DE10051789A1 - Imitation wood used in fireplaces comprises fired clay having communicating pore chambers for receiving a combustible fuel - Google Patents

Imitation wood used in fireplaces comprises fired clay having communicating pore chambers for receiving a combustible fuel

Info

Publication number
DE10051789A1
DE10051789A1 DE2000151789 DE10051789A DE10051789A1 DE 10051789 A1 DE10051789 A1 DE 10051789A1 DE 2000151789 DE2000151789 DE 2000151789 DE 10051789 A DE10051789 A DE 10051789A DE 10051789 A1 DE10051789 A1 DE 10051789A1
Authority
DE
Germany
Prior art keywords
imitation
firewood
clay
combustible
fired clay
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE2000151789
Other languages
German (de)
Inventor
Erwin Strattner
Franz Probst
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE2000151789 priority Critical patent/DE10051789A1/en
Publication of DE10051789A1 publication Critical patent/DE10051789A1/en
Ceased legal-status Critical Current

Abstract

Imitation wood (1) comprises fired clay having communicating pore chambers (2, 3) for receiving a combustible fuel. An Independent claim is also included for a process for the production of an imitation wood comprising producing a mold by deforming a firewood, filling with a clay composition, removing the mold, drying and firing the green body formed, and applying a glaze mixed with combustible fuels. Preferred Features: The fired clay has macropores formed by firing the combustible fuels added to the clay. The combustible fuels are selected from sawdust, paper shreds and polystyrene.

Description

Die Erfindung betrifft ein Kaminholzimitat sowie einen Kit mit einem Kaminholzimitat. Sie betrifft ferner eine Verwen­ dung und ein Verfahren zur Herstellung eines als Brennstoff­ träger geeigneten Kaminholzimitats.The invention relates to an imitation firewood and a kit with an imitation firewood. It also concerns use tion and a method for producing a fuel suitable imitation firewood.

Nach dem Stand der Technik werden zum Feuern einer Kaminstel­ le üblicherweise Holzscheite verbrannt. Die Herstellung, der Transport und die Lagerung von Holzscheiten verursacht Ko­ sten. Beim Verbrennen von Holz entsteht außerdem Asche, wel­ che zu einer Verschmutzung der den Kamin umgebenden Räume führt. Weiterer Aufwand wird durch die Entsorgung der Asche und das Reinigen des Kamins von Rußrückständen verursacht.According to the prior art are used to fire a fireplace le usually burned logs. The manufacture of the Transport and storage of logs causes Ko sten. When wood is burned, ashes also form pollution of the rooms surrounding the fireplace leads. Disposing of the ashes creates additional effort and cleaning the chimney from soot residues.

Aufgabe der Erfindung ist es, die Nachteile nach dem Stand der Technik zu beseitigen. Es soll insbesondere eine Möglich­ keit zur Schaffung eines Kaminfeuers angegeben werden, welche die Herstellung, den Transport und die Lagerung von Holz­ scheiten erübrigt. Ferner soll die unerwünschte Bildung von Ruß und Staub vermieden werden.The object of the invention is to overcome the disadvantages of the prior art of technology to eliminate. In particular, there should be one possible be given to create a log fire, which the manufacture, transport and storage of wood superfluous. Furthermore, the undesirable formation of Soot and dust can be avoided.

Diese Aufgabe wird durch die Merkmale der Ansprüche 1, 7, 9 und 12 gelöst. Zweckmäßige Ausgestaltungen ergeben sich aus den Ansprüchen 2 bis 6, 8, 10 und 13.This object is achieved by the features of claims 1, 7, 9 and 12 solved. Appropriate configurations result from claims 2 to 6, 8, 10 and 13.

Nach Maßgabe der Erfindung ist ein Kaminholzimitat vorgese­ hen, welches aus gebranntem Ton mit einem kommunizierenden Porenraum zur Aufnahme einer brennbaren Flüssigkeit herge­ stellt ist. Das erfindungsgemäße Kaminholzimitat ist wieder­ verwendbar. Es muß nur einmal hergestellt und zur Brennstelle transportiert werden. Eine Lagerung entfällt. Das erfindungs­ gemäße Kaminholzimitat ist dazu geeignet flüssigen Brennstoff in seinem kommunizierenden Porenraum aufzunehmen. Der flüssi­ ge Brennstoff wird während der Verbrennung langsam entgegen der Kapillarkräfte an die Oberfläche des Kaminholzimitats ge­ saugt. Er verdampft dort und verbrennt praktisch rückstands­ frei. Es kommt nicht zur Bildung von Ruß und Staub. Das er­ findungsgemäße Kaminholzimitat läßt sich durch Einlegen in eine brennbare Flüssigkeit wieder mit Brennstoff befüllen.According to the invention, an imitation firewood is provided hen, which is made of fired clay with a communicating Pore space for holding a flammable liquid represents is. The imitation firewood according to the invention is again usable. It only has to be made once and to the burning point be transported. Storage is not necessary. The invention appropriate imitation firewood is suitable for liquid fuel  in his communicating pore space. The liquid fuel is slowly countered during combustion the capillary forces on the surface of the imitation firewood sucks. It evaporates there and practically burns residue free. Soot and dust do not form. That he Imitation firewood according to the invention can be inserted into refill a flammable liquid with fuel.

Nach einer Ausgestaltung ist vorgesehen, daß der gebrannte Ton durch Ausbrennen von der Tonmasse zugesetztem brennbaren Stoffen gebildete Makroporen aufweist. Das Material ist ähn­ lich den für die Herstellung von wärmedämmenden Tonziegeln aus der Bauindustrie bekannten Material. Durch das Vorhanden­ sein von Makroporen wird die Speicherfähigkeit für Brennstoff weiter erhöht. Das Kaminholzimitat weist eine längere Brenn­ dauer auf.According to one embodiment, it is provided that the burned Clay from combustible added by burning out of the clay mass Macropores formed substances. The material is similar Lich for the production of heat-insulating clay tiles material known from the construction industry. By the existence macropores will be the storage capacity for fuel further increased. The imitation firewood has a longer burning time persist.

Die brennbaren Stoffe können aus Sägemehl, Papierschnitzel oder Polystyrol gebildet sein. Solche Stoffe sind billig. Sie bilden beim Ausbrennen geeignete Makroporen. Zweckmäßigerwei­ se sind die brennbaren Stoffe in einem Anteil von bis zu 50 Vol.% der Tonmasse zugesetzt. Es hat sich gezeigt, daß ein solchermaßen hergestellter Makroporenraum noch eine ausrei­ chende Kapillarwirkung aufweist, so daß ein unerwünschtes Austreten der im Kaminholzimitat aufgenommenen brennbaren Flüssigkeit nicht stattfindet.The combustible materials can be made from sawdust, shredded paper or polystyrene. Such fabrics are cheap. she form suitable macropores when burned out. Zweckmäßigerwei These are the flammable substances in a proportion of up to 50 vol.% added to the clay mass. It has been shown that a Macropore space produced in this way is still sufficient has capillary action, so that an undesirable Escaping the flammable in the imitation firewood Liquid does not take place.

Nach einem weiteren Ausgestaltungsmerkmal kann ein aus Scha­ motte gebildeter Kern vorgesehen sein. Ein solcher Kern weist eine besonders große Porosität auf. Es wird dadurch weiter die Speicherfähigkeit von brennbarer Flüssigkeit erhöht. According to a further design feature, a from Scha moth formed core may be provided. Such a core points a particularly large porosity. It continues the storage capacity of flammable liquids increases.  

Zweckmäßigerweise ist der gebrannte Ton mit einer Glasur um­ fangen. Das Aufbringen und Aufschmelzen bzw. Einbrennen der Glasur auf den Tonscherben erfolgt nach herkömmlichen Techni­ ken. Die Glasur ist zweckmäßigerweise mit Durchbrüchen verse­ hen. Die Durchbrüche können durch Mischen der Glasur mit brennbaren Stoffen, wie Sägemehl und dgl., hergestellt wer­ den. Die brennbaren Stoffe brennen beim Aufschmelzen der Gla­ sur aus; es bleiben Durchbrüche zurück.The fired clay is expediently covered with a glaze to catch. The application and melting or baking of the Glaze on the potsherds is done using conventional techniques ken. The glaze is expediently with openings hen. The breakthroughs can be made by mixing the glaze with flammable substances, such as sawdust and the like the. The flammable substances burn when the glass melts sur out; breakthroughs remain.

Nach weiterer Maßgabe der Erfindung ist ein Kit mit minde­ stens einem erfindungsgemäßen Kaminholzimitat und einer brennbaren Flüssigkeit vorgesehen. Die brennbare Flüssigkeit ist vorteilhafterweise, vorzugsweise mit einem Duftstoff ver­ setzter, Alkohol. Eine solche Flüssigkeit ist relativ billig. Es handelt sich dabei um einen "nachwachsenden Rohstoff", dessen Verbrennung die Umwelt nicht besonders stark belastet. Alkohol ist von seiner Viskosität besonders als brennbare Flüssigkeit zum Beladen des erfindungsgemäßen Kaminholzimi­ tats geeignet.According to another measure of the invention, a kit with mind least one imitation firewood according to the invention and one flammable liquid provided. The flammable liquid is advantageously ver, preferably with a fragrance seated, alcohol. Such a liquid is relatively cheap. It is a "renewable raw material", the combustion of which is not particularly harmful to the environment. Alcohol is particularly flammable in its viscosity Liquid for loading the Kaminholzimi according to the invention indeed suitable.

Ferner ist die Verwendung von in Form eines Kaminholzes her­ gestelltem, einen kommunizierenden Porenraum aufweisenden ge­ brannten Ton als Träger zur Aufnahme einer brennbaren Flüs­ sigkeit zum Betreiben eines Kaminfeuers vorgesehen. Wegen der vorteilhaften Ausgestaltungen wird auf die vorangegangenen Ausführungen verwiesen.Furthermore, the use is in the form of a firewood provided, having a communicating pore space burned clay as a carrier for holding a flammable river provided for operating a log fire. Because of the advantageous embodiments are based on the previous ones Executions referenced.

Schließlich wird ein Verfahren zur Herstellung eines als Brennstoffträger geeigneten Kaminholzimitats mit folgenden Schritten beansprucht:
Finally, a process for the production of an imitation firewood suitable as a fuel carrier is claimed with the following steps:

  • a) Herstellen einer Form durch Abformen eines Holzscheits, a) making a shape by molding a log,  
  • b) Füllen der Form mit einer Tonmasse,b) filling the mold with a clay mass,
  • c) Entformen,c) removal from the mold,
  • d) Trocknen und Brennen des Grünlings undd) drying and burning the green body and
  • e) Auftragen einer mit brennbaren Stoffen gemischten Glasur und Einbrennen derselben.e) Apply a glaze mixed with flammable substances and branding them.

Das Verfahren ermöglicht eine effiziente Herstellung des Ka­ minholzimitats.The process enables efficient production of the Ka minholzimitats.

Nachfolgend wird ein Ausführungsbeispiel der Erfindung anhand der Zeichnungen näher erläutert. Es zeigenAn exemplary embodiment of the invention is described below the drawings explained in more detail. Show it

Fig. 1 eine Seitenansicht eines Kaminholzimitats, Fig. 1 is a side view of a wood imitation fireplace,

Fig. 2 eine schematische Teilschnittansicht durch das Ka­ minholzimitat gemäß Fig. 1, und Fig. 2 is a schematic partial sectional view through the Ka minholzimitat according to FIG. 1, and

Fig. 3 eine Schnittansicht eines weiteren Kaminholzimi­ tats. Fig. 3 is a sectional view of another Kaminholzimi act.

Ein in der Fig. 1 allgemein mit dem Bezugszeichen 1 bezeich­ netes Kaminholzimitat ist aus gebranntem Ton hergestellt. Der Ton weist Poren bzw. Porenkanäle 2 auf, welche mit der Ober­ fläche des Kaminholzimitats 1 in Verbindung stehen. Ferner sind Makroporen 3 vorgesehen, deren Porendurchmesser um ein Vielfaches größer als der der Poren 2 ist. Der mittlere Po­ rendurchmesser der Makroporen 3 kann im Bereich von 0,1 bis 3 mm liegen. Der mittlere Porendurchmesser der Poren 2 liegt üblicherweise im Bereich zwischen 10 µm und 1000 µm. Die Makro­ poren 3 sind durch Ausbrennen von in der Tonmasse enthaltenen brennbaren Stoffen, wie Sägemehl, Papierschnitzel oder Po­ lystyrol, gebildet. Die Poren 2 und die Makroporen 3 bilden einen über das gesamte Volumen des Kaminholzimitats 1 im we­ sentlichen kommunizierenden Porenraum.A generally designated in Fig. 1 with the reference numeral 1 imitation firewood is made of fired clay. The clay has pores or pore channels 2 , which are connected to the upper surface of the imitation wood 1 . Macropores 3 are also provided, the pore diameter of which is many times larger than that of the pores 2 . The average diameter of the macropores 3 can be in the range from 0.1 to 3 mm. The average pore diameter of the pores 2 is usually in the range between 10 μm and 1000 μm. The macro pores 3 are formed by burning out combustible substances contained in the clay, such as sawdust, shredded paper or po lystyrene. The pores 2 and the macro pores 3 form a pore space which communicates over the entire volume of the imitation firewood 1 .

In Fig. 2 ist in einer schematischen Teilquerschnittsansicht nochmals der kommunizierende Porenraum gezeigt. Die Poren bzw. Porenkanäle 2 sind in ihrem Durchmesser so ausgebildet, daß sie eine Kapillarkraft auf eine darin aufgenommene Flüs­ sigkeit ausüben. Durch die Kapillarkraft wird einerseits ver­ mieden, daß in das Kaminholzimitat 1 aufgenommene Flüssigkeit daraus entweicht und andererseits wird beim Verbrennen der Flüssigkeit diese mit einer geeigneten Geschwindigkeit an die Oberfläche des Kaminholzimitats 1 gefördert.In FIG. 2, the communicating pore space is shown in a schematic partial cross-sectional view again. The pores or pore channels 2 are formed in their diameter so that they exert a capillary force on a liquid contained therein. The capillary force avoids, on the one hand, that liquid absorbed into the imitation wood 1 escapes therefrom and, on the other hand, when the liquid is burned, it is conveyed to the surface of the imitation wood 1 at a suitable speed.

Als brennbare Flüssigkeit zum Beladen des Kaminholzimitats 1 eignet sich insbesondere Alkohol. Zum Beladen wird das Kamin­ holzimitat 1 etwa 20 Minuten in ein mit Alkohol gefülltes Ge­ fäß gelegt.Alcohol is particularly suitable as the flammable liquid for loading the imitation firewood 1 . For loading, the imitation wood fireplace 1 is placed in a container filled with alcohol for about 20 minutes.

Zur Herstellung des Kaminholzimitats 1 wird zweckmäßigerweise ein Holzscheit mittels herkömmlicher Techniken abgeformt. Zur Herstellung der Form kann z. B. Silikon verwendet werden. In einer nach herkömmlichen Techniken hergestellten Form kann - wie in Fig. 3 gezeigt ist - als Formkern z. B. Schamotte 4 eingesetzt werden. Schamotte 4 ist billig. Der Werkstoff ist porös und ermöglicht die Aufnahme, einer relativ großen Menge an brennbarer Flüssigkeit. Auf das Vorsehen eines aus Scha­ motte 4 hergestellten Kerns kann auch verzichtet werden.To produce the imitation firewood 1 , a log is expediently molded using conventional techniques. To produce the shape, for. B. silicone can be used. In a mold produced by conventional techniques - as shown in Fig. 3 - z. B. chamotte 4 can be used. Fireclay 4 is cheap. The material is porous and allows the absorption of a relatively large amount of flammable liquid. The provision of a core made of sheet 4 can also be dispensed with.

Der aus Schamotte 4 hergestellte Formkern wird anschließend vollständig mit Tonmasse umgeben. In der Tonmasse sind zweck­ mäßigerweise bis zu 50 Vol.% an brennbaren Stoffen, z. B. Sägemehl, zugesetzt. Die Form wird dann entformt. Der Grünling wird getrocknet und anschließend gebrannt. Beim Brennvorgang brennen die brennbaren Stoffe aus. Zurück bleiben Makroporen 3, welche mit den Poren 2 des gebrannten Tons in Verbindung sind. Der aus Schamotte 4 gebildete Formkern ist ebenfalls mit dem Porenraum des gebrannten Tons in Verbindung. Das Ka­ minholzimitat 1 weist eine geeignete Struktur zum Aufnehmen und Speichern von brennbarer Flüssigkeit, wie Alkohol, auf.The mold core made of chamotte 4 is then completely surrounded with clay. Up to 50% by volume of combustible substances, e.g. B. sawdust added. The mold is then removed from the mold. The green body is dried and then burned. The flammable substances burn out during the burning process. Macropores 3 remain, which are connected to the pores 2 of the fired clay. The mold core formed from chamotte 4 is also connected to the pore space of the fired clay. The imitation imitation wood 1 has a suitable structure for receiving and storing combustible liquids such as alcohol.

Zweckmäßigerweise wird der gebrannte Tonscherben anschließend mit einer Glasur versehen. Damit sicher gestellt ist, daß die Glasur die Poren des gebrannten Tons nicht verstopft, wird diese vor dem Aufbringen mit brennbaren Stoffen, z. B. Säge­ mehl und dgl. gemischt., Beim Aufbrennen der Glasur verbren­ nen de brennbaren Stoffe. Es bleiben in der Glasur Durchbrü­ che zurück, durch welche der Alkohol in den gebrannten Ton eingesaugt bzw. aus diesem austreten kann. Die Glasur erhöht die Haltbarkeit des Kaminholzimitats 1.The fired potsherds are then expediently glazed. So that it is ensured that the glaze does not clog the pores of the fired clay, this is before application with flammable substances, for. B. sawdust and the like. Mixed. When burning the glaze NEN combustible materials burn. Breakthroughs remain in the glaze, through which the alcohol can be sucked into the fired clay or can escape from it. The glaze increases the durability of the imitation firewood 1 .

Claims (13)

1. Kaminholzimitat hergestellt aus gebranntem Ton mit einem kommunizierenden Porenraum (2, 3, 4) zur Aufnahme einer brennbaren Flüssigkeit.1. Imitation firewood made of fired clay with a communicating pore space ( 2 , 3 , 4 ) for holding a flammable liquid. 2. Kaminholzimitat nach Anspruch 1, wobei der gebrannte Ton durch Ausbrennen von der Tonmasse zugesetztem brennbaren Stoffen gebildete Makroporen (3) aufweist.2. Imitation firewood according to claim 1, wherein the fired clay has macropores ( 3 ) formed by burning combustible substances added to the clay mass. 3. Kaminholzimitat nach Anspruch 2, wobei die brennbaren Stoffe aus Sägemehl, Papierschnitzel oder Polystyrol gebildet sind.3. imitation firewood according to claim 2, wherein the combustible Fabrics made from sawdust, shredded paper or polystyrene are. 4. Kaminholzimitat nach einem der vorhergehenden Ansprüche, wobei die brennbaren Stoffe in einem Anteil von bis zu 50 Vol.% der Tonmasse zugesetzt sind.4. imitation firewood according to one of the preceding claims, the combustible substances in a proportion of up to 50 vol.% are added to the clay mass. 5. Kaminholzimitat nach einem der vorhergehenden Ansprüche, wobei ein aus Schamotte (4) gebildeter Kern vorgesehen ist.5. Imitation firewood according to one of the preceding claims, wherein a core formed from chamotte ( 4 ) is provided. 6. Kaminholzimitat nach einem der vorhergehenden Ansprüche, wobei der gebrannte Ton mit einer, vorzugsweise mit Durchbrü­ chen versehenen, Glasur umfangen ist.6. imitation firewood according to one of the preceding claims, the fired clay with a, preferably with a breakthrough Chen provided, glaze is embraced. 7. Kit mit mindestens einem Kaminholzimitat nach einem der vorhergehenden Ansprüche und einer brennbaren Flüssigkeit.7. Kit with at least one imitation firewood according to one of the previous claims and a flammable liquid. 8. Kit nach Anspruch 7, wobei die brennbare Flüssigkeit, vorzugsweise mit einem Duftstoff versetzter, Alkohol ist.8. Kit according to claim 7, wherein the combustible liquid, alcohol, preferably with a fragrance. 9. Verwendung von in Form eines Kaminholzes hergestelltem, einen kommunizierenden Porenraum (2, 3, 4) aufweisenden gebrannten Ton als Träger zur Aufnahme einer brennbaren Flüs­ sigkeit zum Betreiben eines Kaminfeuers.9. Use of in the form of a firewood, a communicating pore space ( 2 , 3 , 4 ) having fired clay as a carrier for receiving a flammable liquid to operate a log fire. 10. Verwendung nach Anspruch 9, wobei der gebrannte Ton durch Ausbrennen von der Tonmasse zugesetztem brennbaren Stoffen gebildete Makroporen (3) aufweist.10. Use according to claim 9, wherein the fired clay has macropores ( 3 ) formed by burning out combustible substances added to the clay mass. 11. Verwendung nach einem der Ansprüche 9 oder 10, wobei ein aus Schamotte (4) gebildeter Kern vorgesehen ist.11. Use according to one of claims 9 or 10, wherein a core formed from chamotte ( 4 ) is provided. 12. Verfahren zur Herstellung eines als Brennstoffträger ge­ eigneten Kaminholzimitats (1) mit folgenden Schritten:
  • a) Herstellen einer Form durch Abformen eines Holzscheits,
  • b) Füllen der Form mit einer Tonmasse,
  • c) Entformen,
  • d) Trocknen und Brennen des Grünlings und
  • e) Auftragen einer mit brennbaren Stoffen gemischten Glasur und Einbrennen derselben.
12. A method for producing an imitation firewood ( 1 ) suitable as a fuel carrier, comprising the following steps:
  • a) making a shape by molding a log,
  • b) filling the mold with a clay mass,
  • c) demoulding,
  • d) drying and burning the green body and
  • e) Applying a glaze mixed with flammable substances and baking them.
13. Verfahren nach Anspruch 12, wobei die Tonmasse mit bis zu 50 Vol.% mit brennabren Stoffen versetzt wird.13. The method of claim 12, wherein the clay mass with to 50 vol.% is added to combustible substances.
DE2000151789 2000-10-18 2000-10-18 Imitation wood used in fireplaces comprises fired clay having communicating pore chambers for receiving a combustible fuel Ceased DE10051789A1 (en)