DE102008026965A1 - Drive belt i.e. ribbed drive belt, has force transmission zone provided with flock support, where adhesion of flock support within force transmission zone takes place via chlorine paraffin solution that comprises specific chlorine content - Google Patents

Drive belt i.e. ribbed drive belt, has force transmission zone provided with flock support, where adhesion of flock support within force transmission zone takes place via chlorine paraffin solution that comprises specific chlorine content Download PDF

Info

Publication number
DE102008026965A1
DE102008026965A1 DE200810026965 DE102008026965A DE102008026965A1 DE 102008026965 A1 DE102008026965 A1 DE 102008026965A1 DE 200810026965 DE200810026965 DE 200810026965 DE 102008026965 A DE102008026965 A DE 102008026965A DE 102008026965 A1 DE102008026965 A1 DE 102008026965A1
Authority
DE
Germany
Prior art keywords
drive belt
rubber
transmission zone
flock
paraffin solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE200810026965
Other languages
German (de)
Inventor
Henning Dr. Kanzow
Claus-Lüder Mahnken
Reinhard Dr. Teves
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ContiTech Antriebssysteme GmbH
Original Assignee
ContiTech Antriebssysteme GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ContiTech Antriebssysteme GmbH filed Critical ContiTech Antriebssysteme GmbH
Priority to DE200810026965 priority Critical patent/DE102008026965A1/en
Publication of DE102008026965A1 publication Critical patent/DE102008026965A1/en
Withdrawn legal-status Critical Current

Abstract

The belt (1) has an elastic base body comprising a rubber component, a covering layer (2) and a substructure (5) with a force transmission zone (8). The substructure exhibits a v-ribbed structure formed of ribs (6) and grooves (7). The zone is provided with a flock support (9), where adhesion of the flock support within the force transmission zone takes place via a short or middle chain chlorine paraffin solution. The chlorine paraffin solution comprises a chlorine content that ranges from 10 to 70 percentage. The flock support comprises cotton wool, aramide or cellulose. An independent claim is also included for a method for manufacturing a drive belt.

Description

Die Erfindung betrifft einen Antriebsriemen mit einem elastischen Grundkörper, umfassend eine Decklage und einen Unterbau mit einer Kraftübertragungszone, wobei die Kraftübertragungszone mit einer Flockauflage versehen ist, wobei die Anhaftung der Flockauflage innerhalb der Kraftübertragungszone mittels einer Lösung erfolgt.The The invention relates to a drive belt with an elastic body, comprising a cover layer and a substructure with a power transmission zone, wherein the power transmission zone with a flock pad is provided, wherein the adhesion of the flock pad within the Power transmission zone by means of a solution.

Antriebsriemen, die auch als Kraftübertragungsriemen bezeichnet werden und im Funktionszustand endlos geschlossen sind, können als Flachriemen, Keilriemen, Keilrippenriemen und Zahnriemen ausgebildet sein. Von besonderer Bedeutung ist der Keilrippenriemen, wobei diesbezüglich insbesondere auf folgende Patentliteratur verwiesen wird:

  • DE 38 23 157 A1
  • DE 100 16 351 A1
  • DE 10 2006 007 509 A1
  • EP 0 590 423 A2
  • EP 0 737 228 B1
  • EP 0 831 247 B1
  • EP 0 866 834 B1
  • EP 1 108 750 A1
  • EP 1 129 308 B1
  • US 3 981 206
Drive belts, which are also referred to as power transmission belts and are closed endlessly in the functional state, can be designed as flat belts, V-belts, V-ribbed belts and toothed belts. Of particular importance is the V-ribbed belt, reference being made in this regard in particular to the following patent literature:
  • DE 38 23 157 A1
  • DE 100 16 351 A1
  • DE 10 2006 007 509 A1
  • EP 0 590 423 A2
  • EP 0 737 228 B1
  • EP 0 831 247 B1
  • EP 0 866 834 B1
  • EP 1 108 750 A1
  • EP 1 129 308 B1
  • US 3,981,206

Die Elastizität unter Einbezug der Biegeelastizität eines Antriebsriemens wird dadurch erreicht, dass der Grundkörper und somit die Decklage und der Unterbau aus einem polymeren Werkstoff mit elastischen Eigenschaften bestehen, wobei hier insbesondere die beiden Werkstoffgruppen Elastomere und thermoplastische Elastomere (TPE) zu nennen sind.The Elasticity including flexural elasticity a drive belt is achieved in that the main body and thus the top layer and the base of a polymeric material consist of elastic properties, in particular here the two material groups elastomers and thermoplastic elastomers (TPE) are to be called.

Der elastische Grundkörper ist ferner zumeist noch mit einem eingebetteten Festigkeitsträger bzw. Zugträger versehen, der ein- oder mehrlagig ausgeführt sein kann.Of the Elastic body is also mostly with a embedded reinforcements or tension members provided, which can be implemented in one or more layers.

Antriebsriemen werden zur Geräuschreduzierung wie auch zur Erhöhung der Abriebsbeständigkeit im Bereich der Kraftübertragungszone mit einer Flockauflage, beispielsweise nach der Offenlegungsschrift DE 38 23 157 A1 , oder mit einer Textilauflage (Gewebe, Gewirke, Gestrick), beispielsweise nach der Patentschrift US 3 981 206 , versehen.Drive belts are used for noise reduction as well as for increasing the abrasion resistance in the area of the force transmission zone with a flock coating, for example according to the published patent application DE 38 23 157 A1 , or with a textile cover (fabric, knitted fabric, knitted fabric), for example according to the patent US 3,981,206 , Mistake.

Bei Antriebsriemen auf Basis eines Chloropren-Kautschuks (CR) kann die Flockauflage dadurch gebildet werden, dass nach der Wickelkonfektion und dem Besprühen mit einfachen Lösungsmitteln, beispielsweise mit Xylol, der Riemenrohling mit Baumwolle oder anderen Flockmaterialien beflockt wird. Danach wird der Riemenrohling vulkanisiert. Anschließend werden die Oberflächen gebürstet. Die so erhaltenen Antriebsriemen weisen im Betrieb bei den meisten Motoren sowohl nass als auch trocken keine unerwünschten Geräusche auf.at Drive belt based on a chloroprene rubber (CR), the Flocking pad can be formed by wrapping and spraying with simple solvents, for example with xylene, the belt blank with cotton or others Flock materials is flocked. Thereafter, the belt blank is vulcanized. Then the surfaces are brushed. The drive belts thus obtained have the most in operation Engines both wet and dry are not unwanted Noises on.

Seit einigen Jahren werden jedoch Antriebsriemen auf Basis eines Ethylen-Propylen-Dien-Mischpolymerisates (EPDM) wegen der besseren Haltbarkeit bevorzugt. Bei EPDM-Antriebsriemen reicht jedoch die Beschichtung aus einem einfachen Lösemittel und beispielsweise Baumwollflock nicht aus, um einen hinreichenden Schutz gegen Geräusche zu bieten. Deswegen wird hier eine Lösung eingesetzt, die Komponenten aus Teflon und Polyurethan enthält. Die anderen Schritte, nämlich Flockbildung, Vulkanisation und Bürsten sind gleich.since Some years, however, drive belts based on an ethylene-propylene-diene copolymer (EPDM) preferred for better durability. For EPDM drive belts However, the coating is sufficient from a simple solvent and, for example, cotton flock is insufficient to provide sufficient To provide protection against noise. That's why one here Solution used, the components of Teflon and polyurethane contains. The other steps, namely flocculation, Vulcanization and brushing are the same.

Da die zusätzliche teflonhaltige Beschichtung teuer ist, wird hier auf den Einsatz von Textilauflagen zurückgegriffen. Nach der Patentschrift US 3 981 206 kommt dabei eine gestrickte Textilauflage aus synthetischen Plastikmaterialien, insbesondere Garnen aus zwei synthetischen Plastikmaterialien, zum Einsatz. Der Nachteil hier ist jedoch wiederum, dass auf einem Prüfmotor bei Feuchtigkeit Geräusche entstehen. Außerdem sind Gestricke teuer.Since the additional teflon-containing coating is expensive, the use of textile supports is used here. According to the patent US 3,981,206 In this case, a knitted textile cover made of synthetic plastic materials, in particular yarns of two synthetic plastic materials, is used. The disadvantage here, however, is that noise is generated on a test engine when it is damp. In addition, knits are expensive.

Unter Vermeidung der oben genannten Nachteile zeichnet sich der neue Antriebsriemen mit Flockauflage dadurch aus, dass bei der Bildung der Flockauflage eine Chlorparaffinlösung zum Einsatz gelangt.Under Avoidance of the above-mentioned disadvantages is the new drive belt with Flockauflage characterized in that in the formation of the flock pad a chlorinated paraffin solution is used.

Die Chlorparaffinlösung besitzt einen Chlorgehalt von 10 bis 70%, insbesondere 15 bis 70%, insbesondere wiederum 30 bis 70%. Der besonders bevorzugte Chlorgehalt beträgt 40 bis 50%. Chlorparaffine sind chemikalien- und lichtbeständig, temperaturbeständig bis etwa 200°C, vergleichsweise wenig flüchtig und schwer entflammbar.The chlorinated paraffin solution has a chlorine content of 10 to 70%, in particular 15 to 70%, in particular again 30 to 70%. The most preferred chlorine content is 40 to 50%. Chloroparaffins are resistant to chemicals and light, temperature resistant up to 200 ° C, comparatively low volatility and hardly inflammable.

Ihre Einteilung erfolgt entsprechend der Kettenlänge in langkettige (>C17), mittelkettige (C14 bis C17) und kurzkettige (C10 bis C13) Chlorparaffine. Kurz- und mittelkettige Chlorparaffine, die bevorzugt eingesetzt werden, haben eine ölige Konsistenz, während sich langkettige Produkte durch eine feste, wachsartige Konsistenz auszeichnen.Their classification is carried out according to the chain length in long-chain (> C 17 ), medium-chain (C 14 to C 17 ) and short-chain (C 10 to C 13 ) chlorinated paraffins. Short- and medium-chain chloroparaffins, which are preferably used, have an oily consistency, while long-chain products are characterized by a solid, waxy consistency.

Eine weitere Aufgabe besteht darin, ein Verfahren zur Herstellung eines Antriebsriemens, insbesondere Keilrippenriemens, bereitzustellen, bei dem die eingangs genannten Nachteile nicht auftreten, und zwar unter dem Aspekt der Wirtschaftlichkeit.A Another object is to provide a method for producing a Drive belt, in particular V-ribbed belt, provide in which the aforementioned disadvantages do not occur, under the aspect of economy.

Gelöst wird diese Aufgabe durch wenigstens folgende Verfahrensschritte:

  • – der unvulkanisierte Grundkörper des Riemenrohlings wird innerhalb der Kraftübertragungszone mit einer Chlorparaffinlösung behandelt;
  • – die mit der Chlorparaffinlösung behandelte Kraftübertragungszone wird unter Bildung einer Flockauflage beflockt;
  • – anschließend wird der Riemenrohling vulkanisiert.
This problem is solved by at least the following method steps:
  • - The unvulcanized body of the belt blank is treated within the power transmission zone with a chlorinated paraffin solution;
  • The power-transfer zone treated with the chloro-paraffin solution is flocked to form a flock deposit;
  • - Then the belt blank is vulcanised.

Hinsichtlich Details der Chlorparaffinlösung wird auf das oben Erwähnte verwiesen.Regarding Details of the chlorinated paraffin solution is mentioned above directed.

Die Beflockung erfolgt dabei insbesondere elektrostatisch. Hinsichtlich weiterer Verfahrensschritte, beispielsweise des Bürstens der Flockauflage, wird auf den eingangs erwähnten Stand der Verfahrenstechnik Bezug genommen.The Flocking is carried out in particular electrostatically. Regarding further process steps, such as brushing the flock pad is on the stand mentioned above the process engineering reference.

Im folgenden wird ein Vergleichsversuch vorgestellt. Zwei EPDM-Keilrippenriemen mit Baumwollflock wurden jeweils mit der gleichen Menge Xylol bzw. einer Chlorparaffinlösung behandelt, beispielsweise besprüht, und ohne (trocken) und mit Wasser (nass) auf dem Geräuschprüfstand GPS2 auf das Geräuschverhalten bei verschiedenen Scheibenschiefstellungen (0, 1, 2°) untersucht, wobei die Ergebnisse in zwei Tabellen festgehalten sind: Tabelle 1 GPSE2 (Trocken-20 ml/min·30 sec-Trocken) Kriterien Xylol Bewertung Chlorparaffinlösung Bewertung Trocken (0°) ++ ++ Nass (0°) - ++ Trocken (1°) ++ ++ Nass (1°) -- ++ Trocken (2°) + ++ Nass (2°) -- + Tabelle 2 GPSE2 (Trocken-300 ml/min·30 sec-Trocken) Kriterien Xylol Bewertung Chlorparaffinlösung Bewertung Trocken (0°) ++ ++ Nass (0°) - ++ Trocken (1°) ++ ++ Nass (1°) -- 0 Trocken (2°) + ++ Nass (2°) -- + In the following a comparative experiment is presented. Two EPDM V-ribbed ribbons with cotton flock were each treated with the same amount of xylene or a chlorinated paraffin solution, for example sprayed, and without (dry) and with water (wet) on the GPS2 noise tester, on the noise behavior at different disc misalignments (0, 1, 2 ° The results are shown in two tables: Table 1 GPSE2 (dry 20 ml / min x 30 sec dry) criteria Xylene rating Chlorinated paraffin solution evaluation Dry (0 °) ++ ++ Wet (0 °) - ++ Dry (1 °) ++ ++ Wet (1 °) - ++ Dry (2 °) + ++ Wet (2 °) - + Table 2 GPSE2 (dry 300 ml / min x 30 sec dry) criteria Xylene rating Chlorinated paraffin solution evaluation Dry (0 °) ++ ++ Wet (0 °) - ++ Dry (1 °) ++ ++ Wet (1 °) - 0 Dry (2 °) + ++ Wet (2 °) - +

Der Chlorgehalt der Chlorparaffinlösung betrug dabei jeweils etwa 44%.Of the Chlorine content of the chlorinated paraffin solution was in each case about 44%.

Hinsichtlich der Bewertung des Geräuschverhaltens bedeuten in den Tabellen 1 und 2:

  • sehr gut (++)
  • gut (+)
  • mittel (0)
  • schlecht (-)
  • sehr schlecht (--)
With regard to the evaluation of the noise behavior, in Tables 1 and 2:
  • very good (++)
  • good (+)
  • medium (0)
  • bad (-)
  • very bad (--)

Wie der Vergleichsversuch unter dem Aspekt des Geräuschverhaltens veranschaulicht, schneidet der EPDM-Keilrippenriemen mit Baumwollflock unter Einsatz einer Chlorparaffinlösung im Nasszustand in überraschender Weise wesentlich besser ab als der gleiche Antriebsriemen unter Einsatz von Xylol. Es wird dabei vermutet, dass die Chlorparaffinlösung die Anhaftung des Baumwollflocks an die EPDM-Mischung begünstigt.As the comparative experiment under the aspect of noise behavior As illustrated, the EPDM V-ribbed belt cuts with cotton flock using a wet chlorinated paraffin solution surprisingly much better than the same Drive belt using xylene. It is assumed that the chlorinated paraffin solution attaches to the cotton flock favors the EPDM blend.

Auch wenn der schwerpunktmäßige Einsatz dieser Chlorparaffinlösung bei der Herstellung von EPDM-Antriebsriemen liegt, so ist dieser neue Lösungseinsatz auch für andere Kautschukmischungen anwendbar. Das gleiche gilt auch für andere Flockmaterialien, beispielsweise Aramidflock.Also if the focus of this chlorinated paraffin solution in the production of EPDM drive belts, this is new solution insert also for other rubber compounds applicable. The same applies to other flock materials, for example aramid flock.

Die Erfindung wird nun anhand eines Ausführungsbeispieles unter Bezugnahme auf eine schematische Querschnittsdarstellung beschrieben.The Invention will now be based on an embodiment below Referring to a schematic cross-sectional view described.

Die einzige Figur zeigt einen Antriebsriemen 1 in Form eines Keilrippenriemens mit einer Decklage 2, einer Festigkeitsträgerlage 3 mit in Längsrichtung verlaufenden parallel angeordneten Zugträgern 4 sowie mit einem Unterbau 5. Der Unterbau weist eine Keilrippenstruktur auf, gebildet aus Rippen 6 und Rillen 7. Der Unterbau umfasst dabei die Kraftübertragungszone 8.The single figure shows a drive belt 1 in the form of a V-ribbed belt with a cover layer 2 , a reinforcement layer 3 with extending in the longitudinal direction parallel tension members 4 as well as with a substructure 5 , The substructure has a V-rib structure formed of ribs 6 and grooves 7 , The substructure includes the power transmission zone 8th ,

Die Decklage 2 und der Unterbau 5 bilden dabei als Gesamteinheit den elastischen Grundkörper, der aus einem polymeren Werkstoff besteht, insbesondere in Form einer vulkanisierten Kautschukmischung, enthaltend wenigstens eine Kautschukkomponente und Mischungsingredienzien. Als Kautschukkomponente wird insbesondere ein Ethylen-Propylen-Mischpolymerisat (EPM), ein Ethylen-Propylen-Dien-Mischpolymerisat (EPDM), (teil)hydrierter Nitrilkautschuk (HNBR), Fluorkautschuk (FKM), Naturkautschuk (NR), Styrol-Butadien-Kautschuk (SBR) oder Butadien-Kautschuk (BR) eingesetzt, die unverschnitten oder mit wenigstens einer weiteren Kautschukkomponente, insbesondere mit einem der vorgenannten Kautschuktypen, verschnitten sind, beispielsweise in Form eines EPM/EPDM- oder SBR/BR-Verschnittes. Von besonderer Bedeutung ist dabei EPM oder EPDM oder ein EPM/EPDM-Verschnitt. Die Mischungsingredienzien umfassen dabei wenigstens einen Vernetzer oder ein Vernetzersystem (Vernetzungsmittel und Beschleuniger). Weitere Mischungsingredienzien sind zumeist noch ein Füllstoff und/oder ein Verarbeitungshilfsmittel und/oder ein Weichmacher und/oder ein Alterungsschutzmittel sowie gegebenenfalls weitere Zusatzstoffe, beispielsweise Fasern und Farbpigmente. Diesbezüglich wird auf den allgemeinen Stand der Kautschukmischungstechnologie verwiesen.The top layer 2 and the substructure 5 form as a whole unit the elastic base body, which consists of a polymeric material, in particular in the form of a vulcanized rubber mixture containing at least one rubber component and Mischungsingredienzien. In particular, the rubber component is an ethylene-propylene copolymer (EPM), an ethylene-propylene-diene copolymer (EPDM), (partially) hydrogenated nitrile rubber (HNBR), fluororubber (FKM), natural rubber (NR), styrene-butadiene rubber (SBR) or butadiene rubber (BR), which are uncut or blended with at least one further rubber component, in particular with one of the abovementioned types of rubber, for example in the form of an EPM / EPDM or SBR / BR blend. Of particular importance is EPM or EPDM or an EPM / EPDM blend. The mixture ingredients thereby comprise at least one crosslinker or a crosslinker system (crosslinking agent and accelerator). Other mixing ingredients are usually still a filler and / or a processing aid and / or a plasticizer and / or an aging inhibitor and optionally further additives, such as fibers and color pigments. In this regard, reference is made to the general state of rubber mixing technology.

Die Zugträger sind insbesondere Einzelcorde, beispielsweise aus Stahl, Polyamid, Aramid, Polyester, Glasfasern, Kohlefasern oder Polyethylen-2,6-naphthalat (PEN).The Zugträger are in particular single cords, for example made of steel, polyamide, aramid, polyester, glass fibers, carbon fibers or polyethylene-2,6-naphthalate (PEN).

Innerhalb der Kraftübertragungszone 8 ist der erfindungsgemäße Antriebsriemen 1 mit einer Flockauflage 9 (Abschnitt A), insbesondere aus Baumwolle, versehen. Bei der Bildung dieser Flockauflage wird nun die Chlorparaffinlösung eingesetzt, die zu einer guten Flockanhaftung auf dem Unterbau 5 führt, verbunden mit einer deutlichen Nassgeräuschreduzierung.Inside the power transmission zone 8th is the drive belt according to the invention 1 with a flock location 9 (Section A), in particular of cotton. The formation of this flock coating now uses the chlorinated paraffin solution, which leads to good flock adhesion to the substructure 5 leads, combined with a significant reduction in wet noise.

Im Rahmen einer Vergleichsausführung ist der Antriebsriemen 1 nach der Patentschrift US 3 981 206 mit einer Textilauflage 10 (Abschnitt B) versehen.In a comparative version is the drive belt 1 according to the patent US 3,981,206 with a textile overlay 10 (Section B) provided.

Die Oberfläche der Decklage 2 kann unabhängig von dem Einsatz einer Flockauflage 9 oder Textilauflage 10 zusätzlich noch mit einer Deckauflage ausgestattet sein, wobei beispielsweise ebenfalls auf die Patentschrift US 3 981 206 verwiesen wird.The surface of the top layer 2 can be independent of the use of a flock pad 9 or textile overlay 10 additionally be equipped with a cover edition, for example, also to the patent US 3,981,206 is referenced.

11
Antriebsriemen (Keilrippenriemen)drive belts (V-ribbed belt)
22
Decklagetopsheet
33
FestigkeitsträgerlageReinforcement layer
44
Zugträger in Form von Einzelcordentension members in the form of individual cords
55
Unterbausubstructure
66
Rippenribs
77
Rillengrooves
88th
KraftübertragungszonePower transmission zone
99
Flockauflage (Abschnitt A)Flock edition (Section A)
1010
Textilauflage (Abschnitt B)textile wraps (Section B)

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • - DE 3823157 A1 [0002, 0005] - DE 3823157 A1 [0002, 0005]
  • - DE 10016351 A1 [0002] - DE 10016351 A1 [0002]
  • - DE 102006007509 A1 [0002] DE 102006007509 A1 [0002]
  • - EP 0590423 A2 [0002] - EP 0590423 A2 [0002]
  • - EP 0737228 B1 [0002] - EP 0737228 B1 [0002]
  • - EP 0831247 B1 [0002] - EP 0831247 B1 [0002]
  • - EP 0866834 B1 [0002] - EP 0866834 B1 [0002]
  • - EP 1108750 A1 [0002] - EP 1108750 A1 [0002]
  • - EP 1129308 B1 [0002] - EP 1129308 B1 [0002]
  • - US 3981206 [0002, 0005, 0008, 0026, 0027] - US 3981206 [0002, 0005, 0008, 0026, 0027]

Claims (25)

Antriebsriemen (1) mit einem elastischen Grundkörper, umfassend eine Decklage (2) und einen Unterbau (5) mit einer Kraftübertragungszone (8), wobei die Kraftübertragungszone mit einer Flockauflage (9) versehen ist, wobei die Anhaftung der Flockauflage innerhalb der Kraftübertragungszone mittels einer Lösung erfolgt, dadurch gekennzeichnet, dass die Lösung eine Chlorparaffinlösung ist.Drive belt ( 1 ) having an elastic base body, comprising a cover layer ( 2 ) and a substructure ( 5 ) with a power transmission zone ( 8th ), wherein the power transmission zone with a flock ( 9 ), wherein the adhesion of the flock coating takes place within the power transmission zone by means of a solution, characterized in that the solution is a chlorinated paraffin solution. Antriebsriemen nach Anspruch 1, dadurch gekennzeichnet, dass die Chlorparaffinlösung einen Chlorgehalt von 10 bis 70% besitzt.Drive belt according to claim 1, characterized that the chlorinated paraffin solution has a chlorine content of 10 to 70% owns. Antriebsriemen nach Anspruch 2, dadurch gekennzeichnet, dass die Chlorparaffinlösung einen Chlorgehalt von 15 bis 70% besitzt.Drive belt according to claim 2, characterized that the chlorinated paraffin solution has a chlorine content of 15 to 70% owns. Antriebsriemen nach Anspruch 2 oder 3, dadurch gekennzeichnet, dass die Chlorparaffinlösung einen Chlorgehalt von 30 bis 70% besitzt.Drive belt according to claim 2 or 3, characterized that the chlorinated paraffin solution has a chlorine content of 30 to 70% owns. Antriebsriemen nach Anspruch 2, 3 oder 4, dadurch gekennzeichnet, dass die Chlorparaffinlösung einen Chlorgehalt von 40 bis 50% besitzt.Drive belt according to claim 2, 3 or 4, characterized characterized in that the chlorinated paraffin solution has a chlorine content from 40 to 50% owns. Antriebsriemen nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass kurzkettige oder mittelkettige Chlorparaffine zum Einsatz gelangen.Drive belt according to one of the claims 1 to 5, characterized in that short-chain or medium-chain Chlorinated paraffins are used. Antriebsriemen nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass die Flockauflage (9) aus Baumwolle, Aramid oder Zellulose besteht.Drive belt according to one of claims 1 to 6, characterized in that the flock pad ( 9 ) consists of cotton, aramid or cellulose. Antriebsriemen nach Anspruch 7, dadurch gekennzeichnet, dass die Flockauflage (9) aus Baumwolle besteht.Drive belt according to claim 7, characterized in that the flock pad ( 9 ) consists of cotton. Antriebsriemen nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass der Grundkörper einen elastomeren Werkstoff auf Basis einer vulkanisierten Kautschukmischung umfasst, enthaltend wenigstens eine Kautschukkomponente und Mischungsingredienzien.Drive belt according to one of the claims 1 to 8, characterized in that the basic body a elastomeric material based on a vulcanized rubber mixture comprising at least one rubber component and mixing ingredients. Antriebsriemen nach Anspruch 9, dadurch gekennzeichnet, dass die Kautschukkomponente ein Ethylen-Propylen-Mischpolymerisat (EPM), ein Ethylen-Propylen-Dien-Mischpolymerisat (EPDM), (teil)hydrierter Nitrilkautschuk (HNBR), Chloropren-Kautschuk (CR), Fluor-Kautschuk (FKM), Naturkautschuk (NR), Styrol-Butadien-Kautschuk (SBR) oder Butadien-Kautschuk (BR) ist, die unverschnitten oder im Verschnitt mit wenigstens einer weiteren Kautschukkomponente, insbesondere in Verbindung mit einem der vorgenannten Kautschuktypen, zum Einsatz gelangen.Drive belt according to claim 9, characterized that the rubber component is an ethylene-propylene copolymer (EPM), an ethylene-propylene-diene copolymer (EPDM), (partially) hydrogenated nitrile rubber (HNBR), chloroprene rubber (CR), fluoro rubber (FKM), natural rubber (NR), styrene-butadiene rubber (SBR) or butadiene rubber (BR) which is uncut or blended with at least one another rubber component, in particular in conjunction with a the aforementioned rubber types are used. Antriebsriemen nach Anspruch 10, dadurch gekennzeichnet, dass die Kautschukkomponente EPM oder EPDM oder ein EPM/EPDM-Verschnitt ist.Drive belt according to claim 10, characterized that the rubber component is EPM or EPDM or an EPM / EPDM blend is. Antriebsriemen nach einem der Ansprüche 1 bis 11, dadurch gekennzeichnet, dass der Antriebsriemen (1) als Keilrippenriemen ausgebildet ist.Drive belt according to one of claims 1 to 11, characterized in that the drive belt ( 1 ) is designed as a V-ribbed belt. Verfahren zur Herstellung eines Antriebsriemens (1) mit einem elastischen Grundkörper, umfassend eine Decklage (2) und einen Unterbau (5) mit einer Kraftübertragungszone (8), wobei die Kraftübertragungszone mit einer Flockauflage (9) versehen wird, wobei die Anhaftung der Flockauflage innerhalb der Kraftübertragungszone mittels einer Lösung erfolgt, gekennzeichnet durch wenigstens folgende Verfahrensschritte: – der unvulkanisierte Grundkörper des Riemenrohlings wird innerhalb der Kraftübertragungszone (8) mit einer Chlorparaffinlösung behandelt; – die mit der Chlorparaffinlösung behandelte Kraftübertragungszone (8) wird unter Bildung einer Flockauflage (9) beflockt; – anschließend wird der Riemenrohling vulkanisiert.Method for producing a drive belt ( 1 ) having an elastic base body, comprising a cover layer ( 2 ) and a substructure ( 5 ) with a power transmission zone ( 8th ), wherein the power transmission zone with a flock ( 9 ), whereby the adhesion of the flock coating within the force transmission zone takes place by means of a solution, characterized by at least the following process steps: the unvulcanized main body of the belt blank is placed inside the force transmission zone ( 8th ) treated with a chlorinated paraffin solution; The power transmission zone treated with the chloro-paraffin solution ( 8th ) is added to form a flock ( 9 ) flocked; - Then the belt blank is vulcanised. Verfahren nach Anspruch 13, dadurch gekennzeichnet, dass eine Chlorparaffinlösung mit einem Chlorgehalt von 10 bis 70% eingesetzt wird.Method according to claim 13, characterized in that that a chlorinated paraffin solution with a chlorine content of 10 to 70% is used. Verfahren nach Anspruch 14, dadurch gekennzeichnet, dass eine Chlorparaffinlösung mit einem Chlorgehalt von 15 bis 70% eingesetzt wird.Method according to claim 14, characterized in that that a chlorinated paraffin solution with a chlorine content of 15 to 70% is used. Verfahren nach Anspruch 14 oder 15, dadurch gekennzeichnet, dass eine Chlorparaffinlösung mit einem Chlorgehalt von 30 bis 70% eingesetzt wird.Method according to claim 14 or 15, characterized that a chlorinated paraffin solution with a chlorine content of 30 to 70% is used. Verfahren nach Anspruch 14, 15 oder 16, dadurch gekennzeichnet, dass eine Chlorparaffinlösung mit einem Chlorgehalt von 40 bis 50% eingesetzt wird.The method of claim 14, 15 or 16, characterized characterized in that a chlorinated paraffin solution with a Chlorine content of 40 to 50% is used. Verfahren nach einem der Ansprüche 13 bis 17, dadurch gekennzeichnet, dass kurzkettige oder mittelkettige Chlorparaffine eingesetzt werden.Method according to one of claims 13 to 17, characterized in that short-chain or medium-chain Chloroparaffins are used. Verfahren nach einem der Ansprüche 13 bis 18, dadurch gekennzeichnet, dass die Beflockung mit Baumwolle, Aramid oder Zellulose durchgeführt wird.Method according to one of claims 13 to 18, characterized in that the flocking with cotton, aramid or cellulose is carried out. Verfahren nach Anspruch 19, dadurch gekennzeichnet, dass die Beflockung mit Baumwolle durchgeführt wird.Method according to claim 19, characterized that the flocking is done with cotton. Verfahren nach einem der Ansprüche 13 bis 20, dadurch gekennzeichnet, dass die Beflockung elektrostatisch erfolgt.Method according to one of claims 13 to 20, characterized in that the flocking electrostatically he follows. Verfahren nach einem der Ansprüche 13 bis 21, dadurch gekennzeichnet, dass als Grundkörper ein elastomerer Werkstoff auf Basis einer vulkanisierbaren Kautschukmischung eingesetzt wird, enthaltend wenigstens eine Kautschukkomponente und Mischungsingredienzien.Method according to one of claims 13 to 21, characterized in that the base body is an elastomeric Material used on the basis of a vulcanizable rubber mixture containing at least one rubber component and blend ingredients. Verfahren nach Anspruch 22, dadurch gekennzeichnet, dass als Kautschukkomponente ein Ethylen-Propylen-Mischpolymerisat (EPM), ein Ethylen-Propylen-Dien-Misch-Polymerisat (EPDM), (teil)hydrierter Nitrilkautschuk (HNBR), Chloropren-Kautschuk (CR), Fluor-Kautschuk (FKM), Naturkautschuk (NR), Styrol-Butadien-Kautschuk (SBR) oder Butadien-Kautschuk (BR), die unverschnitten oder im Verschnitt mit wenigstens einer weiteren Kautschukkomponente, insbesondere in Verbindung mit einem der vorgenannten Kautschuktypen, eingesetzt werden.Method according to claim 22, characterized in that that as the rubber component, an ethylene-propylene copolymer (EPM), an ethylene-propylene-diene mixed polymer (EPDM), (partially) hydrogenated nitrile rubber (HNBR), chloroprene rubber (CR), fluoro rubber (FKM), natural rubber (NR), styrene-butadiene rubber (SBR) or butadiene rubber (BR), the uncut or blended with at least one other Rubber component, in particular in conjunction with one of the abovementioned Types of rubber used. Verfahren nach Anspruch 23, dadurch gekennzeichnet, dass als Kautschukkomponente EPM oder EPDM oder ein EPM/EPDM-Verschnitt eingesetzt wird.Method according to claim 23, characterized in that the rubber component is EPM or EPDM or an EPM / EPDM blend is used. Verfahren nach einem der Ansprüche 13 bis 24 zur Herstellung eines Keilrippenriemens (1).Method according to one of claims 13 to 24 for producing a V-ribbed belt ( 1 ).
DE200810026965 2008-06-05 2008-06-05 Drive belt i.e. ribbed drive belt, has force transmission zone provided with flock support, where adhesion of flock support within force transmission zone takes place via chlorine paraffin solution that comprises specific chlorine content Withdrawn DE102008026965A1 (en)