CS274501B2

CS274501B2 - Elasto-plastic hydroisolant

Info

Publication number: CS274501B2
Application number: CS288289A
Authority: CS
Inventors: Bohumil Doc Ing Csc Kloboucek; Bojan Ing Cermak; Josef Ing Speta
Original assignee: Kloboucek Bohumil Doc Ing Cs; Cermak Bojan; Josef Ing Speta
Priority date: 1989-05-15
Filing date: 1989-05-15
Publication date: 1991-04-11
Also published as: CS288289A2

Abstract

The solution concerns an elasto-plastic hydroinsulation matter based on crude-oil asphalt, ataxic amorphous polypropylene and organic admixture, or eventually filling agent. It is characteristic by the fact that it contains from 0.1 to 75 percent by weight of crude-oil asphalt with softening point KK up to 100 degrees C, from 10 to 60 percent of ataxic amorphous polypropylene with softening point KK above 100 degrees C, from 5 to 40 percent by weight of plasticizing agent represented by tall oil or its mixture with mineral oil with viscosity above 70.10<-2> x cm<2> x s<-1> at 50 degrees C, and from 0.1 to 30 percent of elasticizing admixture represented by acrylate polymer. This hydroinsulation matter can be used mainly in building industry and in other branches.

Description

Vynález se týká elasto-plastické hydroizolační hmoty na bázi ropného asfaltu, ataktického amorfního polypropylenu, organických přísad a případně plniva, která slouží k vytváření různých útvarů a výrobků v národním hospodářství, zejména ve stavebnictví a jiných oborech.The present invention relates to an elastic-plastic waterproofing composition based on petroleum asphalt, atactic amorphous polypropylene, organic additives and, optionally, filler, which serves to form various formations and products in the national economy, particularly in the construction and other fields.

K uvedeným účelům se zpravidla používají hmoty, které se zhotovuji z asfaltů oxidovaných s bodem měknutí nad 50 °C KK. Jejich nevýhodou je, že nejsou dostatečně pružné a za chladu jsou křehké, což má za důsledek, že jejich účinek je krátkodobý, nejistý.As a rule, materials are used which are made of asphalts oxidized with a softening point above 50 ° C KK. Their disadvantage is that they are not flexible enough and brittle in the cold, which results in their effect being short-lived, uncertain.

Uvedené nedostatky odstraňuje elasto-pla9tická hydroizolační hmota podle vynálezu, která se vyznačuje tim, že obsahuje v % hmotnosti 0,1 až 75 % ropného asfaltu o bodu měknutí Kl< do 100 °C, 10 až 60 % ataktického amorfního polypropylenu o bodu měknuti KK nad 100 °C, 5 až 40 % plastifikačni přísady, kterou Je tálový olej, případně jeho směs s mi_— Q O _M1 n nerálním olejem o viskozitě nad 70 . 10 cm . s při 50 Ca 0,1 až 30 % elastifikačni přísady, kterou je akrylátový polymer. Podstatou vynálezu Jaou zvolené suroviny a jejich vzájemný poměr tak, aby vytvořily ve hmotě stálý koloidní systém. Vnější souvislou fázi systému tvoří ataktický amorfní polypropylen s plastifikačními a elastifikačnimi přísadami. Vnitřní rozptýlená fáze je dána asfaltovými částicemi a případně plnidly.The above-mentioned drawbacks are overcome by the elastoplastic waterproofing composition according to the invention, characterized in that it contains 0.1% to 75% by weight of petroleum asphalt with a softening point Kl <100 ° C, 10 to 60% of atactic amorphous polypropylene with a softening point KK above 100 ° C, 5 to 40% of a plasticizer, which is tall oil, or a mixture thereof with a mi _- QO _M 1 n mineral oil with a viscosity above 70. 10 cm. with at 50 Ca 0.1 to 30% of an elasticizing additive which is an acrylate polymer. It is an object of the invention to select the raw materials and their ratio to each other so as to form a stable colloidal system. The outer continuous phase of the system consists of atactic amorphous polypropylene with plasticizing and elastifying additives. The internal dispersed phase is determined by the asphalt particles and optionally by the fillers.

Elasto-plastická hydroizolační hmota vytvořená podle vynálezu vykazuje vlastnosti vnějši fáze koloidni soustavy. Elastifikačni přísada zachovává ve hmotě svou strukturu a dává jí tažnost a pružnost. Plastifikačni přísada snižuje bod lámavosti hmoty za hranice, které nemohou dosáhnout asfalty, dává hmotě vysokou lepivost a svými polárními skupinami zajištuje zvýšenou přilnavost hmoty k podkladu, se kterým je spojena. Elasto-plastická hydroizolační hmota vykazuje značný rozsah tepelné citlivosti, který zajištuje, že hmota si zachovává svoji deformační schopnost a tedy i souvislost a tim i svůj hydroizolační účinek v širokém rozsahu záporných a kladných teplot, kterým jsou hydroizolační hmoty v praxi vystaveny, přičemž je významné, že elasto-plastické hydroizolační hmota podle vynálezu je tažná a pružná i při nižších teplotách. Tyto vlastnosti umožňují široké uplatněni elasto-plastické hmoty.The elastic-plastic waterproofing material produced according to the invention exhibits properties of the external phase of the colloidal system. The elasticizing additive retains its structure in the mass and gives it elasticity and elasticity. The plasticizing agent reduces the breaking point of the mass beyond the limits that cannot reach the asphalt, gives the mass a high tack and, with its polar groups, ensures an increased adhesion of the mass to the substrate to which it is attached. The elastic-plastic waterproofing material exhibits a considerable range of thermal sensitivity, which ensures that the material retains its deformation capability and hence its continuity and hence its waterproofing effect over a wide range of negative and positive temperatures to which the waterproofing materials are exposed in practice, The elastomeric waterproofing composition according to the invention is ductile and elastic even at lower temperatures. These properties allow a wide application of the elastic-plastic material.

Důkazam elasto-plastických vlastností hmoty jsou následující příklady složení hmot podle vynálezu a jejich vlastnosti vyjádřené rozsahem tepelné citlivosti, to je jejich bodem měknuti a bodem lámavosti, jejich duktilitou k posouzení tažnosti a pružnosti a návratnosti deformace po protaženi.The following examples of composition of the compositions according to the invention and their properties in terms of thermal sensitivity, i.e. their softening point and breaking point, their ductility to assess the ductility and elasticity, and the recovery of strain after elongation, are proof of the elasto-plastic properties of the mass.

Přiklad 1Example 1

Složení:Ingredients:

asfalt AP 80 o bodu měknuti KK 43 °C v % hmotnosti 50 ataktický amorfní polypropylen o bodu měknuti KK 152 °C a % hmotnosti 20 tálový olej surový v % hmotnosti 20 akrylátový polymer v % hmotnosti 10asphalt AP 80 with softening point KK 43 ° C in% weight 50 atactic amorphous polypropylene with softening point KK 152 ° C and% weight 20 tall oil crude in% weight 20 acrylic polymer in% weight 10

100100 ALIGN!

Vlastnosti:Properties:

bod měknuti KK ve °C 101 bod lámavosti ve °C - 25 duktilita při 25 ^DC v cm 10 návratnost deformace po protaženi v % 40softening point KK in ° C 101 breaking point in ° C - 25 ductility at 25 ^D C in cm 10 recovery of strain after elongation in% 40

Příklad 2Example 2

Složení:Ingredients:

asfalt AP 80 o bodu měknuti KK 43 °C v % hmotnosti 50 ataktický amorfní polypropylen o bodu měknuti KK 152 ^DC v % hmotnosti 25 tálový olej surový v % hmotnosti 11asphalt AP 80 with softening point KK 43 ° C in% weight 50 atactic amorphous polypropylene with softening point KK 152 ^D C in% weight 25 tall oil crude in% weight 11

CS 274 501 B2 minerální olej o viskozitě 80.10^-2._cnl ²,g^ při 50 ^DC v % hmotnosti 10 akrylátový polymer v % hmotnosti 4CS 274 501 B2 mineral oil with viscosity 80.10 ^- 2. _cnl ² , g ^ at 50 ^D C in weight% 10 acrylate polymer in weight% 4

100100 ALIGN!

Vlastnosti:Properties:

bod měknuti KK ve °C 130 bod lémavosti ve °C - 25 duktilita při 25 °C v cm 4 návratnost deformace po protaženi v % 20softening point KK in ° C 130 break point in ° C - 25 ductility at 25 ° C in cm 4 elongation recovery after elongation in% 20

Přiklad 3 Složeni:Example 3 Composition:

asfalt AP 80 o bodu měknuti KK 43 °C v % hmotnosti 33 ataktický amorfní polypropylen o bodu měknuti KK 152 ⁰ v % hmotnosti 27 tálový olej surový v % hmotnosti -27 akrylátový polymer v % hmotnosti 13asphalt AP 80 with softening point KK 43 ° C in% by weight 33 atactic amorphous polypropylene with softening point KK 152 ⁰ in% by weight 27 tall oil crude in% by weight -27 acrylic polymer in% by weight 13

100100 ALIGN!

Vlastnosti: bod měknuti KK ve °C Properties: softening point KK in ° C 116 116 bod lámavosti ve °C breaking point in ° C - 25 - 25 duktilita při 25 °C v cm ductility at 25 ° C in cm 48 48 návratnost deformace po protaženi v % return of strain after elongation in% 40 40

Elasticko-plastické vlastnosti hydroizolační hmoty lze upravit poměrem jednotlivých složek. Stejně je tomu i s lepivosti a přilnavostí hmoty, které jsou závislé na obsahu a vlastnostech plastifikační přísady. Množství plastifikačni přísady ovlivňuje rovněž citlivost hmoty vůči tepelnému a mechanickému namáhání. Duktilita je závislá na množství elastifikačni přísady.The elastic-plastic properties of the waterproofing material can be adjusted by the ratio of the individual components. The same is true of the tackiness and adhesion of the mass, which depend on the content and properties of the plasticizing additive. The amount of plasticizer also affects the sensitivity of the mass to thermal and mechanical stresses. The ductility is dependent on the amount of elastifying additive.

Hmota podle vynálezu je termoplastická a po roztaveni se snadno zpracovává. Má široký rozsah použití, zejména jako hmota hydroizolační ve stavebnictvi u střešních krytin, zálivková u vodohospodářských staveb a v jiných oborech.The composition according to the invention is thermoplastic and is easy to process after melting. It has a wide range of applications, especially as a waterproofing material in the construction industry for roofing, watering in water management structures and in other fields.

Claims

P 8 E D MEASURES OF THE INVENTION

Elasto-plastic waterproofing material based on petroleum asphalt, atactic amorphous polypropylene and organic additives or fillers, characterized in that it contains in% by weight 0.1 to 75% of petroleum bitumen with a softening point KK up to 100 ° C, 10 to 60% of atactic amorphous polypropylene having a softening point KK above 100 ° C, 5 to 40% of a plasticizing additive which is tall oil or a mixture thereof with mineral oil having a viscosity of more than 70.10 .cm. s at 50 ° C and 0.1 up to 30% of an elastifying additive, which is an acrylate polymer.