DE10028215A1 - Melt-blown fiber fleece, for use in e.g. sanitary towels and tampons, contains a metal soap to increase its hydrophobic and alcohol-resisting properties - Google Patents

Melt-blown fiber fleece, for use in e.g. sanitary towels and tampons, contains a metal soap to increase its hydrophobic and alcohol-resisting properties

Info

Publication number
DE10028215A1
DE10028215A1 DE10028215A DE10028215A DE10028215A1 DE 10028215 A1 DE10028215 A1 DE 10028215A1 DE 10028215 A DE10028215 A DE 10028215A DE 10028215 A DE10028215 A DE 10028215A DE 10028215 A1 DE10028215 A1 DE 10028215A1
Authority
DE
Germany
Prior art keywords
metallic soap
fibrous material
nonwoven
nonwoven fibrous
alcohol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE10028215A
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Corovin GmbH
Original Assignee
Corovin GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corovin GmbH filed Critical Corovin GmbH
Priority to DE10028215A priority Critical patent/DE10028215A1/en
Publication of DE10028215A1 publication Critical patent/DE10028215A1/en
Ceased legal-status Critical Current

Abstract

Melt-blown fiber fleece (1) contains a metal soap (6) to increase its hydrophobic and alcohol-resisting properties. Independent claims are included for: (a) a method of making the fleece from a polymer melt comprising adding a metal soap to increase its hydrophobic and alcohol-resisting properties; (b) an agent for increasing hydrophobic properties and alcohol-resistance comprising a metal soap; and (c) the use of a metal soap as an additive in the production of fiber fleeces.

Description

Die Erfindung betrifft einen Vliesfaserstoff mit zumindest einem Zusatz zur Erhöhung einer hydrophoben, alkoholabweisen­ den Eigenschaft des Vliesfaserstoffes sowie ein entsprechen­ des Verfahren zur Herstellung des Vliesfaserstoffes.The invention relates to a nonwoven fibrous material with at least an additive to increase hydrophobic, alcohol-repellent correspond to the property of the nonwoven fiber fabric as well as a of the process for producing the nonwoven fibrous material.

Bekannt sind Vliesfaserstoffe, die eine hydrophobe und damit auch alkoholabweisende Wirkung aufweisen. Dazu werden Silo­ xanverbindungen eingesetzt, wie sie aus der US 5,744,548 und der US 5, 667,750 hervorgehen. Auch werden Fluorcarbonverbin­ dungen eingesetzt, wie sie aus der US 5,025,052 bekannt sind. Diese weisen jedoch Probleme bei der Verwendung in unmittel­ barem oder mittelbarem Kontakt mit der Hautoberfläche auf, insbesondere bei langanhaltendem Kontakt. Ein wesentliches Merkmal von Vliesfaserstoffen für die Verwendung im medizini­ schen oder hygienischen Bereich, insbesondere in der Frauen­ hygiene, ist deren alkoholabstoßende Fähigkeit. Diese ist für die Barrierebildung gegen Flüssigkeiten wie beispielsweise Blut von Wichtigkeit.Nonwoven fibers are known which are hydrophobic and therefore also have an alcohol-repellent effect. This will be silo xan compounds, as used in US 5,744,548 and of US 5, 667,750 emerge. Also become fluorocarbon used as are known from US 5,025,052. However, these have problems when used directly direct or indirect contact with the skin surface, especially with long-term contact. An essential one Characteristic of nonwoven fiber fabrics for use in medicine or hygienic area, especially in women hygiene is their ability to repel alcohol. This is for the barrier formation against liquids such as Blood of importance.

Aufgabe der vorliegenden Erfindung ist es, einen Vliesfaser­ stoff mit einem Zusatz zu schaffen, der alkoholabweisende und hydrophobe Eigenschaften aufweist.The object of the present invention is a nonwoven fiber to create fabric with an additive that is alcohol repellent and has hydrophobic properties.

Diese Aufgabe wird mit einem Vliesfaserstoff mit den Merkma­ len des Anspruchs 1 und mit einem Verfahren mit den Merkmalen des Anspruchs 10 gelöst. Weitere vorteilhafte Ausgestaltungen und Weiterbildungen sind in den Unteransprüchen angegeben.This task is accomplished with a nonwoven fiber with the Merkma len of claim 1 and with a method with the features of claim 10 solved. Further advantageous configurations and further developments are specified in the subclaims.

Der erfindungsgemäße Vliesfaserstoff umfaßt zur Erhöhung ei­ ner hydrophoben, alkoholabweisenden Eigenschaft des Vliesfa­ serstoffes mindestens eine metallische Seife. Es können auch Mischungen von metallischen Seifen Verwendung finden. Es hat sich herausgestellt, daß mit einer metallischen Seife zumindest in etwa die gleichen Resultate erzielt wurden, wie sie mit herkömmlichen Zusätzen auf Basis Siloxanverbindungen oder Fluorverbindungen erzielbar sind. Die erfindungsgemäßen Vliesfaserstoffe weisen jedoch eine erheblich verbesserte Biokompatibilität, insbesondere bei Hautkontakt, auf, da schädigende Langzeiteffekte nicht auftreten.The nonwoven fibrous material according to the invention comprises egg to increase ner hydrophobic, alcohol-repellent property of the fleece fa at least one metallic soap. It can too Mixtures of metallic soaps are used. It has it turned out that with a metallic soap at least  roughly the same results were achieved as they were with conventional additives based on siloxane compounds or Fluorine compounds can be achieved. The invention Nonwoven fiber fabrics, however, have significantly improved Biocompatibility, especially with skin contact, due to harmful long-term effects do not occur.

Vorzugsweise ist die metallische Seife aus einer Carbonsäure hergestellt. Dies hat den Vorteil, daß die metallische Seife bei einsetzbaren Polymeren für den Vliesfaserstoff wie bei­ spielsweise Polyolefinen, Polyamiden, Polyestern, Polyethern und/oder Polyesterethern schon in geringen Konzentrationen eine gute alkoholabweisende Wirkung zeigt. Die Carbonsäure kann eine oder mehrere Carboxylgruppen, insbesondere eine Carbonylgruppe, aufweisen und ist in der Lage, an einer Ober­ fläche einer Faser des Vliesfaserstoffes eine Hydrophobierung zu bewirken. Bevorzugt werden als Carbonsäuren Fettsäuren wie beispielsweise Palmitin-, Stearin, Öl-, Linol- und/oder Lino­ lensäure verwendet, wobei auch andere Carbonsäuren möglich sind. Die eingesetzten Carbonsäuren können gesättigt oder un­ gesättigt sein, wobei gesättigte Carbonsäuren bevorzugt sind, da mit diesen behandelter Vliesfaserstoff ausgesprochen haut­ verträglich ist.The metallic soap is preferably made of a carboxylic acid manufactured. This has the advantage that the metallic soap in the case of usable polymers for the nonwoven fibrous material as in for example polyolefins, polyamides, polyesters, polyethers and / or polyester ethers even in low concentrations shows a good alcohol-repellent effect. The carboxylic acid can one or more carboxyl groups, especially one Carbonyl group, have and is able to on an upper Surface of a fiber of the nonwoven fibrous material is hydrophobic to effect. Preferred carboxylic acids are fatty acids such as for example palmitin, stearin, oil, linoleic and / or lino Lentic acid is used, although other carboxylic acids are also possible are. The carboxylic acids used can be saturated or un be saturated, with saturated carboxylic acids being preferred, because with this treated nonwoven fiber material, it is extremely skin is tolerated.

Gemäß einer Weiterbildung wird eine Carbonsäure eingesetzt, die ein Molekulargewicht in einem Bereich von etwa 60 bis 800 g/mol aufweist. Bevorzugt liegt es in einem Bereich von etwa 400 bis 650 g/mol. Das Molekulargewicht kann gegebenen­ falls jedoch auch größer als 800 g/mol sein. Weiterhin bevor­ zugt weist die metallische Seife ein mindestens zweiwertiges Kation auf. Herausgestellt hat sich des weiteren, daß bei Einsatz von einem oder mehreren der oben angeführten Polymere in Mischung mit einer Metallseife mit einem zweiwertigen Ka­ tion aus den Gruppen II a und II b des Periodensystems, ins­ besondere Magnesium, Calcium und/oder Zink, besonders hydro­ phobe Oberflächen erzielt werden. Insbesondere mit Zinklaurat ergibt sich eine gewünschte einstellbare Hydrophobierung des Vliesfaserstoffes.According to a further development, a carboxylic acid is used which have a molecular weight in a range from about 60 to 800 g / mol. It is preferably in a range of about 400 to 650 g / mol. The molecular weight can be given if, however, be greater than 800 g / mol. Still before the metallic soap has an at least divalent value Cation on. It has also been found that at Use of one or more of the polymers listed above mixed with a metal soap with a divalent Ka tion from groups II a and II b of the periodic table, ins special magnesium, calcium and / or zinc, especially hydro phobic surfaces can be achieved. Especially with zinc laurate  there is a desired adjustable hydrophobization of the Nonwoven fiber.

Bevorzugt ist die Carbonsäure eine Säure mit der allgemeinen Formel H3C(CH2)nCOOH, wobei n = 0 bis 24, bevorzugt 12 bis 22, ist. Die metallische Seife ist vorzugsweise ausgewählt aus einer Gruppe umfassend
The carboxylic acid is preferably an acid with the general formula H 3 C (CH 2 ) n COOH, where n = 0 to 24, preferably 12 to 22. The metallic soap is preferably selected from a group comprising

  • a) Zinklaurat (Zink-Dodecanoat):
    Zn(CH3(CH2)10CO2)2     a) Zinc laurate (zinc dodecanoate):
    Zn (CH 3 (CH 2 ) 10 CO 2 ) 2
  • b) Magnesiummyristat (Magnesium-Tetradecanoat) Mg(CH3(CH2)12CO2)2 b) Magnesium myristate (magnesium tetradecanoate) Mg (CH 3 (CH 2 ) 12 CO 2 ) 2
  • c) Calciumpalmitat (Calcium-Hexadecanoat):
    Ca(CH3(CH2)14CO2)2     c) Calcium palmitate (calcium hexadecanoate):
    Ca (CH 3 (CH 2 ) 14 CO 2 ) 2
  • d) Magnesiumstearat (Magnesium-Octadecanoat):
    Mg(CH3(CH2)16CO2)2     d) Magnesium stearate (magnesium octadecanoate):
    Mg (CH 3 (CH 2 ) 16 CO 2 ) 2
  • e) Calciumbehenat (Calcium-Docosonoat):
    Ca(CH3(CH2)20CO2)2.    e) Calcium behenate (calcium docosonoate):
    Ca (CH 3 (CH 2 ) 20 CO 2 ) 2 .

Besonders bevorzugt ist Zinklaurat (n = 12). Das Zinklaurat ist ein Zinksalz der Laurinsäure, welches durch eine doppelte Umsetzung hergestellt wird. Das Zinklaurat hat vorzugsweise einen freien Fettsäureanteil von unterhalb 1,5% und einen Schmelzpunkt, der zwischen 118°C und 132°C liegt. Der Asche­ gehalt liegt insbesondere zwischen 16% und 20%, kann aber auch darüber oder darunter liegen. Eine bevorzugte Einsatz­ form des Zinklaurats ist als Additiv in Pulverform, das einer Polymerschmelze zugemischt wird.Zinc laurate (n = 12) is particularly preferred. The zinc laurate is a zinc salt of lauric acid, which by a double Implementation is made. The zinc laurate preferably has a free fatty acid content of less than 1.5% and one Melting point, which is between 118 ° C and 132 ° C. The ashes content is in particular between 16% and 20%, but can also lie above or below. A preferred use The form of zinc laurate is in powder form as an additive Polymer melt is mixed.

Die metallische Seife wird in Abhängigkeit von deren Tempera­ turbeständigkeit ausgewählt. Der bevorzugte Stabilitätsbe­ reich ist von der Art der Zuführung der metallischen Seife abhängig. Wird die metallische Seife nach Herstellung des Vliesfaserstoffes aufgebracht, ist eine metallische Seife einsetzbar, die bei Temperaturen von 60°C bei Umgebungsdruck stabil sein muß. Wird die metallische Seife der Schmelze des Polymeren zugeführt, wird eine Temperaturbeständigkeit gewünscht, die über 100°C liegt. Daneben besteht die Möglich­ keit, daß es aufgrund des Temperatureinflusses auch zu einem gewünschten Reaktionsverhalten der metallischen Seife kommt, beispielsweise zu einer Abspaltungsreaktion.The metallic soap depends on its tempera Resistance selected. The preferred stability model is rich in the way of feeding the metallic soap dependent. If the metallic soap is made after the Non-woven fibrous material applied is a metallic soap can be used at temperatures of 60 ° C at ambient pressure must be stable. Will the metallic soap melt the Supplied to polymers, temperature resistance is desired,  which is above 100 ° C. There is also the possibility speed that due to the influence of temperature it also becomes a desired reaction behavior of the metallic soap, for example to a cleavage reaction.

Die verwendete metallische Seife hat vorzugsweise eine Lös­ lichkeit in Wasser von weniger oder gleich etwa 0,01 g/dL in Wasser (15°C).The metallic soap used preferably has a loosening in water of less than or equal to about 0.01 g / dL in Water (15 ° C).

Gemäß einer Weiterbildung wird ein Vliesfaserstoff einge­ setzt, bei dem die Menge der metallischen Seife oder Mischung metallischer Seifen in einem Bereich von etwa 0,2 Gewichts­ prozent bis 20 Gewichtsprozent, vorzugsweise zwischen 0,5 Ge­ wichtsprozent und 8 Gewichtsprozent, bezogen auf die Menge metallischer Seife und den zur Herstellung des Vliesfaser­ stoffes verwendeten Polymeren, beträgt.According to a further development, a nonwoven fibrous material is inserted sets where the amount of metallic soap or mixture metallic soaps in a range of about 0.2 weight percent to 20 percent by weight, preferably between 0.5 Ge percent by weight and 8 percent by weight, based on the amount metallic soap and that used to manufacture the nonwoven fiber substance used polymers.

Ein bevorzugtes Einsatzgebiet für den Vliesfaserstoff ist die Verwendung in einem Hygieneprodukt. Das Hygieneprodukt kann eine Damenbinde, ein Tampon, ein Wundheilverband, eine Win­ del, ein Inkontinenzartikel o. ä. sein. Der Vliesfaserstoff wird insbesondere in denjenigen Bereichen eingesetzt, in de­ nen mit einem Flüssigkeitskontakt zu rechnen ist. Das Produkt kann ein- oder mehrlagig sein, wobei beispielsweise eine ers­ te Lage diesen Vliesfaserstoff aufweisen kann, eine dazu be­ nachbarte Lage dagegen einen anderen Vliesfaserstoff oder ein Tissue. Ein Vliesfaserstoff mit Zinkcarbonsäuren als beige­ setztem Additiv eignet sich als Abdeckung bei Hygieneproduk­ ten wie Wundauflagen, um beispielsweise eine gerichtete Flu­ idbewegung im Hygieneprodukt zu erhalten.A preferred area of use for the nonwoven fibrous material is Use in a hygiene product. The hygiene product can a sanitary napkin, a tampon, a wound dressing, a win del, an incontinence article or the like. The nonwoven fiber fabric is used particularly in those areas in which Liquid contact is to be expected. The product can be one or more layers, for example a first te layer can have this nonwoven fibrous material, one be neighboring layer, on the other hand, another fleece or a Tissue. A non-woven fiber fabric with zinc carboxylic acids as beige The additive is suitable as a cover for hygiene products like wound dressings, for example for a directed flow to maintain id movement in the hygiene product.

Ein weiteres Einsatzgebiet des Vliesfaserstoffs mit einem Zinkcarbonat ist ein Technikprodukt. Als Technikprodukt ist jedes Produkt zu verstehen, das nicht als Hygieneprodukt ein­ gesetzt wird. Darunter können Produkte in der Medikalanwen­ dung, im Baubereich, in Haushaltsgegenständen, im Lebensmit­ telbereich u. a. verstanden werden. Ein derartiges Technikprodukt kann beispielweise als Produkt in oder an Gebäuden ein­ gesetzt sein. Insbesondere sind Produkte bevorzugt, die in Kontakt mit Feuchtigkeit geraten können und dabei feuchtig­ keitsabweisend sein sollen.Another area of application of the nonwoven fiber with one Zinc carbonate is a technical product. As a technical product to understand any product that is not a hygiene product is set. These include products in medical applications dung, in construction, in household items, in food telbereich u. a. be understood. Such a technology product  can be used as a product in or on buildings be set. In particular, products are preferred which are in May come into contact with moisture and be damp are supposed to be repellent.

Ein Produkt aus dem erfindungsgemäßen Vliesfaserstoff kann diesen innerhalb wie auch außerhalb aufweisen. Dazu kann das Produkt auch mehrere Lagen Vliesstoff aufweisen, die insbe­ sondere auch unterschiedliche hydrophobe Eigenschaften haben. Auch kann das Produkt eine Kombination aus Vliesstoff und Film aufweisen.A product made from the nonwoven fibrous material according to the invention can have this inside as well as outside. This can be done Product also have several layers of nonwoven, in particular also have different hydrophobic properties. The product can also be a combination of nonwoven and Feature film.

Weitere Additive können dem Vliesstoff zugegeben sein und diesem weitere Eigenschaften verleihen, beispielsweise eine Oberflächenleitfähigkeit, einen erhöhten Weißegrad, eine ge­ wisse Steifigkeit oder dergleichen.Other additives can be added to the nonwoven and give it further properties, for example a Surface conductivity, an increased degree of whiteness, a ge know stiffness or the like.

Der Vliesfaserstoff ist nach seiner Herstellung auch weiter­ verarbeitbar. Beispielsweise wird dem Vliesfaserstoff eine Substanz aufgesprüht, die eine zusätzliche Eigenschaft auf dem Vliesfaserstoff bewirkt. Auch ist der Vliesfaserstoff mit einem Antistatikmittel, einem antibateriellen Mittel oder auch mit Pigmenten, beispielsweise in Form von Druckfarbe be­ handelbar.The nonwoven fibrous material is also further after its production processable. For example, a Substance sprayed on that has an additional property the nonwoven fibrous material. The fleece fiber is also included an antistatic agent, an antibaterial agent, or also with pigments, for example in the form of printing ink tradable.

Bevorzugter Ausgangsstoff für den Vliesfaserstoff ist ein Po­ lyolefin. Darüber hinaus besteht auch die Möglichkeit, andere Ausgangsstoffe einzusetzen wie Polyamide, Polyester, Poly­ ether und/oder Polyesterether sowie Mischungen daraus, bei­ spielsweise in Form einer Bikomponentenfaser. Bei einem Meltblown-Prozeß weist das verwendete Polymer oder die Poly­ mermischung vorzugsweise einen MFI in einem Bereich von 400 bis 5.000 g/10 min auf, gemessen gemäß DIN 53735. Auch können die verwendeten thermoplastischen Polymere Homopolymere, Co­ polymere, auch Mischungen dieser sein. Verwendbare Polyolefi­ ne können Homopolymere und/oder Copolymere, basierend auf E­ thylen und/oder Propylen, und Mischungen dieser sein. Bevorzugt werden isotaktische thermoplastische Polymere verwendet wie beispielsweise isotaktisches Polypropylen.A preferred starting material for the nonwoven fibrous material is a bottom lyolefin. There is also the possibility of others Use raw materials such as polyamides, polyesters, poly ether and / or polyester ether and mixtures thereof, at for example in the form of a bicomponent fiber. At a Meltblown process has the polymer or poly used mixture preferably an MFI in a range of 400 up to 5,000 g / 10 min, measured according to DIN 53735. Also can the thermoplastic polymers used homopolymers, Co polymers, also mixtures of these. Applicable polyolefi ne can be homopolymers and / or copolymers based on E ethylene and / or propylene, and mixtures of these. Prefers  isotactic thermoplastic polymers are used such as isotactic polypropylene.

Der Vliesfaserstoff wird beispielsweise in einem Produkt ein­ gesetzt, das den Vliesfaserstoff zumindest teilweise in einer Außenlage des Produktes aufweist. Damit wird das Produkt in zumindest einem gezielten Außenbereich hydrophob, während es in anderen Außenbereichen beispielsweise hydrophil oder auf­ grund der Verwendung beispielsweise eines Filmes oder Folie vollständig wasserundurchlässig sein kann. Produkte können auch einen erfindungsgemäßen Vliesfaserstoff als Außenver­ kleidung von Verpackungen, als Inneneinkleidung von Gehäusen jeder Art wie Kartonagen, Schalen oder anderen Hohlräumen, als Auflage von Gegenständen wie Betten, Tischen oder anderen Gebrauchsgegenständen des täglichen Lebens sein. Des weiteren ist der Vliesfaserstoff in weiteren technischen Bereichen einsetzbar wie Filteranlagen, Schutzbekleidungen, Kleidungs­ stücken allgemein, als Randabdeckungen oder Auflageflächen etc.The nonwoven fibrous material is used, for example, in a product set that the nonwoven fibrous material at least partially in one The outer layer of the product. So that the product is in at least one targeted exterior hydrophobic while it in other outdoor areas, for example, hydrophilic or due to the use of a film or foil, for example can be completely impermeable to water. Products can also a nonwoven fibrous material according to the invention as Außenver clothing of packaging, as inner lining of housings any kind like cardboard boxes, trays or other cavities, as a support for objects such as beds, tables or others Everyday objects. Furthermore is the nonwoven fiber material in other technical areas can be used like filter systems, protective clothing, clothing pieces generally, as edge covers or contact surfaces Etc.

Gemäß der Erfindung wird weiterhin ein Verfahren zur Herstel­ lung eines Vliesfaserstoffes aus einer zumindest ein Polymer aufweisenden Schmelze Vorgeschlagen, wobei zur Erhöhung einer hydrophoben, alkoholabweisenden Eigenschaft des Vliesfaser­ stoffes mindestens eine metallische Seife zugesetzt wird. Die metallische Seife kann so wie oben beschrieben sein.According to the invention, a method for manufacturing is furthermore development of a nonwoven fibrous material from at least one polymer Having proposed melt, whereby to increase a hydrophobic, alcohol-repellent property of the non-woven fiber substance at least one metallic soap is added. The metallic soap can be as described above.

Vorzugsweise wird die metallische Seife vor und/oder während der Faserbildung aufgesprüht. Bevorzugt wird die metallische Seife während und/oder nach der Faserbildung aufgesprüht.The metallic soap is preferably used before and / or during sprayed on the fiber formation. The metallic one is preferred Soap sprayed on during and / or after fiber formation.

Als ein weiterer Effekt hat sich bei der Verwendung einer me­ tallischen Seife herausgestellt, daß der Vliesfaserstoff wei­ cher ist als ein Vliesfaserstoff ohne metallische Seife, ins­ besondere wenn die metallische Seife vor der Faserbildung zu­ geführt wird. Another effect has been found when using a me tallish soap found that the nonwoven fibrous white is a non-woven fiber fabric without metallic soap, ins especially if the metallic soap closes before fiber formation to be led.  

Um eine gute Vliesherstellung wie aber auch Lagerhaltung und Einstellung der hydrophoben Eigenschaft des Vliesfaserstoffes gezielt einstellen zu können, wird der Zusatz vorzugsweise in Form eines höherkonzentrierten Masterbatch dem Polymer oder der Polymermischung beigefügt.For good nonwoven production as well as warehousing and Adjustment of the hydrophobic property of the nonwoven fiber material To be able to adjust specifically, the addition is preferably in Form a higher concentrated masterbatch the polymer or added to the polymer mixture.

Die folgende Tabelle zeigt weitere mögliche Kombinationen von metallischen Seifen, die als Zusatz verwendet werden können, wobei deren Löslichkeit als ein berücksichtigbares Kriterium mitangegeben ist.:
The following table shows other possible combinations of metallic soaps that can be used as additives, the solubility of which is given as a criterion that can be taken into account:

Bevorzugt ist ein Zusatz, der vollständig oder zumindest wei­ testgehend vollständig nicht löslich in Alkohol ist.An additive that is complete or at least white is preferred is completely insoluble in alcohol.

Der beschriebene Vliesfaserstoff eignet sich besonders bei derartigen Produkten und Anwendungen, bei denen ein direkter Hautkontakt des Vliesfaserstoffes mit einem Lebewesen auftre­ ten kann. Dieser Hautkontakt kann auch länger andauernd sein.The nonwoven fiber fabric described is particularly suitable for such products and applications where a direct Skin contact of the nonwoven fiber material occurs with a living being can. This skin contact can also last longer.

Der Vliesfaserstoff ist mittels eines Meltblown- oder eines Spunbondverfahrens herstellbar. Der Vliesstoff kann ein- oder mehrlagig aufgebaut sein, beispielsweise mit einem zusätzli­ chen Film. Der Film ist beispielsweise wasserdampfdurchläs­ sig, dagegen jedoch wasserundurchlässig. Desweiteren kann ein hergestelltes Produkt den Vliesfaserstoff in Form einer S-, M-, einer SMS-, einer SMMS-, einer MSMS-Schicht oder ähnli­ chem aufweisen, wobei zumindest eine dieser Lagen eine metal­ lische Seife aufweist. Beispielsweise kann auch eine erste Lage einen höheren Anteil an einer metallischen Seife aufwei­ sen als eine zweite Lage im Produkt. Insbesondere besteht auch die Möglichkeit, den Vliesfaserstoff mit einer metalli­ schen Seife als Filter jeglicher Atz zu nutzen.The nonwoven fibrous material is by means of a meltblown or a Spunbond process can be produced. The nonwoven can one or be constructed in several layers, for example with an additional one chen film. For example, the film is permeable to water vapor sig, however, impermeable to water. Furthermore, a manufactured product the nonwoven fibrous material in the form of an S-, M, an SMS, an SMMS, an MSMS layer or similar chem, wherein at least one of these layers has a metal has soap. For example, a first Layer a higher proportion of a metallic soap as a second layer in the product. In particular, there is also the possibility of the nonwoven fiber with a metallic to use soap as a filter of any kind.

Diese und weitere Vorteile der Erfindung werden anhand der folgenden Zeichnungen beschrieben. Dabei zeigen:These and other advantages of the invention will become apparent from the following drawings. Show:

Fig. 1 ein Technikprodukt, Fig. 1 is a technique product,

Fig. 2 ein Hygieneprodukt und Fig. 2 is a hygiene product and

Fig. 3 einen möglichen Aufbau eines verwendbaren Verbundsystems. Fig. 3 shows a possible structure of a composite system that can be used.

Fig. 1 zeigt einen ersten Vliesfaserstoff 1 in einem Technik­ produkt 2. Der Vliesfaserstoff 1 weist einen Zusatz 6 (metal­ lische Seife) zur Hydrophobisierung auf. Der Zusatz 6 ist an­ gedeutet und kann entweder über den gesamten Querschnitt ei­ ner Faser des Vliesfaserstoffes 1 vorliegen, vermehrt nur entlang eines Umfanges einer Faser oder beispielsweise auf­ grund eines Aufsprühens nur auf den Umfang der Faser. Weiter­ hin bildet der erste Vliesfaserstoff 1 eine Außenschicht 3 eines Filters. Der Außenschicht 3 nachgeschaltet ist eine Zwischenschicht 4. Während die Außenschicht 3 eher grobe Ma­ terialien herausfiltert, filtert die Zwischenschicht 4 feine­ re Materialien heraus. Die Zwischenschicht 4 kann beispiels­ weise besonders hydrophil eingestellt werden. Dadurch kann die Zwischenschicht 4 auch als Speicher dienen. An die Zwi­ schenschicht 4 angrenzend ist eine Innenschicht 5, die vor­ zugsweise den gleichen Vliesfaserstoff 1 wie die Außenschicht 3 aufweist. Die Innenschicht 5 wie auch die Außenschicht 3 können vorzugsweise durch die verwendete metallische Seife antistatisch sein. Fig. 1 shows a first nonwoven fiber 1 in a technology Product 2. The nonwoven fibrous material 1 has an additive 6 (metallic soap) for hydrophobization. The addition 6 is indicated and can either be present over the entire cross-section of a fiber of the nonwoven fiber material 1 , increasingly only along a circumference of a fiber or, for example, due to spraying only onto the circumference of the fiber. Furthermore, the first nonwoven fibrous material 1 forms an outer layer 3 of a filter. An intermediate layer 4 is arranged downstream of the outer layer 3 . While the outer layer 3 filters out rather coarse materials, the intermediate layer 4 filters out fine materials. The intermediate layer 4 can, for example, be adjusted to be particularly hydrophilic. As a result, the intermediate layer 4 can also serve as a memory. Adjacent to the intermediate layer 4 is an inner layer 5 , which preferably has the same nonwoven fibrous material 1 as the outer layer 3 . The inner layer 5 as well as the outer layer 3 can preferably be antistatic due to the metallic soap used.

Fig. 2 zeigt ein Hygieneprodukt 7 in der Form einer Windel 8. Die Windel 8 weist einen ersten Bereich 9 auf, der aus einem zweiten Vliesfaserstoff 10 ist, der mit einer metallischen Seife zur Hydrophobisierung ausgestattet ist. Der erste Be­ reich 9 umgibt einen zweiten Bereich 11, der beispielsweise einen dritten Vliesfaserstoff 12 hat. Dieser kann durch einen entsprechenden Zusatz, beispielsweise Zinklaurat, eine noch größere hydrophobe Wirkung aufweisen als der zweite Vliesfa­ serstoff 10. In einem dritten Bereich 13 kann die Windel 8 einen Film oder Folie aus thermoplastischem Material aufwei­ sen. Fig. 2 shows a hygiene product 7 in the form of a diaper. 8 The diaper 8 has a first area 9 , which is made of a second nonwoven fiber material 10 , which is equipped with a metallic soap for hydrophobization. The first loading area 9 surrounds a second area 11 which , for example, has a third nonwoven fiber material 12 . A corresponding additive, for example zinc laurate, can have an even greater hydrophobic effect than the second nonwoven fabric 10 . In a third area 13 , the diaper 8 can have a film or sheet of thermoplastic material.

Fig. 3 zeigt ein Verbundsystem 14 mit einem vierten Vliesfa­ serstoff 15. An diesen ist eine Spinnfaserschicht 16 angela­ gert, an die wiederum eine gaspermeable Filmschicht 17 an­ grenzt. Der Vliesfaserstoff selbst hat Öffnungen 18, Erhebun­ gen 19 oder Schlaufen 20. Aufgrund der gezielt eingestellten hydrophoben Eigenschaft des Vliesfaserstoffes mittels einer metallischen Seife eignet sich das Verbundsystem wie auch ein Vliesfaserstoff mit einem derartigen Zusatz überhaupt für ei­ nen direkten Hautkontakt, da die metallische Seife sich nicht aus dem Vliesfaserstoff löst und woanders hinwandert. Ande­ rerseits besteht auch die Möglichkeit, eine gezielte Wande­ rung des Zusatzes einstellen zu können, wodurch verschiedene Schichten unterschiedlich hydrophob ausgestattet werden. Fig. 3 shows a composite system 14 with a fourth Vliesfa serstoff 15th A spun fiber layer 16 is attached to these, which in turn is adjacent to a gas-permeable film layer 17 . The nonwoven fibrous material itself has openings 18 , conditions 19 or loops 20 . Due to the specifically set hydrophobic property of the nonwoven fiber material by means of a metallic soap, the composite system, like a nonwoven fiber material with such an additive, is suitable at all for direct skin contact, since the metallic soap does not detach from the nonwoven fiber material and migrates elsewhere. On the other hand, there is also the possibility of being able to set a targeted migration of the additive, as a result of which different layers are given different hydrophobic properties.

In einem weiteren Beispiel wurde eine Meltblown-Vliesschicht hergestellt, die eine metallische Seife enthält. Dazu wurden ein Peroxid-enthaltendes Polypropylen mit einem Zinklaurat gemischt. Das Zinklaurat hatte einen Anteil an der Mischung in der Höhe von 2 Gewichtsprozent. Das Zinklaurat wurde von der Firma Bärlocher GmbH bezogen und in Pulverform dem Po­ lypropylen vor dem Extruder beigemengt. Eine Alkoholabweisung der hergestellten Vliesschicht wurde durch die Beobachtung des Grades der Verteilung eines Tropfens aus 60%igem Äthanol auf der Vliesstoffoberfläche gemessen. Während der Tropfen sich auf einer Meltblown-Vliesschicht ohne Zinklaurat ver­ teilte, verteilte sich der Tropfen nicht, wenn die Vlies­ schicht das Zinklaurat enthielt. Den gleichen Effekt erhielt man bei unterschiedlichen Gewichtsprozenten an Zinklaurat im Bereich zwischen 2 Gewichtsprozent und 4 Gewichtsprozent in der Vliesstoffschicht.Another example was a meltblown nonwoven layer made that contains a metallic soap. To do this a peroxide-containing polypropylene with a zinc laurate mixed. The zinc laurate contributed to the mixture in the amount of 2 percent by weight. The zinc laurate was from sourced from Bärlocher GmbH and in powder form to the bottom lypropylene added before the extruder. An alcohol rejection The nonwoven layer was made by observation the degree of distribution of a drop of 60% ethanol measured on the nonwoven surface. During the drop ver on a meltblown non-woven layer without zinc laurate shared, the drop did not spread when the fleece layer containing zinc laurate. Got the same effect one with different weight percentages of zinc laurate in Range between 2 weight percent and 4 weight percent in the nonwoven layer.

Claims (16)

1. Vliesfaserstoff, insbesondere Meltblown-Vliesfaserstoff (1; 10; 12; 15), umfassend zur Erhöhung einer hydrophoben, alkoholabweisenden Eigenschaft des Vliesfaserstoffes (1; 10; 12; 15) mindestens eine metallische Seife (6).1. Nonwoven fiber fabric, in particular meltblown nonwoven fiber fabric ( 1 ; 10 ; 12 ; 15 ), comprising at least one metallic soap ( 6 ) to increase the hydrophobic, alcohol-repellent property of the nonwoven fiber fabric ( 1 ; 10 ; 12 ; 15 ). 2. Vliesfaserstoff (1; 10; 12; 15) nach Anspruch 1, dadurch gekennzeichnet, daß die metallische Seife (6) aus Carbonsäure hergestellt ist.2. nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to claim 1, characterized in that the metallic soap ( 6 ) is made of carboxylic acid. 3. Vliesfaserstoff (1; 10; 12; 15) nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Carbonsäure ein Molekularge­ wicht in einem Bereich von etwa 60 bis etwa 800 g/mol auf­ weist.3. nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to claim 1 or 2, characterized in that the carboxylic acid has a molecular weight in a range from about 60 to about 800 g / mol. 4. Vliesfaserstoff (1; 10; 12; 15) nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, daß die metallische Seife (6) ein mindestens zweiwertiges Kation aufweist.4. nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to one of claims 1 to 3, characterized in that the metallic soap ( 6 ) has an at least divalent cation. 5. Vliesfaserstoff (1; 10; 12; 15) nach Anspruch 4, dadurch gekennzeichnet, daß als zweiwertiges Kation ein Kation ausge­ wählt ist aus den Gruppen II a und II b des Periodensystems.5. nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to claim 4, characterized in that a cation is selected as the divalent cation from groups II a and II b of the periodic table. 6. Vliesfaserstoff (1; 10; 12; 15) nach einem der vorherge­ henden Ansprüche, dadurch gekennzeichnet, daß die Carbonsäure eine Fettsäure mit der allgemeinen Formel H3C(CH2)n COOH ist, wobei n = 0 bis 24, bevorzugt 12 bis 22, ist.6. nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to one of the preceding claims, characterized in that the carboxylic acid is a fatty acid with the general formula H 3 C (CH 2 ) n COOH, where n = 0 to 24, preferably 12 to 22. 7. Vliesfaserstoff (1; 10; 12; 15) nach einem der vorherge­ henden Ansprüche, dadurch gekennzeichnet, daß die metallische Seife (6) ausgewählt ist aus einer Gruppe umfassend Zinklau­ rat, Magnesiummyristat, Calciumpalmitat, Megnesiumstearat und/oder Calciumbehenat.7. nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to one of the preceding claims, characterized in that the metallic soap ( 6 ) is selected from a group comprising zinc laurate, magnesium myristate, calcium palmitate, magnesium stearate and / or calcium behenate. 8. Vliesfaserstoff (1; 10; 12; 15) nach einem der vorherge­ henden Ansprüche, dadurch gekennzeichnet, daß die metallische Seife (6) in einer Menge in einem Bereich von etwa 0,2 Ge­ wichtsprozent bis etwa 20 Gewichtsprozent, vorzugsweise in einem Bereich von etwa 0,5 Gewichtsprozent bis etwa 8 Ge­ wichtsprozent, bezogen auf die Menge an metallischer Seife (6) und dem zur Herstellung des Vliesfaserstoffes (1; 10; 12; 15) verwendeten Polymeren, zugegeben ist.8. Nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to one of the preceding claims, characterized in that the metallic soap ( 6 ) in an amount in a range from about 0.2% by weight to about 20% by weight, preferably in one Range from about 0.5 percent by weight to about 8 percent by weight, based on the amount of metallic soap ( 6 ) and the polymer used to produce the nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ), is added. 9. Vliesfaserstoff (1; 10; 12; 15) nach einem der vorherge­ henden Ansprüche, dadurch gekennzeichnet, daß die metallische Seife (6) auf dem Vliesfaserstoff (1; 10; 12; 15) aufgesprüht ist.9. nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to one of the preceding claims, characterized in that the metallic soap ( 6 ) is sprayed onto the nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ). 10. Verfahren zur Herstellung eines Vliesfaserstoffes (1; 10; 12; 15) nach einem der Ansprüche 1 bis 9 aus einer zumindest ein Polymer aufweisenden Schmelze, wobei zur Erhöhung einer hydrophoben, alkoholabweisenden Eigenschaft des Vliesfaser­ stoffes (1; 10; 12; 15) mindestens eine metallische Seife (6) zugesetzt wird.10. A method for producing a nonwoven fiber material ( 1 ; 10 ; 12 ; 15 ) according to one of claims 1 to 9 from a melt having at least one polymer, wherein to increase a hydrophobic, alcohol-repellent property of the nonwoven fiber material ( 1 ; 10 ; 12 ; 15 ) at least one metallic soap ( 6 ) is added. 11. Verfahren nach Anspruch 10, dadurch gekennzeichnet, daß die metallische Seife (6) vor und/oder während der Faserbil­ dung zugeführt wird.11. The method according to claim 10, characterized in that the metallic soap ( 6 ) is supplied before and / or during the formation of fibers. 12. Verfahren nach Anspruch 11, dadurch gekennzeichnet, daß die metallische Seife (6) während und/oder nach der Faserbil­ dung auf die Fasern aufgesprüht wird.12. The method according to claim 11, characterized in that the metallic soap ( 6 ) is sprayed onto the fibers during and / or after the formation of the fibers. 13. Verfahren nach einem der Ansprüche 10 bis 12, dadurch ge­ kennzeichnet, daß der Schmelze zwischen 0,2 und 20 Gewichts­ prozent, bezogen auf die Menge an metallischer Seife und den zur Herstellung des Vliesfaserstoffes verwendeten Polymeren, der metallischen Seife (6) zugemischt wird.13. The method according to any one of claims 10 to 12, characterized in that the melt between 0.2 and 20 weight percent, based on the amount of metallic soap and the polymers used to produce the nonwoven fiber material, the metallic soap ( 6 ) admixed becomes. 14. Verwendung eines Vliesfaserstoffes (1; 10; 12; 15) nach einem der vorhergehenden Ansprüche als Technikprodukt und/oder Hygieneprodukt, insbesondere in Damenbinden, Tampons, Verbundstoffen, Windeln, Inkontinenzprodukten und Ver­ packungen.14. Use of a nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ) according to one of the preceding claims as a technical product and / or hygiene product, in particular in sanitary napkins, tampons, composites, diapers, incontinence products and packaging. 15. Alkoholabweisendes Hydrophobierungsmittel für einen Vliesfaserstoff (1; 10; 12; 15), dadurch gekennzeichnet, daß dieses eine metallische Seife (6) nach einem der vorhergehen­ den Ansprüche ist.15. alcohol-repellent hydrophobizing agent for a nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ), characterized in that this is a metallic soap ( 6 ) according to one of the preceding claims. 16. Verwendung einer metallischen Seife (6) als Zusatz bei der Herstellung eines Vliesfaserstoffes (1; 10; 12; 15).16. Use of a metallic soap ( 6 ) as an additive in the production of a nonwoven fibrous material ( 1 ; 10 ; 12 ; 15 ).
DE10028215A 2000-06-09 2000-06-09 Melt-blown fiber fleece, for use in e.g. sanitary towels and tampons, contains a metal soap to increase its hydrophobic and alcohol-resisting properties Ceased DE10028215A1 (en)