dass das Mehrschichtmaterial 1 zur Bildung von dünnwandigen und ebenen Platten 7 vorgesehen ist. Die Platten 7 weisen eine Dicke von 1 mm bis 8 mm, vorzugsweise eine Dicke von 2 mm bis 5 mm, auf. Die Platten 7 eignen sich hierdurch besonders gut zur Herstellung von stabilen, verlegefertigen Boden- sowie Wandplatten für den Innen- und Außenbereich.The figures show that the multilayer material 1 for the formation of thin-walled and flat plates 7 is provided. The plates 7 have a thickness of 1 mm to 8 mm, preferably a thickness of 2 mm to 5 mm. The plates 7 This makes it particularly suitable for the production of stable, ready-to-lay floor and wall panels for indoor and outdoor use.

Insbesondere die 3, 4 und 5 zeigen eine besondere Ausführungsform einer Platte 7 aus erfindungsgemäßem Mehrschichtmaterial 1. Die Platte 7 ist eben gestaltet, von quadratischer Form und für eine Verlegung bzw. Verkleidung vorbereitet. Jeweils zwei senkrecht zueinander stehende Schmalseiten sind von oben gesehen bezüglich der Überzugsschicht 5 abgesetzt ausgeführt. Durch diese Maßnahme werden schmalbandige, abgesetzte Flachseiten 11 geschaffen, auf deren Oberseite jeweils die Unterseite von komplementären Platten 7 aufgelegt werden können.especially the 3 . 4 and 5 show a particular embodiment of a plate 7 from inventive multi-layer material 1 , The plate 7 is evenly designed, of square shape and prepared for installation or disguise. Two mutually perpendicular narrow sides are seen from above with respect to the coating layer 5 deposed. By this measure are narrow-band, remote flat sides 11 created on the top of each of the underside of complementary plates 7 can be hung up.

4 zeigt hierzu ein Verlegebeispiel. In diesem Beispiel sind insgesamt neun Platten 7 zu einem größeren Quadrat zusammengelegt. Die jeweiligen Stoßkanten der Platten 7 sind fugenlos aneinander gelegt. Dies wird insbesondere in 5 gezeigt. Ebenfalls wird hier gezeigt, dass die jeweiligen Überzugsschichten 5 der verlegten Platten 7 bündig aneinandergereiht sind. 4 shows a laying example. In this example, there are a total of nine plates 7 merged into a larger square. The respective edges of the plates 7 are seamlessly put together. This is especially true in 5 shown. It is also shown here that the respective coating layers 5 the laid plates 7 are lined up flush.

Die abgesetzten Flachseiten 11 sind mit Bohrungen 12 für Schrauben 13 versehen. Als Schrauben 13 werden vorzugsweise Senkschrauben vorgesehen, mit welchen die Platten 7 beispielsweise auf entsprechend vorbereiteten Mauerwerk befestigt werden können.The remote flat sides 11 are with holes 12 for screws 13 Mistake. As screws 13 are preferably provided countersunk screws with which the plates 7 for example, can be mounted on appropriately prepared masonry.

Insbesondere 1a zeigt, dass die Überzugschicht 5 aus mehrlagig aufgebrachten Beschichtungen 8 besteht. Zumindest eine Beschichtung 8 ist gegen UV-Licht beständig. Die äußere Oberfläche 9 der äußersten Beschichtung 8 ist nach dem Lotuseffekt hydrophob strukturiert. Jede Beschichtung 8 der Überzugsschicht 5 kann in unterschiedlicher Weise gegenüber äußeren Einwirkungen abweisungsfähig sein. Die abweisungsfähigen Eigenschaften der Beschichtungen 8 können sich in der Überzugsschicht 5 ergänzen und insbesondere bei zunehmender Anzahl der Beschichtungen 8 auch verstärken, sowie gegenseitig in ihrer Wirkung unterstützen.Especially 1a shows that the coating layer 5 from multilayer applied coatings 8th consists. At least one coating 8th is resistant to UV light. The outer surface 9 the outermost coating 8th is structured hydrophobically after the lotus effect. Every coating 8th the coating layer 5 can be repudiated in different ways to external influences. The repellent properties of the coatings 8th can be in the overcoat layer 5 complement and especially with increasing number of coatings 8th also reinforce and support each other in their effect.

In dem in 1a gezeigten Beispiel besteht die Überzugschicht 5 aus insgesamt 3 Beschichtungen 8, von denen wenigstens eine gegen UV-Licht beständig ist, eine weitere z. B. der Erzielung von Farbeffekten dient und die äußere den Lotuseffekt hervorruft.In the in 1a The example shown, the coating layer 5 from a total of 3 coatings 8th of which at least one is resistant to UV light, another z. B. the achievement of color effects and the outer causes the lotus effect.

In dem in 1a gezeigten Beispiel werden die unteren Beschichtungen 8 von einem Klarlack gebildet, der gegenüber UV-Licht beständig ist. Der für die jeweilige Beschichtung 8 verwendete Klarlack kann jeweils unterschiedliche Abweisungsgrade gegenüber UV-Licht aufweisen. Ergänzend hierzu ist darüber hinaus die obere Matrix 4 der Sichtfläche 14 aus einem Harz, welches gegenüber UV-Licht beständig ist.In the in 1a Example shown are the lower coatings 8th formed by a clearcoat, which is resistant to UV light. The one for the respective coating 8th used clearcoat can each have different degrees of repellency to UV light. In addition to this is beyond the upper matrix 4 the visible surface 14 made of a resin that is resistant to UV light.

Die oberste Beschichtung 8 der Überzugschicht 5 besteht aus einer Lotusschicht.The topmost coating 8th the coating layer 5 consists of a lotus layer.

Die oberen und unteren Gewebeschichten 3, 3' bestehen aus einem Glasfasergewebe.The upper and lower tissue layers 3 . 3 ' consist of a fiberglass fabric.

Die Gewebeschichten 3, 3' bestehen aus miteinander verwobenen Schuss- und Kettenfäden, welche jeweils von einer Vielzahl flach gelegter und zueinander parallel verlaufender Filamente gebildet werden. Dies wird insbesondere in 1 und in 3 dargestellt. Durch diese Maßnahme entsteht ein 3D-Gewebe mit irisierender Tiefenwirkung.The fabric layers 3 . 3 ' consist of interwoven weft and warp threads, which are each formed by a plurality of flat laid and mutually parallel filaments. This is especially true in 1 and in 3 shown. This measure creates a 3D fabric with an iridescent depth effect.

Insbesondere in 6 werden für die aus erfindungsgemäßem Mehrschichtmaterial 1 bestehenden Platten 7 verschiedene Verwendungsmöglichkeiten gezeigt. Die Platten 7 werden insbesondere zur Verkleidung von Schränken, zur Schaffung von Arbeitsplatten, und als Boden- und Wandbelag verwendet.In particular in 6 be for the inventive multi-layer material 1 existing panels 7 various uses shown. The plates 7 are used in particular for the cladding of cabinets, for the creation of countertops, and as a floor and wall covering.

Hierbei ist zu erkennen, dass die Platten 7 für den Wand- und Bodenbelag eine fliesenförmige Form aufweisen. Dies gilt ebenfalls für die dort dargestellte Arbeitsplatte 15. Weiterhin wird in 6 gezeigt, dass zur Bildung der Arbeitsplatte 15 die jeweiligen Platten 7 aus erfindungsgemäßem Mehrschichtmaterial 1 zugeschnitten sind.Here it can be seen that the plates 7 have a tile-like shape for the wall and floor covering. This also applies to the worktop shown there 15 , Furthermore, in 6 shown that to form the countertop 15 the respective plates 7 from inventive multi-layer material 1 are tailored.

Zur Verkleidung der in 6 dargestellten Schranktüren 16, ist eine Platte 7 aus dem Mehrschichtmaterial 1 einstückig an die sichtbare Oberfläche der Schranktür 16 angepasst.To disguise the in 6 shown cabinet doors 16 , is a plate 7 from the Multi-layer material 1 in one piece to the visible surface of the cabinet door 16 customized.

BezugszeichenlisteLIST OF REFERENCE NUMBERS

11
MehrschichtmaterialMulti-layer material
22
Trägerschichtbacking
33
obere Gewebeschichtupper fabric layer
3'3 '
untere Gewebeschichtlower fabric layer
44
obere Matrixupper matrix
4'4 '
untere Matrixlower matrix
55
Überzugsschichtcoating layer
66
AbreißgewebePeel ply
77
Ebene PlatteLevel plate
88th
Beschichtungcoating
99
äußere Oberflächeouter surface
1010
Laminiervorrichtunglaminating
1111
abgesetzte Flachseiteremote flat side
1212
Bohrungdrilling
1313
Schraubescrew
1414
Sichtflächeviewing area
1515
Arbeitsplattecountertop
1616
Schranktürcabinet door

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • DE 202004003214 U1 [0004] DE 202004003214 U1 [0004]

Claims (12)

Mehrschichtmaterial (1) in Verbundbauweise für Platten und Formkörper, mit einer Trägerschicht (2) aus verdichtetem Schaum, die zwei Seitenflächen aufweist, wobei jede der Seitenflächen mit einer Gewebeschicht (3, 3') laminiert ist und wobei zumindest eine Gewebeschicht (3, 3') als Dekorationsschicht vorgesehen ist und zu diesem Zweck mit einer durchsichtigen Matrix (4) versiegelt ist, die mit ihrer äußeren Oberfläche eine Sichtfläche (14) bildet, dadurch gekennzeichnet, dass die äußere Oberfläche der Matrix (4) mit einer durchsichtigen Überzugsschicht (5) beschichtet ist, die gegen äußere Einwirkung, insbesondere gegen Strahlungs- und/oder Flüssigkeitseinwirkung, abweisungsfähig ist.Multilayer material ( 1 ) in composite construction for plates and moldings, with a carrier layer ( 2 ) of compressed foam having two side surfaces, each of the side surfaces having a fabric layer ( 3 . 3 ' ) and wherein at least one fabric layer ( 3 . 3 ' ) is provided as a decoration layer and for this purpose with a transparent matrix ( 4 ), which with its outer surface has a visible surface ( 14 ), characterized in that the outer surface of the matrix ( 4 ) with a transparent coating layer ( 5 ) is coated, which is resistant to external influences, especially against radiation and / or liquid exposure. Mehrschichtmaterial (1) nach Anspruch 1, dadurch gekennzeichnet, dass auf der äußeren Oberfläche der anderen laminierten Gewebeschicht (3', 3) ein Abreißgewebe (6) aufgebracht ist.Multilayer material ( 1 ) according to claim 1, characterized in that on the outer surface of the other laminated fabric layer ( 3 ' . 3 ) a tear-off fabric ( 6 ) is applied. Mehrschichtmaterial (1) nach Anspruch 3, dadurch gekennzeichnet, dass das Abreißgewebe (6) beim Trocknungsvorgang ein Verziehen der Trägerschicht (2) verhindert.Multilayer material ( 1 ) according to claim 3, characterized in that the tear-off fabric ( 6 ) during the drying process a distortion of the carrier layer ( 2 ) prevented. Mehrschichtmaterial (1) nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass das Mehrschichtmaterial (1) zur Bildung von dünnwandigen und ebenen Platten (7) vorgesehen ist.Multilayer material ( 1 ) according to one of claims 1 to 3, characterized in that the multilayer material ( 1 ) for the formation of thin-walled and flat plates ( 7 ) is provided. Mehrschichtmaterial (1) nach Anspruch 4, dadurch gekennzeichnet, dass die Platten (7) eine Dicke von 1 mm bis 8 mm, vorzugsweise eine Dicke von 2 mm bis 5 mm, aufweisen.Multilayer material ( 1 ) according to claim 4, characterized in that the plates ( 7 ) have a thickness of 1 mm to 8 mm, preferably a thickness of 2 mm to 5 mm. Mehrschichtmaterial (1) nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass die Überzugsschicht (5) aus ein- oder mehrlagig aufgebrachten Beschichtungen (8) besteht, wobei zumindest eine Beschichtung (8) gegen UV-Licht beständig ist und die äußere Oberfläche (9) der äußersten Beschichtung (8) nach dem Lotuseffekt hydrophob strukturiert ist.Multilayer material ( 1 ) according to one of claims 1 to 5, characterized in that the coating layer ( 5 ) of single or multi-layer coatings ( 8th ), wherein at least one coating ( 8th ) is resistant to UV light and the outer surface ( 9 ) of the outermost coating ( 8th ) is hydrophobic after the lotus effect. Mehrschichtmaterial (1) nach Anspruch 6, dadurch gekennzeichnet, dass für wenigstens eine Beschichtung (8) Klarlack verwendet wird, der gegenüber UV-Licht beständig ist.Multilayer material ( 1 ) according to claim 6, characterized in that for at least one coating ( 8th ) Is used, which is resistant to UV light. Mehrschichtmaterial (1) nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass zumindest für die Matrix (4, 4') der Sichtfläche ein Harz verwendet wird, dass gegenüber UV-Licht beständig ist.Multilayer material ( 1 ) according to one of claims 1 to 7, characterized in that at least for the matrix ( 4 . 4 ' ) of the visible surface a resin is used, which is resistant to UV light. Mehrschichtmaterial (1) nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass die Gewebeschichten (3, 3') aus Glas- oder Kohlefasergewebe bestehen.Multilayer material ( 1 ) according to one of claims 1 to 8, characterized in that the fabric layers ( 3 . 3 ' ) consist of glass or carbon fiber fabric. Mehrschichtmaterial (1) nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass zumindest die im Gebrauchszustand sichtbare Gewebeschicht (3, 3') farbig lackiert ist.Multilayer material ( 1 ) according to one of claims 1 to 9, characterized in that at least the tissue layer visible in the use state ( 3 . 3 ' ) is painted in color. Mehrschichtmaterial (1) nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass für den Schaum der Trägerschicht (2) Hartschaum verwendet wird.Multilayer material ( 1 ) according to one of claims 1 to 10, characterized in that for the foam of the carrier layer ( 2 ) Hard foam is used. Mehrschichtmaterial (1) nach einem der Ansprüche 1 bis 11, dadurch gekennzeichnet, dass die Gewebeschicht (3, 3') aus miteinander verwobenen Schuss- und Kettenfäden besteht, welche jeweils von einer Vielzahl flachgelegter und zueinander parallel verlaufender Filamente gebildet werden.Multilayer material ( 1 ) according to one of claims 1 to 11, characterized in that the fabric layer ( 3 . 3 ' ) consists of interwoven weft and warp threads, which are each formed by a plurality of flattened and mutually parallel filaments.
DE102010018110A 2010-04-24 2010-04-24 Multi-layer material for use in composite construction for panels and moldings, has carrier layer of consolidated froth, which comprises two side surfaces Ceased DE102010018110A1 (en)