DE10024946A1 - Tannin-containing binder liquor for use along with other binders in chip- or fiber-board production, obtained by conventional extraction of bark and then using the extract to break down waste aminoplast-bonded wood materials - Google Patents

Tannin-containing binder liquor for use along with other binders in chip- or fiber-board production, obtained by conventional extraction of bark and then using the extract to break down waste aminoplast-bonded wood materials

Info

Publication number
DE10024946A1
DE10024946A1 DE2000124946 DE10024946A DE10024946A1 DE 10024946 A1 DE10024946 A1 DE 10024946A1 DE 2000124946 DE2000124946 DE 2000124946 DE 10024946 A DE10024946 A DE 10024946A DE 10024946 A1 DE10024946 A1 DE 10024946A1
Authority
DE
Germany
Prior art keywords
bark
tannin
wood
binder
chipboard
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE2000124946
Other languages
German (de)
Inventor
Edmone Roffael
Heinz Schmidt
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE2000124946 priority Critical patent/DE10024946A1/en
Publication of DE10024946A1 publication Critical patent/DE10024946A1/en
Pending legal-status Critical Current

Abstract

Production of a tannin-containing binder liquor from tannin-containing bark and used or waste aminoplast-bonded used wood materials comprising extracting the bark with hot water in a conventional single-stage or multi-stage process and then using the extract to break down the used aminoplast-bonded wood, is new. Independent claims are also included for the following: (1) using the extracted bark as a raw material for energy generation or after fermenting, as a soil improver; and (2) using the broken-down used wood material as a material for chip- or fiber-board.

Description

Die Erfindung betrifft ein Verfahren zur Herstellung einer Bindemittelflotte für Lignocellulosen, insbesondere für Fasern, Späne und Furniere zum Zweck der Holzwerkstoffherstellung. Für die Herstellung von Holzwerkstoffen werden in der Regel Holzzerkleinerungsprodukte wie Furniere, Späne und Fasern mit einem Bindemittel versehen und anschließend, ggf. nach einem Trocknungvorgang, zu Holzwerkstoffen, zusammengepresst. Der Pressvorgang erfolgt üblicherweise unter Anwendung von Wärme und Druck. Er kann auch ohne Anwendung von Wärme oder Druck vonstatten gehen, wenn bestimmte Plattentypen hergestellt werden. Je nach verwendetem Bindemittel und dem herzustellenden Holzwerkstoff sind die Herstellungsbedingungen unterschiedlich. Für die Herstellung von Holzspanplatten werden z. B. in der Regel die Späne zunächst auf eine Feuchte von 1-5% getrocknet, mit einem Bindemittel versehen, zu Spanmatten gestreut und anschließend zu Spanplatten gepresst. Bei der Herstellung von mitteldichten Faserplatten (MDF) nach dem Blow-Line-Verfahren werden die Fasern zuerst mit dem Bindemittel versehen, anschließend bis zu einer Feuchte von maximal 15% getrocknet, zu Fasermatten gestreut und heiß gepresst. Für die Herstellung von Spänen und Fasern muss das Holz in der Regel entrindet werden. Die anfallenden Rinden gelten als Abfall und werden üblicherweise verbrannt. Bestimmte Rinden wie Fichtenrinde enthalten Tannin, das ein Bindungspotential entfalten kann.The invention relates to a method for producing a binder liquor for Lignocelluloses, especially for fibers, chips and veneers for the purpose of Manufacture of engineered wood. For the production of wood-based materials, the Usually wood shredding products such as veneers, chips and fibers with one Provide binder and then, if necessary after a drying process Wood materials, pressed together. The pressing process is usually carried out under Application of heat and pressure. It can also be used without heat or Printing occurs when certain types of plates are manufactured. Depending on The binder used and the wood material to be manufactured are the Manufacturing conditions vary. For the production of chipboard z. B. as a rule, the chips are first dried to a moisture content of 1-5%, provided with a binder, sprinkled into chip mats and then closed Chipboard pressed. In the manufacture of medium density fiberboard (MDF) the blow-line process, the fibers are first provided with the binder, then dried to a maximum moisture of 15% to fiber mats sprinkled and hot pressed. For the production of chips and fibers this has to be done Wood is usually debarked. The resulting bark is considered waste and are usually burned. Contain certain barks such as spruce bark Tannin, which can develop a binding potential.

Als Bindemittel für die Herstellung von Holzwerkstoffen werden Harze der Aminoplast- und Phenoplastgruppe wie Harnstoffformaldehydharze (UF-Harze) und Phenolformaldehydharze (PF-Harze) verwendet. Auch Klebstoffe auf Basis von polymeren Diisocyanaten (PMDI) können eingesetzt werden. Andere Bindemittel wie Tanninformaldehydharze (TF-Harze) und Ligninsulfonate (LS) haben hierfür vergleichsweise nur eine geringe Bedeutung erlangen können.Resins are used as binders for the production of wood-based materials Aminoplast and phenoplast group such as urea formaldehyde resins (UF resins) and Phenol formaldehyde resins (PF resins) are used. Also adhesives based on polymeric diisocyanates (PMDI) can be used. Other binders like For this purpose, tannin formaldehyde resins (TF resins) and lignin sulfonates (LS) are used can be comparatively of little importance.

Nach dem Gebrauch müssen die bindemittelhaltigen Holzwerkstoffe einer stofflichen oder thermischen Verwertung zugeführt werden oder anderweitig entsorgt werden. Es sind verschiedene Verfahren zum Recycling von Holzwerkstoffen bekannt geworden. So ist z. B. bekannt, gebrauchte Holzspanplatten einer thermischen Dampfbehandlung zu unterziehen (DE-OS 195 09 152), ferner ist es bekannt, bindemittelhaltige Holzwerkstoffe chemisch-thermisch aufzulösen (DE-PS 43 34 422). After use, the wood-based materials containing the binder must have a material or thermal recovery or otherwise disposed of. Various methods for recycling wood-based materials are known become. So z. B. known, used chipboard thermal To undergo steam treatment (DE-OS 195 09 152), it is also known to dissolve wood-based materials containing binders chemically and thermally (DE-PS 43 34 422).  

Des weiteres ist es bekannt, gebrauchte Holzspan- und Holzfaserplatten bzw. deren Zerkleinerungsprodukte mit Tannin als Bindemittel zu neuen Spanplatten zu verleimen (DE-OS 195 26 667).Furthermore, it is known to use used chipboard and fiberboard or their Shredding products with tannin as a binder to new chipboard glue (DE-OS 195 26 667).

Es wurde nun überraschend gefunden, dass man aus tanninhaltigen Rinden wie Fichtenrinde und Gebrauchtholzwerkstoffe wie Span- und Faserplatten, die ein Aminoplastharz als Bindemittel enthalten, eine reaktive Bindemittelflotte für die Herstellung von Holzwerkstoffen wie folgt beschrieben herstellen kann: Die Rinde wird mit heißem Wasser extrahiert und der heiße Rindenextrakt ggf. nach einer Aufkonzentrationsstufe mit Zerkleinerungsprodukten von mit Aminoplastharz gebundenen Holzspan- und Holzfaserplatten zusammengebracht. Insofern werden die Gebrauchtholzplatten mit einer Tanninlösung aufgeschlossen. Durch diese Vorgehensweise geht das in Gebrauchtspan- oder Faserplatten vorhandene Aminoplastharz teilweise in Lösung und reagiert mit den Tanninen unter Bildung von einer reaktiven Bindemittelflotte, die geeignet ist, als Bindemittel oder als Bindemittelkomponente bei der Herstellung von Span- und/oder Faserplatten eingesetzt zu werden. Für die Rindenextraktion können dem Heißwasser auch Abwasser aus im Nassverfahren arbeitenden "Reinigungssystemen der Holzwerkstoffindustrie, die z. B. an Trockner und Pressen angeschlossen sind, beigemengt werden.It has now surprisingly been found that bark containing tannins such as Spruce bark and used wood materials such as chipboard and fiberboard, the one Contain aminoplast resin as a binder, a reactive binder fleet for the Manufacture of wood-based materials can be described as follows: The bark is extracted with hot water and the hot bark extract if necessary after a Concentration stage with crushing products from with aminoplast resin bonded chipboard and fibreboard brought together. To that extent the used wood panels digested with a tannin solution. Through this The procedure is the same as in existing chipboard or fiberboard Aminoplast resin partially in solution and reacts with the tannins to form a reactive binder liquor which is suitable as a binder or as Binder component in the production of chipboard and / or fiberboard to be used. Hot water can also be used for bark extraction Waste water from "cleaning systems of the Wood-based materials industry, the z. B. are connected to dryers and presses, be added.

Im Bild ist diese Vorgehensweise gezeigt. Im Druckbehälter (1) wird die tanninhaltige Rinde z. B. Fichtenrinde mit Wasser bei Temperaturen zwischen 70-140°C extrahiert. Zur Beschleunigung der Extraktion können im Extraktionsprozess Stoffe wie Harnstoff zugegeben werden. Nach der Extraktion wird die noch heiße tanninhaltige Flotte einem aufgeheizten zweiten Behälter (2) zugeführt, in dem die tanninhaltige Flotte auf eine Konzentration von 20-25% durch Verdampfen aufkonzentriert wird. Der entweichende Dampf aus dem Zwischenbehälter lässt sich für eine wiederholte Extraktion von Rinde einsetzen. Die tanninhaltige Bindemittelflotte wird einem Zwischenbehälter (3) zugeführt. Die Flotte in den Zwischenbehältern lässt man auf Zerkleinerungsprodukten von aminoplasthaltigen Gebrauchtholzwerkstoffen im Behälter (4) bei Temperaturen von 100-120°C einwirken. Die auf diese Weise durch chemische Wechselwirkung zwischen der tanninhaltigen Lösung und den Gebrauchtplatten entstehenden Flotte ist ein Bindemittel, das bei der Herstellung von Holzwerkstoffen für sich allein oder in Kombination mit anderen Bindemitteln eingesetzt werden kann.This procedure is shown in the picture. In the pressure vessel ( 1 ) the tannic bark is z. B. Spruce bark extracted with water at temperatures between 70-140 ° C. To accelerate the extraction, substances such as urea can be added in the extraction process. After the extraction, the still hot tannin-containing liquor is fed to a heated second container ( 2 ), in which the tannin-containing liquor is concentrated to a concentration of 20-25% by evaporation. The escaping steam from the intermediate container can be used for repeated extraction of bark. The tannin-containing binder liquor is fed to an intermediate container ( 3 ). The liquor in the intermediate containers is allowed to act on comminution products of aminoplast-containing used wood materials in the container ( 4 ) at temperatures of 100-120 ° C. The resulting fleet through chemical interaction between the tannin-containing solution and the used panels is a binder that can be used in the manufacture of wood-based materials alone or in combination with other binders.

Die extrahierte Rinde lässt sich nach der Extraktion thermisch verwerten oder nach einem Fermentierungsvorgang als Rindenkompost einsetzen. Bei einer etwaigen thermischen Nutzung der Rinde kann die gewonnene Wärmeenergie für die Beheizung des Extraktionsbehälters verwendet werden. Die mit einer tanninhaltigen Lösung extrahierten aminoplasthaltigen Zerkleinerungsprodukte der Holzwerkstoffe können der weiteren Verarbeitung in einem Span- und/oder Faserwerk zugeführt werden oder ebenfalls thermisch verwertet werden. Die Leimflotte lässt sich zur Streckung von Bindemitteln wie Tanninformaldehydharzen einsetzen. Auch andere Bindemittel wie Phenolformaldehydharze, Harnstoffformaldehydharze und Klebstoffe auf Basis von PMDI lassen sich durch die auf diese Weise gewonnene Bindemittelkomponente strecken. Das folgende Beispiel verdeutlicht die Erfindung ohne sie einzuschränken.The extracted bark can be used thermally after extraction or after use as a bark compost in a fermentation process. If there is any Thermal use of the bark can be used for the thermal energy gained Heating of the extraction container can be used. The one with a tannic content Solution extracted crushed wood products containing aminoplast can be further processed in a chip and / or fiber mill are or are also used thermally. The glue liquor can be used Use stretching of binders such as tannin formaldehyde resins. Others too Binders such as phenol formaldehyde resins, urea formaldehyde resins and adhesives based on PMDI can be obtained through the Stretch the binder component. The following example illustrates the invention without restricting them.

Holzspäne wurden bis zu einer Feuchte von 2% getrocknet und anschließend mit einer Leimflotte, gewichtsmäßig aus 70% eines Tanninformaldehydharzes und 30% einer nach der beschriebenen Erfindung hergestellten Bindemittelflotte bestehend, beleimt. Der Bindemittelaufwand betrug 10% (Feststoff bezogen auf atro Holzspäne). Nach dem Beleimen wurden die Holzspäne zu 20 mm dicken Holzspanplatten gepresst. Zum Vergleich wurden Holzspanplatten hergestellt, die nur das Tanninformaldehydharz enthalten. Auch hier war der Bindemittelaufwand 10% (Feststoff bezogen auf atro Späne). Die Presszeit für die Herstellung der Platten betrug jeweils 6 Minuten.Wood chips were dried to a moisture of 2% and then with a glue liquor, based on weight of 70% of a tannin formaldehyde resin and 30% consisting of a binder liquor produced according to the described invention, glued. The binder expenditure was 10% (solids based on atro Wood chips). After gluing, the wood chips became 20 mm thick Chipboard pressed. For comparison, chipboard was produced, the contain only the tannin formaldehyde resin. Here, too, was the amount of binder 10% (solid based on dry chips). The press time for making the Plates were 6 minutes each.

Die an den hergestellten Spanplatten ermittelten physikalisch-technologischen Eigenschaften sind in Tab. 1 zusammengestellt The physical and technological properties determined on the chipboard produced are summarized in Table 1

Aus den Ergebnissen wird ersichtlich, dass die Beträge für die mechanisch-technologischen Eigenschaften der unter Einsatz der erfindungsgemäßen Bindemittelflotte hergestellen Spanplatten weitgehend denen entsprechen, die unter alleinigem Einsatz von Tanninformaldehydharzen hergestellt sind.The results show that the amounts for the mechanical-technological properties of using the invention Binder fleece manufactured chipboard largely correspond to those under sole use of tannin formaldehyde resins.

Claims (16)

1. Verfahren zur Herstellung einer tanninhaltigen Bindemittelflotte aus tanninhaltigen Rinden und mit Aminoplastharzen gebundenen gebrauchten Holzwerkstoffen, dadurch gekennzeichnet, dass die tanninhaltigen Rinden in bekannter Weise mit heißem Wasser einstufig oder mehrstufig extrahiert werden und anschließend der gewonnene Extrakt für den Aufschluss von aminoplastgebundenen Holzwerkstoffen bei hohen Temperaturen verwendet wird.1. A process for the production of a tannin-containing binder fleet from tannin-containing bark and used wood-based materials bonded with aminoplast resins, characterized in that the tannin-containing bark is extracted in a known manner with hot water in one or more stages and then the extract obtained for the digestion of aminoplast-bound wood-based materials at high temperatures is used. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die extrahierte Rinde eine Fichtenrinde und der aufzuschließende Holzwerkstoff eine Spanplatte und/oder eine mitteldichte Faserplatte (MDF) und/oder Oriented Strand Board (OSB) und/oder eine Hartfaserplatte ist.2. The method according to claim 1, characterized in that the extracted bark a spruce bark and the wood material to be broken up a chipboard and / or a medium density fiberboard (MDF) and / or oriented strand board (OSB) and / or a hardboard. 3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die extrahierte Rinde eine Kiefernrinde und der aufzuschließende Holzwerkstoff eine Spanplatte und/oder mitteldichte Faserplatte (MDF) ist.3. The method according to claim 1, characterized in that the extracted bark a pine bark and the wood material to be broken up a chipboard and / or medium density fiberboard (MDF). 4. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass die Extraktion der Rinde bei Temperaturen zwischen 70 und 140°C erfolgt.4. The method according to claim 1, characterized in that the extraction of the Bark occurs at temperatures between 70 and 140 ° C. 5. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass der Aufschluss des Holzwerkstoffes mit Tanninlösung bei Temperaturen zwischen 80 und 140°C erfolgt.5. The method according to claim 1, characterized in that the digestion of the Wood material with tannin solution at temperatures between 80 and 140 ° C he follows. 6. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass dem Heisswasser für die Extraktion Abwasser aus im Nassverfahren arbeitenden Abluftreinigungssystemen der Trockner- bzw. Pressenabluft beispielsweise von Spanplattenanlagen zugemischt wird.6. The method according to claim 1, characterized in that the hot water for the extraction of wastewater from wet process workers Exhaust air purification systems of the dryer or press exhaust air, for example from Chipboard plants is added. 7. Verwendung der nach Anspruch 1, anfallenden Leimflotte als Bindemittel in Kombination mit Holzwerkstoff-Bindemitteln, insbesondere mit Phenolformaldehydharzen, Tanninformaldehydharzen, Harnstoffformaldehydhar­ zen und Klebstoffen auf Basis von polymerem Diisocyanat. 7. Use of the resulting glue liquor as a binder in Combination with wood-based binders, especially with Phenol formaldehyde resins, tannin formaldehyde resins, urea formaldehyde resins zen and adhesives based on polymeric diisocyanate.   8. Verfahren nach Anspruch 1 und 7, dadurch gekennzeichnet, dass die Bindemittelflotte nur in den Deckschichten von mehrschichtigen Holzspanplatten oder. MDF oder OSB eingesetzt wird.8. The method according to claim 1 and 7, characterized in that the Binder liquor only in the top layers of multilayer chipboard or. MDF or OSB is used. 9. Verfahren nach Anspruch 1 und 7, dadurch gekennzeichnet, dass die Bindemittelflotte nur in der Mittelschicht von mehrschichtigen Holzwerkstoffplatten eingesetzt wird.9. The method according to claim 1 and 7, characterized in that the Binder fleet only in the middle layer of multi-layer wood-based panels is used. 10. Verfahren nach Anspruch 1 und 7, dadurch gekennzeichnet, dass die Bindemittelflotte in Deck- und Mittelschicht von mehrschichtigen Holzwerkstoffplatten eingesetzt wird.10. The method according to claim 1 and 7, characterized in that the Binder liquor in the top and middle layers of multilayer Wood-based panels are used. 11. Verfahren nach Anspruch 1 und 7, dadurch gekennzeichnet, dass der pH-Wert während der Rindenextraktion alkalisch eingestellt wird.11. The method according to claim 1 and 7, characterized in that the pH is made alkaline during bark extraction. 12. Verfahren nach Anspruch 1 und 7, dadurch gekennzeichnet, dass der pH-Wert der Bindemittelflotte alkalisch eingestellt wird.12. The method according to claim 1 and 7, characterized in that the pH of the Binder liquor is made alkaline. 13. Verfahren nach Anspruch 1 und 7, dadurch gekennzeichnet, dass der pH-Wert der Bindemittelflotte sauer eingestellt wird.13. The method according to claim 1 and 7, characterized in that the pH of the Binder liquor is acidified. 14. Verwendung der extrahierten Rinde nach Fermentierung als Bodenverbesserungsmittel.14. Use of the extracted bark after fermentation as Soil improvers. 15. Verwendung der aufgeschlossenen Gebrauchtspanplatten und Gebrauchtfaserplatten als Rohstoff für Span- und Faserplatten.15. Use of the unlocked chipboard and Used fiberboard as a raw material for chipboard and fiberboard. 16. Verwendung der extrahierten Rinde als Energierohstoff.16. Use of the extracted bark as an energy resource.
DE2000124946 2000-05-22 2000-05-22 Tannin-containing binder liquor for use along with other binders in chip- or fiber-board production, obtained by conventional extraction of bark and then using the extract to break down waste aminoplast-bonded wood materials Pending DE10024946A1 (en)