CS273102B1 - Sintered glass for lustrous covering glazes production with increased hydrolytic resistance conditioned on boron trioxide reduced content - Google Patents
Sintered glass for lustrous covering glazes production with increased hydrolytic resistance conditioned on boron trioxide reduced content Download PDFInfo
- Publication number
- CS273102B1 CS273102B1 CS254787A CS254787A CS273102B1 CS 273102 B1 CS273102 B1 CS 273102B1 CS 254787 A CS254787 A CS 254787A CS 254787 A CS254787 A CS 254787A CS 273102 B1 CS273102 B1 CS 273102B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- oxide
- glazes
- sodium
- sintered glass
- hydrolytic resistance
- Prior art date
Description
CS-273102 Bl
Vynález ee týká frity pro výrobu lesklých krycích glazur ae zvýšenou hydrolitickou odolnosti, podmíněnou sníženým obsahem oxidu boritého,
Frity a z nich vyrobené lesklá krycí glazury na obklódačky ee doeud vyrábějí tavením kmene, eloženého z práškové směsi křemene, živců, boraxu, kyseliny borité, mramoru, vápence, zirkonu, kaolinu, dolomitu a některých fakultativních přísad jako sloučenin barya, zinku, olova, lithia, fluorokřemičltanu sodného a fluoridu vápenatého.
Obsah boru jako oxidu boritého se pohybuje okolo 15 % hmot. Toto množetvi oxidu boritého za přítomnosti alkálii vede ke sníženi hydrolytlcké odolnosti frlt při mokrém mleti na glazury, k tvorbě koloidnich částic, tim k vzniku vad povrchu glazovaného zboží po výpalu, které se projevují nehomogenitou zákalu (bělosti), matnými čmouhami na povrchu glazur, nestejnoměrnou silou glazury, vlnkami a drobnými vpichy.
Z těchto důvodů bylo účelné nalézt hydrolyticky odolnou fritu, která dává glazury s kvalitním povrchem bez vad, jejichž přítomnost je podmíněna hydrolýzou během mleti za mokra. Cestou k tomu byla úprava oxidického složeni frity. Cíle bylo dosaženo tim, že ae vyvinula frita podle vynálezu ae sníženým obsahem oxidu boritého pro přípravu lesklých krycích glazur. Frita byla připravena na bázi oxidu křemičitého, hlinitého, vápenatého, sodného, draselného, boritého, barnatého a zirkomlčltého · možnými přísadami oxidu hořečnatého, zinečnatého, fluoridu vápenatého a fluorokřemičltanu sodného.
Podstata vynálezu spočivá v tom,že frita obsahuje hmotnostně:
| oxid křemičitý oxid hlinitý oxid vápenatý | Si02 ai2o3 CaO | 57,0 až 55,0 % | |
| 2,0 až 1.0 až | 6.5 % 5.5 % | ||
| oxid boritý | B2°3 | 7,0 až | 13.5 % |
| oxid sodný | Na20 | 0,5 až | 5,0 % |
| oxid draselný | 0,5 až | 7.0 % | |
| oxid barnatý | BaO | 1.5 až | 6.5 % a |
| oxid zirkoničitý | Zr02 | 0,5 až | 10.0 % |
| lůže dála obsahovat: | |||
| oxid zinečnatý | ZnO | stopy až | 5.0 % |
| oxid hořečnatý | MgO | stopy až | 4.0 % |
| fluorid vápenatý | CaF2 | stopy až | 3,0 % a/nebo |
| fluorokřemičitan sodný | Na2SiF6 | stopy až | 4.0 %. |
Snížením obsahu oxidu boritého na 7,0 až 13,5 % hmot. bylo dosaženo zvýšeni hydrolytické odolnosti frity při mleti za mokra na glazuru, vyloučeni tvorby koloidnich částic, a v důsledku toho byl odstraněn vznik nehomogenity zákalu (bělosti), matných šmouh, nestej noměrné sily glazury, vlnek a drobných vplchů glazovaného povrchu při pálicím cyklu 30 minut až 16 hodin a výdrži 5 minut až 3 hodiny na maximální teplotě 1 050 °C až 940 °C. Zdrojem oxidů ve fritě byly suroviny uživená ve výrobě keramického zboží: křemen, sodný a draselný živec, kyselina boritá, borax, soda, potaš, kaolin, vápenec, mramor, dolomit, zirkon, uhličitan barnatý, případně i zinková běloba, magnezit, fluorid vápenatý a fluorokřamičitan sodný.
Podstata vynálezu je dále objasněna konkrétními příklady složeni frity podle vynálezu. přičemž všechna uvedené složení jsou složeni hmotnostní.
Přiklad 1
Byl připraven kmen o složeni:
oxid křemičitý 63,0 %t oxid hlinitý 5,2 %, oxid vápenatý 4,8 %, oxid sodný 4,5 %, oxid draselný 5,2 %, oxid boritý 7,5 SS, oxid zirkoničitý 7,0 % a oxid barnatý 2,8 %· Frita pro bílou krycí lesklou glazuru byla připravena tavením při teplotě 1 350 až 1 550 °C po dobu 0,5 až 4 hodiny a použita na přípravu glazury pro obkladačkové střepy.
Přiklad 2
Byl připraven kmen o složeni:
CS 273102 Bl oxid křemičitý 62,5 %, oxid hlinitý 3,0 %,· oxid vápenatý 2,5 %, oxid hořečnatý 1,5 %, oxid sodný 2,0 %,< oxid draselný 4,0 %, oxid zinečnatý 4,0 %, oxid barnatý 3,5 %, oxid zirkoničitý 8,0 %, oxid boritý 9,0 %, Frlta pro bílou krycí lesklou glazuru byle připravena tavením při teplotš 1 350 °C ež 1 550 °C po dobu 0,5 až 4 hodiny a použita pro přípravu glazury na obkladačkové střepy·
Příklad 3
Byl připraven kmen o složeni:
oxid křemičitý 60,'6 %, oxid hlinitý 3,0 %, oxid sodný 2,0 %, oxid draselný 5,1 %, oxid barnatý 2,9 %, oxid zirkoničitý 8,1 %, oxid boritý 10,5 %, oxid vápenatý 2,0 %, fluorokřemičitan sodný 1,0 %, oxid hořečnatý 1,3 %, oxid zinečnatý 3,5 %· Frlta pro bílou krycí lesklou glazuru byla připravena tavením při teplotš 1 350 až 1 550 °C po dobu 0,5 až 4 hodiny a použita pro přípravu glazury na obkladačkové střepy.
Glazury připravené z frit podle příkladů 1 až 3 mletím za mokra byla hydrolyticky odolné a nevykazovaly po výpalu vady povrchu.
Obkladačkové otřepy neglazovanó glazurami připravenými z frit podle uvedených příkladů byly vypalovány po dobu 30 min až 16 hodin s výdrži 5 minut až 3 hodiny na maximální teploti 1 050 až 940 °C, Vzniklé lesklá krycí glazury na střepech nšly odolnost proti náhlým zrninám teploty (Harkortova zkouška) 150 až 200 °C při kvalitním povrchu.
Claims (2)
1. Frlta pro výrobu lesklých krycích .glazur se zvýšenou hydrolytickou odolnosti podmíněnou sníženým obsahem oxidu boritého ne bázi oxidů křemičitého, hlinitého, vápenatého, sodného, draselného, barnatóho, zirkoničitého e boritého, vyznačující se tím, že obsahuje hmotnostně:
2. Frita podle bodu 1, vyznačující ee tin, že obsahuje stopy až 5,0 % hmot. oxidu zinečnatóho ZnO, stopy až 4,0 % hmot. oxidu hořečnatého MgO, stopy až 3,0 % hmot, fluoridu vápenatého CaF2 a stopy až 4,0 % hmot. fluorokřemičitanu sodného NagSiFg.a to jednotlivá nebo v jakékoliv vzájemné kombinaci.